US20130192613A1 - Substituted Cellulose Acetates and Uses Thereof - Google Patents

Substituted Cellulose Acetates and Uses Thereof Download PDF

Info

Publication number
US20130192613A1
US20130192613A1 US13/359,603 US201213359603A US2013192613A1 US 20130192613 A1 US20130192613 A1 US 20130192613A1 US 201213359603 A US201213359603 A US 201213359603A US 2013192613 A1 US2013192613 A1 US 2013192613A1
Authority
US
United States
Prior art keywords
cellulose acetate
substituted cellulose
present
nonmetal
substituted
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/359,603
Other languages
English (en)
Inventor
Michael T. Combs
Thomas S. Garrett
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Acetate International LLC
Original Assignee
Celanese Acetate LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Celanese Acetate LLC filed Critical Celanese Acetate LLC
Priority to US13/359,603 priority Critical patent/US20130192613A1/en
Assigned to CELANESE ACETATE LLC reassignment CELANESE ACETATE LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: COMBS, MICHAEL T., GARRETT, THOMAS S.
Priority to CN201380006636.0A priority patent/CN104105416A/zh
Priority to KR1020147023496A priority patent/KR20140116537A/ko
Priority to CA2861037A priority patent/CA2861037A1/en
Priority to EP13741010.6A priority patent/EP2811852A4/en
Priority to BR112014018021A priority patent/BR112014018021A8/pt
Priority to JP2014554785A priority patent/JP2015510395A/ja
Priority to PCT/US2013/022625 priority patent/WO2013112502A1/en
Priority to MX2014009100A priority patent/MX2014009100A/es
Publication of US20130192613A1 publication Critical patent/US20130192613A1/en
Assigned to ACETATE INTERNATIONAL LLC reassignment ACETATE INTERNATIONAL LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CELANESE ACETATE LLC
Abandoned legal-status Critical Current

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A24—TOBACCO; CIGARS; CIGARETTES; SIMULATED SMOKING DEVICES; SMOKERS' REQUISITES
    • A24D—CIGARS; CIGARETTES; TOBACCO SMOKE FILTERS; MOUTHPIECES FOR CIGARS OR CIGARETTES; MANUFACTURE OF TOBACCO SMOKE FILTERS OR MOUTHPIECES
    • A24D3/00—Tobacco smoke filters, e.g. filter-tips, filtering inserts; Filters specially adapted for simulated smoking devices; Mouthpieces for cigars or cigarettes
    • A24D3/06—Use of materials for tobacco smoke filters
    • A24D3/08—Use of materials for tobacco smoke filters of organic materials as carrier or major constituent
    • A24D3/10—Use of materials for tobacco smoke filters of organic materials as carrier or major constituent of cellulose or cellulose derivatives
    • A—HUMAN NECESSITIES
    • A24—TOBACCO; CIGARS; CIGARETTES; SIMULATED SMOKING DEVICES; SMOKERS' REQUISITES
    • A24D—CIGARS; CIGARETTES; TOBACCO SMOKE FILTERS; MOUTHPIECES FOR CIGARS OR CIGARETTES; MANUFACTURE OF TOBACCO SMOKE FILTERS OR MOUTHPIECES
    • A24D3/00—Tobacco smoke filters, e.g. filter-tips, filtering inserts; Filters specially adapted for simulated smoking devices; Mouthpieces for cigars or cigarettes
    • A24D3/06—Use of materials for tobacco smoke filters
    • A24D3/067—Use of materials for tobacco smoke filters characterised by functional properties
    • A24D3/068—Biodegradable or disintegrable
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
    • D04H1/425—Cellulose series
    • D04H1/4258—Regenerated cellulose series
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/013—Regenerated cellulose series
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/02—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments
    • D04H3/07—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments otherwise than in a plane, e.g. in a tubular way
    • D04H3/077—Stick, rod or solid cylinder shaped
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
    • C09K8/00—Compositions for drilling of boreholes or wells; Compositions for treating boreholes or wells, e.g. for completion or for remedial operations
    • C09K8/02—Well-drilling compositions
    • C09K8/03—Specific additives for general use in well-drilling compositions
    • C09K8/035—Organic additives

Definitions

  • the present invention relates to synthetic polymers and, in particular, to substituted cellulose acetates, and methods of use thereof.
  • Cellulose acetate is an acetate ester derivative of cellulose, a naturally occurring biopolymer comprising ⁇ -D-glucose monomer units, and is widely used to make a variety of consumer products.
  • Naturally occurring cellulose is insoluble in water and most organic solvents.
  • the three free hydroxyl groups of each glucose monomer unit in cellulose can be derivatized to modify certain properties, for example, solubility in certain solvents.
  • Cellulose acetate is thought to be among the most commercially useful derivatives of cellulose, and its specific physical and chemical properties generally depend largely on the degree of substitution of acetate on the three free hydroxyl groups of a glucose monomer unit.
  • cellulose acetate Since its first synthesis, cellulose acetate has been used, among other things, as a film base in photography, a component in adhesives, and a raw material used in the manufacture of cigarette filters.
  • One of the key attributes of cellulose acetate is that it can be processed into many different shapes and forms, including, films, tows, flakes, fibers, and solids, depending on the desirability of the application.
  • cellulose acetate tow is primarily used in the manufacture of cigarette filters.
  • cellulose acetate involves acetylating cellulose, which is commonly obtained from wood pulp, in the presence of acetic anhydride and acids.
  • Acetic acid and sulfuric acid are the two acids usually present during the acetylation reaction.
  • the acetic anhydride serves as the primary acetylating agent; the acetic acid is used primarily as a diluent; and a small amount of the sulfuric acid is used as the catalyst.
  • the monomeric units of cellulose have three hydroxyl groups that are readily available for substitution, e.g., via acetylation.
  • the monomeric units at both ends also have an additional hydroxyl group that are typically involved inter-sugar linkages.
  • the product of the acetylation reaction is a primary cellulose acetate that usually contains high concentration levels of acetate or, in other words, has a high degree of substitution (DS) of acetate.
  • degree of substitution of acetate generally refers to the average number of acetates per glucose monomer unit.
  • the structure of cellulose acetate may be generally characterized by specifying the degree of substitution of acetate.
  • acetylated cellulose is commonly referred to as cellulose triacetate, where, according to Federal Trade Commission guidelines, at least 92% of the hydroxyl groups are substituted with acetyl groups.
  • Acetylated cellulose having reduced DS of acetate can be prepared by controlled hydrolysis of cellulose triacetate.
  • the primary cellulose acetate is hydrolyzed in the presence of acetic acid and sulfuric acid to reduce the DS of acetate of the primary cellulose acetate.
  • the resulting hydrolysis product is usually a cellulose acetate flake having a DS on the order of about 2.4 to about 2.6.
  • cellulose acetate flake may be subjected to further treatment in order to process the cellulose acetate to its desired form.
  • cellulose acetate tow may be formed by dissolving the cellulose acetate flakes in acetone, putting cellulose acetate solution through a series of filtration processes, and dry spinning the acetone dope through microscopic holes in a spinneret. As the cellulose acetate moves through this extrusion process, filaments of cellulose acetate are collected. These filaments are typically bundled and then crimped to ensure tow band cohesion as well as desired bulk.
  • cellulose acetate tow which is essentially a continuous band composed of several thousand filaments held loosely together by crimp.
  • the cellulose acetate tow filaments usually are very thin and may be packed together tightly to create a filter.
  • cellulose acetate tow generally refers to post-synthesis processed bundles of filaments of cellulose acetate.
  • Cellulose acetate is also environmentally friendly in that it is a readily degradable material made largely from a renewable source, wood pulp. While cellulose acetates that vary in their DS of acetate are structurally similar, this variation can have some effect on the biodegradability of the cellulose acetate. At higher degrees of acetyl substitution, the rate of biodegradation can be significantly reduced relative to naturally occurring cellulose or cellulose having less acetyl substitution. Cellulose acetates having a lower DS of acetate biodegrade more readily than cellulose acetates having a higher DS of acetate. This trend is believed to taper off at lower DS of acetate values because the material becomes insoluble in water.
  • the biodegradation rates of cellulose acetate having DS values of 1.85, 2.07, and 2.57 were tested for their biodegradability ( FIG. 1 ).
  • the cellulose acetate with a DS of 1.85 showed the highest biodegradation rate while the cellulose acetate with an acetyl value of 2.57 showed the slowest biodegradation rate.
  • cellulose acetate is a versatile composition with many commercial uses, the properties of certain cellulose acetate derivatives have not been exhaustively studied. For example, in a typical synthesis, residual sulfate groups are typically removed in order to improve thermal stability. As a result, cellulose acetates synthesized by typical means will have about 0.005% or less of sulfur atoms by weight. As such, there are potential derivatives of cellulose acetate that may provide enhanced properties for many of the consumer applications of cellulose acetate.
  • the present invention relates to synthetic polymers and, in particular, to substituted cellulose acetates, and methods of use thereof.
  • the present invention provides diapers comprising: an inner layer comprising an absorbent core comprising a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate; and an outer layer.
  • the present invention provides bandages comprising: an absorbent layer comprising a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate; and a strip designed to place the absorbent layer in contact with a wound.
  • the present invention provides potting soil compositions comprising: an organic compost; and an absorbent composition comprising a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate.
  • the present invention provides amended soil compositions comprising: a soil composition; and a water retention additive comprising a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate.
  • the present invention provides articles comprising: a nonwoven layer that comprises fibers from a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate.
  • the present invention provides methods comprising: providing a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate; and placing the substituted cellulose acetate in an absorbent article.
  • a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate; and placing the substituted cellulose acetate in an absorbent article.
  • the present invention provides methods comprising: providing an absorbent material comprising a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate; and placing the absorbent material in a diaper.
  • FIG. 1 shows a biodegradability plot of cellulose acetate with varying degrees of substitution.
  • FIG. 2 shows water absorbency data as described in Example 3.
  • FIG. 3 shows water absorbency data as described in Example 3.
  • FIG. 4 shows water absorbency data as described in Example 3.
  • FIG. 5 shows water absorbency data as described in Example 3.
  • the present invention relates to synthetic polymers and, in particular, to substituted cellulose acetates, and methods of use thereof.
  • the present invention provides compositions, methods, and processes related to substituted cellulose acetates that have a number of advantageous and/or desirable properties.
  • the substituted cellulose acetates of the present invention may be utilized in a variety of applications including a number of consumer products, especially where absorbency, adhesiveness, and/or degradability, may be useful.
  • substituted cellulose acetate generally refers to a cellulose acetate that has at least one polar substituent substituted on the hydroxyl group of a cellulose polymer.
  • a “polar substituent” is a non-acetyl chemical moiety comprising an electronegative atom (e.g., oxygen) bonded to a nonmetal (e.g., sulfur, phosphorus, boron, and chlorine) atom.
  • substituted cellulose acetate composition having relatively high weight percentage of at least one nonmetal atom corresponding to a polar substituent having a relatively high degree of substitution can be provided.
  • the percentage weight of nonmetal atoms may be adjusted and/or modified to yield or enhance various properties of substituted cellulose acetate as described herein.
  • the substituted cellulose acetates of the present invention are, in some embodiments, versatile (i.e., possess many distinct desirable chemical and physical properties) and environmentally friendly (i.e., made from renewable sources, degradable, biodegradable, etc.) materials suitable for use in a number of consumer products.
  • “degradable” refers to the ability of a material to decompose and/or break down into simpler parts.
  • biodegradable refers to the ability of a material to degrade by the action of living things. Depending on the application, the definition of “biodegradable” may be subject to the results of standard tests, for example, the Organisation for Economic Co-operation and Development (OECD) testing protocols.
  • OECD Organisation for Economic Co-operation and Development
  • a substituted cellulose acetate of the present invention can provide new or enhanced chemical and/or physical properties.
  • certain polar substituents e.g., sulfate
  • hydrophilicity of the substituted cellulose acetate can increase the hydrophilicity of the substituted cellulose acetate as well as increase the potential for electrostatic interaction.
  • the substituted cellulose acetate compositions which are described in more detail hereinafter, have certain advantageous properties and commercial roles (e.g., as an adhesive, chemical stabilizer, absorbent) that may be imparted or enhanced based on the percentage weight of nonmetal atom present.
  • tuning the percentage weight of the nonmetal atom may remove or reduce an undesirable quality or property in the substituted cellulose acetate.
  • a substituted cellulose acetate may be described by the concentration of its polar substituents which, in turn, may be specified in terms of degree of substitution of the polar substituent (i.e., average number of substituent per glucose monomer unit) or as a percentage weight of the nonmetal (e.g., sulfur, phosphorus, boron, and chlorine) atom present relative to the total weight of the substituted cellulose acetate.
  • degree of substitution of the polar substituent i.e., average number of substituent per glucose monomer unit
  • the nonmetal e.g., sulfur, phosphorus, boron, and chlorine
  • the percentage weight of the nonmetal atom in a substituted cellulose acetate may range from about 0.01% to about 25%, which corresponds to a cellulose acetate that has few polar substituents (in some cases, significantly and surprisingly more than typically prepared cellulose acetate) and a cellulose acetate that has been exhaustively substituted. While the present invention is preferably practiced by specifying the percentage weight of the nonmetal of the polar substituent, the present invention may be equivalently practiced by specifying the degree of substitution of the polar substituent or other similar measures of concentration. The degree of substitution of a polar substituent may range from about 0.005 to about 3.
  • substituted cellulose acetate having a polar substituent in a wide range of consumer products.
  • the substituted cellulose acetate compositions of the present invention may be used, among many things, as an effective absorbent, an adhesive, a chemical stabilizer, and a stabilizing film forming agent.
  • the substituted cellulose acetate of the present invention may go from a water-soluble material to a water-swellable material.
  • the water-swellable substituted cellulose acetate composition may be used as a degradable coating to encapsulate, for example, a pharmaceutical composition so that the release of the pharmaceutical composition is delayed in the body.
  • Other properties that may be adjusted include, but are not limited to, solubility in certain solvents, ability to stabilize emulsions, adhesiveness to various surfaces, and biodegradability. These properties may be further adjusted by modifying the percentage weight of the nonmetal atom of the polar substituent present in the substituted cellulose acetate as needed. A person of ordinary skill in the art should be able to modify the percentage weight of nonmetal as necessary in order to practice the many embodiments of the present invention.
  • modifying the degree of substitution of acetate may also yield or enhance certain properties of the substituted cellulose acetate.
  • the water-soluble substituted cellulose acetate has a degree of substitution of acetate between about 0.4 to about 1.
  • the water-swellable substituted cellulose acetate has a degree of substitution of acetate between about 1 to about 2.
  • the appropriate solvent system may change.
  • water is an appropriate solvent.
  • an organic solvent is required. The degree of substitution may be varied so that a solvent system can be selected that is appropriate to the targeted end use.
  • the degree of substitution of a polar substituent may be kept relatively fixed while the degree of substitution of acetate is adjusted. In some embodiments, the combination of adjusting the degree of substitution of polar substituent and degree of substitution of acetate provides the substituted cellulose acetate with the desired properties. In some embodiments, the range of degree of substitution of polar substituent may affect the range of degree of substitution of acetate that is needed to provide the substituted cellulose acetate with the desired properties. In some embodiments, the range of degree of substitution of acetate may affect the range of degree of substitution of polar substituent that is needed to provide the substituted cellulose acetate with the desired properties.
  • substituted cellulose acetate of the present invention are wide ranging and include, but are not limited to, household articles such as buttons, glasses, linings, blouses, dresses, wedding and party attire, home furnishings, draperies, upholstery, slip covers, and the like.
  • Other commercial uses include filters including cigarette, ink reservoirs, playing cards, and the like, and high absorbency products such as diapers and surgical products.
  • the substituted cellulose acetates of the present invention have a water absorption capacity several times (for example, from about 8 times to about 24 times) its weight in an aqueous-based fluid (e.g., water, saline solution, etc.) depending on the percentage weight of the nonmetal atom present on the substituted cellulose acetate.
  • an aqueous-based fluid e.g., water, saline solution, etc.
  • the substituted cellulose acetates of the present invention may be effective as an adhesive, able to glue a variety of substrates including, but not limited to, cardboard, plastic, paper, glass, wood, hemp, saw dust, composites (e.g., fiber reinforced composites), wood shavings and the like. It is also believed that the substituted cellulose acetates of the present invention may be an effective chemical/colloidal stabilizer, able to stabilize various emulsion mixtures.
  • the substituted cellulose acetates of the present invention may be used as a stabilizing film forming agent to promote the formation of film of a given mixture.
  • the formed film may be clear.
  • the substituted cellulose acetate may exist in many different forms and be utilized in many different ways.
  • the substituted cellulose acetate may be fibers, woven fabrics, nonwoven fabrics, tows or tow bands (open or non-open), flakes, foams, emulsions, films, gels, dispersions, solutions, pastes, suspensions, and combinations thereof.
  • the substituted cellulose acetate may be used as coatings, additives, films, layers, cores, and the like.
  • the present invention also provides processes for forming substituted cellulose acetate into various shapes of substituted cellulose acetate (e.g., substituted cellulose acetate tow). These processes typically put the substituted cellulose acetate in a better form to be utilized in certain applications.
  • fibers of substituted cellulose acetate may have the particularly desirable properties of being able to selectively absorb and remove levels of certain organic chemicals; being water-soluble or water-swellable; having a high surface area; and being compatible with dyes. It is also believed that the fibers of substituted cellulose acetate may have resistance to mold and mildew.
  • a substituted cellulose acetate may be particularly desirable in textile applications.
  • cellulose acetates having at least one polar substituent derivatives of cellulose acetates having at least one polar substituent may also be used in accordance with any of the compatible embodiments of the present invention.
  • Derivatives of cellulose acetate may include, but are not limited to, cellulose acetate esters, cellulose acetate mixed esters, and the like.
  • Suitable examples of cellulose acetate esters include, but are not limited to, cellulose acetate propionates, cellulose acetate butyrates, and the like.
  • the degree of esterification of the cellulose acetate esters will depend, at least in part, on the particular application and will be apparent to those of ordinary skill in the art.
  • the substituted cellulose acetate of the present invention may be characterized by having a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, and boron; wherein the nonmetal is present in at least 0.01% by weight of the substituted cellulose acetate.
  • the nonmetal may be present in no more than about 25% by weight of the substituted cellulose acetate. Without being limited by theory, it is believed the upper limit of 25% by weight corresponds to a fully substituted cellulose derivative (e.g., sulfate).
  • the exact range of nonmetal weight percentage will depend on, among other things, the chemical makeup of the polar substituent.
  • the degree of substitution of acetate will be from about 0.05 to about 3, preferably from about 0.4 to about 2.
  • the ratio of degree of substitution of acetate to degree of substitution of polar substituent may be adjusted to produce or enhance the desired property of a substituted cellulose acetate of the present invention.
  • the DS of acetate is higher than the DS of the polar substituent.
  • the substituted cellulose acetate may further comprise or be mixed with a plasticizer.
  • plasticizers include, but are not limited to, glycerin, glycerin esters (including mono, di or triacetyl glycerin and glycerin esters), polyethylene glycol, diethylene glycol, propylene glycol, dimethyl sulfoxide, glycerol triacetate, triethylene glycol diacetate, derivatives thereof, combinations thereof, and mixtures thereof.
  • the plasticizer comprises a plasticizer selected from the group consisting of esters of saturated dibasic acids, esters of saturated polyhydric alcohols, fatty acid esters, sulfonamide resins, derivatives thereof, and combinations thereof.
  • Plasticizers may be added to the substituted cellulose acetate in order to lower the glass transition temperature (T g ) and the melting point of the composition. Plasticizers typically function to facilitate processing and to increase the flexibility and toughness of the final product. It is also believed that certain plasticizers (e.g., ether ester, simple ester type, etc.) may increase the capacity of substituted cellulose acetate filters for phenol removal which is a useful property in cigarette filters.
  • T g glass transition temperature
  • plasticizers typically function to facilitate processing and to increase the flexibility and toughness of the final product. It is also believed that certain plasticizers (e.g., ether ester, simple ester type, etc.) may increase the capacity of substituted cellulose acetate filters for phenol removal which is a useful property in cigarette filters.
  • the polar substituent may be selected from the group consisting of sulfates, phosphates, borates, carbonates, and combinations thereof. In some embodiments, the polar substituent is present in at least about 0.03% by weight of the substituted cellulose acetate. In some embodiments, the nonmetal of the polar substituent is present in no more than about 75% by weight of the substituted cellulose acetate. The exact range of polar substituent weight percentage will depend on, among other things, the chemical makeup of the polar substituent.
  • the substituted cellulose acetate may have properties that may be imparted or enhanced by increasing or decreasing the concentration of polar substituents or nonmetal atoms.
  • the substituted cellulose acetate may be water-soluble.
  • the substituted cellulose acetate may be water-swellable.
  • the substituted cellulose acetate may be water resistant.
  • water-swellable materials are often marked by their ability to absorb water and are used as water-stopping material, water-retaining material, material supplies, and the like.
  • the substituted cellulose acetate may be degradable.
  • the substituted cellulose acetate may be biodegradable.
  • the substituted cellulose acetate of the present invention may be utilized as an absorbent material for a number of consumer applications.
  • the present invention provides, in some embodiments, diapers comprising an absorbent core comprising the substituted cellulose acetate of the present invention and an outer layer.
  • the diaper may further comprise a distribution layer designed to transfer wetness to the absorbent core and/or an outer shell that covers at least a portion of the absorbent core.
  • the distribution layer is interposed between the absorbent core and the outer layer. In some embodiments the distribution layer may be waterproof.
  • the outer layer surrounds the absorbent core. In some embodiments, the outer layer is waterproof. In some embodiments, the outer layer is configured to receive an insertion of the absorbent core. The outer layer may also be colored or feature ornamental designs that increases the visual attractiveness of the diaper. In some embodiments, the outer layer is configured with an opening to receive an insertion of an absorbent core. In some embodiments, the outer layer may be reusable.
  • the outer layer is made from a material comprising a material selected from the group consisting of polyethylene, nonwoven film, composite film, cloth, and combinations thereof.
  • the diaper may be disposable. In some embodiments, at least a portion of the diaper may be reusable.
  • the present invention provides, in some embodiments, bandages comprising an absorbent layer comprising a substituted cellulose acetate of the present invention and a strip designed to maintain the absorbent layer in contact with a wound.
  • the absorbent layer further comprises an active ingredient selected from the group consisting of antibiotics, analgesics, antipyretics, antimicrobials, antiseptics, antiallergies, anti-acne, anesthetics, anti-inflammatories, hemostats, cosmetics, vitamins, vasodilators, emollients, pH regulators, antipruritics, counterirritants, antihistamines, steroids, and combinations thereof.
  • the antiseptic may comprise at least one transition metal.
  • Suitable examples of a transition metal include, but are not limited to, aluminum, nickel, copper, zinc, titanium, iron, and silver.
  • the wound is an incision, a laceration, an abrasion, a puncture wound, a penetration wound, or any combinations of these.
  • the strip may be elastic. In some embodiments, the strip may be adhesive. In some embodiments, the strip comprises a material selected from the group consisting of: woven fabric, nonwoven fabric, plastic, latex, and combinations thereof.
  • the cigarette filter materials of the present invention comprise a segmented filter or a section of a filter comprising a substituted cellulose acetate of the present invention.
  • the cigarette filter materials of the present invention further comprise a conventional secondary cellulose diacetate.
  • the cigarette filter materials further comprise a plasticizer.
  • the substituted cellulose acetate should increase the degradability of the cigarette filter material.
  • plasticizers for use with cigarette filter material related embodiments include phthalate, acetyl triethyl citrate, triethyl citrate, acetyltributyl citrate, dibutylsebacate, triacetin, glyceryl triacetate, polyethylene glycol, propylene glycol, and glycerin.
  • the substituted cellulose acetate may be a tow. In some embodiments, the substituted cellulose acetate is formed in a rod shape.
  • the smoking devices of the present invention comprise a smokeable substance and a cigarette filter that comprises a substituted cellulose acetate filament of the present invention.
  • a “smokeable substance” includes anything (e.g., tobacco) that may be burned and its smoke can be tasted or inhaled.
  • tobaccos may be utilized in any number of different forms including, but not limited to, dried, fermented, cured, cut, and the like.
  • a smoking device may comprise a cigar, a pipe, a cigarette, a vaporizer, and the like.
  • the coated seeds of the present invention comprise a seed that is coated with a coating that comprises a substituted cellulose acetate of the present invention.
  • the coated seeds further comprise a secondary growth augmentation coating.
  • Suitable examples of secondary growth augmentation coating may be selected from the group consisting of primary nutrients, secondary nutrients, hormones, insecticides, pesticides, herbicides, fungicides, bactericides, pigments, binders, surfactants, glidants, and combinations thereof.
  • Suitable examples of primary nutrients for use in conjunction with some embodiments of the present invention may include, but are not limited to, ammonium nitrate, urea, ammonium phosphate, ammonium sulfate, urea phosphate, ammonium molybdate, potassium nitrate, potassium phosphate, potassium hydroxide, potassium sulfate, and potassium chloride.
  • Suitable examples of secondary nutrients are selected from the group consisting of magnesium sulfate, calcium nitrate, sodium borate, magnesium nitrate, chelated complex of copper, calcium, iron, zinc, magnesium, manganese, ammonium molybdate, sodium molybdate, benzoic acid, and salicylic acid.
  • Suitable examples of binders for use in conjunction with some embodiments of the present invention may include, but are not limited to, methylcellulose, carboxymethylcellulose, hydroxymethylcellulose, hydroxypropylcellulose, polyvinyl alcohol, polyvinyl acetate, povidone, copolyvidone, derivatives thereof, and combinations thereof.
  • Suitable examples of surfactants for use in conjunction with some embodiments of the present invention may include, but are not limited to, lecithin, sodium lauryl sulfate, polysorbate 60, polysorbate 80, polyoxethylene polyoxypropylene block copolymer, derivates thereof, and combinations thereof.
  • Suitable examples of pigments for use in conjunction with some embodiments of the present invention may include, but are not limited to, titanium dioxide, iron oxide, natural pigments, natural dyes, FD&C colorants, D&C lakes, derivatives thereof, and combinations thereof.
  • Suitable examples of glidants for use in conjunction with some embodiments of the present invention may include, but are not limited to, talc, colloidal silicon dioxide, stearic acid, derivatives thereof, and combinations thereof.
  • Suitable examples of herbicides for use in conjunction with some embodiments of the present invention may include, but are not limited to, glyphosate, dicamba, alanchlor, meolachlor, oxabetrinil, thiocarbamate 5-ethyl-N,N-dipropyl-thiocarbamate, acetochlor, derivatives thereof, and combinations thereof.
  • Suitable examples of antidotal compounds for use in conjunction with some embodiments of the present invention may include, but are not limited to, fluorazole, cyometrinil, N,N-diallyl dichloroacetamide, derivatives thereof, and combinations thereof.
  • Suitable examples of fungicide, bactericide, insecticide, and pesticide for use in conjunction with some embodiments of the present invention may include, but are not limited to, inorganic coppers, organic coppers, heavy metal compounds, propenoic acids, oximine ethers, substituted oximine ethers, derivatives thereof, and combinations thereof.
  • Suitable examples of plant hormones for use in conjunction with some embodiments of the present invention may include, but are not limited to, auxins, gibberellic acids, cytokines, derivatives thereof, and combinations thereof.
  • the coated pharmaceutical compositions of the present invention comprise a pharmaceutical composition that is coated with a coating that comprises a substituted cellulose acetate of the present invention.
  • the pharmaceutical composition for use in conjunction with some embodiments of the present invention may include, but are not limited to, analgesics, anti-inflammatory agents, anti-arrhythmic agents, anti-asthma agents, anti-bacterial agents, anti-viral agents, anti-coagulants, anti-dementia agents, anti-depressants, anti-diabetics, anti-hypertensive agents, anti-malarials, anti-migraine agents, anti-muscarinic agents, anti-neoplastic agents, immunosuppressants, anti-protozoal agents, anti-thyroid agents, anti-tussives, anxiolytics, sedatives, hypnotics, neuroleptics, neuro-protective agents, beta blockers, cardiac inotropic agents, cell adhesion inhibitors, corticosteroids, cytokine receptor activity modulators, diuretics, anti-parkinsonian agents, gastrointestinal agents, histamine H-receptor antagonists, keratolytics,
  • the pharmaceutical composition for use in conjunction with some embodiments of the present invention may include, but are not limited to, pseudoephedrine, phenylpropanolamine, phenylephrine, ephedrine, dextromethorphan, chlorphedianol, carbetapentane, caramiphen, noscapine, diphenhydramine, codeine, menthol, hydrocodone, hydromorphone, fominoben, glyceryl guaiacolate, terpin hydrate, ammonium chloride, N-acetylcysteine, bromhexine, ambroxol, chlorpheniramine, brompheniramine, dexchlorpheniramine, dexbrompheniramine, tripolidine, azatadine, doxylamine, tripelennamine, cyproheptadine, hydroxyzine, elemastine, carbinoxamine, phenindamine, bromodiphen
  • kits for detection of an analyte comprising a reporter molecule that is coated with a coating that comprises a substituted cellulose acetate of the present invention.
  • the reporter molecule for use in conjunction with some embodiments of the present invention may include, but are not limited to, an antibody, a protein, an enzyme, a peptide, a nucleic acid, a small molecule, a fluorophore, derivatives thereof, and combinations thereof.
  • the coating is water-soluble or water-swellable.
  • the coating provides a protective layer that can delay or prevent the degradation (e.g., denaturation, cleavage) of the reporter molecule during storage.
  • the coated stents of the present invention comprise a stent having an outer coating layer that comprises a substituted cellulose acetate of the present invention and an inner coating layer that comprises a pharmaceutical composition.
  • the stent comprises a shape-memory material.
  • shape-memory material for use in conjunction with some embodiments of the present invention may include, but are not limited to, zinc alloys, copper alloys, gold alloys, iron alloys, copper-zinc-aluminum-nickel alloys, copper-aluminum-nickel alloys, and nickel-titanium alloys.
  • the stent comprises a polymer.
  • Suitable examples of polymer for use in conjunction with some embodiments of the present invention may include, but are not limited to, fibrin, polylactic acid, silicones, polyurethanes, polyesters, vinyl homopolymers, vinyl copolymers, acrylate homopolymers, acrylate copolymers, polyethers, cellulosics, derivatives thereof, and combinations thereof.
  • the pharmaceutical composition is selected from the group consisting of: glucocorticoids, heparin, hirudin, tocopherol, angiopeptin, aspirin, growth factors, oligonucleotides, anti-platelet agents, anti-coagulant agents, anti-mitotic agents, anti-oxidants, anti-metabolite agents, anti-inflammatory agents, and combinations thereof.
  • the potting soil compositions of the present invention comprise an organic compost and an absorbent composition comprising a substituted cellulose acetate of the present invention.
  • the potting soil composition may further comprise at least one component selected from the group consisting of loam, diatomaceous earth component, Perlite component, and combinations thereof.
  • loam comprises components selected from the group consisting of sand, silt, clay, and combinations thereof.
  • the diatomaceous earth component comprises at least one component selected from the group consisting of diatomaceous earth, phosphate, magnesium, potassium, nitrogen, and combinations thereof.
  • the amended soil compositions of the present invention comprise a soil composition and a water retention additive comprising a substituted cellulose acetate of the present invention.
  • the amended soil composition may further comprise an additive selected from the group consisting of sand, silt, clay, calcined clay, iron oxide, dry resin, and combinations of these.
  • Suitable dry resins for use in conjunction with some embodiments of the present invention may include, but are not limited to, acrylic polymer, polyvinyl acetate polymer, vinyl acetate copolymer, derivatives thereof, and combinations thereof.
  • the drilling fluids of the present invention comprise a base fluid and a viscosifier comprising a substituted cellulose acetate of the present invention.
  • the drilling fluid may further comprise an additive selected from the group consisting of fluid loss control agents, clay inhibitors, lubricants, weighting agents, viscosifiers, and any combinations thereof.
  • the base fluid may be an aqueous fluid, an oil-based fluid, a synthetic fluid, or an emulsion.
  • the present invention provides articles comprising a nonwoven layer that comprises fibers from a substituted cellulose acetate of the present invention.
  • the nonwoven layer may include, but are not limited to, diapers, feminine hygiene products, wet wipes, bandages, disposable towels, disposable slippers, isolation gowns, surgical gowns, surgical drapes and covers, surgical scrub suits, caps, filters (e.g., HEPA filters; water, coffee, tea bags; liquid cartridges, vacuum bags; geotextiles (e.g., geomembranes); carpet backing; and envelopes.
  • filters e.g., HEPA filters; water, coffee, tea bags; liquid cartridges, vacuum bags; geotextiles (e.g., geomembranes); carpet backing; and envelopes.
  • the present invention provides a process for making a substituted cellulose acetate tow comprising spinning a dope comprising a solution of cellulose diacetate and substituted cellulose acetate of the present invention; and solvent; taking-up the as-spun substituted cellulose acetate filaments; forming a tow from the substituted cellulose acetate filaments; crimping the tow; conditioning the crimped tow; and baling the dried crimped tow.
  • the process may further comprise the step of lubricating the substituted cellulose acetate filaments.
  • the solvent is water, acetone, methylethyl ketone, methylene chloride, dioxane, dimethyl formamide, methanol, ethanol, glacial acetic acid, supercritical CO 2 , any suitable solvent capable of dissolving the aforementioned polymers, or any combination thereof.
  • a solvent for cellulose acetate may be an acetone/methanol mixture.
  • the substituted cellulose acetate is spun in a spinneret.
  • the spinneret comprises holes. These holes may be of any shape that is compatible with one or more embodiments of the present invention.
  • the spinneret design and/or spinning parameters may affect the rate at which the solvent evaporates from the filament, which may affect the size, cross-sectional shape, strength, and processability of the filaments.
  • a spinneret may comprise a plurality of holes spaced at least 0.070 inches apart.
  • spinnerets for use in conjunction with the present invention may comprise a plurality of extrusion holes in a donut configuration.
  • extrut configuration refers to any shape (circular, ovular, polygonal, triangular, and the like) having a void in the middle, wherein the void does not have holes for extrusion.
  • holes and “extrusion holes,” when used in conjunction with a spinnerets design, may be used interchangeably referring generally to openings through which the dope is extruded.
  • extrusion holes may be tapered, e.g., countersinks, with capillary exits. Tapering may be at a constant angle or at more than one angle. In some embodiments, extrusion holes within a single spinneret may have different tapering angles.
  • the extrusion holes and/or capillary exits may have a cross-sectional shape that produces a desired filament cross-sectional shape.
  • extrusion hole and/or capillary exit cross-sectional shapes may include, but not be limited to, circular, substantially circular, ovular, substantially ovular, crescent, multi-lobal, polygonal (e.g., like tripods, tetrapods, stars, triangles, squares, trapezoids, pentagons, hexagons, and so on with sides of even lengths or varying lengths), polygonal with rounded corners, and any hybrid thereof.
  • a spinneret may comprise at least two different cross-sectional shaped extrusion holes and/or capillary exits. In some embodiments, a spinneret may comprise at least two different size extrusion holes and/or capillary exits. In some embodiments, the size and/or cross-sectional shape of an extrusion hole may vary from that of the corresponding capillary exit.
  • the spinning parameters may include extruding filaments at a drawdown ratio (fiber exit speed to take-up speed) ranging from about 0.7 to about 1.6.
  • the methods of the present invention comprise providing substituted cellulose acetate of the present invention and placing the substituted cellulose acetate in an absorbent article.
  • the absorbent article may be any article (e.g., a garment, a gel, a piece of furniture, etc.) that may utilize an absorbent material. Suitable examples of absorbent articles may include, but are not limited to, diapers, incontinence garments, bandages, surgical pads, hot and cold therapy packs, water beds, artificial snow, and combinations thereof.
  • the absorbent article is disposable and/or degradable.
  • the substituted cellulose acetate may be placed in the inner portion of an absorbent article. In some embodiments, the substituted cellulose acetate may be placed on the outer portion of an absorbent article. In some embodiments, the substituted cellulose acetate may be part of the outer portion of an absorbent article.
  • plaque is not intended to limit the present invention to any specific mode of action.
  • the methods of the present invention comprise coating a seed with a coating comprising a substituted cellulose acetate of the present invention.
  • the coating may further comprise at least one ingredient selected from the group consisting of a plasticizer, a binder, a wax, a stabilizer, and a colorant.
  • methods of the present invention comprise coating a pharmaceutical composition with a coating comprising a substituted cellulose acetate of the present invention.
  • the coating may further comprise an additive selected from the group consisting of a plasticizer, an annealing agent, an emulsifying agent, an emulsion stabilizer, and combinations of these.
  • the annealing agent comprises a water-soluble polymer selected from the group consisting of hydroxypropyl cellulose, hydroxypropyl methyl cellulose, methyl cellulose, methyl ethyl cellulose, polyvinylpyrrolidone, sodium carboxymethylcellulose, derivatives thereof, and combinations thereof.
  • the methods of the present invention comprise providing an adhesive comprising a substituted cellulose acetate of the present invention and applying the adhesive on a surface.
  • the surface may be selected from the group consisting of wood, plastic, paper, glass, cardboard, and combinations of these.
  • the adhesive is a dispersion.
  • the adhesive may further comprise a solvent and/or an additive.
  • the solvent may be aqueous. In some embodiments, the solvent may be a mixture such as an organic/water solvent. In some embodiments, the solvent may be present in about 40% to about 99% by weight of the adhesive.
  • the additive comprises an additive selected from the group consisting of multi-valent salts (e.g., zirconium salts such as zirconium carbonate), polyamide epichlorohydrin resins, aldehydes (e.g., glyoxal, gluteraldehyde, hydroxyadipaldehyde), formaldehyde crosslinkers (e.g., zero-formaldehyde, low-formaldehyde crosslinkers), polyvinyl acetates, polyvinyl alcohols, polystyrenes, polylactic acids, derivatives thereof, and combinations thereof.
  • multi-valent salts e.g., zirconium salts such as zirconium carbonate
  • polyamide epichlorohydrin resins e.g., aldehydes (e.g., glyoxal, gluteraldehyde, hydroxyadipaldehyde), formaldehyde crosslinkers (e.g., zero-formal
  • the present invention provides a paint composition
  • a paint composition comprising a pigment and a stabilizing film forming agent that comprises a substituted cellulose acetate of the present invention and coating a surface with the paint.
  • the paint may further comprise at least one element selected from the group consisting of: a solvent, a filler, an antifreeze additive, a catalyst, a thickener, an adhesion promoter, a UV stabilizer, a de-glossing agent, a biocide, and combinations thereof.
  • solvents include, but are not limited to, an aliphatic solvent, an aromatic solvent, an alcohol, a ketone, a hydrocarbon, an ester, a petroleum distillate, water, derivatives thereof, and combinations thereof.
  • pigments include pigments selected from the group consisting of clay, calcium carbonate, mica, silica, talc, titanium dioxide, derivatives thereof, and combinations thereof.
  • Suitable examples of filters include fillers selected from the group consisting of: diatomaceous earth, talc, lime, barite, clay, derivatives thereof, and combinations of these.
  • the present invention provides a method of providing a paint comprising a pigment; and a stabilizing film forming agent that comprises a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate; and coating a surface with the paint.
  • a stabilizing film forming agent that comprises a substituted cellulose acetate comprising a polar substituent that comprises an oxygen atom covalently bonded to a nonmetal selected from the group consisting of: sulfur, phosphorus, boron, and chlorine; wherein the nonmetal is present in at least about 0.01% by weight of the substituted cellulose acetate; and coating a surface with the paint.
  • the methods of the present invention comprise providing a stabilizing film forming agent comprising a substituted cellulose acetate of the present invention and adding the stabilizing film forming agent to an emulsion.
  • emulsion include, but are not limited to, cosmetic product, hair styling product, photographic film, cutting fluid, skin ointment, paste, balm, oil, wax, detergent, beverage, and combinations of these.
  • the methods of the present invention comprise providing a thickening agent comprising a substituted cellulose acetate of the present invention and adding the thickening agent to a food composition.
  • suitable food compositions may include, but are not limited to, soups, gravy, desserts, jellies, candies, and the like.
  • Substituted cellulose acetates with high sulfur content in accordance with one or more embodiments of the present invention were prepared and tested as a wood adhesive using INSTRON® (Model 3366) Lap Shear test.
  • the results, including the amount of sulfur in the solution are summarized in Tables 1A and 1B above.
  • Two small wooden blocks were glued together using a 10% aqueous solution of the adhesives and allowed to dry. The resulting blocks were difficult to separate (i.e., none of the blocks broke in the tensile testing setup used). When enough force was applied to separate the blocks, the wood fibers broke which suggests that the substituted cellulose acetate adhesive is as strong as the wood fibers.
  • Substituted cellulose acetate adhesives were also used to glue cardboard. The cardboard was also difficult to separate. Substituted cellulose acetate adhesives were optically clear and have a high gloss which may be desirable in commercial applications. Substituted cellulose acetate adhesives dried in less than 30 minutes at ambient conditions.
  • This Example shows, among many things, that substituted cellulose acetate with high sulfur content is effective as an adhesive on a variety of substrates.
  • This Example describes the synthesis of a sulfate substituted cellulose acetate of the present invention.
  • cellulose was acetylated in the presence of acetic anhydride and sulfuric acid.
  • the preparation of cellulose, acetic acid, acetic anhydride and sulfuric acid is similar to the preparation involved in a standard secondary cellulose acetate diacetate production.
  • the reagents were combined to initiate the acetylation reaction. This reaction was allowed to reach completion and then reacted with any excess anhydride by the addition of water.
  • the reaction rate and temperature may be closely monitored and varied to control certain polymer properties.
  • acetylated cellulose i.e., cellulose acetate
  • acetic acid without precipitation and subsequent redissolving steps.
  • thermogravimetric analysis a water-swellable cellulose acetate (low sulfur content) and substituted cellulose acetate (high sulfur content) were tested for their ability to absorb water using a thermogravimetric analysis (TGA).
  • TGA thermogravimetric analysis
  • Each sample was placed in a TGA system and subjected to the following temperatures. The samples were ramped to 110° C. at 20° C./min. The temperature was held at 110° C. for 30 minutes. The temperature was then ramped to 650° C. at 20° C./min. The sample gas was then switched to air and the temperature was held at 650° C. for 30 minutes. In each test run, the cellulose acetate samples were limited to less than 100 mg.
  • FIGS. 2-5 show the various TGA analysis runs measuring the water absorbency of high sulfate substituted cellulose acetate and low sulfate substituted cellulose acetate.
  • FIG. 2 shows a TGA analysis of water-saturated, water-swellable cellulose acetate (WSCA) 1036 RT-16 dry sample.
  • WSCA 1036 RT-16 is a high sulfate substituted cellulose acetate particulate sample containing approximately 0.5% of sulfur by weight of the cellulose acetate.
  • the temperature of the TGA system was then ramped to and held at 650° C., thus allowing the high sulfate substituted cellulose acetate to decompose.
  • WSCA 1036 RT-16 was able to absorb approximately 1440% water by weight as the dry sample or over 14 times its weight in water.
  • FIG. 3 shows TGA duplicate runs for two WSCA 1037 RT-16 dry samples.
  • the WSCA 1037 RT-16 is a low sulfur substituted cellulose acetate (the DS of acetates are similar).
  • the detected water absorption for the two samples were 76.91% and 81.31%, which corresponds to water to dry WSCA ratios of 3.35 and 4.37 respectively.
  • FIG. 4 shows TGA duplicate runs for two saline water ( ⁇ 0.9%) saturated WSCA 1036 (high sulfate) RT-16 samples.
  • the two samples contained 87.05% and 92.14% saline water which corresponded to water to dry WSCA ratios of 7.48 and 13.6 respectively.
  • FIG. 5 shows TGA duplicate runs for saline water ( ⁇ 0.9%) saturated WSCA 1037 RT-16 sample.
  • the two samples contained 78.31% and 83.91% saline water which corresponded to water to dry WSCA ratios of 3.72 and 5.46.
  • This Example shows, among many things, that a substituted cellulose acetate having a high sulfur content is able to absorb water (both deionized and saline) several times its weight.
  • water both deionized and saline
  • the high sulfur substituted cellulose acetate displayed superior water (both DI and saline) absorption.
  • the addition of zirconium can increase the strength required to break the bond formed by the cellose acetate adhesive compositions (substituted cellulose acetate with high sulfur content).
  • Table 3 shows results of lap shear testing of cellulose acetate adhesives 7 and 8 with ammonium zirconium carbonate (0.08% Zr), MW 140,000 polyvinyl acetate (14% of solid) and MW 150,000 polyvinyl alcohol (14% of solid).
  • the sulfur content of cellulose acetate adhesives 6, 7, and 8 are 620 mg/kg, 520 mg/kg, and 557 mg/kg respectively.
  • compositions and methods are described in terms of “comprising,” “containing,” or “including” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components and steps. All numbers and ranges disclosed above may vary by some amount. Whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range falling within the range is specifically disclosed. In particular, every range of values (of the form, “from about a to about b,” or, equivalently, “from approximately a to b,” or, equivalently, “from approximately a-b”) disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Biodiversity & Conservation Biology (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Organic Chemistry (AREA)
  • Materials For Medical Uses (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Cigarettes, Filters, And Manufacturing Of Filters (AREA)
  • Spinning Methods And Devices For Manufacturing Artificial Fibers (AREA)
  • Artificial Filaments (AREA)
US13/359,603 2012-01-27 2012-01-27 Substituted Cellulose Acetates and Uses Thereof Abandoned US20130192613A1 (en)

Priority Applications (9)

Application Number Priority Date Filing Date Title
US13/359,603 US20130192613A1 (en) 2012-01-27 2012-01-27 Substituted Cellulose Acetates and Uses Thereof
MX2014009100A MX2014009100A (es) 2012-01-27 2013-01-23 Acetatos de celulosa sustituida y usos de los mismos.
EP13741010.6A EP2811852A4 (en) 2012-01-27 2013-01-23 SUBSTITUTED CELLULOSE ACETATES AND USES THEREOF
KR1020147023496A KR20140116537A (ko) 2012-01-27 2013-01-23 치환된 셀룰로오스 아세테이트 및 그의 용도
CA2861037A CA2861037A1 (en) 2012-01-27 2013-01-23 Substituted cellulose acetates and uses thereof
CN201380006636.0A CN104105416A (zh) 2012-01-27 2013-01-23 取代纤维素醋酸酯及其用途
BR112014018021A BR112014018021A8 (pt) 2012-01-27 2013-01-23 Material de filtro de cigarro; dispositivo para fumar; e processo para produzir uma estopa de acetato de celulose substituído
JP2014554785A JP2015510395A (ja) 2012-01-27 2013-01-23 置換された酢酸セルロースおよびその使用方法
PCT/US2013/022625 WO2013112502A1 (en) 2012-01-27 2013-01-23 Substituted cellulose acetates and uses thereof

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US13/359,603 US20130192613A1 (en) 2012-01-27 2012-01-27 Substituted Cellulose Acetates and Uses Thereof

Publications (1)

Publication Number Publication Date
US20130192613A1 true US20130192613A1 (en) 2013-08-01

Family

ID=48869190

Family Applications (1)

Application Number Title Priority Date Filing Date
US13/359,603 Abandoned US20130192613A1 (en) 2012-01-27 2012-01-27 Substituted Cellulose Acetates and Uses Thereof

Country Status (9)

Country Link
US (1) US20130192613A1 (enrdf_load_stackoverflow)
EP (1) EP2811852A4 (enrdf_load_stackoverflow)
JP (1) JP2015510395A (enrdf_load_stackoverflow)
KR (1) KR20140116537A (enrdf_load_stackoverflow)
CN (1) CN104105416A (enrdf_load_stackoverflow)
BR (1) BR112014018021A8 (enrdf_load_stackoverflow)
CA (1) CA2861037A1 (enrdf_load_stackoverflow)
MX (1) MX2014009100A (enrdf_load_stackoverflow)
WO (1) WO2013112502A1 (enrdf_load_stackoverflow)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130196063A1 (en) * 2012-01-27 2013-08-01 Celanese Acetate Llc Substituted Cellulose Acetates and Uses Thereof
US20150027465A1 (en) * 2013-07-26 2015-01-29 Qiuming Liu Electronic cigarette
US9023757B2 (en) 2012-01-27 2015-05-05 Celanese Acetate Llc Substituted cellulose acetates and uses thereof
US9167830B2 (en) 2012-01-27 2015-10-27 Celanese Acetate Llc Substituted cellulose acetates and uses thereof
US20150361310A1 (en) * 2014-06-12 2015-12-17 Celanese Acetate Llc Adhesives that include highly-plasticized cellulose esters and methods and articles relating thereto
US20160025900A1 (en) * 2013-03-12 2016-01-28 Konica Minolta, Inc. Organic electroluminescent display device and method for manufacturing same
CN113068868A (zh) * 2021-03-24 2021-07-06 西安医学院 一种电子烟气溶胶滤过装置
CN114521673A (zh) * 2022-03-01 2022-05-24 湖北中烟工业有限责任公司 一种复合增塑剂及其制备方法和应用
CN115299636A (zh) * 2022-08-17 2022-11-08 中国烟草总公司郑州烟草研究院 一种卷烟滤嘴用功能吸附丸芯及其制备方法和烟支
EP4176960A1 (en) * 2013-09-06 2023-05-10 Massachusetts Institute of Technology Filter materials including functionalized cellulose
US20240359903A1 (en) * 2020-09-29 2024-10-31 Byeong Yeol AHN Tea bag

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109518518B (zh) * 2018-11-14 2021-02-02 湖北中烟工业有限责任公司 一种用于醋酸纤维沟槽纸的增塑剂及其制备方法
KR20220110257A (ko) 2019-12-13 2022-08-05 델포르트그룹 아게 흡연 제품용 수력-얽힘 필터 재료
CN111495307B (zh) * 2020-05-25 2021-12-10 新疆新仁化工有限公司 一种化工搅拌反应罐
JP7717848B2 (ja) * 2021-06-15 2025-08-04 デルフォルトグループ、アクチエンゲゼルシャフト 良好な膨張挙動を有する喫煙具用の水流絡合フィルタ材料

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2848343A (en) * 1955-05-04 1958-08-19 American Viscose Corp Process for producing cellulose triesters
US3045006A (en) * 1959-08-19 1962-07-17 Gevaert Photo Prod Nv Preparation of cellulose derivatives
US3057852A (en) * 1961-03-20 1962-10-09 Eastman Kodak Co Method of preparing heat stable cellulose acetate sulfates
US3538079A (en) * 1968-05-14 1970-11-03 Celanese Corp Method for the preparation of a water insoluble,basic dyeable,heat stable cellulose derivative
US3631023A (en) * 1970-02-02 1971-12-28 Celanese Corp Continuous esterification of cellulose
US20050187385A1 (en) * 1998-03-17 2005-08-25 Daicel Chemical Industries, Ltd. Cellulose acetate and dope containing the same
US20050287368A1 (en) * 2004-06-25 2005-12-29 Celanese Acetate Llc Cellulose acetate tow and method of making same
US20090000633A1 (en) * 2007-06-04 2009-01-01 Philip Morris Usa Inc. Cellulose acetate fiber modification

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2780228A (en) * 1954-03-03 1957-02-05 Eastman Kodak Co Filters for tobacco smoke comprising cellulose esters and ethers
US3897782A (en) * 1974-01-07 1975-08-05 Johnson & Johnson Body fluid barrier films
DE2607208A1 (de) * 1976-02-23 1977-08-25 Hoechst Ag Zigarettenfilter
JPS58118801A (ja) * 1982-01-05 1983-07-15 Asahi Chem Ind Co Ltd 超吸湿性セルロ−ス誘導体
JPH06199901A (ja) * 1993-01-06 1994-07-19 Teijin Ltd アセテート組成物
DE9309937U1 (de) * 1993-07-03 1993-08-26 Hoechst Ag, 65929 Frankfurt Filter für Tabakrauch, enthaltend Elektretfasern
JP3342763B2 (ja) * 1994-02-04 2002-11-11 ダイセル化学工業株式会社 シガレットフィルター素材
CN1219797C (zh) * 1994-09-22 2005-09-21 大世吕化学工业株式会社 纤维素衍生物
JP3390278B2 (ja) * 1994-12-05 2003-03-24 ダイセル化学工業株式会社 セルロースエステル組成物および成形品
JP2931810B1 (ja) * 1998-03-31 1999-08-09 日本たばこ産業株式会社 生分解性セルロースアセテート成形品およびたばこ用フィルタープラグ
ES2291193T3 (es) * 1999-03-11 2008-03-01 Japan Tobacco Inc. Construcciones biodegradables de acetato de celulosa y filtro para tabaco.
US6805134B2 (en) * 1999-04-26 2004-10-19 R. J. Reynolds Tobacco Company Tobacco processing
JP4659958B2 (ja) * 2000-09-28 2011-03-30 正光 舩岡 リグノフェノール誘導体を含むセルロース系組成物
US20050042470A1 (en) * 2003-08-22 2005-02-24 Vogler John William Cellulose ester based products and methods for making them
US7425289B2 (en) * 2004-06-25 2008-09-16 Celanese Acetate Llc Process of making cellulose acetate tow
GB2421707A (en) * 2004-12-29 2006-07-05 Acetate Products Ltd Polycomponent fibres for cigarette filters
JP4178164B2 (ja) * 2006-03-20 2008-11-12 群栄化学工業株式会社 複合繊維の製造方法
US20080053922A1 (en) * 2006-09-01 2008-03-06 Honsinger Charles P Jr Nanostructured materials comprising support fibers coated with metal containing compounds and methods of using the same
JP2008295316A (ja) * 2007-05-29 2008-12-11 Kokusai Yugo Kk 喫煙物
US9155335B2 (en) * 2007-12-17 2015-10-13 Celanese Acetate Llc Degradable cigarette filter

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2848343A (en) * 1955-05-04 1958-08-19 American Viscose Corp Process for producing cellulose triesters
US3045006A (en) * 1959-08-19 1962-07-17 Gevaert Photo Prod Nv Preparation of cellulose derivatives
US3057852A (en) * 1961-03-20 1962-10-09 Eastman Kodak Co Method of preparing heat stable cellulose acetate sulfates
US3538079A (en) * 1968-05-14 1970-11-03 Celanese Corp Method for the preparation of a water insoluble,basic dyeable,heat stable cellulose derivative
US3631023A (en) * 1970-02-02 1971-12-28 Celanese Corp Continuous esterification of cellulose
US20050187385A1 (en) * 1998-03-17 2005-08-25 Daicel Chemical Industries, Ltd. Cellulose acetate and dope containing the same
US20050287368A1 (en) * 2004-06-25 2005-12-29 Celanese Acetate Llc Cellulose acetate tow and method of making same
US20090000633A1 (en) * 2007-06-04 2009-01-01 Philip Morris Usa Inc. Cellulose acetate fiber modification

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9212290B2 (en) * 2012-01-27 2015-12-15 Celanese Acetate Llc Substituted cellulose acetates and uses thereof
US20130196063A1 (en) * 2012-01-27 2013-08-01 Celanese Acetate Llc Substituted Cellulose Acetates and Uses Thereof
US9023757B2 (en) 2012-01-27 2015-05-05 Celanese Acetate Llc Substituted cellulose acetates and uses thereof
US9167830B2 (en) 2012-01-27 2015-10-27 Celanese Acetate Llc Substituted cellulose acetates and uses thereof
US20160025900A1 (en) * 2013-03-12 2016-01-28 Konica Minolta, Inc. Organic electroluminescent display device and method for manufacturing same
US20150027465A1 (en) * 2013-07-26 2015-01-29 Qiuming Liu Electronic cigarette
US9596886B2 (en) * 2013-07-26 2017-03-21 Huizhou Kimree Technology Co., Ltd. Shenzhen Branch Electronic cigarette
EP4176960A1 (en) * 2013-09-06 2023-05-10 Massachusetts Institute of Technology Filter materials including functionalized cellulose
US20150361310A1 (en) * 2014-06-12 2015-12-17 Celanese Acetate Llc Adhesives that include highly-plasticized cellulose esters and methods and articles relating thereto
US20240359903A1 (en) * 2020-09-29 2024-10-31 Byeong Yeol AHN Tea bag
CN113068868A (zh) * 2021-03-24 2021-07-06 西安医学院 一种电子烟气溶胶滤过装置
CN114521673A (zh) * 2022-03-01 2022-05-24 湖北中烟工业有限责任公司 一种复合增塑剂及其制备方法和应用
CN115299636A (zh) * 2022-08-17 2022-11-08 中国烟草总公司郑州烟草研究院 一种卷烟滤嘴用功能吸附丸芯及其制备方法和烟支

Also Published As

Publication number Publication date
MX2014009100A (es) 2014-11-10
CN104105416A (zh) 2014-10-15
EP2811852A4 (en) 2015-12-23
EP2811852A1 (en) 2014-12-17
CA2861037A1 (en) 2013-08-01
KR20140116537A (ko) 2014-10-02
JP2015510395A (ja) 2015-04-09
BR112014018021A8 (pt) 2017-07-11
BR112014018021A2 (enrdf_load_stackoverflow) 2017-06-20
WO2013112502A1 (en) 2013-08-01

Similar Documents

Publication Publication Date Title
US9023757B2 (en) Substituted cellulose acetates and uses thereof
US9167830B2 (en) Substituted cellulose acetates and uses thereof
US20130192613A1 (en) Substituted Cellulose Acetates and Uses Thereof
CA2860943C (en) Substituted cellulose acetates and uses thereof
US9212290B2 (en) Substituted cellulose acetates and uses thereof
DE19505708A1 (de) Flächenförmige, superabsorbierende Gebilde
CN110025598A (zh) 一种具有缓释功能的交联载药聚乙烯醇/海藻酸钠复合纳米纤维膜的制备
JP2018059228A (ja) 耐水性繊維集合体及びその製造方法
Rusu et al. Cellulose-based hydrogels: design, structure-related properties, and medical

Legal Events

Date Code Title Description
AS Assignment

Owner name: CELANESE ACETATE LLC, TEXAS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:COMBS, MICHAEL T.;GARRETT, THOMAS S.;REEL/FRAME:027605/0397

Effective date: 20120113

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION

AS Assignment

Owner name: ACETATE INTERNATIONAL LLC, TEXAS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:CELANESE ACETATE LLC;REEL/FRAME:044391/0796

Effective date: 20171024