US20090261041A1 - Composition for Filtering and Removing Particles and/or Constituents from a Fluid - Google Patents
Composition for Filtering and Removing Particles and/or Constituents from a Fluid Download PDFInfo
- Publication number
- US20090261041A1 US20090261041A1 US12/373,753 US37375307A US2009261041A1 US 20090261041 A1 US20090261041 A1 US 20090261041A1 US 37375307 A US37375307 A US 37375307A US 2009261041 A1 US2009261041 A1 US 2009261041A1
- Authority
- US
- United States
- Prior art keywords
- filter
- adsorbent
- component
- filtration
- aid material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C12—BIOCHEMISTRY; BEER; SPIRITS; WINE; VINEGAR; MICROBIOLOGY; ENZYMOLOGY; MUTATION OR GENETIC ENGINEERING
- C12H—PASTEURISATION, STERILISATION, PRESERVATION, PURIFICATION, CLARIFICATION OR AGEING OF ALCOHOLIC BEVERAGES; METHODS FOR ALTERING THE ALCOHOL CONTENT OF FERMENTED SOLUTIONS OR ALCOHOLIC BEVERAGES
- C12H1/00—Pasteurisation, sterilisation, preservation, purification, clarification, or ageing of alcoholic beverages
- C12H1/02—Pasteurisation, sterilisation, preservation, purification, clarification, or ageing of alcoholic beverages combined with removal of precipitate or added materials, e.g. adsorption material
- C12H1/06—Precipitation by physical means, e.g. by irradiation, vibrations
- C12H1/063—Separation by filtration
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D37/00—Processes of filtration
- B01D37/02—Precoating the filter medium; Addition of filter aids to the liquid being filtered
- B01D37/025—Precoating the filter medium; Addition of filter aids to the liquid being filtered additives incorporated in the filter
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D39/00—Filtering material for liquid or gaseous fluids
- B01D39/14—Other self-supporting filtering material ; Other filtering material
- B01D39/20—Other self-supporting filtering material ; Other filtering material of inorganic material, e.g. asbestos paper, metallic filtering material of non-woven wires
- B01D39/2068—Other inorganic materials, e.g. ceramics
-
- C—CHEMISTRY; METALLURGY
- C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F1/00—Treatment of water, waste water, or sewage
- C02F1/28—Treatment of water, waste water, or sewage by sorption
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
- B01D2239/04—Additives and treatments of the filtering material
- B01D2239/0471—Surface coating material
- B01D2239/0478—Surface coating material on a layer of the filter
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
- B01D2239/12—Special parameters characterising the filtering material
- B01D2239/1291—Other parameters
-
- C—CHEMISTRY; METALLURGY
- C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F1/00—Treatment of water, waste water, or sewage
- C02F1/28—Treatment of water, waste water, or sewage by sorption
- C02F1/281—Treatment of water, waste water, or sewage by sorption using inorganic sorbents
-
- C—CHEMISTRY; METALLURGY
- C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F1/00—Treatment of water, waste water, or sewage
- C02F1/28—Treatment of water, waste water, or sewage by sorption
- C02F1/286—Treatment of water, waste water, or sewage by sorption using natural organic sorbents or derivatives thereof
-
- C—CHEMISTRY; METALLURGY
- C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F1/00—Treatment of water, waste water, or sewage
- C02F1/28—Treatment of water, waste water, or sewage by sorption
- C02F1/288—Treatment of water, waste water, or sewage by sorption using composite sorbents, e.g. coated, impregnated, multi-layered
-
- C—CHEMISTRY; METALLURGY
- C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F2209/00—Controlling or monitoring parameters in water treatment
- C02F2209/11—Turbidity
-
- C—CHEMISTRY; METALLURGY
- C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
- C02F2303/00—Specific treatment goals
- C02F2303/20—Prevention of biofouling
Definitions
- filter-aid materials and processes, systems, and methods using such filter-aid materials for filtering and removing particles and/or constituents from a fluid wherein the filter-aid material comprises at least one filterable composite adsorbent comprising at least one adsorbent component formed in-situ on at least one filtration component.
- filter-aid materials and processes, systems, and methods using such filter-aid materials for filtering and removing particles and/or constituents from a fluid wherein the filter-aid material comprises at least one filterable composite adsorbent comprising at least one filtration component (such as a siliceous material) and at least one adsorbent component (such as a precipitated silica gel) having an average particle size of less than about 1 micron. Also disclosed herein are the filter-aid materials described above, wherein the filter-aid material further comprises at least one additional filtration component.
- a filtration device is comprised of both a filter element, such as a septum, and a filter-aid material.
- the filter element may be of any form such that it may support a filter-aid material, for example a cylindrical tube or wafer-like structure covered with a plastic or metal fabric of sufficiently fine weave.
- the filter element may be a porous structure with a filter element void to allow material of a certain size to pass through the filtration device.
- the filter-aid material may comprise one or more filtration components, which for example may be inorganic powders or organic fibrous materials. Such a filter-aid material may be used in combination with a filter element to enhance filtration performance.
- filtration components for use in a filter-aid material are comprised of such materials as diatomite, perlite, and cellulose.
- the filter-aid material may initially be applied to the septum in a process known as “pre-coating.”
- Pre-coating generally involves mixing a slurry of water and filter-aid material and introducing the slurry in a stream flowing through the septum.
- a thin layer such as about 1.5 mm to about 3.0 mm, of filter-aid material will eventually be deposited upon the septum, thus forming the filtration device.
- filter cake As more and more particles and/or constituents are deposited on the filter cake, the filter cake may become saturated with debris to the point where fluid is no longer able to pass through the septum.
- body feeding is the process of introducing additional filter-aid material into the fluid to be filtered before the fluid reaches the filter cake. The filter-aid material will follow the path of the unfiltered fluid and will eventually reach the filter cake.
- the added filter-aid material Upon reaching the filter cake, the added filter-aid material will bind to the cake much the same way the filter-aid material bound to the septum during the pre-coating process. That additional layer of filter-aid material causes the filter cake to swell and thicken and increases the capacity of the cake to entrap additional debris.
- porous filtration components employ, for example, materials chosen from diatomite materials, expanded perlite, natural glasses, and cellulose materials as porous filtration components.
- materials have intricate and porous structures that may be particularly suited to the effective physical entrapment of particles in filtration processes.
- Those intricate and porous structures create networks of void spaces that may result in buoyant filtration media particles that have apparent densities similar to those of the fluids in which they are suspended.
- porous filtration components when improving the clarity of fluids.
- the porous filtration component is often used to remove undesired particles or constituents such as particulate matter from a fluid.
- porous filtration components may not be as well suited for the task of removing particulate matter from a fluid by the process of adsorption and are thus often times used in combination with an adsorbent component.
- Diatomite, perlite, rice-hull ash, and cellulose are some examples of filtration component materials that may be used for particle separation.
- Diatomite also known as diatomaceous earth, is a sediment enriched in biogenic silica in the form of siliceous skeleta of diatoms, a diverse array of microscopic, single-cell algae. Those frustules are sufficiently durable to retain much of their microscopic structure through long periods of geological time and through thermal processing.
- Diatomite products have an inherently intricate and porous structure composed primarily of silica.
- Perlite is a naturally occurring volcanic glass that may thermally expand upon processing.
- perlite may not be as intricate as diatomite and, consequently, perlite may be better suited for separating coarse micro-particulates from liquids having high solids loading.
- cellulose filtration component materials are generally produced by sulfite or sulfate processing of hardwoods and/or softwoods. Like perlite, cellulose filtration component materials may possess a less intricate structure than diatomite filtration component materials.
- Turbidity is the cloudiness or haziness of a fluid, where the haze may be caused by individual particles that are suspended in the fluid.
- Materials that may cause a fluid to be turbid include, for example, clay, silt, organic matter, inorganic matter, and microscopic organisms.
- Turbidity may be measured by using an instrument known as a nephelometer that emits a beam of light through a column of the fluid being tested. A detector positioned on the same side of the fluid column measures the amount of light reflected by the fluid. A fluid that contains a relatively large number of suspended particles will reflect a greater amount of light than a fluid containing fewer particles. Turbidity measured in this fashion may be quantified in Nephelometric Turbidity Units (“NTU”). In addition, Turbidity may also be measured using gravimetric methods.
- NTU Nephelometric Turbidity Units
- Filtration components are produced in grades over a wide range of permeability ratings. As the permeability of the filtration component decreases, the ability of the filter-aid material to remove small particles may increase, but often at the expense of a slower flow rate through the filter-aid material. Conversely, as the filtration component permeability increases, the ability of the filter-aid material to filter particles may decrease and, consequently, the fluid flow through the filter-aid material increases. The extent to which this takes place will depend upon the type and particle size distribution of the suspended particles being removed from the fluid.
- wet density is an indicator of a material's porosity. For example, wet density reflects the void volume available to entrap particulate matter in a filtration process and, consequently, wet density may be used to determine filtration efficiency. Percent porosity may be expressed by the following formula:
- filtration components with lower wet densities may result in products with greater porosity, and thus perhaps greater filtration efficiency, provided that the true density stays relatively constant.
- Typical wet densities for common filtration components may range from at least about 12 lb/ft 3 to about 30 lb/ft 3 or greater.
- adsorption is the tendency of molecules from an ambient fluid phase to adhere to the surface of a solid. This is not to be confused with the term “absorption,” which results when molecules from an ambient fluid diffuse into a solid, as opposed to adhering to the surface of the solid.
- an adsorbent component may have a relatively large surface area, which may imply a highly porous structure with a small adsorbent component particle size.
- porous adsorbent components in their un-reacted powder form, can have surface areas ranging up to several hundred m 2 /g.
- BET Brunauer, Emmett, and Teller
- One method of using an adsorbent component is to place the adsorbent component in contact with a fluid containing particles and/or constituents to be adsorbed, either to purify the fluid by removing the particles and/or constituents, or to isolate the particles and/or constituents so as to purify them.
- the adsorbent component containing the adsorbed particles or constituents is then separated from the fluid, for example by a conventional filtration process.
- Chill-proofing may comprise a process that employs at least one adsorption component and/or at least one filtration component to remove particles creating chill-haze in the beer.
- One form of chill-proofing involves, in one step, adding solid adsorbent components, such as silica gel, to the beer prior to packaging. The particles and/or constituents bind to the added adsorbent components, and then, in a second step, the adsorbent components are subsequently filtered from the beer, which is then packaged for storage, sale, and/or consumption.
- Filtration processes that implement both an adsorption step and a filtration step may be less efficient because of the difficulties of filtering the adsorbent components.
- the adsorbent components may occupy void spaces of the porous filter-aid material. That occupancy may reduce the permeability of the filter-aid material, leading to an overall lower filtration flow rate.
- U.S. Pat. No. 6,712,974 to Palm et al. describes a filterable composite adsorbent comprising at least one adsorbent component that is thermally sintered and/or chemically bonded to at least one filtration component.
- the filterable composite adsorbent of Palm retains the properties of both its adsorbent and filtration components, and binds them in a fashion so as they do not segregated upon physical distress, providing a means for adsorbing particles and/or constituents while filtering the fluid in a single step.
- Palm discloses a filterable composite adsorbent, it does not disclose a filterable composite adsorbent where the adsorbent components have a smaller average particle size, such as 1 micron or smaller.
- Such a small particle size may be achieved by methods other than sintering or chemical bonding that are not contemplated or suggested by Palm, for example, by in-situ precipitation.
- a smaller adsorbent component particle size may lead to an increased surface area and, consequently, an increased efficiency at removing particles and/or constituents from a fluid.
- the present invention overcomes the disadvantages of the prior art by providing an improved system and method for removing particles and/or constituents suspended in a fluid.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be prepared in a manner that retains the properties of both the filtration and adsorbent components.
- a filter-aid material may be prepared that comprises at least one filterable composite adsorbent that may be prepared by in-situ precipitation of at least one adsorbent component on the surface of at least one filtration component.
- such in-situ precipitation may result in the adsorbent component being intimately associated with the at least one filtration component such that the components may be less susceptible to separation by physical distress than a simple mixture of those components.
- an in-situ precipitation process may be used to create a filterable composite adsorbent having relatively small particle-sized adsorbent components, for example, less than 1 micrometer, on the surface of at least one filtration component. Consequently, the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may provide a greater adsorptive surface area than prior implementations, thereby enabling the filter-aid materials to adsorb a greater amount of particles and/or constituents from a fluid than was previously possible.
- the adsorptive effectiveness of the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be evidenced by a lower level of turbidity in the filtered fluid than could previously be achieved.
- the filterable composite adsorbent of the present invention may be formed using an in-situ process that precipitates an adsorbent component with a much smaller particle size and, consequently, a much higher BET surface area than a thermally sintered or chemically bonded composite.
- the larger BET surface area may result in a filterable composite adsorbent with a greater adsorptive capacity, allowing more particles and/or constituents to be adsorbed by a filter-aid material comprising the filterable composite adsorbent.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be more effective at removing particles and/or constituents from a fluid and may produce a fluid with a relatively low turbidity value.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may reduce the turbidity of the filtered fluid as compared with conventional techniques.
- the turbidity of a fluid filtered through the filter-aid materials comprising at least one filterable composite adsorbent described herein is less than the turbidity of a fluid filtered through a simple mixture having the same proportion of adsorbent and filtration components as the filter-aid material comprising at least one filterable composite adsorbent.
- the turbidity of a fluid filtered through the filter-aid materials comprising at least one filterable composite adsorbent may be less than the turbidity of a fluid filtered through a thermally sintered or chemically bonded mixture, having the same proportion of adsorbent and filtration components as the filter-aid material comprising at least one filterable composite adsorbent.
- the increased BET surface area of the filter-aid material comprising at least one filterable composite adsorbent as compared with known simple mixtures or thermally sintered or chemically bonded composites may allow for a greater adsorptive capacity, which may be due to the increased surface area on which particles and/or constituents may be adsorbed.
- the adsorbent component of the filter-aid material comprising at least one filterable composite adsorbent has an average particle size less than that of conventional filter-aid materials.
- the at least one adsorbent component has a particle size of less than about 1 micrometer (micron).
- the at least one adsorbent component has a particle size ranging from about 1 nanometer to about 100 nanometers.
- the at least one adsorbent component has a particle size ranging from about 1 nanometer to about 1 micron.
- the at least one adsorbent component of the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may have a larger BET surface area than was previously possible.
- the at least one adsorbent component may have a surface area ranging from about 50 to about 510 m 2 /g. Having a large adsorptive surface area may ensure that there are a relatively large number of sites where the particles and/or constituents to be removed can be adsorbed by the filter-aid materials comprising at least one filterable composite adsorbent.
- the filter-aid material comprising at least one filterable composite adsorbent disclosed herein may be prepared using an in-situ process that prevents aggregation and enables the at least one adsorbent component to form with smaller average particle sizes than could previously be achieved. Consequently, the filterable composite adsorbent may support larger adsorptive surface areas which, in turn, provide for more effective adsorption properties.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be produced with a wide range of permeabilities.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein have a permeability ranging from about 0.001 to about 1000 Darcies (“Da”).
- the permeability ranges from about 0.05 to about 10.00 Da.
- the range of permeability may allow for either a high flow rate or a lower flow rate. For instance, a lower flow rate may be about 1 ml/min cm 2 , while a high flow rate may be at least about 90 ml/min cm 2 . In one embodiment, the flow rate is about 1.2 ml/min cm 2 .
- the flow rate is about 4 ml/min cm 2 . In a further embodiment, the flow rate ranges from about 1.2 to about 4 ml/min cm 2 .
- Flow rate has a generally measurable pressure which varies with the flow rate. In one embodiment, the pressure is about 1.2 psi. In another embodiment, the pressure is about 15 psi. In a further embodiment, the pressure ranges from about 1.2 to about 15 psi. In yet another embodiment, the flow rate is from about 1.2 to about 4 ml/min cm 2 and the pressure is from about 1.2 to about 15 psi.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein also may exhibit various wet densities.
- the filter-aid material comprising at least one filterable composite adsorbent may have a wet density ranging from about 10 to about 25 lb/ft 3 .
- wet density reflects the void volume of the adsorbent component to entertain matter in the filtration process
- a lower wet density may indicate that the adsorbent component has a high void volume and thus can adsorb more particles and/or constituents in the fluid.
- the at least one adsorbent component of the filterable composite adsorbent may be a silica gel and the at least one filtration component may be chosen from natural glasses, such as expanded perlite, and biogenic silicas, such as diatomite.
- the at least one adsorbent component is a silica gel and the at least one filtration component is diatomite.
- the at least one adsorbent component is a silica gel and the at least one filtration component is perlite.
- other adsorbent and filtration components may be employed.
- the at least one filtration component may be chosen from biogenic silicas (such as rice hull ash and sponge spicules); natural glasses (such as pumice, expanded pumice, pumicite, expanded obsidian, and expanded volcanic ash); buoyant glasses; buoyant polymers; and celluloses.
- the filter-aid material comprises at least one additional filtration component mixed with the at least one filterable composite adsorbent.
- the at least one filtration component of the filterable composite adsorbent and the at least one additional filtration component of the filter-aid material may be the same or different.
- the at least one additional filtration component may be chosen from biogenic silicas (including, but not limited to, rice hull ash and sponge spicules); natural glasses (including, but not limited to, pumice, expanded pumice, pumicite, expanded obsidian, and expanded volcanic ash); buoyant glasses; buoyant polymers; and celluloses.
- the at least one additional filtration component is diatomite.
- the at least one additional filtration component is perlite.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be made in various forms.
- the filter-aid materials comprising at least one filterable composite adsorbent are in the form of a powder.
- the filter-aid materials may be in a form chosen from sheets, pads, and cartridges.
- the filter-aid materials are formed in-situ in the form chosen from rigid shapes, including but not limited to disks, cylinders, plates and polyhedrons.
- the filter-aid materials may be in a form chosen from monolithic supports and aggregate supports.
- the filter-aid materials are a form chosen from monolithic substrates and aggregate substrates.
- the filter-aid materials are pulverized.
- sodium silicate may be mixed in an aqueous solution with an acid, such as sulfuric acid, until the solution pH is sufficiently low enough to support silica gel precipitation in the presence of at least one porous filtration component. At least one filtration component is then added to the solution and stirred until the silica precipitate begins to gel. The addition of the acid causes the at least one adsorbent component, silica gel in this illustrative embodiment, to precipitate onto the surface of the at least one filtration component, thus forming the filterable composite adsorbent.
- an acid such as sulfuric acid
- the filterable composite adsorbent may further be mixed with at least one additional filtration component to form a final filter-aid material product.
- the at least one filtration component of the filterable composite adsorbent and the at least one additional filtration component of the filter-aid material are the same.
- the at least one filtration component of the filterable composite adsorbent and the at least one additional filtration component of the filter-aid material are different.
- One embodiment disclosed herein is a process for removing particles and/or constituents from a fluid comprising (i) providing at least one filter-aid material comprising at least one filterable composite adsorbent, (ii) pre-coating at least one filter element with the at least one filter-aid material comprising at least one filterable composite adsorbent, (iii) suspending the at least one coated filter element in a fluid containing the particles and/or constituents to be adsorbed.
- Another embodiment is a method of adsorbing and filtering particles and/or constituents from a fluid that comprises passing a fluid containing particles and/or constituents to be adsorbed through a filter-aid materials comprising at least one filterable composite adsorbent, as disclosed herein, that is supported on a septum.
- the method of adsorbing and filtering comprises passing a fluid containing particles and/or constituents to be adsorbed through a filter-aid materials comprising at least one filterable composite adsorbent, in the form of a rigid shape, as described above, supported on a septum.
- the filter-aid materials disclosed herein comprise at least one filterable composite adsorbent comprising at least one adsorbent component, and at least one filtration component having pores through which a fluid can pass, wherein the at least one adsorbent component has been precipitated in-situ on the surface of the at least one filtration component.
- a filter element may be used to support the filter-aid material comprising at least one filterable composite adsorbent.
- filter element contains filter element voids through which fluid may flow.
- the filter-aid materials comprising at least one filterable composite adsorbent may retain both the adsorptive properties of the at least one adsorbent component and the porous structure of the at least one filtration component, thus enhancing the utility of the filter-aid materials comprising at least one filterable composite adsorbent.
- the at least one adsorbent component is precipitated in-situ onto the surface of the at least one filtration component.
- the filter-aid material comprising at least one filterable composite adsorbent of the present invention may retain both its component adsorptive and filtration properties.
- the in-situ precipitation of the at least one adsorbent component on the at least one filtration component may also have superior absorptive and filtration properties than a thermally sintered or chemically bonded composite, because the in-situ precipitation process may produce a filter-aid material comprising at least one filterable composite adsorbent with smaller particle-sized adsorbent components and, consequently, a larger surface area for adsorption.
- the larger surface area may allow the filter-aid material comprising at least one filterable composite adsorbent to adsorb a greater number of particles and/or constituents which, in turn, may result in a lower turbidity level for the filtered fluid.
- the average particle size of the at least one adsorbent component that forms upon the surface of the at least one filtration component may be less than about 1 micrometer. In one embodiment, the average particle size is less than about 0.5 microns. In another embodiment, the average particle size is less than about 0.2 microns. In a further embodiment, the average particle size is less than about 0.1 microns. In yet another embodiment, the average particle size is less than about 50 nanometers. In yet a further embodiment, the average particle size is less than about 30 nanometers. In still another embodiment, the average particle size is less than about 20 nanometers. In still a further embodiment, the average particle size is less than about 10 nanometers. In another embodiment, the average particle size ranges from about 5 to about 50 nanometers. In a further embodiment, the average particle size ranges from about 2 to about 100 nanometers. In yet another embodiment, the average particle size ranges from about 5 nanometers to about 1 micrometer.
- the BET surface area of the at least one adsorbent component may increase as the mean diameter of the at least one adsorbent component decreases.
- the BET surface area of the at least one adsorbent component formed upon the surface of the at least one filtration component is greater than about 2 m 2 /g. In another embodiment, the BET surface area is greater than about 5 m 2 /g. In a further embodiment, the BET surface area is greater than about 10 m 2 /g. In yet another embodiment, the BET surface area is greater than about 25 m 2 /g. In yet a further embodiment, the BET surface area is greater than about 50 m 2 /g.
- the BET surface area is greater than about 85 m 2 /g. In still a further embodiment, the BET surface area is greater than about 125 m 2 /g. In another embodiment, the BET surface area is greater than about 250 m 2 /g. In a further embodiment, the BET surface area ranges from about 2 m 2 /g to about 2550 m 2 /g. In yet another embodiment, the BET surface area ranges from about 50 m 2 /g to about 510 m 2 /g.
- the larger BET surface area of the at least one adsorbent component may allow the filter-aid materials comprising at least one filterable composite adsorbent to reduce the number of particles and/or constituents that contribute to turbidity of the fluid.
- the filter-aid materials comprising at least one filterable composite adsorbent may entrap particles and/or constituents from the unfiltered fluid, resulting in the filtered fluid having fewer particles and/or constituents.
- the turbidity of a fluid filtered through the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be less than the turbidity of a fluid filtered through a simple mixture of at least one adsorbent component and at least filtration component, where the proportion of adsorbent component to filtration component in the simple mixture is similar to, or even greater than, the proportion of adsorbent component to filtration component of the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein.
- the turbidity of a fluid filtered through the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be less than the turbidity of a fluid filtered through a thermally sintered or chemically bonded composite of an adsorbent component and a filtration component, where the proportion of adsorbent component to filtration component in the thermally sintered or chemically bonded composite is similar to, or even greater than, the proportion of adsorbent component to filtration component of the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may be processed to provide a wide range of flow rates, which are directly related to permeability. Permeability may be reported in units of darcies (“Da”). One darcy corresponds to the permeability through a filter medium 1 cm thick which allows 1 cm 2 of fluid with a viscosity of 1 centipoise to pass through an area of 1 cm 2 in 1 second under a pressure differential of 1 atm (i.e., 101.325 kPa).
- Permeability may be determined using a device designed to form a filter cake on a septum from a suspension of filter-aid material in water and then measuring the time required for a specified volume of water to flow through a measured thickness of filter cake of known cross-sectional area.
- Many filtration media suitable for micro filtration such as diatomite and perlite products, are commercially available and span a wide range of permeability, ranging from about 0.001 Da to over 30 Da, such as from about 0.05 Da to over 10 Da.
- Filter-aid material for coarse filtration, such as sand may have greater permeabilities, such as at least about 1000 Da.
- filtration permeability for a specific filtration process depends in part on the flow rate and degree of fluid clarification required for the particular application.
- the flow of fluid through a filter-aid material may be closely related to the nature of the filtration component's porosity.
- those of low permeability may have smaller pores capable of providing greater clarity because smaller particles can be retained during the filtration process, whereas those of high permeability may have larger pores capable of providing greater fluid flow, but usually at the expense of the ability to remove particles as small as those removed by their low permeability counterparts.
- the adsorbent component may be selected from any suitable adsorbent known to the skilled artisan or hereafter discovered.
- the adsorbent may be a form of silica.
- the at least one adsorbent component may be chosen from silica gels.
- Silica gels are a form of silicon dioxide (SiO 2 ), which may occur in nature as sand. In general, however, sand is crystalline and non-porous while silica gels are non-crystalline and porous.
- the at least one adsorbent component may be a colloidal silica.
- the at least one adsorbent component may be a fumed silica.
- the at least one adsorbent component may be a silica fume.
- the at least one adsorbent component is chosen from silicates.
- suitable silicates include alumina silicate, calcium silicate, and magnesium silicate.
- the at least one adsorbent component is chosen from an alumina.
- the alumina adsorbent component is an alumina silicate.
- the alumina adsorbent component is a porous alumina.
- the silica adsorbent may, in some embodiments, further be chosen from amorphous or crystalline silicas.
- the silica adsorbent is an amorphous silica.
- the silica is a crystalline silica.
- Filtration components suitable for use in preparation of the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein may possess a variety of pore sizes.
- the filtration component pore size is a relatively large pore size, for example, a mean pore diameter of about 10 microns, such that it is particularly well suited for particle entrapment, thereby permitting mechanical filtration and/or clarification by means of removal of particles and/or constituents.
- the filtration component pore size is a relatively small pore size, for example, a mean pore diameter of about 2 microns.
- Filtration components suitable for use in the preparation of the filterable composite adsorbent disclosed herein may possess a variety of surface areas.
- the filtration component may have a relatively large surface area.
- the filtration component may have a relatively small surface area.
- a filtration component with a large surface area may allow for a reduction in the thickness of an adsorbent component coating which may be formed thereon, for example, a precipitated silica gel.
- the reduced thickness of the adsorbent coating is believed to provide for more sites for adsorption of the particles and/or constituents to be removed.
- the surface area of the filtration component is at least about 1 m 2 /g.
- the surface area is at least about 3 m 2 /g. In a further embodiment, the surface area is at least about 15 m 2 /g. In yet another embodiment, the surface area is at least about 30 m 2 /g. In yet a further embodiment, the surface area is at least about 50 m 2 /g. In still another embodiment, the surface area ranges from about 1 m 2 /g to about 100 m 2 /g. In still yet another embodiment, the surface area is less than about 500 m 2 /g.
- the at least one filtration component and/or the at least one additional filtration component is diatomite (a biogenic silica). In another embodiment, the at least one filtration component and/or the at least one additional filtration component is perlite (a natural glass). In another embodiment, the filtration components are chosen from biogenic silica, including but not limited to diatomite, rice hull ash, and sponge spicules. In a further embodiment, the filtration components are chosen from buoyant glasses. One example of buoyant glasses are natural glasses, including but not limited to pumice, expanded pumice, pumicite, expanded obsidian, expanded volcanic ash, and sand. In yet another embodiment, the filtration components are chosen from synthetic glasses.
- the filtration components are chosen from buoyant polymers.
- Buoyant polymers include but are not limited to fibrous polymers (such as fibrous nylon and fibrous polyester) and powdered polymers (such as polyvinylchloride-acrylic copolymer powder).
- the filtration components are chosen from cellulose.
- the filtration components are chosen from silicates. Non-limiting examples of suitable silicates include alumina silicate, calcium silicate, and magnesium silicate.
- the filtration components are chosen from an alumina.
- the alumina filtration component is an alumina silicate.
- the alumina filtration component is a porous alumina.
- the at least one filtration component and/or the at least one additional filtration component may comprise a mixture of two or more of the filtration components mentioned above.
- the at least one filtration component and/or the at least one additional filtration component may comprise a mixture of diatomite and perlite.
- the at least one filtration component and the at least one additional filtration component (if used) may be the same or different. In one embodiment, the filtration components are the same. In another embodiment, the filtration components are different.
- biogenic silica refers to silica produced or brought about by living organisms.
- biogenic silica is diatomite, obtained from diatomaceous earth (also known as kieselguhr), which is a sediment enriched in biogenic silica in the form of the siliceous frustules (i.e., shells or skeletons) of diatoms.
- Diatoms are a diverse array of microscopic, single-celled algae of the class Bacillariophyceae, which possess an ornate siliceous skeleton (frustule) of varied and intricate structure comprising two valves which, in the living diatom, fit together much like a pill box.
- the morphology of the frustules may vary widely among species and serves as the basis for taxonomic classification; over at least 2,000 distinct species are known.
- the surface of each valve is punctuated by a series of openings that comprise the complex fine structure of the frustule and impart a design that is distinctive to individual species.
- the size of typical frustules may range from about 0.75 ⁇ m to about 1,000 ⁇ m. In one embodiment, the size ranges from about 10 ⁇ m to about 150 ⁇ m.
- Those frustules are sufficiently durable to retain much of their porous and intricate structure virtually intact through long periods of geologic time when preserved in conditions that maintain chemical equilibrium.
- natural glass refers to natural glasses, commonly referred to as volcanic glasses, that are formed by the rapid cooling of siliceous magma or lava.
- natural glasses including, for example, perlite, pumice, pumicite, obsidian, and pitchstone.
- perlite Prior to processing, perlite may be gray to green in color with abundant spherical cracks that cause it to break into small pearl-like masses.
- Pumice Prior to processing, perlite may be gray to green in color with abundant spherical cracks that cause it to break into small pearl-like masses.
- Pumice is a lightweight glassy vesicular rock. Obsidian may be dark in color with a vitreous luster and a characteristic conchoidal fracture.
- Pitchstone has a waxy resinous luster and may be brown, green, or gray.
- Volcanic glasses such as perlite and pumice occur in massive deposits and find wide commercial use.
- Volcanic ash often referred to as tuft when in consolidated form, comprises small particles or fragments that may be in glassy form.
- the term natural glass encompasses volcanic ash.
- Natural glasses may be chemically equivalent to rhyolite. Natural glasses that are chemically equivalent to trachyte, dacite, andesite, latite, and basalt are known but may be less common.
- the term obsidian is generally applied to large numbers of natural glasses that are rich in silica. Obsidian glasses may be classified into subcategories according to their silica content, with rhyolitic obsidians (containing typically about 73% SiO 2 by weight) as the most common.
- Perlite is a hydrated natural glass that may contain, for example, about 72 to about 75% SiO 2 , about 12 to about 14% Al 2 O 3 , about 0.5 to about 2% Fe 2 O 3 , about 3 to about 5% Na 2 O, about 4 to about 5% K 2 O, about 0.4 to about 1.5% CaO (by weight), and small amounts of other metallic elements.
- Perlite may be distinguished from other natural glasses by a higher content (such as about 2 to about 5% by weight) of chemically bonded water, the presence of a vitreous, pearly luster, and characteristic concentric or arcuate onion skin like (i.e., perlitic) fractures.
- Perlite products may be prepared by milling and thermal expansion, and may possess unique physical properties such as high porosity, low bulk density, and chemical inertness.
- Pumice is a natural glass characterized by a mesoporous structure (e.g., having pores or vesicles with a size up to about 1 mm).
- the porous nature of pumice gives it a very low apparent density, in many cases allowing it to float on the surface of water.
- Most commercial pumice contains from about 60% to about 70% SiO 2 by weight.
- Pumice may be processed by milling and classification, and products may be used as lightweight aggregates and also as abrasives, adsorbents, and fillers.
- Unexpanded pumice and thermally expanded pumice may also be used as filtration components in some cases as can volcanic ash.
- the appropriate selection of the at least one adsorbent component and the at least one filtration component of the filter-aid materials comprising at least one filterable composite adsorbent, as well as any at least one additional filtration component, disclosed herein may be determined by the specific application intended. For example, in a filtration process that demands high clarity but tolerates slower flow rate, a filter-aid material comprising at least one filterable composite adsorbent of low permeability may be used, whereas in a filtration process that demands high flow rate but does not require high clarity, a filter-aid materials comprising at least one filterable composite adsorbent of high permeability may be used. Similar reasoning applies to the choice of the at least one adsorbent component, and to the at least one filterable composite adsorbent when used in conjunction with other materials, or when preparing mixtures containing the products.
- a silica gel adsorbent for chill-proofing of beer is precipitated in-situ upon expanded perlite.
- the resulting composite has both the properties of the chill-proofing obtained from the silica gel adsorbent, as well as the filtration properties of the expanded perlite filtration component.
- the resulting silica gel/expanded perlite filterable composite adsorbent may further be mixed with at least one additional filtration component.
- the at least one additional filtration component may also comprise expanded perlite.
- the at least one additional filtration component may comprise a filtration component that is different than expanded perlite.
- silica gel may be precipitated in-situ onto diatomite, a biogenic silica.
- the resulting composite has both the properties of the chill-proofing obtained from the silica gel adsorbent, as well as the filtration properties of the diatomite filtration component.
- the resulting silica gel/diatomite filterable composite adsorbent may further be mixed with an at least one additional filtration component.
- the at least one additional filtration component may also comprise diatomite.
- the at least one additional filtration component may comprise a filtration component that is different than diatomite.
- the filter-aid material comprising at least one filterable composite adsorbent may be pulverized.
- the filter-aid material may comprise at least one filterable composite adsorbent that has been pulverized. Pulverization may lead to an increase in surface area of the filter-aid material and/or filterable composite adsorbent and, thus, an increased ability to adsorb particles and/or constituents in the fluid to be filtered.
- pulverization may lead to a greater number of unlocked silica gel sites of the filter-aid material and/or filterable composite adsorbent and, thus, an increased ability to adsorb particles and/or constituents in the fluid to be filtered.
- too much pulverization can result in a decrease in permeability.
- the pulverization is controlled to achieve the desired balance between adsorbency and permeability.
- Sodium silicate is used herein to refer to any one of several compounds comprising sodium oxide (Na 2 O) and silica (SiO 2 ). Such combinations may include, for example, sodium ortho silicate (Na 4 SiO 4 ), sodium meta silicate (Na 2 SiO 3 ), and sodium disilicate (Na 2 Si 2 O 5 ).
- the sodium silicate is a diatomite-based based sodium silicate.
- sodium silicate is substituted in whole or in part for at least one ammonium silicate and/or at least one alkali metal silicate, such as lithium, sodium, potassium, rubidium, and cesium silicates.
- sodium silicate having an SiO 2 /Na 2 O ratio of about 3.2 and a concentration of about 20% is added to water to a concentration of about 2% by weight.
- Sodium silicate with a SiO 2 /Na 2 O ratio of 3.2 and a concentration of 20% may be purchased, for example, from World Minerals Inc.
- An acid or salt thereof may be added to the slurry in an amount sufficient to increase the acidity (i.e., reduce the pH) of the slurry to a pH range suitable for the precipitation of silica gel.
- Any suitable acid may be selected, such selection being within the skill of one in the art.
- the acid may be sulfuric acid.
- the acid may be phosphoric acid.
- the acid may by hydrochloric acid.
- the acid may be nitric acid.
- the acid may be acetic acid.
- a filtration component chosen from among any suitable filtration component previously known or hereinafter discovered, may then be added to the solution.
- the filtration component is the commercially-available filtration component Celite Standard Super-Cel®, manufactured by World Minerals Inc. In another embodiment, the filtration component is the commercially-available filtration component Celite Hyflo Super-Cel®, manufactured by World Minerals Inc. In a further embodiment, the filtration component is the commercially-available filtration component Celite 512®, manufactured by World Minerals Inc. In a further embodiment, the filtration component is the commercially-available filtration component Celite 512Z®, manufactured by World Minerals Inc. In still another embodiment, the filtration component is the commercially-available filtration component Celite 289®, manufactured by World Minerals Inc. In still a further embodiment, the filtration component is the commercially-available filtration component Filter-Cel®, manufactured by World Minerals Inc.
- the slurry is stirred periodically until gelling occurs. This may take about 25 to about 60 minutes depending upon the acidity of the solution and the sodium silicate concentration of the slurry.
- water is added, for example from about 20 mL to about 500 mL of water, to disperse the gelled slurry.
- the slurry is then filtered and the resulting cake is washed with water. Then the cake is dried until the excess fluid in the cake has evaporated.
- the cake may be dried at a temperature ranging from about 110° C. to about 200° C.
- the amount of the filtration component added may be based upon the amount of silica gel desired to be in the resultant filterable composite adsorbent and/or final filter-aid material. While increasing the percentage of silica gel generally acts to increase the filter-aid material's ability to act as an adsorbent, it generally acts to decrease its ability to act as a filter material. Conversely, decreasing the percentage of silica gel generally acts to decrease the filter-aid material's ability to act as an adsorbent while increasing its ability to act as a filter material.
- the amount of the adsorbent component in the filterable composite adsorbent may comprise from between greater than about 0 to about 100% by weight of the total filterable composite adsorbent.
- the adsorbent component may comprise greater than about 5% by weight of the total filterable composite adsorbent.
- the adsorbent component may comprise greater than about 15% by weight of the total filterable composite adsorbent.
- the adsorbent component may comprise greater than about 25% by weight of the total filterable composite adsorbent.
- the adsorbent component may comprise greater than about 40% by weight of the total filterable composite adsorbent.
- the adsorbent component may comprise greater than about 50% by weight of the total filterable composite adsorbent. In another embodiment, the adsorbent component may comprise greater than about 70% by weight of the total filterable composite adsorbent. In another embodiment, the adsorbent component may comprise greater than about 80% by weight of the total filterable composite adsorbent.
- the amount of the filtration component in the filterable composite adsorbent may comprise from between greater than about 0 to about 100% by weight of the total filterable composite adsorbent. In one embodiment, the filtration component may comprise greater than about 5% by weight of the total filterable composite adsorbent. In another embodiment, the filtration component may comprise greater than about 15% by weight of the total filterable composite adsorbent. In another embodiment, the filtration component may comprise greater than about 25% by weight of the total filterable composite adsorbent. In another embodiment, the filtration component may comprise greater than about 40% by weight of the total filterable composite adsorbent. In another embodiment, the filtration component may comprise greater than about 50% by weight of the total filterable composite adsorbent. In another embodiment, the filtration component may comprise greater than about 70% by weight of the total filterable composite adsorbent. In another embodiment, the filtration component may comprise greater than about 80% by weight of the total filterable composite adsorbent.
- the adsorbent component may comprise from about 5% to about 15% by weight of the total filterable composite adsorbent and the filtration component may comprise from about 85% to about 95% by weight of the total filterable composite adsorbent.
- the adsorbent component may comprise from about 65% to 75% by weight of the total filterable composite adsorbent and the filtration component may comprise from 25% to 35% by weight of the total filterable composite adsorbent.
- the filterable composite adsorbent comprises a greater amount by weight of the adsorbent component than the filtration component.
- the filterable composite adsorbent may then be mixed with at least one additional filtration component.
- the at least one additional filtration component may be chosen from any suitable filtration component previously known or hereinafter discovered and may be either the same or different from the at least one filtration component in the filterable composite adsorbent.
- the additional filtration component is the commercially-available filtration component Celite Standard Super-Cel®, manufactured by World Minerals Inc.
- the additional filtration component is the commercially-available filtration component Celite Hyflo Super-Cel®, manufactured by World Minerals Inc.
- the additional filtration component is the commercially-available filtration component Celite 512®, manufactured by World Minerals Inc.
- the filtration component is the commercially-available filtration component Celite 512Z®, manufactured by World Minerals Inc.
- the additional filtration component is the commercially-available filtration component Celite 289®, manufactured by World Minerals Inc.
- the additional filtration component is the commercially-available filtration component Filter-Cel®, manufactured by World Minerals Inc.
- the additional filtration component may comprise from greater than about 0% to about 100% of the total weight of the filter-aid material. In one embodiment, the additional filtration component may comprise greater than about 5% by weight of the total filter-aid material. In another embodiment, the additional filtration component may comprise greater than about 30% by weight of the total filter-aid material. In a further embodiment, the additional filtration component may comprise greater than about 50% by weight of the total filter-aid material. In yet another embodiment, the additional filtration component may comprise greater than about 65% by weight of the total filter-aid material. In yet a further embodiment, the additional filtration component may comprise greater than about 80% by weight of the total filter-aid material.
- the filterable composite adsorbent may comprise from greater than about 0% to about 100% of the total weight of the filter-aid material. In one embodiment, the filterable composite adsorbent may comprise greater than about 5% by weight of the total filter-aid material. In another embodiment, the filterable composite adsorbent may comprise greater than about 30% by weight of the total filter-aid material. In a further embodiment, the filterable composite adsorbent may comprise greater than about 50% by weight of the total filter-aid material. In yet another embodiment, the filterable composite adsorbent may comprise greater than about 65% by weight of the total filter-aid material. In yet a further embodiment, the filterable composite adsorbent may comprise greater than about 80% by weight of the total filter-aid material.
- the at least one additional filtration component may comprise from about 60% to about 70% by weight of the total filler-aid material and the filterable composite adsorbent may comprise from about 30% to about 40% by weight of the total filler-aid material.
- filter-aid materials comprising at least one filterable composite adsorbent can be modified by further physical or chemical reaction of the material after the initial filter-aid material comprising at least one filterable composite adsorbent has been made, for example to enhance at least one property (for example, solubility and surface characteristics) and/or to yield a new product with a specialized use.
- further modifications include, for example, hydration, acid washing, surface treatment, and organic derivatization, as disclosed, for example, in U.S. Pat. No. 6,712,974 to Palm et al.
- the filter-aid material comprising at least one filterable composite adsorbent described herein may be used in many of the same applications as currently available adsorbents, but offers added properties, such as, for example, increased permeability, low centrifuged wet density, and uniquely shaped particles (e.g., fibers), as well as improved efficiency and/or economy.
- the filter-aid material comprising at least one filterable composite adsorbent disclosed herein, and its optional further modifications, may be used in filtration applications in a manner analogous to that of porous filtration media.
- Filter-aid materials comprising at least one filterable composite adsorbent may be applied to a septum to improve clarity and increase flow rate in filtration processes or added directly to the fluid.
- filter-aid materials comprising at least one filterable composite adsorbent may be used in pre-coating, body feeding, or both.
- the method of adsorption and filtration comprises (i) providing a filter-aid material comprising at least one filterable composite adsorbent, (ii) pre-coating a filter element with the filterable composite adsorbent, and (iii) suspending the filter-aid material comprising at least one filterable composite adsorbent in a fluid containing particles and/or constituents to be removed from the fluid, wherein the filterable composite adsorbent may be supported on a filter element.
- the method of adsorption and filtration comprises (i) providing a filterable composite adsorbent, (ii) further mixing the filterable composite adsorbent with an at least second filtration component to form a filler-aid material (iii) pre-coating a filter element with the filler-aid material, and (iv) suspending the filter-aid material in a fluid containing particles and/or constituents to be removed from the fluid, wherein the filter-aid material may be supported on a filter element.
- one embodiment disclosed herein comprises a combination of pre-coating and body feeding.
- the method of adsorption and filtration comprises the step of passing a fluid containing undesired particles or constituents to be adsorbed through a filter-aid material comprising at least one filterable composite adsorbent, in the form of a rigid shape supported on a septum.
- the filter-aid material comprising at least one filterable composite adsorbent disclosed herein can be shaped, molded, extruded, sintered, or otherwise formed into permeable sheets, plates, disks, polyhedrons, or other formed shapes that have adsorbent properties. Fluids can then be passed through the filter-aid material comprising at least one filterable composite adsorbent to achieve both filtration and adsorption.
- the filter-aid material comprising at least one filterable composite adsorbent disclosed herein may be used in conjunction with other media (e.g., different porous filtration component materials) to form a filter-aid material for use in filtration applications and/or to further modify or optimize a filtration process.
- media e.g., different porous filtration component materials
- mixtures of the filterable composite adsorbent with, for example, diatomite, expanded perlite, pumicite, natural glass, cellulose, activated charcoal, clay, or other materials may be useful additional filtration components.
- these blends are more elaborate and enable the blend to be formed into sheets, pads, cartridges, or monolithic or aggregate media capable of being used as supports or substrates.
- the filter-aid materials comprising at least one filterable composite adsorbent disclosed herein can also be useful in applications other than filtration, since adsorbents or filtration media can be useful in applications that do not necessarily depend explicitly on either conventional adsorption or filtration.
- substances such as silica gel, fumed silica, neutral clay, alkaline clay, zeolites, catalysts, polymers, and alkaline earth silicate hydrates can be used as fillers, and biogenic silica, natural glass, expanded perlite, pumice, expanded pumice, pumicite, expanded obsidian, expanded volcanic ash, buoyant glass, buoyant polymer, and cellulose can also be used as fillers.
- filter-aid materials comprising at least one filterable composite adsorbent as disclosed herein, as well as methods for preparing them, are described in the following examples, which are offered by way of illustration and not by way of limitation.
- a sodium silicate solution with a SiO 2 :Na 2 O weight ratio of 3.2 to 1 was selected based on a combination of efficiency and price, but other ratios of SiO 2 :Na 2 O may also be used.
- the sodium silicate was added to reverse osmosis water with a concentration of about 2%.
- a quantity of sulfuric acid (H 2 SO 4 ) was then added to the slurry to reduce the pH to about 5.5 to 9.
- a filtration component was then added to the solution.
- the filtration component was Harborlite® 200, an expanded milled perlite with a permeability of 0.29 Da and a wet density of about 14.0 lbs/ft 3 .
- the amount of filtration component added was based upon the desired amount of silica gel in the end chill-proofing filter-aid product.
- the slurry was stirred until gelling occurred (about 25-60 minutes depending upon the pH level).
- water was added to disperse the gelled slurry.
- the slurry was then filtered and the composite was washed with water. Then, the filterable composite adsorbent was heated in an oven, to evaporate any excess moisture, until a stable weight was obtained.
- Table 1 provides information regarding the performance of a chill-proofing filter-aid manufactured by the process described above.
- Harborlite® 200 was used as the filtration component and different amounts of silica gel were attached thereto by precipitating diatomite based sodium silicate onto the filtration component by varying the pH of the slurry.
- the control was a simple mixture comprising 90% of Harborlite® 200 and 10% of Millennium Chemical XP103® silica gel.
- the particle size of the adsorbent components were smaller than the adsorbent particle size of the control sample.
- the turbidity of the filtered fluid was lower after the fluid had been processed through the filterable composite adsorbent compared to processing with either the simple mixture of the control or a process that incorporates no chill-proofing.
- Celite Standard Super-Cel® and Celite Hyflo Super-Cel® were used as filtration components in the place of the Harborlite® 200.
- Celite Standard Super-Cel® filtration component is a diatomite-based filtration component with a permeability of 0.25 Da and a wet density of about 9 lbs/ft 3 .
- Celite Hyflo Super-Cel® filtration component is also diatomite based, but has a permeability of 1.10 Da and a wet density of 10 lbs/ft 3 .
- Table 2 shows the filtration properties of a diatomite-based chill-proofing filter-aid using different amounts of silica gel and at different pH levels.
- the base materials were Celite Hyflo Super-Cel® and Celite Standard Super-Cel® diatomite. It is shown that the relative amount of silica gel precipitated upon the filtration component had a direct relationship with the BET surface area of the adsorbent component.
- Table 3 shows the performance of a diatomite based chill-proofing aid of Table 2.
- the filterable composite adsorbent was more effective than either the simple mixture of the control or a process that involves no chill proofing as evidenced by the low turbidity values of the filtered fluid.
- Table 4 shows the performance of diatomite based chill-proofing filter-aid using Celite Standard Super-Cel® from Table 2 with different amounts of silica gel attached thereto by precipitating diatomite based sodium silicate onto the filtration component by varying the pH of the slurry.
- the control was a system simple mixture of 90% of Celite Standard Super-Cel® and 10% of Millennium Chemicals XP103® silica gel.
- the filterable composite adsorbent as disclosed herein provided a superior value than either the control system or the system which implemented no chill-proofing measures.
- FCA filterable composite adsorbent
- FCA filterable composite adsorbent
- Example 2 The procedure of Example 2 was repeated with the exception of replacing the sodium silicate solution used in Example 2 with a commercial sodium silicate solution. Again, different filtration components were used in the process to create the filterable composite adsorbent (Celite Standard Super-Cel®, Celite Hyflo Super-Cel®, and Celite 512®).
- Tables 5-8 show the performance of a commercial non-diatomite based sodium silicate.
- the commercial sodium silicate solution used was PQ N-Clear®, manufactured by PQ Corporation of Valley Forge, Pa.
- PQ N-Clear® has a SiO 2 :Na 2 ratio of 3.22:1 and a pH of 11.3.
- the commercial sodium silicate solution used was PQ N®, manufactured by PQ Corporation of Valley Forge, Pa.
- Table 5 reflects a chill-proofing filtration component formed by Celite Hyflo Super-Cel®.
- Table 6 reflects Celite Standard Super-Cel® as the filtration component.
- Table 7 reflects Celite 512® as the filtration component.
- Celite 512® has a permeability of 0.50 Da and a wet density of about 9 lbs/ft 3 .
- the control comprised a simple mixture 90% Celite Standard Super-Cel® and 10% Millennium Chemical XP103® silica gel.
- FCA filterable composite adsorbent
- FCA filterable composite adsorbent
- FCA filterable composite adsorbent
- FCA filterable composite adsorbent
- a filterable composite adsorbent was made using a Celite Standard Super-Cel® and diatomite based sodium silicate. 43 g of sodium silicate solution (containing 6.75 g of dissolved silica) was added to 450 g of water. Next, 3.16 g of sulfuric acid (98%) was added to the solution to reduce the solution pH to 7.2. The filtration component (Celite Standard Super-Cel®) was then added to the solution. The slurry was stirred for 37 minutes at which time the slurry began to gel. 150 mL of water was added to disperse the gelled slurry. Then the slurry was filtered and the slurry cake was repeatedly washed with 300 mL of water. Finally, the cake was then dried by heating it at 110° C. for three hours.
- Example 2 The procedure of Example 1 was repeated to form a number of filterable composite adsorbent compositions except that Filter-Cel® was used as the filtration component in the place of the Harborlite® 200. Different amounts of silica gel were attached thereto by precipitating diatomite based sodium silicate onto the filtration component by varying the pH of the slurry. The resultant filterable composite adsorbents ranged in make-up from 7.5% by weight silica gel to 70% by weight silica gel. In addition, the filterable composite adsorbents were then treated by pulverization to vary the particle size of the filterable composite adsorbent compositions from a d50 of 19 microns to a d50 of 39 microns.
- the filterable composite adsorbents were mixed with a second filtration component, Celite 512Z®, such that the resultant filter aid materials comprised 35% by weight filterable composite adsorbent and 65% by weight of Celite 512Z®.
- Table 9 provides information regarding the performance of the filter-aid materials as chill-proofing filter-aids.
- the filter-aids were used to filter beer at a rate of 0.6 grams per 100 grams of beer. Three trials were run with each filter-aid material with the chill haze, chill haze average, and chill haze standard deviation being recorded.
- the filter-aids according to this example were compared with the performance of a control comprising a simple mixture of 65% by weight Celite 512Z® and 35% by weight of Brightsorb d-300® (a conventional chillproofing silica gel).
- FCA filterable composite adsorbent
- Brightsorb is used to represent the adsorbent component Brightsorb d-300®
- SG is used to represent the adsorbent component silica gel
- C512Z is used to represent the filtration component Celite 512Z®
- FC is used to represent the filtration component Filter Cel®
- C289 is used to represent the filtration component Celite 289®
- d50 is used to represent median particle size in microns.
- the filterable composite adsorbents may be represented by a short sequence comprising (filtration component ⁇ adsorbent component (#% by weight adsorbent component)).
- “C512Z-SG70” represents a filterable composite adsorbent wherein the filtration component is Celite 512Z®, the adsorbent component is silica gel, and the silica gel comprises 70% by weight of the filterable composite adsorbent.
- FCA Adsorbent
- C512Z 1 2 3 NTU
- NTU NTU
- Control Brightsorb 35% 59.2 59.7 64 61.0 2.64 C512Z 65% C512Z-SG7.5 C512Z-SG7.5 100% 79.2 72.5 76.6 76.1 3.38
- (d50 39) C512Z 65% FC-SG70 FC-SG70 35%: 56.2 57.7 59.3 57.7 1.55
- (d50 32)
- the effectiveness of the filter-aid materials' adsorbency generally increased with an increase in the adsorbent component in the filterable composite adsorbent component.
- the effectiveness of the filter-aid materials' adsorbency generally increased with a decrease in particle size due to pulverization. It is believed that pulverization leads to an increased amount of silica gel sites, thus leading to the improved adsorbency.
- Example 5 The procedure of example 5 was repeated, except that the filterable composite adsorbent did not undergo pulverization and the proportion of the second filtration component (Celite 512Z®) to the filterable composite adsorbent was varied.
- the surface area of the Celite 512Z® was measured as 55 m 2 /gram.
- the effect of the variance of the ratio of the second filtration component to the filterable composite adsorbent on chill haze and permeability are shown in tables 10 and 11. All trials were aged for 75 hours except for those denoted with (*) which were aged for 99 hours and chilled for 24 hours.
- the filter-aid materials of the present invention were able to exhibit comparable adsorbency when compared with the control (trial 2), however at lower concentrations of silica gel by weight of the total filter aid. Such a reduction in the requirement for the adsorbent component may lead to a considerable cost advantage in production.
- the filter-aid material of trial 6 was able to obtain comparable adsorbency while exhibiting a significant increase in permeability as compared to the control.
- Example 6 The procedure of Example 6 was repeated, except that the filtration component of the filterable composite adsorbent was changed from Filter Cel® to Celite 289®.
- the Celite 289® was measured as having a surface area of 35 m 2 /gram.
- the effect of the variance of the ratio of the second filtration component to the filterable composite adsorbent on chill haze and permeability are shown in tables 12 and 13. All trials were aged for 75 hours except for those denoted with (*) which were aged for 99 hours and chilled for 24.
- Example 6 The procedure of Example 6 was repeated, except that the filterable composite adsorbent was changed from Filter Cel® to Celite 512Z®.
- the Celite 512Z® was measured as having a surface area of 3 m 2 /gram.
- the effect of the variance of the ratio of the second filtration component to the filterable composite adsorbent on chill haze is shown in table 14. All trials were aged for 75 hours except for those denoted with (*) which were aged for 99 hours and chilled for 24.
- the filter-aid materials according to the instant invention's adsorbency generally increased with an increase in the surface area of the filtration component of the filterable composite adsorbent. It is believed that a high surface area of the filtration component of the filterable composite adsorbent reduces the thickness of the silica gel coating and thereby providing more sites for adsorption of the chill haze particles.
- Example 5 The procedure of Example 5 was repeated to form a number of filter-aid materials comprising a filterable composite adsorbent, except that the filterable composite adsorbent did not undergo pulverization and, in half of the materials, Celite 289 was used as the filtration component in the place of Filter-Cel®.
- the filter-aid materials were then used in a beer filtration process to analyze the wet density and permeability of those mixtures. The results are shown in table 15. Trials 51, 52, 58, and 59 were the controls.
- the filter-aid materials comprising a filterable composite adsorbent of the present invention demonstrate permeabilities which are comparable to, and in many cases better than, the permeability exhibited by one of the controls (Trial 52).
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Organic Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Genetics & Genomics (AREA)
- Zoology (AREA)
- General Engineering & Computer Science (AREA)
- General Health & Medical Sciences (AREA)
- Biochemistry (AREA)
- Food Science & Technology (AREA)
- Wood Science & Technology (AREA)
- Bioinformatics & Cheminformatics (AREA)
- Toxicology (AREA)
- Environmental & Geological Engineering (AREA)
- Water Supply & Treatment (AREA)
- Hydrology & Water Resources (AREA)
- Ceramic Engineering (AREA)
- Inorganic Chemistry (AREA)
- Geology (AREA)
- Solid-Sorbent Or Filter-Aiding Compositions (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US12/373,753 US20090261041A1 (en) | 2006-07-14 | 2007-07-13 | Composition for Filtering and Removing Particles and/or Constituents from a Fluid |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US83078106P | 2006-07-14 | 2006-07-14 | |
US94595407P | 2007-06-25 | 2007-06-25 | |
US12/373,753 US20090261041A1 (en) | 2006-07-14 | 2007-07-13 | Composition for Filtering and Removing Particles and/or Constituents from a Fluid |
PCT/US2007/073439 WO2008008940A2 (fr) | 2006-07-14 | 2007-07-13 | Composition pour la filtration et l'élimination de particules et/ou de constituants d'un fluide |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2007/073439 A-371-Of-International WO2008008940A2 (fr) | 2006-07-14 | 2007-07-13 | Composition pour la filtration et l'élimination de particules et/ou de constituants d'un fluide |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/421,915 Division US20120172195A1 (en) | 2006-07-14 | 2012-03-16 | Composition for filtering and removing particles and/or constituents from a fluid |
Publications (1)
Publication Number | Publication Date |
---|---|
US20090261041A1 true US20090261041A1 (en) | 2009-10-22 |
Family
ID=38924215
Family Applications (3)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/373,753 Abandoned US20090261041A1 (en) | 2006-07-14 | 2007-07-13 | Composition for Filtering and Removing Particles and/or Constituents from a Fluid |
US13/421,915 Abandoned US20120172195A1 (en) | 2006-07-14 | 2012-03-16 | Composition for filtering and removing particles and/or constituents from a fluid |
US15/182,297 Active US10066197B2 (en) | 2006-07-14 | 2016-06-14 | Composition for filtering and removing particles and/or constituents from a fluid |
Family Applications After (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/421,915 Abandoned US20120172195A1 (en) | 2006-07-14 | 2012-03-16 | Composition for filtering and removing particles and/or constituents from a fluid |
US15/182,297 Active US10066197B2 (en) | 2006-07-14 | 2016-06-14 | Composition for filtering and removing particles and/or constituents from a fluid |
Country Status (5)
Country | Link |
---|---|
US (3) | US20090261041A1 (fr) |
EP (2) | EP2049225B1 (fr) |
CN (1) | CN101528320B (fr) |
PL (2) | PL2684589T3 (fr) |
WO (1) | WO2008008940A2 (fr) |
Cited By (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100038327A1 (en) * | 2008-08-13 | 2010-02-18 | Contech Stormwater Solutions Inc. | Thermally treated expanded perlite |
JP2013537484A (ja) * | 2010-08-18 | 2013-10-03 | ワールド ミネラルズ,インコーポレイテッド | 新規性のある細孔サイズ特性を有する複合濾過補助剤 |
WO2014004349A1 (fr) | 2012-06-26 | 2014-01-03 | Imerys Filtration Minerals, Inc. | Matériaux composites co-agglomérés, procédés de fabrication de matériaux composites co-agglomérés et procédés d'utilisation de matériaux composites co-agglomérés |
WO2015100050A1 (fr) | 2013-12-26 | 2015-07-02 | Imerys Filtration Minerals, Inc. | Matériaux composites co-agglomérés, procédés de fabrication de matériaux composites co-agglomérés, et procédés d'utilisation de matériaux composites co-agglomérés |
US20160168204A1 (en) * | 2013-06-28 | 2016-06-16 | Daiichi Sankyo Company, Limited | Method for purifying oligosaccharide peptide |
WO2017019845A1 (fr) * | 2015-07-29 | 2017-02-02 | Imerys Filtration Minerals, Inc. | Moyen auxiliaire de filtration composite de résistance au froid et procédés associés |
US20180236383A1 (en) * | 2015-02-26 | 2018-08-23 | Imerys Filtration Minerals, Inc. | Filter aids for biodiesel and edible oil filtration and methods and uses of the filtering aids |
WO2019046499A1 (fr) * | 2017-08-31 | 2019-03-07 | Imerys Filtration Minerals, Inc. | Accessoire de filtration à base de perlite haute densité |
US20190076817A1 (en) * | 2017-09-14 | 2019-03-14 | Andrew Ungerleider | Method and apparatus using foamed glass filters for liquid purification, filtration, and filtrate removal and elimination |
US20190112395A1 (en) * | 2016-03-29 | 2019-04-18 | Ch-Bioforce Oy | Method of producing hemicellulose extracts |
US10391433B2 (en) | 2014-12-19 | 2019-08-27 | Ep Minerals, Llc | Opaline biogenic silica/expanded perlite composite products |
JP2021506568A (ja) * | 2017-12-14 | 2021-02-22 | アイメリーズ ユーエスエー,インコーポレーテッド | 油を処理する濾過助剤並びにその作製方法及び使用 |
CN113272041A (zh) * | 2018-12-18 | 2021-08-17 | 美国达拉斯集团公司 | 具有多个突起的过滤器 |
JP7482869B2 (ja) | 2018-11-29 | 2024-05-14 | イメルテック ソシエテ パル アクシオン サンプリフィエ | 鉱物組成物 |
Families Citing this family (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2049225B1 (fr) | 2006-07-14 | 2014-09-03 | Imerys Filtration Minerals, Inc. | Composition pour la filtration et l'élimination de particules et/ou de constituants d'un fluide |
WO2013051405A1 (fr) | 2011-10-03 | 2013-04-11 | 株式会社石垣 | Couche de milieu filtrant de forme non définie et dispositif de filtration doté de celle-ci |
EP3341107B2 (fr) * | 2015-08-28 | 2023-10-18 | Imerys Filtration Minerals, Inc. | Adjuvants de filtration de silicate de magnésium composites à haute perméabilité |
US20180223232A1 (en) * | 2015-09-02 | 2018-08-09 | Ep Minerals, Llc | Regenerated media useful in the treatment of fermented liquids |
WO2017087836A1 (fr) * | 2015-11-18 | 2017-05-26 | Imerys Filtration Minerals, Inc. | Adjuvants de filtration composites cationiques comprenant du silicate |
CN105601704A (zh) * | 2015-11-19 | 2016-05-25 | 天津市亨必达化学合成物有限公司 | 高纯手性阿加曲班新型工业精制方法 |
JP7329325B2 (ja) * | 2016-01-28 | 2023-08-18 | アイメリーズ フィルトレーション ミネラルズ,インコーポレイテッド | 酸処理された濾過助剤配合物 |
CN106268030B (zh) * | 2016-08-08 | 2018-05-08 | 浙江省纺织测试研究院 | 一种耐腐蚀高温烟气复合过滤材料及其制备方法 |
CN107159169B (zh) * | 2017-05-19 | 2020-04-17 | 溧阳市鸿智新材料科技有限公司 | 一种低可溶性铁离子的吸附过滤材料及其制备方法 |
CN110652834B (zh) * | 2018-06-29 | 2022-02-18 | 上海清臣环保科技有限公司 | 一种空气净化材料及其制备方法 |
US20240150686A1 (en) * | 2022-11-09 | 2024-05-09 | Active Minerals International, Llc | Product and method for stabilization/chill proofing of fermented liquids |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5017354A (en) * | 1988-09-02 | 1991-05-21 | Akzo America Inc. | Process for production of high purity silica gel |
US6712898B2 (en) * | 2000-08-08 | 2004-03-30 | Advanced Minerals Corporation | Perlite products with controlled particle size distribution |
US6712974B1 (en) * | 1997-01-10 | 2004-03-30 | Advanced Minerals Corporation | Filterable composite adsorbents |
Family Cites Families (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5776353A (en) * | 1996-02-16 | 1998-07-07 | Advanced Minerals Corporation | Advanced composite filtration media |
US1570537A (en) | 1924-03-27 | 1926-01-19 | Celite Company | Absorbent material and process of making same |
US3917814A (en) | 1969-10-29 | 1975-11-04 | Kenneth B Hedges | Insecticidal composition and method of preparing the same |
US4072537A (en) | 1976-03-19 | 1978-02-07 | Westvaco Corporation | Composite silicate pigment |
US4636494A (en) | 1981-01-30 | 1987-01-13 | Massachusetts Institute Of Technology | Process and composition for treating disorders by administering amphetamine and choline |
US4511473A (en) * | 1982-02-09 | 1985-04-16 | Amf Incorporated | Fibrous media containing millimicron-sized particulates |
US4596660A (en) * | 1982-07-23 | 1986-06-24 | Amf Inc. | Fibrous media containing millimicron-sized particulates |
US4552752A (en) * | 1983-01-31 | 1985-11-12 | Rohm And Haas Company | Microbiocidal article for aqueous systems |
US4508742A (en) | 1983-05-06 | 1985-04-02 | Pq Corporation | Treating beer to prevent chill haze and metal contamination |
JPS6078639A (ja) * | 1983-09-29 | 1985-05-04 | Nippon Petrochem Co Ltd | 水銀分離吸着剤 |
US4606824A (en) * | 1984-10-26 | 1986-08-19 | Chaokang Chu | Modified cellulose separation matrix |
DE3509892C2 (de) | 1985-03-19 | 1994-04-21 | Westfalia Separator Ag | Verfahren zum Nachklären und Stabilisieren von Polyphenole und/oder Eiweißstoffe enthaltenden Flüssigkeiten und Getränken, insbesondere von Bier |
US4810503A (en) | 1987-03-31 | 1989-03-07 | Basf Corporation | Polymers which form gels at low concentrations in water |
US4980334A (en) * | 1989-09-13 | 1990-12-25 | Uop | Macroporous alumina/diatomaceous earth bio-supports |
US5847023A (en) | 1990-10-26 | 1998-12-08 | Mdv Technologies, Inc. | Thermal irreversible gel corneal contact lens formed in situ |
SE507024C2 (sv) | 1991-03-21 | 1998-03-16 | Rollen Jarl Erik | Passivt filter innefattande en självregenererande materialkomposition för upptagning av gasformiga ämnen |
CN1098661A (zh) * | 1993-08-08 | 1995-02-15 | 青岛益民葡萄酒厂 | 一种改善过滤介质性能的方法 |
FR2712508B1 (fr) * | 1993-11-19 | 1996-01-05 | Ceca Sa | Procédé pour l'obtention d'agents filtrants diatomitiques à très faible teneur en cristobalite par agglomération avec des liants silicatés ou siliciques et agents filtrants correspondants. |
CN1108149A (zh) * | 1994-03-08 | 1995-09-13 | 孙书贤 | 一种助滤剂的制造方法 |
US5807494A (en) * | 1994-12-15 | 1998-09-15 | Boes; Ralph Ulrich | Gel compositions comprising silica and functionalized carbon products |
EP0933078A3 (fr) * | 1997-12-10 | 2000-02-09 | Degussa-Hüls Aktiengesellschaft | Silices précipitées contenant un agent actif |
ATE312905T1 (de) * | 1998-05-15 | 2005-12-15 | Isp Investments Inc | Vormischungszusammensetzung zur bierklärung |
US7241729B2 (en) * | 1999-05-26 | 2007-07-10 | Rhodia Inc. | Compositions and methods for using polymeric suds enhancers |
CA2562511A1 (fr) | 2004-04-23 | 2005-12-15 | Genencor International, Inc. | Procede de prevention ou de reduction de trouble dans une boisson a l'aide de couches filtrantes a base de silice traitee avec des silanes |
EP2049225B1 (fr) | 2006-07-14 | 2014-09-03 | Imerys Filtration Minerals, Inc. | Composition pour la filtration et l'élimination de particules et/ou de constituants d'un fluide |
-
2007
- 2007-07-13 EP EP07799552.0A patent/EP2049225B1/fr active Active
- 2007-07-13 CN CN2007800334886A patent/CN101528320B/zh active Active
- 2007-07-13 EP EP13177485.3A patent/EP2684589B1/fr active Active
- 2007-07-13 US US12/373,753 patent/US20090261041A1/en not_active Abandoned
- 2007-07-13 PL PL13177485.3T patent/PL2684589T3/pl unknown
- 2007-07-13 PL PL07799552T patent/PL2049225T3/pl unknown
- 2007-07-13 WO PCT/US2007/073439 patent/WO2008008940A2/fr active Application Filing
-
2012
- 2012-03-16 US US13/421,915 patent/US20120172195A1/en not_active Abandoned
-
2016
- 2016-06-14 US US15/182,297 patent/US10066197B2/en active Active
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5017354A (en) * | 1988-09-02 | 1991-05-21 | Akzo America Inc. | Process for production of high purity silica gel |
US6712974B1 (en) * | 1997-01-10 | 2004-03-30 | Advanced Minerals Corporation | Filterable composite adsorbents |
US6712898B2 (en) * | 2000-08-08 | 2004-03-30 | Advanced Minerals Corporation | Perlite products with controlled particle size distribution |
Cited By (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9284200B2 (en) * | 2008-08-13 | 2016-03-15 | Contech Engineered Solutions LLC | Thermally treated expanded perlite |
US20100038327A1 (en) * | 2008-08-13 | 2010-02-18 | Contech Stormwater Solutions Inc. | Thermally treated expanded perlite |
JP2013537484A (ja) * | 2010-08-18 | 2013-10-03 | ワールド ミネラルズ,インコーポレイテッド | 新規性のある細孔サイズ特性を有する複合濾過補助剤 |
US10105679B2 (en) | 2012-06-26 | 2018-10-23 | Imerys Filtration Minerals, Inc. | Co-agglomerated composite materials |
WO2014004349A1 (fr) | 2012-06-26 | 2014-01-03 | Imerys Filtration Minerals, Inc. | Matériaux composites co-agglomérés, procédés de fabrication de matériaux composites co-agglomérés et procédés d'utilisation de matériaux composites co-agglomérés |
CN104718021A (zh) * | 2012-06-26 | 2015-06-17 | 英默里斯筛选矿物公司 | 共烧结的复合材料、制备共烧结的复合材料的方法和使用共烧结的复合材料的方法 |
US10556221B2 (en) | 2012-06-26 | 2020-02-11 | Imerys Usa, Inc. | Co-agglomerated composite materials |
US20160168204A1 (en) * | 2013-06-28 | 2016-06-16 | Daiichi Sankyo Company, Limited | Method for purifying oligosaccharide peptide |
EP3086875A4 (fr) * | 2013-12-26 | 2017-08-23 | Imerys Filtration Minerals, Inc. | Matériaux composites co-agglomérés, procédés de fabrication de matériaux composites co-agglomérés, et procédés d'utilisation de matériaux composites co-agglomérés |
US10226750B2 (en) | 2013-12-26 | 2019-03-12 | Imerys Filtration Minerals, Inc. | Co-agglomerated composite materials, methods for making co-agglomerated composite materials, and methods for using co-agglomerated composite materials |
WO2015100050A1 (fr) | 2013-12-26 | 2015-07-02 | Imerys Filtration Minerals, Inc. | Matériaux composites co-agglomérés, procédés de fabrication de matériaux composites co-agglomérés, et procédés d'utilisation de matériaux composites co-agglomérés |
US10391433B2 (en) | 2014-12-19 | 2019-08-27 | Ep Minerals, Llc | Opaline biogenic silica/expanded perlite composite products |
US20180236383A1 (en) * | 2015-02-26 | 2018-08-23 | Imerys Filtration Minerals, Inc. | Filter aids for biodiesel and edible oil filtration and methods and uses of the filtering aids |
WO2017019845A1 (fr) * | 2015-07-29 | 2017-02-02 | Imerys Filtration Minerals, Inc. | Moyen auxiliaire de filtration composite de résistance au froid et procédés associés |
US20190112395A1 (en) * | 2016-03-29 | 2019-04-18 | Ch-Bioforce Oy | Method of producing hemicellulose extracts |
US11046790B2 (en) * | 2016-03-29 | 2021-06-29 | Ch-Bioforce Oy | Method of producing hemicellulose extracts |
WO2019046499A1 (fr) * | 2017-08-31 | 2019-03-07 | Imerys Filtration Minerals, Inc. | Accessoire de filtration à base de perlite haute densité |
US20190076817A1 (en) * | 2017-09-14 | 2019-03-14 | Andrew Ungerleider | Method and apparatus using foamed glass filters for liquid purification, filtration, and filtrate removal and elimination |
JP2021506568A (ja) * | 2017-12-14 | 2021-02-22 | アイメリーズ ユーエスエー,インコーポレーテッド | 油を処理する濾過助剤並びにその作製方法及び使用 |
JP7507087B2 (ja) | 2017-12-14 | 2024-06-27 | アイメリーズ ユーエスエー,インコーポレーテッド | 油を処理する濾過助剤並びにその作製方法及び使用 |
JP7482869B2 (ja) | 2018-11-29 | 2024-05-14 | イメルテック ソシエテ パル アクシオン サンプリフィエ | 鉱物組成物 |
CN113272041A (zh) * | 2018-12-18 | 2021-08-17 | 美国达拉斯集团公司 | 具有多个突起的过滤器 |
Also Published As
Publication number | Publication date |
---|---|
US20120172195A1 (en) | 2012-07-05 |
CN101528320B (zh) | 2013-11-20 |
PL2049225T3 (pl) | 2015-03-31 |
US20160289618A1 (en) | 2016-10-06 |
WO2008008940A2 (fr) | 2008-01-17 |
US10066197B2 (en) | 2018-09-04 |
PL2684589T3 (pl) | 2022-11-21 |
WO2008008940A3 (fr) | 2008-04-10 |
EP2684589B1 (fr) | 2022-06-22 |
EP2049225A4 (fr) | 2010-09-08 |
CN101528320A (zh) | 2009-09-09 |
EP2684589A1 (fr) | 2014-01-15 |
EP2049225A2 (fr) | 2009-04-22 |
EP2049225B1 (fr) | 2014-09-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US10066197B2 (en) | Composition for filtering and removing particles and/or constituents from a fluid | |
US8242050B2 (en) | Composite filter aids having novel pore size characteristics | |
US6712974B1 (en) | Filterable composite adsorbents | |
US10556221B2 (en) | Co-agglomerated composite materials | |
JP2013537484A6 (ja) | 新規性のある細孔サイズ特性を有する複合濾過補助剤 | |
US10226750B2 (en) | Co-agglomerated composite materials, methods for making co-agglomerated composite materials, and methods for using co-agglomerated composite materials | |
US20190270067A1 (en) | Composite filter aids and methods of using composite filter aids | |
US20170361306A1 (en) | Diatomaceous earth products, processes for preparing them, and methods of their use | |
EP3328515B1 (fr) | Moyen de filtration composite auxiliaire etant résistant au froid et procédés associés | |
WO1998030324A2 (fr) | Adsorbants composites pouvant etre filtres |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: WORLD MINERALS, INC., CALIFORNIA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HU, QINGCHUN;NYAMEKYE, GEORGE A.;REES, ROBERT H.;AND OTHERS;REEL/FRAME:022697/0440;SIGNING DATES FROM 20090128 TO 20090412 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |