WO1993008142A1 - Verfahren zur herstellung von fugenschaum - Google Patents
Verfahren zur herstellung von fugenschaum Download PDFInfo
- Publication number
- WO1993008142A1 WO1993008142A1 PCT/EP1992/002393 EP9202393W WO9308142A1 WO 1993008142 A1 WO1993008142 A1 WO 1993008142A1 EP 9202393 W EP9202393 W EP 9202393W WO 9308142 A1 WO9308142 A1 WO 9308142A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water
- weight
- mixture
- prepolymers
- foam
- Prior art date
Abstract
Description
Claims