WO1998016483A1 - Compositions pour beton et produits en beton fabriques a partir de telles compositions - Google Patents

Compositions pour beton et produits en beton fabriques a partir de telles compositions Download PDF

Info

Publication number
WO1998016483A1
WO1998016483A1 PCT/NZ1997/000138 NZ9700138W WO9816483A1 WO 1998016483 A1 WO1998016483 A1 WO 1998016483A1 NZ 9700138 W NZ9700138 W NZ 9700138W WO 9816483 A1 WO9816483 A1 WO 9816483A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass
slag
concrete
mixture
microns
Prior art date
Application number
PCT/NZ1997/000138
Other languages
English (en)
Inventor
Cliff James Leed
Original Assignee
Leed, Natalie, Lynette, Tira
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from NZ29959696A external-priority patent/NZ299596A/xx
Application filed by Leed, Natalie, Lynette, Tira filed Critical Leed, Natalie, Lynette, Tira
Priority to BR9712526A priority Critical patent/BR9712526A/pt
Priority to JP51822898A priority patent/JP2001504792A/ja
Priority to AU47289/97A priority patent/AU4728997A/en
Priority to EP97909762A priority patent/EP1032544A4/fr
Priority to IL12944697A priority patent/IL129446A0/xx
Priority to PL33277297A priority patent/PL332772A1/xx
Priority to CA 2268625 priority patent/CA2268625A1/fr
Publication of WO1998016483A1 publication Critical patent/WO1998016483A1/fr
Priority to NO991749A priority patent/NO991749L/no

Abstract

On utilise du verre sous forme de fines particules en tant qu'agrégat du béton en vue de la fabrication de produits en béton. Le verre utilisé comporte un nombre important de particules de dimension inférieure à 150 microns. De préférence, on combine le verre à du laitier, le verre et le laitier étant de préférence soumis à une fusion simultanée suivie d'un broyage effectué jusqu'à l'obtention de particules ayant la taille souhaitée. Les produits de cette invention peuvent présenter diverses caractéristiques intéressantes telles que l'étanchéité à l'eau et aux acides, et la résistance à la dégradation par les alcalis ou la silice tout en conservant une résistance mécanique appropriée. Les compositions préférées sont étanches à l'eau et aux acides, résistantes à la dégradation par les alcalis ou la silice et elles acquièrent rapidement, en durcissant, une résistance mécanique élevée.
PCT/NZ1997/000138 1996-10-16 1997-10-16 Compositions pour beton et produits en beton fabriques a partir de telles compositions WO1998016483A1 (fr)

Priority Applications (8)

Application Number Priority Date Filing Date Title
BR9712526A BR9712526A (pt) 1996-10-16 1997-10-16 Composições para uso em concreto e produtos de concreto obtidos a partir das mesmas
JP51822898A JP2001504792A (ja) 1996-10-16 1997-10-16 コンクリート用組成物及びそれから得られるコンクリート製品
AU47289/97A AU4728997A (en) 1996-10-16 1997-10-16 Compositions for use in concrete and concrete products obtained therefrom
EP97909762A EP1032544A4 (fr) 1996-10-16 1997-10-16 Compositions pour beton et produits en beton fabriques a partir de telles compositions
IL12944697A IL129446A0 (en) 1996-10-16 1997-10-16 Compositions for use in concrete and concrete products obtained therefrom
PL33277297A PL332772A1 (en) 1996-10-16 1997-10-16 Cement compositions used for making concrete mixes and precast concrete products obtained using such compositions
CA 2268625 CA2268625A1 (fr) 1996-10-16 1997-10-16 Compositions pour beton et produits en beton fabriques a partir de telles compositions
NO991749A NO991749L (no) 1996-10-16 1999-04-13 Sammensetninger til bruk i betong og betongprodukter fremstilt derav

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
NZ299596 1996-10-16
NZ29959696A NZ299596A (en) 1996-10-16 1996-10-16 Cement and glass particle composition which has been fused and ground
NZ328130 1997-06-19
NZ32813097 1997-06-19

Publications (1)

Publication Number Publication Date
WO1998016483A1 true WO1998016483A1 (fr) 1998-04-23

Family

ID=26651681

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/NZ1997/000138 WO1998016483A1 (fr) 1996-10-16 1997-10-16 Compositions pour beton et produits en beton fabriques a partir de telles compositions

Country Status (10)

Country Link
EP (1) EP1032544A4 (fr)
JP (1) JP2001504792A (fr)
CN (1) CN1233233A (fr)
AU (1) AU4728997A (fr)
BR (1) BR9712526A (fr)
CA (1) CA2268625A1 (fr)
IL (1) IL129446A0 (fr)
NO (1) NO991749L (fr)
PL (1) PL332772A1 (fr)
WO (1) WO1998016483A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20010045071A (ko) * 1999-11-02 2001-06-05 정영수 콘크리트
ES2224878A1 (es) * 2003-08-22 2005-03-01 Asociacion De Investigacion De Industrias De La Construccion Aidico. Procedimiento de reciclado de residuos procedentes de lodos ceramicos como adiciones para cementos de alta resistencia.
WO2007059773A1 (fr) * 2005-11-23 2007-05-31 Petersen Lars Boerthy Utilisation de verre pulverise dans un materiau composite
CN103637548A (zh) * 2013-12-04 2014-03-19 嘉兴良友休闲制品有限公司 水泥预制板桌面及其制作方法
WO2014188034A1 (fr) * 2013-05-20 2014-11-27 Consejo Superior De Investigaciones Científicas (Csic) Résidu de sanitaires pour l'élaboration de ciments, procédé d'obtention et ciments contenant ledit résidu

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7213646B2 (en) * 2005-09-09 2007-05-08 Halliburton Energy Services, Inc. Cementing compositions comprising cement kiln dust, vitrified shale, zeolite, and/or amorphous silica utilizing a packing volume fraction, and associated methods
CN103274619B (zh) * 2013-06-19 2015-01-07 交通运输部公路科学研究所 彩色反光防滑骨料及其制备方法
SK8310Y1 (sk) * 2017-10-25 2018-12-03 Povazska Cementaren As Betónová zmes
JP7029130B2 (ja) * 2020-05-22 2022-03-03 株式会社エステック 気泡含有グラウト、及び、気泡含有グラウトの製造方法

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE848007A (fr) * 1975-11-14 1977-05-05 Composition de materiau cellulaire disperse dans un liant,
WO1980000959A1 (fr) * 1978-11-03 1980-05-15 Allborg Portland Cement Article faconne, materiau composite et methode de production
US4440576A (en) * 1982-09-27 1984-04-03 Corning Glass Works Hydraulic cements prepared from glass powders
US4484949A (en) * 1981-07-03 1984-11-27 Smith & Nephew Research Limited Cement compositions
EP0219726A1 (fr) * 1985-10-09 1987-04-29 The Tohoku Electric Power Co., Inc. Grain pour matériau de construction
EP0427064A2 (fr) * 1989-11-10 1991-05-15 Gebr. Knauf Westdeutsche Gipswerke KG Liant hydraulique et son utilisation
FR2661362A1 (fr) * 1990-04-25 1991-10-31 Tombini Reynald Materiau composite a base de verre concasse et de liant hydraulique ou resineux.
CN1078963A (zh) * 1992-05-21 1993-12-01 郭湘泗 用废玻璃制造无机仿花岗石技术
WO1994019294A1 (fr) * 1993-02-25 1994-09-01 Svensk Glasåtervinning Ab Procede de production de beton
WO1995026323A1 (fr) * 1994-03-29 1995-10-05 Thierry Lefebvre Materiau composite allege et insonorisant a matrice minerale hydraulique et procede d'elaboration d'un tel materiau

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
LU78185A1 (de) * 1977-09-26 1979-04-09 Arbed Verfahren und vorrichtung zur nutzbarmachung von metallurgischen schlacken,insbesondere hochofenschlacken
JPS59156949A (ja) * 1983-02-24 1984-09-06 日本鋼管株式会社 ポリマ−セメントモルタル組成物

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE848007A (fr) * 1975-11-14 1977-05-05 Composition de materiau cellulaire disperse dans un liant,
WO1980000959A1 (fr) * 1978-11-03 1980-05-15 Allborg Portland Cement Article faconne, materiau composite et methode de production
US4484949A (en) * 1981-07-03 1984-11-27 Smith & Nephew Research Limited Cement compositions
US4440576A (en) * 1982-09-27 1984-04-03 Corning Glass Works Hydraulic cements prepared from glass powders
EP0219726A1 (fr) * 1985-10-09 1987-04-29 The Tohoku Electric Power Co., Inc. Grain pour matériau de construction
EP0427064A2 (fr) * 1989-11-10 1991-05-15 Gebr. Knauf Westdeutsche Gipswerke KG Liant hydraulique et son utilisation
FR2661362A1 (fr) * 1990-04-25 1991-10-31 Tombini Reynald Materiau composite a base de verre concasse et de liant hydraulique ou resineux.
CN1078963A (zh) * 1992-05-21 1993-12-01 郭湘泗 用废玻璃制造无机仿花岗石技术
WO1994019294A1 (fr) * 1993-02-25 1994-09-01 Svensk Glasåtervinning Ab Procede de production de beton
WO1995026323A1 (fr) * 1994-03-29 1995-10-05 Thierry Lefebvre Materiau composite allege et insonorisant a matrice minerale hydraulique et procede d'elaboration d'un tel materiau

Non-Patent Citations (10)

* Cited by examiner, † Cited by third party
Title
DERWENT ABSTRACT, Accession No. 44866A/25, Class L02; & JP,A,53 052 535 (ASAHI GLASS KK), 13 May 1978. *
DERWENT ABSTRACT, Accession No. 76-54526x/29, Class L02; & DE,A,2 558 972 (MATSUSHITA ELEC IND KK), 8 July 1976. *
DERWENT ABSTRACT, Accession No. 77-32770y/19, Class L02; & BE,A,848 007 (BFG GLASS GROUP), 5 May 1977. *
DERWENT ABSTRACT, Accession No. 79-05125B, Class L02; & JP,A,53 140 324 (NIPPON STEEL CORP), 7 December 1978. *
DERWENT ABSTRACT, Accession No. 80-371366/21, Class L02; & JP,A,55 003 349 (SUMITOMO CEMENT KK), 11 January 1980. *
DERWENT ABSTRACT, Accession No. 97-109713/11, Class P64; & CN,A,1 078 963 (GUOX), 21 May 1992. *
PATENT ABSTRACTS OF JAPAN, C-1021, page 83; & JP,A,04 260 644 (NKK CORP), 16 September 1992. *
PATENT ABSTRACTS OF JAPAN, C-1021, page 84; & JP,A,04 260 645 (NKK CORP), 16 September 1992. *
PATENT ABSTRACTS OF JAPAN, M-884, page 57; & JP,A,01 186 306 (TOOMEN CONSTR KK), 25 July 1989. *
See also references of EP1032544A4 *

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20010045071A (ko) * 1999-11-02 2001-06-05 정영수 콘크리트
ES2224878A1 (es) * 2003-08-22 2005-03-01 Asociacion De Investigacion De Industrias De La Construccion Aidico. Procedimiento de reciclado de residuos procedentes de lodos ceramicos como adiciones para cementos de alta resistencia.
WO2007059773A1 (fr) * 2005-11-23 2007-05-31 Petersen Lars Boerthy Utilisation de verre pulverise dans un materiau composite
US8177907B2 (en) 2005-11-23 2012-05-15 Petersen Lars Boerthy Use of pulverized glass in a composite material
WO2014188034A1 (fr) * 2013-05-20 2014-11-27 Consejo Superior De Investigaciones Científicas (Csic) Résidu de sanitaires pour l'élaboration de ciments, procédé d'obtention et ciments contenant ledit résidu
CN103637548A (zh) * 2013-12-04 2014-03-19 嘉兴良友休闲制品有限公司 水泥预制板桌面及其制作方法

Also Published As

Publication number Publication date
PL332772A1 (en) 1999-10-11
IL129446A0 (en) 2000-02-29
BR9712526A (pt) 1999-12-21
EP1032544A4 (fr) 2001-08-22
NO991749D0 (no) 1999-04-13
JP2001504792A (ja) 2001-04-10
EP1032544A1 (fr) 2000-09-06
CN1233233A (zh) 1999-10-27
AU4728997A (en) 1998-05-11
CA2268625A1 (fr) 1998-04-23
NO991749L (no) 1999-06-03

Similar Documents

Publication Publication Date Title
Pahlevani et al. From waste glass to building materials–An innovative sustainable solution for waste glass
Li et al. Feasibility of glass/basalt fiber reinforced seawater coral sand mortar for 3D printing
US6488762B1 (en) Composition of materials for use in cellular lightweight concrete and methods thereof
Nazari et al. RETRACTED: Splitting tensile strength of concrete using ground granulated blast furnace slag and SiO2 nanoparticles as binder
EP1368283B1 (fr) Materiau composite et article forme a conductivite thermique et a gravite specifique a la demande
US5017232A (en) Pomice containing composition
CN114477895A (zh) 一种仿天然大理石纹理的无机人造石及其制备工艺
WO1998016483A1 (fr) Compositions pour beton et produits en beton fabriques a partir de telles compositions
KR102240724B1 (ko) 시멘트 함량을 저감시킨 무수축 내열 그라우트재.
JP2009073677A (ja) 非焼成タイル
CN110590286A (zh) 一种水泥基环保型无机高强度人造石及其制备方法
US5228914A (en) Pumice containing composition
US5292366A (en) Pumice containing composition
Martauz et al. The properties of concrete based on steel slag as a by-product of metallurgical production
JPH11246253A (ja) 軽量コンクリート
MXPA99003531A (en) Compositions for use in concrete and concrete products obtained therefrom
JPH04119957A (ja) 高強度コンクリート
US2278455A (en) Fire resistant composition
CN112723854A (zh) 一种多矿物废料复合掺合料制备方法
JP2003063850A (ja) 無機質成形体および該無機質成形体の製造方法
CN111410490A (zh) 一种用于水泥基工艺制品的彩色超细灌浆料
RU2197450C1 (ru) Способ получения пористого огнеупорного материала
KR20010033574A (ko) 콘크리트에 사용하기 위한 조성물 및 이것으로부터 수득된콘크리트 제품
JPH07126058A (ja) 高強度耐熱性コンクリート
RU2209795C2 (ru) Сырьевая смесь для изготовления керамических изделий, преимущественно кирпича

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 97198752.1

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AT AU AZ BA BB BG BR BY CA CH CN CU CZ CZ DE DE DK DK EE EE ES FI FI GB GE GH HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SK SL TJ TM TR TT UA UG US UZ VN YU ZW AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH KE LS MW SD SZ UG ZW AT BE CH DE DK ES FI

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
ENP Entry into the national phase

Ref document number: 2268625

Country of ref document: CA

Ref document number: 2268625

Country of ref document: CA

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: PA/a/1999/003531

Country of ref document: MX

ENP Entry into the national phase

Ref document number: 1998 518228

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 1019997003325

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 09284575

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 1997909762

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1997909762

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1019997003325

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1997909762

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1019997003325

Country of ref document: KR