US20180297008A1 - High performance sorption binder for gas phase storage devices - Google Patents

High performance sorption binder for gas phase storage devices Download PDF

Info

Publication number
US20180297008A1
US20180297008A1 US15/768,682 US201615768682A US2018297008A1 US 20180297008 A1 US20180297008 A1 US 20180297008A1 US 201615768682 A US201615768682 A US 201615768682A US 2018297008 A1 US2018297008 A1 US 2018297008A1
Authority
US
United States
Prior art keywords
gas storage
article
binder
storage article
adsorbent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/768,682
Other languages
English (en)
Inventor
Sean M. Stabler
Roderick REBER
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Arkema Inc
Original Assignee
Arkema Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arkema Inc filed Critical Arkema Inc
Priority to US15/768,682 priority Critical patent/US20180297008A1/en
Publication of US20180297008A1 publication Critical patent/US20180297008A1/en
Assigned to ARKEMA INC. reassignment ARKEMA INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: REBER, Roderick, STABLER, SEAN M.
Assigned to ARKEMA INC. reassignment ARKEMA INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: REBER, Roderick, STABLER, SEAN M.
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
    • B01J20/20—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising free carbon; comprising carbon obtained by carbonising processes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/02—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols by adsorption, e.g. preparative gas chromatography
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/02—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols by adsorption, e.g. preparative gas chromatography
    • B01D53/04—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols by adsorption, e.g. preparative gas chromatography with stationary adsorbents
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/22—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising organic material
    • B01J20/26—Synthetic macromolecular compounds
    • B01J20/261—Synthetic macromolecular compounds obtained by reactions only involving carbon to carbon unsaturated bonds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
    • B01J20/28014—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their form
    • B01J20/2803—Sorbents comprising a binder, e.g. for forming aggregated, agglomerated or granulated products
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
    • B01J20/28014—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their form
    • B01J20/28042—Shaped bodies; Monolithic structures
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
    • B01J20/28054—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J20/28057—Surface area, e.g. B.E.T specific surface area
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/30—Processes for preparing, regenerating, or reactivating
    • B01J20/3007—Moulding, shaping or extruding
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/30—Processes for preparing, regenerating, or reactivating
    • B01J20/3035—Compressing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2253/00—Adsorbents used in seperation treatment of gases and vapours
    • B01D2253/10—Inorganic adsorbents
    • B01D2253/102—Carbon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2253/00—Adsorbents used in seperation treatment of gases and vapours
    • B01D2253/10—Inorganic adsorbents
    • B01D2253/106—Silica or silicates
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2253/00—Adsorbents used in seperation treatment of gases and vapours
    • B01D2253/10—Inorganic adsorbents
    • B01D2253/116—Molecular sieves other than zeolites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2253/00—Adsorbents used in seperation treatment of gases and vapours
    • B01D2253/20—Organic adsorbents
    • B01D2253/204—Metal organic frameworks (MOF's)
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2253/00—Adsorbents used in seperation treatment of gases and vapours
    • B01D2253/30—Physical properties of adsorbents
    • B01D2253/302—Dimensions
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2253/00—Adsorbents used in seperation treatment of gases and vapours
    • B01D2253/30—Physical properties of adsorbents
    • B01D2253/302—Dimensions
    • B01D2253/306—Surface area, e.g. BET-specific surface
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2253/00—Adsorbents used in seperation treatment of gases and vapours
    • B01D2253/30—Physical properties of adsorbents
    • B01D2253/34—Specific shapes
    • B01D2253/342—Monoliths
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2256/00—Main component in the product gas stream after treatment
    • B01D2256/24—Hydrocarbons
    • B01D2256/245—Methane
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02C—CAPTURE, STORAGE, SEQUESTRATION OR DISPOSAL OF GREENHOUSE GASES [GHG]
    • Y02C20/00—Capture or disposal of greenhouse gases
    • Y02C20/40—Capture or disposal of greenhouse gases of CO2

Definitions

  • the invention relates to the use of high performance thermoplastic polymer binder materials for immobilizing adsorptive materials for gas storage devices.
  • the use of these new binders, especially fluoropolymers or polyamide binders, provides a porous solid having a high adsorbent packing density, low binder fouling of adsorbent, and maximizes the volume of gas to the volume of the storage space.
  • Adsorbed gas storage provides an advancement in the temporary storage of gaseous materials that overcome obstacles related to high pressure systems commercially used today to compress gases.
  • Gases such as noble gases, O 2 , N 2 , hydrocarbons, and other small gas molecules are used in many markets including, but not limited to, industrial, automotive, pharmaceutical, food, beverage, electronics, etc. Specific applications include concentrated medical oxygen, industrial desiccants, portable and residential liquefied petroleum gas (LPG), stranded gas flares, kerosene burners, cook stoves, compressed natural gas (CNG), and many others.
  • LPG portable and residential liquefied petroleum gas
  • stranded gas flares stranded gas flares
  • kerosene burners kerosene burners
  • cook stoves compressed natural gas (CNG)
  • the storage and transport of said gases are typically in vessels where high pressures are used to condense or even liquefy the gas to utilize the greatest concentration safely possible with in an occupied volume.
  • the pressurization process results in unwanted and excessive costs due to the energy and infrastructure requirements.
  • thermoplastic binder The technology to convert low bulk density sorbent powder into an immobilized higher density block using a thermoplastic binder is well known for filtration applications. It is widely believed that high surface area sorption materials formed into high density compacted structures can achieve the economic storage volume needed for gases. The use of binder materials developed takes the immobilization technology even further, providing higher packing densities and better manufacturing productivity, while maintaining the sorbents highest performance. The resulting devices made from the combination of the manufactured immobilized block by specific formulations of thermoplastic binder and adsorption media allows very high volume storage of gas per volume of device, but at a much lower pressure needed compared to liquefying and compressed gas technologies widely used today.
  • U.S. Pat. No. 4,999,330 describes the needs and challenges for the high-density adsorbent used in ANG systems.
  • the efficiency of the system depends on the level of surface area of the adsorbent, the density of the packing of the sorbent, the physical stability of the 3-D structure, and the level of fouling of the adsorbent.
  • the adsorption is proportional to the surface area of the solid. This is generally maximized by using an adsorbent containing macro-, micro-, and nano-pores, as often described for activated carbons.
  • High surface area activated carbon is the adsorbent typically used in high density adsorbent structures.
  • the packing density is also very important. The more adsorbent in a given volume, the more gas can be adsorbed and stored.
  • One drawback of loose carbon packed into a storage tank is that it produces a high level of void space. Adsorbent material that is pressed into less space (known as densified) provides more adsorbent potential.
  • Loose carbon also has a disadvantage in that it can move and settle by vibration of an adsorption storage system during use, producing powdering and reduction of the adsorbent volume.
  • the U.S. Pat. No. 4,999,330 reference solves the above limitations by forming a methyl cellulose or polyvinyl alcohol binder solvent solution, coating high surface area carbon particles with the binder solution, followed by removing the solvent and compressing the binder-coated particles to cause a bulk volume reduction of 50 to 200%.
  • the '330 system suffers from its complexity and many steps. It also involves coating the entire activated carbon particles—which blocks many of the micropores—this fouling reducing the amount of surface area available for adsorption. Some of the pores can be pre-filled with solvent which can later be removed by heat to unblock many of the pores, however the net effect of a full coating is a large reduction in active surface area.
  • Carbon block filters are described in U.S. Pat. No. 5,019,311, U.S. Pat. No. 5,147,722, and U.S. Pat. No. 5,331,037, uses an extrusion process to produce a porous article containing bound active particles, such as activated carbon, bound together by a thermoplastic binder.
  • the carbon block filter is designed to remove contaminants from a fluid stream—such as in the purification of water.
  • the polymer binder which is generally a polyethylene, is used at a high level.
  • U.S. Pat. No. 6,395,190 describes carbon filters and a method for making them having a 15 to 25 weight percent of a thermoplastic binder.
  • the problem with polyethylene and other typical binders is that high loading percentages are required to adequately hold the adsorbent materials together. Poor fouling resistance is also a problem
  • Poly(vinylidene fluoride) as a binder for a porous block article has been found to improve the carbon block article performance by providing effective binding at lower loading—which in turn opens more of the surface area of the active sorbent agent, and providing even greater efficiency.
  • a high v/v o can be obtained in a gas storage article using low levels of polyvinylidene fluoride or polyamide binders with activated carbon or active carbon fibers, formed by an extrusion of compression molding process.
  • the low levels of binder used have little negative effect on the ratio of activated adsorbent volume to container volume.
  • the low binder volume leads to improved permeability compared to lower density binders. Improved permeability increases the rate of adsorption and desorption of the stored gas from the porous solid storage article.
  • the solid porous adsorbent structure of the invention In addition to providing a solid adsorption article having a high density packing, low level of binder volume, the solid porous adsorbent structure of the invention also show excellent resistance to fouling of the adsorbent surface area. Lastly, polyvinylidene fluoride or polyamide binders also provide excellent chemical resistance to the gas storage environment. Additionally, the high relative thermal index of these polymers is useful for the temperature range an adsorptive storage monolith would encounter during the product life cycle.
  • the invention relates to a gas storage article comprising a solid, dense, porous adsorbent media bound together by 0.5 to 30 weight percent of thermoplastic binder particles, wherein said binder particles have a discrete particle size of between 5 and 700 nanometers and agglomerates between 5 and 150 micrometers
  • the invention also relates to a sealed container containing the gas storage block article, having at least one valve opening for charging and discharging of a gas, the container capable of holding a pressurized gas.
  • the invention also relates to a gas storage container, holding the solid adsorbent and containing natural gas (methane).
  • FIG. 1 Is a cross sectional view of a solid gas storage article of the invention.
  • FIG. 2 Is a cross-sectional view of a solid gas storage article of the invention extruded as a center rod and a hollow cylinder, and then nested together to form a similar sized concentric solid block of a diameter similar to FIG. 1 .
  • Interconnectivity means that the active particles or fibers are permanently bonded together by the polymer binder particles without completely coating the active primary and secondary particles or functional particles or fibers.
  • the binder adheres the sorbent at specific discrete points to produce an organized, porous structure.
  • the porous structure allows a gas to pass through the interconnected particles or fibers, and the gas is exposed directly to the surface(s) of the sorbent particles or fibers, favoring the adsorption of the gas onto the adsorbent material. Since the polymer binder adheres to the adsorbent particles in only discrete points, less binder is used for full connectivity compared to a binder that is coated onto the adsorbent.
  • the invention relates to a solid porous gas storage article made of activated carbon or other gas absorbent, the adsorbent material being bound together by small discrete thermoplastic polymer binder particles to provide interconnectivity.
  • the solid porous article is generally present within a closed container, capable of holding a pressurized gas.
  • the adsorbent and binder are combined under pressure to produce a dense porous solid gas-adsorbent structure.
  • the polymer particles of the composite of the invention are thermoplastic polymer particles in the sub-micrometer range.
  • the weight average particle size is less than 150 micrometer, preferably less than 10 micrometers, more preferably less than 1 micrometer, preferably less than 500 nm, preferably less than 400 nm, and more preferably less than 300 nm.
  • the weight average particle size is generally at least 20 nm and preferably at least 50 nm.
  • Useful polymers include, but are not limited to fluoropolymers, styrene-butadiene rubbers (SBR), ethylene vinyl acetate (EVA), acrylic polymers such as polymethyl methacrylate polymer and copolymers, polyurethanes, styrenic polymers, polyamides, polyolefins, including polyethylene, and polypropylene and the copolymers thereof, polyester including polyethylene terephthalate, polyvinyl chlorides, polycarbonate and thermoplastic polyurethane (TPU).
  • the thermoplastic polymers are made by emulsion (or inverse emulsion) polymerization.
  • Preferred polymers are polyamides, and fluoropolymers, with homopolymers and copolymers of polyvinylidene fluoride being especially useful.
  • the binder is a fluoropolymer.
  • Useful fluoropolymers are thermoplastic homopolymers and copolymers having greater than 50 weight percent of fluoromonomer units by weight, preferably more than 65 weight percent, more preferably greater than 75 weight percent and most preferably greater than 90 weight percent of one or more fluoromonomers.
  • Useful fluoromonomers for forming the fluoropolymer include but are not limited to: vinylidene fluoride (VDF or VF2), tetrafluoroethylene (TFE), trifluoroethylene (TrFE), chlorotrifluoroethylene (CTFE), hexafluoropropene (HFP), vinyl fluoride (VF), hexafluoroisobutylene (HFIB), perfluorobutylethylene (PFBE), pentafluoropropene, 3,3,3-trifluoro-1-propene, 2-trifluoromethyl-3,3,3-trifluoropropene, fluorinated vinyl ethers including perfluoromethyl ether (PMVE), perfluoroethylvinyl ether (PEVE), perfluoropropylvinyl ether (PPVE), perfluorobutylvinyl ether (PBVE), longer chain perfluorinated vinyl ethers, illuminated dioxoles,
  • PVDF polyvinylidene fluoride
  • PTFE polytetrafluoroethylene
  • the invention applies to all thermoplastic polymers, and in particular all fluoropolymers and copolymers, and polyamides, vinylidene fluoride polymer will be used to illustrate the invention, and are the preferred polymer.
  • PVDF polyvinylidene fluoride
  • PTFE polytetrafluoroethylene
  • vinylidene fluoride copolymers are preferred, due to their lower crystallinity (or no crystallinity), making them more flexible than the semi-crystalline PVDF homopolymers. Flexibility of the binder allows it to better withstand the manufacturing process, as well as increased pull-through strength and better adhesion properties.
  • preferred copolymers include those containing at least 50 mole percent, preferably at least 75 mole %, more preferably at least 80 mole %, and even more preferably at least 85 mole % of vinylidene fluoride copolymerized with one or more comonomers selected from the group consisting of tetrafluoroethylene, trifluoroethylene, chlorotrifluoroethylene, hexafluoropropene, vinyl fluoride, pentafluoropropene, tetrafluoropropene, trifluoropropene, perfluoromethyl vinyl ether, perfluoropropyl vinyl ether and any other monomer that would readily copolymerize with vinylidene fluoride.
  • HFP hexafluoropropene
  • VDF hexafluoropropene
  • the PVDF used in the invention is generally prepared by means known in the art, using aqueous free-radical emulsion polymerization—although suspension, solution and supercritical CO 2 polymerization processes may also be used.
  • a reactor is charged with deionized water, water-soluble surfactant capable of emulsifying the reactant mass during polymerization and optional paraffin wax antifoulant. The mixture is stirred and deoxygenated.
  • a predetermined amount of chain transfer agent, CTA is then introduced into the reactor, the reactor temperature raised to the desired level and vinylidene fluoride (and possibly one or more comonomers) are fed into the reactor.
  • an initiator emulsion or solution is introduced to start the polymerization reaction.
  • the temperature of the reaction can vary depending on the characteristics of the initiator used and one of skill in the art will know how to do so. Typically the temperature will be from about 30° to 150° C., preferably from about 60° to 120° C.
  • the monomer feed will be stopped, but initiator feed is optionally continued to consume residual monomer. Residual gases (containing unreacted monomers) are vented and the latex recovered from the reactor.
  • the surfactant used in the polymerization can be any surfactant known in the art to be useful in PVDF emulsion polymerization, including perfluorinated, partially fluorinated, and non-fluorinated surfactants.
  • the PVDF emulsion of the invention is fluorosurfactant-free, with no fluorosurfactants being used in any part of the polymerization.
  • Non-fluorinated surfactants useful in the PVDF polymerization could be both ionic and non-ionic in nature including, but are not limited to, 3-allyloxy-2-hydroxy-1-propane sulfonic acid salt, polyvinylphosphonic acid, polyacrylic acids, polyvinyl sulfonic acid, and salts thereof, polyethylene glycol and/or polypropylene glycol and the block copolymers thereof, alkyl phosphonates and siloxane-based surfactants.
  • the PVDF polymerization results in a latex generally having a solids level of 10 to 60 percent by weight, preferably 10 to 50 percent.
  • the latex binder is generally reduced to a powder form by spray drying, coagulation, or other known process, to produce a dry powder.
  • Binder particles are generally from 5 to 700 nm in size, preferably from 50 to 500 nm, and more preferably from 100-300 nm as an average particle size.
  • polymer particles may agglomerate into 1 to 150 micrometer groupings, 3-50 micrometers, 5-15 micrometers, and preferably 6-8 micrometer agglomerates, but it has been found that these agglomerates generally break into individual particles during processing to for an article.
  • the binder particles are discreet particles, and remain as discrete particles in the formed solid porous adsorbent article. During processing into articles, the particles which start essentially spherical are deformed by pressure into thin oblong particles that bind adjoining adsorbent material together and provide interconnectivity.
  • PVDF binders have a very high density of about 1.78 g/cc. Thus the low weight percent of binder needed represents an even lower volume percent.
  • the particle size of the binder plays a role in the lower weight % loadings needed to make a solid immobilized porous media block.
  • the rheology of PVDF resin based on the higher molecular weights of preferably 200,000 to 1,250,000 g/mole, and preferably 300,000-900,000 g/mole, assists in the binder not flowing into the carbon and fouling the high surface area of the activated carbon sorption media.
  • the adsorbents of the invention are those capable of adsorbing and desorbing specific gas molecules.
  • activated carbon is used to adsorb natural gas (methane), however, other adsorbents with adsorption specificity for other gases are also contemplated by this invention.
  • Activated carbon, carbon fibers and molecular sieves are especially useful adsorbents of the invention.
  • Activated carbon having a large level of surface area is especially preferred, as are nano carbon fibers, in order to maximize the surface area of the absorbent.
  • Other useful adsorbents include, but are not limited to: carbon molecular sieves, molecular sieves, silica gel, metal organic framework, etc. have special affinity to specific gas adsorption.
  • the primary active particles of the invention are generally in the size range of 0.1 to 3,000 micrometers, and preferably from 1 to 500 micrometers in diameter and fibers of 0.1 to 250 micrometers in diameter of essentially unlimited length to width ratio. Fibers are preferably chopped to no more than 5 mm in length. Adsorbent fibers or powders should have sufficient thermal conductivity to allow heating of the powder mixtures. In addition, in an extrusion process, the particles and fibers must have melting points sufficiently above the melting point of the fluoropolymer binder resin to prevent both substances from melting and producing a continuous melted phase rather than the usually desired multi phase system.
  • Sources of activated carbon include, but are not limited to, coconut shell, bitumen, coal, grass, organic polymers, hard wood, and soft wood.
  • Each product has their own characteristics which can affect gas sorption and desorption performance. It is known that for gas sorption onto activated carbon it is dependent on the close proximity to surface area contact coupled with Van der Waal's forces to attract gas molecules and temporarily store them until desorption occurs. Key characteristics of the activated carbon which impacts the volume of gas sorption is the macro-, micro-, meso-porosity of the carbon surface area. The porosity is further characterized by the N 2 BET surface area curves.
  • a key property related to manufacturing with solid state extrusion or compression molding methods is the apparent density, as measured by ASTM D2854, for material conveying and the hardness, as measured by ASTM D3802, when densifying.
  • a hard carbon is preferred to economically manufacture densified block with known state of the art manufacturing.
  • the hard carbons having a low BET surface area are not preferred for gas sorption performance, but a soft carbon with high BET surface area is preferred.
  • a soft carbon cannot be highly densified or manufactured at an economical rate using solid state extrusion or compression molding.
  • unique blends of soft carbon and hard carbon can achieve both an economic manufacturing process and also achieve high performance gas sorption characteristics.
  • a minimum of 5 percent by weight, preferably 10 weight percent, and preferably in the range of 10-60 weight percent of hard carbon is used to resist the pressure of the extruder and extrude a block structure.
  • a higher level of the hard carbon, up to 100 weight percent will produce a well-formed solid state extruded block, however, the higher cost, and lower BET surface area of the hard carbon reduce performance and economics.
  • Blocks prepared containing entirely soft carbons are possible, but the extrusion speed may be limited due to their compressibility. Blocks containing entirely soft carbons can be produced by a compression molding process.
  • Hard carbons are considered those with a ball pan hardness per ASTM D 3802 to be greater than 80% and soft carbons are considered when measured by the same method as being less than or equal to 80%.
  • Low N 2 BET surface area is considered less than 1400 m 2 /g. while high N 2 BET surface area is considered greater than or equal to 1400 m 2 /g.
  • the binder and absorbent particles may be blended and processed by several methods.
  • the binder particles are generally in a powder form, which can be dry blended with the sorbent materials. Solvent or aqueous blends may also be formed by known means.
  • 0.3 to 30, preferably 0.5 to 25, and more preferably 1 to 16 weight percent of binder is used for each 84 to 99.5 weight percent of absorbent material.
  • the level of binder is from 4 to 12 weight percent, and even more preferably from about 5 to 10 weight percent.
  • the polymer binder remains as discreet polymer particles that bind the adsorbent materials into an interconnected web, for good permeability.
  • individual polymer particles no longer exist, as they are dissolved and form a continuous coating over the adsorbent particles.
  • the continuous coating reduces the amount of activated surface area available for adsorption on the particles, and can reduce their overall effectiveness.
  • An advantage of the extrusion is that the absorbent density is fairly constant across the article, while a compression molded article tends to show a density gradient. It is increasingly difficult to have a uniform packing density gradient on a compression molded article especially as the aspect ratio (length/diameter ratio) increases.
  • An advantage of a compression molded process is that a large variety of shapes are available.
  • the polymer binder particles can be formed into a porous block article in an extrusion process, such as that described in U.S. Pat. No. 5,331,037.
  • the polymer binder/adsorbent material composite of the invention is dry-blended, optionally with other additives, such as processing aids, and extruded, molded or formed into articles.
  • Continuous extrusion under heat, pressure and shear can produce an infinite length 3-dimensional multi phase profile structure.
  • a critical combination of applied pressure, temperature and shear is used.
  • the composite blend is brought to a temperature above the softening temperature, but below the melting point, significant pressure applied to consolidate the materials, and enough shear to spread the binder and form a continuous web.
  • the extrusion process can produce a continuous block structure at any diameter and length desired. Lengths of 1 cm to hundreds of meters are possible with the right manufacturing equipment.
  • the continuous solid block can then be cut into desired final lengths. Typical diameters of the solid blocks would be 15 cm or less, and more preferably 15 cm or less—though with the proper size die(s) larger diameter structures up to 1.5 meters and larger could be produced.
  • An alternative to a single, solid structure is forming two or more structures—a solid rod, and one or more hollow block cylinders designed to nest together to form the larger structure. Once each annular or rod-shaped block component is formed, the components can be nested together to create a larger structure.
  • This process can provide several advantages over the extrusion of a single large structure.
  • the blocks with smaller cross-sectional diameter can be produced at a faster rate than producing a large, solid, single-pass block.
  • the cooling profile can be better controlled for each of the smaller-cross sectional pieces.
  • a further advantage of this concept may be reduced gas diffusion path lengths through the monoliths as the spacing between concentric blocks could serve as channels for rapid flow of gas.
  • Articles formed by the invention are high density, porous, solid articles that maximize the volume of adsorbent to volume of the container ratio.
  • the articles formed are used within a closed container capable of holding a pressurized gas of up to 5000 psi.
  • the adsorbent composite article should fit with a narrow tolerance inside the container, to maximize the amount of adsorbent per container volume.
  • the container will have an inlet which will be used to fill the container with gas (methane) and will have a discharge end where the gas can leave the container.
  • the adsorbent material does not settle or move during use, such as to power a vehicle, as it is interconnected by the binder particles.
  • Gas is provided into the container under pressure, and is adsorbed and stored by the sorbent material. When the pressure is released, and the container open to a lower pressure environment, the gas will desorb from the adsorbent material, and be used in the application.
  • the gas storage article has an immobilized density greater than 1.1 times, and preferably greater than 1.5 times that of the apparent density of the sorption media. Densification permits more storage capacity per unit volume, thus increasing the possible v/v o in a given gas storage article.
  • the container holding the composite solid adsorbent article is used to power a vehicle.
  • the container holding the composite is for storage purposes to supply fuel to grill and stove burners, refrigerators, freezers, furnaces, generators, emergency equipment, etc.
  • Dry powder blends are formed by dry blending 15 wt % of KyblockTM FG-81 polyvinylidene fluoride homopolymer binder from Arkema and 85 wt % of Oxbow 8325C-AW/70 coconut shell activated carbon.
  • the activated carbon is a nominally 80 ⁇ 325 mesh carbon, but also includes particles smaller than 325 mesh (44 micrometers)and greater than 80 (177 micrometers) mesh with a particle size distribution designed to maximize the particle packing density.
  • the two dry, powdery materials are mixed until they are a homogeneous blend.
  • the blend is then forced into a die which is heated to a minimum of 180° C. under pressures greater than 100 psi, forming a self-supporting, porous structure.
  • the structure is then cooled to room temperature.
  • the density of the activated carbon is initially 0.49 g/cc and this density is increased to 0.71 g/cc when combined with the binder and extruded. Under higher pacing pressure loadings the density can be increased even further.
  • Example 2 The same activated carbon used in Example 1 is combined with 16 wt % of MICROTHENE FN510-00 (LyondellBassell) linear low density polyethylene (PE) binder. A block of the same density is prepared by a comparable solid state extrusion process.
  • MICROTHENE FN510-00 LiondellBassell linear low density polyethylene (PE) binder.
  • PE linear low density polyethylene
  • a dry powder blend of 14 wt. % KYBLOCK® FG-42 polyvinylidene fluoride copolymer and 86 wt. % of the same activated carbon in EXAMPLE 1 was prepared and filled into a 10′′ tall steel annular mold with an outside diameter of 2.5′′ and an inside diameter of 1.25′′.
  • the mold containing powder was heated to 400° F. for one hour, and compressed with a hydraulic ram to achieve a block density of 0.7 g/cc.
  • a dry powder blend of 30 wt % Microthene FN510-00 and 70 wt % of the same activated carbon in EXAMPLE 1 was compression molded into a annular monolith of the same dimensions and density as in EXAMPLE 3.
  • the higher level of Microthene FN510-00 binder was required to produce a block with adequate strength by compression molding.
  • the extruded samples produced in EXAMPLE 1 and EXAMPLE 2 were analyzed using the Brunauer-Emmett-Teller (BET) nitrogen adsorption method to characterize the usable surface area of the carbon sorption media.
  • the pure carbon powder has a surface BET (m ⁇ 2/g) of 1150.
  • the 15 wt % KyblockTM FG-81 has a 973 m 2 /g surface BET and the PE samples has 674 m 2 /g surface BET.
  • the KyblockTM FG-81 is responsible for 0.37% fouling of the activated carbon surface.
  • the PE is responsible for 30.17% fouling of the activated carbon surface.
  • the KyblockTM resin sample is greater than 80 ⁇ more fouling resistant then the PE sample.
  • the polyethylene binder has two drawbacks: 1) high occupied volume and 2) high level of fouling.
  • the KyblockTM FG-81 resin exhibits volume of binder occupied with in a 1 kg carbon block of 84.18 whereas the PE binder volume occupies 173.14 cc of space within a block of the same mass.
  • the KyblockTM binder has over 2 ⁇ less occupied volume with in the composite monoliths.
  • the compression molded samples produced in EXAMPLE 3 and EXAMPLE 4 were also analyzed using the BET method.
  • the monolith produced in EXAMPLE 3 had a BET surface area of 953 m 2 /g whereas the monolith from EXAMPLE 4 has BET surface area of 600 m 2 /g.
  • the block in EXAMPLE 3 had a reduction of surface are of 3.6%, while the block in EXAMPLE 4 has a reduction of 24.5%.
  • An activated carbon monolith of comparable strength can have an adsorptive surface area at least 150% that of a block produced with conventional binders.
  • a solid extruded monolith 10 cm outside diameter was produced using the composition in EXAMPLE 1.
  • the processing temperature was set at 250° C.
  • Output speed was limited to 1 cm per minute due to the time required to raise the core of the monolith above the melting temperature of the Kyblock® binder.
  • An extruded annular monolith was produced by first preparing a dry powder blend containing 20 wt. % FX1184 (Jacobi Carbons) wood based carbon with surface area of 1400 m 2 /g ground and sieved to ⁇ 120 mesh (125 micrometers), 70 wt. % of the 80 ⁇ 325 mesh carbon described in EXAMPLE 1, and 10 wt. % Kyblock® FG-81 binder.
  • a 1.9′′ outside diameter by 1.19′′ inside diameter annulus was extruded using a processing temperature of 230° C. at a rate of 2 cm/min. The density of the resulting block was 0.62 g/cc.
  • BET surface area of the extruded block was 1176 m 2 /g

Landscapes

  • Chemical & Material Sciences (AREA)
  • Analytical Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • General Chemical & Material Sciences (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Inorganic Chemistry (AREA)
  • Solid-Sorbent Or Filter-Aiding Compositions (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
US15/768,682 2015-08-20 2016-08-18 High performance sorption binder for gas phase storage devices Abandoned US20180297008A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US15/768,682 US20180297008A1 (en) 2015-08-20 2016-08-18 High performance sorption binder for gas phase storage devices

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201562207401P 2015-08-20 2015-08-20
PCT/US2016/047445 WO2017031260A1 (en) 2015-08-20 2016-08-18 High performance sorption binder for gas phase storage devices
US15/768,682 US20180297008A1 (en) 2015-08-20 2016-08-18 High performance sorption binder for gas phase storage devices

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2016/047445 A-371-Of-International WO2017031260A1 (en) 2015-08-20 2016-08-18 High performance sorption binder for gas phase storage devices

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US16/032,682 Continuation-In-Part US10532340B2 (en) 2015-08-20 2018-07-11 High performance sorption binder for gas phase storage devices

Publications (1)

Publication Number Publication Date
US20180297008A1 true US20180297008A1 (en) 2018-10-18

Family

ID=58051387

Family Applications (1)

Application Number Title Priority Date Filing Date
US15/768,682 Abandoned US20180297008A1 (en) 2015-08-20 2016-08-18 High performance sorption binder for gas phase storage devices

Country Status (7)

Country Link
US (1) US20180297008A1 (zh)
EP (1) EP3337607B1 (zh)
JP (1) JP7058593B2 (zh)
KR (1) KR102666616B1 (zh)
CN (1) CN107921412A (zh)
BR (1) BR112018002572B1 (zh)
WO (1) WO2017031260A1 (zh)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020131320A1 (en) * 2018-12-19 2020-06-25 Arkema Inc. Evaporative loss control device
CN113993619A (zh) * 2019-04-17 2022-01-28 Csp技术公司 甲醛吸附用包含活性炭的聚合合成物
US11389781B2 (en) * 2016-07-22 2022-07-19 Japan Science And Technology Agency Metal organic framework nanosheet and method for producing same
CN115335320A (zh) * 2020-06-23 2022-11-11 西门子股份公司 气体的固态存储装置及其制造方法

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109642705B (zh) 2016-07-01 2022-03-18 英格维蒂南卡罗来纳有限责任公司 用于增强气体存储和释放系统中的体积容量的方法
DE102018117691B4 (de) * 2018-07-23 2022-04-28 Dr. Ing. H.C. F. Porsche Aktiengesellschaft Filtereinrichtung
CN110270312B (zh) * 2019-06-21 2022-07-15 四川农业大学 一种金属有机骨架材料-活性炭复合纤维膜及其制备方法
WO2020263808A1 (en) * 2019-06-25 2020-12-30 Arkema Inc. Crosslinked binder composition
CN114222619A (zh) * 2019-07-12 2022-03-22 乔治洛德方法研究和开发液化空气有限公司 制造高填充率复合吸附体床层的方法、包括床层的吸附器和使用吸附器的基于吸附的气体分离
CN111992195B (zh) * 2020-07-09 2023-02-28 中山大学 一种新型固相微萃取涂层粘结剂及其制备的探针涂层
CN116622074A (zh) * 2023-07-25 2023-08-22 齐河力厚化工有限公司 一种改性MOFs及其制备方法和应用

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5948398A (en) * 1993-09-14 1999-09-07 Kuraray Chemical Co., Ltd. Deodorant comprising metal oxide-carrying activated carbon
US7080505B2 (en) * 2001-03-06 2006-07-25 Engelhard Corporation Vehicular atmosphere cleansing method
WO2014055473A2 (en) * 2012-10-04 2014-04-10 Arkema Inc. Porous separation article

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4999330A (en) * 1988-03-22 1991-03-12 Universite Du Quebec A Trois-Rivieres High-density adsorbent and method of producing same
US5019311A (en) 1989-02-23 1991-05-28 Koslow Technologies Corporation Process for the production of materials characterized by a continuous web matrix or force point bonding
US5249948A (en) 1991-04-08 1993-10-05 Koslow Technologies Corporation Apparatus for the continuous extrusion of solid articles
JP3446339B2 (ja) * 1994-10-18 2003-09-16 三菱化学株式会社 活性炭の製造方法
US6395190B1 (en) 1996-02-26 2002-05-28 Kx Industries, L.P. Process employing thin-walled, extruded activated carbon filter
IL119663A (en) * 1996-02-26 2000-06-29 Kx Industries Lp Thin-walled extruded activated carbon filter
KR100270100B1 (ko) * 1996-12-23 2000-10-16 이구택 활성탄소섬유를 이용한 이산화탄소의 흡착.분리공정
JP2003038953A (ja) * 2001-07-31 2003-02-12 Toyota Central Res & Dev Lab Inc 水素吸蔵体および水素吸蔵装置
US7169466B2 (en) * 2004-05-21 2007-01-30 The Clorox Company Multiple-component binder systems for porous composite blocks
US7186474B2 (en) * 2004-08-03 2007-03-06 Nanotek Instruments, Inc. Nanocomposite compositions for hydrogen storage and methods for supplying hydrogen to fuel cells
JP2007000724A (ja) * 2005-06-22 2007-01-11 Mitsubishi Gas Chem Co Inc 酸素吸収剤成形体およびその製造法
CN103021671A (zh) * 2012-11-28 2013-04-03 惠州亿纬锂能股份有限公司 锂离子电池电容器
CN102983355A (zh) * 2012-12-25 2013-03-20 天津市捷威动力工业有限公司 一种可大倍率充放电的锂离子电池及其制备方法
BR112015028150B1 (pt) 2013-05-10 2022-08-16 Arkema Inc Produtos em bloco incorporando ligantes termoplásticos de partículas de pequena dimensão e métodos para a produção dos mesmos

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5948398A (en) * 1993-09-14 1999-09-07 Kuraray Chemical Co., Ltd. Deodorant comprising metal oxide-carrying activated carbon
US7080505B2 (en) * 2001-03-06 2006-07-25 Engelhard Corporation Vehicular atmosphere cleansing method
WO2014055473A2 (en) * 2012-10-04 2014-04-10 Arkema Inc. Porous separation article

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11389781B2 (en) * 2016-07-22 2022-07-19 Japan Science And Technology Agency Metal organic framework nanosheet and method for producing same
WO2020131320A1 (en) * 2018-12-19 2020-06-25 Arkema Inc. Evaporative loss control device
EP3897923A4 (en) * 2018-12-19 2022-09-21 Arkema, Inc. EVAPORATIVE LOSS CONTROL DEVICE
CN113993619A (zh) * 2019-04-17 2022-01-28 Csp技术公司 甲醛吸附用包含活性炭的聚合合成物
EP3956057A4 (en) * 2019-04-17 2023-01-18 CSP Technologies, Inc. POLYMERIC COMPOSITIONS COMPRISING ACTIVATED CARBON FOR THE SORPTION OF FORMALDEHYDE
CN115335320A (zh) * 2020-06-23 2022-11-11 西门子股份公司 气体的固态存储装置及其制造方法

Also Published As

Publication number Publication date
JP7058593B2 (ja) 2022-04-22
KR102666616B1 (ko) 2024-05-20
BR112018002572A2 (zh) 2018-10-02
JP2018527172A (ja) 2018-09-20
EP3337607A1 (en) 2018-06-27
WO2017031260A1 (en) 2017-02-23
KR20180042339A (ko) 2018-04-25
BR112018002572B1 (pt) 2021-10-19
CN107921412A (zh) 2018-04-17
EP3337607A4 (en) 2019-01-16
EP3337607B1 (en) 2023-01-04

Similar Documents

Publication Publication Date Title
EP3337607B1 (en) Gas phase storage device with high performance sorption binder
US10532340B2 (en) High performance sorption binder for gas phase storage devices
EP2903714B1 (en) Porous separation article
US10892490B2 (en) Particulate polymer binder composite
JP7513615B2 (ja) 蒸発損失制御装置
US10434478B2 (en) Porous separation article and separation method
CN112261981B (zh) 具有热塑性聚合物粘结剂体系的固定介质装置
JP2022539549A (ja) 架橋バインダー組成物
JP2018513039A (ja) 複合材的多孔性固形物品のための製造システム
EP3037473B1 (en) Compositions comprising vinylidene fluoride polymers and adsorbent carbon materials
JP6085335B2 (ja) 活性炭成形体、および該活性炭成形体の製造方法、並びに該活性炭成形体を用いた吸着材、および吸蔵材

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

AS Assignment

Owner name: ARKEMA INC., PENNSYLVANIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:STABLER, SEAN M.;REBER, RODERICK;REEL/FRAME:054425/0958

Effective date: 20201120

AS Assignment

Owner name: ARKEMA INC., PENNSYLVANIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:STABLER, SEAN M.;REBER, RODERICK;REEL/FRAME:054694/0382

Effective date: 20180416

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION