US20180141867A1 - Advanced fiber reinforced concrete mix designs - Google Patents

Advanced fiber reinforced concrete mix designs Download PDF

Info

Publication number
US20180141867A1
US20180141867A1 US15/573,678 US201515573678A US2018141867A1 US 20180141867 A1 US20180141867 A1 US 20180141867A1 US 201515573678 A US201515573678 A US 201515573678A US 2018141867 A1 US2018141867 A1 US 2018141867A1
Authority
US
United States
Prior art keywords
fibers
concrete mix
mpa
concrete
admixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/573,678
Other languages
English (en)
Inventor
Davide Zampini
Alexandre GUERINI
Giovanni VOLPATTI
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cemex Research Group AG
Original Assignee
Cemex Research Group AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cemex Research Group AG filed Critical Cemex Research Group AG
Assigned to CEMEX RESEARCH GROUP AG reassignment CEMEX RESEARCH GROUP AG ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: Guerini, Alexandre, Volpatti, Giovanni, ZAMPINI, DAVIDE
Publication of US20180141867A1 publication Critical patent/US20180141867A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B16/00—Use of organic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of organic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B16/04—Macromolecular compounds
    • C04B16/06—Macromolecular compounds fibrous
    • C04B16/0675—Macromolecular compounds fibrous from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B16/0691—Polyamides; Polyaramides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/02—Granular materials, e.g. microballoons
    • C04B14/04—Silica-rich materials; Silicates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/02—Granular materials, e.g. microballoons
    • C04B14/04—Silica-rich materials; Silicates
    • C04B14/06—Quartz; Sand
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/38—Fibrous materials; Whiskers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/38—Fibrous materials; Whiskers
    • C04B14/42—Glass
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/38—Fibrous materials; Whiskers
    • C04B14/48—Metal
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B16/00—Use of organic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of organic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B16/04—Macromolecular compounds
    • C04B16/06—Macromolecular compounds fibrous
    • C04B16/0616—Macromolecular compounds fibrous from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B16/0625—Polyalkenes, e.g. polyethylene
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B16/00—Use of organic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of organic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B16/04—Macromolecular compounds
    • C04B16/06—Macromolecular compounds fibrous
    • C04B16/0616—Macromolecular compounds fibrous from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B16/0625—Polyalkenes, e.g. polyethylene
    • C04B16/0633—Polypropylene
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
    • C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
    • C04B28/04—Portland cements
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/34—Non-shrinking or non-cracking materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2201/00—Mortars, concrete or artificial stone characterised by specific physical values
    • C04B2201/50—Mortars, concrete or artificial stone characterised by specific physical values for the mechanical strength
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
    • Y02W30/00—Technologies for solid waste management
    • Y02W30/50—Reuse, recycling or recovery technologies
    • Y02W30/91—Use of waste materials as fillers for mortars or concrete

Definitions

  • the present invention relates to concrete formulations for high mechanical performances in structural designs, fiber reinforcement special mix designs to limit or avoid steel rebars or pre-stressing. More specifically, the invention discloses concrete mix designs with high volumetric content of fibers and that the concrete contains different types of fibers to form a so-called hybrid fiber system.
  • Fiber reinforced concrete technology is known, it has been described in various National and International Norms e.g. RILEM 162 TDF International), Model Code 2010 (International), CNR DT 204 (Italy SS 812310 (Sweden), TR63 (UK) ACI 318 (USA) ACI 360 (USA), DBV (Germany), DAFSTB (Austria).
  • Fiber reinforced concrete mix designs containing different types of fibers have been for examples disclosed for example in WO 2011/053103 and more recently in CN102976697 and KR100940550. Such concrete are mainly used for pavement or deck repairs or to minimize the shrinkage of the concrete during hardening.
  • shrinkage reducing agents namely ethylene glycol, free lime or calcium sulfoaluminate, is used in combination with polymer fibers (synthetic fibers) whose role is mainly to reduce cracking due to shrinkage.
  • the workability of the concretes is located in the classes F5 to F6, yet no data are disclosed concerning the workability retention (opening time) of the final concrete produced. Furthermore, no data and results are disclosed concerning the compressive and flexural strength of the concretes according to the invention.
  • one important disadvantage of the patent application WO 2011/053103 is the requirement to prepare a separate slurry containing water, cement and all shrinkage reducers and plasticizers (or water reducers admixture—namely powdered melamine or phosphonates), or fillers as well as fillers.
  • the slurry is then added to the concrete prepared separately and the fibers are added.
  • a further important drawback of the invention according to WO 2011/053103 is the fact that the final placed concrete has to be cured using water after placing.
  • the present invention provides a concrete mix comprising sand, fine aggregates, binder, fibers, and various admixtures, having a consistency from S2 to SF3, a compressive strength in the range of 30-60 Mpa and a ductility represented by the following values:
  • fc compressive strength
  • ffl flexural strength
  • fR1 strength for crack mouth opening 0.5 mm
  • fR2 strength at CMOD 1.5 mm
  • fR3 is Strength at CMOD 2.5 mm.
  • the concrete mix of the invention is for slabs, floors or structural constructions with high ductility and workability retention.
  • the present invention proposes a solution to overcome the various drawbacks of WO 2011/053103.
  • the concrete mix designs according to the present invention are not limited to shrinkage resistance enhancement using shrinkage reducers and synthetic fibers for this unique goal and true structural properties to be used in structural engineering for decks, bridges, pillars, etc.
  • the fiber reinforced fresh concrete mix designs according to the invention are engineered to comply with industrial production requirements, they are produced in conventional concrete mixing plants, can be transported over large distance since they have a high workability retention and do not need special curing techniques once placed.
  • Another embodiment is the concrete mix of the invention, further comprising coarse aggregates.
  • Another embodiment is the concrete mix of the invention, wherein the dosing of the Admixture system I is of 0.5-5% weight percent with respect to the binder content and the dosing of the admixture system II is of 0.1-2% weight percent with respect to the binder.
  • This concrete mix is for high ductile thin slabs or floors with a consistency of S5-SF3.
  • Another embodiment is the concrete mix of the invention, wherein the dosing of the Admixture system I is of 0.1-1% weight percent with respect to the binder content and the dosing of the admixture system II is of 0.1-0.5% weight percent with respect to the binder.
  • This concrete mix is for high ductile this slabs or floors with a consistency of S2-S4.
  • the concrete mix of the invention comprises an admixture system III, wherein the third Admixture system III is obtained from a compound selected from the group consisting of cellulose microfibers, synthetic waxes, natural waxes, superabsorbing polymers, starch crosslinked polymers, acrylate crosslinked polymers, hexylene glycol (2-Methyl-2,4-pentanediol) and any combination thereof and the dosage of the admixture system III is of 0.3-6 weight percent with respect to the binder.
  • the third Admixture system III is obtained from a compound selected from the group consisting of cellulose microfibers, synthetic waxes, natural waxes, superabsorbing polymers, starch crosslinked polymers, acrylate crosslinked polymers, hexylene glycol (2-Methyl-2,4-pentanediol) and any combination thereof and the dosage of the admixture system III is of 0.3-6 weight percent with respect to the binder.
  • Another embodiment is the concrete mix of the invention, wherein fibers system C, comprising synthetic fibers, is added to the concrete mix.
  • Another embodiment is the concrete mix of the invention, wherein the dosage of fibers system C is of 0.02% to 2% volume with respect to the concrete.
  • Another embodiment is the concrete mix of the invention, wherein a part of the sand or the fine aggregates or the coarse aggregates are substituted by lightweight aggregates selected from the group consisting of expanded glass, expanded clay, pumice and expanded shale.
  • Another embodiment is the concrete mix of the invention, wherein the substitution rate for all aggregates (sand or/and fine or/and coarse aggregates) is at least 30% in volume.
  • the invention concerns special concrete mix designs to achieve any desired classes of compressive strength, while providing a high ductility and the fresh and hardened stages.
  • the ductility at hardened stages (28 days) is measured using flexural stress-strain measurement according to Norm EN 14561 (load increase needed to further opening the mouth size of the notch using a CMOD (Crack Mouth Opening Device)).
  • FIG. 1 shows typical such Load versus Crack Mouth Openings behaviors for different concretes.
  • Table 3 indicates the resistances and ductility values expressed by the strength at various CMOD with respect to norm EN 14 561.
  • the concrete mix designs according to the invention contain at least 2 Fibers Systems A and Fibers System B that in combination provides the targeted mechanical properties.
  • the Fibers System A contains only metallic fibers as described in Table 4:
  • the Fibers system A can be prepared with different types of metallic fibers corresponding to the characteristics indicated in Table 4.
  • the Fibers System B contains high strength fibers that are shorter than the Fibers of Fibers System A. and is described in table 5.
  • the Fibers System B can be made out of steels fibers, glass fibers, polyaramide (PA), carbon fibers and/or basalt fibers or any combination thereof.
  • PA polyaramide
  • the geometry of the none metallic fiber are normally straight whereas the metallic fibers in system B can be hooked end wire, straight slit sheet or wire, deformed slit sheet or wire, flattened-end slit sheet or wire, machined chip, melt extract, etc.
  • the metallic fibers can be made of amorphous metal.
  • the fibers in System A are used to bridge macro-cracks and provide ductility by pull-out whereas the B type fibers have mainly the function to bridge micro cracks and delay the micro-cracks propagation with energy dispersion on pull out and further micro-cracking.
  • the fibers in system A are hooked, with an ultimate resistance above 1100 MPa, preferably above 1300 MPa and even more preferably above 1500 MPa.
  • the ratio length divided by diameter is typically located between 40 and 100, preferably between 45 and 95.
  • the steel fibers in system B are hooked or straight with an ultimate resistance above 1100 MPa, preferably above 1500 MPa and even more preferably above 2000 MPa.
  • the ratio length divided by diameter is typically located between 50 and 95 preferably between 55 and 90.
  • the fibers system B may contain non-metallic fibers like glass fibers, with a minimum strength of 900 MPa, more preferably over 1000 MPa and a minimum length of 12 mm.
  • the fiber system B may also contain basalt fibers, preferably with a minimum strength of 2500 MPa and a minimum length of 12 mm. Both glass and basalt fibers used are straight.
  • a third synthetic fibers System C can be added to the concrete mix according to the invention, for instance acrylic fibers, polyethylene fibers, polypropylene fibers, polyester fibers to enhance properties like fire resistance or intrinsic shrinkage.
  • acrylic fibers for instance acrylic fibers, polyethylene fibers, polypropylene fibers, polyester fibers to enhance properties like fire resistance or intrinsic shrinkage.
  • cellulose fibers may be used in fibers system C.
  • the concrete is designed to allow achieving the targeted performances in terms of strength, ductility, elasticity Modulus, placement and rheological properties, workability retention, etc.
  • the targeted properties are not only achieved by selecting the appropriate fibers mix design.
  • the concrete formulation also plays an important role and is an integral part of the invention. The required ductility and mechanical properties are thus obtained by a combined effect of the concrete matrix and the special design of the hybrid fiber mix design.
  • the concrete according to the invention contains the following ingredients per cubic meter of produced concrete (Table 7).
  • % mass of total binder 0-40 By pass dust % mass of total binder 0-40 Total aggregates + sand kg/m3 1000-2000 Sand - 0/4 mm % volume of total 20-100 aggregates Aggregates - 4/8 mm or % volume of total 0-80 equivalent aggregates Aggregates >7-8 mm, % volume of total 0-50 less than 20 mm aggregates Water/total binder in kg/Kg 0.1-0.8 weight Air % volume of concrete 0.1-20 Volume of paste liters min 250 Volume of fibers System A % volume of concrete 0.03 to 4 Volume of fibers System B 0.03 to 3 Volume of fibers System C 0 to 2 PCE Admixtures systems dry solid content weight % 0.1 to 5 of the total binder Internal Curing admixture dry solid content weight % 0 to 3 system of the total binder
  • the cement is typically CEM I, II and III
  • the fly ash is a conventional fly ash
  • the sand is round or crushed sand, typically 0-4 mm and the fine or coarse aggregates are either round or crushed.
  • All ingredients of the final concrete are mixed using conventional industrial concrete mixers.
  • the mixing time is conventional for about 30 seconds to some minutes.
  • the concrete mix has the following values of mechanical properties:
  • the concrete mix of the invention contains:
  • a third optional third Fibers system C can be optionally used, whereas the fibers volume in Fibers system C ranges from 0 to 1.2 volume % of concrete.
  • the concrete mix of the invention has the following characteristics:
  • the concrete mix of the invention optionally comprises:
  • Fibers in System B contains either 100% volume metallic fibers or 100% none metallic fibers, or a mix of metallic and none metallic structural fibers.
  • the non-metallic fibers are glass fibers or basalt fibers or any mix thereof.
  • the concrete mix of the invention contains Fibers system C, a Fibers system A that is consisting of at least 2 different types of metallic fibers and a fibers system B that contains any mix or combination of high strength fibers metallic, organic, glass based, carbon based or basalt based.
  • Admixture System I Superplasticizing
  • This admixture system is a combination of at least two polycarboxylate ethers, with homo- or co-polymeric backbone, based on acrylic, methacrylic, maleic or allilic constitutional repeating units:
  • the dosage of the Admixture System I typically ranges from 0.05-5% solid content based on weight of total binder (total cement+total fly ash or slag+total silica fume) depending on the concrete placement properties targeted.
  • the ratio in weight (dry solid content) of the strong water reducer PCE and the workability retention PCE is typically located between 20:80 and 60:40 depending of the targeted application.
  • Admixture System II Stabilizing
  • the stabilizer is a solid, a water solution, emulsion or dispersion of compounds such as:
  • the dosage of the admixture system B is typically located between 0.05-2.5% solid content based on weight of binder (total cement+total fly ash or slag+total silica fume), depending on the segregation risk related to the fibers and the workability retention targeted.
  • the internal curing agent a solid, paste, a water solution, emulsion or dispersion of compounds such as:
  • the total dosage of the admixture system I and system II cannot exceed however the value of 5 weight % of the total binder.
  • the typical dosage of Admixture system III ranges from 0.05 to 6% solid content based on weight of binder depending on the conditions (size, temperature, relative humidity of the air, etc.).
  • the concrete mix of the invention may have a partial of full substitution of the sand and aggregates with lightweight sand and aggregates (expanded shale, expanded clay, expanded glass or pumice, natural puzzolans, etc.). This enables to obtain lightweight structural fiber reinforced concretes with densities below 1800 kg/m 3 , preferably below 1600 Kg/m 3 or even more preferably below 1400 kg/m 3 .
  • the concrete mix of the invention may contain strength development accelerators, to reach 4-6 MPa resistance after a couple of hours. This is important for post treatment of slabs (helicopter finishing for instance) that can be done a couple of hours after the casting of the slab, thus saving time and improving efficiency.
  • the concrete mix of the invention may also include a retarding agent for instance and sugar modified structures, vinasses, molasses, or chelating agents, etc.
  • the concrete mix of the invention may use an air entrainer (like surfactants, soaps or hydrophobic compounds) to ensure a trapped volume of air from 2% to 15% in volume of the final concrete for freeze-thaw resistance or fire resistance depending on the application.
  • an air entrainer like surfactants, soaps or hydrophobic compounds
  • the general admixture System consisting of the 3 Admixture Systems I, II and III not only enables to obtain a controlled workability over various classes (S1 to SF3), it also enables to perfectly disperse the high amount of fibers in the Fibers Systems A and B (and optionally in fibers System C) providing a very good stability of the fibers in the concrete matrix, avoiding 30 segregation of the fibers or bleeding of the none metallic fibers thanks to optimized mixing conditions. This explains why the concrete mix of the invention can be produced using conventional concrete mixing techniques.
  • the first advantage is that the combination of the concrete mix designs, the fiber mix designs (fibers systems A, B and optionally C) and admixtures systems (I, II and III) enables to overcome all the problems from the prior art and provide a wide range of consistencies, that can by managed and controlled by the 3 admixture systems I, II and II.
  • the invention provides concrete mixes having high volume of paste that can achieve very high shrinkage reducing and enables to cast very large slabs up to 3000 m 2 without the appearance of cracks due to elevated ductility and resistances without having to use synthetic fibers that are weakening the resistance of the matrix and limits the applications.
  • the combined usage of the high strength fibers system B and the admixture systems provides an optimum combination of shrinkage reduction and mechanical performances (compressive strength, flexural strength and ductility).
  • a further advantage of the invention is that the properties of the concrete paste, as the result of the combination of the paste content and the admixture systems, enable to use short (less than 40 mm) metallic fibers and/or high dosage of metallic fibers (over 70 Kg/m3 of concrete up to 165 kg/m3 of concrete) with no risks of segregation of without impacting the targeted consistency of the final concrete or the workability retention.
  • the concrete mix of the invention doesn't require special time consuming and costs ineffective curing actions, due to the presence when needed of the admixture system III, enabling self curing.
  • the concrete mix of the invention applies to wide range of construction elements, like slabs up to 3000 m2 without joints and without shrinkage cracks, floors, seismic applications, Insulated Concrete Frame for vertical walls, bridge segments, precast industry-tunnel lining segments, structural rehabilitation, etc.
  • the controlled rheology of the concrete mix of the invention enables building flat slabs or slabs with a designed slope.
  • the concrete mix of the invention has applications in large seamless thin slabs, floors and levels, bridges elements, concrete beams, concrete for impact resistance, seismic applications, etc.
  • the concrete mix of the invention do not require any particular mixing processes or sequences and can be obtained in any dry of wet concrete batching plant.
  • One further characteristic of the concrete mix of the invention is that it provides consistency up to the SF3 self placing and self leveling consistency classes in a controlled manner through a sophisticated overall system of admixtures, and do not require any specific curing protection (water spraying, surface covering, etc.).
  • the concrete mix of the invention has high opening times or workability retention (period of time from the initial mixing of the ingredients during which the workability expressed by the consistency classes of the concrete S1-S5 and SF1-SF3 for self placing concretes) of the concrete does change, and remains in the same consistency class.
  • the combination of the concrete mix design, the fibers mix design and the admixture system together enables to achieve the targeted improvements and properties.
  • the most common cement is the ordinary Portland cement (OPC) and a series of Portland cements blended with other cementitious materials. Ordinary Portland Hydraulic cement made from grinding clinker with gypsum. Portland cement cement contains calcium silicate, calcium aluminate and calcium ferroaluminate phases. These mineral phases react with water to produce strength.
  • Mineral Addition Mineral admixture including the following powders: silica fume, fly ash, slags) added to concrete to enhance fresh properties, compressive strength development and improve durability.
  • Total binder Is the sum of all cementitious components (cement, flay ash, slag, silica fume, etc.)
  • Volume of paste Is the total volume of the cement, + fly ash + slag + silica fume + water + entrained air
  • Fibers Material used to increase concrete's structural performance. Fibers include: steel fibers, glass fibers, synthetic fibers and natural fibers.
  • Natural Pozzolan Aluminosilicate material of volcanic origin that reacts with calcium hydroxide to produce calcium silicate hydrates or CSH as known in Portland cement hydration.
  • Inert Filler A material that does alter physical properties of concrete but does not take place in hydration reaction.
  • Admixture Chemical component in an admixture formulation system of one main raw material chemical polymer.
  • Admixture Chemical admixtures used to modify or improve concrete's properties in fresh and hardened state. These could be air entrainers, water reducers, set retarders, accelerators, stabilizers, superplasticizers and others.
  • PCE PCE are Polycarboxylic Acid Co-Polymers used as a class of cement and concrete admixtures, and are comb type polymers that are based on: a polymer backbone made of acrylic, methacrylic, maleic acid, and related monomers, which is grafted with polyoxyalkylene side-chain such as EO and/or PO.
  • the grafting could be, but is not limited to, ester, ether, amide or imide.
  • Initial dispersant is a chemical admixtures used in hydraulic cement compositions such as Portland cement concrete, part of the plasticizer and superplasticizer familiy, which allow a good dispersion of cement particles during the initial hydration stage.
  • Superplasticizers Superplasticizer relates to a class of chemical admixture used in hydraulic cement compositions such as Portland cement concrete having the ability to highly reduce the water demand while maintaining a good dispersion of cement particles. In particular, superplasticizers avoid particle aggregation and improve the rheological properties and workability of cement and concrete at the different stage of the hydration reaction. Concrete Concrete is primarily a combination of hydraulic binder, sand, fine and/or coarse aggregates, water.
  • Admixture can also be added to provide specific properties such as flow, lower water content, acceleration . . .
  • Pourable A material is consider as pourable as soon as its fluidity (with our without construction vibration) allow to full fill a formwork or to be collocate in a definite materials surface. Construction Any materials that can be use to build construction element or structure. It materials includes concrete, masonries (bricks-blocks), stone, ICF . . . Structural A construction material is consider as structural as soon as the applications compressive strength of the material is greater than 25 MPa Workability The workability of a material is measure with a slump test (table 1: slump) Workability Is the capability of a mix to maintain its workability during the time. The retention total time required depends on the application and the transportation.
  • FIG. 1 Flexural test results showing Crack Mouth Opening (CMOD) versus Strength according to EN 14651. This figure shows the values ffl, fR1 and fR3.
  • This other example uses only metallic fibers in Fiber system B.
  • This example shows an alternative according to the inventions with 2 different types of metallic fibers used in fibers system A and only steel fibers in Fibers system B.
  • This example uses only mineral fibers (basalt) in the Fibers system B.
  • This mix design according to the invention includes the Fiber system C with synthetic low resistance fibers (Polypropylene) specifically designed for fire resistance applications.
  • This final example shows an ultra high resistance concrete with very high ductility and full self placing consistency properties.
  • the mix design in example 8 combines 2 types of high strength fibers in the Fiber system a and 3 types of fibers (steel, glass and basalt) in the Fibers system B.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Civil Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Inorganic Chemistry (AREA)
  • Curing Cements, Concrete, And Artificial Stone (AREA)
  • Manufacture Of Alloys Or Alloy Compounds (AREA)
  • Environmental & Geological Engineering (AREA)
  • Preparation Of Clay, And Manufacture Of Mixtures Containing Clay Or Cement (AREA)
  • On-Site Construction Work That Accompanies The Preparation And Application Of Concrete (AREA)
  • Combustion & Propulsion (AREA)
US15/573,678 2015-06-11 2015-06-11 Advanced fiber reinforced concrete mix designs Abandoned US20180141867A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/EP2015/063045 WO2016198108A1 (en) 2015-06-11 2015-06-11 Advanced fiber reinforced concrete mix designs

Publications (1)

Publication Number Publication Date
US20180141867A1 true US20180141867A1 (en) 2018-05-24

Family

ID=53396486

Family Applications (3)

Application Number Title Priority Date Filing Date
US15/573,678 Abandoned US20180141867A1 (en) 2015-06-11 2015-06-11 Advanced fiber reinforced concrete mix designs
US15/573,389 Active US10259747B2 (en) 2015-06-11 2016-06-10 Advanced fiber reinforced concrete mix designs and admixtures systems
US15/573,391 Abandoned US20180134620A1 (en) 2015-06-11 2016-06-10 Concrete mix designs using a plurality of reinforcement fibers systems

Family Applications After (2)

Application Number Title Priority Date Filing Date
US15/573,389 Active US10259747B2 (en) 2015-06-11 2016-06-10 Advanced fiber reinforced concrete mix designs and admixtures systems
US15/573,391 Abandoned US20180134620A1 (en) 2015-06-11 2016-06-10 Concrete mix designs using a plurality of reinforcement fibers systems

Country Status (10)

Country Link
US (3) US20180141867A1 (es)
EP (3) EP3307690A1 (es)
BR (2) BR112017025418A2 (es)
CO (2) CO2017012578A2 (es)
CR (2) CR20170561A (es)
ES (1) ES2764135T3 (es)
IL (2) IL255597A (es)
MA (1) MA43201A (es)
MX (2) MX2017015570A (es)
WO (3) WO2016198108A1 (es)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11718561B2 (en) 2017-10-31 2023-08-08 Perma Edge Industries, LLC Composition and structures created therewith

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CR20170561A (es) * 2015-06-11 2018-07-24 Cemex Res Group Ag Diseños avanzados de mezcla de concreto reforzado con fibra y aditivos.
WO2017067872A1 (de) * 2015-10-21 2017-04-27 Sika Technology Ag Zusatzmittel für die interne nachbehandlung von mineralischen bindemittelzusammensetzungen
CA3040274A1 (en) * 2016-10-14 2018-04-19 Gcp Applied Technologies Inc. Controllable high flow concrete
JP7101312B2 (ja) * 2018-08-31 2022-07-14 中硼（厦▲門▼）医▲療▼器械有限公司 中性子捕捉療法システム
CN111714786A (zh) * 2019-03-18 2020-09-29 中硼(厦门)医疗器械有限公司 中子捕获治疗系统
CN111423192B (zh) * 2020-06-01 2020-12-01 中铁二局集团有限公司 一种改善高延性混凝土变形能力的方法
WO2022154794A1 (en) * 2021-01-15 2022-07-21 Skychase Holdings Corporation Lattice girder and method of concrete reinforcement
CN113111490B (zh) * 2021-03-12 2022-04-29 重庆交通大学 一种基于强度阈值的超高性能混凝土强度设计方法
CN113831071B (zh) * 2021-10-22 2022-10-21 福建省闽宏建材实业有限公司 一种耐久性混凝土
CN114853424B (zh) * 2022-05-24 2023-01-10 绍兴上虞南方普银混凝土有限公司 一种超缓凝耐久性混凝土及其制备工艺
CN114751706B (zh) * 2022-05-26 2022-11-29 浙大宁波理工学院 一种基于纳米材料的混凝土裂缝修补材料及其制备方法

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2804952B1 (fr) * 2000-02-11 2002-07-26 Rhodia Chimie Sa Composition de beton ultra haute performance resistant au feu
KR100940550B1 (ko) 2009-06-08 2010-02-10 (주)오래건설 하이브리드 섬유보강재를 이용한 콘크리트 구조물의 보강구조 및 공법
LV14122B (lv) * 2009-10-26 2010-04-20 Primeteh As Kompozītbetona sastāvs grīdas un pamatu plātņu ieklāšanai
CN102092996A (zh) * 2010-11-30 2011-06-15 南京理工大学 一种耐高温超高性能水泥基复合材料及其制备方法
CN102206068A (zh) * 2011-04-15 2011-10-05 上海交通大学 抗冲击碳纤维混杂纤维混凝土
CZ304478B6 (cs) * 2012-12-17 2014-05-21 ÄŚeskĂ© vysokĂ© uÄŤenĂ­ technickĂ© v Praze - fakulta stavebnĂ­ Drátkobeton ultravysokých pevností
CN102976697B (zh) * 2012-12-24 2014-07-02 武汉理工大学 用于桥面铺装的高韧性低收缩抗裂混凝土及其制备方法
CR20170561A (es) * 2015-06-11 2018-07-24 Cemex Res Group Ag Diseños avanzados de mezcla de concreto reforzado con fibra y aditivos.

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11718561B2 (en) 2017-10-31 2023-08-08 Perma Edge Industries, LLC Composition and structures created therewith

Also Published As

Publication number Publication date
WO2016198603A1 (en) 2016-12-15
BR112017025418A2 (pt) 2018-08-07
US20180111876A1 (en) 2018-04-26
EP3307692B1 (en) 2019-10-09
MX2017015570A (es) 2018-04-26
EP3307692A1 (en) 2018-04-18
CR20170560A (es) 2018-07-24
MX2017015680A (es) 2018-04-18
US20180134620A1 (en) 2018-05-17
BR112017026256A2 (pt) 2018-09-11
EP3307690A1 (en) 2018-04-18
IL255597A (en) 2018-01-31
CR20170561A (es) 2018-07-24
IL255598B (en) 2020-07-30
MA43201A (fr) 2018-09-19
CO2017012578A2 (es) 2018-02-28
EP3307691A1 (en) 2018-04-18
ES2764135T3 (es) 2020-06-02
CO2017012589A2 (es) 2018-02-28
WO2016198108A1 (en) 2016-12-15
US10259747B2 (en) 2019-04-16
IL255598A (en) 2018-01-31
WO2016198608A1 (en) 2016-12-15

Similar Documents

Publication Publication Date Title
US10259747B2 (en) Advanced fiber reinforced concrete mix designs and admixtures systems
Djelloul et al. Performance of self-compacting concrete made with coarse and fine recycled concrete aggregates and ground granulated blast-furnace slag
JP4558569B2 (ja) 超高強度繊維補強セメント組成物、超高強度繊維補強モルタル又はコンクリート、並びに超高強度セメント混和材
Shannag High strength concrete containing natural pozzolan and silica fume
US20070125273A1 (en) Lightweight concrete mix and method of using same
JP5713540B2 (ja) 超高強度繊維補強モルタルの吹付け工法及びモルタル硬化体
JP5165873B2 (ja) 鉄筋継手用充填材を用いた鉄筋継手充填施工方法
JP6550241B2 (ja) 超速硬型高靱性繊維補強コンクリート
JP4709677B2 (ja) プレミクス高靭性ポリマーセメントモルタル材料及び高靭性ポリマーセメントモルタル
JP7395633B2 (ja) ポリマーセメントモルタル
KR20060123031A (ko) 시멘트 혼화재, 시멘트 조성물, 모르타르 및 콘크리트
JP6964548B2 (ja) モルタル組成物及びその製造方法、並びに、コンクリート構造物の補修・補強方法
JP5533967B2 (ja) 水硬性組成物、水硬性組成物の使用方法、水硬性モルタルの製造方法、及び水硬性モルタル硬化体の製造方法
JP7085050B1 (ja) セメント混和材、急硬モルタルコンクリート材料、急硬モルタルコンクリート組成物、及び硬化体
JP2006045054A (ja) 耐硫酸塩モルタル又はコンクリート
JP4809575B2 (ja) 土木構造物用セメント組成物及びこれを用いたコンクリート製品
JP2581803B2 (ja) セメント混和材及びセメント組成物
JP3672518B2 (ja) セメント混和材、セメント組成物及びそれを用いたコンクリート
JP5574758B2 (ja) セメント含有粉体組成物、及び水硬性組成物
JP6985177B2 (ja) 水硬性組成物及びコンクリート
JP5399969B2 (ja) 膨張コンクリートのスランプロス低減方法
JP2007270470A (ja) コンクリート構造体の補修・補強工法
JPH0834652A (ja) コンクリート組成物及びコンクリート
JP6998811B2 (ja) モルタル組成物、吹付け工法、及び、硬化物の製造方法
hamid El Semary et al. Effect of using green building masonary mortar on the behaviour of masonary walls

Legal Events

Date Code Title Description
AS Assignment

Owner name: CEMEX RESEARCH GROUP AG, SWITZERLAND

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ZAMPINI, DAVIDE;GUERINI, ALEXANDRE;VOLPATTI, GIOVANNI;REEL/FRAME:044377/0215

Effective date: 20171206

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION