WO1991020078A1 - Procede de stockage optique de donnees - Google Patents

Procede de stockage optique de donnees Download PDF

Info

Publication number
WO1991020078A1
WO1991020078A1 PCT/EP1991/000912 EP9100912W WO9120078A1 WO 1991020078 A1 WO1991020078 A1 WO 1991020078A1 EP 9100912 W EP9100912 W EP 9100912W WO 9120078 A1 WO9120078 A1 WO 9120078A1
Authority
WO
WIPO (PCT)
Prior art keywords
chromophore
matrix
storage
spectral holes
dyes
Prior art date
Application number
PCT/EP1991/000912
Other languages
German (de)
English (en)
Inventor
Christoph BRÄUCHLE
Thomas BASCHÉ
Bernd Sauter
Moritz Ehrl
Original Assignee
Basf Aktiengesellschaft
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Aktiengesellschaft filed Critical Basf Aktiengesellschaft
Priority to JP91509261A priority Critical patent/JPH05507807A/ja
Publication of WO1991020078A1 publication Critical patent/WO1991020078A1/fr
Priority to KR1019920703288A priority patent/KR930701807A/ko

Abstract

Un procédé permet de stocker optiquement des données dans un matériau qui contient un support et une couche de stockage composée d'une matrice et d'un chromophore. Dans la couche de stockage, des trous spectraux sont générés dans les bandes d'absorption du chromophore par de la lumière ayant des fréquences diverses. A cet effet, on utilise une matrice microporeuse ou ayant une structure en cage ou stratifiée, le chromophore étant adsorbé à la surface de la matrice. Les trous spectraux sont produits dans les bandes d'absorption du chromophore à une température égale ou supérieure à 50 K.
PCT/EP1991/000912 1990-06-19 1991-05-13 Procede de stockage optique de donnees WO1991020078A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP91509261A JPH05507807A (ja) 1990-06-19 1991-05-13 光学的データ記憶法
KR1019920703288A KR930701807A (ko) 1990-06-19 1992-12-21 광 데이타 스토리지

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DEP4019544.9 1990-06-19
DE4019544 1990-06-19

Publications (1)

Publication Number Publication Date
WO1991020078A1 true WO1991020078A1 (fr) 1991-12-26

Family

ID=6408677

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1991/000912 WO1991020078A1 (fr) 1990-06-19 1991-05-13 Procede de stockage optique de donnees

Country Status (4)

Country Link
EP (1) EP0535009A1 (fr)
JP (1) JPH05507807A (fr)
KR (1) KR930701807A (fr)
WO (1) WO1991020078A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1218972A1 (fr) * 1999-05-17 2002-07-03 New Mexico State University Technology Transfer Corporation Amelioration optique au moyen de nanoparticules et de microcavites
WO2002093579A1 (fr) * 2001-05-14 2002-11-21 Swinburne University Of Technology Memoire de donnees optique non effaçable
US7123359B2 (en) 1999-05-17 2006-10-17 Arrowhead Center, Inc. Optical devices and methods employing nanoparticles, microcavities, and semicontinuous metal films

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4101976A (en) * 1977-02-14 1978-07-18 International Business Machines Corporation Frequency selective optical data storage system
EP0352068A2 (fr) * 1988-07-18 1990-01-17 Hitachi Maxell Ltd. Médium d'enregistrement optique
EP0362901A2 (fr) * 1982-05-25 1990-04-11 Unisys Corporation Milieu optique pour l'enregistrement de données numériques

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4101976A (en) * 1977-02-14 1978-07-18 International Business Machines Corporation Frequency selective optical data storage system
EP0362901A2 (fr) * 1982-05-25 1990-04-11 Unisys Corporation Milieu optique pour l'enregistrement de données numériques
EP0352068A2 (fr) * 1988-07-18 1990-01-17 Hitachi Maxell Ltd. Médium d'enregistrement optique

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1218972A1 (fr) * 1999-05-17 2002-07-03 New Mexico State University Technology Transfer Corporation Amelioration optique au moyen de nanoparticules et de microcavites
EP1218972A4 (fr) * 1999-05-17 2003-06-18 Univ New Mexico State Tech Tra Amelioration optique au moyen de nanoparticules et de microcavites
US7123359B2 (en) 1999-05-17 2006-10-17 Arrowhead Center, Inc. Optical devices and methods employing nanoparticles, microcavities, and semicontinuous metal films
WO2002093579A1 (fr) * 2001-05-14 2002-11-21 Swinburne University Of Technology Memoire de donnees optique non effaçable

Also Published As

Publication number Publication date
KR930701807A (ko) 1993-06-12
JPH05507807A (ja) 1993-11-04
EP0535009A1 (fr) 1993-04-07

Similar Documents

Publication Publication Date Title
DE69725607T2 (de) Polymethin-komplex-farbstoffe und ihre verwendung
Schulz-Ekloff et al. Chromophores in porous silicas and minerals: preparation and optical properties
DE3689891T2 (de) Optische Aufzeichnungsmedien mit hoher Dichte, Verfahren zu deren Herstellung und Verfahren um optische Informationen in diesem Medium aufzuzeichnen.
DE69533750T2 (de) Film der einen orientierten farbstoff enthält, herstellungsverfahren desselben, polarisator und flüssigkristallanzeigevorrichtung unter verwendung desselben
DE4126461A1 (de) Farbstoffbeladenes anorganisches molekularsieb, verfahren zu seiner herstellung und seine verwendung als pigment oder material fuer die optische datenspeicherung
DE2828510A1 (de) Verfahren zum herstellen eines mit einem laseraktiven farbstoff impraegnierten kunststoffkoerpers
DE10325459A1 (de) Räumlich hochaufgelöstes Erzeugen einer dauerhaften Struktur
DE69920699T2 (de) Aminiumsalz- oder diimoniumsalz-verbindungen und ihre anwendung
EP1616216B1 (fr) Imagerie spatiale a haute resolution
EP0192215A1 (fr) Complexes de tétraphényldithiolène, benzoines substituées asymétriquement ainsi que matériaux d'enregistrement optiques contenant ces complexes
DE60026679T2 (de) Informationsaufzeichnungsverfahren
EP0655162B1 (fr) Compositions de variantes de bacteriorhodopsine a longevite d'enregistrement accrue et leur utilisation
DE19639675A1 (de) Neue Fullerenverbindung, deren Herstellung und Verwendung
DE60125814T2 (de) Farbstoff beladene zeolithe
EP0241696A2 (fr) Colorants naphtolactames et support d'enregistrement optique les contenant
EP0532029B1 (fr) Compositions de membrane pourpre avec une efficacité d'effraction holographique augmentée
DE69030828T2 (de) Optische Speichermedien
WO1991020078A1 (fr) Procede de stockage optique de donnees
DE2160149A1 (de) Photochromische Einrichtung und Ver fahren zu deren Betneb
WO2004090950A2 (fr) Production haute resolution spatiale d'une structure durable
DE69227475T2 (de) Optisches Aufzeichnungsmedium und Verfahren unter Verwendung desselben
EP0291848A2 (fr) Milieu d'enregistrement optique, comprenant une couche réfléchissante contenant un dérivé de silicium-phtalocyanine
DE3875877T2 (de) Phthalocyaninverbindungen und ihre verwendung.
EP0403971A2 (fr) Méthode de fabrication d'éléments optiques
DE69226740T2 (de) Verfahren zur Änderung optischer Eigenschaften, optische Geräte, Informationsaufzeichnungsmedien und Informationsaufzeichnungsverfahren und Gerät

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): JP KR US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IT LU NL SE

WWE Wipo information: entry into national phase

Ref document number: 1991910104

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1991910104

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1991910104

Country of ref document: EP