WO1996041911A1 - Textiles tisses et tricotes ignifuges a action desodorisante, et leur procede de fabrication - Google Patents
Textiles tisses et tricotes ignifuges a action desodorisante, et leur procede de fabrication Download PDFInfo
- Publication number
- WO1996041911A1 WO1996041911A1 PCT/JP1996/001603 JP9601603W WO9641911A1 WO 1996041911 A1 WO1996041911 A1 WO 1996041911A1 JP 9601603 W JP9601603 W JP 9601603W WO 9641911 A1 WO9641911 A1 WO 9641911A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- knitted fabric
- fiber
- woven
- mol
- knitted
- Prior art date
Abstract
L'invention se rapporte à des textiles ignifuges tissés ou tricotés auxquels on confère des propriétés désodorisantes sans diminuer leur résistance au feu. On obtient ce résultat en appliquant une composition désodorisante qui comprend un silicate d'aluminium constitué, en pourcentage, de 5 à 80 moles de SiO2, de 5 à 65 moles de MOn/2 (où M est au moins un métal choisi parmi: zinc, cuivre, argent, cobalt, nickel, fer, titane, baryum, étain et zirconium; et n est la valence du métal) ainsi que de 1 à 60 moles de Al2O3, et un liant, sur la surface d'un textile tissé ou tricoté fabriqué en fibres modacryliques, d'un fil jaspé tissé ou tricoté ou d'un tissu métisse à base de fibres modacryliques et cellulosiques, ou encore d'un fil jaspé ou d'un tissu métisse tissé ou tricoté en fibres modacryliques et en fibres de polyester ou autres, selon un poids au revêtement de 1 g/m2 ou plus en ce qui concerne le silicate d'aluminium.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP7/145913 | 1995-06-13 | ||
JP7145913A JPH08337964A (ja) | 1995-06-13 | 1995-06-13 | 消臭機能を有する防炎性編織物及びその製造法 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1996041911A1 true WO1996041911A1 (fr) | 1996-12-27 |
Family
ID=15395979
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP1996/001603 WO1996041911A1 (fr) | 1995-06-13 | 1996-06-12 | Textiles tisses et tricotes ignifuges a action desodorisante, et leur procede de fabrication |
Country Status (2)
Country | Link |
---|---|
JP (1) | JPH08337964A (fr) |
WO (1) | WO1996041911A1 (fr) |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0340878A (ja) * | 1989-07-04 | 1991-02-21 | Jinichi Kishi | 防臭呼吸機能性繊維構造物、およびその製造法 |
JPH03213562A (ja) * | 1990-01-12 | 1991-09-18 | Mitsubishi Rayon Co Ltd | 消臭繊維及びその製法 |
JPH05156510A (ja) * | 1991-11-29 | 1993-06-22 | Sumitomo Cement Co Ltd | 繊維及び繊維製品の加工方法及び繊維及び繊維製品 |
JPH06313213A (ja) * | 1993-04-29 | 1994-11-08 | Bergmann Gmbh & Co Kg | ポリエステルを主成分とする単繊維のかつらと代用毛髪及びそれらの製造方法 |
-
1995
- 1995-06-13 JP JP7145913A patent/JPH08337964A/ja active Pending
-
1996
- 1996-06-12 WO PCT/JP1996/001603 patent/WO1996041911A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0340878A (ja) * | 1989-07-04 | 1991-02-21 | Jinichi Kishi | 防臭呼吸機能性繊維構造物、およびその製造法 |
JPH03213562A (ja) * | 1990-01-12 | 1991-09-18 | Mitsubishi Rayon Co Ltd | 消臭繊維及びその製法 |
JPH05156510A (ja) * | 1991-11-29 | 1993-06-22 | Sumitomo Cement Co Ltd | 繊維及び繊維製品の加工方法及び繊維及び繊維製品 |
JPH06313213A (ja) * | 1993-04-29 | 1994-11-08 | Bergmann Gmbh & Co Kg | ポリエステルを主成分とする単繊維のかつらと代用毛髪及びそれらの製造方法 |
Also Published As
Publication number | Publication date |
---|---|
JPH08337964A (ja) | 1996-12-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP4094052B2 (ja) | 防炎性レーヨン繊維及びその製造方法 | |
JP3369380B2 (ja) | 改善された高吸放湿性繊維及びその製造方法 | |
JP6484554B2 (ja) | 難燃性布帛、その製造方法、及びそれを含む防火服 | |
JP3720336B2 (ja) | 消臭材及びその製造方法 | |
US4072784A (en) | Fixation of multivalent metal salts of carboxyl-containing vinyl monomers on fibrous substrates | |
JP6640606B2 (ja) | 不織布 | |
WO1996041911A1 (fr) | Textiles tisses et tricotes ignifuges a action desodorisante, et leur procede de fabrication | |
JP5051544B2 (ja) | アミノ基含有繊維およびその製造方法ならびに該繊維を含む繊維構造物 | |
JP6629638B2 (ja) | 不織布シート | |
US2570566A (en) | Textile treating solutions and compositions containing same | |
JP2005076145A (ja) | 消臭機能を有する織物製品及び織物製品の消臭加工方法 | |
TW202140374A (zh) | 磷酸鋯粒子及使用其之鹼性氣體除臭劑和彼等之製造方法 | |
JP2665807B2 (ja) | 消臭・抗菌性繊維及び製造方法 | |
JPH09176917A (ja) | 消臭・抗菌性アクリル系合成繊維及びその製造方法 | |
JPH03121145A (ja) | イオン交換機能を持ったセルロース系組成物 | |
JP7190830B2 (ja) | 消臭性布帛および衣料 | |
JPH09157978A (ja) | 消臭・抗菌性アクリル系合成繊維からなる繊維製品 | |
JP2018057837A (ja) | 消臭フィルター及びその製造方法 | |
JPH08158201A (ja) | 耐光性に優れた難燃性布帛 | |
JPS6039789B2 (ja) | 不燃性シ−ト | |
JP3235092B2 (ja) | 塩基性ガス吸収繊維及びその製造方法 | |
JP2018150631A (ja) | 機能性繊維物、機能性繊維物の製造方法、及び、機能剤 | |
JP3712310B2 (ja) | 抗菌性を有する高分子成形物 | |
JP4877685B2 (ja) | 染色された消臭性セルロース系布帛類の製造方法 | |
JP3868558B2 (ja) | 光触媒含有シート |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): US |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
122 | Ep: pct application non-entry in european phase |