WO1997045206A1 - Materiau absorbant pour chaussure - Google Patents
Materiau absorbant pour chaussure Download PDFInfo
- Publication number
- WO1997045206A1 WO1997045206A1 PCT/US1997/010216 US9710216W WO9745206A1 WO 1997045206 A1 WO1997045206 A1 WO 1997045206A1 US 9710216 W US9710216 W US 9710216W WO 9745206 A1 WO9745206 A1 WO 9745206A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- foam
- polyol
- polyurethane foam
- polymer
- hydrophilic
- Prior art date
Abstract
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP09543093A JP2000511952A (ja) | 1996-05-30 | 1997-05-30 | 吸収性靴用材料 |
EP97928026A EP0902730A1 (fr) | 1996-05-30 | 1997-05-30 | Materiau absorbant pour chaussure |
AU32343/97A AU3234397A (en) | 1996-05-30 | 1997-05-30 | Absorbent footwear material |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US1889896P | 1996-05-30 | 1996-05-30 | |
US60/018,898 | 1996-05-30 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1997045206A1 true WO1997045206A1 (fr) | 1997-12-04 |
Family
ID=21790326
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US1997/010216 WO1997045206A1 (fr) | 1996-05-30 | 1997-05-30 | Materiau absorbant pour chaussure |
Country Status (5)
Country | Link |
---|---|
EP (1) | EP0902730A1 (fr) |
JP (1) | JP2000511952A (fr) |
AU (1) | AU3234397A (fr) |
CA (1) | CA2257170A1 (fr) |
WO (1) | WO1997045206A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2004500224A (ja) * | 2000-04-17 | 2004-01-08 | プロ−システムズ・プロプライエタリー・リミテッド | 湿度感受性組成物 |
WO2013056401A1 (fr) * | 2011-10-21 | 2013-04-25 | Bayer Materialscience Ag | Procédé pour la production de textiles enduits |
CN109096464A (zh) * | 2018-07-05 | 2018-12-28 | 山东诺威聚氨酯股份有限公司 | 透气鞋垫及其制备方法 |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5281437A (en) * | 1989-12-06 | 1994-01-25 | Purification Products Limited | Production of particulate solid-bearing low density air-permeable sheet materials |
-
1997
- 1997-05-30 JP JP09543093A patent/JP2000511952A/ja active Pending
- 1997-05-30 EP EP97928026A patent/EP0902730A1/fr not_active Withdrawn
- 1997-05-30 CA CA 2257170 patent/CA2257170A1/fr not_active Abandoned
- 1997-05-30 WO PCT/US1997/010216 patent/WO1997045206A1/fr not_active Application Discontinuation
- 1997-05-30 AU AU32343/97A patent/AU3234397A/en not_active Abandoned
Patent Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5281437A (en) * | 1989-12-06 | 1994-01-25 | Purification Products Limited | Production of particulate solid-bearing low density air-permeable sheet materials |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2004500224A (ja) * | 2000-04-17 | 2004-01-08 | プロ−システムズ・プロプライエタリー・リミテッド | 湿度感受性組成物 |
JP4869534B2 (ja) * | 2000-04-17 | 2012-02-08 | ブイエム3・インターナショナル・プロプライエタリー・リミテッド | 湿度感受性組成物 |
WO2013056401A1 (fr) * | 2011-10-21 | 2013-04-25 | Bayer Materialscience Ag | Procédé pour la production de textiles enduits |
CN109096464A (zh) * | 2018-07-05 | 2018-12-28 | 山东诺威聚氨酯股份有限公司 | 透气鞋垫及其制备方法 |
CN109096464B (zh) * | 2018-07-05 | 2020-12-18 | 山东一诺威聚氨酯股份有限公司 | 透气鞋垫及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
CA2257170A1 (fr) | 1997-12-04 |
EP0902730A1 (fr) | 1999-03-24 |
AU3234397A (en) | 1998-01-05 |
JP2000511952A (ja) | 2000-09-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1124461B1 (fr) | Semelle interieure auto-formable | |
US3793241A (en) | Dimensionally stable hydrophilic foam and method of preparing same | |
EP0906184B1 (fr) | Materiau composite servant a absorber et a dissiper les liquides corporels et l'humidite | |
US4674204A (en) | Shock absorbing innersole and method for preparing same | |
US4910886A (en) | Shock-absorbing innersole | |
CN112334034B (zh) | 用于压缩模制泡沫物品的方法 | |
EP0425270A2 (fr) | Structure composite polymère superabsorbante | |
US5002047A (en) | Orthotic pads and methods | |
US3839138A (en) | Dimensionally stable hydrophilic foam and method of preparing same | |
EP2393524B1 (fr) | Matériaux de pansement pour plaie en mousse absorbante | |
CN1723312A (zh) | 将聚氨酯分散液基泡沫应用到制品的方法 | |
JP2004230171A (ja) | 臭気及び湿気吸収性パッドを有する靴及びそれを提供する方法 | |
TWI802219B (zh) | 熱塑性聚胺酯泡沫體及包含其的抗衝擊複合層 | |
EP0902730A1 (fr) | Materiau absorbant pour chaussure | |
US20040078016A1 (en) | Absorbent article with gravity resistant acquisition layer | |
US6537934B1 (en) | Adhesive compositions and composite materials | |
CN1224372A (zh) | 吸收性制鞋材料 | |
JP4163682B2 (ja) | 水分蒸散複合材料およびその製品 | |
JPH07114800B2 (ja) | 積層化被覆材料 | |
WO2024195949A1 (fr) | Composition de mousse polyuréthane contenant une poudre tpu et procédé de fabrication d'une semelle intérieure de chaussure l'utilisant | |
JPS62227354A (ja) | 親水性吸収性平面状材及びその製法 | |
AU749640B2 (en) | Sponge | |
US20240317956A1 (en) | Manufacturing method of foam sheet for shoes with tpu powder and recycled pu scrap powder | |
JP2004010524A (ja) | 薬品保持材及び患部治療材 | |
MXPA01004275A (en) | Custom-formable shoe insert |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 97196062.3 Country of ref document: CN |
|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AU CA CN JP |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
ENP | Entry into the national phase |
Ref document number: 2257170 Country of ref document: CA Ref document number: 2257170 Country of ref document: CA Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1997928026 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 1997928026 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1997928026 Country of ref document: EP |