US20190309413A1 - Zone-controlled rare-earth oxide ald and cvd coatings - Google Patents
Zone-controlled rare-earth oxide ald and cvd coatings Download PDFInfo
- Publication number
- US20190309413A1 US20190309413A1 US15/947,402 US201815947402A US2019309413A1 US 20190309413 A1 US20190309413 A1 US 20190309413A1 US 201815947402 A US201815947402 A US 201815947402A US 2019309413 A1 US2019309413 A1 US 2019309413A1
- Authority
- US
- United States
- Prior art keywords
- crystalline
- oxide
- layer
- layers
- rare
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- Embodiments disclosed herein relate, in general, to rare-earth coatings for articles with an interruption layer, and in particular to yttrium oxide coatings with one or more interruption layers for controlling the yttrium oxide grain growth.
- Various manufacturing processes expose semiconductor process chamber components to high temperatures, high energy plasma, a mixture of corrosive gases, high stress, and combinations thereof. These extreme conditions may erode and/or corrode the chamber components, increasing the chamber components susceptibility to defects.
- Protective coatings used for reducing defects on chamber components due to harsh processing conditions are typically deposited on chamber components. Protective coatings may be deposited by a variety of techniques, including but not limited to thermal spray, sputtering, ion assisted deposition (IAD), plasma spray, evaporation techniques, atomic layer deposition, chemical vapor deposition and so on. Some of these techniques may generate protective coatings with abnormally large crystal grains. Abnormally large crystal grains may increase the protective coating's surface roughness and provide a pathway for diffusion of chemicals through possible cracks between the grains or through grain boundaries.
- In an example embodiment, disclosed herein is an article comprising a plasma resistant protective coating on a surface of the article. The plasma resistant protective coating may comprise a stack of alternating layers of crystalline rare-earth oxide layers and crystalline or amorphous metal oxide layers. The first layer in the stack of alternating layers may be a crystalline rare-earth oxide layer. The crystalline rare-earth oxide layers may have a thickness of about 500-5000 angstroms. In embodiments where the metal oxide layers are crystalline, each of the metal oxide layers may have an atomic crystalline phase different from the crystalline phase of the rare-earth oxide layer and each metal oxide layer may have a thickness of about 1-500 angstroms. The crystalline or amorphous metal oxide layers may inhibit grain growth in the crystalline yttrium oxide layers.
- In an example embodiment, disclosed herein is a method comprising depositing a plasma resistant protective coating onto a surface of an article using an atomic layer deposition (ALD) process or a chemical vapor deposition (CVD) process. Depositing the plasma resistant protective coating may comprise depositing a crystalline rare-earth oxide layer using ALD or CVD. Depositing the plasma resistant protective coating may further comprise depositing a crystalline or amorphous metal oxide layer on the crystalline rare-earth oxide layer using ALD or CVD. In embodiments wherein the metal oxide layer is crystalline, the metal oxide layer may have an atomic crystalline phase different from the crystalline phase of the crystalline rare-earth oxide.
- In an example embodiment, disclosed herein is a method comprising depositing a plasma resistant protective coating onto a surface of an article using an atomic layer deposition (ALD) process or a chemical vapor deposition (CVD) process. Depositing the plasma resistant protective coating may comprise depositing a stack of alternating layers of crystalline yttrium oxide layers and crystalline or amorphous metal oxide layers. Each of the crystalline yttrium oxide layers may have a cubic phase and a thickness of about 500-5000 angstroms. In embodiments where the metal oxide layers are crystalline, the metal oxide layers may have an atomic crystalline phase different from the cubic phase of the crystalline yttrium oxide and each of the metal oxide layers may have a thickness of about 1-500 angstroms. The first layer in the stack of alternating layers may be a crystalline yttrium oxide layer. The crystalline or amorphous metal oxide layers may inhibit grain growth in the crystalline yttrium oxide layers.
- Embodiments of the present invention are illustrated by way of example, and not by way of limitation, in the figures of the accompanying drawings in which like references indicate similar elements. It should be noted that different references to “an” or “one” embodiment in this disclosure are not necessarily to the same embodiment, and such references mean at least one.
-
FIG. 1A depicts one embodiment of an atomic layer deposition process described herein. -
FIG. 1B depicts another embodiment of an atomic layer deposition process described herein. -
FIG. 1C depicts yet another embodiment of an atomic layer deposition process described herein. -
FIG. 2 depicts a chemical vapor deposition technique that may be used when depositing plasma resistant protective coating in accordance with embodiments. -
FIG. 3 depicts different crystal phases of various rare-earth oxides at different temperatures. -
FIGS. 4A and 4B depict Transmission Electron Microscopy (TEM) image of various scales (0.2 μm scale and 100 nm scale, respectively) of a 600 nm yttrium oxide coating without any interruption layers. -
FIG. 4C depicts a TEM image at a 100 nm scale of a yttrium oxide coating with carbon-rich yttria interruption layers. -
FIGS. 5A, 5B, and 5C depict exemplary plasma resistant protective coatings in accordance with examples 1, 2, and 3 respectively. -
FIG. 6A depicts an X-Ray Diffraction (XRD) profile of a cubic yttrium oxide having a Powder Diffraction File (PDF) No. 04-005-4378. -
FIG. 6B depicts an XRD profile of a multiphase mixture of a tetragonal zirconia and monoclinic zirconia as present in the interruption layers of example 1. -
FIG. 6C depicts a transmission electron microscopy and energy dispersive spectroscopy (TEM/EDS) line scan of a multiphase mixture of a tetragonal zirconia and monoclinic zirconia as present in the interruption layers of example 1. -
FIG. 6D depicts a high Angle Annular Dark Field (HAADF) Scanning Transmittion Electron Microscopy (STEM) image of a multiphase mixture of a tetragonal zirconia and monoclinic zirconia as present in the interruption layers of example 1. -
FIG. 7A depicts an XRD profile of a crystalline zirconium yttrium oxide having a chemical formula Zr0.86Y0.14O1.93 and a PDF No. 01-082-1243 as present in the interruption layers of example 2. -
FIG. 7B depicts a TEM/EDS line scan of a crystalline single phase zirconium yttrium oxide having a chemical formula Zr0.86Y0.14O1.9 as present in the interruption layers of example 2. -
FIG. 7C depicts a HAADF STEM image of a crystalline single phase zirconium yttrium oxide having a chemical formula Zr0.86Y0.14O1.9 as present in the interruption layers of example 2. -
FIGS. 7D and 7E depict a TEM image of various scales (10 nm scale and 0.2 μm scale, respectively) of a crystalline zirconium yttrium oxide having a chemical formula Zr0.86Y0.14O1.9 as present in the interruption layers of example 2. -
FIG. 8A depicts an XRD profile of a multiphase mix of yttrium zirconium oxide having a chemical formula Zr0.4Y0.6O1.7 and a PDF No. 01-080-4014 and of yttrium oxide with a PDF No. 01-084-3893 as present in the interruption layers of example 3. -
FIG. 8B depicts a TEM/EDS line scan of a multiphase mix of yttrium zirconium oxide having a chemical formula Zr0.4Y0.6O1.7 and a PDF No. 01-080-4014 and of yttrium oxide with a PDF No. 01-084-3893 as present in the interruption layers of example 3. -
FIG. 8C depicts a HAADF STEM image of a multiphase mix of yttrium zirconium oxide having a chemical formula Zr0.4Y0.6O1.7 and a PDF No. 01-080-4014 and of yttrium oxide with a PDF No. 01-084-3893 as present in the interruption layers of example 3. -
FIG. 8D depicts a 0.2 μm scale TEM image of a multiphase mix of yttrium zirconium oxide having a chemical formula Zr0.4Y0.6O1.7 and a PDF No. 01-080-4014 and of yttrium oxide with a PDF No. 01-084-3893 as present in the interruption layers of example 3. -
FIG. 9A depicts an exemplary plasma resistant protective coating in accordance with example 4. -
FIG. 9B depicts a TEM/EDS line scan of a multiphase mix of yttrium zirconium oxide having a chemical formula Zr0.4Y0.6O1.7 and a PDF No. 01-080-4014 and of yttrium oxide with a PDF No. 01-084-3893 as present in the interruption layers of example 4. -
FIG. 9C depicts a HAADF STEM image of a multiphase mix of yttrium zirconium oxide having a chemical formula Zr0.4Y0.6O1.7 and a PDF No. 01-080-4014 and of yttrium oxide with a PDF No. 01-084-3893 as present in the interruption layers of example 4. -
FIG. 9D depicts a 50 nm scale TEM image of a multiphase mix of yttrium zirconium oxide having a chemical formula Zr0.4Y0.6O1.7 and a PDF No. 01-080-4014 and of yttrium oxide with a PDF No. 01-084-3893 as present in the interruption layers of example 4. -
FIG. 10 depicts an exemplary plasma resistant protective coating of yttrium oxide and gadolinium oxide in accordance with example 5. -
FIG. 11 illustrates a method for creating a plasma resistant protective coating using atomic layer deposition or chemical vapor deposition as described herein. -
FIG. 12 depicts an exemplary plasma resistant protective coating in accordance with example 6. -
FIG. 13A depicts a top down SEM image of a 1 μm yttria coating deposited by ALD without an interruption layer. -
FIG. 13B depicts a top down SEM image of a 1μ yttria coating with interruption layers in accordance with example 6. -
FIG. 14A depicts a cross sectional TEM image of a 1 μm yttria coating deposited by ALD without an interruption layer. -
FIG. 14B depicts a cross sectional TEM image of a 1 μm yttria coating with interruption layers in accordance with example 6. -
FIG. 15A depicts a TEM/EDS line scan of the plasma resistant protective coating of example 6. -
FIG. 15B depicts a TEM image of the plasma resistant protective coating of example 6. - Embodiments described herein cover articles (e.g., coated chamber components) and methods where a plasma resistant protective coating having one or more (poly)crystalline single phase or multiphase rare-earth oxide layers and one or more amorphous or (poly)crystalline single phase or multiphase interruption layers are deposited on a surface of an article. In an exemplary embodiment, the one or more crystalline rare-earth oxide layers may comprise crystalline yttrium oxide in a cubic phase. Embodiments herein are described with a crystalline yttrium oxide layer in a cubic phase as an example. It will be appreciated that the layer or layers between the interruption layers may include any rare earth metal oxide or mixtures of rare earth metal oxides (i.e., with or without yttrium) that are in a (poly)crystalline single phase or multiphase. For instance, the rare earth metal oxide layer(s) between the interruption layers may comprise yttrium oxide and/or yttrium zirconium oxide.
- In an exemplary embodiment, the one or more amorphous or (poly)crystalline single phase or multiphase interruption layers may comprise a crystalline or amorphous metal oxide layer selected from the group consisting of rare-earth metal-containing oxides, zirconium oxide, aluminum oxide and mixtures thereof. In embodiments where the one or more interruption layers are (poly)crystalline single phase or multiphase, the interruption layers may have an atomic crystalline phase or a plurality of atomic crystalline phases that are different from the cubic phase of the crystalline yttrium oxide. For instance, a (poly)crystalline single phase or multiphase phase of the interruption layers may be selected from the group consisting of hexagonal phase, monoclinic phase, cubic phase (if the rare-earth oxide layer is yttrium oxide in the cubic phase, than the interruption layer may have a lattice structure that is different from the lattice structure of the cubic phase of the crystalline yttrium oxide), hexagonal phase, tetragonal phase, and combinations thereof.
- As used herein, the term “plasma resistant” means resistant to one or more types of plasma as well as resistant to chemistry and radicals associated with the one or more types of plasma.
- As used herein, the term “polycrystalline” and “crystalline” are used herein interchangeably and may means a material that includes many crystalline grains (also referred to as crystallites) that are randomly oriented with respect to each other or have preferred orientation or texture, and which may have varying sizes. The areas where crystallites meet are referred to as grain boundaries. A polycrystalline layer may comprise a single crystal phase or a plurality of crystal phases (also referred to herein by the term “multiphase”). As used herein, it is understood that reference to a multiphase layer refers to a crystalline or polycrystalline layer having multiple crystal phases.
- The surface of the article may be a metal material (e.g., such as an aluminum (e.g., Al 6061, Al 6063) and stainless steel) or a ceramic material (e.g., such as alumina (Al2O3)).
- The deposition process may be an atomic layer deposition (ALD) process or a chemical vapor deposition (CVD) process. The ALD and CVD processes may be used for deposition of the one or more crystalline rare-earth oxide layers and of the one or more amorphous or crystalline metal oxide interruption layers. Layers that comprise more than one metal may be deposited through sequential deposition of precursors or through co-deposition of precursors.
- The plasma resistant protective coating may be comprised of a bi-layer stack or of a plurality of alternating layers stack. The bi-layer stack or plurality of alternating layers stack may include one or more layers of crystalline single phase yttrium oxide (Y2O3), e.g., in a cubic phase, and one or more layers of multiphase zirconium oxide layer, e.g., in a tetragonal and monoclinic phase. The bi-layer stack or plurality of alternating layers stack may include one or more layers of crystalline single phase yttrium oxide (Y2O3), e.g., in a cubic phase, and one or more layers of crystalline single phase zirconium yttrium oxide layer, e.g., in a tetragonal phase. The bi-layer stack or plurality of alternating layers stack may include one or more layers of crystalline single phase yttrium oxide (Y2O3), e.g., in a cubic phase in a first lattice structure, and one or more layers of multiphase mixture of zirconium yttrium oxide layer, e.g., in a cubic phase with a second lattice structure, and yttrium oxide, e.g., in a cubic phase with a third lattice structure. The second and the third lattice structures being different from the first lattice structure.
- The thickness of each interruption layer in the multi-layer plasma resistant protective coating may range from about 1 angstroms to about 500 angstroms. The thickness of each rare-earth oxide layer in the multi-layer plasma resistant protective coating may range from about 500 angstroms to about 10000 angstroms. In some embodiments, the thickness of each rare-earth oxide layer in the multi-layer plasma resistant protective coating may range from about 500 angstroms to about 5000 angstroms. In embodiments, multi-layer plasma resistant protective coating may have a thickness of about 1 μm to about 10 μm, or about 1 μm to about 5 μm. The plasma resistant protective coating may coat or cover the surfaces of features in the article having high aspect ratios, e.g., of about 10:1 to about 300:1. The plasma resistant protective coating may also conformally cover such features with a substantially uniform thickness. In one embodiment, the plasma resistant protective coating has a conformal coverage of the underlying surface that is coated (including coated surface features) with a uniform thickness having a thickness variation from one part of the coating to another of less than about +/−20%, a thickness variation of +/−10%, a thickness variation of +/−5%, or a lower thickness variation. The plasma resistant protective coating is also very dense with a porosity of about 0% (e.g., the plasma resistant protective coating may be porosity-free in embodiments).
- ALD allows for a controlled self-limiting deposition of material through chemical reactions with the surface of the article. Aside from being a conformal process, ALD is also a uniform process. All exposed sides of the article, including high aspect ratio features (e.g., about 10:1 to about 300:1) will have the same or approximately the same amount of material deposited. A typical reaction cycle of an ALD process starts with a precursor (i.e., a single chemical A) flooded into an ALD chamber and adsorbed onto the surface of the article. The excess precursor is then flushed out of the ALD chamber before a reactant (i.e., a single chemical R) is introduced into the ALD chamber and subsequently flushed out. The metal oxide interruption layer may, however, be formed by co-deposition of materials. To achieve this, a mixture of two precursors, such as a first metal-containing oxide precursor (A) and a second metal-containing oxide precursor (B), may be co-injected (AxBy) at any number of ratios, for example, A90+B10, A70+B30, A50+B50, A30+B70, A10+A90 and so on, into the chamber and adsorbed on the surface of the article. In these examples, x and y are expressed in molar ratios (mol %) for Ax+By. For example A90+B10 is 90 mol % of A and 10 mol % of B. Alternatively, the two precursors may be injected sequentially (without injecting a reactant in between). Excess precursors are flushed out. A reactant is introduced into the ALD chamber and reacts with the adsorbed precursors to form a solid layer before the excess chemicals are flushed out. For ALD, the final thickness of material is dependent on the number of reaction cycles that are run, because each reaction cycle will grow a layer of a certain thickness that may be one atomic layer or a fraction of an atomic layer.
- CVD allows for deposition of a highly dense, pure, and uniform coating with good reproducibility and adhesion at high deposition rates. A typical reaction cycle of CVD may comprise: generating precursors from a starting material, transporting the precursors into a reaction chamber, absorbing the precursors onto a heated article, chemically reacting the precursor with the surface of the article to be coated to form a deposit and a gaseous by-product, and removing the gaseous by-product and unreacted gaseous precursors from the reaction chamber. The metal oxide interruption layer may, however, be formed by co-deposition of materials. To achieve this, a mixture of two precursors, such as a first metal-containing oxide precursor (A) and a second metal-containing oxide precursor (B), may be co-injected (AxBy) at any number of ratios, similarly to the ALD technique, into the chamber and deposited on the surface of the article.
- Unlike other techniques typically used to deposit coatings on components having high aspect ratio features, such as plasma spray coating and ion assisted deposition, the ALD and CVD techniques can deposit a layer of material within such features (i.e., on the surfaces of the features). Additionally, the ALD and CVD techniques produce relatively thin (e.g., 10 μm or less) coatings that are porosity-free (i.e., pin-hole free), which may eliminate crack formation during deposition. The term “porosity-free” as used herein means absence of any pores, pin-holes, voids, or cracks along the whole depth of the coating as measured by transmission electron microscopy (TEM). The TEM may be performed using a 100 nm thick TEM lamella prepared by focused ion beam milling, with the TEM operated at 200 kV in bright-field, dark-field, and high-resolution mode. In contrast, with conventional e-beam IAD or plasma spray techniques, cracks form upon deposition even at thicknesses of 5 or 10 μm and the porosity may be 1-3% or even higher.
- Plasma resistant protective coatings may be deposited on a variety of articles. In some embodiments, process chamber components, such as an electrostatic chuck, a nozzle, a gas distribution plate, a showerhead, an electrostatic chuck component, a chamber wall, a liner, a liner kit, a gas line, a lid, a chamber lid, a nozzle, a single ring, a processing kit ring, a base, a shield, a plasma screen, a flow equalizer, a cooling base, a chamber viewport, a bellow, a faceplate, selectivity modulating device, plasma generation units (e.g., radiofrequency electrodes with housings), and diffusers, would benefit from having these plasma resistant protective coatings to protect the components in harsh environments with corrosive plasmas. Many of these chamber components have high aspect ratios that range from about 10:1 to about 300:1 and other complex shapes which makes them difficult to coat well using conventional deposition methods. Embodiments described herein enable high aspect ratio articles such as the aforementioned process chamber components to be coated with plasma resistant protective coatings that protect the articles.
- Examples of processing gases that may be used to process substrates in the processing chamber include halogen-containing gases, such as C2F6, SF6, SiCl4, HBr, NF3, CF4, CHF3, CH2F3, F, NF3, Cl2, CCl4, BCl3 and SiF4, among others, and other gases such as O2, or N2O. Examples of carrier gases include N2, He, Ar, and other gases inert to process gases (e.g., non-reactive gases).
-
FIG. 1A depicts one embodiment of adeposition process 100 in accordance with an ALD technique to grow or deposit a plasma resistant protective coating on an article.FIG. 1B depicts another embodiment of adeposition process 102 in accordance with an ALD technique as described herein.FIG. 1C depicts yet another embodiment of adeposition process 104 in accordance with an ALD deposition technique as described herein. Various types of ALD processes exist and the specific type may be selected based on several factors such as the surface to be coated, the coating material, chemical interaction between the surface and the coating material, etc. The general principle for the various ALD processes comprises growing a thin film layer by repeatedly exposing the surface to be coated to pulses of gaseous chemical precursors that chemically react with the surface one at a time in a self-limiting manner. -
FIGS. 1A-1C illustrate anarticle 110 having a surface.Article 110 may represent various process chamber components (e.g., semiconductor process chamber components) including but not limited to an electrostatic chuck, a nozzle, a gas distribution plate, a showerhead, an electrostatic chuck component, a chamber wall, a liner, a liner kit, a gas line, a lid, a chamber lid, a nozzle, a single ring, a processing kit ring, a base, a shield, a plasma screen, a flow equalizer, a cooling base, a chamber viewport, a bellow, a faceplate, selectivity modulating device, and so on. The article 110 (andarticle 230 inFIG. 2 ) may be made from a metal (such as aluminum, stainless steel), a ceramic (such as Y2O3, Al2O3, Y3Al5O12 (YAG), and so forth), a metal-ceramic composite, a polymer, a polymer ceramic composite, mylar, polyester, or other suitable materials, and may further comprise materials such as AlN, Si, SiC, Al2O3, SiO2, and so on. - For ALD, either adsorption of a precursor onto a surface or a reaction of a reactant with the adsorbed precursor may be referred to as a “half-reaction.” During a first half reaction, a precursor is pulsed onto the surface of the article 110 (or onto a layer formed on the article 110) for a period of time sufficient to allow the precursor to fully adsorb onto the surface. The adsorption is self-limiting as the precursor will adsorb onto a finite number of available sites on the surface, forming a uniform continuous adsorption layer on the surface. Any sites that have already adsorbed a precursor will become unavailable for further adsorption with the same precursor unless and/or until the adsorbed sites are subjected to a treatment that will form new available sites on the uniform continuous coating. Exemplary treatments may be plasma treatment, treatment by exposing the uniform continuous adsorption layer to radicals, or introduction of a different precursor able to react with the most recent uniform continuous layer adsorbed to the surface.
- In some embodiments, two or more precursors are injected together and adsorbed onto the surface of an article. The excess precursors are pumped out until an oxygen-containing reactant is injected to react with the adsorbents to form a single metal oxide layer or a multi-metal oxide layer (e.g., of YAG, a phase of Y2O3—ZrO2, and so on). This fresh layer is ready to adsorb the precursors in the next cycle.
- In
FIG. 1A ,article 110 may be introduced to afirst precursor 160 for a first duration until a surface ofarticle 110 is fully adsorbed with thefirst precursor 160 to form anadsorption layer 114. Subsequently,article 110 may be introduced to afirst reactant 165 to react with theadsorption layer 114 to grow a rare-earth oxide layer 116 (e.g., so that the rare-earth oxide layer 116 is fully grown or deposited, where the terms grown and deposited may be used interchangeably herein). Thefirst precursor 160 may be a precursor for yttrium or another metal, for example. Thefirst reactant 165 may be oxygen, water vapor, ozone, pure oxygen, oxygen radicals, or another oxygen source if the rare-earth layer 116 is an oxide. Accordingly, ALD may be used to form the rare-earth oxide layer 116. - In an example where the rare-
earth oxide layer 116 is a yttria (Y2O3) rare-earth oxide layer, article 110 (e.g., an Al6061 substrate with or without an Alumina buffer layer) may be introduced to a first precursor 160 (e.g., tris(methylcyclopentadienyl) yttrium) for a first duration until all the reactive sites on the surface are consumed. The remainingfirst precursor 160 is flushed away and then afirst reactant 165 of H2O is injected into the reactor to start the second half cycle. A rare-earth oxide layer 116 of Y2O3 is formed after H2O molecules react with the Y containing adsorption layer created by the first half reaction. - Rare-
earth oxide layer 116 may be uniform, continuous and conformal. The rare-earth oxide layer 116 may be porosity free (e.g., have a porosity of 0) or have an approximately 0 porosity in embodiments (e.g., a porosity of 0% to 0.01%).Layer 116 may have a thickness of less than one atomic layer to a few atoms in some embodiments after a single ALD deposition cycle. Some metalorganic precursor molecules are large. - Multiple full ALD deposition cycles may be implemented to deposit a thicker rare-
earth oxide layer 116, with each full cycle (e.g., including introducingprecursor 160, flushing, introducingreactant 165, and again flushing) adding to the thickness by an additional fraction of an atom to a few atoms. As shown, up to n full cycles may be performed to grow the rare-earth oxide layer 116, where n is an integer value greater than 1. In embodiments, rare-earth oxide layer 116 may have a thickness of about 500 angstroms to about 10000 angstroms, about 500 angstroms to about 5000 angstroms, about 1000 angstroms to about 5000 angstroms, or about 1500 angstroms to about 2500 angstroms. - Since ALD is used for the deposition, the internal surfaces of high aspect ratio features such as gas delivery holes in a showerhead or a gas delivery line may be coated, and thus an entirety of a component may be protected from exposure to a corrosive environment.
-
Layer 116 may be Y2O3, such as crystalline Y2O3 having a single cubic phase, in embodiments. In one embodiment, the yttrium oxide cubic phase may display an X-Ray Diffraction profile that corresponds to a Powder Dispersion File No. 04-005-4378. - It should be understood that in some embodiments,
layer 116 may comprise more than one rare-earth metal. Depositing a multi-elemental rare earth oxide layer via ALD may occur through sequential deposition as described regarding the metal oxide layer inFIG. 1B or co-deposition as described in more detail inFIG. 1C . - Subsequently,
article 110 havinglayer 116 may be introduced to an additional precursor(s) 170 for a second duration until a surface of rare-earth oxide layer 118 is fully adsorbed with the additional precursor(s) 170 to form anadsorption layer 118. Subsequently,article 110 may be introduced to areactant 175 to react withadsorption layer 118 to grow an amorphous or a crystalline single phase or multiphasemetal oxide layer 120, also referred to as theinterruption layer 120 for simplicity (e.g., so that theinterruption layer 120 is fully grown or deposited). Accordingly, theinterruption layer 120 is fully grown or deposited over rare-earth oxide layer 116 using ALD. In an example,precursor 170 may be a zirconium containing precursor (e.g., tris(dimethylamino)cyclopentadienyl zirconium) used in the first half cycle, andreactant 175 may be ozone used in the second half cycle. - The
interruption layer 120 forms the amorphous or crystalline single phase or multiphase metal oxide layer, which may be uniform, continuous and conformal. Thesecond layer 120 may have a very low porosity of less than 1% in embodiments, and less than 0.1% in further embodiments, and about 0% in embodiments or porosity-free in still further embodiments.Second layer 120 may have a thickness of less than an atom to a few atoms (e.g., 2-3 atoms) after a single full ALD deposition cycle. Multiple ALD deposition stages may be implemented to deposit athicker interruption layer 120, with each stage adding to the thickness by an additional fraction of an atom to a few atoms. As shown, the full deposition cycle may be repeated m times to cause theinterruption layer 120 to have a target thickness, where m is an integer value greater than 1. In embodiments,interruption layer 120 may have a thickness of about 1 angstroms to about 500 angstroms, about 2 angstroms to about 200 angstroms, or about 3 angstroms to about 50 angstroms. - A ratio of the rare-earth oxide layer thickness to the interruption layer thickness may be about 5000:1 to about 1:1 or about 2500:1. In some embodiments, the ratio of rare-earth oxide thickness to the interruption layer thickness may be about 500:1 to about 1:1. In yet other embodiments, the ratio of rare-earth oxide thickness to the interruption layer thickness may be about 2500:8, about 2500:12, or about 2500:16. The ratio of rare-earth oxide layer to the interruption layer may be such that the protective coating provides improved corrosion and erosion resistance as well as improved resistance to cracking and/or delamination caused by chamber processing. The thickness ratio may be selected in accordance with specific chamber applications.
- As shown in
FIGS. 4A and 4B , yttrium oxide layer deposited without an interruption layer result in uncontrollable and abnormally large grain growth. For instance, abnormally large yttrium oxide grains shown inFIGS. 4A and 4B may have a height of about 100 nm and a width of about 200 nm. These abnormally large grains lead to higher surface roughness and make the coating more prone to defect. This phenomenon is apparent with a yttrium oxide coating of 600 nm thickness and will become even more pronounced with a yttrium oxide coating of greater thickness (see for examplesFIG. 14A for grains in a 1 μm thick yttria coating without interruption layers). Furthermore, the lack of interruption layers provides chemicals a direct pathway to diffuse through cracks and spaces between large grains and reach the interface between the coating and the article, potentially harming the coated article. -
FIG. 4C illustrates interruption layers between layers of yttrium oxide (i.e., after every layer of yttrium oxide with a thickness of 250 nm a carbon-rich yttrium oxide interruption layer was deposited). Indeed, the yttrium oxide grain growth is more controlled and so are the surface boundaries and surface roughness. None of the grains inFIG. 4C exceed 100 nm in length of 200 nm in width. Furthermore, there is no direct pathway from the corrosive chamber environment all the way through the coating to the interface between the coating and the article. However, the high carbon content in the interruption layer, makes the layer relatively weak. As a result, during processing, upon the exertion of the compressive stress on the protective coating, the top yttrium oxide layer buckles up and begins to laminate, as depicted inFIG. 4C . Such delamination generates particles and affects the lifetime of the coated article, the lifetime of the coating, and wafer processing. Compressive stress is exerted after fluorination, when the crystalline lattice of the protective coating begins to expand. - If the interruption layer was stronger than the carbon interruption layers, the yttrium oxide layers and interruption layers would remain connected and would not buckle up. A stronger interruption layer is believed to be one that has a similar composition to the yttrium oxide layer but a dissimilar atomic crystalline phase that would inhibit uncontrollable grain growth. Thus, the decision as to the type of metal oxide layer selected for the interruption layer, the type of rare-earth oxide layer selected, and their corresponding thicknesses, should account for the need to control grain growth of the rare earth oxide, while also ensuring a sufficiently strong bond between the rare earth oxide layer and the interruption layer so as to prevent delamination and particle generation.
-
Interruption layer 120 may be any of the aforementioned rare-earth metal-containing oxide layers as well as zirconium oxide, aluminum oxide and mixtures thereof. For example, theinterruption layer 120 may be ZrO2, alone or in combination with one or more other rare earth metal oxides. In some embodiments,interruption layer 120 is a crystalline single phase or multiphase material having a one or more atomic crystalline phases formed from a single metal oxide or a mixture of at least two metal oxide precursors that have been sequentially deposited or co-deposited by ALD. For example,interruption layer 120 may be one of La2O3, Pr2O3, Nd2O3, Sm2O3, Eu2O3, Gd2O3, Tb2O3, Dy2O3, Ho2O3, Er2O3, Tm2O3, Yb2O3, ZrO2, and combinations thereof (as depicted inFIG. 3 ). In certain embodiments, the interruption layer may be amorphous. In embodiments when the interruption layer is crystalline, the one or more crystalline atomic phases of the interruption layer may be different from the one or more crystalline atomic phase of the rare-earth oxide layer. In embodiments when at least one of the crystalline atomic phases of the interruption layer is the same as the at least one crystalline atomic phase of the rare-earth oxide layer, the lattice structure of the similar crystalline atomic phases may differ. For instance, the atomic crystalline phase(s) may be selected from the group consisting of hexagonal, tetragonal, cubic, monoclinic, and combinations thereof. - In some embodiments,
first layer 116 andsecond layer 120 may, independently, include a material such as Y2O3 and Y2O3 based ceramics, Y3Al5O12 (YAG), Al2O3 (alumina), Y4Al2O9 (YAM), ErAlO3, GdAlO3, NdAlO3, YAlO3, TiO2 (titania), ZrO2 (zirconia), Y2O3 stabilized ZrO2 (YSZ), Er2O3 and Er2O3 based ceramics, Gd2O3 and Gd2O3 based ceramics, Er3Al5O12 (EAG), Gd3Al5O12 (GAG), Nd2O3 and Nd2O3 based ceramics, a ceramic compound comprising Y2O3 and YF3 (e.g., Y—O—F), a ceramic compound comprising Y4Al2O9 and a solid-solution of Y2O3—ZrO2, a ceramic compound comprising Y2O3, Er2O3, ZrO2, Gd2O3 and SiO2, or a combination of any of the above. - The material of
first layer 116 andsecond layer 120 may also be based on a solid solution formed by any of the aforementioned ceramics. The material may also be a multiphase material that includes a solid solution of one or more of the aforementioned materials and one or more additional phase. - With reference to the solid-solution of Y2O3—ZrO2, the material may include Y2O3 at a concentration of 10-90 molar ratio (mol %) and ZrO2 at a concentration of 10-90 mol %. In some examples, the solid-solution of Y2O3—ZrO2 may include 10-20 mol % Y2O3 and 80-90 mol % ZrO2, may include 20-30 mol % Y2O3 and 70-80 mol % ZrO2, may include 30-40 mol % Y2O3 and 60-70 mol % ZrO2, may include 40-50 mol % Y2O3 and 50-60 mol % ZrO2, may include 60-70 mol % Y2O3 and 30-40 mol % ZrO2, may include 70-80 mol % Y2O3 and 20-30 mol % ZrO2, may include 80-90 mol % Y2O3 and 10-20 mol % ZrO2, and so on.
- With reference to the ceramic compound comprising Y4Al2O9 and a solid-solution of Y2O3—ZrO2, in one embodiment the ceramic compound includes 62.93 molar ratio (mol %) Y2O3, 23.23 mol % ZrO2 and 13.94 mol % Al2O3. In another embodiment, the ceramic compound can include Y2O3 in a range of 50-75 mol %, ZrO2 in a range of 10-30 mol % and Al2O3 in a range of 10-30 mol %. In another embodiment, the ceramic compound can include Y2O3 in a range of 40-100 mol %, ZrO2 in a range of 0.1-60 mol % and Al2O3 in a range of 0.1-10 mol %. In another embodiment, the ceramic compound can include Y2O3 in a range of 40-60 mol %, ZrO2 in a range of 35-50 mol % and Al2O3 in a range of 10-20 mol %. In another embodiment, the ceramic compound can include Y2O3 in a range of 40-50 mol %, ZrO2 in a range of 20-40 mol % and Al2O3 in a range of 20-40 mol %. In another embodiment, the ceramic compound can include Y2O3 in a range of 80-90 mol %, ZrO2 in a range of 0.1-20 mol % and Al2O3 in a range of 10-20 mol %. In another embodiment, the ceramic compound can include Y2O3 in a range of 60-80 mol %, ZrO2 in a range of 0.1-10 mol % and Al2O3 in a range of 20-40 mol %. In another embodiment, the ceramic compound can include Y2O3 in a range of 40-60 mol %, ZrO2 in a range of 0.1-20 mol % and Al2O3 in a range of 30-40 mol %. In other embodiments, other distributions may also be used for the ceramic compound.
- In one embodiment, the material includes or consists of a ceramic compound that includes a combination of Y2O3, ZrO2, Er2O3, Gd2O3 and SiO2. In one embodiment, the ceramic compound can include Y2O3 in a range of 40-45 mol %, ZrO2 in a range of 0-10 mol %, Er2O3 in a range of 35-40 mol %, Gd2O3 in a range of 5-10 mol % and SiO2 in a range of 5-15 mol %. In a first example, the alternative ceramic compound includes 40 mol % Y2O3, 5 mol % ZrO2, 35 mol % Er2O3, 5 mol % Gd2O3 and 15 mol % SiO2. In a second example, the alternative ceramic compound includes 45 mol % Y2O3, 5 mol % ZrO2, 35 mol % Er2O3, 10 mol % Gd2O3 and 5 mol % SiO2. In a third example, the alternative ceramic compound includes 40 mol % Y2O3, 5 mol % ZrO2, 40 mol % Er2O3, 7 mol % Gd2O3 and 8 mol % SiO2.
- Any of the aforementioned materials may include trace amounts of other materials such as ZrO2, Al2O3, SiO2, B2O3, Er2O3, Nd2O3, Nb2O5, CeO2, Sm2O3, Yb2O3, or other oxides. The materials allow for longer working lifetimes due to the plasma resistance of the ceramic materials and decreased on-wafer or substrate contamination.
- With reference to
FIG. 1B , in some embodiments, the plasma resistant protective coating contains more than two layers. Specifically, the plasma resistant protective coating may include a stack of alternating layers of the rare-earth oxide layer and interruption layer. - Referring to
FIG. 1B , anarticle 110 having a rare-earth oxide layer 116 may be inserted into a deposition chamber. The rare-earth oxide layer 116 may have been formed as set forth with reference toFIG. 1A .FIG. 1B illustrate an ALD process with sequential deposition to form a multi-elemental interruption layer.Article 110 having rare-earth oxide layer 116 may be introduced to one ormore precursors 180 for a duration until a surface of rare-earth oxide layer 116 is fully adsorbed with the one or moreadditional precursors 180 to form anadsorption layer 122. Subsequently,article 110 may be introduced to areactant 182 to react withadsorption layer 122 to grow a solidmetal oxide layer 124. Accordingly, themetal oxide layer 124 is fully grown or deposited over rare-earth oxide layer 116 using ALD. In an example,precursor 180 may be a zirconium containing precursor used in the first half cycle, andreactant 182 may be H2O used in the second half cycle. The metal oxide layer one of La2O3, Pr2O3, Nd2O3, Sm2O3, Eu2O3, Gd2O3, Tb2O3, Dy2O3, Ho2O3, Er2O3, Tm2O3, Yb2O3, ZrO2, Al2O3 or another oxide and combinations thereof. -
Article 110 having rare-earth oxide layer 116 andmetal oxide layer 124 may be introduced to one ormore precursors 184 for a duration until a surface ofmetal oxide layer 124 is fully adsorbed with the one ormore precursors 184 to form anadsorption layer 126.Precursor 184 may be different fromprecursor 180. Subsequently,article 110 may be introduced to areactant 186 to react withadsorption layer 126 to grow an additional solidmetal oxide layer 128. Accordingly, the additionalmetal oxide layer 128 is fully grown or deposited over themetal oxide layer 124 using ALD. In an example,precursor 184 may be a yttrium containing precursor used in the first half cycle, andreactant 186 may be H2O used in the second half cycle. Themetal oxide layer 124 may be one of La2O3, Pr2O3, Nd2O3, Sm2O3, Eu2O3, Gd2O3, Tb2O3, Dy2O3, Ho2O3, Er2O3, Tm2O3, Yb2O3, ZrO2, or another oxide and combinations thereof. - In some embodiments, the metal oxide layer may be crystalline and may be selected from the group consisting of: a composition ranging from a pure crystalline single phase zirconia in at least one of a tetragonal phase or a monoclinic phase to a crystalline multiphase or a crystalline single phase yttrium zirconium oxide with an atomic percentage of zirconium of about 5%, based on the total atoms in the composition; a mixture of about 65 wt % of zirconium oxide in a tetragonal phase and about 35 wt % of zirconium oxide in a monoclinic phase; about 100 wt % multi-elemental oxide of zirconium yttrium oxide in a tetragonal phase; a mixture of about 70 wt % of a multi-elemental oxide of zirconium yttrium oxide in a first cubic phase and about 30 wt % of yttrium oxide in a second cubic phase, wherein the first cubic phase and the second cubic phase have a lattice structure that is different from the lattice structure of the crystalline yttrium oxide layer; and a mixture of about 30 wt % of a multi-elemental oxide of zirconium yttrium oxide in the first cubic phase and about 70 wt % of yttrium oxide in the second cubic phase.
- As shown, the deposition of the
metal oxide 124 and thesecond metal oxide 128 may be repeated x times to form astack 137 of alternating layers, where x is an integer value greater than 1. x may represent a finite number of layers selected based on the targeted thickness and properties. Thestack 137 of alternating layers may be considered as an interruption layer containing multiple alternating sub-layers. Accordingly,precursor 180,reactant 182,precursor 184 andreactant 186 may be repeatedly introduced sequentially to grow or deposit additional alternatinglayers layers - The alternating layers 124-136 described above have a 1:1 ratio, where there is a single layer of a first metal oxide for each single layer of a second metal oxide. However, in other embodiments there may be other ratios such as 2:1, 3:1, 4:1, and so on between the different types of metal oxide layers. For example, three ZrO2 layers may be deposited for every Y2O3 layer in an embodiment. Additionally, the
stack 137 of alternating layers 124-136 have been described as an alternating series of two types of metal oxide layers. However, in other embodiments more than two types of metal oxide layers may be deposited in an alternatingstack 137. For example, thestack 137 may include three different alternating layers (e.g., a first layer of Y2O3, a first layer of Al2O3, a first layer of ZrO2, a second layer of Y2O3, a second layer of Al2O3, a second layer of ZrO2, and so on). - The process of forming
multi-layer stack 137 of metal oxide interruption layer is also referred to herein as sequential deposition. Such sequential deposition may also be used for the rare-earth oxide layer when the rare-earth oxide layer contains more than one rare-earth. - After the
stack 137 of alternating layers has been formed, an anneal process may be performed to cause the alternating layers of different materials to diffuse into one another and form a complex oxide having a single crystalline phase or multiple crystalline phases. After the annealing process, the stack of alternatinglayers 137 may therefore become asingle interruption layer 138. For example, if the layers in the stack are Y2O3, Al2O3, and ZrO2, then the resulting rare-earth metal-containingoxide layer 138 may a ceramic compound comprising Y4Al2O9 and a solid-solution of Y2O3—ZrO2. - In some embodiments, the deposition of rare-
earth oxide layer 116 and interruption layer stack 137 (or 138 if annealed) may be repeated z number of times to form a final plasma resistant protective coating. The final plasma resistant protective coating may comprise alternating layers of rare-earth oxide layers and intermittent metal oxide interruption layers. z may represent a finite number of layers selected based on the targeted thickness and properties of the final plasma resistant protective coating. - Referring to
FIG. 1C , anarticle 110 having a rare-earth oxide layer 116 may be inserted into a deposition chamber. The rare-earth oxide layer 116 may have been formed as set forth with reference toFIG. 1A .Article 110 having rare-earth oxide layer 116 may be introduced, in some embodiments, to a plurality ofprecursors earth oxide layer 116 is fully adsorbed with the plurality ofprecursors multi-elemental adsorption layer 140. Subsequently,article 110 may be introduced to areactant 192 to react withadsorption layer 140 to grow a solid multi-elementalmetal oxide layer 142. Accordingly, the multi-elementalmetal oxide layer 142 is fully grown or deposited over rare-earth oxide layer 116 using ALD. The process of introducing theprecursors reactant 192 may be repeated y times to cause the multi-elemental metaloxide interruption layer 142 to have a target thickness and ultimately form an amorphous or a crystalline single phase or multiphase interruption layer. InFIG. 2C , y is an integer greater than 1. - The process of forming
interruption layer 142 inFIG. 1C is also referred to herein as co-deposition deposition. Such co-deposition may also be used for the rare-earth oxide layer when the rare-earth oxide layer contains more than one rare-earth. - The deposition of the rare-
earth oxide layer 116 andinterruption layer 142 may be repeated z times to form a stack of alternating layers which form the final plasma resistant protective coating. z may be an integer value greater than 1. z may represent a finite number of layers selected based on the targeted thickness and properties of the final plasma resistant protective coating. - The final structure shown in
FIGS. 1A-1B are a cross sectional side view of anarticle 110 coated with a bilayer plasma resistant protective coating that comprises a crystalline rare-earth oxide layer 116 and an amorphous or a crystalline interruption layer 120 (perFIG. 1A ), 137 or 138 (perFIG. 1B ). The final structure shown inFIG. 1C is a cross sectional side view of anarticle 110 coated with a multilayer plasma resistant protective coating that comprises a rare-earth oxide layer 116 and amorphous or crystalline interruption layers 142. The crystalline rare-earth oxide layer 116 may be yttrium oxide in a cubic phase with a first lattice structure in some embodiments. The crystalline oramorphous interruption layer earth oxide layer 116. - Interruption layers 116 and 120, 137/138, or 142 may be, independently, selected from the list of materials enumerated above.
- The crystalline rare-
earth oxide layer 116 may have a thickness of about 500 angstroms to about 5000 angstroms. In embodiments, the rare-earth oxide layer may have a thickness of about 1000-5000 angstroms. In further embodiments, the rare-earth oxide layer 116 may have a thickness of about 1500-2500 angstroms. - The
interruption layer interruption layer interruption layer - In further embodiments, the plasma resistant protective coating may have a thickness of about 500 nm to about 5 μm. In further embodiments, the plasma resistant protective coating may have a thickness of about 1 μm to about 5 μm, or about 1 μm to about 2 μm. The interruption layers 120, 137, 138, or 142 between the rare-earth
metal oxide layers 116 may inhibit uncontrollable and abnormally large crystal growth in the rare-earth oxide layers. - In the embodiments described with reference to
FIGS. 1A-1C , the surface reactions (e.g., half-reactions) may be done sequentially, i.e. where the various precursors and reactants are not in contact. Prior to introduction of a new precursor or reactant, the chamber in which the ALD process takes place may be purged with an inert carrier gas (such as nitrogen or air) to remove any unreacted precursor and/or surface-precursor reaction byproducts. The precursors may be different for each layer. In some embodiments, the surface reactions may be done through co-deposition, i.e., where at least two precursors are used, in some embodiments at least three precursors are used and in yet further embodiments at least four precursors are used. Prior to the introduction of one or more reactants, the plurality of precursors may be co-injected into the ALD chamber. The ALD chamber may be purged with an inert carrier gas (such as nitrogen or air) to remove any unreacted precursors and/or surface-precursor reaction byproducts. - ALD processes may be conducted at various temperatures depending on the type of process. The optimal temperature range for a particular ALD process is referred to as the “ALD temperature window.” Temperatures below the ALD temperature window may result in poor growth rates and non-ALD type deposition. Temperatures above the ALD temperature window may result in reactions taken place via a chemical vapor deposition (CVD) mechanism. The ALD temperature window may range from about 100° C. to about 400° C. In some embodiments, the ALD temperature window is between about 120-300° C.
- The ALD process allows for a conformal plasma resistant protective coating having uniform thickness on articles and surfaces having complex geometric shapes, holes with high aspect ratios, and three-dimensional structures. Sufficient exposure time of each precursor to the surface enables the precursor to disperse and fully react with the surface in its entirety, including all of its three-dimensional complex features. The exposure time utilized to obtain conformal ALD in high aspect ratio structures is proportionate to the square of the aspect ratio and can be predicted using modeling techniques. Additionally, the ALD technique is advantageous over other commonly used coating techniques because it allows in-situ on demand material synthesis of a particular composition or formulation without the need for a lengthy and difficult fabrication of source materials (such as powder feedstock and sintered targets). In some embodiments ALD is used to coat articles aspect ratios of about 10:1 to about 300:1.
- With the ALD techniques described herein, multi-component films can be grown, deposited or co-deposited, for example, by proper mixtures of the precursors used to grow the interruption layer as described above and in more detail in the examples below.
- In some embodiments, the plasma resistant protective coating may be deposited on a surface of an article via CVD. An exemplary CVD system is illustrated in
FIG. 2 . The system comprises a chemical vaporprecursor supply system 205 and aCVD reactor 210. The role of the vaporprecursor supply system 205 is to generatevapor precursors 220 from a startingmaterial 215, which could be in a solid, liquid, or gas form. The vapors may subsequently be transported intoCVD reactor 210 and get deposited as a plasma resistantprotective coat 225 and/or 245 on the surface ofarticle 230, in accordance with an embodiment, which may be positioned onarticle holder 235. - The plasma resistant protective coating depicted in
FIG. 2 comprises a bilayer of a crystalline single phase or multiphase rare-earth oxide layer 225 and an amorphous or a crystalline single phase or multiphase metaloxide interruption layer 245. It is understood by one of ordinary skill in the art that although only a bilayer is exemplified with respect to the CVD process, a multilayer plasma resistant protective coating is also contemplated herein with respect to a CVD process. A multilayer plasma resistant protective coating comprising a stack of alternating layers of a (poly)crystalline single phase or multiphase rare-earth oxide and an amorphous or (poly)crystalline single phase or multiphase metal oxide interruption layers deposited by CVD are contemplated in certain embodiments herein. -
CVD reactor 210heats article 230 to a depositiontemperature using heater 240. In some embodiments, the heater may heat the CVD reactor's wall (also known as “hot-wall reactor”) and the reactor's wall may transfer heat to the article. In other embodiments, the article alone may be heated while maintaining the CVD reactor's wall cold (also known as “cold-wall reactor”). It is to be understood that the CVD system configuration should not be construed as limiting. A variety of equipment could be utilized for a CVD system and the equipment is chosen to obtain optimum processing conditions that may give a coating with uniform thickness, surface morphology, structure, and composition. - The various CVD techniques include the following phases: (1) generate active gaseous reactant species (also known as “precursors”) from the starting material; (2) transport the precursors into the reaction chamber (also referred to as “reactor”); (3) absorb the precursors onto the heated article; (4) participate in a chemical reaction between the precursor and the article at the gas-solid interface to form a deposit and a gaseous by-product; and (5) remove the gaseous by-product and unreacted gaseous precursors from the reaction chamber.
- Suitable CVD precursors may be stable at room temperature, may have low vaporization temperature, can generate vapor that is stable at low temperature, have suitable deposition rate (low deposition rate for thin film coatings and high deposition rate for thick film coatings), relatively low toxicity, be cost effective, and relatively pure. For some CVD reactions, such as thermal decomposition reaction (also known as “pyrolysis”) or a disproportionation reaction, a chemical precursor alone may suffice to complete the deposition.
- CVD has many advantages including its capability to deposit highly dense and pure coatings and its ability to produce uniform films with good reproducibility and adhesion at reasonably high deposition rates. Layers deposited using CVD in embodiments may have a porosity of below 1%, and a porosity of below 0.1% (e.g., around 0%). Therefore, it can be used to uniformly coat complex shaped components and deposit conformal films with good conformal coverage (e.g., with substantially uniform thickness). CVD may also be utilized to deposit a film made of a plurality of components, for example, by feeding a plurality of chemical precursors at a predetermined ratio into a mixing chamber and then supplying the mixture to the CVD reactor system.
- The CVD and ALD processes described herein may be used to form a plasma resistant protective coat that is resistant to erosion and/or corrosion in embodiments. Plasma resistant protective coat deposited by ALD or CVD may comprise a stack of alternating layers of crystalline rare-earth oxide layers and amorphous or crystalline interruption layers. In one embodiment, the plasma resistant protective coating may be a bilayer of a crystalline rare-earth oxide layer and an amorphous or crystalline interruption layer. When the plasma resistant protective coating comprises a stack of alternating layers, the first layer may be a rare-earth oxide layer. The amorphous or crystalline interruption layers may inhibit crystal/grain growth in the crystalline rare-earth oxide layers such that the grain size in the rare-earth oxide layer does not exceed the thickness of the rare-earth oxide layer and in some embodiments, so that the grain size does not exceed 100 nm or 200 nm.
- The rare-earth oxide layers may have one or more atomic crystalline phases. The interruption layers may have one or more atomic crystalline phases that is/are different from the atomic crystalline phase(s) of the rare-earth oxide layer so as to inhibit crystal growth of the rare-earth oxide crystals. For instance, in one embodiment, the rare-earth oxide layers may be yttrium oxide layers in the cubic phase. In one embodiment, the interruption layers may be zirconium oxide layers in the tetragonal and monoclinic phases.
- When the rare-earth oxide layer or the interruption layer contains more than one metal oxide, the materials forming each layer may be deposited sequentially or co-deposited (as described in detail for the ALD process through
FIGS. 1A-1C ). In some embodiments, layers containing more than one metal oxide may be subject to post coating heat treatment. In some embodiments, each layer in the plasma resistant protective coating or the final plasma resistant protective coat may be subject to post coating processing to form one or more features therein. - Exemplary yttrium-containing precursors that may be utilized with the CVD and ALD coating deposition techniques include, but are not limited to, tris(N,N-bis(trimethylsilyl)amide)yttrium (III), yttrium (III)butoxide, tris(cyclopentadienyl)yttrium(III), and Y(thd)3 (thd=2,2,6,6-tetramethyl-3,5-heptanedionato).
- Exemplary erbium-containing precursors that may be utilized with the ALD and CVD coating deposition techniques include, but are not limited to, tris-methylcyclopentadienyl erbium (III) (Er(MeCp)3), erbium boranamide (Er(BA)3), Er(TMHD)3, erbium(III) tris(2,2,6,6-tetramethyl-3,5-heptanedionate), and tris(butylcyclopentadienyl)erbium(III).
- Exemplary aluminum-containing precursors that may be utilized with the ALD and CVD coating deposition techniques include, but are not limited to, diethylaluminum ethoxide, tris(ethylmethylamido)aluminum, aluminum sec-butoxide, aluminum tribromide, aluminum trichloride, triethylaluminum, triisobutylaluminum, trimethylaluminum, and tris(diethylamido) aluminum.
- Exemplary zirconium-containing precursors that may be utilized with the ALD and CVD coating deposition techniques include, but are not limited to, zirconium (IV) bromide, zirconium (IV) chloride, zirconium (IV) tert-butoxide, tetrakis(diethylamido)zirconium (IV), tetrakis(dimethylamido)zirconium (IV), and tetrakis(ethylmethylamido)zirconium (IV).
- Exemplary oxygen-containing reactants that may be utilized with the various coating deposition techniques identified herein and their equivalent include, but are not limited to, ozone, water vapor, oxygen, and oxygen radicals.
-
FIG. 11 illustrates amethod 300 for forming a plasma resistant protective coating comprising a rare-earth oxide layer and a metal oxide interruption layer on an article such as a process chamber component according to embodiments.Method 300 may be used to coat any articles including articles having aspect ratios of about 3:1 to about 300:1 (e.g., aspect ratios of 20:1, 50:1, 100:1, 150:1, and so on). The method may optionally begin by selecting a composition for the rare-earth oxide layer and for the metal oxide interruption layer of the plasma resistant protective coating and by selecting a thickness for each of these layers. The composition of the rare-earth oxide layer and the composition of the metal oxide interruption layer may be selected from any of the materials contemplated hereinabove. The thickness selected for the rare-earth oxide layer and for the metal oxide interruption layer and the ratio among them may also be selected from any of the thicknesses and ratios contemplated hereinabove. The composition selection, thickness selection, and method of forming may be performed by the same entity or by multiple entities. - At
block 310, the article is loaded into an ALD or a CVD deposition chamber. At block 320, the method comprises depositing a plasma resistant protective coating onto a surface of the article using ALD or CVD. In one embodiment, at block 325 ALD or CVD is performed to deposit or co-deposit (for a multi-elemental layer) a rare-earth oxide layer. The rare-earth oxide layer may comprise yttrium oxide and have a cubic crystalline phase in one embodiment. In one embodiment, atblock 330 ALD or CVD is performed to deposit or co-deposit (for a multi-elemental layer) a metal oxide interruption layer. The metal oxide interruption layer may have an atomic crystalline phase different from the cubic phase of the crystalline rare-earth oxide layer. The metal oxide interruption layer may be amorphous. - ALD and CVD are very conformal processes as performed in embodiments, which may cause the surface roughness of the plasma resistant protective coating to match a surface roughness of an underlying surface of the article that is coated. The plasma resistant protective coating may have a total thickness of about 500 nm to about 10 μm or about 500 nm to about 5 μm in some embodiments. In other embodiments, the plasma resistant protective coating may have a thickness of about 500 nm to about 1 μm. The plasma resistant protective coating may have a porosity of about 0% in embodiments, or may be porosity-free in embodiments, and may have a thickness variation across different sections of the coating of about +/−5% or less, +/−10% or less, or +/−20% or less.
- At
block 335, a determination may be made as to whether additional layers are to be added to the plasma resistant protective coating (e.g., if a multi-layer stack is to be formed). If additional layers are to be added, then the method may return to block 320 and an additional rare-earth oxide layer and metal oxide interruption layer may be formed via ALD or CVD. Otherwise the plasma resistant protective coating may be fully formed and the method may reach its end. - Depending on the composition of the rare-earth oxide layer, block 325 may comprise one or more cycles of ALD or CVD to deposit a rare-earth oxide with a target thickness. The target thickness of the rare-earth oxide layer may range from 500 angstroms to about 5000 angstroms. In some embodiment, the rare-earth oxide layer may be a multi-elemental rare earth oxide layer. A multi-elemental rare earth oxide layer may be deposited through sequential ALD or CVD deposition or through co-deposition by co-injecting a plurality of precursors simultaneously into a deposition chamber. The various ALD techniques are described in more detail with respect to
FIGS. 1A-1C and it is understood that similar mechanisms may be utilized with a CVD process as well. - Similarly, depending on the composition of the metal oxide interruption layer, block 330 may comprise one or more cycles of ALD or CVD to deposit a metal oxide interruption layers with a target thickness. The target thickness of a metal oxide interruption layer may range from about 1 angstrom to about 500 angstroms. In some embodiment, the metal oxide interruption layer may be a multi-elemental metal oxide interruption layer. A multi-elemental metal oxide interruption layer may be deposited through sequential ALD or CVD deposition or through co-deposition by co-injecting a plurality of precursors simultaneously into a deposition chamber. The various ALD techniques are described in more detail with respect to
FIGS. 1A-1C and it is understood that similar mechanisms may be utilized with a CVD process as well. - The resistance of the coating material to plasma is measured through “etch rate” (ER), which may have units of micron/hour (μm/hr), throughout the duration of the coated components' operation and exposure to plasma. Measurements may be taken after different processing times. For example, measurements may be taken before processing, after 50 processing hours, after 150 processing hours, after 200 processing hours, and so on. Variations in the composition of the plasma resistant protective coating grown or deposited on the showerhead or on any other process chamber component may result in multiple different plasma resistances or erosion rate values. Additionally, a plasma resistant protective coating with a single composition exposed to various plasmas could have multiple different plasma resistances or erosion rate values. For example, a plasma resistant material may have a first plasma resistance or erosion rate associated with a first type of plasma and a second plasma resistance or erosion rate associated with a second type of plasma. In embodiments, no detectable erosion occurred after exposure to a 200 W NF3 direct capacitive coupled plasma at 450° C. for 2 hours.
- The following examples are set forth to assist in understanding the embodiments described herein and should not be construed as specifically limiting the embodiments described and claimed herein. Such variations, including the substitution of all equivalents now known or later developed, which would be within the purview of those skilled in the art, and changes in formulation or minor changes in experimental design, are to be considered to fall within the scope of the embodiments incorporated herein. These examples may be achieved by performing
method 300 described above. -
FIG. 5A depicts a plasma resistant protective coating deposited on an Al2O3 buffer layer 520A that is deposited on an aluminum substrate of Al 6061 510A. A rare-earth oxide layer 530A of crystalline yttrium oxide was deposited on the aluminum oxide buffer layer using atomic layer deposition. The deposition of the crystalline yttrium oxide layer occurred by injecting a yttrium-containing precursor into the deposition chamber containing the article to cause the yttrium-containing precursor to adsorb onto the surface of the article to form a first half reaction. Thereafter, an oxygen-containing reactant may have been injected into the deposition chamber to form a second half-reaction. This deposition cycle may have been repeated until the target thickness was obtained. - Subsequently, an
interruption layer 540A of multiphase crystalline zirconium oxide layer was deposited on the single phase crystalline yttrium oxide layer using atomic layer deposition. The deposition of the multiphase crystalline zirconium oxide layer occurred by injecting a metal-containing precursor (e.g., zirconium-containing precursor) into the deposition chamber containing the article to cause the metal-containing precursor (e.g., zirconium-containing precursor) to adsorb onto the surface of the article to form a first half reaction. Thereafter, an oxygen-containing reactant may have been injected into the deposition chamber to form a second half-reaction. This deposition cycle may have been repeated until the target thickness was obtained. - These depositions were repeated for several cycles to form a stack of alternating layers of single phase crystalline yttrium oxide layers (530A, 550A, 570A, 590A) and multiphase crystalline zirconium oxide layers (540A, 560A, 580A).
- The
first layer 530A in the plasma resistant protective coating was a single phase crystalline yttrium oxide layer. The crystalline yttrium oxide layers had about 95-100 wt % cubic phase corresponding to a Powder Diffraction File (PDF) No. 04-005-4378. The single phase crystalline yttrium oxide layers demonstrated an X-Ray Diffraction (XRD) profile as depicted inFIG. 6A . - The intermittent zirconium oxide layers in the plasma resistant protective coating were multiphase crystalline with about 65.1±5 wt % of a tetragonal crystalline phase (also referred to as Tazheranite) and about 34.9±5 wt % of a monoclinic crystalline phase (also referred to as Baddeleyite). The tetragonal crystalline phase of zirconia corresponds to a PDF No. 01-070-8758. The monoclinic crystalline phase of zirconia corresponds to a PDF No. 01-070-8739. The multiphase crystalline zirconium oxide layers demonstrated an XRD profile as depicted in
FIG. 6B . - The thickness of the each of the rare earth oxide layers (i.e., the crystalline yttrium oxide layers) was about 240 nm to about 260 nm and the thickness of the interruption layers (i.e., the multiphase crystalline zirconium oxide layers) was about 0.5 nm to about 1.5 nm.
- The zirconium oxide interruption layers in the plasma resistant protective coating were characterized using inter alia Transmission Electron Microscopy and Energy Dispersive Spectroscopy (TEM/EDS) line scan. For analysis via TEM/EDS, the interruption layer of multiphase crystalline zirconium oxide was deposited with a thickness that was sufficient to generate the atomic distribution of the various atoms in the layer. The line scan is depicted in
FIG. 6C . The composition demonstrated between 20 nm and 60 nm in the line scan corresponds to the composition of the multiphase crystalline zirconium oxide interruption layer.FIG. 6C illustrates that the multiphase crystalline zirconium oxide interruption layer comprises about 25 atomic % of zirconium and about 75 atomic % of oxygen. -
FIG. 6D depicts a high Angle Annular Dark Field (HAADF) Scanning Transmittion Electron Microscopy (STEM) image of the multiphase crystalline zirconium oxide interruption layer that was analyzed via TEM/EDS inFIG. 6C .Region 610 depicts Al6061,region 620 depicts the alumina buffer layer, andregion 630 depicts the exemplary multiphase crystalline zirconium oxide interruption layer that was analyzed via TEM/EDS inFIG. 6C .FIG. 6D also shows that the multiphase crystalline zirconium oxide layer deposited by ALD covers the Al6061 and alumina buffer layer conformally and uniformally with low to no porosity. -
FIG. 5B depicts a plasma resistant protective coating deposited on an Al2O3 buffer layer 520B that is deposited on an aluminum substrate of Al 6061 510B. A rare-earth oxide layer 530B of crystalline yttrium oxide was deposited on the aluminum oxide buffer layer using atomic layer deposition. Subsequently, aninterruption layer 540B of crystalline zirconium yttrium oxide layer (e.g., a solid solution of Y2O3—ZrO2) was deposited on the crystalline yttrium oxide layer using atomic layer deposition. The crystalline yttrium oxide layer and crystalline zirconium yttrium oxide layer may have been deposited in a manner similar to that described in Example 1. -
Interruption layer 540B was deposited through sequential atomic layer deposition. Specifically, one cycle of zirconium oxide was deposited via atomic layer deposition, followed by one cycle of yttrium oxide deposited via atomic layer deposition. These two cycles (one cycle of ZrO2 and one cycle of Y2O3) will be together referred to as a supercycle.Interruption layer 540B was fully grown after 4 supercycles. - The depositions of the single phase crystalline yttrium oxide layer and single phase crystalline zirconium yttrium oxide interruption layers were repeated for several cycles to form a stack of alternating layers of crystalline yttrium oxide layers (530B, 550B, 570B, 590B) and crystalline zirconium yttrium oxide layers (540B, 560B, 580B).
- The
first layer 530B in the plasma resistant protective coating was a single phase crystalline yttrium oxide layer. The single phase crystalline yttrium oxide layers had an about 95-100 wt % cubic phase corresponding to a Powder Diffraction File (PDF) No. 04-005-4378. The single phase crystalline yttrium oxide layers demonstrated an X-Ray Diffraction (XRD) profile as depicted inFIG. 6A . - The intermittent zirconium yttrium oxide layers in the plasma resistant protective coating were single phase crystalline with an about 95-100 wt % tetragonal crystalline phase. The tetragonal crystalline phase of zirconium yttrium oxide corresponds to a PDF No. 01-082-1243. The crystalline zirconium yttrium oxide layers demonstrated an XRD profile as depicted in
FIG. 7A . The XRD profile depicted inFIG. 7A and the corresponding PDF No. correlate with Zr0.86Y0.14O1.93 chemical formula. - The thickness of the each of the rare earth oxide layers (i.e., the crystalline yttrium oxide layers) was about 240 nm to about 260 nm and the thickness of the interruption layers (i.e., the crystalline zirconium yttrium oxide layers) was about 0.5 nm to about 1.5 nm, or about 0.8 nm.
- The zirconium yttrium oxide interruption layers in the plasma resistant protective coating were characterized using inter alia Transmission Electron Microscopy and Energy Dispersive Spectroscopy (TEM/EDS) line scan. For analysis via TEM/EDS, the interruption layer of crystalline zirconium yttrium oxide was deposited with a thickness that was sufficient to generate the atomic distribution of the various atoms in the layer. The line scan is depicted in
FIG. 7B . The composition demonstrated between 40 nm and 90 nm in the line scan corresponds to the composition of the crystalline zirconium yttrium oxide interruption layer.FIG. 7B illustrates that the crystalline zirconium yttrium oxide interruption layer comprises about 10-15 atomic % of yttrium, about of 20-25 atomic % of zirconium and about 60-65 atomic % of oxygen. -
FIG. 7C depicts a high Angle Annular Dark Field (HAADF) Scanning Transmission Electron Microscopy (STEM) image of the crystalline zirconium yttrium oxide interruption layer that was analyzed via TEM/EDS inFIG. 7B .Region 710 depicts Al6061,region 720 depicts the alumina buffer layer, andregion 730 depicts the exemplary multiphase crystalline zirconium oxide interruption layer that was analyzed via TEM/EDS inFIG. 7B .FIG. 7C also shows that the crystalline zirconium yttrium oxide layer deposited by ALD covers the Al6061 and alumina buffer layer conformally and uniformally with low to no porosity. -
FIGS. 7D and 7E depicts Transmission Electron Microscopy (TEM) images of a crystalline zirconium yttrium oxide layer and further demonstrate the conformal, uniform, and porosity free coating obtained through atomic layer deposition. -
FIG. 5C depicts a plasma resistant protective coating deposited on an Al2O3 buffer layer 520C that is deposited on an aluminum substrate of Al 6061 510C. A rare-earth oxide layer 530C of single phase crystalline yttrium oxide was deposited on the aluminum oxide buffer layer using atomic layer deposition. Subsequently, aninterruption layer 540C of a mixed multiphase crystalline yttrium zirconium oxide (e.g., a Y2O3—ZrO2 solid solution) and yttrium oxide layer was deposited on the single phase crystalline yttrium oxide layer using atomic layer deposition. The single phase crystalline yttrium oxide layer and multiphase crystalline yttrium zirconium oxide interruption layer may have been deposited in a manner similar to that described in Example 1. -
Interruption layer 540C was deposited through sequential atomic layer deposition. Specifically, one cycle of zirconium oxide was deposited via atomic layer deposition, followed by two cycles of yttrium oxide deposited via atomic layer deposition. These three cycles (one cycle of ZrO2 and two cycle of Y2O3) will be together referred to in this example as a supercycle.Interruption layer 540C was fully grown after 4 supercycles. - The depositions of the single phase crystalline yttrium oxide layer and multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layers were repeated for several cycles to form a stack of alternating layers of single phase crystalline yttrium oxide layers (530C, 550C, 570C, 590C) and multiphase crystalline of yttrium zirconium oxide and yttrium oxide (540C, 560C, 580C).
- The
first layer 530C in the plasma resistant protective coating was a single phase crystalline yttrium oxide layer. The single phase crystalline yttrium oxide layers had an about 95-100 wt % cubic phase corresponding to a Powder Diffraction File (PDF) No. 04-005-4378. The single phase crystalline yttrium oxide layers demonstrated an X-Ray Diffraction (XRD) profile as depicted inFIG. 6A . - The intermittent mix of yttrium zirconium oxide and yttrium oxide layers in the plasma resistant protective coating were multiphase crystalline with an about 64-74 wt %, or about 69.4 wt % cubic crystalline phase (corresponding to a PDF No. 01-080-4014) and about 25-35 wt %, or about 30.6 wt % cubic yttrium oxide phase (corresponding to a PDF No. 01-084-3893). The multiphase crystalline interruption layers demonstrated an XRD profile as depicted in
FIG. 8A . The XRD profile depicted inFIG. 8A and the corresponding PDF Numbers correlate with about 69.4±5 wt % Zr0.4Y0.6O1.7 chemical formula and about 30.6±5 wt % Y2O3 chemical formula. Although the phases of the yttrium zirconium oxide and yttrium oxide are cubic and the phase of the yttrium oxide rare-earth oxide layer is also cubic, the lattice structure of the various cubic phases are different. Thus, the interruption layer may have the same phase as the rare-earth oxide layer as long as the lattice structure of the two crystalline phases vary. - The thickness of the each of the rare earth oxide layers (i.e., the crystalline yttrium oxide layers) was about 240 nm to about 260 nm and the thickness of the interruption layers (i.e., the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide layers) was about 0.5 nm to about 1.5 nm, or about 1.2 nm.
- The interruption layers in the plasma resistant protective coating were characterized using inter alia Transmission Electron Microscopy and Energy Dispersive Spectroscopy (TEM/EDS) line scan. For analysis via TEM/EDS, the interruption layer of multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide was deposited with a thickness that was sufficient to generate the atomic distribution of the various atoms in the layer. The line scan is depicted in
FIG. 8B . The composition demonstrated between 30 nm and 480 nm in the line scan corresponds to the composition of the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer.FIG. 8B illustrates that the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer comprises about 15-25 atomic % of yttrium, about of 5-10 atomic % of zirconium and about 65-75 atomic % of oxygen. -
FIG. 8C depicts a high Angle Annular Dark Field (HAADF) Scanning Transmission Electron Microscopy (STEM) image of the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer that was analyzed via TEM/EDS inFIG. 8B .Region 815 depicts Al6061 andregion 835 depicts the exemplary multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer that was analyzed via TEM/EDS inFIG. 8B .FIG. 8C also shows that the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide layer deposited by ALD covers the Al6061 and alumina buffer layer conformally and uniformally with low to no porosity. -
FIG. 8D depicts Transmission Electron Microscopy (TEM) images of a multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer and further demonstrates the conformal, uniform, and porosity free coating obtained through atomic layer deposition. -
FIG. 9A depicts a plasma resistant protective coating deposited on an Al2O3 buffer layer 920 that is deposited on an aluminum substrate of Al 6061 910. A rare-earth oxide layer 930 of single phase crystalline yttrium oxide was deposited on the aluminum oxide buffer layer using atomic layer deposition. Subsequently, aninterruption layer 940 of a mixed multiphase crystalline yttrium zirconium oxide and yttrium oxide layer was deposited on the single phase crystalline yttrium oxide layer using atomic layer deposition. The single phase crystalline yttrium oxide layer and multiphase crystalline yttrium zirconium oxide interruption layer may have been deposited in a manner similar to that described in Example 1. -
Interruption layer 940 was deposited through sequential atomic layer deposition. Specifically, one cycle of zirconium oxide was deposited via atomic layer deposition, followed by three cycles of yttrium oxide deposited via atomic layer deposition. These four cycles (one cycle of ZrO2 and three cycle of Y2O3) will be together referred to in this example as a supercycle.Interruption layer 940 was fully grown after 4 supercycles. - The depositions of the single phase crystalline yttrium oxide layer and multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layers were repeated for several cycles to form a stack of alternating layers of single phase crystalline yttrium oxide layers (930, 950, 970, 990) and multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide layers (940, 960, 980).
- The
first layer 930 in the plasma resistant protective coating was a single phase crystalline yttrium oxide layer. The single phase crystalline yttrium oxide layers had an about 95-100 wt % cubic phase corresponding to a Powder Diffraction File (PDF) No. 04-005-4378. The single phase crystalline yttrium oxide layers demonstrated an X-Ray Diffraction (XRD) profile as depicted inFIG. 6A . - The intermittent mix of yttrium zirconium oxide and yttrium oxide layers in the plasma resistant protective coating were multiphase crystalline with an about 25-35 wt %, or about 30.8 wt % cubic crystalline phase (corresponding to a PDF No. 01-080-4014) and about 64-74 wt %, or about 69.2 wt % cubic yttrium oxide phase (corresponding to a PDF No. 01-084-3893). The multiphase crystalline interruption layers demonstrated an XRD profile as depicted in
FIG. 8A . The XRD profile depicted inFIG. 8A and the corresponding PDF Numbers correlate with about 30.8±5 wt % Zr0.4Y0.6O1.7 (i.e., x is 0.6, y is 0.4, and z is 1.7) is chemical formula and about 69.2±5 wt % Y2O3 chemical formula. Although the phases of the yttrium zirconium oxide and yttrium oxide are cubic and the phase of the yttrium oxide rare-earth oxide layer is also cubic, the lattice structure of the various cubic phases are different. Thus, the interruption layer may have the same phase as the rare-earth oxide layer as long as the lattice structure of the two crystalline phases vary. - Although x, y, and z in the chemical formula YxZryOz are identified in this example and in the prior example, their values should not be construed as limited and the atomic ratio of yttrium to zirconium can range from 0 (when no yttrium is present) to 9, so long as the resultant crystalline phase(s) is/are different from the crystalline phase(s) of the the rare-earth oxide layer.
- The thickness of the each of the rare earth oxide layers (i.e., the crystalline yttrium oxide layers) was about 240 nm to about 260 nm and the thickness of the interruption layers (i.e., the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide layers) was about 0.5 nm to about 2.0 nm, or about 1.6 nm.
- The interruption layers in the plasma resistant protective coating were characterized using inter alia Transmission Electron Microscopy and Energy Dispersive Spectroscopy (TEM/EDS) line scan. For analysis via TEM/EDS, the interruption layer of multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide was deposited with a thickness that was sufficient to generate the atomic distribution of the various atoms in the layer. The line scan is depicted in
FIG. 9B . The composition demonstrated between 40 nm and 85 nm in the line scan corresponds to the composition of the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer.FIG. 9B illustrates that the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer comprises about 3-7 atomic % of zirconium, about of 15-25 atomic % of zirconium and about 65-75 atomic % of oxygen. -
FIG. 9C depicts a high Angle Annular Dark Field (HAADF) Scanning Transmission Electron Microscopy (STEM) image of the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer that was analyzed via TEM/EDS inFIG. 9B .Region 915 depicts Al6061 andregion 935 depicts the exemplary multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer that was analyzed via TEM/EDS inFIG. 9B .FIG. 9C also shows that the multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide layer deposited by ALD covers the Al6061 and alumina buffer layer conformally and uniformally with low to no porosity. -
FIG. 9D depicts Transmission Electron Microscopy (TEM) images of a multiphase crystalline mix of yttrium zirconium oxide and yttrium oxide interruption layer and further demonstrates the conformal, uniform, and porosity free coating obtained through atomic layer deposition. -
FIG. 10 depicts a plasma resistant protective coating deposited on an Al2O3 buffer layer 1020 that is deposited on an aluminum substrate of Al 6061 1010. A rare-earth oxide layer 1030 of single phase crystalline yttrium oxide was deposited on the aluminum oxide buffer layer using atomic layer deposition. Subsequently, aninterruption layer 1040 of gadolinium oxide was deposited on the single phase crystalline yttrium oxide layer using atomic layer deposition. - The depositions of the single phase crystalline yttrium oxide layer and single/multi-phase crystalline gadolinium oxide interruption layers were repeated for several cycles to form a stack of alternating layers of crystalline yttrium oxide layers (1030, 1050, 1070, 1090) and of crystalline gadolinium oxide layers (1040, 1060, 1080).
- Similar to the crystalline gadolinium oxide interruption layers, other amorphous or crystalline rare-earth oxide interruption layers may be deposited between layers yttrium oxide. When the interruption layer is crystalline, the atomic crystalline phase(s) of the interruption layer should be different from the atomic crystalline phase of the yttrium oxide or at least have a different lattice structure. Dissimilar crystalline phases or dissimilar lattice structures allow the interruption layers to inhibit the growth of the yttrium oxide grains from growing uncontrollably and abnormally large.
- Exemplary, non-limiting, crystalline phases associated with various rare-earth oxides are depicted in
FIG. 3 (e.g., La2O3, Pr2O3, Nd2O3, Sm2O3, Eu2O3, Gd2O3, Tb2O3, Dy2O3, Ho2O3, Er2O3, Tm2O3, Yb2O3, ZrO2, and combinations thereof). InFIG. 3 , where the y axis represents temperature and the x axis represents the rare-earth oxide, it is possible to identify what crystalline single phase or multiphase phase a particular rare-earth oxide will exist in when subjected to a particular temperature. For instance, at certain ALD temperatures La2O3, Pr2O3, Nd2O3 may have a hexagonal crystalline atomic phase; Sm2O3 may have a hexagonal and/or a monoclinic crystalline phase; Eu2O3, Gd2O3, Tb2O3 may exist in a monoclinic crystalline phase; Dy2O3 may exist in a monoclinic and/or cubic crystalline phase; and Ho2O3, Er2O3, Tm2O3, Yb2O3 may exist in a cubic crystalline phase. In some embodiments, the crystalline metal oxide layer may comprise YAG in the cubic phase. -
FIG. 12 depicts a plasma resistant protective coating deposited on an Al2O3 buffer layer 1220 that is deposited on an aluminum substrate of Al 6061 1210. A rare-earth oxide layer 1230 of single phase crystalline yttrium oxide was deposited on the aluminum oxide buffer layer using atomic layer deposition. Subsequently, aninterruption layer 1240 of yttrium zirconium oxide was deposited on the single phase crystalline yttrium oxide layer using atomic layer deposition. The single phase crystalline yttrium oxide layer and yttrium zirconium oxide interruption layer may have been deposited in a manner similar to that described in Example 1. -
Interruption layer 1240 was deposited through sequential atomic layer deposition. Specifically, three cycles of zirconium oxide was deposited via atomic layer deposition, followed by one cycle of yttrium oxide deposited via atomic layer deposition. These four cycles (three cycles of ZrO2 and one cycle of Y2O3) will be together referred to in this example as a supercycle.Interruption layer 1240 was fully grown after 4 supercycles. - The depositions of the single phase crystalline yttrium oxide layer and yttrium zirconium oxide interruption layers were repeated for several cycles to form a stack of alternating layers of single phase crystalline yttrium oxide layers (1230, 1250, 1270, 1290) and yttrium zirconium oxide (1240, 1260, 1280).
- The
first layer 1230 in the plasma resistant protective coating was a single phase crystalline yttrium oxide layer. The single phase crystalline yttrium oxide layers had an about 95-100 wt % cubic phase corresponding to a Powder Diffraction File (PDF) No. 04-005-4378. The single phase crystalline yttrium oxide layers demonstrated an X-Ray Diffraction (XRD) profile as depicted inFIG. 6A . - The thickness of the each of the rare earth oxide layers (i.e., the crystalline yttrium oxide layers) was about 240 nm to about 260 nm and the thickness of the interruption layers was about 0.5 nm to about 2.0 nm, or about 1.6 nm.
- The interruption layers in the plasma resistant protective coating were characterized using inter alia top down Scanning Electron Microscopy (SEM) image, TEM image, and TEM/EDS line scan.
- The top down SEM images are depicted in
FIG. 13A andFIG. 13B .FIG. 13A shows a top down SEM image of a 1 μm yttria coating deposited by ALD without an interruption layer. As shown inFIG. 13A , overgrown grains protrude out of the surface coating.FIG. 13B shows a top down SEM image of a 1μ yttria coating with interruption layers in accordance with the instant example. As shown inFIG. 13B , no overgrown grains protrude from the surface of the coating. - Cross sectional TEM images are depicted in
FIG. 14A andFIG. 14B .FIG. 14A shows a cross sectional TEM image of a 1 μm yttria coating deposited by ALD without an interruption layer. As shown inFIG. 14A , an overgrown grain protrudes out of the surface of the coating.FIG. 14B shows a cross sectional TEM image of a 1μ yttria coating with interruption layers in accordance with the instant example. As shown inFIG. 14B , no overgrown grains protrude from the surface of the coating. - TEM/EDS lines scan are depicted in
FIG. 15A andFIG. 15B . The line scan is depicted inFIG. 15A . The composition demonstrated three zirconium peaks between about 250-350 nm, between about 500-600 nm, and between about 750-850 nm (i.e., in the locations of the interruption layers). -
FIG. 15B depicts a TEM image which shows the three interruption layers identified in the line scan and further demonstrates the conformal, uniform, and porosity free coating obtained through atomic layer deposition. - All interruption layers discussed and exemplified herein only inhibit uncontrolled grain growth of the grains in the crystalline rare-earth oxide layers. The interruption layers do not affect the crystalline phase of the rare-earth oxide layers.
- XRD data presented herein was acquired by grazing incidence XRD (GIXRD) on a PANalytical X'Pert Pro MRD 6-axis diffractometer equipped with a copper X-ray tube and parallel beam optics.
- TEM samples were prepared using the in situ Focused Ion Beam (FIB) lift out technique on an FEI Helios 650 Dual Beam FIB/SEM. The samples were capped with sputtered Irdium (Ir), protective carbon ink, and e-Pt/I-Pt prior to milling. The TEM lamella thickness was ˜100 nm.
- TEM samples were imaged with a FEI Tecnai TF-20 FEG/TEM operated at 200 kV in bright-field (BF) TEM mode, high-resolution (HR) TEM mode.
- Z-contrast STEM is a form of Rutherford Scattering in which electrons are scattered to very large angles and are collected with a special detector. The scattering goes as Z2 and the resulting image can be directly interpreted as qualitative chemical map. The image contrast is due to differences in the average atomic mass; with heavier atomic masses appearing brighter than lighter average atomic masses. There is typically very little diffraction contrast in these images. These images are sometimes referred to as High Angle Annular Dark Field images (HAADF). “Z Contrast” can show atomic columns in the highest resolution images.
- The preceding description sets forth numerous specific details such as examples of specific systems, components, methods, and so forth, in order to provide a good understanding of several embodiments of the present invention. It will be apparent to one skilled in the art, however, that at least some embodiments of the present invention may be practiced without these specific details. In other instances, well-known components or methods are not described in detail or are presented in simple block diagram format in order to avoid unnecessarily obscuring the present invention. Thus, the specific details set forth are merely exemplary. Particular embodiments may vary from these exemplary details and still be contemplated to be within the scope of the present invention.
- Reference throughout this specification to “one embodiment” or “an embodiment” means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment. Thus, the appearances of the phrase “in one embodiment” or “in an embodiment” in various places throughout this specification are not necessarily all referring to the same embodiment. In addition, the term “or” is intended to mean an inclusive “or” rather than an exclusive “or.”
- Reference throughout this specification to numerical ranges should not be construed as limiting and should be understood as encompassing the outer limits of the range as well as each number and/or narrower range within the enumerated numerical range.
- Although the operations of the methods herein are shown and described in a particular order, the order of the operations of each method may be altered so that certain operations may be performed in an inverse order or so that certain operation may be performed, at least in part, concurrently with other operations. In another embodiment, instructions or sub-operations of distinct operations may be in an intermittent and/or alternating manner.
- It is to be understood that the above description is intended to be illustrative, and not restrictive. Many other embodiments will be apparent to those of skill in the art upon reading and understanding the above description. The scope of the invention should, therefore, be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled.
Claims (17)