WO1998032796A1 - Matieres de moulage thermoplastiques a haute tenacite - Google Patents

Matieres de moulage thermoplastiques a haute tenacite Download PDF

Info

Publication number
WO1998032796A1
WO1998032796A1 PCT/EP1998/000199 EP9800199W WO9832796A1 WO 1998032796 A1 WO1998032796 A1 WO 1998032796A1 EP 9800199 W EP9800199 W EP 9800199W WO 9832796 A1 WO9832796 A1 WO 9832796A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
monomers
polymer
polymerization
rubber
Prior art date
Application number
PCT/EP1998/000199
Other languages
German (de)
English (en)
Inventor
Graham Edmund Mc Kee
Bernhard Rosenau
Heiner GÖRRISSEN
Ekkehard Jahns
Original Assignee
Basf Aktiengesellschaft
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Aktiengesellschaft filed Critical Basf Aktiengesellschaft
Priority to EP98906876A priority Critical patent/EP0954551A1/fr
Priority to JP53154298A priority patent/JP2001508821A/ja
Publication of WO1998032796A1 publication Critical patent/WO1998032796A1/fr

Abstract

L'invention concerne des matières de moulage contenant A) entre 30 et 98 % en poids de polymérisat thermoplastique comprenant par rapport à A), a1) entre 50 et 100 % en poids d'un composé styrène de la formule générale (I) dans laquelle R1 et R2 désignent hydrogène ou alkyle C¿1?-C8, ou d'un ester(d'alkyle C1-C8) d'acide acrylique ou d'acide méthacrylique ou de mélanges du composé styrène et de l'ester(d'alkyle C1-C8) de l'acide acrylique ou de l'acide méthacrylique, a2) entre 0 et 40 % en poids d'acrylnitrile ou de méthacrylnitrile ou leurs mélanges, et a3) entre 0 et 40 % d'un monomère ou de plusieurs autres monomères différents de a2), insaturé monéthyléniquement, B) entre 1 et 69 % en poids d'un premier polymérisat B) caoutchouteux particulaire ayant un diamètre particulaire d50 moyen en poids de 300 nm ou moins, C) entre 1 et 69 % en poids d'un second polymérisat C) caoutchouteux particulaire ayant un diamètre particulaire d50 moyen en volume compris entre 700 nm et 100 νm, le polymérisat C) étant obtenu selon le procédé de la polymérisation par microsuspension, par i) dispersion des monomères correspondant au polymérisat C) dans l'eau à l'aide d'au moins un colloïde protecteur pour former une dispersion de gouttelettes de diamètre particulaire d50 moyen en volume compris entre 700 nm et 100 νm, et ii) polymérisation des gouttelettes à l'aide d'un initiateur de polymérisation radicalaire, et D) entre 0 et 80 % en poids d'un ou de plusieurs autres polymères.
PCT/EP1998/000199 1997-01-27 1998-01-15 Matieres de moulage thermoplastiques a haute tenacite WO1998032796A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP98906876A EP0954551A1 (fr) 1997-01-27 1998-01-15 Matieres de moulage thermoplastiques a haute tenacite
JP53154298A JP2001508821A (ja) 1997-01-27 1998-01-15 高い靱性を有する熱可塑性成形組成物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19702733.4 1997-01-27
DE19702733A DE19702733A1 (de) 1997-01-27 1997-01-27 Thermoplastische Formmassen mit hoher Zähigkeit

Publications (1)

Publication Number Publication Date
WO1998032796A1 true WO1998032796A1 (fr) 1998-07-30

Family

ID=7818391

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1998/000199 WO1998032796A1 (fr) 1997-01-27 1998-01-15 Matieres de moulage thermoplastiques a haute tenacite

Country Status (6)

Country Link
EP (1) EP0954551A1 (fr)
JP (1) JP2001508821A (fr)
KR (1) KR20000070463A (fr)
CN (1) CN1251120A (fr)
DE (1) DE19702733A1 (fr)
WO (1) WO1998032796A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999037700A1 (fr) * 1998-01-21 1999-07-29 Basf Aktiengesellschaft Procede de fabrication de polymerisats (greffes) en microsuspension ayant l'elasticite du caoutchouc
WO2000011080A1 (fr) * 1998-08-20 2000-03-02 Basf Aktiengesellschaft Matiere moulable asa pour la production de pieces de moulage mates
CN100358945C (zh) * 2005-06-03 2008-01-02 中化国际余杭高分子材料研发设计有限公司 一种耐冲击高抗张强度低光泽苯乙烯系树脂组合物的制备方法
US8969476B2 (en) 2002-06-21 2015-03-03 Sabic Global Technologies B.V. Impact-modified compositions

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19836621A1 (de) * 1998-08-13 2000-02-17 Basf Ag Schlagzähe thermoplastische Formmassen aus syndiotaktischem Polystyrol und Acrylatmodifier
JP2003064231A (ja) * 2001-08-29 2003-03-05 Asahi Kasei Corp 耐候・耐衝撃性スチレン系樹脂組成物
US20030236350A1 (en) * 2002-06-21 2003-12-25 General Electric Company Impact-modified compositions
US11485833B2 (en) * 2019-10-23 2022-11-01 Hexcel Corporation Thermoplastic toughened matrix resins containing nanoparticles

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0052732A1 (fr) * 1980-11-24 1982-06-02 BASF Aktiengesellschaft Masses de moulage thermoplastique
EP0071099A1 (fr) * 1981-07-25 1983-02-09 BASF Aktiengesellschaft Masses à mouler thermoplastiques
EP0326024A2 (fr) * 1988-01-29 1989-08-02 BASF Aktiengesellschaft Matière à mouler et son utilisation
WO1996017878A1 (fr) * 1994-12-09 1996-06-13 Basf Aktiengesellschaft Polymeres greffes caoutchouteux
WO1998007757A1 (fr) * 1996-08-21 1998-02-26 Basf Aktiengesellschaft Procede de production d'un polymere particulaire

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0052732A1 (fr) * 1980-11-24 1982-06-02 BASF Aktiengesellschaft Masses de moulage thermoplastique
EP0071099A1 (fr) * 1981-07-25 1983-02-09 BASF Aktiengesellschaft Masses à mouler thermoplastiques
EP0326024A2 (fr) * 1988-01-29 1989-08-02 BASF Aktiengesellschaft Matière à mouler et son utilisation
WO1996017878A1 (fr) * 1994-12-09 1996-06-13 Basf Aktiengesellschaft Polymeres greffes caoutchouteux
WO1998007757A1 (fr) * 1996-08-21 1998-02-26 Basf Aktiengesellschaft Procede de production d'un polymere particulaire

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999037700A1 (fr) * 1998-01-21 1999-07-29 Basf Aktiengesellschaft Procede de fabrication de polymerisats (greffes) en microsuspension ayant l'elasticite du caoutchouc
WO2000011080A1 (fr) * 1998-08-20 2000-03-02 Basf Aktiengesellschaft Matiere moulable asa pour la production de pieces de moulage mates
US8969476B2 (en) 2002-06-21 2015-03-03 Sabic Global Technologies B.V. Impact-modified compositions
CN100358945C (zh) * 2005-06-03 2008-01-02 中化国际余杭高分子材料研发设计有限公司 一种耐冲击高抗张强度低光泽苯乙烯系树脂组合物的制备方法

Also Published As

Publication number Publication date
DE19702733A1 (de) 1998-07-30
CN1251120A (zh) 2000-04-19
EP0954551A1 (fr) 1999-11-10
KR20000070463A (ko) 2000-11-25
JP2001508821A (ja) 2001-07-03

Similar Documents

Publication Publication Date Title
EP0800555B1 (fr) Masses thermoplastiques de moulage a base de copolymeres greffes et de polymeres sequences
EP0769524B1 (fr) Utilisation des pièces moulées à base de compositions de moulage thermoplastiques
DE10037280A1 (de) Verfahren zur Agglomeration dispergierter Kautschuke
DE4443966A1 (de) Thermoplastische Formmassen
EP0244856A1 (fr) Composition à mouler thermoplastique à base de polycarbonate, ASA et copolymères contenant des unités aromatiques-vinyliques et AN
DE102005022632A1 (de) Agglomerisation von Kautschukdispersionen
DE3939046A1 (de) Thermoplastische formmassen mit hoher kaeltezaehigkeit
WO2006134096A1 (fr) Matieres a mouler thermoplastiques renforcees
EP1224237B1 (fr) Utilisation d'un polyorganosiloxane pour la diminution du blanchissement par le froid ("cold stress whitening").
EP3274385A1 (fr) Procédé pour produire des compositions polymères thermoplastiques ayant un degré de réticulation optimisé
DE4142910A1 (de) Schlagzaehmodifier und diesen enthaltende formmasse
WO1998032796A1 (fr) Matieres de moulage thermoplastiques a haute tenacite
EP0928314B1 (fr) Matieres moulables thermoplatiques
EP3615578B2 (fr) Procédé amélioré de production de copolymères greffés d'abs
WO1999050348A1 (fr) Matiere moulable thermoplastique presentant une resistance elevee a la perforation et de bonnes proprietes antistatiques
DE60012959T2 (de) Polycarbonatmischungen mit verbesserter fliessfähigkeit
EP1034201A1 (fr) Procede de production de polymeres greffes
EP0326024A2 (fr) Matière à mouler et son utilisation
EP1165676B1 (fr) Copolymerisats de styrene a resistance amelioree aux produits chimiques
DE19910916B4 (de) Verwendung von Tetrafluorethylenpolymerisaten zur Verbesserung der Chemikalienbeständigkeit, Verringerung der Quellung und Verbesserung der Spannungsrißbeständigkeit von Styrolcopolymerisaten
DE10308506A1 (de) Acrylatkautschuke und Verfahren zu ihrer Herstellung
DE19951679A1 (de) Verfahren zur Herstellung schlagzäher Kunststoffe
DE19802094A1 (de) Verfahren zur Herstellung von kautschukelastischen Mikrosuspensions(propf)polymerisaten
DE4017680A1 (de) Abs-formmassen
DE10353952A1 (de) Pfropfkautschuk und Verfahren zu seiner Herstellung

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 98803522.7

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): CN JP KR MX SG US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1998906876

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 09341516

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: PA/a/1999/006692

Country of ref document: MX

WWE Wipo information: entry into national phase

Ref document number: 1019997006701

Country of ref document: KR

ENP Entry into the national phase

Ref document number: 1998 531542

Country of ref document: JP

Kind code of ref document: A

WWP Wipo information: published in national office

Ref document number: 1998906876

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1019997006701

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1998906876

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1019997006701

Country of ref document: KR