WO1991009163A1 - Fibres de viscose modifiees et procede de fabrication de telles fibres - Google Patents

Fibres de viscose modifiees et procede de fabrication de telles fibres Download PDF

Info

Publication number
WO1991009163A1
WO1991009163A1 PCT/FI1990/000292 FI9000292W WO9109163A1 WO 1991009163 A1 WO1991009163 A1 WO 1991009163A1 FI 9000292 W FI9000292 W FI 9000292W WO 9109163 A1 WO9109163 A1 WO 9109163A1
Authority
WO
WIPO (PCT)
Prior art keywords
viscose
modified
chitosan
fibres
viscose fibres
Prior art date
Application number
PCT/FI1990/000292
Other languages
English (en)
Inventor
Pertti Nousiainen
Henryk Struszczyk
Original Assignee
Kemira Oy Säteri
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kemira Oy Säteri filed Critical Kemira Oy Säteri
Publication of WO1991009163A1 publication Critical patent/WO1991009163A1/fr

Abstract

L'invention se rapporte à des fibres de viscose modifiées qui contiennent de la cellulose de viscose et qui comportent dans leur structure du chitosane microcristallin formant après filage essentiellement des liaisons d'hydrogène avec la cellulose régénérée des fibres de viscose. Le chitosane microcristallin contient des ions métalliques chélatés qui modifient et améliorent les propriétés des fibres de viscose.
PCT/FI1990/000292 1989-12-08 1990-12-07 Fibres de viscose modifiees et procede de fabrication de telles fibres WO1991009163A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FI895893A FI895893A (fi) 1989-12-08 1989-12-08 Modifierade viskosfibrer och foerfarande foer deras framstaellning.
FI895893 1989-12-08

Publications (1)

Publication Number Publication Date
WO1991009163A1 true WO1991009163A1 (fr) 1991-06-27

Family

ID=8529487

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/FI1990/000292 WO1991009163A1 (fr) 1989-12-08 1990-12-07 Fibres de viscose modifiees et procede de fabrication de telles fibres

Country Status (3)

Country Link
AU (1) AU6888591A (fr)
FI (1) FI895893A (fr)
WO (1) WO1991009163A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1994009192A1 (fr) * 1992-09-30 1994-04-28 Novasso Oy Fibres de viscose modifiees et leur procede de production
US5541233A (en) * 1992-12-01 1996-07-30 Minnesota Mining And Manufacturing Company Durable anti-microbial agent
WO2003057735A1 (fr) * 2002-01-09 2003-07-17 Abbott Laboratories De Costa Rica Ltd. Complexe chitosane-calcium et son procede de production
WO2003057736A1 (fr) * 2002-01-09 2003-07-17 Abbott Laboratories De Costa Rica Ltd Procedes de production de chitosane microcristalline modifiee et leurs utilisations
US8524326B2 (en) 2008-01-22 2013-09-03 Lenzing Aktiengesellschaft Process for the treatment of cellulosic molded bodies
US9547011B2 (en) 2013-03-14 2017-01-17 Tricol Biomedical, Inc. Biocompatible and bioabsorbable derivatized chitosan compositions
CN110106579A (zh) * 2019-05-11 2019-08-09 唐卫兵 一种含mof的抗菌纤维及其制备方法

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111088550B (zh) * 2019-12-19 2022-08-16 潮州市雅达绣衣有限公司 一种防静电涤纶面料的制备及其染色方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1988001316A1 (fr) * 1986-08-18 1988-02-25 Firextra Oy Produits fibreux modifies et procede de fabrication
FI78127B (fi) * 1986-08-18 1989-02-28 Valtion Teknillinen Modifierade viskosfibrer och foerfarande foer deras framstaellning.
FI78126B (fi) * 1986-08-18 1989-02-28 Valtion Teknillinen Foerfarande foer tillverkning av fibrer av kitosanviskos.

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1988001316A1 (fr) * 1986-08-18 1988-02-25 Firextra Oy Produits fibreux modifies et procede de fabrication
FI78127B (fi) * 1986-08-18 1989-02-28 Valtion Teknillinen Modifierade viskosfibrer och foerfarande foer deras framstaellning.
FI78126B (fi) * 1986-08-18 1989-02-28 Valtion Teknillinen Foerfarande foer tillverkning av fibrer av kitosanviskos.

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
CHEMICAL ABSTRACTS, Volume 102, No. 2, 14 January 1985, (Columbus, Ohio, US), see page 367, Abstract 12433f; & JP,A,59 116 418, (Fuji Spinning Co., Ltd.), 1984. *
CHEMICAL ABSTRACTS, Volume 102, No. 23, 10 June 1985, (Columbus, Ohio, US), OGAWA , KOZO et al.: "X-Ray Diffraction Study on Chitosan-Metal Complexes", see page 625, Abstract 204210c; & CHITIN, CHITOSAN, RELAT. EXZYMES, 1984, 327-345. *

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1994009192A1 (fr) * 1992-09-30 1994-04-28 Novasso Oy Fibres de viscose modifiees et leur procede de production
US5622666A (en) * 1992-09-30 1997-04-22 Novasso Oy Modified viscose fibres and method for their manufacture
US5541233A (en) * 1992-12-01 1996-07-30 Minnesota Mining And Manufacturing Company Durable anti-microbial agent
US5643971A (en) * 1992-12-01 1997-07-01 Minnesota Mining And Manufacturing Company Durable anti-microbial agents
US5821271A (en) * 1992-12-01 1998-10-13 Minnesota Mining And Manufacturing Company Water absorbing porous articles
WO2003057736A1 (fr) * 2002-01-09 2003-07-17 Abbott Laboratories De Costa Rica Ltd Procedes de production de chitosane microcristalline modifiee et leurs utilisations
WO2003057735A1 (fr) * 2002-01-09 2003-07-17 Abbott Laboratories De Costa Rica Ltd. Complexe chitosane-calcium et son procede de production
US7482019B2 (en) 2002-01-09 2009-01-27 Abbott Laboratories Methods of producing modified microcrystalline chitosan and uses therefor
US8524326B2 (en) 2008-01-22 2013-09-03 Lenzing Aktiengesellschaft Process for the treatment of cellulosic molded bodies
US9547011B2 (en) 2013-03-14 2017-01-17 Tricol Biomedical, Inc. Biocompatible and bioabsorbable derivatized chitosan compositions
US9846163B2 (en) 2013-03-14 2017-12-19 Tricol Biomedical, Inc. Biocompatible and bioabsorbable derivatized chitosan compositions
US9925310B2 (en) 2013-03-14 2018-03-27 Tricol Biomedical, Inc. Biocompatible and bioabsorbable derivatized chitosan compositions
US10709817B2 (en) 2013-03-14 2020-07-14 Tricol Biomedical, Inc. Biocompatible and bioabsorbable derivatized chitosan compositions
US11229724B2 (en) 2013-03-14 2022-01-25 Tricol Biomedical, Inc. Biocompatible and bioabsorbable derivatized chitosan compositions
CN110106579A (zh) * 2019-05-11 2019-08-09 唐卫兵 一种含mof的抗菌纤维及其制备方法

Also Published As

Publication number Publication date
AU6888591A (en) 1991-07-18
FI895893A (fi) 1991-06-09
FI895893A0 (fi) 1989-12-08

Similar Documents

Publication Publication Date Title
US5622666A (en) Modified viscose fibres and method for their manufacture
JP2822174B2 (ja) キチンキトサン繊維及び構造体の製造法
Pillai et al. Chitin and chitosan polymers: Chemistry, solubility and fiber formation
CA1082382A (fr) Fibres de cellulose absorbant les fluides, contenant des sels alcalins de polymeres d'acides acryliques, d'acides methacryliques ou d'un acide sulfonique d'acryloamidoalcane, avecdes esters aliphatiques d'acides acryliques ou d'acides methacryliques
US4136697A (en) Fibers of high fluid-holding capacity
CN109252246A (zh) 一种水溶性海藻酸盐抗菌纤维及其制备方法
JPH04289211A (ja) 改質セルロース再生繊維
GB2284421A (en) Treatment of cellulose
US5897821A (en) Method for manufacturing chitosan fiber
CN114395916B (zh) 一种抗原纤化纤维素纤维及其制备方法
WO1991009163A1 (fr) Fibres de viscose modifiees et procede de fabrication de telles fibres
CN114351285A (zh) 一种奶酪蛋白纤维及其制备方法
JP2005534818A (ja) セルロース成型体の製造方法
CN1081686C (zh) 聚乙烯醇湿法交联纺丝工艺
CN112126996B (zh) 一种艾草植物抗菌抗病毒纤维及其制备方法
CN106498554A (zh) 一种含硼壳聚糖/聚乙烯醇复合纤维及其制备方法，非织造布
JPS6059123A (ja) キトサン繊維の製造方法
US3919385A (en) Process for producing high fluid-holding fiber mass
CA1082866A (fr) Fibres a matrice de cellulose regeneree contenant un polymere de n-vinyle amide
US4179416A (en) Alloy rayon fibers having dispersed therein an amide polymer and a polyacrylic acid salt
US3843378A (en) Regenerated cellulose-polyethylene glycol high fluid-holding fiber mass
CN1164807C (zh) 保健型高湿模量粘胶纤维、制造方法及用途
CN114232120B (zh) 一种抗原纤化纤维素纤维及其制备方法
KR100363448B1 (ko) 키토산 살균 필터 제조방법.
KR100496242B1 (ko) 가교 키토산섬유 및 제조방법.

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AT AU BB BG BR CA CH DE DK ES FI GB GR HU JP KP KR LK LU MC MG MW NL NO RO SD SE SU US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE BF BJ CF CG CH CM DE DK ES FR GA GB GR IT LU ML MR NL SE SN TD TG

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

NENP Non-entry into the national phase

Ref country code: CA