US20230348294A1 - Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same - Google Patents

Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same Download PDF

Info

Publication number
US20230348294A1
US20230348294A1 US18/025,728 US202118025728A US2023348294A1 US 20230348294 A1 US20230348294 A1 US 20230348294A1 US 202118025728 A US202118025728 A US 202118025728A US 2023348294 A1 US2023348294 A1 US 2023348294A1
Authority
US
United States
Prior art keywords
positive electrode
active material
electrode active
particles
secondary battery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US18/025,728
Other languages
English (en)
Inventor
Jong-Wook Heo
Ji-Hye Kim
Tae-Gu Yoo
Wang-Mo Jung
Hae-Jung Jung
Chi-Ho Jo
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LG Energy Solution Ltd
Original Assignee
LG Energy Solution Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LG Energy Solution Ltd filed Critical LG Energy Solution Ltd
Assigned to LG ENERGY SOLUTION, LTD. reassignment LG ENERGY SOLUTION, LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HEO, Jong-Wook, JO, CHI-HO, JUNG, Hae-Jung, JUNG, WANG-MO, KIM, JI-HYE, YOO, TAE-GU
Publication of US20230348294A1 publication Critical patent/US20230348294A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/362—Composites
    • H01M4/366—Composites as layered products
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/40—Nickelates
    • C01G53/42—Nickelates containing alkali metals, e.g. LiNiO2
    • C01G53/44—Nickelates containing alkali metals, e.g. LiNiO2 containing manganese
    • C01G53/50—Nickelates containing alkali metals, e.g. LiNiO2 containing manganese of the type [MnO2]n-, e.g. Li(NixMn1-x)O2, Li(MyNixMn1-x-y)O2
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
    • C01F7/00—Compounds of aluminium
    • C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G51/00—Compounds of cobalt
    • C01G51/04—Oxides; Hydroxides
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G51/00—Compounds of cobalt
    • C01G51/40—Cobaltates
    • C01G51/42—Cobaltates containing alkali metals, e.g. LiCoO2
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/006—Compounds containing, besides nickel, two or more other elements, with the exception of oxygen or hydrogen
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/131—Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/139—Processes of manufacture
    • H01M4/1391—Processes of manufacture of electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/485—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of mixed oxides or hydroxides for inserting or intercalating light metals, e.g. LiTi2O4 or LiTi2OxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
    • H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
    • H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/60—Compounds characterised by their crystallite size
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/01—Particle morphology depicted by an image
    • C01P2004/03—Particle morphology depicted by an image obtained by SEM
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/50—Agglomerated particles
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/51—Particles with a specific particle size distribution
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/80—Particles consisting of a mixture of two or more inorganic phases
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/11—Powder tap density
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/40—Electric properties
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M2004/021—Physical characteristics, e.g. porosity, surface area
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M2004/026—Electrodes composed of, or comprising, active material characterised by the polarity
    • H01M2004/028—Positive electrodes
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries

Definitions

  • the present disclosure relates to a positive electrode active material for a lithium secondary battery comprising primary macro particles and a method for preparing the same.
  • lithium secondary batteries have are gaining attention as a power source for driving mobile devices due to their light weight and high energy density advantages. Accordingly, there are many efforts to improve the performance of lithium secondary batteries.
  • a lithium secondary battery includes an organic electrolyte solution or a polymer electrolyte solution filled between a positive electrode and a negative electrode made of an active material capable of intercalating and deintercalating lithium ions, and electrical energy is produced by oxidation and reduction reactions during intercalation/deintercalation of lithium ions at the positive electrode and the negative electrode.
  • the positive electrode active material of the lithium secondary battery includes lithium cobalt oxide (LiCoO 2 ), lithium nickel oxide (LiNiO 2 ), lithium manganese oxide (LiMnO 2 or LiMn 2 O 4 ) and a lithium iron phosphate compound (LiFePO 4 ).
  • lithium cobalt oxide (LiCoO 2 ) is widely used due to its high operating voltage and large capacity advantages, and is used as a positive electrode active material for high voltage.
  • cobalt (Co) has a limitation on the use in a large amount as a power source in the field of electric vehicles due to its price rise and unstable supply, and thus there is a need for development of an alternative positive electrode active material.
  • NCM-based lithium composite transition metal oxide nickel cobalt manganese based lithium composite transition metal oxide
  • Ni nickel
  • Mn manganese
  • the conventionally developed NCM-based lithium composite transition metal oxide is in the form of a secondary particle formed by agglomeration of primary micro particles, and has a large specific surface area and low particle strength.
  • the positive electrode active material comprising the secondary particle formed by agglomeration of primary micro particles is used to manufacture an electrode, followed by a rolling process, particle cracking is severe and a large amount of gas is produced during the cell operation, resulting in low stability.
  • the structural and chemical stability is lower, and it is more difficult to ensure the thermal stability.
  • the monolith exists independently of the secondary particle, and refers to a particle having seemingly absent grain boundary.
  • the monolith changes in the crystal structure of the particle surface from a layered structure to a rock salt structure.
  • the surface of the nonconductive rock salt structure hinders the movement of lithium ions during charge/discharge, resulting in a shorter life of the battery.
  • the present disclosure is designed to solve the above-described problem, and therefore the present disclosure is directed to providing a new concept of secondary particle.
  • the present disclosure is further directed to improving the electrical and chemical properties by partial coating of the secondary particle with cobalt compound and aluminum compound on the surface.
  • the present disclosure is further directed to providing a nickel-based positive electrode active material with improved stability, especially, at high temperature and high voltage.
  • An aspect of the present disclosure provides a positive electrode active material according to the following embodiments.
  • a first embodiment relates to a positive electrode active material for a lithium secondary battery, comprising secondary particles, each secondary particle comprising an agglomerate of primary macro particles, wherein an average particle size D50 of the primary macro particles is 1.5 ⁇ m or more, part of a surface of the secondary particles is coated with a cobalt compound and an aluminum compound, an average particle size D50 of the secondary particles is 3 to 10 ⁇ m, and the primary macro particles comprise a nickel-based lithium transition metal oxide.
  • a second embodiment relates to the positive electrode active material for a lithium secondary battery according to the first embodiment, wherein the cobalt compound and the aluminum compound are coated in a dot pattern.
  • a third embodiment relates to the positive electrode active material for a lithium secondary battery according to the first or second embodiment, wherein the nickel-based lithium transition metal oxide comprises Li(Ni x Co y Mi 1-x-y )O 2 , wherein M is at least one selected from Mn, Al, Y, Ti and Zr.
  • a fourth embodiment relates to the positive electrode active material for a lithium secondary battery according to any one of the above-described embodiments, wherein the cobalt compound comprises at least one of LiCoO 2 , Co(OH) 2 , CoO, Co 2 O 3 , Co 3 O 4 , CoO(OH) or Co(OCOCH 3 ) 2 ⁇ 4H 2 O.
  • a fifth embodiment relates to the positive electrode active material for a lithium secondary battery according to any one of the above-described embodiments, wherein the aluminum compound comprises at least one of Al 2 O 3 , Al(OH) 3 , Al(CH 3 CO 2 ) 3 , LiAlO 2 or Li 5 AlO 4 .
  • a sixth embodiment relates to the positive electrode active material for a lithium secondary battery according to any one of the above-described embodiments, wherein a ratio of the average particle size D50 of the primary macro particles to an average crystal size of the primary macro particles is 2 or more.
  • a seventh embodiment relates to the positive electrode active material for a lithium secondary battery according to any one of the above-described embodiments, wherein an average crystal size of the primary macro particles is 130 nm or more.
  • An eighth embodiment relates to the positive electrode active material for a lithium secondary battery according to any one of the above-described embodiments, wherein a ratio of the average particle size D50 of the secondary particles to the average particle size D50 of the primary macro particles is 2 to 4 times.
  • Another aspect of the present disclosure provides a positive electrode for a lithium secondary battery.
  • a ninth embodiment relates to a positive electrode for a lithium secondary battery comprising the above-described positive electrode active material.
  • Still another aspect of the present disclosure provides a lithium secondary battery according to the following embodiment.
  • a tenth embodiment provides a lithium secondary battery comprising the above-described positive electrode active material.
  • Yet another aspect of the present disclosure provides a method for preparing a positive electrode active material according to the following embodiments.
  • An eleventh embodiment relates to a method for preparing a positive electrode active material for a lithium secondary battery, comprising (S1) mixing a precursor comprising nickel, cobalt and manganese with hydroxide to prepare a porous nickel-based lithium transition metal hydroxide precursor; (S2) mixing the porous nickel-based lithium transition metal hydroxide precursor with a lithium raw material and performing thermal treatment to prepare secondary particles; and (S3) mixing the secondary particles with a cobalt compound and an aluminum compound and performing thermal treatment to form a positive electrode active material, wherein the positive electrode active material comprising secondary particles, each secondary particle comprising an agglomerate of primary macro particles, an average particle size D50 of the primary macro particles is 1.5 ⁇ m or more, part of a surface of the secondary particles is coated with cobalt and aluminum, and an average particle size D50 of the secondary particles is 3 to 10 ⁇ m, and the primary macro particles comprises a nickel-based lithium transition metal oxide.
  • a twelfth embodiment relates to the method for preparing a positive electrode active material according to the eleventh embodiment, wherein the step (S1) is performed at 35 to 80° C., and the step (S2) is performed at 700 to 1000° C.
  • a thirteenth embodiment relates to the method for preparing a positive electrode active material according to any one of the above-described embodiments, wherein the step (S3) is performed at 600 to 750° C.
  • a fourteenth embodiment relates to the method for preparing a positive electrode active material according to any one of the above-described embodiments, which the step (S1) is performed in a condition of pH 8 to 12.
  • a fifteenth embodiment relates to the method for preparing a positive electrode active material according to any one of the above-described embodiments, wherein does not comprise a washing process between the step (S2) and the step (S3).
  • a sixteenth embodiment relates to the method for preparing a positive electrode active material according to any one of the above-described embodiments, wherein a tap density of the porous nickel-based lithium transition metal hydroxide precursor of the step (S2) is 1.5 to 2.5 g/cc.
  • a positive electrode active material comprising a secondary particle with improved resistance by simultaneous growth of the average particle size D50 and the crystal size of the primary macro particles.
  • FIGS. 1 A to 1 E are scanning electron microscope (SEM) images of positive electrode active materials according to comparative examples 1 to 3 and examples 1 to 2 of the present disclosure.
  • FIG. 2 A is an SEM image of a positive electrode active material according to comparative example 3 of the present disclosure.
  • FIG. 2 B shows a measured amount of cobalt in the SEM image of FIG. 2 A .
  • FIG. 2 C shows a measured amount of aluminum in the SEM image of FIG. 2 A .
  • FIG. 3 A is an SEM image of a positive electrode active material according to example 1 of the present disclosure.
  • FIG. 3 B shows a measured amount of cobalt in the SEM image of FIG. 3 A .
  • FIG. 3 C shows a measured amount of aluminum in the SEM image of FIG. 3 A .
  • FIG. 4 is a graph showing the high temperature storage characteristics of an example and comparative example of the present disclosure.
  • FIG. 5 is a graph showing the continuous charge characteristics of an example and comparative example of the present disclosure.
  • the crystal size of the crystal grain may be quantitatively analyzed using X-ray diffraction analysis (XRD) by Cu K ⁇ X-ray (Xr ⁇ ).
  • XRD X-ray diffraction analysis
  • Xr ⁇ Cu K ⁇ X-ray
  • the average crystal size of the crystal grain may be quantitatively analyzed by putting a prepared particle into a holder and analyzing diffraction grating for X-ray radiation onto the particle.
  • D50 may be defined as a particle size at 50% of particle size distribution, and may be measured using a laser diffraction method.
  • a method for measuring the average particle size D50 of a positive electrode active material may include dispersing particles of the positive electrode active material in a dispersion medium, introducing into a commercially available laser diffraction particle size measurement device (for example, Microtrac MT 3000), irradiating ultrasound of about 28 kHz with the output power of 60 W, and calculating the average particle size D50 corresponding to 50% of cumulative volume in the measurement device.
  • a laser diffraction particle size measurement device for example, Microtrac MT 3000
  • ‘primary particle’ refers to a particle having seemingly absent grain boundary when observed with the field of view of 5000 to 20000 magnification using a scanning electron microscope.
  • the primary particle may be classified into a primary micro particle and a primary macro particle according to the average particle size D50.
  • ‘secondary particle’ is a particle formed by agglomeration of the primary particles.
  • ‘monolith’ refers to a particle that exists independently of the secondary particle, and has seemingly absent grain boundary, and for example, it is a particle having the particle diameter of 0.5 ⁇ m or more.
  • ‘particle’ may include any one of the monolith, the secondary particle and the primary particle or all of them.
  • An aspect of the present disclosure provides a positive electrode active material in the form of a secondary particle of different type from the conventional art.
  • a positive electrode active material for a lithium secondary battery 1 comprising secondary particles, each secondary particle comprising an agglomerate of primary macro particles,
  • the average particle size D50 of the primary macro particles is 1.5 ⁇ m or more
  • the average particle size D50 of the secondary particles is 3 to 10 ⁇ m
  • the positive electrode active material comprises nickel-based lithium transition metal oxide.
  • the secondary particle having the above-described features may provide a nickel-based positive electrode active material with improved stability at high temperature and high voltage.
  • nickel-based lithium transition metal oxide is a secondary particle.
  • the secondary particle may be an agglomerate of primary particles.
  • a secondary particle of dense nickel-based lithium transition metal hydroxide prepared by a coprecipitation method is used for a precursor, and when the precursor is mixed with a lithium precursor and sintered at the temperature of less than 960° C., a secondary particle of nickel-based lithium transition metal oxide may be obtained.
  • a positive electrode active material comprising the conventional secondary particle is coated on a current collector, followed by a rolling process, the particle itself cracks, and the specific surface area increases. When the specific surface area increases, rock salt is formed on the surface and the resistance reduces.
  • monolithic positive electrode active materials have been additionally developed.
  • the use of a porous precursor makes it possible to synthesize at lower sintering temperature compared to the same nickel content, thereby obtaining monolithic nickel-based lithium transition metal oxide, which does not assume the form of a secondary particle any longer.
  • the monolith changes in the crystal structure of the particle surface from a layered structure to a rock salt structure. The surface of the nonconductive rock salt structure hinders the movement of lithium ions during charge/discharge, resulting in a shorter life of the battery.
  • An aspect of the present disclosure is provided to solve the problem.
  • the average particle size D50 of the primary particles increases, and at the same time, the average particle size D50 of the secondary particles increases as well.
  • the secondary particle according to an aspect of the present disclosure is different from the method for obtaining the conventional monolith as described below.
  • the conventional monoliths are formed at higher primary sintering temperature, but still use the conventional precursor for secondary particles.
  • the secondary particle according to an aspect of the present disclosure uses a porous precursor. Accordingly, it is possible to grow the primary macro particle having a large particle size without increasing the sintering temperature, and by contrast, the secondary particle grows less than the conventional art.
  • the secondary particles according to an aspect of the present disclosure has the same or similar average particle size D50 to the conventional art and a large average particle size D50 of the primary particles. That is, as opposed to the typical configuration of the conventional positive electrode active material, i.e., in the form of a secondary particle formed by agglomeration of primary particles having a small average particle size, it is provided in the form of a secondary particle formed by agglomeration of primary macro particles, namely, primary particles having the increased size.
  • the ‘primary macro particles’ have the average particle size D50 of 1.5 ⁇ m or more.
  • the average particle size of the primary macro particles may be 1.5 ⁇ m or more, 2 ⁇ m or more, 2.5 ⁇ m or more, 3 ⁇ m or more, or 3.5 ⁇ m or more, and may be 5 ⁇ m or less, 4.5 ⁇ m or less, or 4 ⁇ m or less.
  • the average particle size of the primary macro particles is less than 1.5 ⁇ m, it corresponds to the conventional secondary particle, and particle cracking may occur in the rolling process.
  • the ‘primary macro particles’ may have a ratio of the average particle size D50/the average crystal size of 3 or more. That is, when compared with the primary micro particles that form the conventional secondary particle, the primary macro particles have simultaneous growth of the average particle size and the average crystal size of the primary particles.
  • the inventors have focused on the growth of the average particle size D50 of the primary particles.
  • the average particle size D50 of the primary particles is only increased by over-sintering, rock salt is formed on the surface of the primary particle and the initial resistance increases. Additionally, in an attempt to solve the problem, it is necessary to grow the average crystal size of the primary particle together to reduce the resistance.
  • the primary macro particles refers to particles having a large average particle size as well as a large average crystal size and a seemingly absent grain boundary.
  • the average particle size and the average crystal size of the primary particles are simultaneously grown, it is advantageous in terms of low resistance and long life, compared to the conventional monolith having the increased resistance due to the rock salt formed on the surface by sintering at high temperature.
  • the “secondary particle formed by agglomeration of primary macro particles” used in an aspect of the present disclosure is advantageous in terms of low resistance resulting from the increased size of the primary particle itself and the reduced rock salt formation.
  • the average crystal size of the primary macro particles may be quantitatively analyzed using X-ray diffraction analysis (XRD) by Cu K ⁇ X-ray.
  • XRD X-ray diffraction analysis
  • the average crystal size of the primary macro particle may be quantitatively analyzed by putting the prepared particle into a holder and analyzing diffraction grating for X-ray radiation onto the particle.
  • the ratio of the average particle size D50 to the average crystal size may be 2 or more, 2.5 or more, or 3 or more, and may be 50 or less, 40 or less, or 35 or less.
  • the average crystal size of the primary macro particles may be 130 nm or more, 150 nm or more, 170 nm or more, or 200 nm or more, and may be 300 nm or less, 270 nm or less, or 250 nm or less.
  • the secondary particles according to an aspect of the present disclosure has the same or similar average particle size D50 to the conventional art and a large average particle size D50 of the primary particles. That is, as opposed to the typical configuration of the conventional positive electrode active material, i.e., in the form of a secondary particle formed by agglomeration of primary particles having a small average particle size, it is provided in the form of a secondary particle formed by agglomeration of primary macro particles, namely, primary particles having the increased size.
  • the secondary particle may be an agglomerate of 1 to 30 primary macro particles. More specifically, the secondary particle may be an agglomerate of 1 or more, 2 or more, 3 or more, or 4 or more primary macro particles in the numerical range, and may be an agglomerate of 30 or less, 25 or less, 20 or less, 15 or less, or 10 or less primary macro particles in the numerical range.
  • the secondary particles according to an aspect of the present disclosure has the average particle size D50 of 3 ⁇ m to 10 ⁇ m. More specifically, the average particle size D50 is 3 ⁇ m or more, 3.5 ⁇ m or more, 4 ⁇ m or more, or 4.5 ⁇ m or more, and is 10 ⁇ m or less, 8 ⁇ m or less, or 7 ⁇ m or less.
  • the primary macro particle may grow to a larger particle size using the porous precursor without increasing the sintering temperature, and by contrast, the secondary micro particle grows less than the conventional art.
  • the secondary particles according to an aspect of the present disclosure has the same or similar average particle size D50 to the conventional secondary particle and comprises primary macro particles having a larger average particle size and a larger average crystal size than the conventional primary micro particles.
  • a ratio of the average particle size D50 of the secondary particles to the average particle size D50 of the primary macro particles may be 2 to 4 times.
  • the primary macro particles are separated but do not crack in the rolling process of the secondary particle.
  • the rolling condition may be the pressure of 9 tons.
  • the secondary particle comprises nickel-based lithium transition metal oxide.
  • the nickel-based lithium transition metal oxide comprises Li(Ni x Co y M 1-x-y )O 2 , wherein M is at least one selected from Mn, Al, Y, Ti and Zr.
  • x and y denote a mole ratio of each element in the nickel-based lithium transition metal oxide.
  • the nickel-based lithium transition metal oxide may be selected from the group consisting of LiNi 0.8 Co 0.1 Mn 0.1 O 2 , LiNi 0.6 Co 0.2 Mn 0.2 O 2 , LiNi 0.5 Co 0.2 Mn 0.3 O 2 , and LiNi 0.5 Co 0.3 Mn 0.2 O 2 .
  • Nickel (Ni) contributes to increasing the potential and capacity of the secondary battery, and an amount corresponding to x may be included in an amount of 0 ⁇ x ⁇ 1.
  • the charge/discharge capacity characteristics may degrade, and when an x value is larger than 1, the structure and thermal stability of the active material may degrade and as a consequence, the life characteristics may degrade.
  • the nickel When considering the higher potential and higher capacity effect by the control of the nickel content, the nickel may be included in an amount of more specifically, x 0.5 ⁇ x ⁇ 1, and even more specifically, 0.5 ⁇ x ⁇ 0.8.
  • Co Co
  • the structure stability and lithium ion conductivity may degrade and as a consequence, the charge/discharge capacity may reduce, and when y is larger than 0.35, the operating voltage of the positive electrode active material may increase and the charge/discharge capacity may reduce under a given upper limit of voltage.
  • the cobalt may be included in an amount of, more specifically 0.1 ⁇ y ⁇ 0.35, and even more specifically 0.1 ⁇ y ⁇ 0.3.
  • part of the surface of the secondary particle is coated with a cobalt compound and an aluminum compound.
  • the cobalt compound may be at least one of LiCoO 2 , Co(OH) 2 , CoO, Co 2 O 3 , Co 3 O 4 , CoO(OH) or Co(OCOCH 3 ) 2 ⁇ 4H 2 O.
  • the aluminum compound may be at least one of Al 2 O 3 , Al(OH) 3 , Al(CH 3 CO 2 ) 3 , LiAlO 2 or Li 5 AlO 4 .
  • the cobalt compound and the aluminum compound are coated on only part of the secondary particle surface.
  • the cobalt compound and the aluminum compound may be coated in a dot pattern.
  • the resistance may be higher than a desired level.
  • the positive electrode active material according to an aspect of the present disclosure may be prepared by the following method. However, the present disclosure is not limited thereto.
  • the present disclosure relates to a method for preparing a positive electrode active material for a lithium secondary battery, comprising:
  • the positive electrode active material precursor comprising nickel (Ni), cobalt (Co) and manganese (Mn) is prepared.
  • the precursor for preparing the positive electrode active material may be a commercially available positive electrode active material precursor, or may be prepared by a method for preparing a positive electrode active material precursor well known in the corresponding technical field.
  • the precursor may have a tap density of 1.5 to 2.5 g/cc.
  • the precursor may be prepared by adding an ammonium cation containing complex forming agent and a basic compound to a transition metal solution comprising a nickel containing raw material, a cobalt containing raw material and a manganese containing raw material and causing coprecipitation reaction.
  • the nickel containing raw material may include, for example, nickel containing acetate, nitrate, sulfate, halide, sulfide, hydroxide, oxide or oxyhydroxide, and specifically, may include at least one of Ni(OH) 2 , NiO, NiOOH, NiCO 3 ⁇ 2Ni(OH) 2 ⁇ 4H 2 O, NiC 2 O 2 ⁇ 2H 2 O, Ni(NO 3 ) 2 ⁇ 6H 2 O, NiSO 4 , NiSO 4 ⁇ 6H 2 O, an fatty acid nickel salt or nickel halide, but is not limited thereto.
  • the cobalt containing raw material may include cobalt containing acetate, nitrate, sulfate, halide, sulfide, hydroxide, oxide or oxyhydroxide, and specifically, may include at least one of Co(OH) 2 , CoOOH, Co(OCOCH 3 ) 2 ⁇ 4H 2 O, Co(NO 3 ) 2 ⁇ 6H 2 O, CoSO 4 , or Co(SO 4 ) 2 ⁇ 7H 2 O, but is not limited thereto.
  • the manganese containing raw material may include, for example, at least one of manganese containing acetate, nitrate, sulfate, halide, sulfide, hydroxide, oxide or oxyhydroxide, and specifically, may include, for example, at least one of manganese oxide such as Mn 2 O 3 , MnO 2 , Mn 3 O 4 ; a manganese salt such as MnCO 3 , Mn(NO 3 ) 2 , MnSO 4 , manganese acetate, a manganese salt of dicarboxylic acid, manganese citrate and an fatty acid manganese salt; manganese oxyhydroxide or manganese chloride, but is not limited thereto.
  • the transition metal solution may be prepared by adding the nickel containing raw material, the cobalt containing raw material and the manganese containing raw material to a solvent, to be specific, water, or a mixed solvent of water and an organic solvent (for example, alcohol, etc.) that mixes with water to form a homogeneous mixture, or by mixing an aqueous solution of the nickel containing raw material, an aqueous solution of the cobalt containing raw material and the manganese containing raw material.
  • a solvent to be specific, water, or a mixed solvent of water and an organic solvent (for example, alcohol, etc.) that mixes with water to form a homogeneous mixture, or by mixing an aqueous solution of the nickel containing raw material, an aqueous solution of the cobalt containing raw material and the manganese containing raw material.
  • the ammonium cation containing complex forming agent may include, for example, at least one of NH 4 OH, (NH 4 ) 2 SO 4 , NH 4 NO 3 , NH 4 Cl, CH 3 COONH 4 or (NH 4 ) 2 CO 3 , but is not limited thereto.
  • the ammonium cation containing complex forming agent may be used in the form of an aqueous solution, and in this instance, a solvent may include water or a mixture of water and an organic solvent (specifically, alcohol, etc.) that mixes with water to form a homogeneous mixture.
  • the basic compound may include at least one of hydroxide or hydrate of alkali metal or alkaline earth metal such as NaOH, KOH or Ca(OH) 2 .
  • the basic compound may be used in the form of an aqueous solution, and in this instance, a solvent may include water, or a mixture of water and an organic solvent (specifically, alcohol, etc.) that mixes with water to form a homogeneous mixture.
  • the basic compound may be added to control the pH of the reaction solution, and may be added in such an amount that the pH of the metal solution is 8 to 12.
  • the precursor comprising nickel, cobalt and manganese may be mixed with hydroxide to prepare a porous nickel-based lithium transition metal hydroxide precursor.
  • the coprecipitation reaction may be performed at 35° C. to 80° C. in an inert atmosphere of nitrogen or argon.
  • the porous nickel-based lithium transition metal hydroxide precursor may be prepared by mixing the precursor comprising nickel, cobalt and manganese with hydroxide (S1).
  • Particles of nickel-cobalt-manganese hydroxide are produced by the above-described process, and settle down in the reaction solution.
  • the precursor having the nickel (Ni) content of 60 mol % or more in the total metal content may be prepared by controlling the concentration of the nickel containing raw material, the cobalt containing raw material and the manganese containing raw material.
  • the settled nickel-cobalt-manganese hydroxide particles are separated by the common method and dried to obtain the nickel-cobalt-manganese precursor.
  • the precursor may be a secondary particle formed by agglomeration of primary particles.
  • the above-described precursor is mixed with the lithium raw material and goes through thermal treatment (primary sintering) (S2).
  • the lithium raw material may include, without limitation, any type of material that dissolves in water, and may include, for example, lithium containing sulfate, nitrate, acetate, carbonate, oxalate, citrate, halide, hydroxide or oxyhydroxide.
  • the lithium raw material may include at least one of Li 2 CO 3 , LiNO 3 , LiNO 2 , LiOH, LiOH ⁇ H 2 O, LiH, LiF, LiCl, LiBr, LiI, CH 3 COOLi, Li 2 O, Li 2 SO 4 , CH 3 COOLi, or Li 3 C 6 H 5 O 7 .
  • the primary sintering may be performed at 700 to 1,000° C., more preferably 780 to 980° C., and even more preferably 780 to 900° C.
  • the primary sintering may be performed in air or an oxygen atmosphere, and may be performed for 15 to 35 hours.
  • the primary sintering may be followed by mixing with the cobalt compound and the aluminum compound and additional thermal treatment (secondary sintering) (S3).
  • the secondary sintering may be performed at 600 to 750° C., more preferably 630 to 730° C., and even more preferably 600 to 700° C.
  • the secondary sintering may be performed in air or an oxygen atmosphere, and may be performed for 10 to 24 hours.
  • the method does not comprise any washing process between the step (S2) and the step (S3).
  • the total amount of lithium remaining in the particle after the primary sintering may be 0.5 to 1.5 wt % based on the total weight of the positive electrode active material.
  • the conventional art performs a washing process to wash out the lithium by-products present on the positive electrode active material surface.
  • the lithium by-products cause side reactions with the electrolyte solution in the battery, and increases the amount of produced gas when stored at high temperature.
  • the preparation method according to an aspect of the present disclosure does not comprise any washing process.
  • lithium by-products exist on the particle surface, and when the lithium by-products are present in an amount of 0.5 to 1.5 wt % based on the total weight of the positive electrode active material, it is possible to prepare a positive electrode active material comprising secondary particles, each secondary particle being an agglomerate comprising primary macro particles according to an aspect of the present disclosure.
  • a positive electrode for a lithium secondary battery comprising the positive electrode active material, and a lithium secondary battery.
  • the positive electrode comprises a positive electrode current collector and a positive electrode active material layer comprising the positive electrode active material, formed on the positive electrode current collector.
  • the positive electrode current collector is not limited to a particular type and may include any type of material having conductive properties without causing any chemical change to the battery, for example, stainless steel, aluminum, nickel, titanium, sintered carbon or aluminum or stainless steel treated with carbon, nickel, titanium or silver on the surface. Additionally, the positive electrode current collector may be generally 3 to 500 ⁇ m in thickness, and may have microtexture on the surface to improve the adhesion strength of the positive electrode active material.
  • the positive electrode current collector may come in various forms, for example, films, sheets, foils, nets, porous bodies, foams and non-woven fabrics.
  • the positive electrode active material layer may comprise a conductive material and a binder.
  • the conductive material is used to impart conductivity to the electrode, and may include, without limitation, any type of conductive material having electron conductivity without causing any chemical change in the battery.
  • the conductive material may include at least one of graphite, for example, natural graphite or artificial graphite; carbon-based materials, for example, carbon black, acetylene black, ketjen black, channel black, furnace black, lamp black, thermal black and carbon fibers; metal powder or metal fibers, for example, copper, nickel, aluminum and silver; conductive whiskers, for example, zinc oxide and potassium titanate; conductive metal oxide, for example, titanium oxide; or conductive polymers, for example, polyphenylene derivatives.
  • the conductive material may be included in an amount of 1 to 30 weight % based on the total weight of the positive electrode active material layer.
  • the binder serves to improve the bonds between the positive electrode active material particles and the adhesion strength between the positive electrode active material and the positive electrode current collector.
  • the binder may include at least one of polyvinylidene fluoride (PVDF), polyvinylidene fluoride-hexafluoropropylene copolymer (PVDF-co-HFP), polyvinylalcohol, polyacrylonitrile, carboxymethylcellulose (CMC), starch, hydroxypropyl cellulose, regenerated cellulose, polyvinylpyrrolidone, polytetrafluoroethylene, polyethylene, polypropylene, ethylene-propylene-diene polymer (EPDM), sulfonated-EPDM, styrene butadiene rubber (SBR), fluoro rubber, or a variety of copolymers thereof.
  • the binder may be included in an amount of 1 to 30 weight % based on the total weight of the positive electrode active material layer.
  • the positive electrode may be manufactured by the commonly used positive electrode manufacturing method except using the above-described positive electrode active material. Specifically, the positive electrode may be manufactured by coating a positive electrode active material layer forming composition comprising the positive electrode active material and optionally, the binder and the conductive material on the positive electrode current collector, drying and rolling. In this instance, the type and amount of the positive electrode active material, the binder and the conductive material may be the same as described above.
  • the solvent may include solvents commonly used in the corresponding technical field, for example, at least one of dimethyl sulfoxide (DMSO), isopropyl alcohol, N-methylpyrrolidone (NMP), acetone or water.
  • DMSO dimethyl sulfoxide
  • NMP N-methylpyrrolidone
  • acetone water
  • the solvent may be used in such an amount to have sufficient viscosity for good thickness uniformity when dissolving or dispersing the positive electrode active material, the conductive material and the binder and coating to manufacture the positive electrode in view of the slurry coating thickness and the production yield.
  • the positive electrode may be manufactured by casting the positive electrode active material layer forming composition on a support, peeling off a film from the support and laminating the film on the positive electrode current collector.
  • an electrochemical device comprising the positive electrode.
  • the electrochemical device may include a battery or a capacitor, and more specifically, a lithium secondary battery.
  • the lithium secondary battery comprises a positive electrode, a negative electrode disposed opposite the positive electrode, a separator interposed between the positive electrode and the negative electrode and an electrolyte, and the positive electrode is the same as described above.
  • the lithium secondary battery may further comprise a battery case in which an electrode assembly comprising the positive electrode, the negative electrode and the separator is received, and a sealing member to seal up the battery case.
  • the negative electrode comprises a negative electrode current collector and a negative electrode active material layer positioned on the negative electrode current collector.
  • the negative electrode current collector may include any type of material having high conductivity without causing any chemical change to the battery, for example, copper, stainless steel, aluminum, nickel, titanium, sintered carbon, copper or stainless steel treated with carbon, nickel, titanium or silver on the surface and an aluminum-cadmium alloy, but is not limited thereto. Additionally, the negative electrode current collector may be generally 3 to 500 ⁇ m in thickness, and in the same way as the positive electrode current collector, the negative electrode current collector may have microtexture on the surface to improve the bonding strength of the negative electrode active material.
  • the negative electrode current collector may come in various forms, for example, films, sheets, foils, nets, porous bodies, foams and non-woven fabrics.
  • the negative electrode active material layer optionally comprises a binder and a conductive material.
  • the negative electrode active material layer may be made by coating a negative electrode forming composition comprising the negative electrode active material, and optionally the binder and the conductive material on the negative electrode current collector and drying, or by casting the negative electrode forming composition on a support, peeling off a film from the support and laminating the film on the negative electrode current collector.
  • the negative electrode active material may include compounds capable of reversibly intercalating and deintercalating lithium.
  • Specific examples of the negative electrode active material may include at least one of a carbonaceous material, for example, artificial graphite, natural graphite, graphitizing carbon fibers, amorphous carbon; a metallic substance that can form alloys with lithium, for example, Si, Al, Sn, Pb, Zn, Bi, In, Mg, Ga, Cd, Si alloy, Sn alloy or Al alloy; metal oxide capable of doping and undoping lithium such as SiO ⁇ (0 ⁇ 2), SnO 2 , vanadium oxide, lithium vanadium oxide; or a complex comprising the metallic substance and the carbonaceous material such as a Si—C complex or a Sn—C complex.
  • a metal lithium thin film may be used for the negative electrode active material.
  • the carbon material may include low crystalline carbon and high crystalline carbon.
  • the low crystalline carbon typically includes soft carbon and hard carbon
  • the high crystalline carbon typically includes high temperature sintered carbon, for example, amorphous, platy, flaky, spherical or fibrous natural graphite or artificial graphite, Kish graphite, pyrolytic carbon, mesophase pitch based carbon fiber, meso-carbon microbeads, mesophase pitches and petroleum or coal tar pitch derived cokes.
  • the binder and the conductive material may be the same as those of the above-described positive electrode.
  • the separator separates the negative electrode from the positive electrode and provides a passage for movement of lithium ions
  • the separator may include, without limitation, any separator commonly used in lithium secondary batteries, and in particular, preferably the separator may have low resistance to the electrolyte ion movement and good electrolyte solution wettability.
  • the separator may include, for example, a porous polymer film made of polyolefin-based polymer such as ethylene homopolymer, propylene homopolymer, ethylene/butene copolymer, ethylene/hexene copolymer and ethylene/methacrylate copolymer or a stack of two or more porous polymer films.
  • the separator may include common porous non-woven fabrics, for example, nonwoven fabrics made of high melting point glass fibers and polyethylene terephthalate fibers. Additionally, to ensure the heat resistance or mechanical strength, the coated separator comprising ceramics or polymer materials may be used, and may be selectively used with a single layer or multilayer structure.
  • the electrolyte used in the present disclosure may include an organic liquid electrolyte, an inorganic liquid electrolyte, a solid polymer electrolyte, a gel polymer electrolyte, a solid inorganic electrolyte and a molten inorganic electrolyte, available in the manufacture of lithium secondary batteries, but is not limited thereto.
  • the electrolyte may comprise an organic solvent and a lithium salt.
  • the organic solvent may include, without limitation, any type of organic solvent that acts as a medium for the movement of ions involved in the electrochemical reaction of the battery.
  • the organic solvent may include an ester-based solvent, for example, methyl acetate, ethyl acetate, ⁇ -butyrolactone, ⁇ -caprolactone; an ether-based solvent, for example, dibutyl ether or tetrahydrofuran; a ketone-based solvent, for example, cyclohexanone; an aromatic hydrocarbon-based solvent, for example, benzene, fluorobenzene; a carbonate-based solvent, for example, dimethylcarbonate (DMC), diethylcarbonate (DEC), ethylmethylcarbonate (EMC), ethylene carbonate (EC), propylene carbonate (PC); an alcohol-based solvent, for example, ethylalcohol, isopropyl alcohol; nitriles of R—CN (R is C2 to C20 straight-
  • the carbonate-based solvent is desirable, and more preferably, cyclic carbonate (for example, ethylene carbonate or propylene carbonate) having high dielectric constant which contributes to the improved charge/discharge performance of the battery may be mixed with a linear carbonate-based compound (for example, ethylmethyl carbonate, dimethyl carbonate or diethyl carbonate) of low viscosity.
  • cyclic carbonate and the chain carbonate may be mixed at a volume ratio of about 1:1 to about 1:9 to improve the performance of the electrolyte solution.
  • the lithium salt may include, without limitation, any compound that can provide lithium ions used in lithium secondary batteries.
  • the lithium salt may include LiPF 6 , LiClO 4 , LiAsF 6 , LiBF 4 , LiSbF 6 , LiAl0 4 , LiAlCl 4 , LiCF 3 SO 3 , LiC 4 F 9 SO 3 , LiN(C 2 F 5 SO 3 ) 2 , LiN(C 2 F 5 SO 2 ) 2 , LiN(CF 3 SO 2 ) 2 .
  • LiCl, LiI, or LiB(C 2 O 4 ) 2 The concentration of the lithium salt may range from 0.1 to 2.0M. When the concentration of the lithium salt is included in the range, the electrolyte has appropriate conductivity and viscosity, resulting in good performance of the electrolyte and effective movement of lithium ions.
  • the electrolyte may further comprise, for example, at least one type of additive of a haloalkylene carbonate-based compound such as difluoro ethylene carbonate, pyridine, triethylphosphite, triethanolamine, cyclic ether, ethylene diamine, n-glyme, hexaphosphoric triamide, a nitrobenzene derivative, sulfur, a quinone imine dye, N-substituted oxazolidinone, N,N-substituted imidazolidine, ethylene glycol dialkyl ether, an ammonium salt, pyrrole, 2-methoxy ethanol or aluminum trichloride to improve the life characteristics of the battery, prevent the capacity fading of the battery and improve the discharge capacity of the battery.
  • the additive may be included in an amount of 0.1 to 5 weight % based on the total weight of the electrolyte.
  • the lithium secondary battery comprising the positive electrode active material according to the present disclosure is useful in the field of portable devices including mobile phones, laptop computers and digital cameras, and electric vehicles including hybrid electric vehicles (HEVs).
  • portable devices including mobile phones, laptop computers and digital cameras
  • electric vehicles including hybrid electric vehicles (HEVs).
  • HEVs hybrid electric vehicles
  • a battery module comprising the lithium secondary battery as a unit cell and a battery pack comprising the same.
  • the battery module or the battery pack may be used as a power source of at least one medium-large scale device of power tools; electric vehicles comprising electric vehicles (EVs), hybrid electric vehicles, and plug-in hybrid electric vehicles (PHEVs); or energy storage systems.
  • electric vehicles comprising electric vehicles (EVs), hybrid electric vehicles, and plug-in hybrid electric vehicles (PHEVs); or energy storage systems.
  • EVs electric vehicles
  • PHEVs plug-in hybrid electric vehicles
  • a coprecipitation reactor (capacity 20 L), and while the temperature is maintained at 50° C., a transition metal solution with the concentration of 3.2 mol/L, in which NiSO 4 , CoSO 4 and MnSO 4 are mixed at a mole ratio of nickel:cobalt:manganese of 0.8:0.1:0.1, and a 28 wt % ammonia aqueous solution are continuously put into the reactor at 300 mL/hr and 42 mL/hr, respectively. Stirring is performed at the impeller speed of 400 rpm, and a 40 wt % sodium hydroxide solution is used to maintain the pH at 9.
  • Precursor particles are formed by 10-hour coprecipitation reaction. The precursor particles are separated, washed and dried in an oven of 130° C. to prepare a precursor.
  • Ni 0.8 Co 0.1 Mn 0.1 (OH) 2 precursor synthesized by coprecipitation reaction is mixed with LiOH at a mole ratio of Li/Me (Ni, Co, Mn) of 1.05, and thermally treated at 850° C. in an oxygen atmosphere for 10 hours to prepare a positive electrode active material comprising secondary particles of LiNi 0.8 Co 0.1 Mn 0.1 O 2 nickel-based lithium transition metal oxide.
  • Cobalt is coated on the secondary particles prepared in comparative example 1 using a dry process. Specifically, the following method is used.
  • Co(OH) 2 is mixed with LiNi 0.8 Co 0.1 Mn 0.1 O 2 of comparative example 1 in a dry condition such that a weight ratio of Co(OH) 2 /LiNi 0.8 Co 0.1 Mn 0.1 O 2 is 0.1 wt %, and the mixture is thermally treated at 700° C. in an oxygen atmosphere for 10 hours to prepare a LiNi 0.8 Co 0.1 Mn0.1O 2 positive electrode active material coated with cobalt.
  • Cobalt and aluminum are simultaneously coated on the secondary particles prepared in comparative example 1 at 800° C. using a dry process. Specifically, the following method is used.
  • Co(OH) 2 and Al 2 O 3 are mixed with LiNi 0.8 Co 0.1 Mn 0.1 O 2 of comparative example 1 in a dry condition such that a weight ratio of Co(OH) 2 , Al 2 O 3 /LiNi 0.8 Co 0.1 Mn 0.1 O 2 is 0.1 wt %, and the mixture is thermally treated at 800° C. in an oxygen atmosphere for 10 hours to prepare a LiNi 0.8 Co 0.1 Mn 0.1 O 2 positive electrode active material coated with cobalt+aluminum.
  • Cobalt and aluminum are simultaneously coated on the secondary particles prepared in comparative example 1 at 700° C. using a dry process. Specifically, the following method is used.
  • Co(OH) 2 and Al 2 O 3 are mixed with LiNi 0.8 Co 0.1 Mn 0.1 O 2 of comparative example 1 in a dry condition such that a weight ratio of Co(OH) 2 , Al 2 O 3 /LiNi 0.8 Co 0.1 Mn 0.1 O 2 is 0.1wt %, and the mixture is thermally treated at 700° C. in an oxygen atmosphere for 10 hours to prepare a LiNia 0.8 Co 0.1 Mn 0.01 O 2 positive electrode active material coated with cobalt+aluminum.
  • Ni 0.8 Co 0.1 Mn 0.1 (OH) 2 precursor synthesized by coprecipitation reaction according to comparative example 1 is mixed with LiOH such that a mole ratio of Li/Me(Ni, Co, Mn) is 1.05, and thermally treated at 880° C. in an oxygen atmosphere for 10 hours to prepare a positive electrode active material comprising secondary particles of LiNi 0.8 Co 0.1 Mn 0.1 O 2 nickel-based lithium transition metal oxide.
  • Cobalt and aluminum are simultaneously coated on the prepared secondary particles at 700° C. using the same dry process as example 1.
  • example 2 (90.8%) (255%) cobalt alone Comparative 39.9 1.44 36.9 2.78 230 1 15 5 Penetration of example 3 (92.4%) (193%) cobalt and/or aluminum into secondary particle due to too high sintering temperature
  • Example 1 40.1 1.39 38.4 1.97 230 1 15 5
  • Partial coating (95.7%) (142%) with cobalt and aluminum
  • Example 2 40.0 1.45 38.6 1.98 235 1.5 8 4 Partial coating (96.5%) (136%) with cobalt and aluminum
  • FIGS. 1 A to 1 E Images of the positive electrode active materials prepared in comparative examples 1-3 and examples 1-2 when observed with magnification using a scanning electron microscope (SEM) are shown in FIGS. 1 A to 1 E , respectively.
  • FIGS. 2 A to 2 C are an SEM image of comparative example 3, the content of cobalt in FIG. 2 A , and the content of aluminum in FIG. 2 A , respectively.
  • FIGS. 3 A to 3 C are an SEM image of example 1, the content of cobalt in FIG. 3 A , and the content of aluminum in FIG. 3 A , respectively.
  • D50 may be defined as a particle size at 50% of particle size distribution, and is measured using a laser diffraction method.
  • a lithium secondary battery half cell manufactured as below using the positive electrode active material prepared in each of example 1 and comparative examples 1 to 3 is charged at 0.5C, 45° C. in a CC—CV until 4.25V and discharged at 1.0 C constant current until 2.5V, and capacity retention in 50 cycles of the charge/discharge test is measured to evaluate the life characteristics.
  • the results are shown in Table 1.
  • the lithium secondary battery half cell is prepared as follows.
  • the positive electrode active material prepared in each of example 1 and comparative example 1, a carbon black conductive material and a PVdF binder are mixed at a weight ratio of 96:2:2 in an N-methylpyrrolidone solvent to prepare a positive electrode material mixture, and the positive electrode material mixture is coated on one surface of an aluminum current collector, dried at 100° C. and rolled to manufacture a positive electrode.
  • Lithium metal is used for a negative electrode.
  • An electrode assembly including the positive electrode and the negative electrode manufactured as described above and a porous polyethylene separator between the positive electrode and the negative electrode is made and placed in a case, and an electrolyte solution is injected into the case to manufacture a lithium secondary battery.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Composite Materials (AREA)
  • Materials Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Geology (AREA)
  • Battery Electrode And Active Subsutance (AREA)
US18/025,728 2020-11-10 2021-11-08 Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same Pending US20230348294A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
KR10-2020-0149674 2020-11-10
KR20200149674 2020-11-10
PCT/KR2021/016170 WO2022103105A1 (ko) 2020-11-10 2021-11-08 리튬 이차 전지용 양극 활물질, 그 제조방법 및 이를 포함하는 리튬 이차 전지

Publications (1)

Publication Number Publication Date
US20230348294A1 true US20230348294A1 (en) 2023-11-02

Family

ID=81601496

Family Applications (1)

Application Number Title Priority Date Filing Date
US18/025,728 Pending US20230348294A1 (en) 2020-11-10 2021-11-08 Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same

Country Status (6)

Country Link
US (1) US20230348294A1 (zh)
EP (1) EP4203100A1 (zh)
JP (1) JP2023542196A (zh)
KR (1) KR102667603B1 (zh)
CN (1) CN116057733A (zh)
WO (1) WO2022103105A1 (zh)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2023554627A (ja) * 2020-12-24 2023-12-28 エルジー エナジー ソリューション リミテッド リチウム二次電池用正極活物質、その製造方法、それを含む正極及びリチウム二次電池
CN114122385B (zh) * 2022-01-26 2022-04-26 瑞浦能源有限公司 一种锂离子电池用低钴三元正极材料及其制备方法、锂离子电池正极极片和锂离子电池
KR20240032661A (ko) * 2022-09-02 2024-03-12 주식회사 엘지화학 양극 활물질 전구체, 이의 제조 방법, 이를 이용한 양극 활물질의 제조 방법 및 양극 활물질
KR20240101438A (ko) * 2022-12-22 2024-07-02 주식회사 엘지에너지솔루션 양극 활물질, 이의 제조 방법, 이를 포함하는 양극 및 리튬 이차전지

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5971109B2 (ja) * 2011-12-20 2016-08-17 住友金属鉱山株式会社 ニッケル複合水酸化物とその製造方法、非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池
KR101785262B1 (ko) * 2013-07-08 2017-10-16 삼성에스디아이 주식회사 양극 활물질, 그 제조방법, 이를 채용한 양극 및 리튬이차전지
JP6624885B2 (ja) * 2015-02-19 2019-12-25 パナソニック株式会社 非水電解質二次電池用正極活物質及び非水電解質二次電池
KR102402388B1 (ko) * 2017-04-28 2022-05-26 삼성에스디아이 주식회사 양극 활물질, 이를 채용한 양극과 리튬 이차 전지, 및 상기 양극 활물질의 제조방법
KR102629461B1 (ko) * 2017-08-30 2024-01-26 삼성전자주식회사 복합양극활물질, 그 제조방법, 이를 포함한 양극 및 리튬전지
KR102460353B1 (ko) * 2017-11-06 2022-10-31 주식회사 엘지에너지솔루션 리튬 이차전지
KR102359103B1 (ko) * 2018-02-01 2022-02-08 주식회사 엘지에너지솔루션 이차전지용 양극 활물질, 그 제조방법 및 이를 포함하는 리튬 이차전지
JP6871888B2 (ja) * 2018-09-27 2021-05-19 住友化学株式会社 リチウム二次電池用正極活物質、リチウム二次電池用正極及びリチウム二次電池

Also Published As

Publication number Publication date
KR102667603B1 (ko) 2024-05-22
EP4203100A1 (en) 2023-06-28
JP2023542196A (ja) 2023-10-05
KR20220063757A (ko) 2022-05-17
CN116057733A (zh) 2023-05-02
WO2022103105A1 (ko) 2022-05-19

Similar Documents

Publication Publication Date Title
US20230348294A1 (en) Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same
US20240250254A1 (en) Positive Electrode Active Material for Lithium Secondary Battery and Lithium Secondary Battery Comprising the Same
US12100837B2 (en) Method of preparing positive electrode active material precursor and positive electrode active material precursor
US20240047668A1 (en) Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same, and Positive Electrode and Lithium Secondary Battery Comprising the Same
US20230303405A1 (en) Positive Electrode Active Material Precursor for Lithium Secondary Battery, Positive Electrode Active Material and Positive Electrode Comprising the Same
US20240132375A1 (en) Positive Electrode Active Material for Lithium Secondary Battery, Method for Manufacturing the Same, and Positive Electrode and Lithium Secondary Battery Comprising the Same
US20230339777A1 (en) Positive Electrode Active Material For Lithium Secondary Battery, Method For Preparing The Same And Lithium Secondary Battery Comprising The Same
US20230378456A1 (en) Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same
EP3984960B1 (en) Preparation method for positive electrode active material for secondary battery
US20240339597A1 (en) Positive Electrode for Lithium Secondary Battery and Positive Electrode and Lithium Secondary Battery Comprising the Same
US20240079584A1 (en) Positive Electrode Active Material For Lithium Secondary Battery, Method For Preparing Same, And Lithium Secondary Battery Comprising Same
US20230416113A1 (en) Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same
US20240030428A1 (en) Positive Electrode for Lithium Secondary Battery and Positive Electrode and Lithium Secondary Battery Comprising the Same
US20240105934A1 (en) Positive Electrode Active Material for Lithium Secondary Battery and Positive Electrode Material Mixture, Positive Electrode, Lithium Secondary Battery Comprising the Same
US20240018015A1 (en) Positive Electrode Active Material for Lithium Secondary Battery, Method for Preparing the Same and Lithium Secondary Battery Comprising the Same
EP4411876A1 (en) Cathode material, and cathode and lithium secondary battery comprising same
KR20220092244A (ko) 리튬 이차 전지용 양극 활물질, 그 제조방법, 이를 포함하는 양극 및 리튬 이차 전지
KR20220013166A (ko) 양극 활물질 전구체 및 이의 제조 방법

Legal Events

Date Code Title Description
AS Assignment

Owner name: LG ENERGY SOLUTION, LTD., KOREA, REPUBLIC OF

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HEO, JONG-WOOK;KIM, JI-HYE;YOO, TAE-GU;AND OTHERS;REEL/FRAME:062960/0946

Effective date: 20230106

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION