WO2000015381A1 - Ultrasonic bonding method - Google Patents
Ultrasonic bonding method Download PDFInfo
- Publication number
- WO2000015381A1 WO2000015381A1 PCT/US1999/000990 US9900990W WO0015381A1 WO 2000015381 A1 WO2000015381 A1 WO 2000015381A1 US 9900990 W US9900990 W US 9900990W WO 0015381 A1 WO0015381 A1 WO 0015381A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- applying
- horn
- anvil
- pressure
- acoustic energy
- Prior art date
Links
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K20/00—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating
- B23K20/10—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating making use of vibrations, e.g. ultrasonic welding
- B23K20/103—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating making use of vibrations, e.g. ultrasonic welding using a roller
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C65/00—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor
- B29C65/02—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by heating, with or without pressure
- B29C65/08—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by heating, with or without pressure using ultrasonic vibrations
- B29C65/083—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by heating, with or without pressure using ultrasonic vibrations using a rotary sonotrode or a rotary anvil
- B29C65/087—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by heating, with or without pressure using ultrasonic vibrations using a rotary sonotrode or a rotary anvil using both a rotary sonotrode and a rotary anvil
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
- B29C66/73—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset
- B29C66/739—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of the parts to be joined being a thermoplastic or a thermoset
- B29C66/7392—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of at least one of the parts being a thermoplastic
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
- B29C66/73—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset
- B29C66/739—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of the parts to be joined being a thermoplastic or a thermoset
- B29C66/7392—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of at least one of the parts being a thermoplastic
- B29C66/73921—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the material of at least one of the parts being a thermoplastic characterised by the materials of both parts being thermoplastics
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/80—General aspects of machine operations or constructions and parts thereof
- B29C66/81—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps
- B29C66/814—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps
- B29C66/8141—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps characterised by the surface geometry of the part of the pressing elements, e.g. welding jaws or clamps, coming into contact with the parts to be joined
- B29C66/81427—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps characterised by the surface geometry of the part of the pressing elements, e.g. welding jaws or clamps, coming into contact with the parts to be joined comprising a single ridge, e.g. for making a weakening line; comprising a single tooth
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/80—General aspects of machine operations or constructions and parts thereof
- B29C66/83—General aspects of machine operations or constructions and parts thereof characterised by the movement of the joining or pressing tools
- B29C66/834—General aspects of machine operations or constructions and parts thereof characterised by the movement of the joining or pressing tools moving with the parts to be joined
- B29C66/8341—Roller, cylinder or drum types; Band or belt types; Ball types
- B29C66/83411—Roller, cylinder or drum types
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/92—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools
- B29C66/924—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the pressure, the force, the mechanical power or the displacement of the joining tools
- B29C66/9241—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the pressure, the force or the mechanical power
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/92—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools
- B29C66/929—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools characterized by specific pressure, force, mechanical power or displacement values or ranges
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/93—Measuring or controlling the joining process by measuring or controlling the speed
- B29C66/934—Measuring or controlling the joining process by measuring or controlling the speed by controlling or regulating the speed
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/93—Measuring or controlling the joining process by measuring or controlling the speed
- B29C66/939—Measuring or controlling the joining process by measuring or controlling the speed characterised by specific speed values or ranges
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/95—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94
- B29C66/951—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools
- B29C66/9512—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools by controlling their vibration frequency
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/95—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94
- B29C66/951—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools
- B29C66/9516—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools by controlling their vibration amplitude
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/40—General aspects of joining substantially flat articles, e.g. plates, sheets or web-like materials; Making flat seams in tubular or hollow articles; Joining single elements to substantially flat surfaces
- B29C66/41—Joining substantially flat articles ; Making flat seams in tubular or hollow articles
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/80—General aspects of machine operations or constructions and parts thereof
- B29C66/82—Pressure application arrangements, e.g. transmission or actuating mechanisms for joining tools or clamps
- B29C66/824—Actuating mechanisms
- B29C66/8242—Pneumatic or hydraulic drives
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/80—General aspects of machine operations or constructions and parts thereof
- B29C66/83—General aspects of machine operations or constructions and parts thereof characterised by the movement of the joining or pressing tools
- B29C66/834—General aspects of machine operations or constructions and parts thereof characterised by the movement of the joining or pressing tools moving with the parts to be joined
- B29C66/8351—Jaws mounted on rollers, cylinders, drums, bands, belts or chains; Flying jaws
- B29C66/83511—Jaws mounted on rollers, cylinders, drums, bands, belts or chains; Flying jaws jaws mounted on rollers, cylinders or drums
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/92—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools
- B29C66/924—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the pressure, the force, the mechanical power or the displacement of the joining tools
- B29C66/9261—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the displacement of the joining tools
- B29C66/92611—Measuring or controlling the joining process by measuring or controlling the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the pressure, the force, the mechanical power or the displacement of the joining tools by controlling or regulating the displacement of the joining tools by controlling or regulating the gap between the joining tools
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/93—Measuring or controlling the joining process by measuring or controlling the speed
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/95—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94
- B29C66/951—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools
- B29C66/9513—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools characterised by specific vibration frequency values or ranges
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/95—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94
- B29C66/951—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools
- B29C66/9517—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the vibration frequency and/or the vibration amplitude of vibrating joining tools, e.g. of ultrasonic welding tools characterised by specific vibration amplitude values or ranges
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C66/00—General aspects of processes or apparatus for joining preformed parts
- B29C66/90—Measuring or controlling the joining process
- B29C66/95—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94
- B29C66/954—Measuring or controlling the joining process by measuring or controlling specific variables not covered by groups B29C66/91 - B29C66/94 by measuring or controlling the thickness of the parts to be joined
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
- B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
- B29K2105/0854—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns in the form of a non-woven mat
Definitions
- the present invention relates to ultrasonic bonding. More particularly, the present invention relates to ultrasonic bonding at high speeds.
- Ultrasonics is the science of the effects of sound vibrations beyond the limit of audible frequencies.
- the object of high power ultrasonic applications is to bring about some permanent physical change in the material treated. This process requires the flow of vibratory energy per unit of area or volume.
- the resulting power density may range from less than a watt to thousands of watts per square centimeter.
- Ultrasonics is used in a wide variety of applications.
- ultrasonics can be used for dust, smoke and mist precipitation; preparation of colloidal dispersions; cleaning of metal parts and fabrics; thermoplastic bonding; the formation of catalysts; the degassing and solidification of molten metals; metal welding; the extraction of flavor oils in brewing; electroplating; drilling hard materials; fluxless soldering; and nondestructive testing such as in diagnostic medicine.
- Ultrasonic force is used to perforate sheet materials.
- U.S. Patent No. 3,966,519 discloses perforating non-woven webs. The ultrasonic energy amount is controlled by applying a fluid to the area where the ultrasonic energy is applied.
- U.S. Patent No. 3,949,127 discloses perforating non-woven webs by applying intermittent ultrasonic fusion to the web and then stretching the web to break the most intensely fused regions causing perforations to form in the web.
- U.S. Patent No. 5,269,981 discloses perforating a thin nonporous film which requires applying a liquid to the film before subjecting it to ultrasonic vibrations.
- U.S. Patent No.5, 735, 984 discloses forming apertures in an adhesive coated non-woven or foam sheet where the height of the flattened raised areas on the anvil is equal to or less than the thickness of the sheet material and adhesive.
- U.S Patent No. 3,697,357 discloses welding sheets made entirely or partially of thermoplastic material or fiber by sealing an area of material.
- U.S. Patent No. 3,939,033 discloses using ultrasonics to simultaneously seal and cut thermoplastic textile material.
- U.S. Patent No. 5,061,331 discloses an ultrasonic cutting and edge sealing apparatus for cutting and sealing semi-permeable and at least partially thermoplastic fabric.
- acoustic bonding or welding such as ultrasonic welding
- two parts to be joined are placed directly below an ultrasonic horn.
- the horn plunges (travels toward the parts) and transmits ultrasonic vibrations into the top part.
- the vibrations travel through the top part to the interface of the two parts.
- the vibrational energy is converted to heat due to intermolecular friction that melts and fuses the two parts.
- the vibrations stop the two parts solidify under force, producing a weld at the joining surface.
- Continuous ultrasonic welding is typically used for sealing fabrics, films, and other parts. In the continuous mode, typically the ultrasonic horn is stationary and the part is moved beneath it.
- Scan welding is a type of continuous welding in which the plastic part or web material is scanned beneath one or more stationary horns.
- rotary horn welding a rotating horn is used typically in conjunction with a rotating anvil.
- traverse welding both the table over which the parts pass and the part being welded remain stationary with respect to each other while moving underneath the horn or while the horn moves over them.
- a horn is an acoustical tool usually having a length of a multiple of one-half of the horn material wavelength and made of, for example, aluminum, titanium, or steel that transfers the mechanical vibratory energy to the part. (Typically, these materials have wavelengths of approximately 25 cm (10 in) . )
- Horn displacement or amplitude is the peak-to- peak movement of the horn face. The ratio of horn output amplitude to the horn input amplitude is termed gain. Gain is a function of the ratio of the mass of the horn at the vibration input and output sections .
- the direction of amplitude at the face of the horn is coincident with the direction of the applied mechanical vibrations.
- ultrasonic cutting and welding use horns which vibrate axially against a rigid anvil, with the material to be welded or cut being placed between the horn and anvil.
- the horn is stationary while the anvil is rotated, and the part passes between the horn and the anvil.
- the linear velocity of the part is matched with the tangential velocity of the working surface of the rotating anvil.
- drag between the part and the horn can cause stress in and around the weld area during welding. Additionally, closure or nip forces also create stress in the bond area.
- One way to minimize these limitations is to shape the working surface of the horn to attain a progressive convergent or divergent gap depending upon the part. This can reduce the stresses but does not eliminate the drag stress. A carrier web can virtually eliminate drag stress.
- a rotary horn with a rotating anvil.
- This system can reduce or eliminate the drag stress during the weld.
- a rotary horn is cylindrical and rotates around an axis.
- the input vibration is in the axial direction and the output vibration is in the radial direction.
- the horn and anvil can be two cylinders close to each other, rotating in opposite directions with substantially equal tangential velocities.
- the part to be bonded passes between these cylindrical surfaces at a linear velocity which equals the tangential velocity of these cylindrical surfaces. Matching the tangential velocities of the horn and the anvil with the linear velocity of the material can minimize the drag between the horn and the material.
- the excitation in the axial direction is similar to that in conventional plunge welding.
- U.S. Patent No. 5,096,532 describes two classes of rotary horn.
- the patent compares a commercially available rotary horn, manufactured by Mecasonic of Annemasse France (Mecasonic horn) and a rotary horn described in the '532 patent.
- the shape of the '532 horn differs from that of the Mecasonic horn; the '532 horn is solid, and the Mecasonic horn is a partially hollowed cylinder.
- the Mecasonic horn is a full wavelength horn.
- the axial vibration excites the cylindrical bending mode to provide the radial motion, and the mode of vibration depends on Poisson' s ratio.
- the radial motion of the weld face is in phase with the excitation, and there are two nodes for the axial motion, and two nodes for radial motion.
- the '532 horn is a half wavelength horn.
- the axial vibration provides the radial motion.
- the mode of vibration is independent of Poisson' s ratio.
- the radial motion of the weld face is out of phase with the excitation, and there is only one node, at the geometric center of the weld face.
- U.S. Patent No. 5,707,483 and U.S. Patent No. 5,645,681 describe novel rotary acoustic horns.
- welding is governed by the various parameters which can be changed to alter the welding process. These parameters include the frequency, amplitude of vibration, the duration of ultrasonic exposure, temperature (which is a function of the frequency) , and the pressure between the horn and the anvil.
- the invention is a method of high speed bonding at least one material including at least one thermoplastic component.
- the method includes applying acoustic energy, using an acoustic horn and an anvil, to the material.
- the method also includes applying force to at least one of the horn and the anvil to yield a peak pressure between the horn and the anvil of at least
- the acoustic energy and pressure are applied for a time sufficient to create bonds within the material such that the material is sufficiently quenched before reducing the pressure.
- the method can include applying acoustic energy at an amplitude of vibration selected in combination with the frequency of vibration to yield an acoustic velocity of no greater than 4.72 m/s.
- the acoustic energy and pressure can be applied for a time sufficient to create bonds in the material such that the material is sufficiently quenched before reducing the pressure.
- Thermoplastic peak temperatures are reached such that sufficient heating occurs to create acceptable bond strength and the bond area is cooled adequately and in sufficient time to prevent internal and external stresses from adversely affecting bond quality and to prevent bond degradation such as holes or cut edges.
- the peak pressure could be at least 3.448 x 10 7 N/m 2 , or at least 6.895 x 10 7 N/m 2 .
- the total basis weight of the laminates can be at least 200 gm/m 2 .
- the acoustic energy can be at a frequency of at least 10,000 Hz, and can be from 14,000 Hz through 32,000 Hz.
- the acoustic velocity can be no greater than 3.15 m/s.
- the method can include continuous welding or plunge welding and the materials can move past the acoustic horn at speeds of more than 30 cm/min.
- the material can include woven layers; films; non- wovens; and non-thermoplastic materials which includes at least one of a cotton-based material and a paper- based material.
- the anvil dimensions can be selected in combination with the properties of the material being bonded, the amplitude of the applied acoustic energy, the pressure on the anvil, and the thermal conductivities of the horn and anvil.
- the Figure is a side view of patterned rotating anvil with a rotary horn.
- the invention is a method of rapidly bonding (also called welding) materials using acoustic energy using acoustic horns and anvils.
- a material 10 passes from an unwind roll 12 to a winder roll 14 between a horn 16 and an anvil 18. As shown in the Figure, both the horn 16 and the anvil 18 rotate. The anvil 18 is patterned.
- the horn can operate at various frequencies such as those above 10,000 Hz.
- the horn can be an ultrasonic horn operating at frequencies at or above 20,000 Hz.
- This method can be used to bond materials which can have low or high loft. (Bonding includes reinforcing, laminating, joining.)
- Laminates refers to flexible web-type materials and can include two or more layers. Materials which have at least one thermoplastic layer where the total basis weight of the material is at least 200 gm/m 2 can be bonded (as can less massive materials) .
- the method can be used on laminates including thermoplastic and non-thermoplastic combinations, such as non-wovens, wovens, films, papers, and cottons.
- the method can include applying acoustic energy to the materials at relatively low amplitudes and creating a pressure between the horn and the anvil that is relatively high.
- a key is the use of very high weld pressures typically in combination with amplitudes that are lower than would typically be used for high speed bonding of high basis weight materials.
- the amplitude of vibration and the applied frequency are related; the resulting transfer of energy for a low amplitude and high frequency can be the same as that for a relatively high amplitude and relatively low frequency. These parameters are proportional. That is, increasing the amplitude and decreasing the frequency can yield the same heating.
- the rate of transfer of energy from acoustic waves depends on the square of the amplitude and the square of the angular frequency. Because the ultrasonic velocity is the amplitude times the angular frequency, the rate of energy transfer is dependent on the square of the ultrasonic velocity. (The rate of viscoelastic heating in a polymer is proportional to the angular frequency times the square of the amplitude.) Thus, the rate of energy transfer can be the same if one uses twice the frequency but half the amplitude. For example, for an amplitude that is 75 microns peak-to- peak and a frequency of 20,000 Hz, the peak amplitude is 37.5 microns. The angular frequency is 2 ⁇ times 20,000 Hz. The ultrasonic velocity is therefore:
- the amplitude values are those for systems operating at a frequency of 20,000 Hz.
- the required amplitude decreases with higher frequencies.
- the equivalent amplitudes to arrive at the same ultrasonic velocities for other frequency systems can be obtained by multiplying the listed amplitudes by the ratio of 20,000 Hz (the frequency used to obtain the listed amplitudes) and the frequency of interest.
- the method can include applying acoustic energy to the materials at an amplitude of vibration no greater than 75 microns peak-to-peak. Amplitudes of no greater than 50 microns peak-to-peak can be used. These amplitudes are less than those conventionally used, which are typically 75 to 100 microns or more even for lower speed continuous bonding.
- the method also includes applying a force to at least one of the horn and the anvil to yield an average pressure between the horn and the anvil of at least 2.068 x 10 7 N/m 2 (3,000 psi) .
- This pressure is high, and in many instances can be greater than 1.379 x 10 8 N/m 2 (20,000 psi). These pressures are much more than those currently used, which typically are from 6.895 x 10 5 N/m 2 (100 psi) to 6.895 x 10 6 N/m 2 (1000 psi).
- the force can be created using known methods including pneumatics, hydraulics, mass and gravity, springs, material expansion (such as by piezoelectric or thermal) or by setting a fixed gap between the horn and anvil.
- the pressure between the horn and anvil is determined by dividing the force applied to the horn or anvil by the area of the weld site(s) where the material is in contact with the horn and anvil. For plunge welding, dividing the applied force by the weld area in contact between the horn and anvil yields a pressure that is an average over the weld area for that weld (the mechanical alignment variation or welding rate variation of particular weld locations in the weld area can give rise to locally higher or lower forces) . Additionally, the applied force can vary during welding. The force for the calculation is the highest force that is applied during the part of the weld cycle where the material is being welded.
- the area is the area of the material in contact with the weld sites between the horn and anvil on the upweb side of the weld nip. This area is the length of the material times the width of the weld sites.
- the average pressure then is determined by applying the force between the horn and anvil, while keeping the horn, anvil, and material stationary. The horn is vibrated for the short time necessary to create a bond, and the surface area of the resultant weld is measured. If the weld area includes discrete weld pads, then the measured area is the length of the pad times the width times the number of pads bonded.
- This area measured is about twice the actual area because during a continuous operation the material leaving the weld nip has already been bonded and is thinner; in the static weld test, the material on both the input and output side of the nip is bonded.
- the applied force is divided by half the measured weld surface area to yield the average pressure. This is an average pressure because the radius of a rotating anvil creates a pressure profile on the material between the horn and anvil as a function of the closure gap and the weld state of the material as it progresses through the nip.
- the application of acoustic energy and pressure occurs for a time sufficient to create bonds between the adjacent layers of materials and to sufficiently quench the materials before reducing the pressure.
- the pressure reduction occurs when the material leaves the weld nip area.
- the materials must reach thermoplastic peak temperatures to yield sufficient polymer diffusion for compatible materials or melting of at least one polymer to create a bond to another material such as to form a laminate. (This could be, for example, polypropylene flowing into or around a non-melting surface or fiber.)
- the heating needs to be sufficient to yield diffusion bonding or movement of one material around or into another material's surface to make a mechanical surface bond. Yet the heating need not actually melt the materials.
- the bond area must be cooled adequately and quickly before leaving the nip between the horn and the anvil and before relieving the applied force to prevent internal and external stresses from adversely affecting bond quality such as by weakening of the bonds, creating holes, or material melt back.
- the heating must be sufficiently localized to avoid excessive temperatures at the transition line between the melted or partially melted polymer at the joint and the polymer adjacent to the bond area.
- the material is not subjected to stresses which can adversely affect the bond quality. Rapid heating without overheating and rapid cooling reduces excessive temperatures in the bond (or seal) and in the periphery of the bond. This increases the strength of the weld and reduces bond degradation such as excessively brittle bonds; overheating at the edges of the bond; and hole formation; it increases the ability of the bond to withstand both internal and external stresses immediately after bonding.
- the inventors have found that despite the large body of publicly available information about ultrasonic bonding, there was still an unfilled need to improve the bonding process and to bond at higher speeds.
- the particular parameters to be optimized and the combinations of levels of each parameter solves a long-felt, unmet need.
- the method combines very high pressures with relatively low amplitudes of ultrasonic vibration. These characteristics are selected within relatively narrow and previously unknown process windows which permit high speed continuous ultrasonic bonding of web materials. These process windows can also extended to plunge weld applications to improve weld quality.
- the method can be varied by optimizing various parameters which can include: ultrasonic amplitude; pressure; exposure time; material properties (such as melt temperatures, absorption coefficients, melt rheology, and thermal conductivities) ; heat losses (such as by thermal conductivity) to the anvil, the horn, carrier webs, surrounding polymers, absorptive additives, and other locations; and weld geometries. These parameters are selected in combination with each other. Characteristics to vary include the properties of the material being bonded, the amplitude of the applied acoustic energy and the pressure between the horn and anvil, and the thermal conductivities of the horn and anvil.
- Anvil properties include its length, width, edge radius, surface texture, and thermal conductivity, and the dimensions of the weld sites on the anvil, their orientation and spacing. The specific method is to choose anvil dimensions, then optimize the processing conditions using the material properties. If they are suboptimal, then modify the anvil dimensions. If subsequent iterations are unsuccessful, then investigate material property alternatives.
- weld strength and quality tend to decrease with higher processing speeds and with increases in the web loft and mass during high speed continuous bonding of web-based materials. (Also, the weld quality decreases with increases in the non-woven material basis weight for plunge welding.) Tests by the inventors have demonstrated that this problem exists because the melted web layers do not become adequately quenched before leaving the bonding nip.
- the inventors have found that by increasing the pressure on the weld site by 5 to 50 times over typical applications one creates a process that is a hybrid between thermal and ultrasonic bonding. It has also been shown to be beneficial for many materials, such as lofty non-wovens, to reduce the weld amplitude by about half of what would normally be desired. When working with less lofty materials, such as woven materials or film, reduced weld amplitude is not critical. Good bonding can be attained by the application of acoustic energy at high pressures without reducing amplitude. The selection of amplitude is material dependent.
- This process produces high quality welds and bonds and can do so at relatively high speeds of more than 30 m/min (100 ft/min) with high basis weight materials. These conditions also improve the bonding ability of thinner constructions and allow higher web speeds to be used.
- Non-woven bonding of 430 gm/m 2 materials has been demonstrated at speeds of 120 m/min (400 ft/min) . Higher speeds are possible because this speed was limited by the capabilities of the equipment used, not the process itself. Typically, higher loft materials, higher web speeds, and lower amplitudes require higher bonding pressure.
- the high pressures and low amplitudes are sufficient to create a diffusion bond; the high pressure rapidly decreases the thickness at the weld site to limit the rate of energy input, to decrease the quantity of heat to be removed, and to reduce the weld thickness to allow the thin weld area to more rapidly give up its heat to the horn and anvil (which serve as heat sinks) .
- the higher pressures promote freezing of the thin weld area before excessive displacement of the material from the weld site occurs and cuts the weld area or creates a too thin weld.
- the seal thickness and the floating gap between the horn and anvil are a result of the material freezing before leaving top dead center area of the anvil.
- the method of welding can be continuous welding or plunge welding.
- a support which can be located at the nodes, allows the use of higher forces than are possible with known horns.
- the support can be in sliding contact; have a low friction, high PV plastic bearing surface (that stands up to the forces and surface speeds used) ; thin (so it loses its heat quickly to the support structure) ; and have a thermally conductive (for example, aluminum) support structure with cooling passages.
- the support can be rigidly or compliantly mounted and can be a block of aluminum with a concave radius where the bearing material is. Alternatively, multiple supports can rollingly contact the horn while incorporating the thin polymer feature.
- the inertial force can help compensate for thicker areas in nonwoven materials.
- the magnitude of this inertial force can be altered by changing the mass of the horn, the anvil, or both.
- the component that is floating and biased toward the other component is the member whose mass is changed.
- the force is less, and with the proper masses it does not become less than the pressures required to bond the thinner material.
- Alternative systems to achieve the additional force could include dual stage springs; piezoelectric; or staged (progressive) pneumatic or hydraulic systems.
Landscapes
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Lining Or Joining Of Plastics Or The Like (AREA)
- Pressure Welding/Diffusion-Bonding (AREA)
- Treatment Of Fiber Materials (AREA)
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU22336/99A AU2233699A (en) | 1998-09-11 | 1999-01-18 | Ultrasonic bonding method |
EP19990902326 EP1112139B1 (en) | 1998-09-11 | 1999-01-18 | Ultrasonic bonding method |
DE1999602928 DE69902928T2 (de) | 1998-09-11 | 1999-01-18 | Ultraschallsverbindungsverfahren |
JP2000569957A JP2002524267A (ja) | 1998-09-11 | 1999-01-18 | 超音波接合法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US09/151,619 US6099670A (en) | 1998-09-11 | 1998-09-11 | Ultrasonic bonding method |
US09/151,619 | 1998-09-11 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2000015381A1 true WO2000015381A1 (en) | 2000-03-23 |
Family
ID=22539541
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US1999/000990 WO2000015381A1 (en) | 1998-09-11 | 1999-01-18 | Ultrasonic bonding method |
Country Status (6)
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1146578A1 (en) * | 2000-04-10 | 2001-10-17 | Matsushita Electric Industrial Co., Ltd. | Battery electrode and manufacturing method and apparatus for the same |
DE10153706A1 (de) * | 2001-10-31 | 2003-07-31 | Kunststoff Zentrum Leipzig | Verfahren und Vorrichtung zur Einkopplung von Ultraschall in ein Spritzgießwerkzeug |
US8129220B2 (en) | 2009-08-24 | 2012-03-06 | Hong Kong Polytechnic University | Method and system for bonding electrical devices using an electrically conductive adhesive |
EP1421000B2 (en) † | 2001-06-19 | 2018-05-30 | Robert Bosch GmbH | Method and system for ultrasonic sealing of food product packaging |
Families Citing this family (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
AR016248A1 (es) * | 1998-05-01 | 2001-06-20 | Dow Global Technologies Inc | Metodo para fabricar capas o laminas fibrosas por soplado en fusion, las laminas o capas de material asi obtenidas |
US6165298A (en) * | 1999-04-30 | 2000-12-26 | Kimberly-Clark Worldwide, Inc. | Patterned anvil-roll |
US6457626B1 (en) * | 2001-01-29 | 2002-10-01 | Branson Ultrasonics Corporation | Symmetric ultrasonic rotary horn |
US6634539B2 (en) | 2001-09-21 | 2003-10-21 | 3M Innovative Properties Company | Adjustable-gap rotary ultrasonic horn mounting apparatus and method for mounting |
US20030148694A1 (en) * | 2002-02-05 | 2003-08-07 | Ghiam Farid F. | Absorbent composition and method of assembling |
US6988500B1 (en) | 2003-05-15 | 2006-01-24 | J. Palmero Sales Company, Inc. | Fog free medical face mask |
EP1900499B1 (de) | 2003-08-13 | 2011-10-26 | Herrmann Ultraschalltechnik GmbH & Co. KG | Vorrichtung zum kontinuierlichen Verbinden und/oder Verfestigen von Materialbahnen mittels Ultraschall |
DE10343325A1 (de) * | 2003-08-13 | 2005-03-10 | Herrmann Ultraschalltechnik | Vorrichtung zum kontinuierlichem Verbinden und/oder Verfestigen von Materialbahnen mittels Ultraschall |
US7229512B2 (en) * | 2003-10-28 | 2007-06-12 | Streicher James G | Non-invasive tear mechanism for flexible packaging and apparatus |
JP4044104B2 (ja) * | 2005-03-31 | 2008-02-06 | 大王製紙株式会社 | 紙シートならびに紙シートの接合方法 |
US20070065592A1 (en) * | 2005-09-16 | 2007-03-22 | Ut-Battelle, Llc | Ultrasonically-assisted bonding of plastics to surfaces of solid material and product formed thereby |
DE102006005734A1 (de) * | 2006-02-07 | 2007-08-09 | Bhs Corrugated Maschinen- Und Anlagenbau Gmbh | Ultraschall-Verbindungsvorrichtung und Verfahren zum Verbinden von Materialbahnen |
US20080254264A1 (en) * | 2007-04-11 | 2008-10-16 | Hiroki Yamaguchi | Textile sleeve for protecting elongate members and method of construction |
US7794555B2 (en) * | 2007-09-05 | 2010-09-14 | Albany International Corp. | Formation of a fabric seam by ultrasonic gap welding of a flat woven fabric |
BRPI0816197B1 (pt) * | 2007-09-05 | 2018-12-18 | Albany Int Corp | método de solda de parte de tecido industrial e costura. |
US7897018B2 (en) * | 2007-09-05 | 2011-03-01 | Albany International Corp. | Process for producing papermaker's and industrial fabrics |
US8088256B2 (en) * | 2007-09-05 | 2012-01-03 | Albany International Corp. | Process for producing papermaker's and industrial fabric seam and seam produced by that method |
JP5341784B2 (ja) * | 2010-01-12 | 2013-11-13 | プライムアースEvエナジー株式会社 | 超音波接合方法、超音波接合装置、及び電池用電極の製造方法 |
DE102014110634A1 (de) * | 2014-07-28 | 2016-01-28 | Herrmann Ultraschalltechnik Gmbh & Co. Kg | Vorrichtung zum Ultraschallbearbeiten von Materialien mit Triggereinrichtung |
DE102015120318B4 (de) * | 2015-11-24 | 2021-05-06 | Webasto SE | Verfahren zum Herstellen einer Rollobahn für eine Rolloanordnung eines Fahrzeugs sowie Rolloanordnung |
MX2018008406A (es) * | 2016-01-29 | 2018-08-23 | Kimberly Clark Co | Sellador ultrasonico. |
US11097444B1 (en) * | 2021-01-22 | 2021-08-24 | Bobak Ha'Eri | Bonding wood or other plant products using ultrasound energy |
US20230405943A1 (en) * | 2022-06-10 | 2023-12-21 | The Procter & Gamble Company | Methods and apparatuses for altering portions of substrates with vibration energy |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2507531A1 (fr) * | 1981-06-12 | 1982-12-17 | Mecasonic Sa | Procede et dispositif de soudage de films en matiere plastique par ultrasons |
EP0457187A2 (en) * | 1990-05-18 | 1991-11-21 | Kimberly-Clark Corporation | Ultrasonic rotary horn and application of same |
EP0894612A2 (en) * | 1990-05-18 | 1999-02-03 | Kimberly-Clark Worldwide, Inc. | Ultrasonic rotary horn and application of same |
Family Cites Families (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3229076A1 (de) * | 1981-08-07 | 1983-03-24 | Pola Chemical Industries, Inc., Shizuoka | Verfahren und vorrichtung zum verschweissen des bodens eines rohrfoermigen behaelters aus kunstharz |
US4534818A (en) * | 1983-12-22 | 1985-08-13 | Frito-Lay, Inc. | Method and apparatus for ultrasonic sealing |
US4668316A (en) * | 1985-12-10 | 1987-05-26 | Branson Ultrasonics Corporation | Welding thin thermoplastic film by ultrasonic energy |
US5096532A (en) * | 1990-01-10 | 1992-03-17 | Kimberly-Clark Corporation | Ultrasonic rotary horn |
US5057182A (en) * | 1990-01-19 | 1991-10-15 | Sonokinetics Group | Ultrasonic comb horn and methods for using same |
US5110403A (en) * | 1990-05-18 | 1992-05-05 | Kimberly-Clark Corporation | High efficiency ultrasonic rotary horn |
GB2282559B (en) * | 1993-10-07 | 1998-04-15 | Rawson Francis F H | Ultrasonic cutting device |
US5552013A (en) * | 1994-06-29 | 1996-09-03 | Kimberly-Clark Corporation | Apparatus and method for rotary bonding |
BR9509635A (pt) * | 1994-11-08 | 1998-01-06 | Minnesota Mining & Mfg | Processo para formar perfurações em uma folha fina de material e respectiva folha fina de material |
US5682618A (en) * | 1995-04-03 | 1997-11-04 | Minnesota Mining And Manufacturing Company | Viral resistant seam for protective apparel, and method of manufacturing same |
US5645681B1 (en) * | 1996-07-05 | 2000-03-14 | Minnesota Mining & Mfg | Stacked rotary acoustic horn |
US5707483A (en) * | 1996-07-05 | 1998-01-13 | Minnesota Mining And Manufacturing Company | Rotary acoustic horn |
-
1998
- 1998-09-11 US US09/151,619 patent/US6099670A/en not_active Expired - Lifetime
-
1999
- 1999-01-18 JP JP2000569957A patent/JP2002524267A/ja active Pending
- 1999-01-18 DE DE1999602928 patent/DE69902928T2/de not_active Expired - Lifetime
- 1999-01-18 EP EP19990902326 patent/EP1112139B1/en not_active Expired - Lifetime
- 1999-01-18 WO PCT/US1999/000990 patent/WO2000015381A1/en active IP Right Grant
- 1999-01-18 AU AU22336/99A patent/AU2233699A/en not_active Abandoned
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2507531A1 (fr) * | 1981-06-12 | 1982-12-17 | Mecasonic Sa | Procede et dispositif de soudage de films en matiere plastique par ultrasons |
