US20190319223A1 - Partition member, assembled battery and method for controlling heat transfer in an assembled battery - Google Patents
Partition member, assembled battery and method for controlling heat transfer in an assembled battery Download PDFInfo
- Publication number
- US20190319223A1 US20190319223A1 US16/452,587 US201916452587A US2019319223A1 US 20190319223 A1 US20190319223 A1 US 20190319223A1 US 201916452587 A US201916452587 A US 201916452587A US 2019319223 A1 US2019319223 A1 US 2019319223A1
- Authority
- US
- United States
- Prior art keywords
- partition member
- single cell
- cells
- cell
- thermal resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 238000005192 partition Methods 0.000 title claims abstract description 244
- 238000012546 transfer Methods 0.000 title claims description 30
- 238000000034 method Methods 0.000 title claims description 15
- 230000014509 gene expression Effects 0.000 claims abstract description 86
- 238000010438 heat treatment Methods 0.000 claims description 52
- 230000002159 abnormal effect Effects 0.000 claims description 44
- 230000002829 reductive effect Effects 0.000 claims description 18
- 239000000463 material Substances 0.000 description 72
- 230000000052 comparative effect Effects 0.000 description 50
- 125000006850 spacer group Chemical group 0.000 description 21
- 229920005989 resin Polymers 0.000 description 18
- 239000011347 resin Substances 0.000 description 18
- -1 polyethylene Polymers 0.000 description 16
- 238000002844 melting Methods 0.000 description 11
- 230000008018 melting Effects 0.000 description 11
- 239000008151 electrolyte solution Substances 0.000 description 10
- 229940021013 electrolyte solution Drugs 0.000 description 10
- 238000001816 cooling Methods 0.000 description 9
- HBBGRARXTFLTSG-UHFFFAOYSA-N Lithium ion Chemical compound [Li+] HBBGRARXTFLTSG-UHFFFAOYSA-N 0.000 description 7
- 239000002131 composite material Substances 0.000 description 7
- 238000010586 diagram Methods 0.000 description 7
- 238000005516 engineering process Methods 0.000 description 7
- 229910001416 lithium ion Inorganic materials 0.000 description 7
- 239000004743 Polypropylene Substances 0.000 description 6
- 238000000354 decomposition reaction Methods 0.000 description 6
- 239000007788 liquid Substances 0.000 description 6
- 229920001155 polypropylene Polymers 0.000 description 6
- 230000008859 change Effects 0.000 description 5
- 238000006243 chemical reaction Methods 0.000 description 5
- 239000000126 substance Substances 0.000 description 5
- 239000011248 coating agent Substances 0.000 description 4
- 238000000576 coating method Methods 0.000 description 4
- 239000002826 coolant Substances 0.000 description 4
- 239000013078 crystal Substances 0.000 description 4
- 230000020169 heat generation Effects 0.000 description 4
- 229910052751 metal Inorganic materials 0.000 description 4
- 239000002184 metal Substances 0.000 description 4
- 239000004417 polycarbonate Substances 0.000 description 4
- 229920000515 polycarbonate Polymers 0.000 description 4
- 239000007774 positive electrode material Substances 0.000 description 4
- LYCAIKOWRPUZTN-UHFFFAOYSA-N Ethylene glycol Chemical compound OCCO LYCAIKOWRPUZTN-UHFFFAOYSA-N 0.000 description 3
- 239000004698 Polyethylene Substances 0.000 description 3
- 238000004458 analytical method Methods 0.000 description 3
- 238000009835 boiling Methods 0.000 description 3
- 230000015556 catabolic process Effects 0.000 description 3
- 239000004020 conductor Substances 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 238000011156 evaluation Methods 0.000 description 3
- 230000004907 flux Effects 0.000 description 3
- 239000000155 melt Substances 0.000 description 3
- 229920000573 polyethylene Polymers 0.000 description 3
- 238000007789 sealing Methods 0.000 description 3
- 230000007480 spreading Effects 0.000 description 3
- 230000001629 suppression Effects 0.000 description 3
- KMTRUDSVKNLOMY-UHFFFAOYSA-N Ethylene carbonate Chemical compound O=C1OCCO1 KMTRUDSVKNLOMY-UHFFFAOYSA-N 0.000 description 2
- PEDCQBHIVMGVHV-UHFFFAOYSA-N Glycerine Chemical compound OCC(O)CO PEDCQBHIVMGVHV-UHFFFAOYSA-N 0.000 description 2
- WHXSMMKQMYFTQS-UHFFFAOYSA-N Lithium Chemical compound [Li] WHXSMMKQMYFTQS-UHFFFAOYSA-N 0.000 description 2
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 2
- 239000004962 Polyamide-imide Substances 0.000 description 2
- 239000004793 Polystyrene Substances 0.000 description 2
- 239000011358 absorbing material Substances 0.000 description 2
- 229940081735 acetylcellulose Drugs 0.000 description 2
- 229920000122 acrylonitrile butadiene styrene Polymers 0.000 description 2
- 239000000956 alloy Substances 0.000 description 2
- 229910045601 alloy Inorganic materials 0.000 description 2
- 229910052782 aluminium Inorganic materials 0.000 description 2
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 2
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 2
- 230000005540 biological transmission Effects 0.000 description 2
- 229920002301 cellulose acetate Polymers 0.000 description 2
- 239000000919 ceramic Substances 0.000 description 2
- 239000000470 constituent Substances 0.000 description 2
- JBTWLSYIZRCDFO-UHFFFAOYSA-N ethyl methyl carbonate Chemical compound CCOC(=O)OC JBTWLSYIZRCDFO-UHFFFAOYSA-N 0.000 description 2
- 239000002360 explosive Substances 0.000 description 2
- 239000004088 foaming agent Substances 0.000 description 2
- 238000005755 formation reaction Methods 0.000 description 2
- 239000011521 glass Substances 0.000 description 2
- 229910052744 lithium Inorganic materials 0.000 description 2
- 229910052760 oxygen Inorganic materials 0.000 description 2
- 239000001301 oxygen Substances 0.000 description 2
- 229920002312 polyamide-imide Polymers 0.000 description 2
- 229920006324 polyoxymethylene Polymers 0.000 description 2
- 229920002223 polystyrene Polymers 0.000 description 2
- 239000004800 polyvinyl chloride Substances 0.000 description 2
- 229920000915 polyvinyl chloride Polymers 0.000 description 2
- 239000011253 protective coating Substances 0.000 description 2
- 238000011160 research Methods 0.000 description 2
- 230000004044 response Effects 0.000 description 2
- 230000000630 rising effect Effects 0.000 description 2
- 238000005979 thermal decomposition reaction Methods 0.000 description 2
- VZXTWGWHSMCWGA-UHFFFAOYSA-N 1,3,5-triazine-2,4-diamine Chemical compound NC1=NC=NC(N)=N1 VZXTWGWHSMCWGA-UHFFFAOYSA-N 0.000 description 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 1
- 229920000298 Cellophane Polymers 0.000 description 1
- 239000004709 Chlorinated polyethylene Substances 0.000 description 1
- 239000004641 Diallyl-phthalate Substances 0.000 description 1
- OIFBSDVPJOWBCH-UHFFFAOYSA-N Diethyl carbonate Chemical compound CCOC(=O)OCC OIFBSDVPJOWBCH-UHFFFAOYSA-N 0.000 description 1
- 229920000219 Ethylene vinyl alcohol Polymers 0.000 description 1
- 229910004424 Li(Ni0.8Co0.15Al0.05)O2 Inorganic materials 0.000 description 1
- 229920000106 Liquid crystal polymer Polymers 0.000 description 1
- 239000004977 Liquid-crystal polymers (LCPs) Substances 0.000 description 1
- 239000000020 Nitrocellulose Substances 0.000 description 1
- 239000004677 Nylon Substances 0.000 description 1
- 239000002033 PVDF binder Substances 0.000 description 1
- 229930040373 Paraformaldehyde Natural products 0.000 description 1
- 239000004696 Poly ether ether ketone Substances 0.000 description 1
- 239000004952 Polyamide Substances 0.000 description 1
- 239000005062 Polybutadiene Substances 0.000 description 1
- 239000004642 Polyimide Substances 0.000 description 1
- 239000004734 Polyphenylene sulfide Substances 0.000 description 1
- 239000004372 Polyvinyl alcohol Substances 0.000 description 1
- 229920001328 Polyvinylidene chloride Polymers 0.000 description 1
- 239000004809 Teflon Substances 0.000 description 1
- 229920006362 Teflon® Polymers 0.000 description 1
- 239000004699 Ultra-high molecular weight polyethylene Substances 0.000 description 1
- 229920001807 Urea-formaldehyde Polymers 0.000 description 1
- SMEGJBVQLJJKKX-HOTMZDKISA-N [(2R,3S,4S,5R,6R)-5-acetyloxy-3,4,6-trihydroxyoxan-2-yl]methyl acetate Chemical compound CC(=O)OC[C@@H]1[C@H]([C@@H]([C@H]([C@@H](O1)O)OC(=O)C)O)O SMEGJBVQLJJKKX-HOTMZDKISA-N 0.000 description 1
- FJWGYAHXMCUOOM-QHOUIDNNSA-N [(2s,3r,4s,5r,6r)-2-[(2r,3r,4s,5r,6s)-4,5-dinitrooxy-2-(nitrooxymethyl)-6-[(2r,3r,4s,5r,6s)-4,5,6-trinitrooxy-2-(nitrooxymethyl)oxan-3-yl]oxyoxan-3-yl]oxy-3,5-dinitrooxy-6-(nitrooxymethyl)oxan-4-yl] nitrate Chemical compound O([C@@H]1O[C@@H]([C@H]([C@H](O[N+]([O-])=O)[C@H]1O[N+]([O-])=O)O[C@H]1[C@@H]([C@@H](O[N+]([O-])=O)[C@H](O[N+]([O-])=O)[C@@H](CO[N+]([O-])=O)O1)O[N+]([O-])=O)CO[N+](=O)[O-])[C@@H]1[C@@H](CO[N+]([O-])=O)O[C@@H](O[N+]([O-])=O)[C@H](O[N+]([O-])=O)[C@H]1O[N+]([O-])=O FJWGYAHXMCUOOM-QHOUIDNNSA-N 0.000 description 1
- XYLMUPLGERFSHI-UHFFFAOYSA-N alpha-Methylstyrene Chemical compound CC(=C)C1=CC=CC=C1 XYLMUPLGERFSHI-UHFFFAOYSA-N 0.000 description 1
- 230000008901 benefit Effects 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- QUDWYFHPNIMBFC-UHFFFAOYSA-N bis(prop-2-enyl) benzene-1,2-dicarboxylate Chemical compound C=CCOC(=O)C1=CC=CC=C1C(=O)OCC=C QUDWYFHPNIMBFC-UHFFFAOYSA-N 0.000 description 1
- 229920005549 butyl rubber Polymers 0.000 description 1
- OJIJEKBXJYRIBZ-UHFFFAOYSA-N cadmium nickel Chemical compound [Ni].[Cd] OJIJEKBXJYRIBZ-UHFFFAOYSA-N 0.000 description 1
- 238000007707 calorimetry Methods 0.000 description 1
- 229910052799 carbon Inorganic materials 0.000 description 1
- 238000004891 communication Methods 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 238000006731 degradation reaction Methods 0.000 description 1
- 238000013461 design Methods 0.000 description 1
- IEJIGPNLZYLLBP-UHFFFAOYSA-N dimethyl carbonate Chemical compound COC(=O)OC IEJIGPNLZYLLBP-UHFFFAOYSA-N 0.000 description 1
- 230000005518 electrochemistry Effects 0.000 description 1
- 239000003792 electrolyte Substances 0.000 description 1
- 239000003822 epoxy resin Substances 0.000 description 1
- 150000002170 ethers Chemical class 0.000 description 1
- 239000012530 fluid Substances 0.000 description 1
- HDNHWROHHSBKJG-UHFFFAOYSA-N formaldehyde;furan-2-ylmethanol Chemical compound O=C.OCC1=CC=CO1 HDNHWROHHSBKJG-UHFFFAOYSA-N 0.000 description 1
- 239000007849 furan resin Substances 0.000 description 1
- 235000011187 glycerol Nutrition 0.000 description 1
- LNEPOXFFQSENCJ-UHFFFAOYSA-N haloperidol Chemical compound C1CC(O)(C=2C=CC(Cl)=CC=2)CCN1CCCC(=O)C1=CC=C(F)C=C1 LNEPOXFFQSENCJ-UHFFFAOYSA-N 0.000 description 1
- 238000009413 insulation Methods 0.000 description 1
- 150000002576 ketones Chemical class 0.000 description 1
- 230000007246 mechanism Effects 0.000 description 1
- 230000001404 mediated effect Effects 0.000 description 1
- 150000002739 metals Chemical class 0.000 description 1
- 125000005395 methacrylic acid group Chemical group 0.000 description 1
- 239000000203 mixture Substances 0.000 description 1
- 239000007773 negative electrode material Substances 0.000 description 1
- 229910000652 nickel hydride Inorganic materials 0.000 description 1
- 229920001220 nitrocellulos Polymers 0.000 description 1
- JFNLZVQOOSMTJK-KNVOCYPGSA-N norbornene Chemical compound C1[C@@H]2CC[C@H]1C=C2 JFNLZVQOOSMTJK-KNVOCYPGSA-N 0.000 description 1
- 229920001778 nylon Polymers 0.000 description 1
- 230000003647 oxidation Effects 0.000 description 1
- 238000007254 oxidation reaction Methods 0.000 description 1
- 239000003208 petroleum Substances 0.000 description 1
- 229920001568 phenolic resin Polymers 0.000 description 1
- 239000005011 phenolic resin Substances 0.000 description 1
- 229920000083 poly(allylamine) Polymers 0.000 description 1
- 229920001200 poly(ethylene-vinyl acetate) Polymers 0.000 description 1
- 229920002492 poly(sulfone) Polymers 0.000 description 1
- 229920002037 poly(vinyl butyral) polymer Polymers 0.000 description 1
- 229920002239 polyacrylonitrile Polymers 0.000 description 1
- 229920002647 polyamide Polymers 0.000 description 1
- 229920001230 polyarylate Polymers 0.000 description 1
- 229920002857 polybutadiene Polymers 0.000 description 1
- 229920001083 polybutene Polymers 0.000 description 1
- 229920001707 polybutylene terephthalate Polymers 0.000 description 1
- 229920000647 polyepoxide Polymers 0.000 description 1
- 229920000728 polyester Polymers 0.000 description 1
- 229920006393 polyether sulfone Polymers 0.000 description 1
- 229920002530 polyetherether ketone Polymers 0.000 description 1
- 229920001601 polyetherimide Polymers 0.000 description 1
- 229920000139 polyethylene terephthalate Polymers 0.000 description 1
- 239000005020 polyethylene terephthalate Substances 0.000 description 1
- 229920001721 polyimide Polymers 0.000 description 1
- 229920000306 polymethylpentene Polymers 0.000 description 1
- 239000011116 polymethylpentene Substances 0.000 description 1
- 229920001955 polyphenylene ether Polymers 0.000 description 1
- 229920000069 polyphenylene sulfide Polymers 0.000 description 1
- 229920002689 polyvinyl acetate Polymers 0.000 description 1
- 239000011118 polyvinyl acetate Substances 0.000 description 1
- 229920002451 polyvinyl alcohol Polymers 0.000 description 1
- 229920001289 polyvinyl ether Polymers 0.000 description 1
- 229920002620 polyvinyl fluoride Polymers 0.000 description 1
- 239000005033 polyvinylidene chloride Substances 0.000 description 1
- 229920002981 polyvinylidene fluoride Polymers 0.000 description 1
- 230000002250 progressing effect Effects 0.000 description 1
- 230000001681 protective effect Effects 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 238000000638 solvent extraction Methods 0.000 description 1
- 230000006641 stabilisation Effects 0.000 description 1
- 238000011105 stabilization Methods 0.000 description 1
- 229920000638 styrene acrylonitrile Polymers 0.000 description 1
- 230000005469 synchrotron radiation Effects 0.000 description 1
- BFKJFAAPBSQJPD-UHFFFAOYSA-N tetrafluoroethene Chemical group FC(F)=C(F)F BFKJFAAPBSQJPD-UHFFFAOYSA-N 0.000 description 1
- 229920002725 thermoplastic elastomer Polymers 0.000 description 1
- 229920002803 thermoplastic polyurethane Polymers 0.000 description 1
- 229920001187 thermosetting polymer Polymers 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
- 229920000785 ultra high molecular weight polyethylene Polymers 0.000 description 1
- 229920006337 unsaturated polyester resin Polymers 0.000 description 1
- 238000012795 verification Methods 0.000 description 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 1
Images
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/61—Types of temperature control
- H01M10/617—Types of temperature control for achieving uniformity or desired distribution of temperature
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/20—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders
- H01M50/289—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders characterised by spacing elements or positioning means within frames, racks or packs
-
- H01M2/028—
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/42—Methods or arrangements for servicing or maintenance of secondary cells or secondary half-cells
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/62—Heating or cooling; Temperature control specially adapted for specific applications
- H01M10/625—Vehicles
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/62—Heating or cooling; Temperature control specially adapted for specific applications
- H01M10/627—Stationary installations, e.g. power plant buffering or backup power supplies
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/64—Heating or cooling; Temperature control characterised by the shape of the cells
- H01M10/647—Prismatic or flat cells, e.g. pouch cells
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/65—Means for temperature control structurally associated with the cells
- H01M10/651—Means for temperature control structurally associated with the cells characterised by parameters specified by a numeric value or mathematical formula, e.g. ratios, sizes or concentrations
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/65—Means for temperature control structurally associated with the cells
- H01M10/653—Means for temperature control structurally associated with the cells characterised by electrically insulating or thermally conductive materials
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/65—Means for temperature control structurally associated with the cells
- H01M10/655—Solid structures for heat exchange or heat conduction
- H01M10/6554—Rods or plates
- H01M10/6555—Rods or plates arranged between the cells
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/60—Heating or cooling; Temperature control
- H01M10/65—Means for temperature control structurally associated with the cells
- H01M10/658—Means for temperature control structurally associated with the cells by thermal insulation or shielding
-
- H01M2/0262—
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/20—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/20—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders
- H01M50/204—Racks, modules or packs for multiple batteries or multiple cells
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/20—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders
- H01M50/249—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders specially adapted for aircraft or vehicles, e.g. cars or trains
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/20—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders
- H01M50/289—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders characterised by spacing elements or positioning means within frames, racks or packs
- H01M50/291—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders characterised by spacing elements or positioning means within frames, racks or packs characterised by their shape
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/20—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders
- H01M50/289—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders characterised by spacing elements or positioning means within frames, racks or packs
- H01M50/293—Mountings; Secondary casings or frames; Racks, modules or packs; Suspension devices; Shock absorbers; Transport or carrying devices; Holders characterised by spacing elements or positioning means within frames, racks or packs characterised by the material
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M2220/00—Batteries for particular applications
- H01M2220/10—Batteries in stationary systems, e.g. emergency power source in plant
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M2220/00—Batteries for particular applications
- H01M2220/20—Batteries in motive systems, e.g. vehicle, ship, plane
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
- Y02E60/10—Energy storage using batteries
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y02T10/00—Road transport of goods or passengers
- Y02T10/60—Other road transportation technologies with climate change mitigation effect
- Y02T10/70—Energy storage systems for electromobility, e.g. batteries
Definitions
- the present invention relates to a partition member, to an assembled battery and to a method for controlling heat transfer in an assembled battery.
- the surface temperature of the battery in the case of damage to the secondary battery, for instance due to overcharge or internal short-circuits may exceed several hundred ° C., and reach about 1000° C.
- Secondary batteries that are used as power sources for instance in vehicles are generally utilized in the form of assembled batteries made up of a plurality of single cells (hereafter also referred to as “cells”); accordingly, in a case where such a temperature region is arrived at due to damage to one of the constituent battery cells, battery cells adjacent thereto may become damaged due to the generated heat, the damage spreading thereupon in a positive-feedback fashion throughout the assembled battery.
- technologies have been proposed that involve cooling the damaged battery cells or suppressing flow of heat from damaged battery cells to undamaged battery cells.
- PTL 1 addresses a method for cooling an abnormally heated battery.
- PTL 1 discloses a battery module wherein cooling units are provided in which a cooling material is accommodated in the vicinity of single cells, each cooling unit having a sealing portion that is formed through sealing of a sheet-shaped portion, and wherein an openable portion is provided, in part of the sealing portion, which becomes open upon abnormal heating of the single cells.
- PTL 2 addresses the structure of a coolant storage part for cooling of a battery having heated up abnormally, and a coolant release mechanism.
- a battery module provided with: a battery unit made up of a plurality of single cells; a case having a storage part that has an open end on at least one surface, such that the battery unit is accommodated in the storage part; a lid body having an opening, and which covers the open end of the case; and a heat-absorbing member having a heat-absorbing material and an exterior film that encloses the heat-absorbing material, the heat-absorbing member being provided in contact with a side face of the battery unit, wherein the outer film has a multilayer structure that includes a resin layer and a metal film having a higher melting point than the softening temperature of the resin layer, and which melts due to heat generated by the single cells.
- PTL 3 discloses a method in which a partition member that is disposed between battery cells is configured out of a meltable base material and a thermosetting resin, such that transfer of heat from an abnormally heated battery cell to an adjacent battery cell is reduced through suppression of heat conduction, by the partition member, due to melting of the base material.
- PTL 4 discloses a method wherein a partition member that is disposed between electric storage elements is configured to have a base material formed of a resin, and a foaming agent held in the base material and which undergoes thermal decomposition in response to a rise in temperature derived from generation of heat by the electric storage elements, so that transfer of heat from an abnormally heated battery cell to an adjacent battery cell is suppressed as a result.
- PTL 1 discloses a detailed study on a method for cooling an abnormally heated battery, but the quantity of heat generated by abnormally heated cells and the cooling capacity of a coolant are not quantitatively addressed.
- PTL 2 discloses a detailed study on a method for cooling an abnormally heated battery, but the quantity of heat generated by abnormally heated cells and the cooling capacity of a coolant are not quantitatively addressed.
- bus bars which are good heat conductors, are ordinarily used in bus bars, and hence it is not conceivable that transfer of heat between battery cells can be avoided by means of the bus bars, even upon suppression of transfer of heat between the battery cells due to melting of the base material of the partition members that are disposed between the battery cells.
- the inventors focused on thermal resistance values, not addressed in conventional technologies, that are necessary for preventing positive-feedback damage between battery cells, and studied in detail conditions pertaining to the thermal resistance values.
- the inventors found that in a partition member which has two surfaces in the thickness direction, and which separates single cells that make up an assembled battery, it is important to control properly a thermal resistance value depending on whether the average temperatures of the two surfaces are comparable to cell temperature in a normal state, or whether the average temperatures of the two surfaces are comparable to cell temperature in an abnormal heating state, and arrived at the present invention on the basis of that finding.
- the embodiments of the present invention is as follows.
- a partition member which has two surfaces in a thickness direction, and which separates single cells that make up an assembled battery
- An assembled battery comprising the partition member according to any one of [1] to [4].
- An assembled battery comprising:
- a plurality of single cells including a first single cell, a second single cell and a third single cell
- first partition member that separates the first single cell from the second single cell
- second partition member that separates the second single cell from the third single cell
- the partition member has two surfaces in a thickness direction, one of the surfaces being a first surface opposing a first single cell and the other surface being a second surface opposing a second single cell;
- FIG. 1 is a diagram illustrating an example of a partition member.
- FIG. 2 is a diagram illustrating an example of a partition member having a comb-shaped structure.
- FIG. 3 is a diagram illustrating an example of an assembled battery.
- FIG. 4 is a diagram illustrating an example of heat transfer paths in an assembled battery.
- FIG. 5 is an example of a bag-like structure, being an example of an embodiment of the present invention.
- FIG. 6 is a variation of a bag-like structure, being an example of an embodiment of the present invention.
- FIG. 7 is a graph illustrating changes in temperature in the interior of cells in Comparative example 1.
- FIG. 8 is a graph illustrating the evolution of surface average temperature of partition members in Comparative example 1.
- FIG. 9 is a set of graphs illustrating the evolution of thermal resistance of partition members in Comparative example 1.
- FIG. 10 is a graph illustrating changes in temperature in the interior of cells in Example 1.
- FIG. 11 is a graph illustrating the evolution of surface average temperature of partition members in Example 1.
- FIG. 12 is a set of graphs illustrating the evolution of thermal resistance of partition members in Example 1.
- FIG. 13 is a graph illustrating changes in temperature in the interior of cells in Comparative example 2.
- FIG. 14 is a graph illustrating the evolution of surface average temperature of partition members in Comparative example 2.
- FIG. 15 is a set of graphs illustrating the evolution of thermal resistance of partition members in Comparative example 2.
- FIG. 16 is a graph illustrating changes in temperature in the interior of cells in Comparative example 3.
- FIG. 17 is a graph illustrating the evolution of surface average temperature of partition members in Comparative example 3.
- FIG. 18 is a set of graphs illustrating the evolution of thermal resistance of partition members in Comparative example 3.
- FIG. 19 is a graph illustrating changes in temperature in the interior of cells in Comparative example 4.
- FIG. 20 is a graph illustrating the evolution of surface average temperature of partition members in Comparative example 4.
- FIG. 21 is a set of graphs illustrating the evolution of thermal resistance of partition members in Comparative example 4.
- the partition member according to the present invention is a partition member that separates single cells that make up an assembled battery.
- the partition member which separates single cells that make up an assembled battery, has two surfaces in the thickness direction, wherein when the average temperature of one of the two surfaces exceeds 180° C., a thermal resistance per unit area ( ⁇ 1 ) in the thickness direction satisfies Expression 1 below; and when the average temperatures of both of the two surface do not exceed 80° C., a thermal resistance per unit area ( ⁇ 2 ) in the thickness direction satisfies Expression 2 below.
- ⁇ 1 is 1.0 ⁇ 10 ⁇ 2 or greater and more preferably 2.0 ⁇ 10 ⁇ 2 or greater.
- ⁇ 2 is preferably 2.0 ⁇ 10 ⁇ 3 or smaller and more preferably 1.0 ⁇ 10 ⁇ 3 or smaller.
- the thermal resistance per unit area ( ⁇ 1 ) satisfies Expression 1 above, and when the average temperatures of both of two surfaces do not exceed 100° C., the thermal resistance per unit area ( ⁇ 2 ) satisfies Expression 2 above.
- FIG. 1 is a diagram illustrating an example of a partition member.
- FIG. 1 illustrates a rectangular parallelepiped (plate body) partition member 1 (referred to as partition member 1 A in the explanation of FIG. 1 ) having length, width and thickness (depth).
- the partition member 1 A has two surfaces, namely a surface 1 a and a surface 1 b opposing each other in the thickness direction.
- the partition member 1 A is disposed between respective single cells that make up an assembled battery, in order to partition the single cells from each other.
- the surface 1 a and the surface 1 b are brought to a state in which the foregoing oppose respective single cells to be partitioned.
- the surface 1 a and the surface 1 b can be used as “two thickness-direction surfaces that partition single cells making up an assembled battery”.
- one of the “two thickness-direction surfaces that partition single cells making up an assembled battery”, may in some instances not oppose a single cell.
- the thermal resistance per unit area ( ⁇ ) of a partition member is referred to as heat transfer resistance per unit cross-sectional area of the partition member in the thickness direction.
- the thermal resistance per unit area ( ⁇ ) of the partition member can be expressed using the thermal conductivity (k (W/m ⁇ K)) in the thickness direction of the material used as the partition member and using the thickness (d (m)) of the partition member.
- the thermal resistance per unit area ( ⁇ ) of the partition member 1 A illustrated in FIG. 1 will be explained next. To make the explanation simpler, the partition member 1 A will be assumed to be formed out of a single material and to have constant density.
- k (W/m ⁇ K) denotes the thermal conductivity of the partition member 1 A in the thickness direction and d (m) denotes the thickness of the partition member 1 A.
- T 1 (° C.) denotes the average value of surface temperature of the surface 1 b of the partition member 1 A
- T 2 (° C.) denotes the average value of the surface temperature of the surface 1 a.
- a surface temperature difference T 1 ⁇ T 2 arises between the surface 1 b side and the surface 1 a side of the partition member 1 A in a case where T 2 is lower than T 1 .
- the heat flow rate (heat flux) q per unit cross-sectional area of the partition member 1 A can be given by Expression (1) below.
- the heat flux (q) can be expressed herein by Expression (2) below, using the thermal resistance per unit area ( ⁇ ).
- the thermal resistance per unit area ( ⁇ ) can be expressed using the thermal conductivity (k) of the partition member 1 A in the thickness direction and the thickness (d) of the partition member. That is, the thermal resistance per unit area ( ⁇ ) can be given by Expression (3) below.
- the shape (structure) of the partition member 1 is not limited to a rectangular parallelepiped. So long as the partition member 1 is shaped to have a thickness direction, the thermal resistance of the partition member 1 can be expressed by Expression (3) also in a case where the partition member has for instance a comb-type structure, a hollow structure or a lattice structure.
- the partition member 1 is not limited to being formed out of single material, and may be formed of a combination of a plurality of materials.
- the thermal resistance per unit area of the partition member 1 can be given by Expression (3) above also in a case where the partition member 1 is formed of a combination of a plurality of materials.
- polyethylene chlorinated polyethylene, ethylene-vinyl chloride copolymers, ethylene-vinyl acetate copolymers, polyvinyl acetate, polypropylene, polybutene, polybutadiene, polymethylpentene, polystyrene, poly ⁇ -methylstyrene, poly(p-vinyl phenol), ABS resins, SAN resins, AES resins, AAS resins, methacrylic resins, norbornene resins, PVC, acrylic-modified polyvinyl chloride, polyvinylidene chloride, polyallylamine, polyvinyl ether, polyvinyl alcohol, ethylene vinyl alcohol copolymers, petroleum resins, thermoplastic elastomers, thermoplastic polyurethane resins, polyacrylonitrile, polyvinyl butyral, phenolic resins, epoxy resins, urea resins, melafine resins,
- FIG. 2 illustrates an example of a partition member 1 (referred to as partition member 1 B in the explanation of FIG. 2 ) having a comb-type structure.
- the partition member 1 B is formed to have overall a plate-like shape the cross section of which has a comb shape.
- the partition member 1 B as well has two surfaces, namely a surface 1 c and a surface 1 d opposing each other in the thickness direction.
- the surface 1 c is a surface having stripe-like crenellations, while the surface 1 d is a flat surface.
- the cross section resulting from cutting the partition member 1 B along a plane in the thickness direction is a comb shape.
- the surface 1 c and the surface 1 d can be treated in the same manner as the surface 1 a and the surface 1 b.
- the thermal resistance per unit area ( ⁇ ) of the partition member 1 B illustrated in FIG. 2 can be worked out as follows.
- the average temperatures at the surface 1 c and the surface 1 d can be used as T 1 and T 2 in Expression (1) and Expression (2) above.
- the average value of heat flow rate per unit cross-sectional area of the partition member 1 B can be used as the heat flux (q) in Expression (1) and Expression (2) above.
- the thermal resistance per unit area ( ⁇ ) can be expressed using Expression (3) above by using, as the thermal conductivity (k) in Expression (1) and Expression (3), a combined thermal conductivity that is calculated taking into consideration the structure and material types of the partition member 1 B.
- the thermal resistance per unit area ( ⁇ ) an effective thermal resistance per unit area, which is calculated with consideration of the structure and material types of the partition member 1 B, can be used.
- R n thermal resistance
- the thermal resistance (R) can be given by Expression (4) below.
- R R 1 +R 2 +R 3 + . . . +R n (4)
- a combined thermal conductivity of the composite member in a case where n types of material are arrayed in series will be calculated next.
- Expression (7) is obtained by rewriting Expression (4) using Expression (6) and Expression (3).
- the combined thermal conductivity ( ⁇ ) can be expressed as follows using Expression (7) and Expression (8).
- the combined thermal conductivity of a composite member in a case where n types of material are arrayed in parallel will be calculated next.
- the thermal resistance (R n ) of each material can be expressed as follows using a respective thermal resistance ( ⁇ n ) per unit cross-sectional area, with A n (m 2 ) denoting the respective cross-sectional area of the n types of material in the heat transfer direction.
- Expression (10) below is obtained by rewriting Expression (5) using Expression (9) and Expression (3).
- the combined thermal conductivity ( ⁇ ) of the composite member can be expressed as given by Expression (11) below, since the total cross-sectional area of the composite member is herein ⁇ A n .
- the combined thermal conductivity ( ⁇ ) can be expressed as follows using Expression (10) and Expression (11).
- the combined thermal conductivity can be calculated, even when the partition member 1 B is a partition member of comb-shaped structure such as the partition member 1 B, or a partition member of hollow structure, lattice structure or the like, on the basis of the thermal conductivity of air, being the material of hollow portions, and on the basis of the thickness and cross-sectional area of the hollow portions.
- the thickness-direction thermal conductivity is preferably 2.0 ⁇ 10 ⁇ 2 W/m ⁇ K or more and 2.0 W/m ⁇ K or less, and when the average temperature of that surface (for instance any one of surfaces 1 a to 1 d ) does not exceed 80° C., the thickness-direction thermal conductivity is preferably 5.0 ⁇ 10 ⁇ 2 W/m ⁇ K or more and 50 W/m ⁇ K or less.
- the thickness of the partition member 1 is preferably L/50 mm to L/10 mm, where L is the thickness of each single cell that makes up the assembled battery.
- L is the thickness of each single cell that makes up the assembled battery.
- a conceivable range of the thickness (L) of each single cell that makes up the assembled battery assembled battery is ordinarily herein 10 mm ⁇ L ⁇ 100 mm, preferably 15 mm ⁇ L ⁇ 80 mm.
- partition member is suitable as the partition member of the present invention or not can be checked in the manner described below.
- the barycenter of the partition member to be checked is worked out.
- a perpendicular line is drawn from the barycenter to one face of the partition member, and the obtained intersection point is taken as a first point.
- Heating is then performed so that entire surface that encompasses the first point is heated to 160° C.
- the heating method is not particularly limited, so long as heating can be performed through control of the temperature so that the entire surface including a given first point is at 160° C. to 300° C.
- the temperature of the surface including the first point is raised from 160° C. to 300° C., on the basis of the first point and the second point.
- the thermal resistance ( ⁇ 1 ) is then worked out in accordance with the method described above, when the temperature of the entire system reaches a steady state, at temperatures of 160° C., 180° C., 210° C., 240° C., 270° C. and 300° C.
- the entire surface including the first point is heated at 100° C.
- the heating method is not particularly limited, so long as heating can be performed through control of the temperature so that the entire surface including the above first point lies in the range of 20° C. to 1000° C.
- the temperature of the surface including the first point is lowered from 100° C. to 20° C., on the basis of the first point and the second point.
- the thermal resistance ( ⁇ 2 ) is then worked out in accordance with the method described above, when the temperature of the entire system reaches a steady state, at temperatures of 80° C., 60° C., 40° C. and 20° C.
- the partition member 1 is one constituent element that makes up an assembled battery.
- the assembled battery that can be used in the present invention is utilized in a battery pack mounted for instance in electric vehicles (EVs), hybrid electric vehicles (HEVs), plug-in hybrid electric vehicles (PHEVs), electric heavy equipment, electric bikes, electrically assisted bicycles, ships, aircraft, trains, uninterruptible power supplies (UPSs), household storage systems, and storage battery systems for stabilization of electric power systems that utilize renewable energy such as wind power, solar power, tidal power, and geothermal power.
- the assembled battery can also be used as a power source for supplying power to equipment other than the abovementioned EVs and so forth.
- FIG. 3 is a diagram illustrating an example of an assembled battery.
- FIG. 3 illustrates a three-cell connected simple battery pack as the assembled battery 10 .
- the assembled battery is formed through connection of a number of single cells (also referred to as cells) corresponding to the desired output power, in series, in parallel, or in a combination thereof.
- the number of cells is set as appropriate depending on the requested power.
- the single cells are connected in series, with a partition member disposed between respective single cells.
- the assembled battery 10 in the example of the assembled battery 10 depicted in FIG. 3 has: a cell 21 (Cell 1 : first single cell), a cell 22 (Cells 2 : second single cell) and a cell 23 (Cell 3 : third single cell); as well as a partition member 11 (Spacer 1: first partition member) and a partition member 12 (Spacer 2: second partition member) disposed between respective cells and which partition the cells from each other.
- the assembled battery 10 is provided with bus bars 3 and a case 4 .
- the partition member 11 and the partition member 12 will be referred to as partition members 1 in the explanation below.
- the cell 21 , cells 22 and cell 23 will be notated as cells 2 .
- the first single cell, second single cell and third single cell, as well as the first partition member and the second partition member obey a relative positional relationship such as the one illustrated in FIG. 3 .
- a given single cell reaches an abnormal heating state, that single cell is regarded as the first single cell, to determine thus the second single cell, third single cell, first partition member and second partition member.
- the cells 2 are each a lithium ion secondary battery cell provided for instance with a positive electrode and a negative electrode capable of storing and releasing lithium ions, and with an electrolyte.
- secondary batteries such as lithium ion all-solid-state battery cells, nickel-hydride battery cells, nickel cadmium battery cells and lead storage battery cells can be used.
- each partition member 1 explained on the basis of FIG. 1 and FIG. 2 can be used herein as each partition member 1 .
- Each bus bar 3 is a conductor rod used in order to supply power outputted from respective cells to a load (for instance a motor), and is for instance formed of a conductor such as aluminum.
- the case 4 accommodates the partition members 1 and the cells 2 .
- the case 4 can be formed for instance of a metal, a resin (for instance polypropylene), or of a combination of metal and a resin.
- the cells 2 having the partition members 1 inserted between cells may be clamped by end plates that are in turn connected by connecting plates, in such a manner that the cells 2 and the partition members 1 become fixed to each other.
- part or the entirety of the chemical substances that make up for instance the electrolyte solution and the electrodes that constitute the cells 2 undergo decomposition reactions inside the cells 2 with generation of heat as a result of which the temperature in the cells 2 increases and partial regions or the entirety of the cells 2 may reach a temperature of 200° C. or higher. This state is referred to as an “abnormal heating state”.
- a charging negative electrode (lithium-intercalated carbon negative electrode) exhibits basically the same strong reducibility as that of metallic lithium; as is known, a coating film forms thus on the negative electrode surface upon reaction with the electrolyte solution, with further reactions being inhibited by that coating film. Therefore the chemical composition, structure and thermal stability of this protective coating film exerts a significant influence the thermal stability of the charging negative electrode at the time of rises in temperature. Reactions between the charging negative electrode and the electrolyte solution are ordinarily explained by the formation of a protective coating film and by ensuing explosive reductive decomposition reactions arising from breakdown of that film.
- the protective film formation reaction on the negative electrode proceeds generally from around 130° C., and the subsequent coating film decomposition reaction proceeds at about 200° C., eventually leading to an explosive reductive decomposition reaction.
- an instance where part or the entire area of the cells 2 is at 200° C. or above denotes ongoing breakdown of the coating film on the negative electrode surface, i.e. indicates that the cells 2 are in a thermal runaway state (Reference 4: Battery Handbook, 1st Edition Ohm Co., p. 591; Reference 5: Cutting-Edge High-Safety Technologies and Evaluation Technologies in Lithium Ion Batteries, CMC Publishing Co., Ltd., p. 90).
- a state in which a chemical substance constituting for instance the electrolyte solution or the electrodes that make up the cells 2 does not elicit a decomposition reaction at or above a given heat generation rate in the interior of the cells 2 will be referred to herein as a “normal state”.
- the heat generation state in the cells 2 can be evaluated by ARC (Accelerating Rate Calorimetry), which is a means for measuring quantitatively thermal behavior during self-heating decomposition, under adiabatic conditions, of a reactive chemical substance. According to the definition by Dahn et al., as a dependable yardstick, a self-heating reaction is progressing inside a cell when the heating rate observed by ARC exceeds 0.04° C./min (Reference 6: J.
- Cells 2 in a normal state will be referred to as “single cells maintaining a normal state”, and cells 2 deviating from the normal state but not having reached an abnormal heating state will be referred to as “single cells deviating from the normal state”. Heat generated inside the cells 2 is transmitted to other cells 2 via various transmission paths.
- Cells 2 in a normal state will be referred to as “single cells maintaining a normal state”, and cells 2 deviating from the normal state but not having reached an abnormal heating state will be referred to as “single cells deviating from the normal state”. Heat generated inside the cells 2 is transmitted to other cells 2 via various transmission paths.
- FIG. 4 is a diagram illustrating an example of heat transfer paths in an assembled battery.
- the heat generated by the cell 21 is transmitted to other cells 22 , 23 via: (1) the partition member 11 disposed between the cells, (2) the bus bars 3 , and (3) the case 4 of the assembled battery 10 in contact with the cells 2 ; in addition, (4) the heat is also dissipated out of the case of the assembled battery 10 .
- the upper limit of a surface average temperature envisaged for a case where the cells 2 in contact with or in the vicinity of partition members 1 deviate from the normal state but have not reached an abnormal heating state is set herein to 180° C. It is known that the meltdown temperature of generic separator materials is 160° C. to 200° C. When the surface average temperature of the cells 2 exceeds 180° C., therefore, there is a risk of meltdown of part of the generic separator material that makes up the cells 2 , leading to an abnormal heating state.
- the upper limit of surface average temperature envisaged for an instance where cells 2 in contact with or in the vicinity of partition members 1 do not deviate from the normal state is set herein to 80° C.
- the boiling points of generic electrolyte solution components are 90° C. or higher, as given in Table 1.
- Generic electrolyte solution components include for instance ethylene carbonate (EC), diethyl carbonate, dimethyl carbonate (DMC) and ethyl methyl carbonate (EMC). If the surface average temperature of the cells 2 is lower than 80° C. there ensues thus no boiling of the generic electrolyte solution itself that makes up the cells 2 .
- a means for controlling the thermal resistance per unit area ( ⁇ ) depending on the surface temperature of the partition members 1 will be explained next. Firstly a material A and a material B that make up the partition members 1 will be illustrated below.
- the thermal resistance per unit area ( ⁇ ) of the material A satisfies (Expression 1) above.
- the material A is for instance a resin plate made of polycarbonate or butyl rubber.
- the thermal resistance per unit area ( ⁇ ) of the material B satisfies (Expression 2) above.
- the material B is for instance a ceramic, a glass plate or polyethylene, in solid form, or water, ethylene glycol or glycerin, in liquid form.
- the partition member 1 has a substantially rectangular parallelepiped bag-like structure ( FIG. 5 ), of hollow interior, made up of the material A having a melting point at a temperature higher than T (° C.).
- the interior of the bag-like structure is filled with the material B, which is in liquid state at T (° C.).
- the lower face of the bag-like structure is provided with an opening through which the interior of the bag-like structure communicates with the exterior.
- the opening is closed by a plug made of a material C having for instance a melting point around T (° C.).
- the partition member 1 is designed so that when the plug made of the material C melts, at around T (° C.), an opening becomes formed through which the material B that fills the interior flows down to the exterior.
- the outer shape of the bag-like structure may be other than a rectangular parallelepiped shape. In FIG. 5 an opening is provided at the lower face of the bag-like structure, but the opening may be provided at a side face, so long as the opening lies at a position at which the material B can flow down out of the bag-like structure.
- the partition member 1 may have a structure formed through juxtaposition of multiple bag-like structures described above, each filled with the material B, in the transversal direction or the longitudinal direction.
- the plug is not necessarily essential herein.
- the melting point of the material C may be similar or lower than that of the material B.
- the plug may in some instances be made of the material B.
- the material B need no necessarily be liquid at T (° C.), and may be in a fluid state other than liquid.
- the thermal resistance per unit area ( ⁇ ) satisfies (Expression 2), thanks to the material B inside the bag-like structure, when the surface temperature of such a partition member 1 having a bag-like structure is lower than T (° C.).
- T temperature of the partition member 1
- the thermal resistance per unit area ( ⁇ ) of the partition member 1 satisfies (Expression 1), given that the material B flows down out of the bag-like structure whereupon the partition member 1 is now made up of the material A.
- the partition member 1 has a structure ( FIG. 6 ) in which a lattice-like frame is provided inside the bag-like structure of FIG. 5 .
- the interior of the bag-like structure is filled with the material B, which is liquid at T (° C.), at a portion other than the frame, the lower face of the bag-like structure being closed off by a plug formed of the material C that has a melting point around T (° C.).
- the partition member 1 is designed so that in a case where the plug formed of the material C melts at around T (° C.), the material B that fills the space portions of the bag-like structure flows down to the exterior, through the opening that becomes formed upon melting of the plug.
- the frame has the effect of maintaining the rigidity (strength) of the bag-like structure when the material B flows out.
- the thermal resistance per unit area ( ⁇ ) satisfies (Expression 2) thanks to the material B that filters the space portions of the bag-like structure.
- the thermal resistance per unit area ( ⁇ ) of the partition members 1 satisfies (Expression 1), given that the material B flows down out of the bag-like structure whereupon the partition members 1 is now made up of the material A.
- Transfer of heat between the cells 2 that make up the assembled battery 10 is controlled in such a manner so as not to reduce the quantity of heat transmitted from cells 2 having reached an abnormal heating state to cells 2 maintaining a normal state, without mediation of electrode bodies of cells 2 deviating from the normal state, or the quantity of heat transmitted from cells 2 deviating from the normal state to cells 2 maintaining the normal state, while reducing the quantity of heat transmitted from cells 2 having reached an abnormal heating state to the cells 2 deviating from the normal state.
- the electrode bodies of the cells 2 are structures having electrodes, separators and electrolyte solutions, i.e. are bodies of respective cells.
- control is performed so that the quantity of heat transmitted from the cell 21 to the cell 22 is reduced, and so as not to reduce the quantity of heat transmitted from the cell 21 to the cell 23 without mediation of the electrode body of the cell 22 , or the quantity of heat transmitted from the cell 22 to the cell 23 .
- Transfer of heat among the cells 2 can be controlled on the basis of a switching function of the partition members 1 . Specifically, the quantity of heat that is transmitted to the cell 22 , from among the quantity of heat generated by the cell 21 , is reduced through an increase in the heat transfer resistance of the partition member 11 disposed between the cell 22 deviating from the normal state and the cell 21 having reached an abnormal heating state. Also, by not increasing the heat transfer resistance of the partition member 12 that is disposed between the cell 22 deviating from the normal state and the cell 23 maintaining the normal state, the quantity of heat transmitted from the cell 22 to the cell 23 , and the quantity of heat transmitted to the cell 23 , without mediation of the electrode body of the cell 22 , from among the quantity of heat generated by the cell 21 are not reduced.
- the quantity of heat generated by the cell 21 having reached an abnormal heating state is controlled to be transmitted to the cell 23 maintaining a normal state, while reducing the quantity of heat that is transmitted to the cell 22 deviating from the normal state, so that the temperatures of the cells 2 in the assembled battery 10 are equalized. This allows as a result preventing that an abnormal heating state should be reached by cells 2 other than those cells 2 that have reached abnormal heating state.
- Analyses were performed drawing on References 9 and 10 below, using COMSOL Multiphysics which is a general-purpose physical simulation software developed by COMSOL AB. The paths explained in FIG. 4 are conceivable herein as heat transfer paths between the cells (Reference 9: Japanese Patent Application Publication No. 2006-010648; Reference 10: R. M. Spotnitz et al., J. Power Sources 163, 1080-1086, (2007)).
- FIG. 3 there were estimated the temperatures in the interior of the adjacent cell 22 and cell 23 , as well as the surface average temperature and thermal resistance per unit area of the partition members 1 , upon abnormal heating of the left-end cell 21 , and there was evaluated the effect for instance of suppressing spread of burning on the basis of changes in the heat transfer resistance of the partition members 1 .
- the temperature in the interior of each cell 2 was assumed to be the temperature obtained by measuring the average temperature in the interior of respective electrode bodies (structure including electrodes, separators and electrolyte solutions).
- the partition members 1 were assumed to be made of a general resin such as polypropylene (PP), with thickness set to 1 mm and thermal conductivity set to 0.24 W/m ⁇ K.
- the bus bars 3 were assumed to be made of aluminum, with thermal conductivity set to 237 W/m ⁇ K.
- the case 4 was assumed to be made of a general resin such as polypropylene, with thermal conductivity set to 0.24 W/m ⁇ K. Under these conditions there were estimated the temperature inside each cell 2 , as well as the surface average temperature and thermal resistance per unit area of each partition member 1 .
- FIG. 7 is a graph illustrating changes in temperature in the interior of the cells in Comparative example 1.
- the vertical axis represents absolute temperature (K) in the interior of the cells 2
- the horizontal axis represents the time (seconds) elapsed since the cell 21 has reached an abnormal heating state.
- K absolute temperature
- seconds time
- the graph suggests that after about 150 seconds have elapsed since the cell 21 reached an abnormal heating state, the temperature in the interior of the cell 22 and the cell 23 exceeds 1000K, with spreading of burning from the abnormally heated cell 21 to the cell 22 and the cell 23 .
- FIG. 8 is a graph illustrating the evolution of surface average temperature of partition members in Comparative example 1.
- the average temperature at the surface of the partition members, on the side of the abnormally heated cell 21 was taken herein as the surface average temperature of each partition member 1 .
- the vertical axis represents the surface average temperature (° C.) of the partition members 1 and the horizontal axis represents the time (seconds) after the cell 21 has reached an abnormal heating state. It was estimated that immediately after the cell 21 reaches an abnormal heating state, the surface average temperature of the partition member 11 (Spacer 1) rises rapidly and reaches 400° C., and after about 150 second have elapsed, also the surface average temperature of the partition member 12 (Spacer 2) rises rapidly and exceeds 700° C.
- FIG. 9 is a set of graphs illustrating the evolution of thermal resistance per unit area of the partition members in Comparative example 1.
- the vertical axis represents thermal resistance per unit area (m 2 ⁇ K/W) and the horizontal axis represents the surface average temperature (° C.) of the respective partition members 1 .
- the value of thermal resistance per unit area ( ⁇ 1 ) at a surface average temperature of 190° C. of the partition member 11 (Spacer 1) and of the partition member 12 (Spacer 2) was 4.2 ⁇ 10 ⁇ 3 m 2 ⁇ K/W
- the value of thermal resistance per unit area ( ⁇ 2 ) at an average temperature of 70° C. was 4.2 ⁇ 10 ⁇ 3 m 2 ⁇ K/W. That is, the partition members 1 in Comparative example 1 fail to satisfy the conditions of (Expression 1) and (Expression 2) described above pertaining to thermal resistance per unit area.
- Example 1 the partition members 1 were assumed to be high-performance partition members having a switching function whereby thermal conductivity changes at the point in time where the surface temperature of the partition members 1 , on the side of abnormally heated cell, reaches a predetermined temperature.
- the thickness of the partition members 1 was set to 1.0 mm.
- Various conditions pertaining to the bus bars 3 and the case 4 were set to be identical to those in Comparative example 1.
- the partition members 1 having a switching function can be prescribed to have each a structure wherein for instance a substance being in a liquid state at 150° C., from among the materials B described above, is sealed in the interior of a bag-like structure made up of a material having a melting point in the vicinity of 150° C., from among the materials A described above, the structure of the partition member being designed so that upon melting of part of the bag-like structure made up of the material A at 150° C., the material B sealed in the interior flows down out of the bag-like structure.
- each partition member 1 in such a structure was set to 150° C., the initial thermal conductivity to 1.0 W/m ⁇ K and the thermal conductivity after switching to 0.10 W/m ⁇ K, and there were estimated the temperature inside each cell 2 , as well as the surface average temperature and thermal resistance per unit area of each partition member 1 .
- FIG. 10 is a graph illustrating changes in temperature in the interior of the cells in Example 1.
- the vertical axis represents absolute temperature (K) in the interior of the cells 2
- the horizontal axis represents the time (seconds) elapsed since the cell 21 has reached an abnormal heating state.
- the graph reveals that after the cell 21 has reached an abnormal heating state, the temperature in the interior of the cell 22 and the cell 23 rises gradually, but does not reach an abnormal heating state, and converges at about 430K, which indicates that it is possible to suppress spread of burning between the cells 2 .
- FIG. 11 is a graph illustrating the evolution of surface average temperature of partition members in Example 1.
- the vertical axis represents the surface average temperature (° C.) of the partition members 1 and the horizontal axis represents the time (seconds) after the cell 21 has reached an abnormal heating state. It was estimated that immediately after the cell 21 reaches an abnormal heating state the surface average temperature of the partition member 11 (Spacer 1) rises rapidly and exceeds 400° C., but the surface average temperature of the partition member 12 (Spacer 2) converges at about 160° C., without rising rapidly.
- FIG. 12 is a set of graphs illustrating the evolution of thermal resistance per unit area of the partition members in Example 1.
- the vertical axis represents thermal resistance per unit area (m 2 ⁇ K/W) and the horizontal axis represents the surface average temperature (° C.) of the respective partition members 1 .
- the value of thermal resistance per unit area ( ⁇ 1 ) at a surface average temperature of 190° C. of the partition member 11 (Spacer 1) and of the partition member 12 (Spacer 2) was 1.0 ⁇ 10 ⁇ 2 m 2 ⁇ K/W
- the value of thermal resistance per unit area ( ⁇ 2 ) at an average temperature of 70° C. was 1.0 ⁇ 10 ⁇ 3 m 2 ⁇ K/W. That is, the partition members 1 in Comparative example 1 satisfy the conditions of both (Expression 1) and (Expression 2) described above pertaining to thermal resistance per unit area.
- Comparative example 2 and Comparative example 3 illustrate examples envisaging partition members 1 not having a switching function.
- the partition members 1 are assumed to be partition members 1 of lower thermal conductivity than that in Comparative example 1, with thickness set to 1.0 mm and thermal conductivity set to 0.10 W/m ⁇ K.
- Various conditions pertaining to the bus bars 3 and the case 4 were set to be identical to those in Comparative example 1.
- FIG. 13 is a graph illustrating changes in temperature in the interior of the cells in Comparative example 2.
- the vertical axis represents absolute temperature (K) in the interior of the cells 2
- the horizontal axis represents the time (seconds) elapsed since the cell 21 has reached an abnormal heating state.
- the graph indicated that the time required for the occurrence of spread of burning from the abnormally heated cell 21 to the cell 22 and cell 23 was herein longer than that in Comparative example 1, in which partition members 1 made of a general resin were used, but there was not achieved suppression of the spread of burning.
- FIG. 14 is a graph illustrating the evolution of the surface average temperature of partition members in Comparative example 2.
- the vertical axis represents the surface average temperature (° C.) of partition members 1 and the horizontal axis represents the time (seconds) after the cell 21 has reached an abnormal heating state.
- the surface average temperature of the partition member 11 (Spacer 1) began rising about 250 seconds after the cell 21 reached an abnormal heating state. From these results it was estimated that in a case where the thermal insulation properties of the members 1 is enhanced, the heat generated by the cell 21 is not eliminated efficiently, at an initial stage where the cell 21 has reached the abnormal heating state and as a result spread of burning is not suppressed.
- FIG. 15 is a set of graphs illustrating the evolution of thermal resistance per unit area of the partition members in Comparative example 2.
- the vertical axis represents thermal resistance per unit area (m 2 ⁇ K/W) and the horizontal axis represents the surface average temperature (° C.) of the respective partition members 1 .
- the value of thermal resistance per unit area ( ⁇ 1 ) at a surface average temperature of 190° C. of the partition member 11 (Spacer 1) and of the partition member 12 (Spacer 2) was 1.0 ⁇ 10 ⁇ 2 m 2 ⁇ K/W
- the value of thermal resistance per unit area ( ⁇ 2 ) at an average temperature of 70° C. was 1.0 ⁇ 10 ⁇ 2 m 2 ⁇ K/W. That is, the partition members 1 in Comparative example 2 satisfy the condition of (Expression 1) described above pertaining to thermal resistance per unit area, but not the condition of (Expression 2).
- the partition members 1 are assumed to be partition members 1 of higher thermal conductivity than that in Comparative example 1, with thickness set to 1.0 mm and thermal conductivity set to 1.0 W/m ⁇ K.
- Various conditions pertaining to the bus bars 3 and the case 4 were set to be identical to those in Comparative example 1.
- FIG. 16 is a graph illustrating changes in temperature in the interior of the cells in Comparative example 3.
- the vertical axis represents absolute temperature (K) in the interior of the cells 2
- the horizontal axis represents the time (seconds) elapsed since the cell 21 has reached an abnormal heating state.
- the graph indicated that the time required for the occurrence of spread of burning from the abnormally heated cell 21 to the cell 22 and cell 23 was shorter than that in Comparative example 1, in which partition members 1 made of a general resin were used, and that the cell 22 and cell 23 underwent abnormal heating substantially simultaneously with cell 21 .
- FIG. 17 is a graph illustrating the evolution of surface average temperature of partition members in Comparative example 3.
- the vertical axis represents the surface average temperature (° C.) of the partition members 1 and the horizontal axis represents the time (seconds) after the cell 21 has reached an abnormal heating state. It was estimated that immediately after the cell 21 reaches an abnormal heating state, the surface average temperatures of the partition member 11 (Spacer 1) and of the partition member 12 (Spacer 2) rise rapidly, and the surface average temperature of all the foregoing exceeds 600° C. by the time that 100 seconds have elapsed. From these results it was estimated that in a case where heat transfer properties of the partition members 1 are improved, spread of burning cannot be suppressed given that heat generated upon abnormal heating of the cell 21 propagates quickly to the adjacent cell 22 and cell 23 .
- FIG. 18 is a set of graphs illustrating the evolution of thermal resistance per unit area of the partition members in Comparative example 3.
- the vertical axis represents thermal resistance per unit area (m 2 ⁇ K/W) and the horizontal axis represents the surface average temperature (° C.) of the respective partition members 1 .
- the value of thermal resistance per unit area ( ⁇ 1 ) at a surface average temperature of 190° C. of the partition member 11 (Spacer 1) and of the partition member 12 (Spacer 2) was 1.0 ⁇ 10 ⁇ 3 m 2 ⁇ K/W
- the value of thermal resistance per unit area ( ⁇ 2 ) at an average temperature of 70° C. was 1.0 ⁇ 10 ⁇ 3 m ⁇ K/W. That is, the partition members 1 in Comparative example 3 do not satisfy the condition of (Expression 1) described above pertaining to thermal resistance per unit area, but satisfy the condition of (Expression 2).
- Comparative example 4 provides an example in which even with high-performance partition members having a switching function with change in thermal conductivity, burning spreads from an abnormally heated cell to adjacent cells due to the fact that the value of thermal resistance per unit area before and after a change in thermal conductivity does not lie within an appropriate range.
- Comparative example 4 the partition members 1 were set to have a thickness of 1.0 mm, a switching temperature of 150° C., an initial thermal conductivity of 0.24 W/m ⁇ K, and a thermal conductivity after switching of 0.10 W/m ⁇ K.
- Various conditions pertaining to the bus bars 3 and the case 4 were set to be identical to those in Comparative example 1.
- FIG. 19 is a graph illustrating changes in temperature in the interior of the cells in Comparative example 4.
- the vertical axis represents absolute temperature (K) in the interior of the cells 2
- the horizontal axis represents the time (seconds) elapsed since the cell 21 has reached an abnormal heating state.
- K absolute temperature
- seconds time
- the graph suggests that after about 600 seconds have elapsed since the cell 21 reached an abnormal heating state, the temperature in the interior of the cell 22 and the cell 23 exceeds 1200K, with spreading of burning from the abnormally heated cell 21 to the cell 22 and the cell 23 .
- FIG. 20 is a graph illustrating the evolution of surface average temperature of partition members in Comparative example 4.
- the vertical axis represents the surface average temperature (° C.) of the partition members 1 and the horizontal axis represents the time (seconds) after the cell 21 has reached an abnormal heating state. It was estimated that immediately after the cell 21 reaches an abnormal heating state, the surface average temperature of the partition member 11 (Spacer 1) rises rapidly beyond 400° C., and after about 600 seconds have elapsed, also the surface average temperature of the partition member 12 (Spacer 2) rises rapidly beyond 800° C. From the above results it was estimated that even when the partition members 1 have a switching function, spread of burning cannot be reduced unless the thermal conductivity of the partition members 1 is properly controlled.
- FIG. 21 is a set of graphs illustrating the evolution of thermal resistance per unit area of the partition members in Comparative example 4.
- the vertical axis represents thermal resistance per unit area (m 2 ⁇ K/W) and the horizontal axis represents the surface average temperature (° C.) of the respective partition members 1 .
- the value of thermal resistance per unit area ( ⁇ 1 ) at a surface average temperature of 190° C. of the partition member 11 (Spacer 1) and of the partition member 12 (Spacer 2) was 1.0 ⁇ 10 ⁇ 2 m 2 ⁇ K/W
- the value of thermal resistance per unit area ( ⁇ 2 ) at an average temperature of 70° C. was 4.2 ⁇ 10 ⁇ 3 m 2 ⁇ K/W. That is, the partition members 1 in Comparative example 4 satisfy the condition of (Expression 1) described above pertaining to thermal resistance per unit area, but not the condition of (Expression 2).
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Electrochemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Manufacturing & Machinery (AREA)
- Physics & Mathematics (AREA)
- Algebra (AREA)
- General Physics & Mathematics (AREA)
- Mathematical Analysis (AREA)
- Mathematical Optimization (AREA)
- Pure & Applied Mathematics (AREA)
- Aviation & Aerospace Engineering (AREA)
- Secondary Cells (AREA)
- Battery Mounting, Suspending (AREA)
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US17/656,632 US11837705B2 (en) | 2016-12-27 | 2022-03-25 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
US18/500,945 US20240072325A1 (en) | 2016-12-27 | 2023-11-02 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2016254342 | 2016-12-27 | ||
JP2016-254342 | 2016-12-27 | ||
PCT/JP2017/047090 WO2018124231A1 (fr) | 2016-12-27 | 2017-12-27 | Élément de séparation, batterie assemblée et procédé de commande de transmission de chaleur pour batterie assemblée |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2017/047090 Continuation WO2018124231A1 (fr) | 2016-12-27 | 2017-12-27 | Élément de séparation, batterie assemblée et procédé de commande de transmission de chaleur pour batterie assemblée |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US17/656,632 Division US11837705B2 (en) | 2016-12-27 | 2022-03-25 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
Publications (1)
Publication Number | Publication Date |
---|---|
US20190319223A1 true US20190319223A1 (en) | 2019-10-17 |
Family
ID=62709555
Family Applications (3)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/452,587 Abandoned US20190319223A1 (en) | 2016-12-27 | 2019-06-26 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
US17/656,632 Active US11837705B2 (en) | 2016-12-27 | 2022-03-25 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
US18/500,945 Pending US20240072325A1 (en) | 2016-12-27 | 2023-11-02 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
Family Applications After (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US17/656,632 Active US11837705B2 (en) | 2016-12-27 | 2022-03-25 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
US18/500,945 Pending US20240072325A1 (en) | 2016-12-27 | 2023-11-02 | Partition member, assembled battery and method for controlling heat transfer in an assembled battery |
Country Status (7)
Country | Link |
---|---|
US (3) | US20190319223A1 (fr) |
EP (1) | EP3565020A4 (fr) |
JP (1) | JP6835101B2 (fr) |
KR (2) | KR102650754B1 (fr) |
CN (2) | CN115472995A (fr) |
CA (1) | CA3048603A1 (fr) |
WO (1) | WO2018124231A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11515587B2 (en) * | 2019-10-10 | 2022-11-29 | Robert Bosch Gmbh | Physics-based control of battery temperature |
US11929478B2 (en) | 2018-09-14 | 2024-03-12 | Mitsubishi Chemical Corporation | Filling member and battery pack |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP7167802B2 (ja) * | 2019-03-26 | 2022-11-09 | 三菱ケミカル株式会社 | 仕切り部材及び組電池 |
JP7464042B2 (ja) | 2019-03-28 | 2024-04-09 | 三菱ケミカル株式会社 | 仕切り部材及び組電池 |
CN115009524B (zh) * | 2022-07-17 | 2023-11-17 | 西北工业大学 | 一种基于正常运行状态下的太阳能飞机热控系统及方法 |
Family Cites Families (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS49534B1 (fr) | 1969-05-16 | 1974-01-08 | ||
JPS5651210Y2 (fr) | 1976-10-07 | 1981-11-30 | ||
JP4576903B2 (ja) | 2004-06-29 | 2010-11-10 | 三菱化学株式会社 | 温度分布評価方法並びにシミュレーション装置及びシミュレーションプログラム |
US7981536B2 (en) | 2006-08-31 | 2011-07-19 | Toray Tonen Specialty Separator Godo Kaisha | Microporous membrane, battery separator and battery |
JP2009135088A (ja) | 2007-10-29 | 2009-06-18 | Panasonic Corp | 電池パックおよび電池搭載機器 |
JP2010061982A (ja) * | 2008-09-03 | 2010-03-18 | Toyota Motor Corp | 蓄電装置 |
JP5326480B2 (ja) | 2008-10-14 | 2013-10-30 | トヨタ自動車株式会社 | 蓄電装置 |
JP2010165597A (ja) | 2009-01-16 | 2010-07-29 | Toyota Motor Corp | 蓄電装置 |
CN102301503A (zh) | 2009-02-24 | 2011-12-28 | 松下电器产业株式会社 | 电池组件和使用了该电池组件的电池组件集合体 |
US8372269B2 (en) | 2009-10-02 | 2013-02-12 | Basf Corporation | Heavy metals trapping co-catalyst for FCC processes |
JP5740103B2 (ja) * | 2009-10-19 | 2015-06-24 | 日東電工株式会社 | 熱伝導部材、及びそれを用いた組電池装置 |
CN102362388B (zh) * | 2009-11-25 | 2013-09-25 | 松下电器产业株式会社 | 电池模块 |
DE112010004856A5 (de) * | 2009-12-18 | 2012-12-13 | Magna E-Car Systems Gmbh & Co Og | Kühl-/Heizelement für einen Akkumulator |
TWI419391B (zh) * | 2009-12-25 | 2013-12-11 | Ind Tech Res Inst | 電池系統中的散熱與熱失控擴散防護結構 |
CN102117945A (zh) * | 2009-12-31 | 2011-07-06 | 财团法人工业技术研究院 | 电池系统中的散热与热失控扩散防护结构 |
JP5379238B2 (ja) * | 2010-03-30 | 2013-12-25 | パナソニック株式会社 | 電池パック |
DE102010030881A1 (de) * | 2010-07-02 | 2012-01-05 | Robert Bosch Gmbh | Thermische Entkopplung von Batteriezellen im Störfall |
CN102523762B (zh) * | 2010-09-09 | 2014-12-31 | 松下电器产业株式会社 | 电池组件 |
JP5520320B2 (ja) * | 2010-11-05 | 2014-06-11 | パナソニック株式会社 | 電池モジュール |
JP2013033723A (ja) * | 2011-07-04 | 2013-02-14 | Nissan Motor Co Ltd | 組電池 |
US8993145B2 (en) * | 2011-09-19 | 2015-03-31 | Zee.Aero Inc. | Preventing cell thermal runaway propagation within a battery |
KR101272524B1 (ko) * | 2011-09-20 | 2013-06-11 | 현대자동차주식회사 | 배터리 셀용 방열판 및 이를 갖는 배터리 모듈 |
KR101417248B1 (ko) * | 2012-02-08 | 2014-07-09 | 현대자동차주식회사 | 배터리 셀 모듈용 방열 플레이트 및 이를 갖는 배터리 셀 모듈 |
JP6153702B2 (ja) * | 2012-05-08 | 2017-06-28 | 東洋ゴム工業株式会社 | 熱伝導率可変材料 |
JP2015208894A (ja) | 2014-04-24 | 2015-11-24 | 東レバッテリーセパレータフィルム株式会社 | ポリオレフィン製積層微多孔膜 |
JP6135660B2 (ja) * | 2014-12-25 | 2017-05-31 | トヨタ自動車株式会社 | 組電池 |
-
2017
- 2017-12-27 JP JP2018559611A patent/JP6835101B2/ja active Active
- 2017-12-27 CA CA3048603A patent/CA3048603A1/fr active Pending
- 2017-12-27 KR KR1020197019964A patent/KR102650754B1/ko active IP Right Grant
- 2017-12-27 KR KR1020247009201A patent/KR20240042179A/ko not_active Application Discontinuation
- 2017-12-27 WO PCT/JP2017/047090 patent/WO2018124231A1/fr unknown
- 2017-12-27 CN CN202211104938.9A patent/CN115472995A/zh active Pending
- 2017-12-27 EP EP17886854.3A patent/EP3565020A4/fr active Pending
- 2017-12-27 CN CN201780080853.2A patent/CN110114903B/zh active Active
-
2019
- 2019-06-26 US US16/452,587 patent/US20190319223A1/en not_active Abandoned
-
2022
- 2022-03-25 US US17/656,632 patent/US11837705B2/en active Active
-
2023
- 2023-11-02 US US18/500,945 patent/US20240072325A1/en active Pending
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11929478B2 (en) | 2018-09-14 | 2024-03-12 | Mitsubishi Chemical Corporation | Filling member and battery pack |
US11515587B2 (en) * | 2019-10-10 | 2022-11-29 | Robert Bosch Gmbh | Physics-based control of battery temperature |
Also Published As
Publication number | Publication date |
---|---|
EP3565020A1 (fr) | 2019-11-06 |
CN110114903B (zh) | 2022-09-27 |
CN115472995A (zh) | 2022-12-13 |
EP3565020A4 (fr) | 2020-01-08 |
WO2018124231A1 (fr) | 2018-07-05 |
JP6835101B2 (ja) | 2021-02-24 |
US11837705B2 (en) | 2023-12-05 |
KR102650754B1 (ko) | 2024-03-22 |
US20220223946A1 (en) | 2022-07-14 |
KR20190097112A (ko) | 2019-08-20 |
CA3048603A1 (fr) | 2018-07-05 |
CN110114903A (zh) | 2019-08-09 |
US20240072325A1 (en) | 2024-02-29 |
KR20240042179A (ko) | 2024-04-01 |
JPWO2018124231A1 (ja) | 2019-11-14 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US11837705B2 (en) | Partition member, assembled battery and method for controlling heat transfer in an assembled battery | |
JP4434237B2 (ja) | 車両用の蓄電装置及び車両 | |
EP2210311B1 (fr) | Véhicule doté d'un système de batterie | |
KR100414445B1 (ko) | 복합 전극을 가진 재충전가능한 리튬 배터리 | |
JP7354842B2 (ja) | 仕切り部材及び組電池 | |
JP6217987B2 (ja) | 組電池 | |
EP3142173B1 (fr) | Électrode positive pour accumulateurs à électrolyte non aqueux et accumulateur à électrolyte non aqueux | |
EP3951916A1 (fr) | Barre omnibus de borne pour sécurité améliorée et module de batterie, et bloc-batterie le comprenant | |
JP2011090830A (ja) | 2次電池 | |
CN105633502A (zh) | 一种可抑制热失控蔓延的锂离子电池模块 | |
JP6954213B2 (ja) | 充填部材、組電池及び熱伝達の制御方法 | |
JP7043813B2 (ja) | 仕切り部材及び組電池 | |
KR102258286B1 (ko) | 배터리셀, 및 이를 포함하는 배터리 모듈 | |
US20210159559A1 (en) | Filling member and battery pack | |
CN117352893A (zh) | 用于袋式电池单元的集成冷却和热失控缓解容器 | |
Sangiri et al. | Electro-thermal modeling of Lithium-ion cell for higher discharge rate applications | |
JP6954214B2 (ja) | 充填部材、組電池、及び熱伝達の制御方法 | |
KR20190099597A (ko) | 열흡수형 첨가제를 사용한 이차전지 | |
US20230124905A1 (en) | Battery cell pack for electric vehicle | |
EP4383376A1 (fr) | Ensemble électrode, batterie secondaire, bloc-batterie et appareil électrique | |
JP2022175333A (ja) | 二次電池、電池モジュールおよび二次電池の製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: MITSUBISHI CHEMICAL CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WATANABE, YOKO;KAWAI, TOMOHIRO;SOGA, IWAO;SIGNING DATES FROM 20190614 TO 20190617;REEL/FRAME:049588/0071 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: AWAITING RESPONSE FOR INFORMALITY, FEE DEFICIENCY OR CRF ACTION |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |