WO1998030324A2 - Adsorbants composites pouvant etre filtres - Google Patents

Adsorbants composites pouvant etre filtres Download PDF

Info

Publication number
WO1998030324A2
WO1998030324A2 PCT/US1997/023571 US9723571W WO9830324A2 WO 1998030324 A2 WO1998030324 A2 WO 1998030324A2 US 9723571 W US9723571 W US 9723571W WO 9830324 A2 WO9830324 A2 WO 9830324A2
Authority
WO
WIPO (PCT)
Prior art keywords
adsorbent
expanded
filterable composite
filterable
composite adsorbent
Prior art date
Application number
PCT/US1997/023571
Other languages
English (en)
Other versions
WO1998030324A3 (fr
Inventor
Scott K. Palm
Timothy R. Smith
Jerome C. Shiuh
John S. Roulston
Original Assignee
Advanced Minerals Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Advanced Minerals Corporation filed Critical Advanced Minerals Corporation
Priority to AU58031/98A priority Critical patent/AU5803198A/en
Publication of WO1998030324A2 publication Critical patent/WO1998030324A2/fr
Publication of WO1998030324A3 publication Critical patent/WO1998030324A3/fr

Abstract

Cette invention porte sur des adsorbants composites pouvant être filtrés et comprenant un ou plusieurs composants adsorbants et un ou plusieurs composants filtrants, sur leurs procédés de préparation et d'utilisation. Cette invention porte plus particulièrement sur des adsorbants composites pouvant être filtrés et sur des produits de ceux-ci appropriés pour être utilisés dans des applications de filtration. Ces adsorbants et leurs produits comprennent un ou plusieurs composants adsorbants microparticulaires ou colloïdaux sélectionnés dans le groupe constitué par un gel de silice, une silice sublimée, de l'argile neutre, de l'argile alcaline, une zéolite, un catalyseur solide, une alumine, un polymère adsorbant, un hydrate de silicate alcalino-terreux et des combinaisons de ceux-ci, tous ces composants possédant des propriétés d'adsorption, et étant intimement liés à un ou plusieurs composants filtrants fonctionnels sélectionnés dans le groupe constitué par une silice biogène, un verre naturel (tels que la perlite expansée, la pierre ponce, la pierre ponce expansée, la pumicite, l'obsidienne expansée, la cendre volcanique expansée), un verre flotté, un polymère flotté, une cellulose et des combinaisons de ceux-ci, ces composants présentant une structure particulière, complexe et poreuse, et une flottabilité appropriée à la filtration.
PCT/US1997/023571 1997-01-10 1997-12-31 Adsorbants composites pouvant etre filtres WO1998030324A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU58031/98A AU5803198A (en) 1997-01-10 1997-12-31 Filterable composite adsorbents

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US78132597A 1997-01-10 1997-01-10
US08/781,325 1997-01-10

Publications (2)

Publication Number Publication Date
WO1998030324A2 true WO1998030324A2 (fr) 1998-07-16
WO1998030324A3 WO1998030324A3 (fr) 1998-11-05

Family

ID=25122362

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1997/023571 WO1998030324A2 (fr) 1997-01-10 1997-12-31 Adsorbants composites pouvant etre filtres

Country Status (2)

Country Link
AU (1) AU5803198A (fr)
WO (1) WO1998030324A2 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110548480A (zh) * 2019-10-14 2019-12-10 广汉市迈德乐食品有限公司 一种用于火锅牛油的脱胶吸附剂及其应用

Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1375532A (en) * 1917-03-16 1921-04-19 Muller Enrique Filtering material
FR1241881A (fr) * 1959-08-14 1960-09-23 Absorbants, en particulier pour la purification de substances en phase liquide, leurpréparation et leurs applications
GB1116664A (en) * 1964-04-30 1968-06-12 Union Carbide Corp Process for preparing a coated zeolitic molecular sieve agglomerate
US3813347A (en) * 1970-10-05 1974-05-28 Universal Oil Prod Co Manufacture of adsorbent composite
GB1373394A (en) * 1970-10-08 1974-11-13 Poegel H J Building elements
US4059544A (en) * 1972-08-10 1977-11-22 Fujimi Kenmazai Kogyo Kabushiki Kaisha Active material compositions with porous protective sheath and method for preparing
EP0144200A2 (fr) * 1983-12-01 1985-06-12 Ecc International Limited Séparation de composés organiques de liquides aqueux
GB2166427A (en) * 1984-11-06 1986-05-08 Kenneth Mckenzie Brown Composition - silicate bound pumice, pulverised fuel ash, light expanded clay aggregates, cintered clay, furnace bottom ash, sand and or aerated concrete
US4732887A (en) * 1984-10-12 1988-03-22 Asahi Kasei Kogyo Kabushiki Kaisha Composite porous material, process for production and separation of metallic element
US5077070A (en) * 1989-07-07 1991-12-31 Gycor International, Ltd. Method of making a composite filter material and its use in treating edible oils
US5104632A (en) * 1989-02-23 1992-04-14 Minnesota Mining And Manufacturing Company Method of making thin silica flakes
EP0573303A1 (fr) * 1992-06-05 1993-12-08 Peter Barnes Sorbant granulaire stabilisant de liquides
US5484620A (en) * 1990-12-22 1996-01-16 Schenk-Filterbau Gesellschaft Mit Beschrankter Haftung Method of manufacturing stabilizing and/or filtering aids for use in the processing of liquids, especially beverages
EP0790070A1 (fr) * 1996-02-16 1997-08-20 Advanced Minerals Corporation Milieux filtrants composites

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3331018B2 (ja) * 1993-08-04 2002-10-07 昭和化学工業株式会社 ケイソウ土・パーライト複合濾過助剤およびその製造方法

Patent Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1375532A (en) * 1917-03-16 1921-04-19 Muller Enrique Filtering material
FR1241881A (fr) * 1959-08-14 1960-09-23 Absorbants, en particulier pour la purification de substances en phase liquide, leurpréparation et leurs applications
GB1116664A (en) * 1964-04-30 1968-06-12 Union Carbide Corp Process for preparing a coated zeolitic molecular sieve agglomerate
US3813347A (en) * 1970-10-05 1974-05-28 Universal Oil Prod Co Manufacture of adsorbent composite
GB1373394A (en) * 1970-10-08 1974-11-13 Poegel H J Building elements
US4059544A (en) * 1972-08-10 1977-11-22 Fujimi Kenmazai Kogyo Kabushiki Kaisha Active material compositions with porous protective sheath and method for preparing
EP0144200A2 (fr) * 1983-12-01 1985-06-12 Ecc International Limited Séparation de composés organiques de liquides aqueux
US4732887A (en) * 1984-10-12 1988-03-22 Asahi Kasei Kogyo Kabushiki Kaisha Composite porous material, process for production and separation of metallic element
GB2166427A (en) * 1984-11-06 1986-05-08 Kenneth Mckenzie Brown Composition - silicate bound pumice, pulverised fuel ash, light expanded clay aggregates, cintered clay, furnace bottom ash, sand and or aerated concrete
US5104632A (en) * 1989-02-23 1992-04-14 Minnesota Mining And Manufacturing Company Method of making thin silica flakes
US5077070A (en) * 1989-07-07 1991-12-31 Gycor International, Ltd. Method of making a composite filter material and its use in treating edible oils
US5484620A (en) * 1990-12-22 1996-01-16 Schenk-Filterbau Gesellschaft Mit Beschrankter Haftung Method of manufacturing stabilizing and/or filtering aids for use in the processing of liquids, especially beverages
EP0573303A1 (fr) * 1992-06-05 1993-12-08 Peter Barnes Sorbant granulaire stabilisant de liquides
EP0790070A1 (fr) * 1996-02-16 1997-08-20 Advanced Minerals Corporation Milieux filtrants composites

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 095, no. 005, 30 June 1995 & JP 07 047266 A (SHOWA KAGAKU KOGYO KK), 21 February 1995 *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110548480A (zh) * 2019-10-14 2019-12-10 广汉市迈德乐食品有限公司 一种用于火锅牛油的脱胶吸附剂及其应用

Also Published As

Publication number Publication date
AU5803198A (en) 1998-08-03
WO1998030324A3 (fr) 1998-11-05

Similar Documents

Publication Publication Date Title
US6712974B1 (en) Filterable composite adsorbents
US10066197B2 (en) Composition for filtering and removing particles and/or constituents from a fluid
US10556221B2 (en) Co-agglomerated composite materials
CA2241946C (fr) Milieu composite de filtration
JP5988975B2 (ja) 新規性のある細孔サイズ特性を有する複合濾過補助剤
EP2346981B1 (fr) Produits de terre à diatomées, leurs procédés de préparation, et procédés d'utilisation
EP3086875B1 (fr) Matériaux composites co-agglomérés et procédés de fabrication de matériaux composites co-agglomérés
US20190270067A1 (en) Composite filter aids and methods of using composite filter aids
US20200060316A1 (en) High-purity composite materials, methods of making high-purity composite materials, and methods of using high-purity composite materials
WO2013096578A1 (fr) Produits à base de terre à diatomées, leurs procédés de préparation et leurs procédés d'utilisation
WO1998030324A2 (fr) Adsorbants composites pouvant etre filtres

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GM GW HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZW AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW SD SZ UG ZW AT BE CH DE DK ES FI FR GB GR IE IT

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
AK Designated states

Kind code of ref document: A3

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GM GW HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZW AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A3

Designated state(s): GH GM KE LS MW SD SZ UG ZW AT BE CH DE DK ES FI FR GB GR IE IT

121 Ep: the epo has been informed by wipo that ep was designated in this application
WA Withdrawal of international application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

NENP Non-entry into the national phase in:

Ref country code: CA