US20240279848A1 - Undrawn multifilament, method for producing the same, multifilament, method for producing the same, staple, and method for producing the same - Google Patents

Undrawn multifilament, method for producing the same, multifilament, method for producing the same, staple, and method for producing the same Download PDF

Info

Publication number
US20240279848A1
US20240279848A1 US18/682,731 US202218682731A US2024279848A1 US 20240279848 A1 US20240279848 A1 US 20240279848A1 US 202218682731 A US202218682731 A US 202218682731A US 2024279848 A1 US2024279848 A1 US 2024279848A1
Authority
US
United States
Prior art keywords
multifilament
filaments
undrawn
individual filaments
roll unit
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US18/682,731
Other languages
English (en)
Inventor
Tsuyoshi Mihayashi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kaneka Corp
Original Assignee
Kaneka Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kaneka Corp filed Critical Kaneka Corp
Assigned to KANEKA CORPORATION reassignment KANEKA CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MIHAYASHI, TSUYOSHI
Publication of US20240279848A1 publication Critical patent/US20240279848A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/58—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolycondensation products
    • D01F6/62—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolycondensation products from polyesters
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D5/00—Formation of filaments, threads, or the like
    • D01D5/08—Melt spinning methods
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D5/00—Formation of filaments, threads, or the like
    • D01D5/08—Melt spinning methods
    • D01D5/088—Cooling filaments, threads or the like, leaving the spinnerettes
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D5/00—Formation of filaments, threads, or the like
    • D01D5/08—Melt spinning methods
    • D01D5/098—Melt spinning methods with simultaneous stretching
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D5/00—Formation of filaments, threads, or the like
    • D01D5/12—Stretch-spinning methods
    • D01D5/16—Stretch-spinning methods using rollers, or like mechanical devices, e.g. snubbing pins
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F1/00—General methods for the manufacture of artificial filaments or the like
    • D01F1/02—Addition of substances to the spinning solution or to the melt
    • D01F1/10—Other agents for modifying properties
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/58—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolycondensation products
    • D01F6/62—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolycondensation products from polyesters
    • D01F6/625—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolycondensation products from polyesters derived from hydroxy-carboxylic acids, e.g. lactones
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/88—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polycondensation products as major constituent with other polymers or low-molecular-weight compounds
    • D01F6/92—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polycondensation products as major constituent with other polymers or low-molecular-weight compounds of polyesters
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01G—PRELIMINARY TREATMENT OF FIBRES, e.g. FOR SPINNING
    • D01G1/00—Severing continuous filaments or long fibres, e.g. stapling
    • D01G1/02—Severing continuous filaments or long fibres, e.g. stapling to form staple fibres not delivered in strand form
    • D01G1/04—Severing continuous filaments or long fibres, e.g. stapling to form staple fibres not delivered in strand form by cutting
    • D—TEXTILES; PAPER
    • D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
    • D02J—FINISHING OR DRESSING OF FILAMENTS, YARNS, THREADS, CORDS, ROPES OR THE LIKE
    • D02J1/00—Modifying the structure or properties resulting from a particular structure; Modifying, retaining, or restoring the physical form or cross-sectional shape, e.g. by use of dies or squeeze rollers
    • D02J1/22—Stretching or tensioning, shrinking or relaxing, e.g. by use of overfeed and underfeed apparatus, or preventing stretch
    • D02J1/225—Mechanical characteristics of stretching apparatus
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/04—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyesters, e.g. polyethylene terephthalate [PET]

Definitions

  • the present invention relates to: an undrawn multifilament: a method for producing the undrawn multifilament: a multifilament: a method for producing the multifilament: a staple; and a method for producing the staple.
  • waste plastics have become problematic since they have caused a significant impact on the global environment, for example, by affecting ecosystems, emitting hazardous gases during combustion, or generating a huge amount of combustion heat which contributes to global warming.
  • biodegradable plastics are under active development.
  • the biodegradable plastics include those obtained using plant-derived materials. Carbon dioxide emitted upon combustion of plant-derived biodegradable plastics is that which originally existed in the air, and does not cause an increase in the amount of atmospheric carbon dioxide. This is called “carbon neutrality”. The carbon neutrality is emphasized under the Kyoto Protocol which specifies a carbon dioxide reduction goal, and the active use of carbon-neutral plastics is desired.
  • Patent Literature 1 discloses a multifilament including a plurality of individual filaments containing a 3-hydroxyalkanoate polymer.
  • Patent Literature 1 further discloses obtaining the multifilament by melt extrusion.
  • the method of Patent Literature 1 includes the steps of: (A) in melt spinning, discharging a melt using a spinning nozzle having four discharge holes to obtain a plurality of raw filaments in a molten state; and (B) cooling the plurality of raw filaments in the molten state while transferring the plurality of raw filaments to obtain an undrawn multifilament.
  • the undrawn multifilament can be stretched by means of rolls to obtain a multifilament.
  • Modified cross-section fibers containing a wholly aromatic polyamide are known, and an example of such fibers is a wholly aromatic polyamide modified cross-section fiber in which the coefficient of variation of the finenesses of individual filaments is 9.0% or less and which meets other specific requirements (see Patent Literature 2, for example).
  • a demand for a high-strength multifilament including thin individual filaments containing a poly(3-hydroxyalkanoate) could arise in the future.
  • the present inventors attempted to obtain a multifilament including thin individual filaments and having high strength using a poly(3-hydroxyalkanoate) resin.
  • the inventors prepared an undrawn multifilament including thin individual filaments and tried to stretch the undrawn multifilament at a high stretching ratio. However, the individual filaments broke during the stretching, and a multifilament was not able to be obtained.
  • a first object of the present invention is to obtain an undrawn multifilament including individual filaments containing a poly(3-hydroxyalkanoate) resin, the undrawn multifilament being easily processable into a multifilament that has high strength despite including individual filaments having finenesses whose mean is small.
  • a second object is to obtain a multifilament including individual filaments containing a poly(3-hydroxyalkanoate) resin, the multifilament having high strength despite the individual filaments having finenesses whose mean is small.
  • a third object is to obtain a staple including a cut piece of the multifilament.
  • a first aspect of the present invention relates to an undrawn multifilament including 30 or more individual filaments, wherein
  • the poly(3-hydroxyalkanoate) resin includes a poly(3-hydroxy butyrate) resin.
  • a second aspect of the present invention relates to a multifilament having been stretched, the multifilament including 30 or more individual filaments, wherein
  • a coefficient of variation of the finenesses of the individual filaments is 33% or less.
  • a third aspect of the present invention relates to a staple including a cut piece of the multifilament, the staple having a length of 20 cm or less.
  • a fourth aspect of the present invention relates to an undrawn multifilament production method for obtaining an undrawn multifilament by melt spinning, the undrawn multifilament production method including the steps of:
  • the coefficient of heat transfer is 125 W/(m 2 ⁇ K) or more.
  • a speed of the gas blown onto the 30 or more raw filaments is 0.1 m/s or more.
  • a fifth aspect of the present invention relates to a multifilament production method including:
  • the gas having a temperature of 0 to 50° C. is blown onto the 30 or more raw filaments in the molten state to cool the 30 or more raw filaments to 50° C. below and obtain the undrawn multifilament, and
  • a sixth aspect of the present invention relates to a staple production method including:
  • the present invention can provide an undrawn multifilament including individual filaments containing a poly(3-hydroxyalkanoate) resin, the undrawn multifilament being easily processable into a multifilament that has high strength despite including individual filaments having finenesses whose mean is small.
  • the present invention can further provide a multifilament including individual filaments containing a poly(3-hydroxyalkanoate) resin, the multifilament having high strength despite the individual filaments having finenesses whose mean is small.
  • the present invention can further provide a staple including a cut piece of the multifilament.
  • FIG. 1 is a schematic diagram of an apparatus used in steps (A) and (B) in a first embodiment.
  • FIG. 2 is a schematic diagram of an apparatus used in step (C) in the first embodiment.
  • FIG. 3 is a schematic diagram of an apparatus used in a second embodiment.
  • the undrawn multifilament according to the present embodiment includes 30 or more first individual filaments.
  • the first individual filaments contain a poly(3-hydroxyalkanoate) resin and a nucleating agent.
  • the mean of the finenesses of the first individual filaments is 30 dtex or less.
  • the coefficient of variation of the finenesses of the first individual filaments is 33% or less.
  • a multifilament can be obtained by stretching the undrawn multifilament according to the present embodiment.
  • a staple can be obtained by cutting the multifilament.
  • poly(3-hydroxyalkanoate) resins are difficult to subject to forming processes.
  • an undrawn multifilament including first individual filaments containing a poly (3-hydroxyalkanoate) resin it has been difficult for an undrawn multifilament including first individual filaments containing a poly (3-hydroxyalkanoate) resin to be such that the mean of the finenesses of the first individual filaments is small and the coefficient of variation of the finenesses of the first individual filaments is also small.
  • the present inventors conducted an intensive study on an undrawn multifilament including 30 or more first individual filaments containing a poly(3-hydroxyalkanoate) resin. As a result, the present inventors have succeeded in controlling the mean of the finenesses of the first individual filaments to 30 dtex or less and the coefficient of variation of the finenesses of the first individual filaments to 33% or less.
  • the present inventors conducted a further study on the undrawn multifilament including the 30 or more first individual filaments containing a poly(3-hydroxyalkanoate) resin. As a result, the present inventors have found that when the mean of the finenesses of the first individual filaments is controlled to 30 dtex or less and the coefficient of variation of the finenesses of the first individual filaments is controlled to 33% or less, the undrawn multifilament provided is easily processable into a multifilament that has high strength despite including individual filaments having finenesses whose mean is small.
  • the first individual filaments are obtained by forming a polymer composition containing a polymer component into filaments.
  • the polymer component contains a poly (3-hydroxyalkanoate) resin.
  • the polymer component may contain an additional polymer as well as the poly(3-hydroxyalkanoate) resin.
  • the polymer composition contains a nucleating agent.
  • the polymer composition may contain an additional additive as well as the nucleating agent.
  • the poly(3-hydroxyalkanoate) resin is a polyester whose monomer is a 3-hydroxyalkanoate.
  • the poly(3-hydroxyalkanoate) resin is a resin containing a 3-hydroxyalkanoate as a structural unit.
  • the poly(3-hydroxyalkanoate) resin is a biodegradable polymer.
  • biodegradability refers to the property of being degradable into low-molecular-weight compounds by microorganisms in nature. Specifically, the possession or lack of biodegradability can be determined based on any of various tests each of which is adapted for a different environment. Examples of tests adapted for aerobic conditions include ISO 14855 (compost) and ISO 14851 (activated sludge), and examples of tests adapted for anaerobic conditions include ISO 14853 (aqueous phase) and ISO 15985 (solid phase). The microbial degradability in seawater can be evaluated by measurement of biochemical oxygen demand.
  • the poly(3-hydroxyalkanoate) resin may be a homopolymer or a copolymer.
  • the poly(3-hydroxyalkanoate) resin preferably contains a structural unit represented by the following formula (1).
  • R is an alkyl group represented by C p H 2p+1 and p is an integer from 1 to 15.
  • the poly (3-hydroxyalkanoate) resin preferably includes a poly(3-hydroxybutyrate) resin.
  • the poly(3-hydroxybutyrate) resin is a resin containing 3-hydroxy butyrate as a structural unit.
  • the poly(3-hydroxybutyrate) resin may be a homopolymer or a copolymer.
  • poly(3-hydroxyalkanoate) resin containing 3-hydroxybutyrate as a structural unit examples include P3HB, P3HB3HH, P3HB3HV, P3HB4HB, poly(3-hydroxy butyrate-co-3-hydroxyoctanoate), and poly (3-hydroxy butyrate-co-3-hydroxyoctadecanoate).
  • P3HB refers to poly(3-hydroxy butyrate).
  • P3HB3HH refers to poly (3-hydroxy butyrate-co-3-hydroxyhexanoate).
  • P3HB3HV refers to poly (3-hydroxy butyrate-co-3-hydroxyvalerate).
  • P3HB4HB refers to poly (3-hydroxy butyrate-co-4-hydroxy butyrate).
  • the poly (3-hydroxyalkanoate) resin preferably includes P3HB because P3HB has the function of accelerating its own crystallization and crystallization of another poly (3-hydroxy alkanoate) resin.
  • the poly (3-hydroxyalkanoate) resin is preferably, but not limited to, P3HB, P3HB3HH, P3HB3HV, or P3HB4HB.
  • the poly (3-hydroxyalkanoate) resin is preferably P3HB3HH.
  • the poly (3-hydroxyalkanoate) resin preferably contains 85.0 to 99.5 mol %, more preferably 85.0 to 97.0 mol %, 3-hydroxy butyrate as a structural unit.
  • the multifilament according to the present embodiment has high stiffness.
  • the multifilament according to the present embodiment has high flexibility.
  • the polymer component may contain only one poly(3-hydroxyalkanoate) resin as described above or two or more such poly (3-hydroxyalkanoate) resins.
  • the poly(3-hydroxyalkanoate) resin includes a copolymer (such as P3HB3HH)
  • the poly(3-hydroxyalkanoate) resin may include two or more copolymers differing in the average proportions of structural units.
  • the weight-average molecular weight of the poly (3-hydroxyalkanoate) resin is preferably from 50,000 to 3,000,000 and more preferably from 50,000 to 1,500,000.
  • the undrawn multifilament according to the present embodiment and the multifilament can be easily formed.
  • the strength of the multifilament can be increased.
  • the weight-average molecular weight in the present embodiment refers to that determined from a polystyrene-equivalent molecular weight distribution measured by gel permeation chromatography (GPC) using a chloroform eluent.
  • GPC gel permeation chromatography
  • the column used in the GPC may be any column suitable for measurement of the molecular weight.
  • the additional polymer preferably has biodegradability.
  • additional polymer having biodegradability examples include polycaprolactone, polylactic acid, polybutylene succinate, poly butylene succinate adipate, polybutylene adipate terephthalate, polyethylene succinate, polyvinyl alcohol, polyglycolic acid, native starch, modified starch, cellulose acetate, and chitosan.
  • the polycaprolactone is a polymer resulting from ring-opening polymerization of ⁇ -caprolactone.
  • the polymer composition may contain one additional polymer or two or more additional polymers.
  • the amount of the poly (3-hydroxy alkanoate) resin contained in the polymer component is preferably 50 mass % or more, more preferably 80 mass % or more, and even more preferably 90 mass % or more.
  • the undrawn multifilament according to the present embodiment contains a biodegradable polymer, a multifilament or staple obtained from the undrawn multifilament can be easily degraded in the environment when discarded into the environment. Thus, the use of the undrawn multifilament leads to a reduced impact on the environment.
  • the polymer composition contains a nucleating agent.
  • the nucleating agent is a compound that can accelerate crystallization of the poly (3-hydroxyalkanoate) resin.
  • the nucleating agent has a higher melting point than the poly (3-hydroxyalkanoate) resin.
  • nucleating agent examples include: inorganic substances (such as boron nitride, titanium oxide, talc, layered silicates, calcium carbonate, sodium chloride, and metal phosphates): sugar alcohol compounds derived from natural sources (such as pentaerythritol, erythritol, galactitol, mannitol, and arabitol): polyvinyl alcohol: chitin: chitosan: polyethylene oxide: salts of aliphatic carboxylic acids: aliphatic alcohols: esters of aliphatic carboxylic acids; dicarboxylic acid derivatives (such as dimethyl adipate, dibutyl adipate, diisodecyl adipate, and dibutyl sebacate): cyclic compounds having in the molecule C ⁇ O and a functional group selected from NH, S, and O (such as indigo, quinacridone, and quinacridone magenta): sorbito
  • P3HB which is an example of the poly(3-hydroxyalkanoate) resin, can be used also as the nucleating agent.
  • One of the above-mentioned substances may be used alone, or two or more thereof may be used in combination.
  • sugar alcohol compounds polyvinyl alcohol, chitin, and chitosan are preferred as the nucleating agent in terms of increasing the rate of crystallization of the poly (3-hydroxyalkanoate) resin and in terms of the compatibility with and affinity for the poly (3-hydroxyalkanoate) resin.
  • pentaerythritol is preferred.
  • the nucleating agent preferably has a crystal structure at normal temperature (25° C.).
  • the nucleating agent When the nucleating agent has a crystal structure at normal temperature (25° C.), the nucleating agent has the advantage of further accelerating crystallization of the poly (3-hydroxyalkanoate) resin.
  • the nucleating agent which has a crystal structure at normal temperature (25° C.) is preferably in the form of a powder at normal temperature (25° C.).
  • the nucleating agent which is in the form of a powder at normal temperature (25° C.) preferably has an average particle size of 10 ⁇ m or less.
  • the amount of the nucleating agent contained in the polymer composition is preferably 0.05 parts by mass or more, more preferably 0.1 parts by mass or more, and even more preferably 0.5 parts by mass or more per 100 parts by mass of the poly (3-hydroxyalkanoate) resin.
  • the amount of the nucleating agent contained in the polymer composition is 0.05 parts by mass or more per 100 parts by mass of the poly (3-hydroxy alkanoate) resin, the advantage is that crystallization of the poly(3-hydroxyalkanoate) resin can be further accelerated.
  • the amount of the nucleating agent contained in the polymer composition is preferably 10 parts by mass or less, more preferably 8 parts by mass or less, and even more preferably 5 parts by mass or less per 100 parts by mass of the poly (3-hydroxyalkanoate) resin.
  • the amount of the nucleating agent contained in the polymer composition is 10 parts by mass or less per 100 parts by mass of the poly(3-hydroxyalkanoate) resin, the advantage is that during making of the undrawn multifilament from a melt of the polymer composition, the viscosity of the melt can be made low enough to easily accomplish the making of the undrawn multifilament.
  • P3HB can be used as the poly (3-hydroxyalkanoate) resin and can function as the nucleating agent.
  • the amount of P3HB is included both in the amount of the poly (3-hydroxyalkanoate) resin and in the amount of the nucleating agent.
  • the additional additive examples include a lubricant, a stabilizer (such as an antioxidant or an ultraviolet absorber), a colorant (a dye or a pigment), a plasticizer, a flame retardant, an inorganic filler, an organic filler, and an antistat.
  • the polymer composition preferably contains the lubricant.
  • the lubricity of the first individual filaments is enhanced, and fusion between the first individual filaments can be prevented.
  • Examples of the lubricant include an amide bond-containing compound.
  • the amide bond-containing compound preferably includes at least one selected from lauramide, myristamide, stearamide, behenamide, and erucamide.
  • the amount of the lubricant contained in the polymer composition is preferably 0.05 parts by mass or more, more preferably 0.1 parts by mass or more, and even more preferably 0.5 parts by mass or more per 100 parts by mass of the polymer component.
  • the advantage is that the first individual filaments have high lubricity:
  • the amount of the lubricant contained in the polymer composition is preferably 12 parts by mass or less, more preferably 10 parts by mass or less, even more preferably 8 parts by mass or less, and most preferably 5 parts by mass or less per 100 parts by mass of the polymer component.
  • the advantage is that bleed-out of the lubricant to the surface of the undrawn multifilament, the multifilament, or the staple can be prevented.
  • the plasticizer is preferably a biodegradable plasticizer in terms of improving the formability into the undrawn multifilament.
  • biodegradable plasticizer examples include polyglycerin fatty acid esters abbreviated as PGFEs (such as “Chirabasol” manufactured by Taiyo Kagaku Co., Ltd.), mixed dibasic acid esters (such as “DAIFATTY” manufactured by Daihachi Chemical Industry Co., Ltd.), and glycerin fatty acid esters (such as “RIKEMAL” manufactured by Riken Vitamin Co., Ltd.).
  • PGFEs such as “Chirabasol” manufactured by Taiyo Kagaku Co., Ltd.
  • mixed dibasic acid esters such as “DAIFATTY” manufactured by Daihachi Chemical Industry Co., Ltd.
  • glycerin fatty acid esters such as “RIKEMAL” manufactured by Riken Vitamin Co., Ltd.
  • a plasticizer which is a supercritical fluid at a temperature and pressure at which materials are heated and kneaded in the step (A) described later and which is a gas at normal temperature and pressure (25° C., 1 atmosphere).
  • plasticizer examples include nitrogen (N 2 ), carbon dioxide, and lower aliphatic hydrocarbons.
  • Examples of the lower aliphatic hydrocarbons include propane, butane, and isobutane.
  • the undrawn multifilament according to the present embodiment includes 30 or more first individual filaments, and the number of the first individual filaments is preferably from 30 to 500,000 and more preferably from 50 to 300,000.
  • the first individual filaments are, for example, circular in cross-section (the term “circular” is intended to include a true circular shape, an approximately circular shape, an elliptical shape, and an approximately elliptical shape).
  • the mean of the finenesses of the first individual filaments is 30 dtex or less.
  • the mean of the finenesses of the first individual filaments is preferably 20 dtex or less and more preferably 10 dtex or less.
  • the mean of the finenesses of the first individual filaments is preferably 1.5 dtex or more and more preferably 3.0 dtex or more.
  • the fineness of a filament refers to the thickness of the filament and is defined as the mass per unit length of the filament. Specifically, the fineness is expressed in units of mass (g) per 10,000 m (dtex).
  • the mean of the finenesses of the first individual filaments can be determined as follows.
  • the fineness of the undrawn multifilament (total fineness) is measured.
  • the number of the first individual filaments in the undrawn multifilament is also determined.
  • Mean of finenesses of first individual filaments fineness of undrawn multifilament/number of first individual filaments in undrawn multifilament
  • the coefficient of variation of the finenesses of the first individual filaments is 33% or less.
  • the coefficient of variation of the finenesses of the first individual filaments is preferably 32% or less, more preferably 30% or less, and even more preferably 28% or less.
  • the coefficient of variation of the finenesses of the first individual filaments is preferably as small as possible.
  • the coefficient of variation of the finenesses of the first individual filaments is, for example, 5% or more and in particular 10% or more.
  • the fact that the coefficient of variation of the finenesses of the first individual filaments is 33% or less means that the undrawn multifilament is less likely to include extremely thin or thick first individual filaments.
  • the low likelihood of inclusion of extremely thin filaments in the undrawn multifilament contributes to improving the stability of the bundling step (“bundling” will be described later) or the stretching step. Specifically, the ease of feed of the undrawn multifilament or the multifilament from a winding roll unit (in particular, a bobbin of the winding roll unit) is improved (the “winding roll unit” and “bobbin” will be described later: the term “bobbin” is intended to include a “paper core”). Additionally, the undrawn multifilament is resistant to breakage under stretching tension. Furthermore, the undrawn multifilament can be wound well on a stretching roll unit (the “stretching roll unit” will be described later). Moreover, the undrawn multifilament and the multifilament can be prevented from sagging during transfer.
  • the low likelihood of inclusion of extremely thick filaments in the undrawn multifilament leads to a stretching stress acting uniformly on the undrawn multifilament being stretched and to prevention of uneven stretching. As a result, the finenesses of the first individual filaments are uniformly decreased, and the mechanical properties (such as strength) of the resulting multifilament are improved.
  • the coefficient of variation of the finenesses of the first individual filaments can be determined as follows.
  • the undrawn multifilament is cut perpendicular to the length of the undrawn multifilament by means of a cutter, and the cut surface is imaged with a microscope to obtain a cross-sectional image.
  • the cross-sectional areas of all the first individual filaments constituting the undrawn multifilament are measured.
  • 30 or more of the first individual filaments in the undrawn multifilament are randomly selected, and the cross-sectional areas of the selected first individual filaments are measured. It is sometimes impractical to measure the cross-sectional areas of all the first individual filaments constituting the undrawn multifilament; in such a case, 30 or more of the first individual filaments in the undrawn multifilament may be randomly selected, and the cross-sectional areas of the selected first individual filaments may be measured.
  • the arithmetic mean and standard deviation of the measured cross-sectional areas of the first individual filaments are determined.
  • Coefficient of variation (%) of finenesses of first individual filaments (standard deviation of cross-sectional areas of first individual filaments/arithmetic mean of cross-sectional areas of first individual filaments) ⁇ 100 (%)
  • the undrawn multifilament according to the present embodiment preferably further includes a spinning oil on the surfaces of the first individual filaments.
  • spinning oil examples include a cationic surfactant, an anionic surfactant, a non-ionic surfactant, a refined esterified oil, a mineral oil, a poly(oxyethylene) alkyl ether, a silicone oil, and a paraffin wax.
  • a cationic surfactant an anionic surfactant, a non-ionic surfactant, a refined esterified oil, a mineral oil, a poly(oxyethylene) alkyl ether, a silicone oil, and a paraffin wax.
  • a cationic surfactant examples include a cationic surfactant, an anionic surfactant, a non-ionic surfactant, a refined esterified oil, a mineral oil, a poly(oxyethylene) alkyl ether, a silicone oil, and a paraffin wax.
  • One of these materials may be used alone, or two or more thereof may be used in combination.
  • a silicone oil is preferred as the spinning oil in terms of preventing fusion between the adjacent first individual filaments.
  • An anionic surfactant or a non-ionic surfactant is preferred as the spinning oil in terms of preventing the adjacent first individual filaments from moving away from each other due to static electricity.
  • the spinning oil used may be one that contains a silicone oil and an anionic surfactant (an example of such a spinning oil is “Polymax FKY” manufactured by Marubishi Yuka Kogyo Co., Ltd.).
  • the multifilament according to the present embodiment is a multifilament having been stretched.
  • the multifilament according to the present embodiment includes 30 or more second individual filaments.
  • the second individual filaments contain a poly(3-hydroxyalkanoate) resin and a nucleating agent.
  • the mean of the finenesses of the second individual filaments is 20 dtex or less.
  • the coefficient of variation of the finenesses of the second individual filaments is 33% or less.
  • the second individual filaments are obtained by forming the above-described polymer composition into filaments.
  • the number of the second individual filaments in the multifilament according to the present embodiment is 30 or more, preferably from 30 to 500,000, and more preferably from 50 to 300,000.
  • the second individual filaments are, for example, circular in cross-section (the term “circular” is intended to include a true circular shape, an approximately circular shape, an elliptical shape, and an approximately elliptical shape).
  • the mean of the finenesses of the second individual filaments is 20 dtex or less.
  • the mean of the finenesses of the second individual filaments may be chosen in the range up to 20 dtex depending on the quality required for the intended use of the multifilament or the quality required of a staple obtained from the multifilament.
  • the mean of the finenesses of the second individual filaments is preferably more than 1.0 dtex, more preferably 1.2 dtex or more, and even more preferably 1.5 dtex or more.
  • the mean of the finenesses of the second individual filaments is preferably 18 dtex or less and more preferably 16 dtex or less.
  • the mean of the finenesses of the second individual filaments can be determined as follows.
  • the fineness of the multifilament (total fineness) is measured.
  • the number of the second individual filaments in the multifilament is also determined.
  • Mean of finenesses of second individual filaments fineness of multifilament/number of second individual filaments in multifilament
  • the coefficient of variation of the finenesses of the second individual filaments is 33% or less.
  • the coefficient of variation of the finenesses of the second individual filaments is preferably 32% or less, more preferably 30% or less, and even more preferably 28% or less.
  • the coefficient of variation of the finenesses of the second individual filaments is preferably as small as possible.
  • the coefficient of variation of the finenesses of the second individual filaments is, for example, 5% or more and in particular 10% or more.
  • the coefficient of variation of the finenesses of the second individual filaments can be determined as follows.
  • the multifilament is cut perpendicular to the length of the multifilament by means of a cutter, and the cut surface is imaged with a microscope to obtain a cross-sectional image.
  • the cross-sectional areas of all the second individual filaments constituting the multifilament are measured.
  • 30 or more of the second individual filaments in the multifilament are randomly selected, and the cross-sectional areas of the selected second individual filaments are measured. It is sometimes impractical to measure the cross-sectional areas of all the second individual filaments constituting the multifilament: in such a case, 30 or more of the second individual filaments in the multifilament may be randomly selected, and the cross-sectional areas of the selected second individual filaments may be measured.
  • the arithmetic mean and standard deviation of the measured cross-sectional areas of the second individual filaments are determined.
  • Coefficient ⁇ of ⁇ variation ⁇ ( % ) ⁇ of ⁇ finenesses ⁇ of ⁇ second ⁇ individual ⁇ filaments ( standard ⁇ deviation ⁇ of ⁇ cross - sectional ⁇ areas ⁇ of ⁇ second ⁇ individual ⁇ filaments / arithmetic ⁇ mean ⁇ of ⁇ cross - sectional ⁇ areas ⁇ of ⁇ second ⁇ individual ⁇ filaments ) ⁇ 100 ⁇ ( % )
  • the mean of the tensile strengths of the second individual filaments is preferably 1.5 cN/dtex or more, more preferably 1.7 cN/dtex or more, and even more preferably 2.0 cN/dtex or more.
  • the mean of the tensile strengths of the second individual filaments is preferably as large as possible. However, the mean of the tensile strengths of the second individual filaments is, for example, 20 cN/dtex or less (in particular, 10 cN/dtex or less).
  • the mean of the tensile strengths of the second individual filaments can be determined as follows.
  • the tensile strengths of all the second individual filaments constituting the multifilament are measured.
  • 10 or more of the second individual filaments in the multifilament are randomly selected, and the tensile strengths of the selected second individual filaments are measured. It is sometimes impractical to measure the tensile strengths of all the second individual filaments constituting the multifilament: in such a case, 10 or more of the second individual filaments in the multifilament may be randomly selected, and the tensile strengths of the selected second individual filaments may be measured.
  • the arithmetic mean of the measured tensile strengths of the second individual filaments is determined as the mean of the tensile strengths of the second individual filaments.
  • the tensile strength of each second individual filament can be measured at an initial length of 20 mm and a tensile speed of 20 mm/min in accordance with JIS L 1015:2021 “Test methods for man-made staple fibres”.
  • the tensile strength of each second individual filament can be determined as follows.
  • the load (CN) at which the second individual filament breaks is measured using a tensile testing machine named Autograph AG-I (manufactured by Shimadzu Corporation) under the conditions listed below.
  • the fineness of each second individual filament is also measured.
  • the measurement of the fineness of each second individual filament can be performed using an automatic vibroscope method.
  • a staple according to the present embodiment is a staple including a cut piece of the multifilament according to the present embodiment.
  • the length (also referred to as “fiber length”) of the staple according to the present embodiment is 20 cm or less and in particular from 0.1 to 10 cm.
  • the length of the staple refers to “mean of fiber lengths” as determined by “c) Method C (replacement method)” as specified in JIS L 1015:2021 “Test methods for man-made staple fibers”, “8.4 Fiber length”, “8.4.1 Average fiber length”.
  • the staple according to the present embodiment may be a crimped yarn.
  • the staple according to the present embodiment may have crimps.
  • the length (fiber length) of the staple having crimps can be chosen as appropriate depending on the intended use of the staple and is, for example, from 1.5 to 16 cm.
  • the length (fiber length) of the staple having crimps may be from 2.0 to 11 cm or from 2.5 to 7.6 cm.
  • the crimp number of the staple is preferably from 5 to 25/25 mm, more preferably from 6 to 20/25 mm, even more preferably from 7 to 18/25 mm, and particularly preferably from 8 to 17/25 mm in terms of increasing the ease of passage through a carding machine used to obtain a non-woven fabric from such staples, improving the texture of the obtained non-woven fabric, and reducing the water absorbency of the non-woven fabric to improve the quick drying properties of the non-woven fabric.
  • the crimp number of a staple refers to the number of crimps per 25 mm of the staple.
  • the crimp number refers to the mean of the crimp numbers of 15 randomly selected staples. In the case where the number of staples is less than 15, the crimp number refers to the mean of the crimp numbers of all the staples.
  • the crimp number of each staple can be determined by counting the number of crimp peaks in 25 mm of the staple with the aid of a microscope.
  • the number of crimp peaks in the entire length of the staple may be counted with the aid of a microscope, and the number of crimps per 25 mm may be calculated from the counted number of crimp peaks.
  • An undrawn multifilament production method is a method for obtaining an undrawn multifilament by melt spinning.
  • the undrawn multifilament production method includes the steps of: (A) in the melt spinning, discharging a melt using a spinning nozzle having 30 or more discharge holes to obtain 30 or more raw filaments in a molten state; and (B) blowing a gas having a temperature of 0 to 50° C. onto the 30 or more raw filaments in the molten state to cool the 30 or more raw filaments and obtain an undrawn multifilament.
  • the melt contains a poly(3-hydroxyalkanoate) resin and a nucleating agent.
  • the mean of the finenesses of individual filaments of the undrawn multifilament is 30 dtex or less.
  • the coefficient of heat transfer between the gas and the 30 or more raw filaments in the molten state is 60 W/(m 2 ⁇ K) or more.
  • the speed of the gas blown onto the 30 or more raw filaments is preferably 0.3 m/s or more.
  • the melt is the above-described polymer composition in a molten state.
  • the undrawn multifilament production method according to the present embodiment is used to obtain the undrawn multifilament.
  • the multifilament production method includes the step of (C) stretching the undrawn multifilament by a stretching roll unit at a stretching ratio of 1.5 or more to obtain a multifilament.
  • the gas having a temperature of 0 to 50° C. is blown onto the 30 or more raw filaments in the molten state to cool the 30 or more raw filaments to 50° C. or below and obtain the undrawn multifilament, and in the step (C), the undrawn multifilament is heated, and the heated undrawn multifilament is stretched by the stretching roll unit.
  • an undrawn multifilament production method and a multifilament production method according to a first embodiment will be described with reference to FIGS. 1 and 2 .
  • the example described below is one in which an undrawn multifilament and a multifilament are produced by a sequential stretching process (also referred to as a “post-stretching process”).
  • step (A) materials of the melt are first placed into a material feeder 101 .
  • the materials fed from the material feeder 101 are kneaded under heating by a kneading extruder 102 to obtain the melt.
  • a screw extruder is suitable for use as the kneading extruder 102 .
  • the kneading extruder 102 may be a single-screw extruder or a twin-screw extruder.
  • a spinning nozzle 104 having 30 or more discharge holes is used; specifically, the melt obtained in the kneading extruder 102 is discharged from the 30 or more discharge holes to obtain 30 or more raw filaments 100 A in a molten state.
  • the flow rate of the melt discharged from the discharge holes of the spinning nozzle 104 is adjusted by a gear pump 103 .
  • the temperature of the spinning nozzle 104 is, for example, from 140 to 180° C.
  • the number of the discharge holes of the spinning nozzle 104 is 30 or more, preferably from 30 to 10000, and more preferably from 30 to 5000.
  • the shapes and sizes of the discharge holes are selected depending on the properties (such as appearance, fineness, strength, and cross-sectional shape) required of the undrawn multifilament.
  • the discharge holes are circular (the term “circular” is intended to include a true circular shape, an approximately circular shape, an elliptical shape, and an approximately elliptical shape).
  • each discharge hole is, for example, from 10 to 5000 times the cross-sectional area of a corresponding one of the first individual filaments of the undrawn multifilament.
  • all the discharge holes have substantially the same shape. Additionally, all the discharge holes have substantially the same area.
  • the area of each discharge hole is preferably from 1.0 ⁇ 10 ⁇ 3 to 20 mm 2 and more preferably from 5.0 ⁇ 10 ⁇ 3 to 10 mm 2 .
  • the speed at which the melt is discharged from the spinning nozzle 104 is preferably from 0.02 to 20 m/min, more preferably from 0.05 to 10 m/min, and even more preferably from 0.1 to 5.0 m/min.
  • the spinning oil as previously described may be applied to the surfaces of the 30 or more cooled raw filaments 100 A.
  • a gas having a temperature of 0 to 50° C. is blown onto the 30 or more raw filaments obtained in a molten state in the step (A), and thus the 30 or more raw filaments are cooled to obtain an undrawn multifilament.
  • the raw filaments 100 A are cooled by a gas having a temperature of 0 to 50° C. in a first cooling box 105 .
  • the raw filament 100 A cooled in the first cooling box 105 may be further cooled by a gas having a temperature of 0 to 50° C. in a second cooling box 106 .
  • the temperature of the gas blown onto the raw filaments 100 A obtained in a molten state in the step (A) is from 0 to 50° C., preferably from 0 to 40° C., and even more preferably from 15 to 40° C.
  • the temperature of the gas When the temperature of the gas is 0° C. or above, fusion between the first individual filaments of the undrawn multifilament is prevented. Additionally, when the temperature of the gas is 0° C. or above, the mechanical properties (such as strength) of the undrawn multifilament are improved.
  • the temperature of the gas is 50° C. or below, the variation in fineness among the first individual filaments is reduced (the coefficient of variation of the finenesses of the first individual filaments can be made small). Additionally, when the temperature of the gas is 50° C. or below; breakage of any of the raw filaments 100 A can be prevented.
  • the temperature of the gas is preferably equal to or higher than the glass transition temperature of the polymer composition.
  • the temperature of the gas is equal to or higher than the glass transition temperature of the polymer composition, the polymer composition is easy to plastically deform, and the raw filaments 100 A are resistant to breakage.
  • the “temperature of the gas blown onto the raw filaments 100 A obtained in a molten state in the step (A)” refers to the temperature that the gas has when contacting the raw filaments 100 A.
  • the speed of the gas blown onto the 30 or more raw filaments is preferably 0.10 m/s or more, more preferably from 0.20 to 5.0 m/s, even more preferably from 0.20 to 3.0 m/s, still even more preferably from 0.30 to 3.0 m/s, and particularly preferably from 0.32 to 3.0 m/s.
  • the speed of the gas is 0.10 m/s or more, the cooling effect of the gas can be easily achieved.
  • the raw filaments 100 A discharged in a molten state from the spinning nozzle 104 are not much shaken by the gas. This prevents fusion between, and/or breakage of, the raw filaments 100 A in a molten state and therefore ensures high spinning stability.
  • the “speed of the gas blown onto the raw filaments 100 A obtained in a molten state in the step (A)” refers to the relative speed that the gas has relative to the raw filaments 100 A when contacting the raw filaments 100 A.
  • gas examples include air, inert gases (such as nitrogen gas and argon gas), and steam.
  • the rate of heat flow Q between a gas and a solid satisfies the following relationship with the coefficient of heat transfer h between the gas and the solid, the area of contact A between the gas and the solid, and the temperature difference ⁇ T between the gas and the solid.
  • the coefficient of heat transfer between the gas and the 30 or more raw filaments in a molten state is 60 W/(m 2 ⁇ K) or more, preferably 65 W/(m 2 ⁇ K) or more, more preferably 70 W/(m 2 ⁇ K) or more, even more preferably 125 W/(m 2 ⁇ K) or more, particularly preferably 130 W/(m 2 ⁇ K) or more, and most preferably 135 W/(m 2 ⁇ K) or more.
  • the coefficient of heat transfer between the gas and the 30 or more raw filaments in a molten state is, for example, 500 W/(m 2 ⁇ K) or less (in particular, 350 W/(m 2 ⁇ K) or less).
  • the coefficient of heat transfer can be determined from the temperature T of the gas, the speed u of the gas, and the diameter d of a cross-section of the raw filament.
  • cross-section of the raw filament refers to a cross-section perpendicular to the length of the raw filament.
  • discharge hole diameter is used as the “diameter of the cross-section of the raw filament”.
  • the area of the discharge hole is determined, then the determined area is used to calculate the diameter of the discharge hole assumed to be in the shape of a true circle, and the calculated diameter is used as the “diameter of the cross-section of the raw filament”.
  • the coefficient of heat transfer can be determined through the following procedures [1] to [5].
  • the density ⁇ , viscosity coefficient ⁇ , specific heat C p , and thermal conductivity ⁇ of the gas are determined from the temperature T of the gas.
  • the density ⁇ (kg/m 3 ) of the gas can be determined from the temperature T (K) of the gas by using the following equation.
  • the viscosity coefficient ⁇ (Pa ⁇ S) of the gas can be determined from the temperature T (K) of the gas by using the following equation.
  • the specific heat C p (J/(kg ⁇ K)) of the gas can be determined from the temperature T (K) of the gas by using the following equation.
  • the thermal conductivity ⁇ (W/(m ⁇ K)) of the gas can be determined from the temperature T (K) of the gas by using the following equation.
  • the density p, viscosity coefficient ⁇ , specific heat C p , and thermal conductivity ⁇ of the gas can be determined from the temperature T of the gas by using hitherto known equations related to the gas.
  • the Reynolds number Re is determined from the density ⁇ of the gas, the speed u of the gas, the diameter d of the cross-section of the raw filament (discharge hole diameter), and the viscosity coefficient ⁇ of the gas by using the following equation.
  • Prandtl number Pr is determined from the viscosity coefficient ⁇ , specific heat C p , and thermal conductivity ⁇ of the gas by using the following equation.
  • the Nusselt number Nu is determined from the Reynolds number Re and the Prandtl number Pr by using the following equation.
  • C and m are coefficients dependent on the Reynolds number Re.
  • the values of C and m for different Reynolds numbers Re are listed in Table 1 below.
  • the coefficient of heat transfer h is determined from the Nusselt number Nu, the diameter d of the cross-section of the raw filament (discharge hole diameter d), and the thermal conductivity ⁇ of the gas by using the following equation.
  • a preferred method for blowing the gas onto the 30 or more raw filaments in a molten state is a method in which the gas is blown onto each raw filament from at least four directions with respect to the raw filament as viewed in the direction of the length of the raw filament, namely, as viewed in a cross-section perpendicular to the length of the raw filament (this method is called “circular quenching”).
  • the gas is preferably blown onto each raw filament from eight or more directions, more preferably 16 or more directions.
  • the directions from which the gas is blown onto each raw filament preferably lie between the flow direction of the raw filament and a direction perpendicular to the flow direction of the raw filament.
  • the distance between each discharge hole of the spinning nozzle 104 and the location where the gas contacts the corresponding raw filament discharged from the discharge hole is defined depending on the properties required of the undrawn multifilament.
  • Controlling the degree of orientation and the crystallinity of the raw filaments 100 A to suitable ranges makes it possible to stably perform the step of obtaining a multifilament from the undrawn multifilament and improve the mechanical properties of the multifilament.
  • the gas having contacted the raw filaments is preferably discharged out of the cooling box along the flow direction of the raw filaments.
  • the following tools can be used to allow the gas having contacted the raw filaments to be discharged out of the cooling box along the flow direction of the raw filaments: a flow control plate, a flow control fin, an ejector, a Venturi tube, and Transvector which is manufactured by Kogi Corporation.
  • the 30 or more raw filaments 100 A cooled by the gas having a temperature of 0 to 50° C. are received on a first receiving roll unit 107 .
  • the first receiving roll unit 107 includes two rolls.
  • the first receiving roll unit 107 may include one roll or three or more rolls.
  • the 30 or more raw filaments 100 A received on the first receiving roll unit 107 are transferred by using a first transfer roll unit 108 , a second transfer roll unit 109 , a third transfer roll unit 110 , and a fourth transfer roll unit 111 , and the 30 or more raw filaments 100 A transferred by the transfer roll units 108 , 109 , 110 , and 111 are wound on a first winding roll unit 112 to obtain an undrawn multifilament.
  • the first winding roll unit 112 includes a bobbin.
  • the term “bobbin” is intended to include a paper core.
  • the bobbin may or may not include a flange.
  • the raw filaments 100 A are wound on the bobbin of the first winding roll unit 112 to obtain an undrawn multifilament.
  • Each of the transfer roll units includes two rolls in FIG. 1 .
  • Each of the transfer roll units may include one roll or three or more rolls.
  • the 30 or more raw filaments 100 A are preferably cooled to 70° C. or below, more preferably 60° C. or below, even more preferably 50° C. or below; particularly preferably 40° C. or below:
  • the 30 or more raw filaments 100 A are cooled to, for example, 0° C. or above, preferably 10° C. or above.
  • the 30 or more raw filaments 100 A are preferably cooled to a temperature equal to or higher than the glass transition temperature of the polymer composition.
  • the 30 or more raw filaments may be cooled to 70° C. or below by the blowing of the gas having a temperature of 0 to 50° C.
  • the 30 or more raw filaments 100 A may be cooled to a certain extent by the blowing of the gas having a temperature of 0 to 50° C., and then the 30 or more raw filaments 100 A may be cooled to 70° C. or below by ambient air during transfer of the 30 or more raw filaments 100 A from the first receiving roll unit 107 to the first winding roll unit 112 .
  • the 30 or more raw filaments 100 A should not be substantially stretched or should not be stretched very much in the step (B).
  • the stretching ratio in the step (B) is preferably 1.5 or less, more preferably 1.2 or less, and even more preferably 1.1 or less.
  • the stretching ratio in the step (B) can be determined by the following equation.
  • Stretching ratio in step (B) speed (m/min) of transfer roll unit/speed (m/min) of receiving roll unit used in step (B) (“first receiving roll unit 107 ” in the case of the first embodiment)
  • the “speed (m/min) of receiving roll unit used in the step (B)” refers to the length by which the 30 or more raw filaments 100 A are received on the receiving roll unit used in the step (B) (“first receiving roll unit 107 ” in the case of the first embodiment) per unit time.
  • the “speed (m/min) of transfer roll unit” refers to the length by which the 30 or more raw filaments 100 A are transferred by the transfer roll unit per unit time.
  • the highest of the speeds of the transfer roll units is used as the “speed (m/min) of transfer roll unit”.
  • Fineness ⁇ ( dtex ) ⁇ of ⁇ first ⁇ individual ⁇ filament ⁇ of ⁇ undrawn ⁇ multifilament ( ( ( a ⁇ 1000 / 60 ) / b ⁇ 10000 ) / c ) / d
  • the finenesses of the first individual filaments of the undrawn multifilament can be controlled by adjusting the parameters such as b.
  • the 30 or more raw filaments 100 A are wound on the first winding roll unit 112 .
  • the 30 or more raw filaments 100 A need not be wound on the first winding roll unit 112 but may be placed into a container to obtain the undrawn multifilament.
  • the stretching ratio in the step (B) is 1.0.
  • the undrawn multifilament 100 B is heated, and the heated undrawn multifilament 100 B is stretched by a stretching roll unit 114 .
  • the undrawn multifilament is fed from the first winding roll unit 112 and received on a second receiving roll unit 113 .
  • the undrawn multifilament 100 B received on the second receiving roll unit 113 is stretched by the stretching roll unit 114 .
  • the undrawn multifilament 100 B stretched by the stretching roll unit 114 is wound on a second winding roll unit 116 to obtain a multifilament.
  • the second winding roll unit 116 includes a bobbin.
  • the term “bobbin” is intended to include a paper core.
  • the bobbin may or may not include a flange.
  • the undrawn multifilament 100 B having been stretched is wound on the bobbin of the second winding roll unit 116 to obtain a multifilament.
  • the undrawn multifilament 100 B stretched by the stretching roll unit 114 is wound on the second winding roll unit 116 to obtain a multifilament
  • the undrawn multifilament 100 B stretched by the stretching roll unit 114 need not be wound on the second winding roll unit 116 to obtain a multifilament.
  • the undrawn multifilament 100 B stretched by the stretching roll unit 114 may be transferred by a take-off roll unit 115 .
  • the second receiving roll unit 113 includes two rolls.
  • the second receiving roll unit 113 may include one roll or three or more rolls.
  • the undrawn multifilament 100 B is preferably heated by the second receiving roll unit 113 .
  • heating the undrawn multifilament 100 B by the second receiving roll unit 113 makes it easy to control the temperature of the first individual filaments of the undrawn multifilament 100 B within a temperature range suitable for increasing the degree of orientation of the polymer component contained in the first individual filaments, thus making it easy to increase the degree of orientation of the polymer component of the first individual filaments.
  • the temperature of the second receiving roll unit 113 is preferably 15° C. or above but below 60° C. and more preferably from 20 to 55° C.
  • the undrawn multifilament 100 B need not be heated by the second receiving roll unit 113 .
  • the stretching roll unit 114 includes two rolls.
  • the stretching roll unit 114 may include one roll or three or more rolls.
  • the undrawn multifilament 100 B may or may not be heated by the stretching roll unit 114 . That is, in the first embodiment, the stretching roll unit 114 may serve as a heat treatment roll unit.
  • heating the undrawn multifilament 100 B by the stretching roll unit 114 makes it possible to accelerate crystallization of the polymer component contained in the first individual filaments of the undrawn multifilament 100 B or increase the heat resistance of the polymer component contained in the first individual filaments.
  • the temperature of the stretching roll unit (heat treatment roll unit) 114 is preferably from 30 to 100° C. and more preferably from 40 to 90° C.
  • the take-off roll unit 115 preferably serves as a heat treatment roll unit.
  • the take-off roll unit 115 (heat treatment roll unit 115 ) includes two rolls.
  • the take-off roll unit 115 (heat treatment roll unit 115 ) may include one roll or three or more rolls.
  • heating the undrawn multifilament 100 B by the heat treatment roll unit 115 makes it possible to accelerate crystallization of the polymer component contained in the first individual filaments of the undrawn multifilament 100 B or increase the heat resistance of the polymer component contained in the first individual filaments.
  • the temperature of the take-off roll unit (heat treatment roll unit) 115 is preferably from 30 to 100° C. and more preferably from 40 to 90° C.
  • Either the stretching roll unit 114 or the take-off roll unit 115 may serve as a heat treatment roll unit, or both the stretching roll unit 114 and the take-off roll unit 115 may serve as heat treatment roll units.
  • the first individual filaments are heated by the receiving roll unit 113 , the stretching roll unit 114 , and the take-off roll unit 115 .
  • the heating of the first individual filaments may be performed in any suitable manner for the purpose of controlling the degree or orientation, the crystallization, and the heat resistance of the polymer component of the first individual filaments.
  • the first individual filaments may be heated by the first winding roll unit 112 .
  • the first individual filaments may be heated by the second winding roll unit 116 to obtain a multifilament.
  • the first individual filaments may be heated by all of the series of roll units starting with the first winding roll unit 112 and ending with the second winding roll unit 116 .
  • the first individual filaments may be heated by only one or some of the series of roll units starting with the first winding roll unit 112 and ending with the second winding roll unit 116 without being heated by the other roll units.
  • the heating of the first individual filaments by the roll units is preferably controlled for each roll unit.
  • the method for heating the polymer component of the first individual filaments in the step (C) of the first embodiment may be to heat the polymer component of the first individual filaments by heating the rolls of any of the roll units.
  • any of the roll units may include a container holding the rolls and a liquid (such as water) held in the container together with the rolls, and the heating method may be to heat the polymer component of the first individual filaments by heating the liquid.
  • stretching may be performed in a bath.
  • the heating method may be to heat the polymer component of the first individual filaments by blowing a heated gas (such as air) onto or around any of the roll units.
  • a heated gas such as air
  • the heating methods mentioned above may be used in combination.
  • the stretching ratio in the step (C) is 1.5 or more and preferably 1.7 or more.
  • the stretching ratio in the step (C) is, for example, 20 or less.
  • the stretching ratio in the step (C) is 1.5 or more, the degree of orientation of the polymer component of the first individual filaments of the undrawn multifilament 100 B is further increased.
  • the stretching ratio in the step (C) can be determined by the following equation.
  • Stretching ratio in step (C) speed (m/min) of stretching roll unit/speed (m/min) of receiving roll unit used in step (C) (“second receiving roll unit 113 ” in the case of the first embodiment)
  • the relaxation rate determined by the following equation is preferably from 1 to 30% and more preferably from 1 to 15%.
  • Relaxation rate (%) ((speed of stretching roll unit 114 ⁇ speed of winding roll unit on which undrawn multifilament is wound (“second winding roll unit 116”in the case of the first embodiment)/speed of winding roll unit on which undrawn multifilament is wound) ⁇ 100
  • the “speed (m/min) of stretching roll unit” refers to the length by which the undrawn multifilament is transferred by the stretching roll unit per unit time.
  • only one stretching roll unit is used.
  • a plurality of stretching roll units may be used.
  • the highest of the speeds of the stretching roll units is used as the “speed of stretching roll unit”.
  • the “speed (m/min) of receiving roll unit used in the step (C)” refers to the length by which the undrawn multifilament is transferred by the receiving roll unit per unit time.
  • the “speed (m/min) of winding roll unit on which undrawn multifilament is wound” refers to the length by which the undrawn multifilament is wound on the winding roll unit per unit time.
  • step (C) only one undrawn multifilament may be stretched to obtain a multifilament.
  • a plurality of undrawn multifilaments may be bundled, and the plurality of bundled undrawn multifilaments may be stretched to obtain a multifilament.
  • a multifilament production method is a method for producing an undrawn multifilament and a multifilament by a spin draw process.
  • the spin draw process is a process in which the step of discharging a melt from a plurality of discharge holes to obtain a plurality of raw filaments in a molten state and the step of stretching an undrawn multifilament by a stretching roll unit are carried out in one stage.
  • the spin draw process is also called “SDY process” or “direct spin draw process”.
  • a gas having a temperature of 0 to 50° C. is blown onto the 30 or more raw filaments 100 A in a molten state to cool the 30 or more raw filament 100 A and obtain an undrawn multifilament 200 B in the step (B), and the undrawn multifilament 200 B obtained in the step (B) is received on a receiving roll unit 207 .
  • the undrawn multifilament 200 B received on the receiving roll unit 207 is stretched by three stretching roll units (a first stretching roll unit 208 , a second stretching roll unit 209 , and a third stretching roll unit 210 ).
  • the undrawn multifilament 200 B having been stretched is wound on a winding roll unit 212 to obtain a multifilament.
  • the winding roll unit 212 includes a bobbin.
  • the term “bobbin” is intended to include a paper core.
  • the bobbin may or may not include a flange.
  • the undrawn multifilament 200 B having been stretched is wound on the bobbin of the winding roll unit 212 to obtain a multifilament.
  • the undrawn multifilament 200 B stretched by the stretching roll units is wound on the winding roll unit 212 to obtain a multifilament
  • the undrawn multifilament 200 B stretched by the stretching roll units need not be wound on the winding roll unit 212 to obtain a multifilament.
  • the undrawn multifilament 200 B stretched by the stretching roll units may be transferred by a take-off roll unit 211 .
  • step (B) the 30 or more raw filaments 100 A are cooled in the first cooling box
  • the undrawn multifilament 200 B is received on the receiving roll unit 207 .
  • the 30 or more raw filaments 100 A cooled in the first cooling box 105 may be further cooled in the second cooling box 106 to obtain the undrawn multifilament 200 B.
  • the receiving roll unit 207 includes two rolls in FIG. 1 .
  • the receiving roll unit 207 may include one roll or three or more rolls.
  • each of the stretching roll units may serve as a heat treatment roll unit.
  • Each of the stretching roll units 208 , 209 , and 210 (heat treatment roll units 208 , 209 , and 210 ) includes two rolls in FIG. 1 .
  • Each of the stretching roll units 208 , 209 , and 210 (heat treatment roll units 208 , 209 , and 210 ) may include one roll or three or more rolls.
  • the temperatures of the heat treatment roll units are preferably from 30 to 100° C. and more preferably from 40 to 90° C.
  • the spinning draft ratio is preferably 50 or more and more preferably 80 or more.
  • the NDR is usually 5000 or less.
  • the NDR can be determined by the following equation.
  • NDR speed (m/min) of receiving roll unit (first receiving roll unit) that first receives filaments from spinning nozzle/spinning nozzle flow speed (m/min)
  • the degree of orientation of the polymer component contained in the first individual filaments of the undrawn multifilament 100 B or 200 B can be increased, and consequently the strength of the resulting multifilament can be further increased.
  • the “first receiving roll unit” is the first receiving roll unit 107 which receives the 30 or more raw filaments 100 A.
  • the “first receiving roll unit” is the receiving roll unit 207 that receives the undrawn multifilament 200 B.
  • the multifilament production method according to the present embodiment is used to obtain the multifilament.
  • the multifilament is cut to obtain a staple having a length of 20 cm or less.
  • a plurality of multifilaments may be bundled together, and the plurality of bundled multifilaments may be cut to obtain a staple having a length of 20 cm or less.
  • the multifilament may be subjected to crimping and then cut to obtain a staple in the form of a crimped yarn.
  • the undrawn multifilament having been stretched may be subjected to crimping to obtain a crimped multifilament before the undrawn multifilament having been stretched is wound on the winding roll unit 116 or 212 .
  • the undrawn multifilament having been stretched may be wound on the winding roll unit 116 or 212 (in particular, on the bobbin such as a paper core of the winding roll unit 116 or 212 ) to obtain a multifilament, and then the multifilament may be subjected to crimping.
  • a multifilament obtained without the use of any winding roll unit may be subjected to crimping.
  • the undrawn multifilament having been stretched may be subjected to crimping during transfer from the take-off roll unit 115 or 211 to the winding roll unit 116 or 212 .
  • the crimping is not limited to using particular means and can be performed by a known crimping method (such as a gear crimping method or a stuffing box method).
  • the staple has crimps (in particular, mechanical crimps).
  • the yarn (multifilament or undrawn multifilament having been stretched) to be subjected to the crimping may be pre-heated in a pre-heating step before the crimping.
  • the surface temperature of the yarn to be subjected to the crimping is measured, and suitable conditions are chosen in view of factors such as degree of orientation, crystallinity, strength, and heat resistance.
  • the surface temperature is typically from 40 to 140° C., preferably from 40 to 120° C., and more preferably from 50 to 120° C. When the surface temperature is 40° C. or above, mechanical properties suitable for the crimping can be achieved. When the surface temperature is 140° C. or below; draw-down can be reduced, and the process stability of the crimping is improved.
  • the pre-heating step may include a moist heat treatment or a dry heat treatment. In the moist heat treatment, for example, steam may be used. In the dry heat treatment, for example, a hot air oven or an electric heater may be used.
  • the multifilament is preferably crimped at a stuffing box pressure of 0.001 to 0.1 MPa.
  • the stuffing box pressure is more preferably from 0.001 to 0.08 MPa, even more preferably from 0.001 to 0.06 MPa, and still even more preferably from 0.001 to 0.04 MPa.
  • the present embodiment has the features as described above and thus offers the following advantages.
  • an undrawn multifilament according to the present embodiment includes 30 or more first individual filaments.
  • the first individual filaments contain a poly(3-hydroxyalkanoate) resin and a nucleating agent.
  • the mean of the finenesses of the first individual filaments is 30 dtex or less.
  • the coefficient of variation of the finenesses of the first individual filaments is 33% or less.
  • the coefficient of variation of the finenesses of the first individual filaments of the undrawn multifilament according to the present embodiment is as small as 33% or less means that the undrawn multifilament according to the present embodiment is less likely to include extremely thin second individual filaments.
  • the first individual filaments resist breaking even if the stretching ratio is increased to reduce the mean of the finenesses of the second individual filaments.
  • a multifilament according to the present embodiment is a multifilament having been stretched.
  • the multifilament according to the present embodiment includes 30 or more second individual filaments.
  • the second individual filaments contain a poly(3-hydroxyalkanoate) resin and a nucleating agent.
  • the mean of the finenesses of the second individual filaments is 20 dtex or less.
  • the coefficient of variation of the finenesses of the second individual filaments is 33% or less.
  • the fact that the coefficient of variation of the finenesses of the second individual filaments of the multifilament according to the present embodiment is 33% or less means that the coefficient of variation of the finenesses of the first individual filaments of the undrawn multifilament used to make the multifilament is small.
  • the coefficient of variation of the finenesses of the first individual filaments of the undrawn multifilament is small means that the undrawn multifilament is less likely to include extremely thin second individual filaments.
  • the individual filaments resist breaking even if the stretching ratio is increased to reduce the mean of the finenesses of the second individual filaments.
  • the multifilament according to the present embodiment is a multifilament that can have high strength despite the second individual filaments having finenesses whose mean is small.
  • An undrawn multifilament production method is a method for obtaining an undrawn multifilament by melt spinning.
  • the undrawn multifilament production method includes the steps of: (A) in the melt spinning, discharging a melt using a spinning nozzle having 30 or more discharge holes to obtain 30 or more raw filaments in a molten state; and (B) blowing a gas having a temperature of 0) to 50° C. onto the 30 or more raw filaments in the molten state to cool the 30 or more raw filaments and obtain an undrawn multifilament.
  • the melt contains a poly(3-hydroxyalkanoate) resin and a nucleating agent.
  • the mean of the finenesses of the first individual filaments of the undrawn multifilament is 30 dtex or less.
  • the coefficient of heat transfer between the gas and the 30 or more raw filaments in the molten state is 60 W/(m 2 ⁇ K) or more.
  • the step (B) where a gas having a temperature of 0) to 50° C. is blown onto the 30 or more raw filaments in a molten state to cool the 30 or more raw filaments and where the coefficient of heat transfer between the gas and the 30 or more raw filaments in the molten state is 60 W/(m 2 ⁇ K) or more, the time during which the temperature of the raw filaments is in a temperature range where the poly(3-hydroxyalkanoate) resin contained in the raw filaments crystallize can be suitably controlled to achieve desired crystallization of the poly(3-hydroxyalkanoate) resin.
  • the undrawn multifilament can have suitable stretchability. As such, when the undrawn multifilament is stretched to obtain a multifilament, the individual filaments resist breaking even if the stretching ratio is increased.
  • the raw filaments are slightly stretched due to being received on a receiving roll unit.
  • those of the raw filaments which are at inner locations such filaments are hereinafter also referred to as “inner individual filaments”
  • those of the raw filaments which are at outer locations such filaments are hereinafter also referred to as “outer individual filaments”
  • the gas having a temperature of 0) to 50° C. the gas having a temperature of 0 to 50° C.
  • the undrawn multifilament is less likely to include extremely thin first individual filaments.
  • the first individual filaments of the undrawn multifilament resist breaking even if the stretching ratio is increased.
  • an undrawn multifilament can be obtained which is easily processable into a multifilament that has high strength despite including second individual filaments having finenesses whose mean is small.
  • the undrawn multifilament production method according to the present embodiment is used to obtain the undrawn multifilament described above.
  • the multifilament production method includes the step of (C) stretching the undrawn multifilament by a stretching roll unit at a stretching ratio of 1.5 or more to obtain a multifilament.
  • the multifilament obtained can have high strength despite including second individual filaments having finenesses whose means is small.
  • a gas having a temperature of 0 to 50° C. is blown onto the 30 or more raw filaments in a molten state to cool the 30 or more raw filaments to 50° C. or below and obtain the undrawn multifilament in the step (B), followed by the step (C) in which the undrawn multifilament is heated and the heated undrawn multifilament is stretched by the stretching roll unit.
  • stretching the undrawn multifilament can increase the degree of orientation of the poly(3-hydroxyalkanoate) resin contained in the undrawn multifilament and thus can increase the strength of the resulting multifilament.
  • the undrawn multifilament is stretched in a temperature range suitable for increasing the degree of orientation of the poly (3-hydroxyalkanoate) resin. This is because, if the undrawn multifilament is stretched at a temperature above the temperature range, the poly (3-hydroxyalkanoate) resin is brought into a molten state and thus the stretching does not increase the degree of orientation of the poly (3-hydroxyalkanoate) resin very much.
  • a gas having a temperature of 0 to 50° C. is blown onto the 30 or more raw filaments in a molten state to cool the 30 or more raw filaments to 50° C. or below and obtain the undrawn multifilament in the step (B), followed by the step (C) in which the undrawn multifilament is heated and the heated undrawn multifilament is stretched by the stretching roll unit.
  • the temperature of the undrawn multifilament to be stretched is easier to control within a temperature range suitable for increasing the degree of orientation of the poly (3-hydroxyalkanoate) resin than in the case of a SDY process (spin draw process) in which the undrawn multifilament is cooled by ambient air while being stretched.
  • the degree of orientation of the poly (3-hydroxyalkanoate) resin of the undrawn multifilament can be easily increased.
  • the strength of the multifilament can be easily increased.
  • the multifilament or staple according to the present embodiment may be used in the form of a yarn.
  • the multifilament or staple according to the present embodiment may be used to make a fibrous product (fabric).
  • the fibrous product may take any of various forms (such as a non-woven fabric).
  • the multifilament, staple, and fibrous product according to the present embodiment are suitable for use in known applications.
  • the multifilament, staple, and fibrous product according to the present embodiment are suitable for use in various fields such as agricultural industry (e.g., horticulture), fishery industry, forestry industry, medical industry, and food industry.
  • agricultural industry e.g., horticulture
  • fishery industry e.g., fishery industry
  • forestry industry e.g., forestry industry
  • medical industry e.g., medical industry
  • food industry e.g., horticulture
  • fibrous product examples include clothes, curtains, carpets, bags, shoes, wiping materials, hygiene products, automobile parts, building materials, and filtration materials (filters).
  • An undrawn multifilament including 30 or more individual filaments, wherein
  • a multifilament having been stretched including 30 or more individual filaments, wherein
  • a staple including a cut piece of the multifilament according to item 3 the staple having a length of 20 cm or less.
  • An undrawn multifilament production method for obtaining an undrawn multifilament by melt spinning including the steps of:
  • a multifilament production method including:
  • a staple production method including:
  • the present invention is not limited to the above embodiment.
  • the present invention is not limited by the advantageous effects described above.
  • the present invention may be modified in various ways without departing from the gist of the present invention.
  • an undrawn multifilament according to the present invention is obtained by the production method as described above, an undrawn multifilament according to the present invention may be obtained, for example, as follows.
  • the undrawn multifilament may be obtained by selectively gathering 30 or more first individual filaments such that the mean of the finenesses of the first individual filaments is 30 dtex or less and the coefficient of variation of the finenesses of the first individual filaments is 33% or less.
  • a multifilament was made by the method of the first embodiment (sequential stretching process).
  • Poly(3-hydroxyalkanoate) resin 100 parts by mass
  • the resin was a (3-hydroxy butyrate-co-3-hydroxyhexanote) copolymer resin (P3HB3HH) (3-hydroxyhexanoate content: 6 mol %, Mw: 35 ⁇ 10 4 , melt flow rate (MFR) at 165° C., 5 kg: 12 g/10 min
  • Pentaerythritol used as nucleating agent (Neulizer P manufactured by Nippon Synthetic Chemical Industry Co., Ltd.): 1.0 parts by mass
  • Erucamide used as amide bond-containing lubricant 0.5 parts by mass
  • Behenamide used as amide bond-containing lubricant 0.5 parts by mass
  • the glass transition temperature of the pellets was 2° C.
  • the crystallization temperature of the pellets was 100° C.
  • the melting point of the pellets was 146° C.
  • the pyrolysis temperature of the pellets was 180° C.
  • the pellets were melted by the kneading extruder 102 (single-screw extruder, screw diameter: 25 mm) to obtain a melt.
  • the melt was discharged from the spinning nozzle 104 (temperature: 175° C., number of discharge holes: 368, shape of discharge holes: circular, diameter of discharge holes: 0.3 mm) to obtain 368 raw filaments 100 A.
  • the flow rate of the melt was adjusted to 5.6 kg/h by the gear pump 103 .
  • the 368 raw filaments 100 A were subjected to circular quenching in which 20° C. air was blown onto the 368 raw filaments 100 A at a speed of 0.7 m/s.
  • the coefficient of heat transfer between the air and the 368 raw filaments 100 A in a molten state was determined from the temperature of the air, the speed of the air, and the diameter of the discharge holes by the method previously described.
  • the coefficient of heat transfer was 194 W/(m 2 ⁇ K). Any gas was not blown onto the raw filaments in the cooling box 106 .
  • the 368 raw filaments 100 A cooled in the cooling boxes 105 and 106 were received on the first receiving roll unit 107 (448 m/min).
  • the 368 raw filaments 100 A were passed successively through the first transfer roll unit 108 (471 m/min), the second transfer roll unit 109 (471 m/min, 70° C.), the third transfer roll unit 110 (471 m/min), and the fourth transfer roll unit 111 (471 m/min) and then wound on the first winding roll unit (461 m/min).
  • the wound raw filaments 100 A were stored at room temperature (5 to 35° C.) for 18 hours to obtain an undrawn multifilament.
  • the undrawn multifilament was fed from the first winding roll unit 112 and received on the second receiving roll unit 113 (4.8 m/min, 30° C.).
  • the undrawn multifilament was then stretched by the stretching roll unit 114 (11.5 m/min, 25° C.), transferred by the take-off roll unit (heat treatment roll unit) 115 (10.4 m/min, 90° C.), and wound on the second winding roll unit 116 (10.4 m/min) to obtain a multifilament.
  • the stretching ratio was 2.4.
  • the second individual filaments remained unbroken. Additionally, no fusion between the second individual filaments was found.
  • the multifilament had good appearance.
  • Each of the receiving and transfer roll units used was a roll unit including two rolls rotating at the same speed and having the same temperature.
  • the multifilament obtained was used to make a staple as follows.
  • the plurality of bundled multifilaments were pre-heated with steam such that the surface temperature of the bundled multifilaments reached 65° C.
  • the pre-heated multifilaments were delivered to a stuffing box at a transfer speed of 30 m/min and were crimped at a nip pressure of 0.20 MPa and a stuffing pressure of 0.03 MPa to obtain a crimped yarn.
  • the crimped yarn was then cut by means of a tow cutter to obtain a staple having crimps and a length of 51 mm.
  • the crimp number of the staple was 14/25 mm.
  • the crimp number of the staple was 14/25 mm.
  • the undrawn multifilament was used in an attempt to obtain a multifilament in the same manner as in Example 1, except that the condition in the step (C) was changed as shown in Table 2 below. However, some of the first individual filaments broke, and a multifilament was not able to be made.
  • the mean and coefficient of variation of the finenesses of the first individual filaments of each undrawn multifilament were determined by the methods previously described.
  • the mean and coefficient of variation of the finenesses of the second individual filaments of each multifilament were determined by the methods previously described.
  • the mean of the tensile strengths of the second individual filaments of each multifilament was determined by the method previously described.
  • Step (A) Step (B) Stretchable Spinning nozzle multifilament Diameter Coeffi- Finenesses of of Air cient of first individual Shape of Number of discharge Temper- heat filaments discharge discharge holes ature Speed transfer Mean holes holes (mm) (° C.) (m/s) (W/(m 2 ⁇ K) (dtex) Ex. 1 Circular 368 0.3 20 0.70 194 5.5 Ex. 2 Circular 368 0.3 20 0.47 166 Ex. 3 Circular 368 0.3 20 0.37 152 Ex. 4 Circular 180 0.3 20 0.47 166 Ex. 5 Circular 180 0.5 20 0.47 121 Ex. 6 Circular 180 0.5 30 0.47 122 Ex. 7 Circular 180 0.5 40 0.47 122 Comp.
  • Circular 368 0.3 20 0.01 45 Comp. 2 Circular 368 0.3 20 0.01 45 Comp. 3 Circular 368 0.3 20 0.00 0 Not able to be made
  • the tensile strength of the second individual filaments of the multifilament was higher than in Comparative Examples 1 and 5 where the coefficient of variation of the finenesses of the first individual filaments of the undrawn multifilament was 38.1% or more.
  • the present invention can provide an undrawn multifilament easily processable into a multifilament that has high strength despite including individual filaments having finenesses whose mean is small.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Manufacturing & Machinery (AREA)
  • Artificial Filaments (AREA)
  • Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
US18/682,731 2021-08-18 2022-08-04 Undrawn multifilament, method for producing the same, multifilament, method for producing the same, staple, and method for producing the same Pending US20240279848A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2021133240 2021-08-18
JP2021-133240 2021-08-18
PCT/JP2022/030015 WO2023022015A1 (ja) 2021-08-18 2022-08-04 延伸用マルチフィラメント及びその製造方法、マルチフィラメント及びその製造方法、並びに、ステープル及びその製造方法

Publications (1)

Publication Number Publication Date
US20240279848A1 true US20240279848A1 (en) 2024-08-22

Family

ID=85239523

Family Applications (1)

Application Number Title Priority Date Filing Date
US18/682,731 Pending US20240279848A1 (en) 2021-08-18 2022-08-04 Undrawn multifilament, method for producing the same, multifilament, method for producing the same, staple, and method for producing the same

Country Status (4)

Country Link
US (1) US20240279848A1 (https=)
JP (1) JPWO2023022015A1 (https=)
CN (1) CN117795140A (https=)
WO (1) WO2023022015A1 (https=)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2025058065A1 (ja) * 2023-09-14 2025-03-20 旭化成株式会社 脂肪族共重合ポリエステル連続長繊維、及びその製法
WO2025105018A1 (ja) * 2023-11-14 2025-05-22 株式会社カネカ ポリ（３－ヒドロキシアルカノエート）系繊維用樹脂組成物、並びに、繊維及びその製造方法

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06264306A (ja) * 1993-03-09 1994-09-20 Unitika Ltd 微生物分解性マルチフイラメントとその製造法
JP3432340B2 (ja) * 1995-10-03 2003-08-04 ユニチカ株式会社 生分解性成形用長繊維不織布およびその製造方法
JPH1161560A (ja) * 1997-08-25 1999-03-05 Unitika Ltd 生分解性短繊維およびその製造方法
JP3614020B2 (ja) * 1999-03-02 2005-01-26 東レ株式会社 脂肪族ポリエステルマルチフィラメントの製造方法
JP5924623B2 (ja) * 2011-03-25 2016-05-25 国立大学法人 東京大学 熱安定性と強度に優れた生分解性ポリエステル系繊維およびその製造方法
CN102181960A (zh) * 2011-04-22 2011-09-14 中国科学院宁波材料技术与工程研究所 一种含phbv的生物基可降解纤维及其制备方法
WO2016094669A1 (en) * 2014-12-11 2016-06-16 Tepha, Inc. Methods of orienting multifilament yarn and monofilaments of poly-4-hydroxybutyrate and copolymers thereof
CN106521688A (zh) * 2016-09-22 2017-03-22 江南大学 一种高强粗旦聚（3‑羟基丁酸酯‑co‑3‑羟基戊酸酯）单丝及其制备方法
CN106400183A (zh) * 2016-09-22 2017-02-15 江南大学 一种聚（3‑羟基丁酸酯‑co‑3‑羟基戊酸酯）复丝及其制备方法
CN115380136B (zh) * 2020-04-09 2024-08-16 株式会社钟化 脂肪族聚酯纤维的制造方法、脂肪族聚酯纤维及复丝
JP7580283B2 (ja) * 2021-01-26 2024-11-11 株式会社カネカ 生分解性短繊維不織布

Also Published As

Publication number Publication date
JPWO2023022015A1 (https=) 2023-02-23
CN117795140A (zh) 2024-03-29
WO2023022015A1 (ja) 2023-02-23

Similar Documents

Publication Publication Date Title
CN115380136B (zh) 脂肪族聚酯纤维的制造方法、脂肪族聚酯纤维及复丝
US20240279848A1 (en) Undrawn multifilament, method for producing the same, multifilament, method for producing the same, staple, and method for producing the same
US8182725B2 (en) Methods for making polylactic acid stereocomplex fibers
JP2022114186A (ja) 生分解性短繊維不織布
EP4317554A1 (en) Multifilament, method for manufacturing multifilament, staple, and method for manufacturing staple
CN1662683B (zh) 聚对苯二甲酸丙二醇酯双组分纤维工艺
JP2009518555A (ja) ポリ（トリメチレンテレフタレート）／ポリ（α−ヒドロキシ酸）二成分フィラメント
WO2023167245A1 (ja) マルチフィラメント、及び、その製造方法
JP4270734B2 (ja) 嵩高性を有する生分解性繊維の製造方法
JP2021042511A (ja) ポリ乳酸長繊維の製造方法
US20250223727A1 (en) Multifilament and method for producing the same
EP4667629A1 (en) Multifilament production method
EP4355938A1 (en) Method of preparation of hierarchically structured self-reinforcing composite systems based on biopolymers of polylactic acid, and such composite systems
JP2025136573A (ja) 延伸用繊維の製造方法、及び、繊維の製造方法
FI4087962T3 (en) BIODEGRADABLE POLYMER FIBER FROM RENEWABLE RAW MATERIALS
JP2009084759A (ja) ポリ乳酸短繊維およびその製造方法
WO2025105082A1 (ja) 繊維、及び、その製造方法
WO2025089095A1 (ja) 繊維、及び、不織布
JP2004084118A (ja) 生分解性繊維の製造方法
JP2024167706A (ja) 圧電繊維とその製造方法
WO2025205578A1 (ja) フィラメント、及び、その製造方法
WO2024048250A1 (ja) パイル布帛、及びその製造方法
WO2023157915A1 (ja) 生分解性不織布及びその製造方法
JP2024104657A (ja) 釣糸
WO2024058076A1 (ja) 染色されたｐ３ｈｂ３ｈｈ系繊維、及びそれを含む繊維集合体、並びにそれらの製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: KANEKA CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:MIHAYASHI, TSUYOSHI;REEL/FRAME:067144/0488

Effective date: 20240221

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION COUNTED, NOT YET MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION COUNTED, NOT YET MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER