US20180180330A1 - Improved packed-screen-type magnetocaloric element - Google Patents

Improved packed-screen-type magnetocaloric element Download PDF

Info

Publication number
US20180180330A1
US20180180330A1 US15/736,155 US201615736155A US2018180330A1 US 20180180330 A1 US20180180330 A1 US 20180180330A1 US 201615736155 A US201615736155 A US 201615736155A US 2018180330 A1 US2018180330 A1 US 2018180330A1
Authority
US
United States
Prior art keywords
magnetocaloric
fibres
lattice element
lattice
longitudinal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/736,155
Other languages
English (en)
Inventor
Florian Scharf
Lian Zhang
Bernard Hendrik Reesink
David VAN ASTEN
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Magneto BV
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Publication of US20180180330A1 publication Critical patent/US20180180330A1/en
Assigned to BASF SE reassignment BASF SE ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SCHARF, Florian
Assigned to BASF NEDERLAND B.V. reassignment BASF NEDERLAND B.V. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ZHANG, LIAN, REESINK, BERNARD, VAN ASTEN, David
Assigned to BASF SE reassignment BASF SE ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BASF NEDERLAND B.V.
Assigned to MAGNETO B.V. reassignment MAGNETO B.V. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BASF SE
Abandoned legal-status Critical Current

Links

Images

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F25—REFRIGERATION OR COOLING; COMBINED HEATING AND REFRIGERATION SYSTEMS; HEAT PUMP SYSTEMS; MANUFACTURE OR STORAGE OF ICE; LIQUEFACTION SOLIDIFICATION OF GASES
    • F25B—REFRIGERATION MACHINES, PLANTS OR SYSTEMS; COMBINED HEATING AND REFRIGERATION SYSTEMS; HEAT PUMP SYSTEMS
    • F25B21/00—Machines, plants or systems, using electric or magnetic effects
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/012—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials adapted for magnetic entropy change by magnetocaloric effect, e.g. used as magnetic refrigerating material
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F7/00—Magnets
    • H01F7/02—Permanent magnets [PM]
    • H01F7/0231—Magnetic circuits with PM for power or force generation
    • H01F7/0247—Orientating, locating, transporting arrangements
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F25—REFRIGERATION OR COOLING; COMBINED HEATING AND REFRIGERATION SYSTEMS; HEAT PUMP SYSTEMS; MANUFACTURE OR STORAGE OF ICE; LIQUEFACTION SOLIDIFICATION OF GASES
    • F25B—REFRIGERATION MACHINES, PLANTS OR SYSTEMS; COMBINED HEATING AND REFRIGERATION SYSTEMS; HEAT PUMP SYSTEMS
    • F25B2321/00—Details of machines, plants or systems, using electric or magnetic effects
    • F25B2321/002—Details of machines, plants or systems, using electric or magnetic effects by using magneto-caloric effects
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F25—REFRIGERATION OR COOLING; COMBINED HEATING AND REFRIGERATION SYSTEMS; HEAT PUMP SYSTEMS; MANUFACTURE OR STORAGE OF ICE; LIQUEFACTION SOLIDIFICATION OF GASES
    • F25B—REFRIGERATION MACHINES, PLANTS OR SYSTEMS; COMBINED HEATING AND REFRIGERATION SYSTEMS; HEAT PUMP SYSTEMS
    • F25B2321/00—Details of machines, plants or systems, using electric or magnetic effects
    • F25B2321/002—Details of machines, plants or systems, using electric or magnetic effects by using magneto-caloric effects
    • F25B2321/0021—Details of machines, plants or systems, using electric or magnetic effects by using magneto-caloric effects with a static fixed magnet
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02B—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO BUILDINGS, e.g. HOUSING, HOUSE APPLIANCES OR RELATED END-USER APPLICATIONS
    • Y02B30/00—Energy efficient heating, ventilation or air conditioning [HVAC]

Definitions

  • the invention relates to a magnetocaloric lattice element, to a magnetocaloric regenerator, to a magnetocaloric heat pump, to a cooling device, to a magnetocaloric power generator and to method for operating a magnetocaloric heat pump.
  • Magnetocaloric materials change their temperature upon an application and removal of an external magnetic field. This behavior is the basis for development of magnetic cooling systems. Furthermore, the magnetocaloric effect can be used for power generation.
  • the magnetocaloric effect occurs under application of an external magnetic field to a suitable magnetocaloric material and under an ambient temperature in the vicinity of its Curie temperature.
  • the applied external magnetic field causes an alignment of the randomly aligned magnetic moments of the magnetocaloric material from a disordered paramagnetic phase to an ordered ferromagnetic phase and thus a magnetic phase transition, which can also be described as an induced increase of the Curie temperature of the material above the ambient temperature.
  • This magnetic phase transition implies a loss in magnetic entropy ⁇ S mag and in an adiabatic process (thermal isolation from the ambient temperature) leads to an increase in the entropy contribution of the crystal lattice of the magnetocaloric material by phonon generation in order to conserve entropy under the adiabatic condition.
  • ⁇ T temperature rise
  • this additional heat is removed from the material by heat transfer to an ambient heat sink in the form or a heat transfer medium.
  • Water is an example of a heat transfer medium used for heat removal from the magnetocaloric material.
  • Subsequently removing the external magnetic field can be described as a decrease of the Curie temperature back below the ambient temperature, and thus allows the magnetic moments reverting back to a random arrangement.
  • the external magnetic field is removed under adiabatic conditions, i.e., thermal isolation from the ambient temperature, which means that the overall entropy within the system stays unchanged. Since the magnetic entropy increases to its starting level without the external magnetic field, the entropy contribution of the crystal lattice of the magnetocaloric material itself is reduced, and under adiabatic process conditions thus results in a cooling of the magnetocaloric material below the ambient temperature. Thus, the temperature of the magnetocaloric material falls below the ambient temperature.
  • the described process cycle including magnetization and demagnetization is typically performed periodically in device applications.
  • the magnetocaloric effect can also be used for power conversion, in particular to convert heat generated during the described process cycle into electricity.
  • the present invention covers different aspects.
  • the invention provides a mesh-shaped magnetocaloric element of the packed-screen type, which herein is referred to as a magnetocaloric lattice element.
  • a second aspect is formed by a magnetocaloric regenerator; in a third aspect, the present invention provides a magnetocaloric heat pump.
  • a cooling device is a fourth aspect of the invention.
  • a magnetocaloric power generator forms a fifth aspect of the invention.
  • a magnetocaloric lattice element is provided.
  • the magnetocaloric lattice element is formed by fibres of magnetocaloric material, wherein
  • the magnetocaloric element according to the first aspect of the invention contains fibres of magnetocaloric material that are arranged in planes. Fibres of a given plane do not contact each other. However, the fibres are in mechanical contact with at least two fibres of a next neighbouring plane.
  • An at least roughly regular structure of this type is herein referred to as a magnetocaloric lattice structure of packed fibres, and the different planes of fibres are referred to as lattice planes.
  • the magnetocaloric element of the first aspect is therefore also called a magnetocaloric lattice element. As such, the magnetocaloric lattice element forms a magnetocaloric element of high structural stability.
  • the magnetocaloric element may also be described as a magnetocaloric element of the packed-screen type.
  • Embodiments of the magnetocaloric lattice element achieve an effective heat transfer in cooling applications with a low fluid resistance.
  • such embodiments of the magnetocaloric lattice elements structure achieve a low fluidic pressure loss in comparison, for instance, with a porous magnetocaloric element made of packed spheres.
  • the magnetocaloric lattice element of the first aspect of the present invention further features a predominant mass-weighted direction of longitudinal fibre extension.
  • the predominant mass-weighted direction of longitudinal fibre extension forms the most suitable direction for magnetization of the magnetocaloric lattice element. Suitable relative alignment of the magnetocaloric lattice element and the external magnetic field with respect to the predominant mass-weighted direction of longitudinal fibre extension thus leads to a particularly high magnetization of the magnetocaloric lattice element.
  • the magnetocaloric lattice element of the present invention is based on the recognition that its magnetization characteristic arises in view of a demagnetizing effect of any section of its magnetocaloric fibres that is not oriented along a direction of an external magnetic field.
  • the demagnetizing effect is a reduction of a maximal magnetization which could be generated in a magnetocaloric material of the same volume if all fibres were infinitesimally thin and arranged in a field direction of an external magnetic field.
  • the demagnetizing effect is a reduction of the magnetization caused by a given geometrical shape and arrangement of the fibres of magnetocaloric material.
  • the magnetocaloric lattice element according to the first aspect of the invention achieves an advantageous, particularly high magnetization of the magnetocaloric material, and as a consequence improves the performance of the application device, such as a magnetocaloric heat pump, cooling device or power generator.
  • a fibre shape can generally be described as having a longitudinal fibre extension which is larger than any lateral fibre extension, the latter referring to an extension in a direction that is perpendicular to the longitudinal fibre extension.
  • a typical example of a fibre shape is a cylindrical shape, which includes as different variants fibres having a circular, ellipsoidal, oval or rectangular cross-sectional shape in planes that are perpendicular to the longitudinal fibre extension.
  • the fibres do not necessarily exhibit a cylindrical shape.
  • the lateral fibre extension of the fibre may vary along the longitudinal fibre extension of the fibre.
  • an extension of the fibres in a direction perpendicular to their longitudinal fibre extension, i.e., in a lateral direction is between 50 ⁇ m and 800 ⁇ m.
  • the lateral extension varies in different lateral directions. In such embodiments, the mentioned values refer to a preferred maximum lateral extension.
  • all fibres of the magnetocaloric lattice element have essentially the same lateral extension perpendicular to their longitudinal fibre extension.
  • the lateral fibre extension is different for different fibres in other variants.
  • the magnetocaloric lattice element as a whole has fibres extending in least two directions.
  • the direction of longitudinal fibre extension is different in different sections of a given fibre. Examples will be discussed further below.
  • a fibre is made of a single magnetocaloric material. In some embodiments, however, the fibres are not homogenous in their material composition. Different fibre sections contain more or less magnetocaloric material, or different magnetocaloric materials.
  • the magnetocaloric lattice element may contain any suitable number of fibres.
  • the minimum number of fibres required to form the magnetocaloric lattice element is four fibres.
  • Lattice planes of the magnetocaloric lattice element are planar in some embodiments. However, the term lattice plane is not restricted to a crystallographic meaning implying strict planar extension. Lattice planes of the magnetocaloric lattice element have the form of curved surfaces in other embodiments.
  • the achievement of a predominant mass-weighted direction of longitudinal fibre extension can be described as follows: if each fibre is regarded as being partitioned into longitudinal fibre segments each having a segment mass and a longitudinal segment extension along a respective longitudinal segment direction, the predominant mass-weighted direction of longitudinal fibre extension is defined by the requirement that a weighted sum of all scalar projections of the respective longitudinal segment extensions of all fibre segments onto this predominant direction of longitudinal fibre extension is larger than the corresponding weighted sum of all scalar projections of the respective longitudinal segment extensions of all fibre segments onto any other direction of longitudinal segment extension, wherein each fibre segment is weighted in the weighted sum in proportion to its respective segment mass.
  • scalar projection means that a longitudinal segment n with a longitudinal segment extension along a respective longitudinal segment direction can be regarded as vector ⁇ right arrow over (a n ) ⁇ with length 1, and the corresponding scalar projection on the predominant mass-weighted direction of longitudinal fibre extension ⁇ right arrow over (e PMD ) ⁇ can be written as
  • ⁇ n is the angle between the respective longitudinal segment direction and the predominant mass-weighted direction of longitudinal fibre extension. Therefore, in this preferred embodiment the predominant mass-weighted direction of longitudinal fibre extension ⁇ right arrow over (e PMD ) ⁇ satisfies the following relation:
  • Eq.(1) defines the fact that the predominant mass-weighted direction of longitudinal fibre extension is exactly that direction, or that vector with length 1, for which a weighted sum of all scalar projections of the respective longitudinal segment extensions of all fibre segments onto this predominant direction of longitudinal fibre extension shows a maximum.
  • the predominant mass-weighted direction of longitudinal fibre extension is achieved as follows: all fibres belong to a first or second set of fibres and the fibres of the first set of fibres all extend along a common first longitudinal direction of fibre extension and the fibres of the second set of fibres all extend along a common second longitudinal direction of fibre extension different from the first longitudinal direction.
  • the fibres of the magnetocaloric lattice element extent into two directions, so that there are just two different longitudinal segment directions for determining the predominant mass-weighted direction of longitudinal fibre extension according to Eq.(1). Parallel fibres require less effort in production and provide a high structural stability.
  • each lattice plane provides fibres of a respective set of fibres all extend along a common respective longitudinal direction of fibre extension.
  • neighbouring planes alternate between fibres of the first and second set of fibres. This can lead to a basically regular structure of the magnetocaloric lattice element and therefore provide a high structural stability.
  • a lattice angle between the first longitudinal direction and the second longitudinal direction is a sharp angle between 5° and 85° (arc degrees).
  • An even smaller lattice angle i.e. a lattice angle below 5°, would lead to a high pressure loss of a heat transfer medium that flows through the magnetocaloric lattice element.
  • An even larger lattice angle i.e., a lattice angle approaching 90°, increases the already described demagnetizing effect of the magnetocaloric lattice element in case of fibres substantially equal in shape and number for the first and second longitudinal directions.
  • the sharp angle preferably is in a range between 20° and 70°, even more preferably between 40° and 60°.
  • the fibres have equal sizes and are produced with the same magnetocaloric material and all belong to either the first or second set of fibres.
  • the predominant mass-weighted direction of longitudinal fibre extension in this variant is basically along a bisection of the sharp lattice angle with respect to the first direction of the first set of fibres and to the second direction of the second set of fibres.
  • the first set of fibres has a smaller mass amount of magnetocaloric material than the second set of fibres.
  • the different mass amounts cause the predominant mass-weighted direction of longitudinal fibre extension to be influenced more strongly by the longitudinal direction of fibre extension of the second set of fibres than that of first set of fibres.
  • Using such different mass amounts of magnetocaloric material can be advantageous in order to reduce the pressure loss of a heat transfer fluid flowing through the magnetocaloric lattice element in case of using the magnetocaloric lattice element within a heat pump, a cooling device or a power generator.
  • a total number of fibres in the first set of fibres is smaller than a total number of fibres in the second set of fibres.
  • each of the fibres belongs to either the first or second set of fibres and the first and second sets of fibres are oriented perpendicular to each other.
  • the predominant mass-weighted direction of longitudinal fibre extension is oriented along the longitudinal direction of fibre extension of the second set of fibres.
  • the first set of fibres is at least two times smaller than the second set of fibres, considering a cross-sectional surface area having a surface vector parallel to the longitudinal extension of the respective fibre segments.
  • all fibres belong to the first and second set of fibres and the first and second sets of fibres are oriented perpendicular to each other.
  • the predominant mass-weighted direction of longitudinal fibre extension is oriented along the longitudinal direction of fibre extension of the second set of fibres.
  • the magnetocaloric lattice element is for instance formed by extruding a highly loaded paste comprising magnetocaloric material, using a moving nozzle so that the fibres of the magnetocaloric lattice element can be produced layer by layer.
  • the paste comprising the magnetocaloric material may additionally comprise a solvent, such as water, a binder and additives.
  • a defoamer is also added to avoid air bubbles in the paste.
  • the magnetocaloric lattice element is formed by a threedimensional-printing process.
  • all fibres consist of the same magnetocaloric material.
  • the magnetocaloric lattice element consists of at least two different magnetocaloric materials.
  • the magnetocaloric material in respective subsequent planes exhibits a series of decreasing Curie-temperatures of the respective magnetocaloric materials. Such a series of decreasing Curie-temperatures in subsequent planes can allow an energy efficient cooling of a cooling device comprising the magnetocaloric lattice element far below an ambient temperature of the cooling device.
  • the invention relates to a magnetocaloric regenerator, comprising
  • the magnetocaloric regenerator according to the second aspect of the invention shares the advantages of the magnetocaloric lattice element of the first aspect of the invention.
  • the magnetocaloric regenerator further provides a fluid channel system that in operation of the regenerator achieves a flow of a heat transfer fluid through the magnetocaloric lattice element, according to a desired process cycle, for instance in an application as a magnetocaloric cooling device, heat pump or power generator.
  • the invention relates to a magnetocaloric heat pump, comprising
  • the magnetocaloric heat pump according to the third aspect of the invention shares the advantages described in the context of the magnetocaloric lattice element according to the first aspect of the invention.
  • the magnetocaloric heat pump further achieves a mutual arrangement of the magnetocaloric lattice element and the magnet assembly in an advantageous orientation of the predominant mass-weighted direction of longitudinal fibre extension in alignment parallel to the direction of the generated external magnetic field within the magnetocaloric heat pump.
  • the heat pump is in one embodiment configured to allow different relative alignment positions achieving different ones of a plurality of possible field directions with respect to the predominant mass-weighted direction of longitudinal fibre extension of the magnetocaloric lattice element in different operational alignment positions.
  • An optimum of the magnetocaloric effect and its desired technical impact is achieved in parallel alignment.
  • a reduced effect can also be achieved if only a field component of the external magnetic field, which is applied to the magnetocaloric lattice element, exhibits the field direction parallel to the predominant mass-weighted direction of longitudinal fibre extension.
  • the magnetocaloric heat pump further comprises a magnetocaloric lattice element
  • the predominant mass-weighted direction of longitudinal fibre extension is oriented along the bisector of the sharp lattice angle between the first longitudinal direction and the second longitudinal direction.
  • the magnetocaloric heat pump comprises a magnetocaloric lattice element
  • the magnetocaloric heat pump further comprises a controlling unit arranged and configured to control a mutually arrangement of the magnet assembly and the magnetocaloric lattice element for applying the external magnetic field to the magnetocaloric lattice element with a field direction which is parallel to the predominant mass-weighted direction of longitudinal fibre extension.
  • the controlling unit provides an advantageous orientation of the magnetocaloric lattice element and of the magnet assembly with respect to each other, automatically and/or manually.
  • the controlling unit comprises a processor device which is configured to compare the orientation of the magnetocaloric lattice element and of the magnet assembly with reference values stored in the processor device.
  • the controlling unit comprises a visual indicator that is configured to show the user what changes of the orientation of the magnetocaloric lattice element and of the magnet assembly should be executed manually.
  • the controlling unit automatically executes a periodic motion of the magnetocaloric lattice element according to a periodic motion of the magnet assembly.
  • the invention relates to a cooling device, comprising a magnetocaloric lattice element according to at least one of the embodiments of the first aspect of the invention.
  • the cooling device according to the fourth aspect of the invention shares the advantages described in the context of the magnetocaloric lattice element according to the first aspect of the invention.
  • the cooling device comprises the magnetocaloric regenerator according to at least one of the embodiments of the second aspect of the invention.
  • the cooling device comprises the magnetocaloric heat pump according to at least one of the embodiments of the third aspect of the invention.
  • the cooling device performs a process cycle including magnetization and demagnetization of the magnetocaloric lattice element.
  • the cooling device performs a process cycle as explained above, exhibiting a first phase and a second phase of magnetocaloric cooling.
  • the invention relates to a magnetocaloric power generator, comprising a magnetocaloric lattice element according to at least one of the embodiments of the first aspect of the invention.
  • the magnetocaloric power generator comprises a heating reservoir and a cooling reservoir, which are arranged and configured to heat and cool the magnetocaloric lattice element to change its magnetic field periodically, and a coil, which is arranged at the magnetocaloric lattice element in order to provide an electrical current which is induced by changes in the magnetic field of the magnetocaloric lattice element.
  • the invention relates to a method for operating a magnetocaloric heat pump.
  • the method comprises the steps of
  • the method according to the fifth aspect of the invention shares the advantages described in the context of the magnetocaloric lattice element according to the first aspect of the invention.
  • magnetocaloric lattice element of the first aspect of the invention also defined in claim 1
  • the magnetocaloric regenerator of the second aspect also defined in claim 9
  • the magnetocaloric heat pump of the third aspect also defined in claim 10
  • the cooling device of the fourth aspect also defined in claim 13
  • the magnetocaloric power generator of the fifth aspect also defined in claim 14
  • the method for operating a magnetocaloric lattice element also defined in claim 15
  • FIG. 1 shows an embodiment of a magnetocaloric lattice element according to the first aspect of the invention
  • FIG. 2 shows another embodiment of a magnetocaloric lattice element according to the first aspect of the invention
  • FIG. 3 shows another embodiment of a magnetocaloric lattice element according to the first aspect of the invention
  • FIGS. 4 a, b show further embodiments of a magnetocaloric lattice element according to the first aspect of the invention
  • FIG. 5 shows an embodiment of a single fibre of a magnetocaloric lattice element according to the first aspect of the invention
  • FIGS. 6 a - d show further embodiments of a magnetocaloric lattice element according to the first aspect of the invention
  • FIG. 7 shows an embodiment of a magnetocaloric regenerator according to the second aspect of the invention
  • FIG. 8 shows an embodiment of a magnetocaloric heat pump according to the third aspect of the invention
  • FIG. 9 shows a schematic illustration of an embodiment of a cooling device according to the fourth aspect of the invention.
  • FIG. 10 shows a schematic illustration of an embodiment of a magnetocaloric power generator according to the fifth aspect of the invention.
  • FIG. 11 shows an embodiment of a method for operating a magnetocaloric heat pump according to the sixth aspect of the invention.
  • FIG. 1 shows an embodiment of a magnetocaloric lattice element 100 according to the first aspect of the invention.
  • the magnetocaloric lattice element 100 is formed by fibres 105 ′, 105 ′′ of magnetocaloric material, wherein the fibres 105 ′, 105 ′′ are arranged in two respective parallel and planar lattice planes 134 , 138 , each fibre 105 ′, 105 ′′ having a respective one of two longitudinal directions 114 , 118 and a respective mass of magnetocaloric material.
  • the depicted fibres 105 ′, 105 ′′ of the magnetocaloric lattice element 100 exhibit an extension (diameter) of between 50 ⁇ m and 800 ⁇ m in a direction perpendicular to their longitudinal fibre extension. All fibres belong to a first or second set of fibres 105 ′, 105 ′′ and the fibres of the first set of fibres 105 ′ all extend along a common first longitudinal direction 114 of fibre extension and the fibres of the second set of fibres 105 ′′ all extend along a common second longitudinal direction 118 of fibre extension different from the first longitudinal direction 114 .
  • each fibre 105 ′ of the given lattice plane 134 is attached to fibres 105 ′′ in the other lattice plane 138 , and vice versa.
  • the attachment points of a given fibre are the crossing points of the given fibre with other fibres of one of its next neighboring lattice planes.
  • each lattice plane has two next neighbouring lattice planes, and there are contact points for each fibre of a given lattice plane to other fibres in both next neighboring lattice planes.
  • the contact points provide for an attachment of the fibres to each other and thus achieve mechanical stability of the packed-screen structure as a whole.
  • a lattice angle 110 between the first longitudinal direction 114 and the second longitudinal direction 118 is a sharp angle between 40° and 60°.
  • the resulting rhombic structure of the magnetocaloric lattice element 100 exhibits exactly one predominant mass-weighted direction 140 of longitudinal fibre extension, which is oriented along a bisector of the sharp lattice angle 110 .
  • FIG. 2 shows an embodiment of a magnetocaloric lattice element 200 according to the first aspect of the invention.
  • All fibres 205 ′, 205 ′′ belong to a first or second set of fibres and the fibres of the first set of fibres 205 ′ all extend along a common first longitudinal direction 214 of fibre extension and the fibres of the second set of fibres 205 ′′ all extend along a common second longitudinal direction 218 of fibre extension perpendicular to the first longitudinal direction 214 .
  • a total number of fibres in the first set of fibres 205 ′ is smaller than a total number of fibres in the second set of fibres 205 ′′.
  • the first set of fibres 205 ′ includes a smaller mass amount of magnetocaloric material than the second set of fibres 205 ′′.
  • This design measure achieves that the predominant mass-weighted direction 240 of longitudinal fibre extension is oriented along the second longitudinal direction 218 .
  • the determination of the predominant mass-weighted direction 240 of longitudinal fibre extension is explained quantitatively in the context of FIG. 5 .
  • FIG. 3 shows a further embodiment of a magnetocaloric lattice element 300 according to the first aspect of the invention.
  • all fibres 305 ′, 305 ′′ belong to either a first or a second set of fibres, and the fibres of the first set of fibres 305 ′ all extend along a common first longitudinal direction 314 of fibre extension, and the fibres of the second set of fibres 305 ′′ all extend along a common second longitudinal direction 318 of fibre extension, which is perpendicular to the first longitudinal direction 314 .
  • a lateral extension of the fibres of the first set of fibres 305 ′ is at least two times smaller than a lateral extension of the fibres of the second set of fibres 305 ′′, as determined for instance by considering their cross-sectional surface area having a surface vector parallel to the longitudinal extension of the respective fibres.
  • the predominant mass-weighted direction 340 of longitudinal fibre extension is oriented along the second longitudinal direction 318 .
  • the determination of the orientation of the predominant mass-weighted direction 340 of longitudinal fibre extension is explained quantitatively in the context of FIG. 5 .
  • the lateral extension of the fibres of the first set of fibres is between four and eight times smaller than the lateral extension of the fibres of the second set of fibres.
  • FIG. 4 a and FIG. 4 b show two further embodiments of a magnetocaloric lattice element 400 a , 400 b according to the first aspect of the invention.
  • the structure of the illustrated embodiment is similar to those shown in FIG. 1 and FIG. 2 .
  • Fibres of the first set of fibres 405 a ′, 405 b ′ extend in parallel to each other, but in contrast to the earlier embodiments they are not straight. They exhibit a curved, cosine-type ( FIG. 4 a ) or saw-tooth-type ( FIG. 4 b ) or zigzag line shape along their longitudinal extension. In fabrication, the saw-tooth shape is typically made with a certain radius of curvature at points of attachment with the fibres 405 b ′′ of the second set of fibres.
  • the fibres of the second set of fibres 405 a ′′, 405 b ′′ are in the shape of straight lines and have a common second longitudinal direction of fibre extension 418 a , 418 b.
  • the predominant mass-weighted direction 440 a , 440 b of longitudinal fibre extension is in both embodiments oriented along the second longitudinal direction 418 a , 418 b .
  • the determination of the orientation of the predominant mass-weighted direction 440 a , 440 b of longitudinal fibre extension is explained quantitatively in the context of FIG. 5 .
  • no fibres are arranged parallel to each other, so that there is not a common first or second longitudinal direction.
  • FIG. 5 shows an embodiment of two single fibres 500 , 510 of a magnetocaloric lattice element according to the first aspect of the invention.
  • the fibres are not straight, so that they cannot be said to extend in a fixed longitudinal direction.
  • FIG. 5 illustrates the concept of determination of the orientation of the predominant mass-weighted direction for a magnetocaloric lattice element.
  • Such partitioning into fibre segments can be achieved easily by modern computer-aided design tools using a computer model of the magnetocaloric lattice elements.
  • the partitioning serves to break down a given fibre into fibre segments along its longitudinal extension.
  • the size of the segments along the longitudinal extension can be chosen using the following considerations: For each of the fibre segments, a single direction of longitudinal extension shall be determined. An optimum partitioning provides an exact direction of longitudinal extension for each fibre segment. However, achieving the optimum partitioning may not be required, and an inaccuracy of a certain angular range may be acceptable in the determination of the respective directions.
  • these finite longitudinal fibre segments 505 , 515 the predominant mass-weighted direction 540 of longitudinal fibre extension for the two fibres 500 , 510 can be determined by finding a direction ⁇ right arrow over (e PMD ) ⁇ that satisfies the following relation:
  • partitioning of fibres into longitudinal fibre sections such a partitioning is chosen to be precise enough for essentially finding the predominant mass-weighted direction of longitudinal fibre extension.
  • a partitioning into a finite number of longitudinal fibre sections is sufficient to determine the predominant mass-weighted direction of longitudinal fibre extension.
  • FIGS. 6 a , 6 b , 6 c and 6 d show further embodiments of a magnetocaloric lattice element 600 a , 600 b , 600 c , and 600 d according to the first aspect of the invention.
  • the Figures each show a respective schematic view of a section of a magnetocaloric lattice element and are not drawn to scale.
  • the numbers of fibres of the respective magnetocaloric lattice elements in the paper plane is typically much larger than that covered by the respective section shown.
  • the views in FIGS. 6 a to 6 d each cover only two neighbouring lattice planes, neighbouring in a direction perpendicular to the paper plane of the respective Figures.
  • the graphical representation of the sections shown has a circular outer shape in order to restrict the illustration to the essential feature of the structure in the context of the present invention.
  • the circular shape does not necessarily reflect an actual outer shape of the respective magnetocaloric lattice element, which can have any outer shape suitable for a given application case.
  • the respective magnetocaloric lattice elements form packed-screen type magnetocaloric lattice elements and have further lattice planes stacked in the direction perpendicular to the paper plane.
  • a porosity of the respective magnetocaloric lattice element 600 a , 600 b , 600 c , 600 d i.e., the relation between the volume of the magnetocaloric material of the fibres divided by a total volume of the magnetocaloric lattice element, amounts to the same value of 0.4764 for all four embodiments of FIGS. 6 a to 6 d.
  • FIG. 6 a shows a magnetocaloric lattice element 600 a wherein a lattice angle 620 a between the first longitudinal direction 614 a and the second longitudinal direction 618 a is a sharp angle of 70°.
  • the resulting rhombic structure of the magnetocaloric lattice element 600 a exhibits exactly one predominant mass-weighted direction 630 a of longitudinal fibre extension, which is oriented along a bisector of the sharp lattice angle 620 a .
  • a gray-scaled tone of the fibres visualizes a demagnetizing factor N of the magnetocaloric lattice element 600 a , which is 14% smaller than in the case of a corresponding reference magnetocaloric lattice element of the same porosity with fibres in a perpendicular arrangement (not shown).
  • FIG. 6 b shows another variant of a magnetocaloric lattice element 600 b , wherein a lattice angle 620 b between the first longitudinal direction 614 b and the second longitudinal direction 618 b is a sharp angle of 50°.
  • the resulting rhombic structure of the magnetocaloric lattice element 600 b exhibits exactly one predominant mass-weighted direction 630 b of longitudinal fibre extension, which is oriented along a bisector of the sharp lattice angle 620 b .
  • the gray-scaled tone of the fibres indicates a demagnetizing factor N of the magnetocaloric lattice element 600 b , which is even further reduced in comparison with the magnetocaloric lattice element of FIG. 6 a , namely, 27% smaller than in the case of the reference magnetocaloric lattice element.
  • FIG. 6 c shows a further variant of a magnetocaloric lattice element 600 c , wherein a lattice angle 620 c between the first longitudinal direction 614 c and the second longitudinal direction 618 c is a sharp angle of 30°.
  • the resulting rhombic structure of the magnetocaloric lattice element 600 c exhibits exactly one predominant mass-weighted direction 630 c of longitudinal fibre extension, which is oriented along a bisector of the sharp lattice angle 620 c .
  • the gray-scaled tone of the fibres indicates a demagnetizing factor N of the magnetocaloric lattice element 600 c , which is even further reduced in comparison with the magnetocaloric lattice element of FIG. 6 b , namely, 37% smaller than in the case the reference magnetocaloric lattice element.
  • FIG. 6 d shows a magnetocaloric lattice element 600 d , wherein a lattice angle 620 d between the first longitudinal direction 614 d and the second longitudinal direction 618 d is a sharp angle of 10°.
  • the resulting rhombic structure of the magnetocaloric lattice element 600 d exhibits exactly one predominant mass-weighted direction 630 d of longitudinal fibre extension, which is oriented along a bisector of the sharp lattice angle 620 d .
  • the gray-scaled tone visualizes a demagnetizing factor N of the magnetocaloric lattice element 600 c , which is even further reduced in comparison with the magnetocaloric lattice element of FIG. 6 c , namely, 43% smaller than in the case of the reference magnetocaloric lattice element.
  • FIGS. 6 a , 6 b , 6 c and 6 d show that small sharp lattice angles achieve a strong reduction of the demagnetizing effect in the magnetocaloric lattice element.
  • the positive effect regarding demagnetization with decreasing lattice angles 620 a , 620 b , 620 c , 620 d is accompanied by an increase in pressure loss of a heat transfer medium that is guided through the pores of the respective magnetocaloric lattice elements 600 a , 600 b , 600 c , 600 d within a cooling device.
  • a high pressure loss is usually not desired. Both effects have to be taken into account and balanced in the design of a magnetocaloric lattice element that is optimally suited for a given application scenario.
  • FIG. 7 illustrates an embodiment of a magnetocaloric regenerator 700 according to the second aspect of the invention.
  • the magnetocaloric regenerator 700 comprises a regenerator housing 710 , a magnetocaloric lattice element 720 in the regenerator housing 710 , and a fluid channel system 730 configured to guide a flow of a fluid 740 through the magnetocaloric lattice element 720 .
  • the magnetocaloric lattice element 720 is similar to the magnetocaloric lattice element 600 a shown in FIG. 6 a.
  • FIG. 8 shows an embodiment of a magnetocaloric heat pump 800 according to the third aspect of the invention.
  • the magnetocaloric heat pump 800 comprises the magnetocaloric regenerator 700 shown in FIG. 7 with the magnetocaloric lattice element 720 , and a magnet assembly 840 , 840 ′ at a ring-shaped rotatable support structure (not shown) for applying an external magnetic field to the magnetocaloric lattice element 720 .
  • the magnetocaloric lattice element 720 and the magnet assembly 840 , 840 ′ are mutually arranged for providing the external magnetic field to the magnetocaloric lattice element 720 with a field direction 830 , which is parallel to the predominant mass-weighted direction 850 of longitudinal fibre extension of the magnetocaloric lattice element 720 .
  • the magnetic field is preferably substantially homogeneous at least in the volume assumed by the magnetocaloric lattice element 720 .
  • all fibres of the magnetocaloric lattice element 720 have a same respective mass amount of magnetocaloric material, and the magnetocaloric lattice element 720 and the magnet assembly 840 , 840 ′ are configured to be mutually arranged for applying the external magnetic field to the magnetocaloric lattice element 720 with a field direction 830 which is oriented along a bisector of the sharp lattice angle 822 between the first longitudinal direction 824 and the second longitudinal direction 826 .
  • the bisector is oriented along the predominant mass-weighted direction 850 of longitudinal fibre extension.
  • the first longitudinal direction of the fibres of the magnetocaloric lattice element is perpendicular to the second longitudinal direction, as shown in FIGS. 2 and 3 , and the magnetocaloric lattice element and the magnet assembly are configured to be mutually arranged for applying the external magnetic field to the magnetocaloric lattice element with a field direction which is oriented along the second longitudinal direction which forms the predominant mass-weighted direction of longitudinal fibre extension.
  • FIG. 9 shows a schematic illustration of an embodiment of a cooling device 900 according to the fourth aspect of the invention.
  • the cooling device 900 comprises a magnetocaloric lattice element 910 according to the first aspect of the invention, which is arranged within a magnetocaloric regenerator 920 according to an embodiment of the second aspect of the invention.
  • the magnetocaloric regenerator 920 is arranged within a magnetocaloric heat pump 930 according to an embodiment of the third aspect of the invention, which in operation pumps heat out of the cooling device 900 into an ambient environment and thus effectively cools the cooling device 900 .
  • the pumping of heat out of the cooling device 900 comprises a process cycle including a magnetization and demagnetization of the magnetocaloric lattice element 910 , as already explained above.
  • FIG. 10 shows a schematic illustration of an embodiment of a magnetocaloric power generator 1000 according to the fifth aspect of the invention.
  • the magnetocaloric power generator 1000 comprises a heating reservoir 1010 and a cooling reservoir 1020 , which are arranged and configured to heat and cool a magnetocaloric lattice element 1030 to change its magnetic field periodically.
  • the magnetocaloric power generator 1000 comprises a permanent magnet 1040 , which is arranged at the magnetocaloric lattice element 1030 in order to provide an electrical current which is induced by changes in the magnetic field of the magnetocaloric lattice element 1030 .
  • the magnetocaloric lattice element 1030 fibres of magnetocaloric material are arranged in lattice planes, which are stacked parallel to each other.
  • the fibres of any given lattice plane do not contact each other but the fibres of the given lattice plane each contact at least two respective other fibres of a next neighbouring lattice plane.
  • the magnetocaloric lattice element exhibits exactly one predominant mass-weighted direction of longitudinal fibre extension.
  • the predominant mass-weighted direction of longitudinal fibre extension is in parallel with a field direction of the permanent magnet 1040 .
  • FIG. 11 shows an embodiment of a method for operating a magnetocaloric heat pump according to the sixth aspect of the invention.
  • the method comprises as a first step 1110 a providing of a magnetocaloric lattice element according to at least one embodiment according to the first aspect of the invention.
  • the second step 1120 of the method is a providing of a magnet assembly for applying an external magnetic field to the magnetocaloric lattice element.
  • the final step 1130 is an arranging of the magnetocaloric lattice element and of the magnet assembly for applying the external magnetic field to the magnetocaloric lattice element with a field direction which is parallel to the predominant mass-weighted direction of longitudinal fibre extension.
  • the invention relates to a magnetocaloric lattice element formed by fibres of magnetocaloric material, wherein the fibres are arranged in respective parallel lattice planes, each fibre having a respective mass of magnetocaloric material, the fibres of a given lattice plane do not contact each other but each fibre of a given lattice plane is attached to at least two fibres in a next neighbouring lattice plane, and wherein the magnetocaloric lattice element exhibits exactly one predominant mass-weighted direction of longitudinal fibre extension.
  • the invention is not limited to the disclosed embodiments.
  • the invention is not restricted to the use of particular shapes of fibres, or to just two longitudinal directions of fibre extension, or to a using of the magnetocaloric lattice element with a cooling device.
  • the invention is furthermore not restricted to combinations with a magnet assembly.

Landscapes

  • Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • Power Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Thermal Sciences (AREA)
  • General Engineering & Computer Science (AREA)
  • Electromagnetism (AREA)
  • Hard Magnetic Materials (AREA)
  • General Induction Heating (AREA)
US15/736,155 2015-06-19 2016-06-08 Improved packed-screen-type magnetocaloric element Abandoned US20180180330A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP15173006 2015-06-19
EP15173006.6 2015-06-19
PCT/EP2016/063034 WO2016202663A1 (en) 2015-06-19 2016-06-08 Packed-screen type magnetocaloric element

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2016/063034 A-371-Of-International WO2016202663A1 (en) 2015-06-19 2016-06-08 Packed-screen type magnetocaloric element

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US17/979,010 Continuation US11802720B2 (en) 2015-06-19 2022-11-02 Packed-screen type magnetocaloric element

Publications (1)

Publication Number Publication Date
US20180180330A1 true US20180180330A1 (en) 2018-06-28

Family

ID=53487223

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/736,155 Abandoned US20180180330A1 (en) 2015-06-19 2016-06-08 Improved packed-screen-type magnetocaloric element
US17/979,010 Active US11802720B2 (en) 2015-06-19 2022-11-02 Packed-screen type magnetocaloric element

Family Applications After (1)

Application Number Title Priority Date Filing Date
US17/979,010 Active US11802720B2 (en) 2015-06-19 2022-11-02 Packed-screen type magnetocaloric element

Country Status (6)

Country Link
US (2) US20180180330A1 (ko)
EP (1) EP3311081B1 (ko)
JP (2) JP7218988B2 (ko)
KR (1) KR102522939B1 (ko)
CN (1) CN107735628B (ko)
WO (1) WO2016202663A1 (ko)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7218988B2 (ja) * 2015-06-19 2023-02-07 マグネート ベー．フェー． パックスクリーン型磁気熱量素子
JP6486998B2 (ja) * 2017-08-10 2019-03-20 株式会社フジクラ 熱交換器及び磁気ヒートポンプ装置
CN111872356B (zh) * 2020-08-06 2021-12-03 上海大学 一种碳纤维增强的磁制冷功能合金复合材料制备装置与制备方法
CN112863846B (zh) * 2021-01-08 2022-12-09 哈尔滨工业大学 一种磁制冷机回热器的磁相变材料的制备方法及磁制冷循环系统

Citations (42)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2898091A (en) * 1956-09-27 1959-08-04 Philips Corp Thermal regenerator
US4651808A (en) * 1985-03-13 1987-03-24 Aisin Seiki Kabushiki Kaisha Regenerator
US5332029A (en) * 1992-01-08 1994-07-26 Kabushiki Kaisha Toshiba Regenerator
US5429177A (en) * 1993-07-09 1995-07-04 Sierra Regenators, Inc. Foil regenerator
US5593517A (en) * 1993-09-17 1997-01-14 Kabushiki Kaisha Toshiba Regenerating material and refrigerator using the same
US5897963A (en) * 1995-01-10 1999-04-27 Composite Materials Technology, Inc. Composite wires and process of forming same
US6022486A (en) * 1988-02-02 2000-02-08 Kabushiki Kaisha Toshiba Refrigerator comprising a refrigerant and heat regenerative material
US6131644A (en) * 1998-03-31 2000-10-17 Advanced Mobile Telecommunication Technology Inc. Heat exchanger and method of producing the same
US20010025494A1 (en) * 2000-03-24 2001-10-04 Kabushiki Kaisha Toshiba Regenerator and cold accumulation refrigerator using the same
US6475935B1 (en) * 1999-07-09 2002-11-05 Irie Kouken Co., Ltd Regenerator and regenerative material used therein
US20030051774A1 (en) * 2001-03-27 2003-03-20 Akiko Saito Magnetic material
US6595004B1 (en) * 2002-04-19 2003-07-22 International Business Machines Corporation Apparatus and methods for performing switching in magnetic refrigeration systems using thermoelectric switches
US6680663B1 (en) * 2000-03-24 2004-01-20 Iowa State University Research Foundation, Inc. Permanent magnet structure for generation of magnetic fields
US6732785B2 (en) * 2002-09-20 2004-05-11 Matthew P. Mitchell Tab joint in etched foil regenerator
US6825681B2 (en) * 2002-07-19 2004-11-30 Delta Design, Inc. Thermal control of a DUT using a thermal control substrate
US6854509B2 (en) * 2001-07-10 2005-02-15 Matthew P. Mitchell Foil structures for regenerators
US20050068140A1 (en) * 2003-09-29 2005-03-31 General Electric Company Permanent magnet assembly with movable permanent body for main magnetic field adjustable
US20050110602A1 (en) * 2003-11-22 2005-05-26 Bruker Biospin Gmbh Low resistance shield
US7148777B2 (en) * 2004-02-03 2006-12-12 Astronautics Corporation Of America Permanent magnet assembly
US7168255B2 (en) * 2003-03-28 2007-01-30 Kabushiki Kaisha Toshiba Magnetic composite material and method for producing the same
US20070144181A1 (en) * 2002-12-24 2007-06-28 Andrej Kitanovski Method and device for continuous generation of cold and heat by means of the magneto-calorific effect
US20070283994A1 (en) * 2006-06-12 2007-12-13 Texas Instruments, Inc. Novel solid state heat pump
US20080078184A1 (en) * 2006-09-28 2008-04-03 Kabushiki Kaisha Toshiba Magnetic refrigerating device and magnetic refrigerating method
US20100107654A1 (en) * 2005-10-28 2010-05-06 Andrew Rowe Shimmed active magnetic regenerator for use in thermodynamic devices
US20100116471A1 (en) * 2007-12-27 2010-05-13 Georg Werner Reppel Composite article with magnetocalorically active material and method for its production
US20110048031A1 (en) * 2009-08-28 2011-03-03 General Electric Company Magneto-caloric regenerator system and method
US20110048690A1 (en) * 2008-05-16 2011-03-03 Vacuumschmelze Gmbh & Co. Kg Article for Magnetic Heat Exchange and Method for Manufacturing an Article for Magnetic Heat Exchange
US20110173993A1 (en) * 2008-09-25 2011-07-21 Cooltech Applications S.A.S. Magnetocaloric element
US20120031108A1 (en) * 2010-08-05 2012-02-09 Tadahiko Kobayashi Magnetic refrigerating device and magnetic refrigerating system
US20120031109A1 (en) * 2010-06-07 2012-02-09 Jan Vetrovec Magnetocaloric refrigerator
US20120073307A1 (en) * 2010-09-29 2012-03-29 Shiori Kaji Heat exchanger unit and thermal cycling unit
US20120272666A1 (en) * 2011-04-28 2012-11-01 Denso Corporation Magnetic heat pump system
US8537053B2 (en) * 2009-07-20 2013-09-17 Commissariat A L'energie Atomique Et Aux Energies Alternatives Left handed body, wave guide device and antenna using this body, manufacturing method for this body
US20140113828A1 (en) * 2011-03-30 2014-04-24 Ambature Inc. Electrical, mechanical, computing/ and/or other devices formed of extremely low resistance materials
US20140338365A1 (en) * 2011-09-14 2014-11-20 Nissan Motor Co., Ltd. Magnetic structure and magnetic air-conditioning and heating device using same
US20150033763A1 (en) * 2012-03-30 2015-02-05 Kabushiki Kaisha Toshiba Material for magnetic refrigeration and magnetic refrigeration device
US8991170B2 (en) * 2011-05-01 2015-03-31 Thomas Mallory Sherlock Solar air conditioning heat pump with minimized dead volume
US9175885B2 (en) * 2007-02-12 2015-11-03 Vacuumschmelze Gmbh & Co. Kg Article made of a granular magnetocalorically active material for heat exchange
US20170297760A1 (en) * 2014-09-23 2017-10-19 Tetra Laval Holdings & Finance S.A. Method and device for magnetising a package material, and packaging material magnetised with said method
US20180252445A1 (en) * 2016-03-31 2018-09-06 Fujikura Ltd. Heat exchanger and magnetic heat pump device
JP2018146154A (ja) * 2017-03-03 2018-09-20 株式会社フジクラ 熱交換器及び磁気ヒートポンプ装置
JP2019032145A (ja) * 2017-08-10 2019-02-28 株式会社フジクラ 熱交換器及び磁気ヒートポンプ装置

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5924188A (ja) * 1982-07-30 1984-02-07 Hitachi Ltd 蓄熱装置
JPH0792286B2 (ja) * 1988-02-02 1995-10-09 株式会社東芝 冷凍機
JPH0752542Y2 (ja) * 1988-02-26 1995-11-29 東芝設備機器株式会社 冷却器
JPH1020591A (ja) 1996-06-28 1998-01-23 Sharp Corp 画像消去装置を備えた画像形成装置
EP0870814B1 (en) 1996-10-30 2002-06-05 Kabushiki Kaisha Toshiba Cold accumulation material for ultra-low temperature, refrigerating machine using the material, and heat shield material
WO2000038831A1 (en) 1998-12-31 2000-07-06 Hexablock, Inc. Magneto absorbent
JP4303879B2 (ja) * 2000-10-02 2009-07-29 株式会社東芝 磁気冷凍装置
SE0102753D0 (sv) * 2001-08-17 2001-08-17 Abb Ab A fluid handling system
FR2890158A1 (fr) * 2005-09-01 2007-03-02 Cooltech Applic Soc Par Action Generateur thermique a materiau magnetocalorique
JP4842327B2 (ja) * 2005-11-10 2011-12-21 株式会社大宇エレクトロニクス 磁気冷凍機
DE202007003576U1 (de) * 2006-12-01 2008-04-10 Liebherr-Hausgeräte Ochsenhausen GmbH Kühl- und/oder Gefriergerät
GB0903974D0 (en) 2009-03-09 2009-04-22 Univ Denmark Tech Dtu A parallel magnetic refrigeration assembly and a method of refrigeration
JP5468424B2 (ja) * 2010-03-12 2014-04-09 住友重機械工業株式会社 蓄冷器、蓄冷式冷凍機、クライオポンプ、および冷凍装置
EP2634511A4 (en) 2010-10-29 2014-07-09 Toshiba Kk HEAT EXCHANGERS AND MAGNETIC COOLING SYSTEM
JP5665005B2 (ja) * 2011-05-17 2015-02-04 日産自動車株式会社 磁気冷暖房装置
JP5556739B2 (ja) * 2011-05-17 2014-07-23 株式会社デンソー 磁気ヒートポンプ装置
EP2796811A1 (en) * 2013-04-24 2014-10-29 Technical University of Denmark Magnetocaloric heat pump device, a heating or cooling system and a magnetocaloric heat pump assembly
CN104613671B (zh) * 2015-03-02 2016-08-31 天津商业大学 圆柱型活性蓄冷器
JP7218988B2 (ja) * 2015-06-19 2023-02-07 マグネート ベー．フェー． パックスクリーン型磁気熱量素子

Patent Citations (42)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2898091A (en) * 1956-09-27 1959-08-04 Philips Corp Thermal regenerator
US4651808A (en) * 1985-03-13 1987-03-24 Aisin Seiki Kabushiki Kaisha Regenerator
US6022486A (en) * 1988-02-02 2000-02-08 Kabushiki Kaisha Toshiba Refrigerator comprising a refrigerant and heat regenerative material
US5332029A (en) * 1992-01-08 1994-07-26 Kabushiki Kaisha Toshiba Regenerator
US5429177A (en) * 1993-07-09 1995-07-04 Sierra Regenators, Inc. Foil regenerator
US5593517A (en) * 1993-09-17 1997-01-14 Kabushiki Kaisha Toshiba Regenerating material and refrigerator using the same
US5897963A (en) * 1995-01-10 1999-04-27 Composite Materials Technology, Inc. Composite wires and process of forming same
US6131644A (en) * 1998-03-31 2000-10-17 Advanced Mobile Telecommunication Technology Inc. Heat exchanger and method of producing the same
US6475935B1 (en) * 1999-07-09 2002-11-05 Irie Kouken Co., Ltd Regenerator and regenerative material used therein
US20010025494A1 (en) * 2000-03-24 2001-10-04 Kabushiki Kaisha Toshiba Regenerator and cold accumulation refrigerator using the same
US6680663B1 (en) * 2000-03-24 2004-01-20 Iowa State University Research Foundation, Inc. Permanent magnet structure for generation of magnetic fields
US20030051774A1 (en) * 2001-03-27 2003-03-20 Akiko Saito Magnetic material
US6854509B2 (en) * 2001-07-10 2005-02-15 Matthew P. Mitchell Foil structures for regenerators
US6595004B1 (en) * 2002-04-19 2003-07-22 International Business Machines Corporation Apparatus and methods for performing switching in magnetic refrigeration systems using thermoelectric switches
US6825681B2 (en) * 2002-07-19 2004-11-30 Delta Design, Inc. Thermal control of a DUT using a thermal control substrate
US6732785B2 (en) * 2002-09-20 2004-05-11 Matthew P. Mitchell Tab joint in etched foil regenerator
US20070144181A1 (en) * 2002-12-24 2007-06-28 Andrej Kitanovski Method and device for continuous generation of cold and heat by means of the magneto-calorific effect
US7168255B2 (en) * 2003-03-28 2007-01-30 Kabushiki Kaisha Toshiba Magnetic composite material and method for producing the same
US20050068140A1 (en) * 2003-09-29 2005-03-31 General Electric Company Permanent magnet assembly with movable permanent body for main magnetic field adjustable
US20050110602A1 (en) * 2003-11-22 2005-05-26 Bruker Biospin Gmbh Low resistance shield
US7148777B2 (en) * 2004-02-03 2006-12-12 Astronautics Corporation Of America Permanent magnet assembly
US20100107654A1 (en) * 2005-10-28 2010-05-06 Andrew Rowe Shimmed active magnetic regenerator for use in thermodynamic devices
US20070283994A1 (en) * 2006-06-12 2007-12-13 Texas Instruments, Inc. Novel solid state heat pump
US20080078184A1 (en) * 2006-09-28 2008-04-03 Kabushiki Kaisha Toshiba Magnetic refrigerating device and magnetic refrigerating method
US9175885B2 (en) * 2007-02-12 2015-11-03 Vacuumschmelze Gmbh & Co. Kg Article made of a granular magnetocalorically active material for heat exchange
US20100116471A1 (en) * 2007-12-27 2010-05-13 Georg Werner Reppel Composite article with magnetocalorically active material and method for its production
US20110048690A1 (en) * 2008-05-16 2011-03-03 Vacuumschmelze Gmbh & Co. Kg Article for Magnetic Heat Exchange and Method for Manufacturing an Article for Magnetic Heat Exchange
US20110173993A1 (en) * 2008-09-25 2011-07-21 Cooltech Applications S.A.S. Magnetocaloric element
US8537053B2 (en) * 2009-07-20 2013-09-17 Commissariat A L'energie Atomique Et Aux Energies Alternatives Left handed body, wave guide device and antenna using this body, manufacturing method for this body
US20110048031A1 (en) * 2009-08-28 2011-03-03 General Electric Company Magneto-caloric regenerator system and method
US20120031109A1 (en) * 2010-06-07 2012-02-09 Jan Vetrovec Magnetocaloric refrigerator
US20120031108A1 (en) * 2010-08-05 2012-02-09 Tadahiko Kobayashi Magnetic refrigerating device and magnetic refrigerating system
US20120073307A1 (en) * 2010-09-29 2012-03-29 Shiori Kaji Heat exchanger unit and thermal cycling unit
US20140113828A1 (en) * 2011-03-30 2014-04-24 Ambature Inc. Electrical, mechanical, computing/ and/or other devices formed of extremely low resistance materials
US20120272666A1 (en) * 2011-04-28 2012-11-01 Denso Corporation Magnetic heat pump system
US8991170B2 (en) * 2011-05-01 2015-03-31 Thomas Mallory Sherlock Solar air conditioning heat pump with minimized dead volume
US20140338365A1 (en) * 2011-09-14 2014-11-20 Nissan Motor Co., Ltd. Magnetic structure and magnetic air-conditioning and heating device using same
US20150033763A1 (en) * 2012-03-30 2015-02-05 Kabushiki Kaisha Toshiba Material for magnetic refrigeration and magnetic refrigeration device
US20170297760A1 (en) * 2014-09-23 2017-10-19 Tetra Laval Holdings & Finance S.A. Method and device for magnetising a package material, and packaging material magnetised with said method
US20180252445A1 (en) * 2016-03-31 2018-09-06 Fujikura Ltd. Heat exchanger and magnetic heat pump device
JP2018146154A (ja) * 2017-03-03 2018-09-20 株式会社フジクラ 熱交換器及び磁気ヒートポンプ装置
JP2019032145A (ja) * 2017-08-10 2019-02-28 株式会社フジクラ 熱交換器及び磁気ヒートポンプ装置

Also Published As

Publication number Publication date
EP3311081A1 (en) 2018-04-25
US11802720B2 (en) 2023-10-31
CN107735628B (zh) 2021-07-06
CN107735628A (zh) 2018-02-23
JP2022000892A (ja) 2022-01-04
EP3311081B1 (en) 2019-05-15
US20230046873A1 (en) 2023-02-16
JP2018526600A (ja) 2018-09-13
KR102522939B1 (ko) 2023-04-17
WO2016202663A1 (en) 2016-12-22
KR20180019676A (ko) 2018-02-26
JP7218988B2 (ja) 2023-02-07

Similar Documents

Publication Publication Date Title
US20230046873A1 (en) Packed-Screen Type Magnetocaloric Element
US10229775B2 (en) Magnetocaloric cascade and method for fabricating a magnetocaloric cascade
US20130319012A1 (en) Magnetic cooling device
WO2017036282A1 (zh) 一种用于循环冷却系统的风冷半导体制冷装置
CA2746204A1 (en) Cooling system of an electromagnet assembly
US9593894B2 (en) Thermal interface material and related systems and methods
US20170198976A1 (en) Heat exchangers
JP2018526600A5 (ko)
US11788805B2 (en) Self-regulating heat exchanger
US20150114600A1 (en) Heat-exchange apparatus
US20190049158A1 (en) Wire, heat exchanger, and magnetic heat pump device
JP5665005B2 (ja) 磁気冷暖房装置
JPWO2017171077A1 (ja) 熱交換器、及び磁気ヒートポンプ装置
Manglik et al. Resolving the energy–water nexus in large thermoelectric power plants: a case for application of enhanced heat transfer and high-performance thermal energy storage
CN105588228A (zh) 一种空调防水散热器及空调电器模块
JP2017096528A (ja) 熱交換器及び磁気ヒートポンプ装置
CN207407545U (zh) 磁制冷器件和包括其的磁制冷装置
CN202304567U (zh) 一种具有内置扰流片的换热器盘管
JP2011192756A (ja) 廃熱発電機能付き電子機器
Czernuszewicz et al. Balancing performance of active magnetic regenerators: a comprehensive experimental study of aspect ratio, particle size, and operating conditions
Lei et al. Modelling and comparison studies of packed screen regenerators for active magnetocaloric refrigeration
Khan et al. Evaluation of cooling capability of an eco-cooler: experimental and numerical analyses
CN208338194U (zh) 一种特异形状翅片搭配型led散热器
Borcuch et al. The analysis of heat exchangers geometry in thermoelectric generators for waste heat utilization
JP6235452B2 (ja) リアクトル

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

AS Assignment

Owner name: BASF SE, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SCHARF, FLORIAN;REEL/FRAME:047699/0567

Effective date: 20170210

Owner name: BASF NEDERLAND B.V., NETHERLANDS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ZHANG, LIAN;REESINK, BERNARD;VAN ASTEN, DAVID;SIGNING DATES FROM 20180502 TO 20180515;REEL/FRAME:047699/0531

AS Assignment

Owner name: BASF SE, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:BASF NEDERLAND B.V.;REEL/FRAME:047726/0885

Effective date: 20180614

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

AS Assignment

Owner name: MAGNETO B.V., NETHERLANDS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:BASF SE;REEL/FRAME:055751/0211

Effective date: 20210211

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE AFTER FINAL ACTION FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION