US20130243643A1 - Aluminum alloy having improved oxidation resistance, corrosion resistance, or fatigue resistance, and die-cast material and extruded material prepared by using the aluminum alloy - Google Patents

Aluminum alloy having improved oxidation resistance, corrosion resistance, or fatigue resistance, and die-cast material and extruded material prepared by using the aluminum alloy Download PDF

Info

Publication number
US20130243643A1
US20130243643A1 US13/880,724 US201113880724A US2013243643A1 US 20130243643 A1 US20130243643 A1 US 20130243643A1 US 201113880724 A US201113880724 A US 201113880724A US 2013243643 A1 US2013243643 A1 US 2013243643A1
Authority
US
United States
Prior art keywords
alloy
molten
based compound
compound
prepared
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/880,724
Other languages
English (en)
Inventor
Se-Kwang KIM
Young-Ok YOON
Jin-Kyu Lee
Jeong-ho Seo
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Korea Institute of Industrial Technology KITECH
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Assigned to KOREA INSTITUTE OF INDUSTRIAL TECHNOLOGY reassignment KOREA INSTITUTE OF INDUSTRIAL TECHNOLOGY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KIM, SE-KWANG, LEE, JIN-KYU, SEO, JEONG-HO, YOON, YOUNG-OK
Publication of US20130243643A1 publication Critical patent/US20130243643A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C1/00—Making non-ferrous alloys
    • C22C1/02—Making non-ferrous alloys by melting
    • C22C1/026—Alloys based on aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21C—MANUFACTURE OF METAL SHEETS, WIRE, RODS, TUBES OR PROFILES, OTHERWISE THAN BY ROLLING; AUXILIARY OPERATIONS USED IN CONNECTION WITH METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL
    • B21C23/00—Extruding metal; Impact extrusion
    • B21C23/002—Extruding materials of special alloys so far as the composition of the alloy requires or permits special extruding methods of sequences
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D21/00—Casting non-ferrous metals or metallic compounds so far as their metallurgical properties are of importance for the casting procedure; Selection of compositions therefor
    • B22D21/02—Casting exceedingly oxidisable non-ferrous metals, e.g. in inert atmosphere
    • B22D21/04—Casting aluminium or magnesium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C1/00—Making non-ferrous alloys
    • C22C1/02—Making non-ferrous alloys by melting
    • C22C1/03—Making non-ferrous alloys by melting using master alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C23/00—Alloys based on magnesium
    • C22C23/02—Alloys based on magnesium with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C22F1/047—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys with magnesium as the next major constituent

Definitions

  • the present invention relates to an aluminum (Al) alloy, and more particularly, to an Al alloy having improved oxidation resistance, corrosion resistance, or fatigue resistance, and a die-cast material and an extruded material prepared by using the alloy.
  • magnesium (Mg) is regarded as one of main alloying elements in an aluminum (Al) alloy. Addition of Mg allows an Al alloy to have a high strength, to be favorable to surface treatment, and to have improved corrosion resistance.
  • Mg due to Mg having a chemically high oxidizing potential, an oxide or another inclusion may be mixed into molten Al during Mg is alloyed into the molten Al and thus the quality of molten metal may deteriorate.
  • the surface of molten metal may be covered with a protective gas such as SF 6 when Mg is added.
  • the present invention provides an aluminum (Al) alloy prepared environment friendly and having improved chemical-mechanical properties such as oxidation resistance, corrosion resistance, or fatigue resistance, and a die-cast material and an extruded material prepared by using the Al alloy.
  • Al aluminum
  • the above problem to be solved is provided as an example and the scope of the present invention is not limited thereto.
  • an aluminum (Al) alloy casted by adding a magnesium (Mg) master alloy, in which a calcium (Ca)-based compound is distributed in an Mg matrix, into molten Al, wherein an Al matrix includes the Ca-based compound, and wherein the Al alloy has superior oxidation resistance, corrosion resistance against salt water, or fatigue resistance to a corresponding Al alloy not including the Ca-based compound.
  • Mg magnesium
  • Ca calcium
  • the Ca-based compound may include at least one of an Mg—Ca compound, an Al—Ca compound, and an Mg—Al—Ca compound
  • the Mg—Ca compound may include Mg 2 Ca
  • the Al—Ca compound may include at least one of Al 2 Ca and Al 4 Ca
  • the Mg—Al—Ca compound may include (Mg,Al) 2 Ca.
  • the Mg master alloy may be prepared by adding a Ca-based additive into molten parent material including pure Mg, or an Mg alloy including Al, as a parent material.
  • the Ca-based compound may be formed by dispersively adding a Ca-based additive onto a surface of an upper part of molten Mg, and then exhausting at least a portion of the Ca-based additive in the molten Mg.
  • the Ca-based compound may be formed by exhausting the Ca-based additive in the molten Mg in such a way that the Ca-based additive does not substantially remain in the Mg master alloy.
  • the upper part of the molten Mg may be stirred and the stirring may be performed at the upper part which is within 20% of a total depth of the molten Mg.
  • the Ca-based additive may include at least one of calcium oxide (CaO), calcium cyanide (CaCN 2 ), and calcium carbide (CaC 2 ).
  • At least a portion of the Ca-based additive may be exhausted in molten parent material, and the Ca-based compound may be formed due to reaction between Ca supplied from the Ca-based additive and Mg or Al of the parent material.
  • the Mg master alloy may be added by 0.0001 parts by weight to 30 parts by weight based on 100 parts by weight of Al
  • the Ca-based additive may be added by 0.0001 parts by weight to 30 parts by weight based on 100 parts by weight of the parent material.
  • Mg may be dissolved in the Al matrix within a range of 0.1 wt % to 15 wt %.
  • a content of the Ca-based compound is increased, a weight gain of the Ca-based compound due to oxidation under the same oxidation condition may be reduced.
  • the superior fatigue resistance may refer to a larger cycle number leading fatigue fracture if a cyclic load is applied at a predetermined frequency under stress conditions of 40% to 80% of a tensile strength.
  • an aluminum (Al) alloy extruded material prepared by extruding the above-described Al alloy, and having a higher strength in comparison to an Al alloy extruded material prepared under the same condition except that the Ca-based compound is not included.
  • an aluminum (Al) alloy die-cast material prepared by using molten metal of the above-described Al alloy, and having a higher strength in comparison to an Al alloy die-cast material prepared under the same condition except that the Ca-based compound is not included.
  • a method of preparing an aluminum (Al) alloy extruded material including preparing molten Al including magnesium (Mg); preparing an Al alloy by casting the molten Al; and extruding the Al alloy, wherein the molten Al is prepared by melting Al together with an Mg master alloy in which a calcium (Ca)-based compound combined with at least one of Mg and Al is included in an Mg matrix.
  • Mg magnesium
  • Ca calcium
  • the method may further include performing heat treatment on the Al alloy extruded material after the Al alloy is extruded.
  • a method of preparing an aluminum (Al) alloy die-cast material including preparing molten Al including magnesium (Mg); and casting the molten Al; and wherein the molten Al is prepared by melting Al together with an Mg master alloy in which a calcium (Ca)-based compound combined with at least one of Mg and Al is included in an Mg matrix.
  • an aluminum (Al) alloy according to the present invention is used, even when a protective gas conventionally used to prevent oxidation of molten Al, for example, SF 6 , is greatly reduced in amount or is not used, a die-cast product may be stably prepared and an extruded material having excellent mechanical properties may be prepared by performing an extruding process.
  • a protective gas conventionally used to prevent oxidation of molten Al for example, SF 6
  • the Al alloy according to an embodiment of the present invention since a calcium (Ca)-based compound added when a magnesium (Mg) master alloy is added is distributed in an Al matrix so as to achieve a distribution strengthening effect and a grain refinement effect, mechanical properties of the Al alloy, for example, strength and fatigue resistance, may be remarkably improved. Due to the improvement in casting properties and/or mechanical properties, oxidation resistance and corrosion resistance of the Al alloy may be improved.
  • FIG. 1 is a flowchart of a method of preparing a magnesium (Mg) master alloy to be added into molten aluminum (Al) so as to prepare an Al alloy, according to an embodiment of the present invention.
  • FIGS. 2A through 2D are images showing electron probe microanalysis (EPMA) results of microstructures and components of an Mg master alloy, according to an embodiment of the present invention.
  • EPMA electron probe microanalysis
  • FIG. 3 is a flowchart of a method of preparing an Al alloy, according to an embodiment of the present invention.
  • FIGS. 4A and 4B are images showing the surfaces of a molten Al alloy prepared by adding an Mg master alloy including calcium oxide (CaO), according to an embodiment of the present invention, and a molten Al alloy prepared by adding pure Mg.
  • an Mg master alloy including calcium oxide (CaO) according to an embodiment of the present invention
  • FIGS. 5A and 5B are images showing the surfaces of a cast material of an Al alloy prepared by adding an Mg master alloy including CaO, according to an embodiment of the present invention, and a cast material of an Al alloy prepared by adding pure Mg.
  • FIGS. 6A and 6B are images showing analysis results on components of an Al alloy prepared by adding an Mg master alloy including CaO, according to an embodiment of the present invention, and components of an Al alloy prepared by adding pure Mg.
  • FIG. 7A is an EPMA image of a microstructure of an Al alloy prepared by adding an Mg master alloy including CaO, according to an embodiment of the present invention
  • FIGS. 7B through 7E are EPMA images showing component mapping results of Al, calcium (Ca), Mg, and oxygen (O), respectively.
  • FIGS. 8 through 10 are images comparatively showing microstructures according to Experimental Examples 2 to 4 and Comparative Examples 2 to 4.
  • FIGS. 11 through 13 are images comparatively showing microstructures according to Experimental Examples 5, 6, and 7 and Comparative Examples 5, 6, and 7.
  • FIG. 14 is a graph showing oxidation resistance of Al alloys based on the content of CaO added to prepare an Mg master alloy.
  • FIG. 15 is a graph showing oxidation resistance of Al alloys according to comparative examples and Al alloys according to embodiments of the present invention, based on the content of Mg.
  • FIGS. 16A through 16G are images showing oxidation resistance of Al alloys according to comparative examples and Al alloys according to embodiments of the present invention, based on the content of Mg.
  • FIG. 17 is a graph showing corrosion resistance of an Al alloy according to a comparative example and an Al alloy according to an embodiment of the present invention.
  • FIG. 18 is an image showing corrosion properties of an Al alloy according to a comparative example.
  • FIG. 19 is an image showing corrosion properties of an Al alloy according to an embodiment of the present invention.
  • FIG. 20 is a graph showing mechanical properties of an Al alloy used in a fatigue test, according to an embodiment of the present invention.
  • FIG. 21 is a schematic diagram showing decomposition of CaO at an upper part of molten Mg when CaO is added in to the molten Mg.
  • an aluminum (Al) alloy is prepared by preparing a master alloy into which a predetermined additive is added, and then adding the master alloy into Al.
  • any of pure magnesium (Mg) and an Mg alloy may be used as a parent material of the master alloy, and is denoted as an Mg master alloy.
  • Pure Mg refers to Mg into which no alloying element is intentionally added, and is substantially defined to include an impurity that is inevitably added during Mg is prepared.
  • An Mg alloy is an alloy prepared by intentionally adding another alloying element such as Al into Mg.
  • the Mg alloy including Al as an alloying element may be referred to as an Mg—Al alloy.
  • the Mg—Al alloy may further include another alloying element other than Al.
  • FIG. 1 is a flowchart of a method of preparing an Mg master alloy, according to an embodiment of the present invention.
  • the method of preparing an Mg master alloy includes forming molten Mg (S1), adding an additive (S2), stirring or holding (S3), and casting (S4).
  • a heating temperature may be, for example, in a range of 400° C. to 800° C.
  • pure Mg may melt at a temperature higher than or equal to 600° C.
  • the Mg alloy may melt at a temperature lower than or equal to 600° C. and higher than or equal to 400° C.
  • the temperature is lower than 400° C.
  • the molten Mg may not be easily formed.
  • the temperature is higher than 800° C., the molten Mg may be sublimated or ignited.
  • the Mg alloy used in operation S1 may include one selected from the group consisting of AZ91 D, AM20, AM30, AM50, AM60, AZ31, AS141, AS131, AS121X, AE42, AE44, AX51, AX52, AJ50X, AJ52X, AJ62X, MR1153, MR1230, AM-HP2, Mg—Al, Mg—Al—Re, Mg—Al—Sn, Mg—Zn—Sn, Mg—Si, Mg—Zn—Y, and equivalents thereof.
  • the Mg alloy is not limited thereto. Any Mg alloy that is commonly used in the industrial field may be used.
  • a small amount of a protective gas may be optionally provided in order to prevent the molten Mg from being ignited.
  • the protective gas may typically use SF 6 , SO 2 , CO 2 , HFC-134a, NovecTM612, an inert gas, an equivalent thereof, or a gas mixture thereof, and may suppress the molten Mg from being ignited.
  • a calcium (Ca)-based additive is added to the molten Mg.
  • the added Ca-based additive may include at least one of calcium oxide (CaO), calcium cyanide (CaCN 2 ), and calcium carbide (CaC 2 ).
  • the Ca-based additive may improve oxidation resistance in the molten Mg and thus a protective gas required to melt Mg may be greatly reduced in amount or may not be used.
  • a protective gas such as SF 6 that is restricted due to an environmental reason may be solved.
  • oxidation resistance of the molten Mg is improved, ignition resistance may be increased and thus an oxide or another inclusion may be suppressed from being mixed into the molten Mg. Accordingly, the cleanliness of molten metal may be significantly improved and thus mechanical properties of an Mg alloy casted by using the molten metal may be improved.
  • At least a portion of the Ca-based additive may be exhausted in the molten Mg. Under an appropriate condition, substantially all of the Ca-based additive may be exhausted in the molten Mg.
  • the Ca-based additive may be reduced in the molten Mg so as to be decomposed to Ca.
  • CaO may be decomposed into Ca and O.
  • the decomposed oxygen may be discharged from the molten Mg into the air in the form of a gas or may float on the molten Mg in the form of dross or sludge.
  • Ca decomposed from CaO may form a compound due to various reactions in molten metal.
  • the compound may be an intermetallic compound formed due to a chemical reaction between metals.
  • the reduced Ca may react with another element(s) in a parent material, e.g., Mg and/or Al, and thus may form a Ca-based compound.
  • the Ca-based additive is a source of Ca used to form a Ca-based compound in the Mg master alloy and is an additive element added into a molten parent material formed to prepare a master alloy.
  • the Ca-based compound is a compound newly formed due to a reaction between Ca supplied from the Ca-based additive and another element(s) in a parent material.
  • Ca has solubility with respect to Mg, it is uncovered that Ca, which is reduced from the Ca-based additive in the molten Mg as in the present invention, is only partially dissolved in the molten Mg and mostly forms the Ca-based compound.
  • a formable Ca-based compound may be an Mg—Ca compound, e.g., Mg 2 Ca.
  • a parent material of the Mg master alloy is an Mg alloy, e.g., an Mg—Al alloy
  • a formable Ca-based compound may include at least one of an Mg—Ca compound, an Al—Ca compound, and an Mg—Al—Ca compound.
  • the Mg—Ca compound may be Mg 2 Ca
  • the Al—Ca compound may include at least one of Al 2 Ca and Al 4 Ca
  • the Mg—Al—Ca compound may be (Mg,Al) 2 Ca.
  • the decomposition and reaction of the Ca-based additive may be more inactivated due to stirring, and a detailed description thereof will be provided below in relation to operation S3.
  • the Ca-based additive is favorable to have a large surface area in order to improve reactivity and thus is favorable to have a form of powder.
  • the Ca-based additive is not limited thereto and may have a form of pellets or masses formed by allowing powder to agglomerate in order to prevent scattering of powder.
  • the Ca-based additive may have a size of 0.1 ⁇ m to 500 ⁇ m, and more particularly, 0.1 ⁇ m to 200 ⁇ m. If the Ca-based additive has a size less than 0.1 ⁇ m, the size is too small and thus the Ca-based additive may be scattered due to hot air of sublimated Mg and thus may not be easily put into a crucible. Also, the Ca-based additive may agglomerate and thus may not be easily mixed with molten metal having a form of a liquid. Such agglomerates reduce a surface area for reaction and thus are not preferable. If the Ca-based additive has a size greater than 500 ⁇ m, a surface area for reaction may be reduced and, furthermore, the Ca-based additive may not react with the molten Mg.
  • the Ca-based additive may be added by 0.001 wt % to 30 wt %, and more particularly, by 0.01 wt % to 15 wt %. If the Ca-based additive is added by less than 0.001 wt %, mechanical properties of the Mg alloy are slightly or hardly improved. Also, if the Ca-based additive is added by more than 30 wt %, intrinsic properties of Mg may not appear.
  • the Ca-based additive may be added into the molten Mg all at once or separately with time intervals. Also, a required amount of the Ca-based additive may be added all at once or the Ca-based additive may be divided into appropriate amounts and may be added separately with time intervals. If the Ca-based additive has a form of powder having fine particles, the Ca-based additive may be added separately with time intervals so as to reduce the possibility that the Ca-based additive agglomerates and to accelerate reaction of the Ca-based additive.
  • stirring may be performed in operation S3.
  • the stirring may be started at the same time when the Ca-based additive is added or after the added Ca-based additive is heated to a certain temperature in molten metal.
  • molten metal and an alloying element are actively stirred by using, for example, a convection method, in order to cause a reaction in the molten metal.
  • a convection method in order to cause a reaction in the molten metal.
  • the Ca-based additive reacts less efficiently and thus is greatly remains in the ultimate molten metal in an un-decomposed state. If the Ca-based additive remains in the ultimate molten metal as described above, the Ca-based additive may be included in a casted Mg alloy and thus mechanical properties of the Mg alloy may deteriorate.
  • FIG. 21 is a schematic diagram showing decomposition of CaO at an upper part of molten Mg when CaO is added in to the molten Mg.
  • CaO is decomposed into O and Ca at the upper part of the molten Mg.
  • the decomposed oxygen may be discharged outside in the form of a gas (O 2 ) or may float on the molten Mg in the form of dross or sludge.
  • the decomposed calcium may react with another element(s) in molten metal to form various compounds.
  • the upper part of the molten Mg may be stirred.
  • Table 1 shows results of measuring CaO residues according to a stirring method when CaO is added into molten Mg of AM60B.
  • the added CaO is 70 ⁇ m in size, and CaO is added by 5 wt %, 10 wt %, and 15 wt %.
  • the stirring method upper part stirring, internal stirring, and no stirring of the molten Mg are selected.
  • the most part of the added CaO is reduced to Ca.
  • the stirring may be performed at the upper part which is within 20%, and desirably, within 10%, of a total depth of the molten metal from the surface thereof. If the stirring is performed at a depth greater than or equal to 20%, the decomposition of the Ca-based additive does not easily occur at the surface of the molten Mg.
  • a stirring time may differ according to the state of an added powder and the temperature of the molten metal, and it is preferable to stir the molten metal sufficiently until the added Ca-based additive is completely exhausted in the molten metal as long as possible.
  • the exhaustion means that decomposition of the Ca-based additive is substantially completed.
  • Decomposition of the Ca-based additive in the molten Mg due to the stirring and Ca formed due to the decomposition may further accelerate a reaction for forming various compounds.
  • operation S4 for solidifying the molten Mg in a mold is performed to prepare the Mg master alloy.
  • the temperature of the mold may be in a range of room temperature (for example, 25° C.) to 400° C.
  • a master alloy may be separated from the mold after the mold is cooled to room temperature. However, if the master alloy is completely solidified, the master alloy may be separated even before the temperature reaches room temperature.
  • the mold may use any one selected from a metallic mold, a ceramic mold, a graphite mold, and equivalents thereof.
  • the casting method may include sand casting, die casting, gravity casting, continuous casting, low-pressure casting, squeeze casting, lost wax casting, thixo casting, or the like.
  • Gravity casting may denote a method of pouring a molten alloy into a mold by using gravity
  • low-pressure casting may denote a method of pouring a molten alloy into a mold by applying a pressure onto the surface of the molten alloy by using a gas.
  • Thixo casting is a casting method performed in a semisolid state and is a combination method adopting advantages of typical casting and forging.
  • the present invention is not limited to a mold type and a casting method or process.
  • the above prepared Mg master alloy has a matrix having a plurality of domains divided from each other by boundaries therebetween.
  • the plurality of domains divided from each other may typically be a plurality of grains divided by grain boundaries therebetween and, as an another example, may be a plurality of phase regions defined by two or more different phase boundaries therebetween.
  • a Ca-based compound formed during the Mg master alloy may be dispersed and exist in the matrix of the Mg master alloy.
  • the Ca-based compound may be one formed due to reaction between the Ca-based additive added in operation S2 and another element(s), e.g., Mg and/or Al, in the Mg parent material.
  • the Ca-based additive is reduced to Ca during the Ca-based additive is added into the molten Mg and is stirred or held.
  • the Ca-based additive is thermodynamically more stable than Mg, Ca is not expected to be separated from the Ca-based additive due to reduction in the molten Mg.
  • the Ca-based additive is reduced in the molten Mg.
  • the reduced Ca may react with another element(s), e.g., Mg and/or Al, in the parent material, thereby forming a Ca-based compound.
  • the Ca-based additive is a source of Ca used to form a Ca-based compound in the Mg master alloy and is an additive element added into a molten parent material formed to prepare a master alloy.
  • the Ca-based compound is a compound newly formed due to a reaction between Ca supplied from the Ca-based additive and another element(s) in a parent material.
  • Ca has solubility with respect to Mg, it is uncovered that Ca, which is reduced from the Ca-based additive in the molten Mg as in the present invention, is only partially dissolved in the molten Mg and mostly forms the Ca-based compound.
  • a formable Ca-based compound may be an Mg—Ca compound, e.g., Mg 2 Ca.
  • a parent material of the Mg master alloy is an Mg alloy, e.g., an Mg—Al alloy
  • a formable Ca-based compound may include at least one of an Mg—Ca compound, an Al—Ca compound, and an Mg—Al—Ca compound.
  • the Mg—Ca compound may be Mg 2 Ca
  • the Al—Ca compound may include at least one of Al 2 Ca and Al 4 Ca
  • the Mg—Al—Ca compound may be (Mg,Al) 2 Ca.
  • the Ca-based compound is distributed at grain boundaries, i.e., boundaries between grains, or phase boundaries, i.e., boundaries between phase regions. This is because such boundaries are further open and have a relatively high energy in comparison to the inside of the grains or the phase regions, and thus may provide a favorable site for nucleation and growth of the Ca-based compound.
  • FIGS. 2A through 2D are images showing electron probe microanalysis (EPMA) results of an Mg master alloy prepared by adding CaO as a Ca-based compound into an Mg—Al alloy, according to an embodiment of the present invention.
  • EPMA electron probe microanalysis
  • FIG. 2A shows a microstructure of the Mg master alloy observed by using back scattered electrons.
  • the Mg master alloy includes regions surrounded by a compound (bright part), that is, a microstructure having a plurality of grains.
  • the compound (bright part) is formed along grain boundaries.
  • FIGS. 2B through 2D are EPMA images showing component mapping results of Al, Ca, and O, respectively, in a region of the compound (bright part).
  • Al and Ca are detected in the compound (bright part in FIG. 2A ) as shown in FIGS. 2B and 2C but O is not detected as shown in FIG. 2D .
  • an Al—Ca compound which is formed due to reaction between Ca separated from CaO and Al included in the parent material, is distributed at grain boundaries of the Mg master alloy.
  • the Al—Ca compound may be Al 2 Ca or Al 4 Ca, which is an intermetallic compound.
  • an Mg master alloy includes a Ca-based compound, which is formed due to reaction between Ca supplied from the Ca-based additive during an alloying process, and Mg and/or Al.
  • All Ca-based compounds are intermetallic compounds and have a melting point higher than the melting point (658° C.) of Al.
  • the melting points of Al 2 Ca and Al 4 Ca as Al—Ca compounds are 1079° C. and 700° C., respectively, which are higher than the melting point of Al.
  • the Ca-based compound may mostly remain without being melted in molten metal. Furthermore, if an Al alloy is prepared by casting the molten metal, the Ca-based compound may be included in the Al alloy.
  • An Al alloy according to an embodiment of the present invention may be prepared, in order to form molten metal in which an Mg master alloy and Al are melted, melting Al to form molten Al and then adding and melting the Mg master alloy including a Ca-based compound, into the molten Al.
  • Al and the Mg master alloy may be s put into a melting apparatus such as a crucible, and then may be heated together to be melted.
  • FIG. 3 is a flowchart of a method of preparing an Al alloy, according to an embodiment of the present invention, and more particularly, a method of preparing an Al alloy by forming molten Al and then adding and melting an Mg master alloy prepared by using the above-described method, into the molten Al.
  • the method of preparing an Al alloy includes forming molten Al (S11), adding an Mg master alloy (S12), stirring or holding (S13), and casting (S14).
  • molten Al is formed by putting Al into a crucible and is heating Al at a temperature ranging from 600° C. to 900° C.
  • Al may be any one selected from pure Al, an Al alloy, and equivalents thereof.
  • the Al alloy for example, may be any one selected from 1000-series, 2000-series, 3000-series, 4000-series, 5000-series, 6000-series, 7000-series, and 8000-series wrought Al, and 100-series, 200-series, 300-series, 400-series, 500-series, and 700-series casting Al.
  • the Mg master alloy prepared by using the above-described method is added into the molten Al.
  • the Mg master alloy used in operation S12 may be added by 0.0001 parts by weight to 30 parts by weight based on 100 parts by weight of Al. If the added Mg master alloy is added by less than 0.0001 parts by weight, effects (hardness, corrosion resistance, weldability, etc.) achieved by adding the Mg master alloy may be insufficient. Also, if the Mg master alloy is added by more than 30 parts by weight, intrinsic properties of Al alloy may not appear.
  • the Mg master alloy may be added in the form of an ingot.
  • the Mg master alloy is not limited thereto and may be added in various forms such as a form of powder and a form of granules.
  • the size of the Mg master alloy is not limited.
  • the Ca-based compound included in the Mg master alloy is provided together into the molten Al.
  • the Ca-based compound provided into the molten Al may include at least one of an Mg—Ca compound, an Al—Ca compound, and an Mg—Al—Ca compound.
  • a small amount of a protective gas may be additionally provided in order to prevent the Mg master alloy from being oxidized.
  • the protective gas may typically use SF 6 , SO 2 , CO 2 , HFC-134a, NovecTM612, an inert gas, an equivalent thereof, or a gas mixture thereof, and may suppress the molten Mg from being oxidized.
  • the above protective gas is not essentially needed and may not be provided. That is, if the Mg master alloy including the Ca-based compound is added as in the present invention, ignition resistance is increased due to an increase in oxidation resistance of the Mg master alloy and an inclusion of an impurity such as an oxide in molten metal is remarkably reduced in comparison to a typical case when Mg not including a Ca-based compound is added. As such, according to the above-described method, even without using a protective gas, the cleanliness of molten Al may be greatly improved and thus the quality of molten metal may be significantly improved.
  • the molten Al is stirred or held for 1 to 400 minutes.
  • the stirring or holding time is less than 1 minute, the Mg master alloy is not sufficiently mixed into the molten Al. Otherwise, if the stirring or holding time is more than 400 minutes, the molten Al is stirred or held for a unnecessarily long time.
  • operation S14 for solidifying the molten Al in a mold is performed to prepare the Al alloy.
  • the temperature of the mold may be in a range of room temperature (for example, 25° C.) to 400° C.
  • a master alloy may be separated from the mold after the mold is cooled to room temperature. However, if the master alloy is completely solidified, the master alloy may be separated even before the temperature reaches room temperature.
  • the casting method is described in detail above in relation to the method of preparing an Mg master alloy and thus is not described here.
  • the prepared Al alloy may be any one selected from 1000-series, 2000-series, 3000-series, 4000-series, 5000-series, 6000-series, 7000-series, and 8000-series wrought Al, and 100-series, 200-series, 300-series, 400-series, 500-series, and 700-series casting Al.
  • the cleanliness of molten Al may be improved and thus mechanical properties of a casted Al alloy may be remarkably improved. That is, due to an improved cleanliness of molten metal, an impurity such as an oxide or another inclusion which deteriorates mechanical properties does not exist in an Al alloy casted by using the molten metal, and bubbles inside the casted Al alloy are also reduced remarkably. Since the above-casted Al alloy has a cleaner internal state than a conventional Al alloy, the Al alloy according to the present invention has mechanical properties, for example, yield strength, tensile strength, and elongation, superior to the conventional Al ally.
  • an Al alloy may be economically prepared to have substantially the same content of Mg as the conventional case.
  • an Mg master alloy according to the present invention is added into molten Al, instability of Mg in the molten Al may be remarkably improved and thus the content of Mg may be more easily increased in comparison to a conventional case.
  • Mg may be dissolved by up to 15 wt % in Al and thus may increase mechanical properties of an Al alloy. For example, if Mg is added into a 300-series or 6000-series Al alloy, strength and elongation of the Al alloy may be improved.
  • an Mg master alloy may be stably added into molten Al such that castability may be ensured while increasing the ratio of Mg by easily increasing the content of Mg in an Al alloy in comparison to a conventional case. Accordingly, if an Mg master alloy is added into a 300-series or 6000-series Al alloy according to the present invention, an oxide or another inclusion may be suppressed from being mixed and strength, elongation, and castability may be improved. Furthermore, a 500-series or 5000-series Al alloy which is not substantially used at present may be used.
  • an Al alloy according to the present invention may easily increase a dissolved amount of Mg up to 0.1 wt % or more, up to 5 wt % or more, up to 6 wt % or more, further up to 10 wt % or more, and even further up to 15 wt % corresponding to a limit of solubility.
  • the stability of Mg in an Al alloy may act favorably when a waste of the Al alloy is reused. For example, if the content of Mg is high in the waste used to prepare the Al alloy, a process of reducing the content of Mg to a required ratio (hereinafter referred to as a ‘demagging process’) is performed. If the required ratio of the content of Mg is low, the difficulty and the cost of the demagging process are increased.
  • a process reducing the content of Mg to a required ratio
  • an Al alloy prepared by using an Mg master alloy including a Ca-based compound, according to the present invention may maintain the ratio of Mg to be more than 0.3 wt % and thus has technical, environmental, and cost advantages.
  • the method of preparing an Al alloy may further include adding a small amount of iron (Fe) after operation S11 or S12.
  • Fe iron
  • the amount of added Fe may be less than that added in a conventional case. That is, if an Al alloy is conventionally casted, for example, die-casted, due to soldering between a die made of an iron-based metal and an Al cast material, the die may be damaged.
  • 1.0 wt % to 1.5 wt % of Fe has been conventionally added into an Al alloy when the Al alloy is die-casted.
  • the addition of Fe may cause another problem of reducing corrosion resistance and elongation of the Al alloy.
  • an Al alloy according to the present invention may include Mg at a high ratio and the conventional soldering problem of a die may be significantly improved even though a considerably small ratio of Fe in comparison to a conventional case is added. Accordingly, the conventional problem of reducing corrosion resistance and elongation may be solved.
  • the content of Fe added to prepare the Al alloy may be less than or equal to 1.0 wt % (and greater than 0 wt %) with respect to the Al alloy, and more particularly, less than or equal to 0.2 wt % (and greater than 0 wt %).
  • Fe within the above composition range may be included in a matrix of the Al alloy.
  • An Al alloy prepared by using the method of preparing the Al ally, according to the present invention includes an Al matrix and a Ca-based compound existing in the Al matrix, wherein Mg may be dissolved in the Al matrix.
  • Mg may be dissolved in the Al matrix within a range of 0.1 wt % to 15 wt %.
  • Ca may be dissolved in the Al matrix by an amount less than or equal to a limit of solubility, for example, less than or equal to 500 ppm.
  • Ca reduced from a Ca-based additive added into an Mg master alloy mostly exists in the form of the Ca-based compound and only a part of it is dissolved in an Mg matrix. If the Mg master alloy is added into molten Al, since Ca dissolved in the Mg master alloy is diluted, the amount of Ca substantially dissolved in the matrix of the Al alloy also has a small value less than or equal to the limit of solubility.
  • the Al alloy according to the present invention has a microstructure in which Ca is dissolved in the Al matrix by an amount less than the limit of solubility, for example, less than 500 ppm, and the Ca-based compound is formed separately in the Al matrix.
  • the Al matrix may have a plurality of domains divided from each other by boundaries therebetween, and the Ca-based compound may exist at the boundaries or the inside of the domains.
  • the Al matrix may be defined as a metal structure body in which Al is a major component and another alloying element is dissolved, or another alloying element other than the Ca-based compound or a compound including the other alloying element is formed as a separate phase.
  • the plurality of domains divided from each other may typically be a plurality of grains divided by grain boundaries therebetween and, as an another example, may be a plurality of phase regions defined by two or more different phase boundaries therebetween.
  • the Al alloy according to the present invention may improve mechanical properties depending on the Ca-based compound formed in the Mg master alloy. As already described above, if the Mg master alloy is added into the molten Al, the Ca-based compound included in the Mg master alloy is also added into the molten Al. All Ca-based compounds are intermetallic compounds formed due to reaction between Ca and other metal elements and have higher melting points than Al.
  • the Ca-based compound may be remains without being melted in molten metal.
  • the Ca-based compound may be included in the Al alloy.
  • the Ca-based compound may be dispersed and distributed in the Al alloy in the form of fine particles.
  • the Ca-based compound, as an intermetallic compound, is a high strength material in comparison to Al which is a matrix. Due to the dispersive distribution of such a high strength material, the strength of the Al alloy may be increased.
  • the Ca-based compound may provide a site for nucleation during phase transition of the Al alloy occurs from a liquid phase to a solid phase. That is, the phase transition from the liquid phase to the solid phase when the Al alloy is solidified will be carried out in the form of nucleation and growth.
  • the Ca-based compound itself acts as a heterogeneous nucleation site, nucleation for phase transition to the solid phase is initially occurs on the interface between the Ca-based compound and the liquid phase. The nucleated solid phase grows around the Ca-based compound.
  • the Ca-based compounds are distributed, solid phases growing at the interfaces of the different Ca-based compounds meet each other to form boundaries, and these boundaries may form grain boundaries or phase boundaries. Accordingly, if the Ca-based compound functions as a nucleation site, the Ca-based compound exists inside grains or phase regions, and the grains or phase regions become finer in comparison to a case when the Ca-based compound does not exist.
  • the Ca-based compound may be distributed at grain boundaries, i.e., boundaries between grains, or phase boundaries, i.e., boundaries between phase regions. This is because such boundaries are further open and have a relatively high energy in comparison to the inside of the grains or the phase regions, and thus may provide a favorable site for nucleation and growth of the Ca-based compound.
  • the Ca-based compound is distributed at grain boundaries or phase boundaries of an Al alloy, since this Ca-based compound acts as an obstacle to the movement of the grain boundaries or the phase boundaries, the movement of the grain boundaries or the phase boundaries may be suppressed and thus an average size of the grains or the phase regions may be reduced.
  • the Al alloy according to the present invention may have averagely finer and smaller grains or phase regions in comparison to an Al alloy not including the Ca-based compound. These fine and small grains or phase regions due to the Ca-based compound may improve both strength and elongation of the Al alloy.
  • the Al matrix may be any one selected from 1000-series, 2000-series, 3000-series, 4000-series, 5000-series, 6000-series, 7000-series, and 8000-series wrought Al, and 100-series, 200-series, 300-series, 400-series, 500-series, and 700-series casting Al.
  • a total amount of Ca may be 0.0001 parts by weight to 10 parts by weight based on 100 parts by weight of Al.
  • the total amount of Ca is a sum of the amount of Ca dissolved in the Al matrix and the amount of Ca existing in the Ca-based compound.
  • the Al matrix may include dissolved Mg by 0.1 wt % to 15 wt %, by 5 wt % to 15 wt %, further by 6 wt % to 15 wt %, and even further by 10 wt % to 15 wt %. That is, as described above, if the Mg master alloy prepared by adding the Ca-based additive, according to the present invention, is used, the amount of Mg added into the molten Al may be stably increased. Accordingly, the amount of Mg dissolved in the Al matrix may also be increased.
  • the increase in the amount of dissolved Mg may greatly contribute to improvement of strength of the Al alloy according to solid solution strengthening and heat treatment, and may achieve superior castability and excellent mechanical properties in comparison to a conventional commercial alloy.
  • an Al alloy according to an embodiment of the present invention has an improved oxidation resistance in comparison to an Al alloy corresponding to the Al alloy according to an embodiment and not including the above-described Ca-based compound.
  • the oxidation resistance of the Al alloy according to the present invention may be increased if the content of the Ca-based additive added to prepare the Mg master alloy is high.
  • the improvement in oxidation resistance is related to an improvement in quality of an Al alloy and/or a distribution of the Ca-based compound in a matrix.
  • an Al alloy corresponding to the Al alloy according to an embodiment may refer to a typical Al alloy including the same additive elements other than the Ca-based additive as the Al alloy according to an embodiment, for example, the same elements according to the standards of the Aluminum Association of America.
  • an Al alloy corresponding to the Al alloy according to an embodiment may be the typical 6061 alloy.
  • an Al alloy corresponding to the Al alloy according to an embodiment may refer to an Al alloy including the same-composition additive elements other than the Ca-based additive as the Al alloy according to an embodiment.
  • the Al alloy is a new Al alloy that does not belong to those according to the standards of the Aluminum Association of America
  • an Al alloy corresponding to the Al alloy may refer to an Al ally having substantially the same contents of additive elements (except for the Ca-based additive) as the new Al alloy.
  • the same does not mean mathematically the same but means practically the same in consideration of, for example, an experimental error range.
  • Table 2 comparatively shows cast properties of an Al alloy prepared by adding an Mg master alloy including CaO as a Ca-based additive into Al (Experimental Example 1) and an Al alloy prepared by adding pure Mg including no Ca-based additive into Al (Comparative Example 1).
  • the Al alloy of Experimental Example 1 is prepared by adding 305 g of the Mg master alloy into 2750 g of Al, and the Al alloy of Comparative Example 1 is prepared by adding 305 g of pure Mg into 2750 g of Al.
  • the Mg master alloy used in Experimental Example 1 employed an Mg—Al alloy as a parent material, and a weight ratio of CaO with respect to the parent material is 0.3.
  • Example 1 Amount of Dross 206 g 510 g (Impurity Floating on Surface of Molten Metal) Content of Mg in Al alloy 4.89% 2.65% Fluidity of Molten Metal Good Bad Hardness 92.6 92 (HR Load 60 kg, 1/16′′ Steel Ball)
  • the amount of an impurity floating on the surface of molten metal (the amount of dross) is remarkably smaller in the case when the Mg master alloy is added (Experimental Example 1) than the case when pure Mg is added (Comparative Example 1). Also, the content of Mg in the Al alloy is larger in the case when the Mg master alloy is added (Experimental Example 1) than the case when pure Mg is added (Comparative Example 1). As such, it may be seen that, according to the present invention, the loss of Mg is remarkably reduced in comparison to a method of adding pure Mg.
  • the fluidity of the molten metal and the hardness of the Al alloy are superior in the case when the Mg master alloy is added (Experimental Example 1) than the case when pure Mg is added (Comparative Example 1).
  • FIGS. 4A and 4B are images showing the states of molten metal according to Experimental Example 1 and Comparative Example 1. Referring to FIGS. 4A and 4B , the state of the molten metal is good in Experimental Example 1 ( FIG. 4A ), but the surface of the molten metal changes to black due to oxidation of Mg in Comparative Example 1 ( FIG. 4B ).
  • FIGS. 5A and 5B are images comparatively showing the surfaces of cast materials of the Al alloys according to Experimental Example 1 and Comparative Example 1.
  • the surface of the cast material of the Al alloy prepared by adding the Mg master alloy according to Experimental Example 1 is cleaner than that of the cast material of the Al alloy prepared by adding pure Mg according to Comparative Example 1 ( FIG. 5B ).
  • the quality of the molten metal is remarkably improved and thus castability is improved in the case when the Mg master alloy is added in comparison to the case when pure Mg is added.
  • FIGS. 6A and 6B are images showing results of energy dispersive spectroscopy (EDS) analysis on the Al alloys according to Experimental Example 1 and Comparative Example 1 by using a scanning electron microscope (SEM).
  • EDS energy dispersive spectroscopy
  • FIGS. 6A and 6B in the Al alloy prepared by adding pure Mg according to Comparative Example 1 ( FIG. 6B ), only Mg and Al are detected.
  • the Al alloy prepared by adding the Mg master alloy including CaO according to Experimental Example 1 ( FIG. 6A ) Ca exists.
  • Mg and Al are detected at the same position and oxygen is hardly detected. As such, it may be seen that Ca exists as a Ca-based compound by reacting with Mg and/or Al after being reduced from CaO.
  • FIG. 7A is an EPMA image of a microstructure of the Al alloy of Experimental Example 1
  • FIGS. 7B through 7E are EPMA images showing component mapping results of Al, Ca, Mg, and O, respectively.
  • Ca and Mg are detected at the same position in an Al matrix as shown in FIGS. 7B through 7D, and O is not detected as shown in FIG. 7E .
  • Table 3 comparatively shows mechanical properties of die-cast alloys according to comparative examples and die-cast alloys according to experimental examples of the present invention.
  • Experimental Example 2 shows a die-cast binary Al—Mg alloy and prepared by adding 10 wt % of an Mg master alloy including CaO into Al.
  • Comparative Example 2 shows, as a commercial Al alloy, a Magsimal-59 alloy including 5.0 wt % to 6.0 wt % of Mg, which is a quite high content of Mg in a commercial Al alloy.
  • FIG. 8 is an image showing a microstructure according to Experimental Example 2.
  • the content of Mg is 10 wt %, an impurity such as an oxide or another inclusion is not observed and very fine grains are obtained.
  • the size of the grains according to Experimental Example 2 is very small in comparison to a general commercial alloy. These clean and fine-grain properties are regarded as one factor for achieving excellent mechanical properties of Experimental Example 2.
  • Comparative Example 3 shows a die-cast material prepared by using a 7xx alloy including Mg by about 2 wt % to about 3.5 wt %
  • Experimental Example 3 shows a die-cast material the same as that of Comparative Example 3 except that an Mg master alloy including CaO is added instead of pure Mg as an alloying element.
  • Experimental Example 3 achieves a significantly higher tensile strength and yield strength and achieves an equivalent elongation. As described above, it is regarded that the above result is related to an improvement in cleanliness of molten metal when an Al alloy according to an experimental example of the present invention is prepared.
  • FIGS. 9A and 9B are images comparatively showing microstructures according to Experimental Example 3 and Comparative Example 3.
  • the alloy according to Experimental Example 3 has much finer grains. As described above, it is regarded that these fine grains of the die-cast Al alloys according to the experimental examples are achieved because growth at grain boundaries is suppressed by the Ca-based compound distributed at the grain boundaries or because the Ca-based compound functions as a site for nucleation during solidification. Also, these fine grains are regarded as one factor for achieving excellent mechanical properties of the Al alloys according to the experimental examples.
  • Comparative Example 4 shows a die-cast material of an ALDC12 alloy that is the most commonly used as a commercial die-cast alloy and its mechanical properties are as shown in the ASM handbook.
  • Experimental Examples 4-1 and 4-2 show die-cast materials having the same composition as that of Comparative Example 4 except that an Mg master alloy including CaO is added instead of pure Mg as an alloying element.
  • Experimental Example 4-1 0.3 wt % of the Mg master alloy including 0.5 wt % of CaO is added to Al.
  • Experimental Example 4-2 0.5 wt % of the Mg master alloy including 1.0 wt % of CaO is added to Al.
  • Experimental Examples 4-1 and 4-2 according to embodiments of the present invention achieve higher tensile strengths and yield strengths and superior elongations.
  • Experimental Example 4-2 including a larger content of CaO the elongation as well as the strength is superior.
  • the above result may be related to an improvement in cleanliness of molten metal when an Al alloy according to an experimental example of the present invention is prepared.
  • FIGS. 10A through 10C are images showing microstructures of the die-cast Al alloy according to Comparative Example 4 and the die-cast Al alloys according to Experimental Examples 4-1 and 4-2.
  • Experimental Examples 4-1 and 4-2 achieve finer grains. As described above, it is regarded that these fine grains of the die-cast Al alloys according to the experimental examples are achieved because growth at grain boundaries is suppressed by the Ca-based compound distributed at the grain boundaries or because the Ca-based compound functions as a site for nucleation during solidification. Also, these fine grains are regarded as one factor for achieving excellent mechanical properties of the Al alloys according to the experimental examples.
  • Table 5 shows mechanical properties of Al alloy extruded materials according to experimental examples and Al alloy extruded materials according to comparative examples.
  • Experimental Examples 5, 6, and 7 respectively show Al alloy extruded materials prepared by adding an Mg master alloy including CaO into a 5056 alloy, a 6061 alloy, and a 7075 alloy which are commercial Al alloys, and Comparative Examples 5, 6, and 7 respectively show the 5056 alloy, the 6061 alloy, and the 7075 alloy.
  • Specimens according to Experimental Examples 5, 6, and 7 are obtained by performing casting, extruding, and then T6 heat treatment, and Comparative Examples 5, 6, and 7 use data according to the ASM standards (T6 heat treatment data).
  • the Al alloy extruded materials according to experimental examples of the present invention achieve higher tensile strengths and yield strengths and superior or equivalent elongations.
  • the tensile strength may be greatly increased by about 1.46 times and the elongation may be maintained at an equivalent level.
  • Experimental Example 5 is about 1.46 times of Comparative Example 5
  • Experimental Example 6 is about 1.13 times of Comparative Example 6
  • Experimental Example 7 is about 1.16 times of Comparative Example 7. That is, the tensile strengths according to the experimental examples are about 1.13 times to about 1.46 times higher than the tensile strengths according to the comparative examples.
  • Experimental Example 5 is about 0.98 times of Comparative Example 5
  • Experimental Example 6 is about 1.48 times of Comparative Example 6
  • Experimental Example 7 is about 1.24 times of Comparative Example 7.
  • the Al alloys according to the experimental examples of the present invention have ideal properties for increasing the strength and the elongation. As described above, the above result may be related to an improvement in cleanliness of molten metal of an Al alloy.
  • FIGS. 11 through 13 are images comparatively showing microstructures according to Experimental Examples 5, 6, and 7 and Comparative Examples 5, 6, and 7 shown in Table 5.
  • grains according to Experimental Example 5 have an average size of about 25 ⁇ m
  • grains according to Comparative Example 5 have an average size of about 60 ⁇ m. That is, the grain size according to Experimental Example 5 is merely about 0.42 times of the grain size according to Comparative Example 5.
  • grains according to Experimental Example 6 have an average size of about 30 ⁇ m
  • grains according to Comparative Example 6 have an average size of about 50 ⁇ m. That is, the grain size according to Experimental Example 6 is merely about 0.6 times of the grain size according to Comparative Example 6.
  • grains according to Experimental Example 7 have an average size of about 25 ⁇ m
  • grains according to Comparative Example 7 have an average size of about 50 ⁇ m. That is, the grain size according to Experimental Example 7 is merely about 0.5 times (half) of the grain size according to Comparative Example 7.
  • the Al alloy extruded materials according to the experimental examples of the present invention have much finer grains in comparison to the commercial Al alloy extruded materials.
  • the grain size of the Al alloy extruded materials according to the experimental examples of the present invention is in a range of about 0.42 times to about 0.6 times of the grain size of the commercial Al alloy is extruded materials.
  • these fine grains of the Al alloys according to the experimental examples are achieved because growth at grain boundaries is suppressed by the Ca-based compound distributed at the grain boundaries or because the Ca-based compound functions as a site for nucleation during solidification. Also, these fine grains are regarded as one factor for achieving excellent mechanical properties of the Al alloys according to the experimental examples.
  • Table 6 comparatively shows mechanical properties of Al alloy extruded materials according to experimental examples and Al alloy extruded materials according to comparative examples, based on heat treatment conditions.
  • Comparative Examples 6-1, 6-2, and 6-3 respectively show specimens (extruded materials) prepared by casting, extruding, and heat-treating a commercial 6061 alloy under conditions T1, T5, and T6, and
  • Experimental Examples 6-1, 6-2, and 6-3 respectively show specimens prepared by casting, extruding, and heat-treating an Al alloy, which is prepared by adding an Mg master alloy including CaO into the commercial 6061 alloy, under conditions T1, T5, and T6.
  • an Al alloy substantially refers to an Al alloy extruded material that is completely heat-treated after being extruded.
  • the Al alloys according to the experimental examples of the present invention have ideal properties for increasing the strength and the elongation. As described above, the above result may be related to an improvement in cleanliness of molten metal of an Al alloy.
  • the Al alloy extruded materials according to embodiments of the present invention (Experimental Examples 6-1 and 6-2) have higher hardness levels than the commercial Al alloy extruded materials (Comparative Examples 6-1 and 6-2).
  • the commercial Al alloy extruded material (Comparative Example 6-3) has a higher hardness level than the Al alloy extruded material according to an embodiment of the present invention (Experimental Example 6-3).
  • FIG. 14 is a graph showing oxidation resistance of Al alloys based on the content of CaO added to prepare an Mg master alloy.
  • oxidation is performed in an O 2 atmosphere at about 550° C. for about 40 hours.
  • the content of CaO added to prepare the Mg master alloy varies from 0 wt %, to 0.35 wt %, to 0.7 wt %, and to 1.0 wt %, and Al alloys prepared by using the Mg master alloy are represented as Al-5Mg, Al-5(Mg-5Al-0.35CaO), Al-5(Mg-5Al-0.7CaO), and Al-5(Mg-5Al-1.0CaO).
  • the contents of additive elements other than CaO are substantially the same.
  • weight gains (%) of the specimens with respect to the increase in isothermal oxidation time are small. Furthermore, if the content of CaO is increased, that is, if the content of the Ca-based compound in the Al alloy is increase, the weight gain of the specimen is small. Considering that the weight of the specimen is increased as oxidation is processed, if the content of CaO is increased or if the content of the Ca-based compound in the Al alloy is increased, oxidation resistance of the Al alloy is increased.
  • FIG. 15 is a graph comparatively showing oxidation resistance of Al alloys according to comparative examples and Al alloys according to embodiments of the present invention, based on the content of Mg.
  • FIGS. 16A through 16G are images comparatively showing oxidation resistance of Al alloys according to comparative examples and Al alloys according to embodiments of the present invention, based on the content of Mg.
  • the Al alloys according to embodiments of the present invention have the same contents of additive elements as the Al alloys according to the comparative examples except that a Ca-based additive is added to prepare an Mg master alloy.
  • the Al alloys according to embodiments of the present invention are marked as “Eco” in FIGS. 15 and 16 .
  • the Al alloys according to embodiments of the present invention have higher oxidation resistances than the Al alloys according to the comparative examples.
  • the Al alloy including 2.5 wt % of Mg according to an experimental example of the present invention (Eco Al-2.5Mg) has a higher oxidation resistance than pure Al.
  • the Al alloys according to embodiments of the present invention may be referred to as oxidation-resistant Al alloys in comparison to typical Al alloys.
  • FIG. 17 is a graph showing corrosion resistance of an Al alloy according to a comparative example and an Al alloy according to an embodiment of the present invention.
  • FIG. 18 is an image showing corrosion properties of an Al alloy according to a comparative example.
  • FIG. 19 is an image showing corrosion properties of an Al alloy according to an embodiment of the present invention.
  • a corrosion rate may be represented as a corrosion loss for a unit period of time.
  • the corrosion rate s is calculated in units of milimeters/year (mmy).
  • a K-factor is calculated as 8.75 ⁇ 10 4 .
  • a commercial 7075 alloy (AA7075) is used in the comparative example, and an Al alloy prepared by adding an Mg master alloy including CaO into the commercial 7075 alloy (Eco 7075) is used in the experimental example.
  • a salt spray test is performed by using a 3% NaCl solution, at 25° C. and pH 7.0, for 240 hours.
  • a corrosion rate of the Al alloy according to an embodiment of the present invention (Eco 7075) is lower than or equivalent to the Al alloy according to the comparative example (AA7075).
  • the Al alloy according to an embodiment of the present invention may be referred to as an oxidation-resistant Al alloy in comparison to a typical Al alloy.
  • Table 7 shows results of a fatigue test of an Al alloy according to an experimental example of the present invention.
  • the present experimental example uses an Al alloy having the same composition as a commercial 7075 alloy except that an Mg master alloy including CaO is added (hereinafter referred to as ECO-7075).
  • the Al alloy according to the present experimental example has a yield strength of 590.89 Mpa (29.92 kN).
  • stresses are 40%, 60%, and 80% of the yield strength (590.89 MPa)
  • a stress amplitude is 5 kN
  • frequencies are 10 Hz and 2 Hz.
  • the Al alloy according to the experimental example of the present invention has superior fatigue properties to a corresponding commercial Al alloy (i.e., a 7075 alloy).
  • FIG. 20 is a graph showing mechanical properties of an Al alloy used in a fatigue test, according to an experimental example of the present invention.
  • the Al alloy according to the experimental example has a yield strength of 590.89 Mpa, a tensile strength of 651.9 Mpa, and an elongation of 13.6%.
  • the above strength and elongation are much higher than a typical 7075 alloy.
  • the Al alloy according to the present experimental example has a high strength and excellent fatigue properties in comparison to a conventional Al alloy.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Manufacture And Refinement Of Metals (AREA)
  • Extrusion Of Metal (AREA)
US13/880,724 2010-10-19 2011-10-19 Aluminum alloy having improved oxidation resistance, corrosion resistance, or fatigue resistance, and die-cast material and extruded material prepared by using the aluminum alloy Abandoned US20130243643A1 (en)

Applications Claiming Priority (15)

Application Number Priority Date Filing Date Title
KR10-2010-0102116 2010-10-19
KR20100102116 2010-10-19
KR10-2011-0013082 2011-02-15
KR20110013082 2011-02-15
KR1020110100340A KR101273579B1 (ko) 2010-10-19 2011-09-30 알루미늄 합금 압출재 및 그 제조 방법
KR10-2011-0100339 2011-09-30
KR1020110100337A KR101273533B1 (ko) 2010-10-19 2011-09-30 피로특성이 개선된 알루미늄 합금 및 그 제조 방법
KR1020110100338A KR101273584B1 (ko) 2010-10-19 2011-09-30 내부식성 알루미늄 합금 및 그 제조 방법
KR10-2011-0100337 2011-09-30
KR10-2011-0100341 2011-09-30
KR1020110100341A KR101273577B1 (ko) 2010-10-19 2011-09-30 알루미늄 합금 다이캐스팅재 및 그 제조방법
KR10-2011-0100338 2011-09-30
KR1020110100339A KR101273582B1 (ko) 2010-10-19 2011-09-30 내산화성 알루미늄 합금 및 그 제조 방법
KR10-2011-0100340 2011-09-30
PCT/KR2011/007771 WO2012053813A2 (ko) 2010-10-19 2011-10-19 내산화성, 내부식성 또는 내피로성이 개선된 알루미늄 합금 및 상기 알루미늄 합금을 이용하여 제조한 다이캐스팅재 및 압출재

Publications (1)

Publication Number Publication Date
US20130243643A1 true US20130243643A1 (en) 2013-09-19

Family

ID=46140508

Family Applications (1)

Application Number Title Priority Date Filing Date
US13/880,724 Abandoned US20130243643A1 (en) 2010-10-19 2011-10-19 Aluminum alloy having improved oxidation resistance, corrosion resistance, or fatigue resistance, and die-cast material and extruded material prepared by using the aluminum alloy

Country Status (5)

Country Link
US (1) US20130243643A1 (ko)
EP (1) EP2631311A4 (ko)
KR (5) KR101273582B1 (ko)
RU (1) RU2562589C9 (ko)
WO (1) WO2012053813A2 (ko)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018204100A (ja) * 2017-04-15 2018-12-27 ザ・ボーイング・カンパニーＴｈｅ Ｂｏｅｉｎｇ Ｃｏｍｐａｎｙ マグネシウムと、クロム、マンガン及びジルコニウムのうちの少なくとも１つとを添加したアルミニウム合金、並びにその製造方法

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20140063959A (ko) 2012-11-19 2014-05-28 한국생산기술연구원 아연합금 및 이의 제조방법
CN105296822A (zh) * 2015-12-09 2016-02-03 苏州爱盟机械有限公司 一种轻质阻垢型自行车链条
US11098391B2 (en) * 2017-04-15 2021-08-24 The Boeing Company Aluminum alloy with additions of magnesium, calcium and at least one of chromium, manganese and zirconium, and method of manufacturing the same
KR101961468B1 (ko) * 2017-09-29 2019-04-15 (주)한국주조산업 알루미늄합금용 Al-Mg-Ca 모합금 및 그 제조방법
US20240254594A1 (en) * 2021-05-14 2024-08-01 Lg Electronics Inc. Aluminum alloy, method for manufacturing same, and parts using same

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110123390A1 (en) * 2009-11-20 2011-05-26 Korea Institute Of Industrial Technology Aluminum alloy and manufacturing method thereof
US20110123391A1 (en) * 2009-11-20 2011-05-26 Korea Institute Of Industrial Technology Aluminum alloy and manufacturing method thereof

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01156446A (ja) * 1987-12-14 1989-06-20 Nippon Light Metal Co Ltd 耐圧性の優れた鋳物用アルミニウム合金
RU2163939C1 (ru) * 1999-08-09 2001-03-10 Государственное предприятие "Всероссийский научно-исследовательский институт авиационных материалов" Сплав на основе алюминия, способ получения полуфабрикатов и изделие из этого сплава
RU2163938C1 (ru) * 1999-08-09 2001-03-10 Государственное предприятие "Всероссийский научно-исследовательский институт авиационных материалов" Коррозионно-стойкий сплав на основе алюминия, способ получения полуфабрикатов и изделие из него
JP4093221B2 (ja) * 2003-10-17 2008-06-04 株式会社豊田中央研究所 鋳物用アルミニウム合金、アルミニウム合金鋳物およびその製造方法
SI1612286T1 (sl) * 2004-06-29 2011-10-28 Rheinfelden Aluminium Gmbh Aluminijeva legura za tlačno litje
JP4623372B2 (ja) * 2005-07-27 2011-02-02 アイシン・エィ・ダブリュ株式会社 鋳物用アルミニウム合金およびその製造方法、ならびにアルミニウム合金鋳造製品の製造方法
JP4706011B2 (ja) * 2005-07-27 2011-06-22 国立大学法人東北大学 マグネシウム合金、成形品およびマグネシウム合金の成形方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110123390A1 (en) * 2009-11-20 2011-05-26 Korea Institute Of Industrial Technology Aluminum alloy and manufacturing method thereof
US20110123391A1 (en) * 2009-11-20 2011-05-26 Korea Institute Of Industrial Technology Aluminum alloy and manufacturing method thereof

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
Alloy Phase Diagrams (Aluminum Binary Alloy Phase Diagrams), Vol 3, ASM Handbook, ASM International, 1992, p. 2.4 - 2.56. *
Alloy Phase Diagrams (Calcium Binary Alloy Phase Diagrams), Vol 3, ASM Handbook, ASM International, 1992, p. 2.116 - 2.123. *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018204100A (ja) * 2017-04-15 2018-12-27 ザ・ボーイング・カンパニーＴｈｅ Ｂｏｅｉｎｇ Ｃｏｍｐａｎｙ マグネシウムと、クロム、マンガン及びジルコニウムのうちの少なくとも１つとを添加したアルミニウム合金、並びにその製造方法
US11149332B2 (en) * 2017-04-15 2021-10-19 The Boeing Company Aluminum alloy with additions of magnesium and at least one of chromium, manganese and zirconium, and method of manufacturing the same
JP7294773B2 (ja) 2017-04-15 2023-06-20 ザ・ボーイング・カンパニー マグネシウムと、クロム、マンガン及びジルコニウムのうちの少なくとも１つとを添加したアルミニウム合金、並びにその製造方法

Also Published As

Publication number Publication date
KR20120040654A (ko) 2012-04-27
EP2631311A4 (en) 2017-12-27
KR20120040652A (ko) 2012-04-27
RU2562589C9 (ru) 2016-03-10
RU2013117706A (ru) 2014-11-27
KR20120040653A (ko) 2012-04-27
KR20120040650A (ko) 2012-04-27
KR20120040651A (ko) 2012-04-27
WO2012053813A2 (ko) 2012-04-26
KR101273584B1 (ko) 2013-06-11
RU2562589C2 (ru) 2015-09-10
WO2012053813A3 (ko) 2012-06-21
EP2631311A2 (en) 2013-08-28
KR101273582B1 (ko) 2013-06-11
KR101273533B1 (ko) 2013-06-17
KR101273579B1 (ko) 2013-06-11
KR101273577B1 (ko) 2013-06-11

Similar Documents

Publication Publication Date Title
US9200348B2 (en) Aluminum alloy and manufacturing method thereof
US8808423B2 (en) Magnesium-based alloy for high temperature and manufacturing method thereof
AU2011233970B2 (en) Magnesium-based alloy with superior fluidity and hot-tearing resistance and manufacturing method thereof
US9080225B2 (en) Aluminum alloy and manufacturing method thereof
EP2675930B1 (en) Method of refining metal alloys
KR101199912B1 (ko) 알루미늄 합금의 제조 방법
US20130243643A1 (en) Aluminum alloy having improved oxidation resistance, corrosion resistance, or fatigue resistance, and die-cast material and extruded material prepared by using the aluminum alloy
KR20130012662A (ko) 고강도 고연성 난연성 마그네슘 합금
US9657376B2 (en) Aluminum alloy and production method thereof
EP2374905B1 (en) Manufacturing method of magnesium based alloy for high temperature
JP2012197486A (ja) マグネシウム合金

Legal Events

Date Code Title Description
AS Assignment

Owner name: KOREA INSTITUTE OF INDUSTRIAL TECHNOLOGY, KOREA, R

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KIM, SE-KWANG;YOON, YOUNG-OK;LEE, JIN-KYU;AND OTHERS;REEL/FRAME:030573/0379

Effective date: 20130418

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION