WO1999039892A1 - Verfahren und vorrichtung zum herstellen von vernetzten polyolefinschäumen - Google Patents
Verfahren und vorrichtung zum herstellen von vernetzten polyolefinschäumen Download PDFInfo
- Publication number
- WO1999039892A1 WO1999039892A1 PCT/DE1999/000277 DE9900277W WO9939892A1 WO 1999039892 A1 WO1999039892 A1 WO 1999039892A1 DE 9900277 W DE9900277 W DE 9900277W WO 9939892 A1 WO9939892 A1 WO 9939892A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- hot air
- plate
- polyolefin
- heat tunnel
- Prior art date
Abstract
Description
Claims