EP0457187A2 (en) * | 1990-05-18 | 1991-11-21 | Kimberly-Clark Corporation | Ultrasonic rotary horn and application of same |
EP0894612A2 (en) * | 1990-05-18 | 1999-02-03 | Kimberly-Clark Worldwide, Inc. | Ultrasonic rotary horn and application of same |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1146578A1 (en) * | 2000-04-10 | 2001-10-17 | Matsushita Electric Industrial Co., Ltd. | Battery electrode and manufacturing method and apparatus for the same |
US6815120B2 (en) | 2000-04-10 | 2004-11-09 | Matsushita Electric Industrial Co., Ltd. | Battery electrode and manufacturing method and apparatus for the same |
US6972044B2 (en) | 2000-04-10 | 2005-12-06 | Matsushita Electric Industrial Co., Ltd. | Battery electrode and manufacturing method and apparatus for the same |
EP1421000B2 (en) † | 2001-06-19 | 2018-05-30 | Robert Bosch GmbH | Method and system for ultrasonic sealing of food product packaging |
DE10153706A1 (de) * | 2001-10-31 | 2003-07-31 | Kunststoff Zentrum Leipzig | Verfahren und Vorrichtung zur Einkopplung von Ultraschall in ein Spritzgießwerkzeug |
DE10153706B4 (de) * | 2001-10-31 | 2005-04-07 | Kunststoff-Zentrum in Leipzig gemeinnützige Gesellschaft mbH | Vorrichtung zur Einkopplung von Ultraschall in ein Spritzgießwerkzeug |
US8129220B2 (en) | 2009-08-24 | 2012-03-06 | Hong Kong Polytechnic University | Method and system for bonding electrical devices using an electrically conductive adhesive |
US8833418B2 (en) | 2009-08-24 | 2014-09-16 | The Hong Kong Polytechnic University | Method and system for bonding electrical devices using an electrically conductive adhesive |
Also Published As
Publication number | Publication date |
---|---|
EP1112139B1 (en) | 2002-09-11 |
EP1112139A1 (en) | 2001-07-04 |
US6099670A (en) | 2000-08-08 |
DE69902928T2 (de) | 2003-05-22 |
JP2002524267A (ja) | 2002-08-06 |
DE69902928D1 (de) | 2002-10-17 |
AU2233699A (en) | 2000-04-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US6099670A (en) | Ultrasonic bonding method | |
EP1113916B1 (en) | Rotary acoustic horn with sleeve | |
JP3796534B2 (ja) | 積重回転式音響ホーン | |
US9579845B2 (en) | Ultrasonic sealing of packages | |
CA1196260A (en) | Dynamic ultrasonic laminating apparatus having post- bonding pressure roll, and concomitant method | |
WO1998049009A1 (en) | Simultaneous amplitude and force profiling during ultrasonic welding of thermoplastic workpieces | |
EP0909225B1 (en) | Rotary acoustic horn | |
CN101137494A (zh) | 弹性层压材料和制造方法 | |
EP1058615B1 (en) | Method and apparatus for welding polymer fabrics | |
US7754141B2 (en) | Bi-material ultrasonic horn with integral isolation member | |
WO2014022801A2 (en) | Ultrasonic sealing of packages | |
KR20020063267A (ko) | 개선된 강도를 갖는 마찰용접된 열가소성 제품 | |
Khmelev et al. | Perfecting of the Technology and Development of the Apparatuses for Ultrasonic Welding | |
US20020197345A1 (en) | Method and device for ultrasound treatment of a fabric | |
EP0589222A2 (en) | Hydrosonically bonded nonwoven/paper material and process for forming the same | |
EP4384383A1 (en) | Depth control of seal line penetration for rotary ultrasonic horn/anvil welding without mechanical stop | |
JP2010143156A (ja) | 超音波溶着法 | |
US20230059804A1 (en) | Ultrasonic consolidation of materials | |
US20230053660A1 (en) | Depth control of seal line penetration for rotary ultrasonic horn/anvil welding without mechanical stop | |
JPS59225917A (ja) | ワイポイント形状模様の形成方法および装置 | |
MXPA01002815A (en) | Rotary acoustic horn with sleeve |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG UZ VN YU ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
ENP | Entry into the national phase |
Ref country code: JP Ref document number: 2000 569957 Kind code of ref document: A Format of ref document f/p: F |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1999902326 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 1999902326 Country of ref document: EP |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
WWG | Wipo information: grant in national office |
Ref document number: 1999902326 Country of ref document: EP |