WO1998024974A1 - Procede de fabrication de papier resistant a l'etat humide - Google Patents
Procede de fabrication de papier resistant a l'etat humide Download PDFInfo
- Publication number
- WO1998024974A1 WO1998024974A1 PCT/US1997/021414 US9721414W WO9824974A1 WO 1998024974 A1 WO1998024974 A1 WO 1998024974A1 US 9721414 W US9721414 W US 9721414W WO 9824974 A1 WO9824974 A1 WO 9824974A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- wet strength
- agent
- web
- fiber
- anionic compound
- Prior art date
Abstract
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
BR9713842-8A BR9713842A (pt) | 1996-12-04 | 1997-11-25 | Método para fabricar papel com resistência úmida |
EP97950660A EP0943036A1 (fr) | 1996-12-04 | 1997-11-25 | Procede de fabrication de papier resistant a l'etat humide |
NZ336391A NZ336391A (en) | 1996-12-04 | 1997-11-25 | method for making wet strength paper by adding a colourless reactive eanionic compound to the slurry |
JP52562898A JP2001505627A (ja) | 1996-12-04 | 1997-11-25 | 湿潤強度紙製造方法 |
CA002271384A CA2271384A1 (fr) | 1996-12-04 | 1997-11-25 | Procede de fabrication de papier resistant a l'etat humide |
AU53606/98A AU729194B2 (en) | 1996-12-04 | 1997-11-25 | Method for making wet strength paper |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US76033196A | 1996-12-04 | 1996-12-04 | |
US08/760,331 | 1996-12-04 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1998024974A1 true WO1998024974A1 (fr) | 1998-06-11 |
Family
ID=25058779
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US1997/021414 WO1998024974A1 (fr) | 1996-12-04 | 1997-11-25 | Procede de fabrication de papier resistant a l'etat humide |
Country Status (10)
Country | Link |
---|---|
EP (1) | EP0943036A1 (fr) |
JP (1) | JP2001505627A (fr) |
KR (1) | KR20000069273A (fr) |
CN (1) | CN1240010A (fr) |
AU (1) | AU729194B2 (fr) |
BR (1) | BR9713842A (fr) |
CA (1) | CA2271384A1 (fr) |
ID (1) | ID22290A (fr) |
NZ (1) | NZ336391A (fr) |
WO (1) | WO1998024974A1 (fr) |
Cited By (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1999045201A1 (fr) * | 1998-03-06 | 1999-09-10 | Kimberly-Clark Worldwide, Inc. | Procede de fabrication de papier presentant une resistance accrue a l'humidite |
WO2000029670A1 (fr) * | 1998-11-12 | 2000-05-25 | Paper Technology Foundation Inc. | Compositions pour le renfort et le traitement de materiaux lignocellulosiques |
WO2000056978A1 (fr) * | 1999-03-19 | 2000-09-28 | Weyerhaeuser Company | Procede d'accroissement de la retention de la charge de feuilles de fibres cellulosiques |
US6194057B1 (en) | 1998-11-12 | 2001-02-27 | Paper Technology Foundation Inc. | Partially impregnated lignocellulosic materials |
US6211357B1 (en) | 1999-12-09 | 2001-04-03 | Paper Technology Foundation, Inc. | Strengthening compositions and treatments for lignocellulosic materials |
WO2001031122A1 (fr) * | 1999-10-25 | 2001-05-03 | Kimberly-Clark Worldwide, Inc. | Papier a hautes performances a l'etat humide, utilisant des composes anioniques polymeres, et son procede de production |
WO2001038638A1 (fr) * | 1999-11-23 | 2001-05-31 | Kimberly-Clark Worldwide, Inc. | Produits de papier hygienique a aptitude au rinçage amelioree |
US6281350B1 (en) | 1999-12-17 | 2001-08-28 | Paper Technology Foundation Inc. | Methods for the reduction of bleeding of lignosulfonates from lignosulfonate-treated substrates |
US6537616B2 (en) | 1998-11-12 | 2003-03-25 | Paper Technology Foundation Inc. | Stam-assisted paper impregnation |
US6537615B2 (en) | 1998-11-12 | 2003-03-25 | Paper Technology Foundation Inc. | Steam-assisted paper impregnation |
US6610174B2 (en) | 1999-10-25 | 2003-08-26 | Kimberly-Clark Worldwide, Inc. | Patterned application of polymeric reactive compounds to fibrous webs |
WO2004001127A2 (fr) * | 2002-06-19 | 2003-12-31 | Lanxess Corporation | Produits de papier resistants et dispersables |
US6787545B1 (en) | 1999-08-23 | 2004-09-07 | Shiongi & Co., Ltd. | Pyrrolotriazine derivatives having spla2-inhibitory activities |
WO2014105689A1 (fr) * | 2012-12-26 | 2014-07-03 | Kimberly-Clark Worldwide, Inc. | Fibres cellulosiques modifiées ayant une liaison à l'hydrogène réduite |
US9410292B2 (en) | 2012-12-26 | 2016-08-09 | Kimberly-Clark Worldwide, Inc. | Multilayered tissue having reduced hydrogen bonding |
US9416494B2 (en) | 2012-12-26 | 2016-08-16 | Kimberly-Clark Worldwide, Inc. | Modified cellulosic fibers having reduced hydrogen bonding |
CN106457860A (zh) * | 2014-04-28 | 2017-02-22 | 惠普发展公司,有限责任合伙企业 | 轻质数字印刷介质 |
US10391094B2 (en) | 2010-11-07 | 2019-08-27 | Impact Biomedicines, Inc. | Compositions and methods for treating myelofibrosis |
US20220412634A1 (en) * | 2017-01-16 | 2022-12-29 | Domtar Paper Company,Llc | Disposable ice pack |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4013188B2 (ja) * | 2002-02-22 | 2007-11-28 | 星光Pmc株式会社 | (メタ)アクリルアミド系ポリマー、その製造方法、製紙用薬品、及びそれを含有する紙 |
JP4522692B2 (ja) * | 2003-11-28 | 2010-08-11 | ダイヤニトリックス株式会社 | 抄紙用粘剤 |
FR2916768B1 (fr) * | 2007-05-31 | 2009-07-24 | Arjowiggins Licensing Soc Par | Feuille de securite resistante au froissement, son procede de fabrication et un document de securite la comprenant |
CN104074098A (zh) * | 2014-06-25 | 2014-10-01 | 金东纸业(江苏)股份有限公司 | 一种造纸浆料的配制方法以及造纸浆料 |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5032226A (en) * | 1988-02-16 | 1991-07-16 | Felix Schoeller Jr. Gmbh & Co., Kg | Base paper for photographic layer support |
EP0685593A2 (fr) * | 1994-05-27 | 1995-12-06 | Kimberly-Clark Corporation | Cellulose sulfonée et son procédé de préparation |
-
1997
- 1997-11-25 CN CN97180292A patent/CN1240010A/zh active Pending
- 1997-11-25 AU AU53606/98A patent/AU729194B2/en not_active Ceased
- 1997-11-25 CA CA002271384A patent/CA2271384A1/fr not_active Abandoned
- 1997-11-25 JP JP52562898A patent/JP2001505627A/ja active Pending
- 1997-11-25 WO PCT/US1997/021414 patent/WO1998024974A1/fr not_active Application Discontinuation
- 1997-11-25 EP EP97950660A patent/EP0943036A1/fr not_active Withdrawn
- 1997-11-25 KR KR1019997004895A patent/KR20000069273A/ko not_active Application Discontinuation
- 1997-11-25 ID IDW990444A patent/ID22290A/id unknown
- 1997-11-25 NZ NZ336391A patent/NZ336391A/xx unknown
- 1997-11-25 BR BR9713842-8A patent/BR9713842A/pt not_active Application Discontinuation
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5032226A (en) * | 1988-02-16 | 1991-07-16 | Felix Schoeller Jr. Gmbh & Co., Kg | Base paper for photographic layer support |
EP0685593A2 (fr) * | 1994-05-27 | 1995-12-06 | Kimberly-Clark Corporation | Cellulose sulfonée et son procédé de préparation |
Non-Patent Citations (1)
Title |
---|
ALLAN, G. G. ET AL: "FIBER SURFACE MODIFICATION. (IX) STEREOTOPOCHEMISTRY OF IONIC BONDING IN PAPER", SVENSK PAPPERSTID. 54, NO. 18: 563-70 (SEPT. 30, 1971). [ENGL.;SWED. & GER. SUM.] CF. ABIPC 41: ABSTR. 9532: 42: ABSTR. 96., XP002060127 * |
Cited By (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1999045201A1 (fr) * | 1998-03-06 | 1999-09-10 | Kimberly-Clark Worldwide, Inc. | Procede de fabrication de papier presentant une resistance accrue a l'humidite |
AU738654B2 (en) * | 1998-03-06 | 2001-09-20 | Research Foundation Of The State University Of New York, The | Method for improved wet strength paper |
WO2000029670A1 (fr) * | 1998-11-12 | 2000-05-25 | Paper Technology Foundation Inc. | Compositions pour le renfort et le traitement de materiaux lignocellulosiques |
US6114471A (en) * | 1998-11-12 | 2000-09-05 | The Proctor & Gamble Company | Strengthening compositions and treatments for lignocellulosic materials |
US6537616B2 (en) | 1998-11-12 | 2003-03-25 | Paper Technology Foundation Inc. | Stam-assisted paper impregnation |
US6194057B1 (en) | 1998-11-12 | 2001-02-27 | Paper Technology Foundation Inc. | Partially impregnated lignocellulosic materials |
US6537615B2 (en) | 1998-11-12 | 2003-03-25 | Paper Technology Foundation Inc. | Steam-assisted paper impregnation |
WO2000056978A1 (fr) * | 1999-03-19 | 2000-09-28 | Weyerhaeuser Company | Procede d'accroissement de la retention de la charge de feuilles de fibres cellulosiques |
US6824649B2 (en) | 1999-03-19 | 2004-11-30 | Weyerhaeuser Company | Method for increasing filler retention of cellulosic fiber sheets |
US6514384B1 (en) | 1999-03-19 | 2003-02-04 | Weyerhaeuser Company | Method for increasing filler retention of cellulosic fiber sheets |
US6787545B1 (en) | 1999-08-23 | 2004-09-07 | Shiongi & Co., Ltd. | Pyrrolotriazine derivatives having spla2-inhibitory activities |
WO2001031122A1 (fr) * | 1999-10-25 | 2001-05-03 | Kimberly-Clark Worldwide, Inc. | Papier a hautes performances a l'etat humide, utilisant des composes anioniques polymeres, et son procede de production |
US6610174B2 (en) | 1999-10-25 | 2003-08-26 | Kimberly-Clark Worldwide, Inc. | Patterned application of polymeric reactive compounds to fibrous webs |
WO2001038638A1 (fr) * | 1999-11-23 | 2001-05-31 | Kimberly-Clark Worldwide, Inc. | Produits de papier hygienique a aptitude au rinçage amelioree |
US6548427B1 (en) | 1999-11-23 | 2003-04-15 | Kimberly-Clark Worldwide, Inc. | Sanitary tissue products with improved flushability |
EP1250196A4 (fr) * | 1999-12-09 | 2003-07-02 | Paper Technology Foundation In | Compositions pour le renfort et le traitement de materiaux lignocellulosiques |
US6306464B2 (en) | 1999-12-09 | 2001-10-23 | Paper Technology Foundation Inc | Strengthening compositions and treatments for lignocellulosic materials |
US6211357B1 (en) | 1999-12-09 | 2001-04-03 | Paper Technology Foundation, Inc. | Strengthening compositions and treatments for lignocellulosic materials |
EP1250196A1 (fr) * | 1999-12-09 | 2002-10-23 | Paper Technology Foundation Inc. | Compositions pour le renfort et le traitement de materiaux lignocellulosiques |
US6281350B1 (en) | 1999-12-17 | 2001-08-28 | Paper Technology Foundation Inc. | Methods for the reduction of bleeding of lignosulfonates from lignosulfonate-treated substrates |
US6458419B2 (en) | 1999-12-17 | 2002-10-01 | Paper Technology Foundation Inc. | Methods for the reduction of bleeding of lignosulfonates from lignosulfonate-treated substrates |
US6620461B2 (en) | 1999-12-17 | 2003-09-16 | Paper Technology Foundation Inc. | Methods for the reduction of bleeding of lignosulfonates from lignosulfonate-treated substrates |
US6623806B2 (en) | 1999-12-17 | 2003-09-23 | Paper Technology Foundation Inc. | Methods for the reduction of bleeding of lignosulfonates from lignosulfonate-treated substrates |
WO2004001127A3 (fr) * | 2002-06-19 | 2004-04-22 | Bayer Chemicals Corp | Produits de papier resistants et dispersables |
WO2004001127A2 (fr) * | 2002-06-19 | 2003-12-31 | Lanxess Corporation | Produits de papier resistants et dispersables |
US10391094B2 (en) | 2010-11-07 | 2019-08-27 | Impact Biomedicines, Inc. | Compositions and methods for treating myelofibrosis |
WO2014105689A1 (fr) * | 2012-12-26 | 2014-07-03 | Kimberly-Clark Worldwide, Inc. | Fibres cellulosiques modifiées ayant une liaison à l'hydrogène réduite |
US9410292B2 (en) | 2012-12-26 | 2016-08-09 | Kimberly-Clark Worldwide, Inc. | Multilayered tissue having reduced hydrogen bonding |
US9416494B2 (en) | 2012-12-26 | 2016-08-16 | Kimberly-Clark Worldwide, Inc. | Modified cellulosic fibers having reduced hydrogen bonding |
CN106457860A (zh) * | 2014-04-28 | 2017-02-22 | 惠普发展公司,有限责任合伙企业 | 轻质数字印刷介质 |
US20220412634A1 (en) * | 2017-01-16 | 2022-12-29 | Domtar Paper Company,Llc | Disposable ice pack |
Also Published As
Publication number | Publication date |
---|---|
CA2271384A1 (fr) | 1998-06-11 |
CN1240010A (zh) | 1999-12-29 |
AU729194B2 (en) | 2001-01-25 |
KR20000069273A (ko) | 2000-11-25 |
EP0943036A1 (fr) | 1999-09-22 |
NZ336391A (en) | 2000-09-29 |
BR9713842A (pt) | 2000-10-31 |
ID22290A (id) | 1999-09-30 |
AU5360698A (en) | 1998-06-29 |
JP2001505627A (ja) | 2001-04-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU729194B2 (en) | Method for making wet strength paper | |
US5935383A (en) | Method for improved wet strength paper | |
US3248353A (en) | Alkylene polyamine resin | |
US2595935A (en) | Wet strength paper and process for the production thereof | |
EP0548960B1 (fr) | Amélioration de la résistance à l'état sec d'un papier grâce à une combinaison de guars anionique et cationique | |
US5225047A (en) | Crosslinked cellulose products and method for their preparation | |
EP0723047B1 (fr) | Amélioration de la résistance du papier fait à partir de pâte des composés carboxyl tensioactifs | |
US5633300A (en) | Enhancement of paper dry strength by anionic and cationic guar combination | |
US5674362A (en) | Method for imparting strength to paper | |
US2721140A (en) | Paper of high wet strength and process therefor | |
KR0159921B1 (ko) | 양이온성 및 음이온성 중합체의 혼합물, 그 제법 및 종이용 건조강도 개선 첨가제로서의 용도 | |
US5783041A (en) | Method for imparting strength to paper | |
US5994449A (en) | Resin compositions for making wet and dry strength paper and their use as creping adhesives | |
JPH03167391A (ja) | 活性サイジング組成物 | |
US4880498A (en) | Dry strength resin of amino/aldehyde acid colloid with acrylamide polymer, process for the production thereof and paper produced therefrom | |
JP2540164B2 (ja) | アミノ―アルデヒド樹脂含有組成物およびその製造方法 | |
US2497074A (en) | Modified urea-formaldehyde resins and methods of preparing the same | |
CN111433407A (zh) | 纸强度改进聚合物组合物和添加剂体系、其用途以及纸制品的制造 | |
FI68435B (fi) | Lignocellulosamaterial med foerbaettrad styrka avvattningsfoermaoga och malbarhet samt saett att framstaella detta | |
US2698787A (en) | Urea-formaldehyde resins for wet strength paper and their use | |
MXPA00008734A (en) | Method for improved wet strength paper | |
McKeel | Impact of Aluminum Chemistry and Order of Addition on Anionic Polyacrylamide Dry Strength Resins |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 97180292.0 Country of ref document: CN |
|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG UZ VN YU ZW AM AZ BY KG KZ MD RU TJ TM |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH KE LS MW SD SZ UG ZW AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
ENP | Entry into the national phase |
Ref document number: 2271384 Country of ref document: CA |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1997950660 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: PA/a/1999/005056 Country of ref document: MX |
|
ENP | Entry into the national phase |
Ref document number: 1998 525628 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1019997004895 Country of ref document: KR |
|
WWE | Wipo information: entry into national phase |
Ref document number: 336391 Country of ref document: NZ |
|
WWE | Wipo information: entry into national phase |
Ref document number: 53606/98 Country of ref document: AU |
|
WWP | Wipo information: published in national office |
Ref document number: 1997950660 Country of ref document: EP |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
WWP | Wipo information: published in national office |
Ref document number: 1019997004895 Country of ref document: KR |
|
WWG | Wipo information: grant in national office |
Ref document number: 53606/98 Country of ref document: AU |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1997950660 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1019997004895 Country of ref document: KR |