US20180104793A1 - Vitreous bond abrasive articles and methods of making the same - Google Patents

Vitreous bond abrasive articles and methods of making the same Download PDF

Info

Publication number
US20180104793A1
US20180104793A1 US15/573,326 US201615573326A US2018104793A1 US 20180104793 A1 US20180104793 A1 US 20180104793A1 US 201615573326 A US201615573326 A US 201615573326A US 2018104793 A1 US2018104793 A1 US 2018104793A1
Authority
US
United States
Prior art keywords
abrasive
particles
vitreous bond
abrasive article
precursor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/573,326
Other languages
English (en)
Inventor
Carsten Franke
Robert L.W. Smithson
Brian D. Goers
Negus B. Adefris
Maiken Givot
Thomas J. Anderson
Steven J. Keipert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to US15/573,326 priority Critical patent/US20180104793A1/en
Assigned to 3M INNOVATIVE PROPERTIES COMPANY reassignment 3M INNOVATIVE PROPERTIES COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: FRANKE, CARSTEN, GIVOT, MAIKEN, SMITHSON, ROBERT L.W., ADEFRIS, NEGUS B., ANDERSON, THOMAS J., GOERS, BRIAN D., KEIPERT, STEVEN J.
Publication of US20180104793A1 publication Critical patent/US20180104793A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D5/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor
    • B24D5/02—Wheels in one piece
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D11/00—Constructional features of flexible abrasive materials; Special features in the manufacture of such materials
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D11/00—Constructional features of flexible abrasive materials; Special features in the manufacture of such materials
    • B24D11/04—Zonally-graded surfaces
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D18/00—Manufacture of grinding tools or other grinding devices, e.g. wheels, not otherwise provided for
    • B24D18/0009—Manufacture of grinding tools or other grinding devices, e.g. wheels, not otherwise provided for using moulds or presses
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
    • B24D3/02—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent
    • B24D3/04—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic
    • B24D3/06—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic metallic or mixture of metals with ceramic materials, e.g. hard metals, "cermets", cements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
    • B24D3/02—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent
    • B24D3/04—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic
    • B24D3/14—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic ceramic, i.e. vitrified bondings
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D5/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor
    • B24D5/10—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor with cooling provisions, e.g. with radial slots
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D5/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor
    • B24D5/14—Zonally-graded wheels; Composite wheels comprising different abrasives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D7/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting otherwise than only by their periphery, e.g. by the front face; Bushings or mountings therefor
    • B24D7/02—Wheels in one piece
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D7/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting otherwise than only by their periphery, e.g. by the front face; Bushings or mountings therefor
    • B24D7/10—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting otherwise than only by their periphery, e.g. by the front face; Bushings or mountings therefor with cooling provisions
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D7/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting otherwise than only by their periphery, e.g. by the front face; Bushings or mountings therefor
    • B24D7/14—Zonally-graded wheels; Composite wheels comprising different abrasives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D2203/00—Tool surfaces formed with a pattern
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/165—Processes of additive manufacturing using a combination of solid and fluid materials, e.g. a powder selectively bound by a liquid binder, catalyst, inhibitor or energy absorber

Definitions

  • the present disclosure broadly relates to methods of making abrasive articles having abrasive particles in a vitreous bonding matrix, and methods of making them.
  • vitrified bond abrasive articles e.g., abrasive wheels, abrasive segments, and whetstones
  • abrasive particles e.g., diamond, cubic boron nitride, alumina, or SiC
  • a vitreous bond precursor e.g., glass frit, ceramic precursor
  • an optional pore inducer e.g., glass bubbles, naphthalene, crushed coconut or walnut shells, or acrylic glass or PMMA
  • a temporary organic binder in a liquid vehicle e.g., aqueous solutions of phenolic resin, polyvinyl alcohol, urea-formaldehyde resin, or dextrin.
  • vitreous bond precursor The abrasive particles, vitreous bond precursor, and usually the pore inducer are typically dry blended together.
  • the temporary organic binder solution is then added to wet out the grain mix.
  • the blended mix is then placed in a hardened steel mold treated with a mold release, and then heated until the vitreous bond precursor is converted into a vitreous bond matrix (also referred to in the art as “vitreous bond” and “vitreous binder”.
  • each abrasive article shape requires a specialized mold; the molds typically are expensive and have a long lead time to make; any design change requires the manufacture of a new mold; there are limitations to the shapes that can be molded, complicated shapes with undercuts or internal structures such as cooling channels are generally not possible; molds wear out and have a limited number of units that can be manufactured per mold; while the molds are filled with the abrasive mixture, separation of the components can occur, leading to inhomogeneous abrasive components and density variation, which is easily visible. Moreover, the process is manual and labor intensive.
  • Powder bed binder jetting is an additive manufacturing, or “3D printing” technology, in which a thin layer of a powder is temporarily bonded at desired locations by a jetted liquid binder mixture.
  • that binder mixture is dispensed by an inkjet printing head, and consists of a polymer dissolved in a suitable solvent or carrier solution.
  • the binder is a powder which is mixed with the other powder, or coated onto the powder and dried, and then an activating liquid, such as water or a solvent mixture, is jetted onto the powder, activating the binder in select areas.
  • the printed powder layer is then at least partially dried and lowered so that a next powder layer can be spread.
  • the powder spreading, bonding and drying processes can be repeated until the full object is created.
  • the object and surrounding powder is removed from the printer and often dried or cured to impart additional strength so that the now hardened object can be extracted from the surrounding powder.
  • the present disclosure provides a method of making a vitreous bond abrasive article, the method comprising sequential steps:
  • methods according to the present disclosure are suitable for making vitreous bond abrasive articles, either in large volume or short run production.
  • the present disclosure provides a vitreous bond abrasive article comprising a vitreous bond material having abrasive particles retained therein, wherein the vitreous bond abrasive article has at least one tortuous cooling channel extending at least partially therethrough.
  • the present disclosure provides a vitreous bond abrasive article comprising a vitreous bond material having abrasive particles retained therein, wherein the vitreous bond abrasive article has at least one arcuate cooling channel extending at least partially therethrough.
  • the present disclosure provides a vitreous bond abrasive article precursor comprising abrasive particles bonded together by a vitreous bond precursor material, wherein the vitreous bond abrasive article precursor further comprises at least one of:
  • the present disclosure provides a unitary structured abrasive disc comprising:
  • precisely-shaped ceramic abrasive elements extending from the working major surface, wherein the precisely-shaped ceramic abrasive elements and the planar ceramic base form a unitary body.
  • the present disclosure provides a unitary structured abrasive disc according to the nineteenth embodiment, wherein the precisely-shaped abrasive elements are curved around a common rotational axis.
  • vitrreous bond includes inorganic ceramics, glasses, and glass-ceramics.
  • FIG. 1 is a schematic process flow diagram of a method of making a vitreous bond abrasive article according to the present disclosure.
  • FIG. 2 is a schematic cross-sectional top view of an exemplary vitreous bond abrasive wheel 200 , preparable according to the present disclosure.
  • FIG. 3 is a schematic cross-sectional top view of an exemplary vitreous bond abrasive wheel 300 , preparable according to the present disclosure.
  • FIG. 4 is a schematic perspective view of an exemplary vitreous bond abrasive segment 400 , preparable according to the present disclosure.
  • FIG. 5 is a schematic perspective view of a vitreous bond abrasive wheel 500 , preparable according to the present disclosure.
  • FIG. 6A is a schematic perspective view of a unitary structured abrasive disc 600 , preparable according to the present disclosure.
  • FIG. 6B is a schematic top view of unitary structured abrasive disc 600 .
  • FIG. 7A is a schematic perspective view of a unitary structured abrasive disc 700 , preparable according to the present disclosure.
  • FIG. 7B is a schematic top view of unitary structured abrasive disc 700 .
  • FIG. 8 is a schematic perspective view of rotary abrasive tool 800 , preparable according to the present disclosure.
  • Methods of making vitreous bond abrasive articles according to the present disclosure include a common additive subprocess.
  • the subprocess comprises sequentially, preferably consecutively (although not required) carrying out at least three steps.
  • FIG. 1 schematically depicts an exemplary powder bed jetting process 100 used in making a vitreous bond abrasive article.
  • a layer 138 of loose powder particles 110 is deposited in a confined region 140 .
  • the layer 138 should be of substantially uniform thickness.
  • the thickness of the layer may vary less than 50 microns, preferably less than 30 microns, and more preferably less than 10 microns.
  • the layers may have any thickness up to about 1 millimeter, as long as the jetted liquid binder precursor material can bind all the loose powder where it is applied.
  • the thickness of the layer is from about 10 microns to about 500 microns, 10 microns to about 250 microns, more preferably about 50 microns to about 250 microns, and more preferably from about 100 microns to about 200 microns.
  • the loose powder particles comprise vitreous bond precursor particles and abrasive particles.
  • the vitreous bond precursor particles may comprise particles of any material that can be thermally converted into a vitreous material. Examples include glass frit particles, ceramic particles, ceramic precursor particles, and combinations thereof.
  • the vitreous bond which binds together the abrasive grain in accordance with this disclosure can be of any suitable composition which is known in the abrasives art, for example.
  • the vitreous bond phase also variously known in the art as a “ceramic bond”, “vitreous phase”, vitreous matrix”, or “glass bond” (e.g., depending on the composition) may be produced from one or more oxide (e.g., a metal oxide and/or boria) and/or at least one silicate as frit (i.e., small particles), which upon being heated to a high temperature react to form an integral vitreous bond phase.
  • oxide e.g., a metal oxide and/or boria
  • silicate as frit i.e., small particles
  • glass particles e.g., recycled glass frit, water glass frit
  • silica frit e.g., sol-gel silica frit
  • alumina trihydrate particles e.g., alumina particles, zirconia particles, and combinations thereof.
  • Suitable frits, their sources and compositions are well known in the art.
  • Abrasive articles are typically prepared by forming a green structure comprised of abrasive grain, the vitreous bond precursor, an optional pore former, and a temporary binder. The green structure is then fired.
  • the vitreous bond phase is usually produced in the firing step of the process for producing the abrasive article of this disclosure. Typical firing temperatures are in the range of from 540° C. to 1700° C. (1000° F. to 3100° F.). It should be understood that the temperature selected for the firing step and the composition of the vitreous bond phase must be chosen so as to not have a detrimental effect on the physical properties and/or composition of abrasive particles contained in the vitreous bond abrasive article.
  • Useful glass frit particles may include any glass frit material known for use in vitreous bond abrasive articles. Examples include glass frit selected from the group consisting of silica glass frit, silicate glass frit, borosilicate glass frit, and combinations thereof.
  • a typical vitreous binding material contains about 70-90% SiO 2 +B 2 O 3 , 1-20% alkali oxides, 1-20% alkaline earth oxides, and 1-20% transition metal oxides.
  • the vitreous binding material has a composition of about 82 wt % SiO 2 +B 2 O 3 , 5% alkali metal oxide, 5% transition series metal oxide, 4% Al 2 O 3 , and 4% alkaline earth oxide.
  • a frit having about 20% B 2 O 3 , 60% silica, 2% soda, and 4% magnesia may be utilized as the vitreous binding material.
  • a frit having about 20% B 2 O 3 , 60% silica, 2% soda, and 4% magnesia may be utilized as the vitreous binding material.
  • the particular components and the amounts of those components can be chosen in part to provide particular properties of the final abrasive article formed from the composition.
  • the size of the glass frit can vary. For example, it may be the same size as the abrasive particles, or different. Typically, the average particle size of the glass frit ranges from about 0.01 micrometer to about 100 micrometers, preferably about 0.05 micrometer to about 50 micrometers, and most preferably about 0.1 micrometer to about 25 micrometers. The average particle size of the glass frit in relation to the average particle size of the abrasive particles having a Mohs hardness of at least about 5 can vary. Typically, the average particle size of the glass frit is about 1 to about 200 percent of the average particle size of the abrasive, preferably about 10 to about 100 percent, and most preferably about 15 to about 50 percent.
  • the weight ratio of vitreous bond precursor particles to abrasive particles in the loose powder particles ranges from about 10:90 to about 90:10.
  • the shape of the vitreous bond precursor particles can also vary. Typically, they are irregular in shape (e.g., crushed and optionally graded), although this is not a requirement. For example, they may be spheroidal, cubic, or some other predetermined shape.
  • the coefficient of thermal expansion of the vitreous bond precursor particles is the same or substantially the same as that of the abrasive particles.
  • One preferred vitreous bond has an oxide-based mole percent (%) composition of SiO 2 63.28; TiO 2 0.32; Al 2 O 3 10.99; B 2 O 3 5.11; Fe 2 O 3 0.13; K 2 O 3.81; Na 2 O 4.20; Li 2 O 4.98; CaO 3.88; MgO 3.04 and BaO 0.26. Firing of these ingredients is typically accomplished by raising the temperature from room temperature to 1149° C. (2100° F.) over a prolonged period of time (e.g., about 25-26 hours), holding at the maximum temperature (e.g., for several hours), and then cooling the fired article to room temperature over an extended period of time (e.g., 25-30 hours).
  • the vitreous bond precursor particles may comprise ceramic particles. In such cases sintering and/or fusing of the ceramic particles forms the vitreous matrix. Any sinterable and/or fusible ceramic material may be used. Preferred ceramic materials include alumina, zirconia, and combinations thereof.
  • alpha-alumina ceramic particles may be modified with oxides of metals such as magnesium, nickel, zinc, yttria, rare earth oxides, zirconia, hafnium, chromium, or the like.
  • Alumina and zirconia abrasive particles may be made by a sol-gel process, for example, as disclosed in U.S. Pat. No. 4,314,827 (Leitheiser et al.); U.S. Pat. No. 4,518,397 (Leitheiser et al.); U.S. Pat. No. 4,574,003 (Gerk); U.S. Pat. No. 4,623,364 (Cottringer et al.); U.S. Pat. No. 4,744,802 (Schwabel); and U.S. Pat. No. 5,551,963 (Larmie).
  • the vitreous bond precursor particles may be present in an amount from 10 to 40 volume percent of the combined volume of the vitreous bond precursor particles and abrasive particles, preferably from 15 to 35 volume percent of the abrasive composition.
  • additives in the making of vitreous bonded abrasive articles both to assist in the making of the abrasive article and/or improve the performance of such articles.
  • Such conventional additives which may also be used in the practice of this disclosure include but are not limited to lubricants, fillers, pore inducers, and processing aids.
  • lubricants include, graphite, sulfur, polytetrafluoroethylene and molybdenum disulfide.
  • pore inducers include glass bubbles and organic particles. Concentrations of the additives as are known in the art may be employed for the intended purpose of the additive, for example. Preferably, the additives have little or no adverse effect on abrasive particles employed in the practice of this disclosure.
  • the loose powder particles may optionally be modified to improve their flowability and the uniformity of the layer spread.
  • Methods of improving the powders include agglomeration, spray drying, gas or water atomization, flame forming, granulation, milling, and sieving. Additionally, flow agents such as, for example, fumed silica, nanosilica, stearates, and starch may optionally be added.
  • the vitreous bond precursor particles may comprise a ceramic precursor (e.g., a precursor of alumina or zirconia) such as, for example, bauxite, boehmite, calcined alumina, or calcined zirconia that when fired converts to the corresponding ceramic form.
  • a ceramic precursor e.g., a precursor of alumina or zirconia
  • bauxite, boehmite calcined alumina, or calcined zirconia that when fired converts to the corresponding ceramic form.
  • Procedures and conditions known in the art for producing vitreous bonded abrasive articles e.g., grinding wheels
  • procedures and conditions for producing vitreous bond abrasive articles may be used to make the abrasive articles of this disclosure. These procedures may employ conventional and well known equipment in the art.
  • the abrasive particles may comprise any abrasive particle used in the abrasives industry.
  • the abrasive particles have a Mohs hardness of at least 4, preferably at least 5, more preferably at least 6, more preferably at least 7, more preferably at least 8, more preferably at least 8.5, and more preferably at least 9.
  • the abrasive particles comprise superabrasive particles.
  • the term “superabrasive” refers to any abrasive particle having a hardness greater than or equal to that of silicon carbide (e.g., silicon carbide, boron carbide, cubic boron nitride, and diamond).
  • suitable abrasive materials include aluminum oxide (e.g., alpha alumina) materials (e.g., fused, heat-treated, ceramic, and/or sintered aluminum oxide materials), silicon carbide, titanium diboride, titanium nitride, boron carbide, tungsten carbide, titanium carbide, aluminum nitride, diamond, cubic boron nitride (CBN), garnet, fused alumina-zirconia, sol-gel derived abrasive particles, cerium oxide, zirconium oxide, titanium oxide, and combinations thereof. Examples of sol-gel derived abrasive particles can be found in U.S. Pat. No. 4,314,827 (Leitheiser et al.), U.S.
  • sol-gel derived abrasive particles can be found in U.S. Pat. No. 4,314,827 (Leitheiser et al.), U.S.
  • the loose powder particles are preferably sized (e.g., by screening) to have a maximum size of less than or equal to 400 microns, preferably less than or equal to 250 microns, more preferably less than or equal to 200 microns, more preferably less than or equal to 150 microns, less than or equal to 100 microns, or even less than or equal to 80 microns, although larger sizes may also be used.
  • the vitreous bond precursor particles, abrasive particles, and any optional additional particulate components may have the same or different maximum particle sizes, D 90 , D 50 , and/or D 10 particle size distribution parameters.
  • the loose powder particles may optionally further comprise other components such as, for example, pore inducers, and/or filler particles.
  • pore inducers include glass bubbles and organic particles.
  • a liquid binder precursor material 170 is jetted by printer 150 onto predetermined region(s) 180 of layer 138 .
  • the liquid binder precursor material thus coats the loose powder particles in region 180 , and is subsequently converted to a binder material that binds the loose powder particles in region 180 to each other.
  • the liquid binder precursor material may be any composition that can be converted (e.g., by evaporation, or thermal, chemical, and/or radiation curing (e.g., using UV or visible light)) into a binder material that bonds the loose powder particles together according to the jetted pattern (and ultimate 3-D shape upon multiple repetitions).
  • the liquid binder precursor material comprises a liquid vehicle having a polymer dissolved therein.
  • the liquid may include one or more of organic solvent and water.
  • organic solvents include alcohols (e.g., butanol, ethylene glycol monomethyl ether), ketones, and ethers, preferably having a flash point above 100° C.
  • a suitable solvent or solvents will typically depend upon requirements of the specific application, such as desired surface tension and viscosity, the selected particulate solid, for example.
  • the liquid vehicle can be entirely water, or can contain water in combination with one or more organic solvents.
  • the aqueous vehicle contains, on a total weight basis, at least 20 percent water, at least 30 percent water, at least 40 percent water, at least 50 percent water, or even at least 75 percent water.
  • one or more organic solvents may be included in the liquid vehicle, for instance, to control drying speed of the liquid vehicle, to control surface tension of the liquid vehicle, to allow dissolution of an ingredient (e.g., of a surfactant), or, as a minor component of any of the ingredients; e.g., an organic co-solvent may be present in a surfactant added as an ingredient to the liquid vehicle.
  • an ingredient e.g., of a surfactant
  • an organic co-solvent may be present in a surfactant added as an ingredient to the liquid vehicle.
  • Exemplary organic solvents include: alcohols such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, t-butyl alcohol, and isobutyl alcohol; ketones or ketoalcohols such as acetone, methyl ethyl ketone, and diacetone alcohol; esters such as ethyl acetate and ethyl lactate; polyhydric alcohols such as ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, butylene glycol, 1,4-butanediol, 1,2,4-butanetriol, 1,5-pentanediol, 1,2,6-hexanetriol, hexylene glycol, glycerol, glycerol ethoxylate, trimethylolpropane ethoxylate; lower alkyl ethers such as ethylene glycol methyl or ethyl
  • the amounts of organic solvent and/or water within the liquid vehicle can depend on a number of factors, such as the particularly desired properties of the liquid binder precursor material such as the viscosity, surface tension, and/or drying rate, which can in turn depend on factors such as the type of ink jet printing technology intended to be used with the liquid vehicle ink, such as piezo-type or thermal-type printheads, for example.
  • the liquid binder precursor material may include a polymer that is soluble or dispersible in the liquid vehicle.
  • suitable polymers may include polyvinyl pyrrolidones, polyvinyl caprolactams, polyvinyl alcohols, polyacrylamides, poly(2-ethyl-2-oxazoline) (PEOX), polyvinyl butyrate, copolymers of methyl vinyl ether and maleic anhydride, certain copolymers of acrylic acid and/or hydroxyethyl acrylate, methyl cellulose, natural polymers (e.g., dextrin, guar gum, xanthan gum).
  • PEOX poly(2-ethyl-2-oxazoline)
  • polyvinyl butyrate copolymers of methyl vinyl ether and maleic anhydride
  • acrylic acid and/or hydroxyethyl acrylate methyl cellulose
  • natural polymers e.g., dextrin, guar gum, xanthan gum.
  • the liquid binder precursor material may include one or more free-radically polymerizable or otherwise radiation-curable materials; for example, acrylic monomers and/or oligomers and/or epoxy resins.
  • An effective amount of photoinitiator and/or photocatalysts for curing the free-radically polymerizable or otherwise radiation-curable materials may also be included.
  • suitable (meth)acrylate monomers and oligomers and otherwise radiation-curable materials e.g., epoxy resins
  • suitable (meth)acrylate monomers and oligomers and otherwise radiation-curable materials can be found in, for example, U.S. Pat. No. 5,766,277 (DeVoe et al.).
  • the liquid binder precursor material is essentially free of (e.g., contains less than 1 percent, less than 0.1 percent, less than 0.01 percent, or is even free of) metal nanoparticles and/or metal oxide nanoparticles.
  • nanoparticles refers to particles having an average particle diameter of less than or equal to one micron; for example less than or equal to 500 nanometers (nm), or even less than or equal to 150 nm.
  • the liquid binder precursor may be an aqueous sol comprising a ceramic precursor for alumina and/or zirconia.
  • aqueous boehmite sols and zirconia sols examples include aqueous boehmite sols and zirconia sols.
  • the liquid binder precursor may have the same or different composition as the abrasive particles. Details concerning zirconia sols can be found, for example, in U.S. Pat. No. 6,376,590 (Kolb et al.). Details concerning boehmite sols can be found, for example, in U.S. Pat. No. 4,314,827 (Leitheiser et al.), U.S. Pat. No. 5,178,849 (Bauer) U.S. Pat.
  • the jetted liquid binder precursor material is converted into a binder material that bonds together the loose powder particles in predetermined regions of the loose powder particles to form a layer of bonded powder particles; for example, by evaporation of a liquid vehicle in the liquid binder precursor material.
  • heating the binder material to sufficiently high temperature causes it to volatilize and/or decompose (e.g., “burn out”) during a subsequent firing step. Cooling may be accomplished by any means known to the art (e.g., cold quenching or air cooling to room temperature).
  • the jetted liquid binder precursor material 170 is converted (step 190 ) into a binder material that bonds together the loose powder particles in at least one predetermined region of the loose powder particles to form a layer of bonded powder particles; for example, by evaporation of a liquid vehicle in the liquid binder precursor material.
  • heating the binder material to sufficiently high temperature causes it to volatilize and/or decompose (e.g., “burn out”) during subsequent sintering or infusion steps.
  • step 185 The above steps are then repeated (step 185 ) with changes to the region where jetting is carried out according to a predetermined design resulting through repetition, layer on layer, in a three-dimensional (3-D) abrasive article preform.
  • the loose powder particles and the liquid binder precursor material may be independently selected; that is, either or both or the loose powder particles and the liquid binder precursor material may be the same as, or different from those in adjacent deposited layers.
  • the abrasive article preform comprises the bonded powder particles and remaining loose powder particles. Once sufficient repetitions have been carried out to form the abrasive article preform, it is preferably separated from substantially all (e.g., at least 85 percent, at least 90 percent, preferably at least 95 percent, and more preferably at least 99 percent) of the remaining loose powder particles, although this is not a requirement.
  • multiple particle reservoirs each containing a different powder may be used.
  • multiple different liquid binder precursor materials may be used, either through a common printhead or, preferably, through separate printheads. This results in different powders/binders distributed in different and discrete regions of the vitrified bond abrasive article.
  • relatively inexpensive, but lower performing abrasive particles and or vitreous bond precursor particles may be relegated to regions of the vitrified bond abrasive article where it is not particularly important to have high performance properties (e.g., in the interior away from the abrading surface).
  • vitreous bond abrasive articles made in such ways have considerable porosity throughout their volumes. Accordingly, the abrasive article preform may then be infused with a solution or dispersion of additional vitreous bond precursor material, or grain growth modifiers.
  • Powder bed jetting equipment suitable for practicing the present disclosure is commercially available, for example, from ExOne, North Huntington, Pa. Further details concerning powder bed jetting techniques suitable for practicing the present disclosure can be found, for example, in U.S. Pat. No. 5,340,656 (Sachs et al.) and U.S. Pat. No. 6,403,002 B1 (van der Geest).
  • cooling channels having tortuous and or arcuate paths can be readily manufactured using methods of the present disclosure. Cooling channels are open to the exterior of the vitreous bond abrasive article. In some embodiments, they have a single opening, but more typically they have two or more openings.
  • a cooling medium e.g., air, water or oil
  • exemplary vitreous bond abrasive wheel 200 has arcuate and tortuous cooling channels 210 , respectively.
  • FIG. 3 shows another exemplary vitreous bond abrasive wheel 300 that has tortuous cooling channels 320 .
  • Vitreous bond abrasive articles preparable according to methods of the present disclosure include essentially any known vitreous bond abrasive article; for example, unitary structured abrasive discs, grinding bits, abrasive segments, shaped abrasive particles (e.g., triangular abrasive particles), and abrasive wheels as well as many hitherto unknown vitreous bond abrasive articles.
  • FIG. 4 shows an exemplary vitreous bond abrasive segment 400 .
  • multiple vitreous bond abrasive segments 400 are mounted evenly spaced along the circumference of a metal disc to form an abrasive wheel.
  • FIG. 5 shows a vitreous bond abrasive disc 500 has two regions 510 , 520 . Each region has abrasive particles 530 , 540 retained in a vitreous bond matrix material 550 , 560 , respectively.
  • FIGS. 6A-6B and 7A-7B respectively show various unitary structured abrasive discs with precisely-shaped ceramic abrasive elements 610 , 710 formed integrally with ceramic planar bases 620 , 720 .
  • FIG. 8 shows a rotary abrasive tool 800 (a bit for a handheld motor driven shaft such as, for example, a Dremel tool).
  • vitreous abrasive wheels shown in FIGS. 2 and 3 can be prepared by firing corresponding green bodies (i.e., having the same general shape features, but comprising a vitreous bond precursor particles held together by a temporary binder).
  • the present disclosure provides a method of making a vitreous bond abrasive article, the method comprising sequential steps:
  • the present disclosure provides a method according to the first embodiment, wherein the abrasive particles comprise at least one of diamond particles or cubic boron nitride particles.
  • the present disclosure provides a method according to the first or second embodiment, wherein the abrasive particles comprise metal oxide ceramic particles.
  • the present disclosure provides a method according to any one of the first to third embodiments, wherein the abrasive particles and the vitreous bond material have the same chemical composition.
  • the present disclosure provides a method according to any one of the first to fourth embodiments, wherein the vitreous bond abrasive article includes at least one cooling channel
  • the present disclosure provides a method according to any one of the first to fifth embodiments, wherein the vitreous bond abrasive article is selected from the group consisting of an unitary structured abrasive disc, an abrasive grinding bit, abrasive segments, and an abrasive wheel.
  • the present disclosure provides a method according to any one of the first to sixth embodiments, wherein the liquid binder precursor material comprises a liquid vehicle having a polymer dissolved and/or dispersed therein.
  • the present disclosure provides a method according to any one of the first to seventh embodiments, wherein the liquid binder precursor material comprises a liquid vehicle having an inorganic vitreous bond precursor dissolved and/or dispersed therein.
  • the present disclosure provides a method according to the eighth embodiment, wherein the inorganic vitreous bond precursor comprises a precursor of alpha alumina.
  • the present disclosure provides a method according to the eighth or ninth embodiment, wherein the loose powder particles comprise submicron ceramic particles.
  • the present disclosure provides a method according to any one of the first to tenth embodiments, wherein the loose powder particles further comprise flow agent particles.
  • step d) further comprises burning out the temporary binder material.
  • the present disclosure provides a vitreous bond abrasive article comprising a vitreous bond material having abrasive particles retained therein, wherein the vitreous bond abrasive article has at least one tortuous cooling channel extending at least partially therethrough.
  • the present disclosure provides vitreous bond abrasive article comprising a vitreous bond material having abrasive particles retained therein, wherein the vitreous bond abrasive article has at least one arcuate cooling channel extending at least partially therethrough.
  • the present disclosure provides a vitreous bond abrasive article according to the thirteenth or fourteenth embodiment, wherein the abrasive particles comprise first abrasive particles and second abrasive particles, wherein the first abrasive particles and second abrasive particles are disposed in predetermined different regions within the vitreous bond abrasive article.
  • the present disclosure provides a vitreous bond abrasive article according to the fifteenth embodiment, wherein the different regions are layers.
  • the present disclosure provides a vitreous bond abrasive article according to any one of the thirteenth to sixteenth embodiments, wherein the abrasive particles comprise at least one of diamond particles or cubic boron nitride particles.
  • the present disclosure provides a vitreous bond abrasive article according to any one of the thirteenth to seventeenth embodiments, wherein the abrasive particles comprise at least one of silicon carbide, boron carbide, silicon nitride, or metal oxide ceramic particles.
  • the present disclosure provides a vitreous bond abrasive article precursor according to any one of the thirteenth to eighteenth embodiments, wherein the vitreous bond abrasive article is selected from the group consisting of a unitary structured abrasive disc, an abrasive grinding bit, an abrasive segment, and an abrasive wheel.
  • the present disclosure provides a vitreous bond abrasive article precursor comprising abrasive particles bonded together by a vitreous bond precursor material, wherein the vitreous bond abrasive article precursor further comprises at least one of:
  • the present disclosure provides a vitreous bond abrasive precursor according to the twentieth embodiment, wherein the abrasive particles comprise at least one of silicon carbide, boron carbide, silicon nitride, or metal oxide ceramic particles.
  • the present disclosure provides a unitary structured abrasive disc comprising:
  • precisely-shaped ceramic abrasive elements extending from the working major surface, wherein the precisely-shaped ceramic abrasive elements and the planar ceramic base form a unitary body.
  • the present disclosure provides a unitary structured abrasive disc according to the twenty-second embodiment, wherein the precisely-shaped abrasive elements are curved around a common rotational axis.
  • the present disclosure provides a unitary structured abrasive disc according to the twenty-third or twenty-fourth embodiment, wherein the precisely-shaped ceramic abrasive elements are curved.
  • Abrasive particles were agglomerated with the binder matrix PDR3 to form agglomerates (AG1 or AG2, respectively) with sizes that ranged from 5 micrometers to 45 micrometers using a spray drying atomization method described as follows. A mixture containing the following components was blended with the help of a laboratory ultrasonic bath: 123.0 grams (g) of a 25 wt.
  • % aqueous dextrin solution 100.0 g of PDR3, 90.0 g of PDR5 (to make AG1) or PDR8 (to make AG2), 295.0 g of distilled water, 1.9 g of N-octadecyl sulfosuccinamate (obtained as CYANASOL AY from American Cyanamid Co., Wayne, N.J.).
  • the mixture was then atomized in a centrifugal atomizer (Mobile Minor from Niro Inc., Columbia, Md.).
  • the atomization wheel was running at 20000 rpm. Air supplied at 200° C. into the atomization chamber was used to dry the particles as they formed into droplets. The particles were then collected using a cyclone equipped with the atomizer and sieved through a 45 micrometer sieve to remove the coarser particles.
  • a print material was prepared by mixing, based on the mixture weight, 80 wt. % of PDR1 and 20 wt. % of PDR3.
  • the print material was filled into the build box of an X1-LAB 3D printer, obtained from The ExOne Company, North Huntingdon, Pa.
  • the binder supply bottle of the printer was filled with BIN.
  • the printed object and the powder bed were extracted from the printer and placed into an ambient atmosphere oven to cure for 2 hours at 195° C. After cooling down to 23° C., the printed object was removed from the powder bed and loose powder was removed using a soft bristle brush. The object was then placed into a furnace and burned out at 400° C. for 2 hours, followed by sintering at 700° C. for 4 hours, resulting in an abrasive bit suitable for use with a handheld rotary tool device (e.g., Dremel rotary tool for Robert Bosch Tool Corp., Mount Prospect, Ill.).
  • a handheld rotary tool device e.g., Dremel rotary tool for Robert Bosch Tool Corp., Mount Prospect, Ill.
  • a print material was prepared by mixing, based on the mixture weight, 80 wt. % of AG2 and 20 wt. % of PDR3. The procedure described in Example 4 was repeated, except that the furnace sintering temperature was set at 630° C. for 4 hours.
  • vitreous bond abrasive articles from Examples 1 to 5 were evaluated for abrasive performance against a variety of materials, such as aluminum, a microscopy glass slide, and a piece of wood.
  • rotary tools were assembled on a mandrel and tested with a Dremel handheld rotary tool. All the objects were effective for abrading the materials.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Ceramic Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Polishing Bodies And Polishing Tools (AREA)
US15/573,326 2015-06-25 2016-06-23 Vitreous bond abrasive articles and methods of making the same Abandoned US20180104793A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US15/573,326 US20180104793A1 (en) 2015-06-25 2016-06-23 Vitreous bond abrasive articles and methods of making the same

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201562184695P 2015-06-25 2015-06-25
PCT/US2016/038902 WO2016210057A1 (en) 2015-06-25 2016-06-23 Vitreous bond abrasive articles and methods of making the same
US15/573,326 US20180104793A1 (en) 2015-06-25 2016-06-23 Vitreous bond abrasive articles and methods of making the same

Publications (1)

Publication Number Publication Date
US20180104793A1 true US20180104793A1 (en) 2018-04-19

Family

ID=57586429

Family Applications (1)

Application Number Title Priority Date Filing Date
US15/573,326 Abandoned US20180104793A1 (en) 2015-06-25 2016-06-23 Vitreous bond abrasive articles and methods of making the same

Country Status (5)

Country Link
US (1) US20180104793A1 (de)
EP (1) EP3313614A4 (de)
JP (1) JP7458693B2 (de)
CN (1) CN107787264B (de)
WO (1) WO2016210057A1 (de)

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20180022025A1 (en) * 2015-04-30 2018-01-25 Hewlett-Packard Development Company, L.P. Three-dimensional (3d) printing
US10087099B2 (en) * 2015-07-28 2018-10-02 Il Metronic Sensortechnik Gmbh Method for producing blanks for sintered glass bodies for glass seals
WO2020123203A1 (en) * 2018-12-12 2020-06-18 Corning Incorporated Grinding wheels and methods of producing the same
WO2020128779A2 (en) 2018-12-18 2020-06-25 3M Innovative Properties Company Bonded abrasive articles and methods of manufacture
US10730109B2 (en) * 2016-04-11 2020-08-04 Stratasys Ltd. Method and apparatus for additive manufacturing with powder material
US10906237B2 (en) * 2017-12-19 2021-02-02 Seiko Epson Corporation Production method of three-dimensionally shaped object
US10994333B2 (en) 2014-05-08 2021-05-04 Stratasys Ltd. Method and apparatus for 3D printing by selective sintering
WO2021171141A1 (en) 2020-02-25 2021-09-02 3M Innovative Properties Company Bonded abrasive articles and methods of manufacture
CN113910116A (zh) * 2021-10-29 2022-01-11 江西冠亿研磨股份有限公司 一种陶瓷砂轮成型用可溶性无机液体粘结剂制备方法
US11358254B2 (en) * 2016-04-13 2022-06-14 3M Innovative Properties Company Abrasive article
US11400516B2 (en) 2017-03-20 2022-08-02 Stratasys Ltd. Method and system for additive manufacturing with powder material
US11404180B2 (en) * 2017-10-09 2022-08-02 Ut-Battelle, Llc Method for producing collimators and other components from neutron absorbing materials using additive manufacturing
US11440831B2 (en) 2018-12-13 2022-09-13 Corning Incorporated Conveying apparatus and conveying ribbon
WO2023280872A1 (en) 2021-07-05 2023-01-12 Admatec Europe B.V. Additive manufacturing method and apparatus for abrasive articles
WO2023130088A1 (en) * 2021-12-30 2023-07-06 Saint-Gobain Abrasives, Inc. Abrasive articles and methods for forming same

Families Citing this family (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013102177A1 (en) 2011-12-30 2013-07-04 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle and method of forming same
PL2797716T3 (pl) 2011-12-30 2021-07-05 Saint-Gobain Ceramics & Plastics, Inc. Kompozytowe ukształtowane cząstki ścierne i sposób ich formowania
CA2987793C (en) 2012-01-10 2019-11-05 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
WO2013106602A1 (en) 2012-01-10 2013-07-18 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
KR102197361B1 (ko) 2012-05-23 2021-01-05 생-고뱅 세라믹스 앤드 플라스틱스, 인코포레이티드 형상화 연마입자들 및 이의 형성방법
IN2015DN00343A (de) 2012-06-29 2015-06-12 Saint Gobain Ceramics
WO2014062701A1 (en) 2012-10-15 2014-04-24 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
KR101818946B1 (ko) 2012-12-31 2018-01-17 생-고뱅 세라믹스 앤드 플라스틱스, 인코포레이티드 미립자 소재 및 이의 형성방법
EP4364891A2 (de) 2013-03-29 2024-05-08 Saint-Gobain Abrasives, Inc. Schleifpartikel mit besonderen formen und verfahren zur formung solcher partikel
AU2014324453B2 (en) 2013-09-30 2017-08-03 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
JP6290428B2 (ja) 2013-12-31 2018-03-07 サンーゴバン アブレイシブズ，インコーポレイティド 成形研磨粒子を含む研磨物品
US9771507B2 (en) 2014-01-31 2017-09-26 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle including dopant material and method of forming same
US10557067B2 (en) 2014-04-14 2020-02-11 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
KR101884178B1 (ko) 2014-04-14 2018-08-02 생-고뱅 세라믹스 앤드 플라스틱스, 인코포레이티드 형상화 연마 입자들을 포함하는 연마 물품
WO2015184355A1 (en) 2014-05-30 2015-12-03 Saint-Gobain Abrasives, Inc. Method of using an abrasive article including shaped abrasive particles
US9707529B2 (en) 2014-12-23 2017-07-18 Saint-Gobain Ceramics & Plastics, Inc. Composite shaped abrasive particles and method of forming same
US9914864B2 (en) 2014-12-23 2018-03-13 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US9676981B2 (en) 2014-12-24 2017-06-13 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle fractions and method of forming same
WO2016161157A1 (en) 2015-03-31 2016-10-06 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
TWI634200B (zh) 2015-03-31 2018-09-01 聖高拜磨料有限公司 固定磨料物品及其形成方法
PL3307483T3 (pl) 2015-06-11 2020-11-16 Saint-Gobain Ceramics&Plastics, Inc. Wyrób ścierny zawierający ukształtowane cząstki ścierne
WO2016209696A1 (en) 2015-06-25 2016-12-29 3M Innovative Properties Company Methods of making metal bond abrasive articles and metal bond abrasive articles
US11072053B2 (en) 2016-01-21 2021-07-27 3M Innovative Properties Company Methods of making metal bond and vitreous bond abrasive articles, and abrasive article precursors
US11072115B2 (en) 2016-03-30 2021-07-27 3M Innovative Properties Company Methods of making metal bond and vitreous bond abrasive articles, and abrasive article precursors
EP3231558B1 (de) 2016-04-11 2020-02-05 3M Innovative Properties Company Ein grünkörper, eine schleifscheibe und ein verfahren zur herstellung mindestens eines grünkörpers
WO2017197002A1 (en) 2016-05-10 2017-11-16 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same
SI3455321T1 (sl) 2016-05-10 2022-10-28 Saint-Gobain Ceramics & Plastics, Inc. Metode oblikovanja abrazivnih delcev
EP4349896A2 (de) 2016-09-29 2024-04-10 Saint-Gobain Abrasives, Inc. Feste schleifartikel und verfahren zur formung davon
CN108015906A (zh) 2016-10-28 2018-05-11 圣戈班磨料磨具有限公司 空芯钻头及其制造方法
KR102458318B1 (ko) * 2016-12-23 2022-10-24 쓰리엠 이노베이티브 프로퍼티즈 캄파니 중합체 접합제 연마 물품 및 그의 제조 방법
US10759024B2 (en) 2017-01-31 2020-09-01 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US10563105B2 (en) 2017-01-31 2020-02-18 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
EP3589450A4 (de) 2017-02-28 2021-04-07 3M Innovative Properties Company Metallbindungsschleifartikel und verfahren zur herstellung von metallbindungsschleifartikeln
EP3642293A4 (de) 2017-06-21 2021-03-17 Saint-Gobain Ceramics&Plastics, Inc. Teilchenförmige materialien und verfahren zur herstellung davon
DE102019207822A1 (de) * 2019-05-28 2020-12-03 Robert Bosch Gmbh Verfahren zur Herstellung eines Schleifartikels sowie Schleifartikel
WO2021009673A1 (en) 2019-07-15 2021-01-21 3M Innovative Properties Company Abrasive articles having internal coolant features and methods of manufacturing the same
KR20220116556A (ko) 2019-12-27 2022-08-23 세인트-고바인 세라믹스 앤드 플라스틱스, 인크. 연마 물품 및 이의 형성 방법
CN116745069A (zh) 2020-10-28 2023-09-12 3M创新有限公司 用于向主动磨削区域提供冷却剂的系统和方法

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5876268A (en) * 1997-01-03 1999-03-02 Minnesota Mining And Manufacturing Company Method and article for the production of optical quality surfaces on glass
WO2000000344A1 (en) * 1998-06-30 2000-01-06 Trustees Of Tufts College Multiple-material prototyping by ultrasonic adhesion
US6258137B1 (en) * 1992-02-05 2001-07-10 Saint-Gobain Industrial Ceramics, Inc. CMP products
US20050077226A1 (en) * 2003-10-14 2005-04-14 Bishop Bruce A. Membrane devices using reaction bonded monolith supports
US6945857B1 (en) * 2004-07-08 2005-09-20 Applied Materials, Inc. Polishing pad conditioner and methods of manufacture and recycling
US20050233678A1 (en) * 2004-04-20 2005-10-20 3M Innovative Properties Company Abrasive articles, and methods of making and using the same
WO2006073486A1 (en) * 2005-01-05 2006-07-13 D-M-E Company Method and tool for molding
US20060185256A1 (en) * 2005-02-22 2006-08-24 Saint-Gobain Abrasives, Inc. Rapid tooling system and methods for manufacturing abrasive articles
US20060185255A1 (en) * 2005-02-22 2006-08-24 Saint-Gobain Abrasives, Inc. Rapid tooling system and methods for manufacturing abrasive articles
US20060185257A1 (en) * 2005-02-22 2006-08-24 Saint-Gobain Abrasives, Inc. Rapid tooling system and methods for manufacturing abrasive articles
US20060185225A1 (en) * 2005-02-22 2006-08-24 Lewis Leonard T Fuels comprising hydrophobic starch and methods of fueling an enginge
US20060199013A1 (en) * 2005-03-07 2006-09-07 Malshe Ajay P Nanoparticle compositions, coatings and articles made therefrom, methods of making and using said compositions, coatings and articles
US8828411B2 (en) * 2004-11-26 2014-09-09 Aprecia Pharmaceuticals Company Dosage forms and methods of use thereof

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3850590A (en) * 1970-09-28 1974-11-26 Impregnated Diamond Prod Ltd An abrasive tool comprising a continuous porous matrix of sintered metal infiltrated by a continuous synthetic resin
JPS5148831B2 (de) * 1972-11-28 1976-12-23
US5178644A (en) * 1992-01-23 1993-01-12 Cincinnati Milacron Inc. Method for making vitreous bonded abrasive article and article made by the method
CA2142636C (en) * 1994-02-18 2005-09-20 Salvatore Caldarise Implantable articles with as-cast macrotextured surface regions and method of manufacturing the same
KR19990081117A (ko) * 1998-04-25 1999-11-15 윤종용 씨엠피 패드 컨디셔닝 디스크 및 컨디셔너, 그 디스크의 제조방법, 재생방법 및 세정방법
AU755858B2 (en) 1999-01-12 2003-01-02 Therics, Inc. Method and apparatus for managing and/or utilizing data received from a CAD model
US6123744A (en) * 1999-06-02 2000-09-26 Milacron Inc. Vitreous bond compositions for abrasive articles
EP1226019B1 (de) * 1999-11-05 2004-03-03 Z Corporation Verfahren für dreidimensionales drucken
JP3679013B2 (ja) * 2001-02-07 2005-08-03 株式会社ノリタケカンパニーリミテド ビトリファイド砥石の製造方法
US6797023B2 (en) * 2002-05-14 2004-09-28 Saint-Gobain Abrasives Technology Company Coated abrasives
DE102006015014B4 (de) * 2006-03-31 2008-07-24 Uibel, Krishna, Dipl.-Ing. Verfahren zur Herstellung dreidimensionaler keramischer Formkörper
WO2007114895A2 (en) * 2006-04-06 2007-10-11 Z Corporation Production of three-dimensional objects by use of electromagnetic radiation
KR20090013366A (ko) * 2007-08-01 2009-02-05 주식회사 세라코리 연마패드용 컨디셔닝 디스크
JP5675767B2 (ja) 2009-03-24 2015-02-25 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ 熱交換器のための熱磁気成形体を製造するための印刷方法
CN201419362Y (zh) * 2009-06-16 2010-03-10 河南富耐克超硬材料有限公司 一种复合磨料磨盘
CN102612734A (zh) * 2009-09-01 2012-07-25 圣戈班磨料磨具有限公司 化学机械抛光修整器
BR112012012238A2 (pt) 2009-12-02 2016-04-19 Saint Gobain Abrasifs Sa artigo abrasivo; e método para a formação de um artigo abrasivo
JP6000342B2 (ja) 2011-06-01 2016-09-28 バム ブンデサンスタルト フィア マテリアルフォルシュングウント−プリュフング 成形体の製造方法、および装置
KR102002194B1 (ko) * 2011-09-07 2019-07-19 쓰리엠 이노베이티브 프로퍼티즈 컴파니 접합된 연마 용품
JP6474346B2 (ja) * 2012-08-02 2019-02-27 スリーエム イノベイティブ プロパティズ カンパニー 精密に成形された形成部を有する研磨要素前駆体及びその作製方法
JP6550335B2 (ja) * 2012-10-31 2019-07-24 スリーエム イノベイティブ プロパティズ カンパニー 成形研磨材粒子、その製造方法、及びそれを含む研磨材物品

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6258137B1 (en) * 1992-02-05 2001-07-10 Saint-Gobain Industrial Ceramics, Inc. CMP products
US5876268A (en) * 1997-01-03 1999-03-02 Minnesota Mining And Manufacturing Company Method and article for the production of optical quality surfaces on glass
WO2000000344A1 (en) * 1998-06-30 2000-01-06 Trustees Of Tufts College Multiple-material prototyping by ultrasonic adhesion
US20050077226A1 (en) * 2003-10-14 2005-04-14 Bishop Bruce A. Membrane devices using reaction bonded monolith supports
US20050233678A1 (en) * 2004-04-20 2005-10-20 3M Innovative Properties Company Abrasive articles, and methods of making and using the same
US6945857B1 (en) * 2004-07-08 2005-09-20 Applied Materials, Inc. Polishing pad conditioner and methods of manufacture and recycling
US8828411B2 (en) * 2004-11-26 2014-09-09 Aprecia Pharmaceuticals Company Dosage forms and methods of use thereof
WO2006073486A1 (en) * 2005-01-05 2006-07-13 D-M-E Company Method and tool for molding
US20060185255A1 (en) * 2005-02-22 2006-08-24 Saint-Gobain Abrasives, Inc. Rapid tooling system and methods for manufacturing abrasive articles
US20060185257A1 (en) * 2005-02-22 2006-08-24 Saint-Gobain Abrasives, Inc. Rapid tooling system and methods for manufacturing abrasive articles
US20060185225A1 (en) * 2005-02-22 2006-08-24 Lewis Leonard T Fuels comprising hydrophobic starch and methods of fueling an enginge
US20060185256A1 (en) * 2005-02-22 2006-08-24 Saint-Gobain Abrasives, Inc. Rapid tooling system and methods for manufacturing abrasive articles
US20060199013A1 (en) * 2005-03-07 2006-09-07 Malshe Ajay P Nanoparticle compositions, coatings and articles made therefrom, methods of making and using said compositions, coatings and articles

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10994333B2 (en) 2014-05-08 2021-05-04 Stratasys Ltd. Method and apparatus for 3D printing by selective sintering
US10576685B2 (en) * 2015-04-30 2020-03-03 Hewlett-Packard Development Company, L.P. Three-dimensional (3D) printing
US20180022025A1 (en) * 2015-04-30 2018-01-25 Hewlett-Packard Development Company, L.P. Three-dimensional (3d) printing
US10087099B2 (en) * 2015-07-28 2018-10-02 Il Metronic Sensortechnik Gmbh Method for producing blanks for sintered glass bodies for glass seals
US11980941B2 (en) 2016-04-11 2024-05-14 Stratasys Ltd. Method and apparatus for additive manufacturing with powder material
US11691196B2 (en) 2016-04-11 2023-07-04 Stratasys Ltd. Method and apparatus for additive manufacturing with powder material
US10730109B2 (en) * 2016-04-11 2020-08-04 Stratasys Ltd. Method and apparatus for additive manufacturing with powder material
US11059100B2 (en) 2016-04-11 2021-07-13 Stratasys Ltd. Method and apparatus for additive manufacturing with powder material
US11358254B2 (en) * 2016-04-13 2022-06-14 3M Innovative Properties Company Abrasive article
US11400516B2 (en) 2017-03-20 2022-08-02 Stratasys Ltd. Method and system for additive manufacturing with powder material
US11404180B2 (en) * 2017-10-09 2022-08-02 Ut-Battelle, Llc Method for producing collimators and other components from neutron absorbing materials using additive manufacturing
US10906237B2 (en) * 2017-12-19 2021-02-02 Seiko Epson Corporation Production method of three-dimensionally shaped object
WO2020123203A1 (en) * 2018-12-12 2020-06-18 Corning Incorporated Grinding wheels and methods of producing the same
US11739020B2 (en) 2018-12-13 2023-08-29 Corning Incorporated Conveying apparatus and methods for conveying ribbon
US11440831B2 (en) 2018-12-13 2022-09-13 Corning Incorporated Conveying apparatus and conveying ribbon
WO2020128779A2 (en) 2018-12-18 2020-06-25 3M Innovative Properties Company Bonded abrasive articles and methods of manufacture
WO2021171141A1 (en) 2020-02-25 2021-09-02 3M Innovative Properties Company Bonded abrasive articles and methods of manufacture
WO2023280872A1 (en) 2021-07-05 2023-01-12 Admatec Europe B.V. Additive manufacturing method and apparatus for abrasive articles
CN113910116A (zh) * 2021-10-29 2022-01-11 江西冠亿研磨股份有限公司 一种陶瓷砂轮成型用可溶性无机液体粘结剂制备方法
WO2023130088A1 (en) * 2021-12-30 2023-07-06 Saint-Gobain Abrasives, Inc. Abrasive articles and methods for forming same

Also Published As

Publication number Publication date
JP7458693B2 (ja) 2024-04-01
WO2016210057A1 (en) 2016-12-29
CN107787264B (zh) 2020-10-13
EP3313614A1 (de) 2018-05-02
JP2018522746A (ja) 2018-08-16
CN107787264A (zh) 2018-03-09
EP3313614A4 (de) 2019-05-15

Similar Documents

Publication Publication Date Title
US20180104793A1 (en) Vitreous bond abrasive articles and methods of making the same
US11597058B2 (en) Methods of making metal bond abrasive articles and metal bond abrasive articles
JP6960373B2 (ja) 成形研磨材粒子、その製造方法、及びそれを含む研磨材物品
EP3405309B1 (de) Verfahren zur herstellung von metall- und glasbond-schleifartikeln
EP1337597B1 (de) Sprühtrocknungsverfahren zur herstellung von schleifkornagglomeraten und schleifgegenständen
US20230219195A1 (en) Polymer bond abrasive articles and methods of making them
KR102354617B1 (ko) 접합된 연마 용품 및 제조 방법
WO2021001730A1 (en) Methods of making metal bond abrasive articles and metal bond abrasive articles
US20240001511A1 (en) Systems and methods for providing coolant to an active grinding area
US20220266421A1 (en) Abrasive articles having internal coolant features and methods of manufacturing the same

Legal Events

Date Code Title Description
AS Assignment

Owner name: 3M INNOVATIVE PROPERTIES COMPANY, MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FRANKE, CARSTEN;SMITHSON, ROBERT L.W.;GOERS, BRIAN D.;AND OTHERS;SIGNING DATES FROM 20171023 TO 20171027;REEL/FRAME:044093/0311

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE AFTER FINAL ACTION FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STCV Information on status: appeal procedure

Free format text: APPEAL BRIEF (OR SUPPLEMENTAL BRIEF) ENTERED AND FORWARDED TO EXAMINER

STCV Information on status: appeal procedure

Free format text: APPEAL BRIEF (OR SUPPLEMENTAL BRIEF) ENTERED AND FORWARDED TO EXAMINER

STCV Information on status: appeal procedure

Free format text: EXAMINER'S ANSWER TO APPEAL BRIEF MAILED

STCV Information on status: appeal procedure

Free format text: ON APPEAL -- AWAITING DECISION BY THE BOARD OF APPEALS

STCV Information on status: appeal procedure

Free format text: BOARD OF APPEALS DECISION RENDERED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION