WO1986003694A1 - Catalyseurs d'hydrocraquage et procede utilisant des tamis moleculaires de silicoaluminophosphate - Google Patents

Catalyseurs d'hydrocraquage et procede utilisant des tamis moleculaires de silicoaluminophosphate Download PDF

Info

Publication number
WO1986003694A1
WO1986003694A1 PCT/US1985/002476 US8502476W WO8603694A1 WO 1986003694 A1 WO1986003694 A1 WO 1986003694A1 US 8502476 W US8502476 W US 8502476W WO 8603694 A1 WO8603694 A1 WO 8603694A1
Authority
WO
WIPO (PCT)
Prior art keywords
sapo
catalyst
weight
percent
group
Prior art date
Application number
PCT/US1985/002476
Other languages
English (en)
Inventor
Frank Peter Gortsema
Regis Joseph Pellet
Albert Raymond Springer
Jule Anthony Rabo
Gary Norman Long
Original Assignee
Union Carbide Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Union Carbide Corporation filed Critical Union Carbide Corporation
Publication of WO1986003694A1 publication Critical patent/WO1986003694A1/fr
Priority to FI863335A priority Critical patent/FI863335A0/fi

Abstract

Procédés d'hydrocraquage utilisant des catalyseurs comprenant des silicoaluminophosphates caractérisés dans leur forme calcinée par une adsorption d'oxygène d'au moins 4% en poids à une pression partielle de 100 torr et à une température de -186oC.
PCT/US1985/002476 1984-12-18 1985-12-17 Catalyseurs d'hydrocraquage et procede utilisant des tamis moleculaires de silicoaluminophosphate WO1986003694A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
FI863335A FI863335A0 (fi) 1984-12-18 1986-08-18 Hydrokrackningskatalysatorer och foerfaranden som utnyttjar molekylaersaoll av silikoaluminofosfat.

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US68294684A 1984-12-18 1984-12-18
US682,946 1984-12-18

Publications (1)

Publication Number Publication Date
WO1986003694A1 true WO1986003694A1 (fr) 1986-07-03

Family

ID=24741900

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1985/002476 WO1986003694A1 (fr) 1984-12-18 1985-12-17 Catalyseurs d'hydrocraquage et procede utilisant des tamis moleculaires de silicoaluminophosphate

Country Status (6)

Country Link
EP (1) EP0207133A1 (fr)
JP (1) JPS62501426A (fr)
CN (2) CN1007991B (fr)
AU (1) AU5307686A (fr)
FI (1) FI863335A0 (fr)
WO (1) WO1986003694A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4695368A (en) * 1986-07-31 1987-09-22 Union Oil Company Of California Process for producing high octane gasoline
EP0242616A1 (fr) * 1986-03-27 1987-10-28 Uop Catalyseurs et procédés de reformage ou de deshydrocyclisation
US4724066A (en) * 1985-01-22 1988-02-09 Mobil Oil Corporation Composites of microporous aluminum phosphates and zeolites and conversions over these catalysts
WO1988005070A1 (fr) * 1987-01-12 1988-07-14 Chevron Research Company Procede de fabrication de distillats moyens a l'aide d'un tamis moleculaire en silico-aluminophosphate
US5139647A (en) * 1989-08-14 1992-08-18 Chevron Research And Technology Company Process for preparing low pour middle distillates and lube oil using a catalyst containing a silicoaluminophosphate molecular sieve
DE4497286T1 (de) * 1993-09-29 1996-09-26 Boreskova Inst Kataliza Sibir Verfahren zur Verarbeitung von organischen Abfällen und Kohlenwasserstoffgemischen sekundärer Herkunft zu Motorkraftstoffen
US6710218B1 (en) 1997-10-02 2004-03-23 Casale Chemicals Sa Catalytic process for the preparation of light olefins from methanol in fluidized bed reactor
WO2011091206A3 (fr) * 2010-01-21 2012-08-09 Shell Oil Company Composition d'hydrocarbures
WO2011091203A3 (fr) * 2010-01-21 2012-08-09 Shell Oil Company Composition hydrocarbonée
WO2011091200A3 (fr) * 2010-01-21 2012-08-09 Shell Oil Company Composition hydrocarbonée
US8597498B2 (en) 2010-01-21 2013-12-03 Shell Oil Company Process for treating a hydrocarbon-containing feed
US8597499B2 (en) 2010-01-21 2013-12-03 Shell Oil Company Process for treating a hydrocarbon-containing feed
EP3888789A4 (fr) * 2018-12-13 2022-01-26 China Petroleum & Chemical Corporation Catalyseur d'hydrocraquage, son procédé de préparation et son application

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1048429C (zh) * 1994-02-05 2000-01-19 中国科学院大连化学物理研究所 以双模板剂合成磷酸硅铝分子筛的方法
CN1122637C (zh) * 2001-08-29 2003-10-01 复旦大学 一种浓胺体系合成新型磷酸铍分子筛的方法
CN100448536C (zh) * 2005-06-27 2009-01-07 中国科学院大连化学物理研究所 一种临氢异构化催化剂及其制备方法
CN101757929B (zh) * 2008-12-24 2012-01-25 中国石油化工股份有限公司 一种加氢裂化催化剂及其制备方法
CN109806907A (zh) * 2017-11-20 2019-05-28 中国石油天然气股份有限公司 负载型Pt/TiO2/ZSM-5分子筛催化剂及其制备方法与应用
CN108851966A (zh) * 2018-04-24 2018-11-23 浙江绍兴苏泊尔生活电器有限公司 一种电压力锅及烹饪方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1506429A (en) * 1975-05-13 1978-04-05 Union Carbide Corp Catalyst for hydrocarbon processes and process for preparing same
US4440871A (en) * 1982-07-26 1984-04-03 Union Carbide Corporation Crystalline silicoaluminophosphates
EP0111768A1 (fr) * 1982-12-23 1984-06-27 FIAT AUTO S.p.A. Un dispositif mécanique pour règler une soupape d'un moteur à combustion interne
EP0124119A1 (fr) * 1983-05-02 1984-11-07 Union Carbide Corporation Procédé de conversion de pétroles bruts avec composés de fragmentation contenant du carbone et de l'hydrogène sur des catalyseurs non-zéolitiques
EP0124120A1 (fr) * 1983-05-02 1984-11-07 Union Carbide Corporation Catalyseur d'hydrocraquage et procédé d'hydrocraquage

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1506429A (en) * 1975-05-13 1978-04-05 Union Carbide Corp Catalyst for hydrocarbon processes and process for preparing same
US4440871A (en) * 1982-07-26 1984-04-03 Union Carbide Corporation Crystalline silicoaluminophosphates
EP0111768A1 (fr) * 1982-12-23 1984-06-27 FIAT AUTO S.p.A. Un dispositif mécanique pour règler une soupape d'un moteur à combustion interne
EP0124119A1 (fr) * 1983-05-02 1984-11-07 Union Carbide Corporation Procédé de conversion de pétroles bruts avec composés de fragmentation contenant du carbone et de l'hydrogène sur des catalyseurs non-zéolitiques
EP0124120A1 (fr) * 1983-05-02 1984-11-07 Union Carbide Corporation Catalyseur d'hydrocraquage et procédé d'hydrocraquage

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4724066A (en) * 1985-01-22 1988-02-09 Mobil Oil Corporation Composites of microporous aluminum phosphates and zeolites and conversions over these catalysts
EP0242616A1 (fr) * 1986-03-27 1987-10-28 Uop Catalyseurs et procédés de reformage ou de deshydrocyclisation
US4695368A (en) * 1986-07-31 1987-09-22 Union Oil Company Of California Process for producing high octane gasoline
WO1988005070A1 (fr) * 1987-01-12 1988-07-14 Chevron Research Company Procede de fabrication de distillats moyens a l'aide d'un tamis moleculaire en silico-aluminophosphate
US4859312A (en) * 1987-01-12 1989-08-22 Chevron Research Company Process for making middle distillates using a silicoaluminophosphate molecular sieve
US5139647A (en) * 1989-08-14 1992-08-18 Chevron Research And Technology Company Process for preparing low pour middle distillates and lube oil using a catalyst containing a silicoaluminophosphate molecular sieve
DE4497286T1 (de) * 1993-09-29 1996-09-26 Boreskova Inst Kataliza Sibir Verfahren zur Verarbeitung von organischen Abfällen und Kohlenwasserstoffgemischen sekundärer Herkunft zu Motorkraftstoffen
US6710218B1 (en) 1997-10-02 2004-03-23 Casale Chemicals Sa Catalytic process for the preparation of light olefins from methanol in fluidized bed reactor
WO2011091206A3 (fr) * 2010-01-21 2012-08-09 Shell Oil Company Composition d'hydrocarbures
WO2011091203A3 (fr) * 2010-01-21 2012-08-09 Shell Oil Company Composition hydrocarbonée
WO2011091200A3 (fr) * 2010-01-21 2012-08-09 Shell Oil Company Composition hydrocarbonée
US8562818B2 (en) 2010-01-21 2013-10-22 Shell Oil Company Hydrocarbon composition
US8597498B2 (en) 2010-01-21 2013-12-03 Shell Oil Company Process for treating a hydrocarbon-containing feed
US8597499B2 (en) 2010-01-21 2013-12-03 Shell Oil Company Process for treating a hydrocarbon-containing feed
US8679319B2 (en) 2010-01-21 2014-03-25 Shell Oil Company Hydrocarbon composition
EP3888789A4 (fr) * 2018-12-13 2022-01-26 China Petroleum & Chemical Corporation Catalyseur d'hydrocraquage, son procédé de préparation et son application
US11779909B2 (en) 2018-12-13 2023-10-10 China Petroleum & Chemical Corporation Hydrocracking catalyst, preparation method therefor and application thereof

Also Published As

Publication number Publication date
CN85109634A (zh) 1986-06-10
FI863335A (fi) 1986-08-18
EP0207133A1 (fr) 1987-01-07
JPS62501426A (ja) 1987-06-11
CN1034679A (zh) 1989-08-16
AU5307686A (en) 1986-07-22
CN1007991B (zh) 1990-05-16
FI863335A0 (fi) 1986-08-18

Similar Documents

Publication Publication Date Title
US4960504A (en) Dewaxing catalysts and processes employing silicoaluminophosphate molecular sieves
AU599460B2 (en) Process for making middle distillates using a silicoaluminophosphate molecular sieve
EP0205578B1 (fr) Catalyseurs d'hydrocraquage et procedes utilisant des tamis moleculaires non zeolitiques
AU594659B2 (en) Dewaxing catalysts and processes employing non-zeolitic molecular sieves
WO1986003694A1 (fr) Catalyseurs d'hydrocraquage et procede utilisant des tamis moleculaires de silicoaluminophosphate
US8633128B2 (en) Lacunary Keggin type heteropolyanion based on tungsten for hydrocracking
AU640690B2 (en) Process for preparing low pour middle distillates and lube oil using a catalyst containing a silicoaluminophosphate molecular sieve
JPH03501863A (ja) 低流動点潤滑油の製造法
EP0185329B1 (fr) Catalyseurs et procédés de déparaffinage avec des tamis moléculaires silicoaluminophosphates
US4777157A (en) Hydrocracking catalyst
US4913798A (en) Hydrocracking catalyts and processes employing silicoaluminophosphate molecular sieves
EP0261769A1 (fr) Procédé de production d'essence à haut indice d'octane
JPS59216635A (ja) 炭化水素転化用結晶性触媒組成物およびその製法
US4857495A (en) Hydrocracking catalysts and processes employing silicoaluminophosphate molecular sieves
WO2006032989A1 (fr) Procede d'hydrocraquage et composition de catalyseur
JPH08501113A (ja) 中間留分の水素化分解製法
US4871445A (en) Hydrocarbon conversion
JP3045544B2 (ja) 第二段階の水素化分解のために中間細孔サイズのシリコアルミノ燐酸塩分子ふるい触媒及び水素化分解触媒の組合せを使用して中間留分を製造する方法
EP0070824B2 (fr) Catalyseur de conversion d'hydrocarbures

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU FI JP

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE FR GB IT LU NL SE

WWE Wipo information: entry into national phase

Ref document number: 1986900501

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 863335

Country of ref document: FI

WWP Wipo information: published in national office

Ref document number: 1986900501

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1986900501

Country of ref document: EP