US20070243098A1 - Lead-Free Solder - Google Patents
Lead-Free Solder Download PDFInfo
- Publication number
- US20070243098A1 US20070243098A1 US11/578,827 US57882706A US2007243098A1 US 20070243098 A1 US20070243098 A1 US 20070243098A1 US 57882706 A US57882706 A US 57882706A US 2007243098 A1 US2007243098 A1 US 2007243098A1
- Authority
- US
- United States
- Prior art keywords
- solder
- lead
- mass
- free solder
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 229910000679 solder Inorganic materials 0.000 title claims abstract description 132
- 229910045601 alloy Inorganic materials 0.000 claims abstract description 42
- 239000000956 alloy Substances 0.000 claims abstract description 42
- 229910052759 nickel Inorganic materials 0.000 claims abstract description 9
- 229910052733 gallium Inorganic materials 0.000 claims abstract description 8
- 229910052725 zinc Inorganic materials 0.000 claims description 2
- 229910020836 Sn-Ag Inorganic materials 0.000 abstract description 3
- 229910020988 Sn—Ag Inorganic materials 0.000 abstract description 3
- 230000000694 effects Effects 0.000 description 14
- 238000004383 yellowing Methods 0.000 description 14
- 235000012431 wafers Nutrition 0.000 description 10
- 238000012360 testing method Methods 0.000 description 9
- 229910017518 Cu Zn Inorganic materials 0.000 description 8
- 238000000034 method Methods 0.000 description 8
- 238000005476 soldering Methods 0.000 description 8
- 229910020220 Pb—Sn Inorganic materials 0.000 description 7
- 238000010438 heat treatment Methods 0.000 description 7
- 229910017752 Cu-Zn Inorganic materials 0.000 description 6
- 229910017943 Cu—Zn Inorganic materials 0.000 description 6
- PCHJSUWPFVWCPO-UHFFFAOYSA-N gold Chemical compound [Au] PCHJSUWPFVWCPO-UHFFFAOYSA-N 0.000 description 6
- 230000000052 comparative effect Effects 0.000 description 5
- 230000003247 decreasing effect Effects 0.000 description 5
- 239000000203 mixture Substances 0.000 description 5
- 238000003878 thermal aging Methods 0.000 description 5
- 238000002845 discoloration Methods 0.000 description 4
- 238000007689 inspection Methods 0.000 description 4
- 238000002844 melting Methods 0.000 description 4
- 230000008018 melting Effects 0.000 description 4
- 238000003916 acid precipitation Methods 0.000 description 3
- 239000011521 glass Substances 0.000 description 3
- 229910052737 gold Inorganic materials 0.000 description 3
- 239000010931 gold Substances 0.000 description 3
- 229910052751 metal Inorganic materials 0.000 description 3
- 239000002184 metal Substances 0.000 description 3
- 229910017944 Ag—Cu Inorganic materials 0.000 description 2
- 239000004593 Epoxy Substances 0.000 description 2
- 229910020830 Sn-Bi Inorganic materials 0.000 description 2
- 229910020888 Sn-Cu Inorganic materials 0.000 description 2
- 229910020935 Sn-Sb Inorganic materials 0.000 description 2
- 229910020994 Sn-Zn Inorganic materials 0.000 description 2
- 229910018728 Sn—Bi Inorganic materials 0.000 description 2
- 229910019204 Sn—Cu Inorganic materials 0.000 description 2
- 229910008757 Sn—Sb Inorganic materials 0.000 description 2
- 229910009069 Sn—Zn Inorganic materials 0.000 description 2
- 229910002056 binary alloy Inorganic materials 0.000 description 2
- 230000015572 biosynthetic process Effects 0.000 description 2
- 238000009933 burial Methods 0.000 description 2
- 229910052802 copper Inorganic materials 0.000 description 2
- 230000007423 decrease Effects 0.000 description 2
- 239000011888 foil Substances 0.000 description 2
- 239000000463 material Substances 0.000 description 2
- 229910052709 silver Inorganic materials 0.000 description 2
- 239000000758 substrate Substances 0.000 description 2
- 238000010998 test method Methods 0.000 description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 2
- 206010027439 Metal poisoning Diseases 0.000 description 1
- 229910020816 Sn Pb Inorganic materials 0.000 description 1
- 229910020922 Sn-Pb Inorganic materials 0.000 description 1
- 229910008783 Sn—Pb Inorganic materials 0.000 description 1
- 229910052782 aluminium Inorganic materials 0.000 description 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 1
- 229910052787 antimony Inorganic materials 0.000 description 1
- 238000003491 array Methods 0.000 description 1
- 239000010953 base metal Substances 0.000 description 1
- 230000005540 biological transmission Effects 0.000 description 1
- 229910052797 bismuth Inorganic materials 0.000 description 1
- 230000008602 contraction Effects 0.000 description 1
- 230000007797 corrosion Effects 0.000 description 1
- 238000005260 corrosion Methods 0.000 description 1
- 230000007547 defect Effects 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 238000003384 imaging method Methods 0.000 description 1
- 238000009863 impact test Methods 0.000 description 1
- 229910052738 indium Inorganic materials 0.000 description 1
- 208000008127 lead poisoning Diseases 0.000 description 1
- 244000144972 livestock Species 0.000 description 1
- 230000007257 malfunction Effects 0.000 description 1
- 238000004519 manufacturing process Methods 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 238000007747 plating Methods 0.000 description 1
- 239000010970 precious metal Substances 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 238000011160 research Methods 0.000 description 1
- 239000011347 resin Substances 0.000 description 1
- 229920005989 resin Polymers 0.000 description 1
- 230000008646 thermal stress Effects 0.000 description 1
- 229910052718 tin Inorganic materials 0.000 description 1
- 239000011800 void material Substances 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
- B23K35/24—Selection of soldering or welding materials proper
- B23K35/26—Selection of soldering or welding materials proper with the principal constituent melting at less than 400 degrees C
- B23K35/262—Sn as the principal constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C13/00—Alloys based on tin
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K2101/00—Articles made by soldering, welding or cutting
- B23K2101/36—Electric or electronic devices
Definitions
- This invention relates to a solder alloy which does not contain lead, and particularly to a lead-free solder alloy which is suitable for forming minute soldered portions such as solder bumps.
- solder bumps In general, mounting of multi-functional parts such as BGA's (ball grid arrays) or CSP's (chip size packages) (referred to below as BGA's and the like) on a printed circuit board is carried out using solder bumps. Namely, at the time of mounting on a printed circuit board, solder bumps previously formed on the electrodes of a BGA or the like are made to contact the portions to be soldered of the printed circuit board, and then heating is performed in a heating apparatus such as a reflow furnace to melt the bumps. As a result, the solder bumps formed on the BGA or the like solder the electrodes of the BGA or the like to the printed circuit board and they are electrically connected to each other.
- a heating apparatus such as a reflow furnace
- wire bonding is carried out using extremely fine gold wires to connect between the electrodes of the wafer and the electrodes of a workpiece on which the wafer is to be mounted.
- Present-day wire bonding techniques can perform connection at an extremely high speed, and connection of one location can now be performed in a short period of 0.1 seconds or less.
- no matter how rapidly wire bonding is carried out since a gold wire must be connected to each electrode and an electronic part has a large number of electrodes, time is required to connect all the electrodes.
- gold wire is made of a precious metal, and not only is the material itself expensive, but many man hours are required to form extremely fine wires having a diameter of several tens of ⁇ m. Thus, costs are further increased.
- wire bonding is not possible with respect to a workpiece having a large number of electrodes at its center because the gold wires end up contacting each other.
- the DCA (direct chip attachment) method in which electrical connection between a wafer and a workpiece is carried out by directly connecting the electrodes thereof without using gold wires has come to be employed.
- solder bumps are previously formed on the electrodes of a wafer, and when the wafer is mounted on a workpiece, the solder bumps are made to contact the electrodes of the workpiece, and both parts are electrically connected to each other by melting the solder bumps.
- the DCA method can inexpensively perform manufacture without using gold wire. All the electrodes can be connected in a single operation, and it has excellent productivity. Accordingly, recently, connection of electrodes by the DCA method has come to make extensive use of connection by means of solder bumps.
- Connection using solder bumps can be performed by placing the electrodes of a workpiece and a member to be mounted thereon opposite each other and connecting them by the bumps, even when a large number of electrodes are disposed at the center of a workpiece. Contact of wires with each other such as occurs with wire bonding does not take place.
- solder balls and solder paste are generally used as methods of forming solder bumps on BGA's and the like or wafers.
- a conventional solder alloy for use in forming solder bumps was a Pb—Sn base solder alloy.
- Pb—Sn base solder alloys have been much used for solder balls and solder paste for forming solder bumps on the above-described BGA's and the like or wafers.
- Pb—Sn base solder alloys have excellent solderabilty. When soldering of a workpiece and a printed circuit board is performed using a Pb—Sn base solder alloy, highly reliable soldering with little occurrence of soldering defects is carried out.
- Lead-free solder is solder having Sn as a main component to which Ag, Bi, Cu, Sb, In, Ni, Zn, or the like is suitably added.
- lead-free solders there have been binary alloys having Sn as a main component such as Sn—Cu, Sn—Sb, Sn—Bi, Sn—Zn, and Sn—Ag, and multiple-element lead free solders in which other elements are added to these binary alloys.
- a lead-free solder alloy having Sn as a main component has inferior solderability compared to a conventional Pb—Sn solder, but binary and multiple-element Sn—Cu base and Sn—Sb base solders are even worse.
- solder With Sn—Bi base solders, the solder becomes brittle, so when an impact is applied to soldered joints, not only do they easily break, but lift-off may occur if a small amount of Pb is mixed in from the plating on leads. Since Zn is a base metal, when Sn—Zn base alloys are made into a solder paste, changes with the passage of time take place, and problems may occur such as it becoming impossible to perform application thereof by printing or of electrical corrosion occurring between soldered joints after soldering. As a lead-free solder having Sn as a primary component, a Sn—Ag base solder is superior to other binary lead-free solders with respect to solderability, brittleness, changes over time, and the like.
- the resistance to heat cycles of lead-free solders is not inferior to that of Pb—Sn solder alloys, and a Sn—Ag—Cu base solder alloy has excellent resistance to heat cycles (Japanese Published Unexamined Patent Application (Kokai) Hei 3-050286).
- So-called mobile electronic equipment such as portable telephones, notebook computers, and digital cameras have come to demand excellent impact resistance of soldered joints connecting electronic parts within the electronic equipment. This is because mobile electronic equipment often receives impacts. When the electronic equipment peels off at soldered joints as a result of the impact, the electronic equipment can no longer perform its function. For example, a portable telephone which is placed into a shirt pocket may slip out and fall from the pocket when the user bends forward, and recent portable telephones which have an e-mail function may be dropped when being operated with one hand. In addition, when a notebook computer is carried in a briefcase, the entire briefcase is often dropped, and digital cameras are often dropped during use. Therefore, solder used in mobile electronic equipment has come to require excellent impact resistance.
- Lead-free solder alloys have a tendency to be weaker with respect to impacts from dropping compared to Pb—Sn base solder alloys.
- a lead-free solder which has good resistance to impacts from dropping is a lead-free solder characterized by comprising 0.5-5 mass % of Ag, 0.01-0.1 mass % of Cu, 0.001-0.05 mass % of P, and a remainder of Sn (Japanese Patent Application 2003-000788).
- Patent Document 1 Japanese Published Unexamined Patent Application (Kokai) Hei 3-050286
- Patent Document 2 Japanese Patent Application 2003-000788
- Patent Document 3 Japanese Published Unexamined Patent Application (Kokai) 2003-326386
- Patent Document 4 Japanese Published Unexamined Patent Application (Kokai) 2002-185130
- Sn—Ag—Cu base lead-free solder alloys having excellent resistance to heat cycles could not be said to have sufficient impact resistance, particularly with respect to soldered joints having a small soldered area.
- recent electronic equipment has been increasing in performance and decreasing in size, and electronic parts incorporated therein are also becoming higher in performance and smaller in size.
- Solder bumps formed on the electrodes of electronic parts which are becoming smaller in this manner are also decreasing in size. If the solder in small soldered joints of lead-free solder has poor impact resistance, when an impact is imparted such as when the electronic equipment is dropped, the soldered joints can easily peel off, and the electronic equipment cannot perform its intended function.
- the lead-free solder of Patent Document 2 is a solder alloy having good resistance to impacts from dropping, but there is still a demand for a lead-free solder alloy which has greater impact resistance after exposure to thermal aging and which is not damaged even when electronic equipment having minute soldered joints is dropped and which has both adequate impact resistance and adequate resistance to heat cycles.
- the present inventors found that by adding a minute amount of Zn to a lead-free solder alloy composition of Sn, Ag, and Cu, a lead-free solder alloy is obtained which has adequate impact resistance even after exposure to thermal aging and also has adequate resistance to heat cycles.
- the present invention is a lead-free solder alloy characterized by comprising 0.1-less than 2.0 mass % of Ag, 0.01-0.2 mass % of Cu, 0.005-0.1 mass % of Zn, and a remainder of Sn.
- Ag has an effect on resistance to heat cycles. If the added amount thereof is less than 0.1 mass %, it has no effect on improving resistance to heat cycles, while if more than 2.0 mass % is added, impact resistance ends up decreasing.
- Cu can increase impact resistance. If the added amount of Cu is less than 0.01 mass %, the effect of improving impact resistance is not obtained, while if it is contained in excess of 0.2 mass %, many voids end up being formed in soldered joints.
- the addition of Zn has an effect on impact resistance after thermal aging. If the added amount is less than 0.005 mass %, it has no effect on improving impact resistance, while if it is added in excess of 0.1 mass %, the wettability of the solder alloy is markedly decreased, and the frequency of occurrence of voids increases.
- At least one of Ga, Ge, and P can also be added in an amount of 0.0005-0.1 mass %. These elements have the effect of preventing yellowing of a lead-free solder. Yellowing can be ascertained by performing a high temperature exposure test on an electronic part such as a BGA using a lead-free solder. The conditions of a high temperature exposure test vary depending upon the maker of electronic parts or the maker of electronic equipment, but yellowing can be readily determined by exposure to a high temperature atmosphere at 125° C. for 200 hours.
- Ga, Ge, and P have the effect of preventing yellowing. To prevent yellowing, it is necessary to add at least one of these in an amount of 0.0005 mass %. If more than 0.1 mass % of Ga, Ge, or P is added, solderability is worsened.
- Ni or Co can be further added in an amount of 0.01-0.1 mass % to an Ag—Cu—Zn base lead-free solder to which at least one of Ga, Ge, and P has been added.
- the effect is obtained of improving resistance to heat cycles.
- This effect is obtained if the total of Ni and Co is at least 0.01 mass %, but if more than 0.1 mass % is added, the melting point of the solder increases, and unmelted portions remain during soldering.
- the present invention has the object of increasing impact resistance and improving resistance to heat cycles of minute soldered joints.
- An application for which this object is appropriate is solder bumps, but the effect of improving impact resistance and resistance to heat cycles can also be exhibited in ordinary soldering.
- solder balls or solder paste to form solder bumps. Namely, with BGA's and the like, solder balls are mounted on the substrate of a BGA and the like, and solder bumps are formed by melting the solder balls, while with a wafer, a solder paste is applied atop the wafer, and solder bumps are formed by melting the solder paste.
- a lead-free solder alloy according to the present invention is superior to conventional lead-free solder alloys with respect to impact resistance and resistance to heat cycles after bump formation. Namely, the solder alloy of the present invention has excellent reliability in that soldered joints do not readily peel off when electronic equipment is accidentally dropped during use or during transport, and in that even if use and non-use of electronic equipment are repeated over a long period, soldered joints do not peel off due to heat cycles.
- a lead-free solder alloy according to the present invention does not undergo yellowing even in a high temperature test following bump formation. Namely, errors do not occur during inspection of solder bumps by imaging, and excellent effects are also provided with respect to ability to undergo inspection.
- solder alloys according to the present invention having the compositions shown in Table 1 were prepared, and together with comparative examples of solder alloys, they were subjected to a dropping impact resistance test, a heat cycle resistance test, and a discoloration test.
- examples of the present invention and comparative examples of solder alloys having the compositions shown in Table 2 were prepared, and the occurrence of voids was compared.
- Dropping impact resistance An impact was applied between a CSP and a printed circuit board soldered by soldered bumps by dropping, and the number of times that dropping was performed until cracks formed in the soldered joints was measured. Measurement was performed after holding at room temperature after soldering and after 100 hours of heat treatment at 125° C.
- a solder paste was applied by printing to a 10 ⁇ 10 mm CSP having 150 electrodes, and solder balls having a diameter of 0.3 mm were mounted thereon.
- the CSP on which the solder balls were mounted was heated in a reflow furnace, and solder bumps were formed on the electrodes.
- the CSP on which the solder bumps were formed was mounted at the center of a glass epoxy printed circuit board measuring 30 ⁇ 120 mm, heating was performed in a reflow furnace, and the CSP was soldered to the printed circuit board.
- An impact was imparted to the printed circuit board by dropping the jig from a height of 500 mm. At this time, the center of the printed circuit board having both ends secured to the jig vibrated, and an impact was applied to the soldered joints connecting the printed circuit board and the CSP substrate by the vibration. Using this dropping test, the number of times that dropping was performed until cracks formed in the soldered joints of the CSP was measured. One hundred or more times in an initial state and forty or more times after heat treatment were evaluated as good.
- Heat cycles were applied to a printed circuit board on which electronic parts were mounted, and the number of cycles until failure of a soldered joint was measured.
- Solder paste was applied by printing to a CSP measuring 10 ⁇ 10 mm and having 150 electrodes, and solder balls with a diameter of 0.3 mm were counted thereon.
- the CSP on which the solder balls were mounted was heated in a reflow furnace, and solder bumps were formed on the electrodes.
- the CSP on which the solder bumps were formed was mounted on a glass epoxy printed circuit board measuring 120 ⁇ 140 mm, heating was performed in a reflow furnace, and the CSP was soldered to the printed circuit board.
- the printed circuit board to which the CSP was soldered was placed into a heat cycle tester, it was subjected to heat cycles comprising exposure to ⁇ 40° C. for 10 minutes and +120° C. for 10 minutes, and the number of cycles until the occurrence of failure of the soldered joints was measured. A value of 1500 cycles or higher was considered good.
- Discoloration test Yellowing of the solder surface after high temperature heating was visually observed.
- Solder balls with a diameter of 0.3 mm were mounted on a CSP.
- solder balls mounted on the CSP were melted in a reflow furnace to form solder bumps.
- Voids in the solder bumps on the CSP were observed using an X-ray radiographic inspection apparatus, and the rate of occurrence was calculated.
- Solder balls with a diameter of 0.3 mm were mounted on a CSP.
- the CSP on which the solder balls were mounted was heated in a reflow furnace to form solder bumps.
- the CSP on which the solder bumps were formed was placed into an x-ray transmission apparatus, and the strength and contrast were set to permit voids in the bumps to be detected.
- the number of bumps having voids was divided by the number of observed bumps to calculate the rate of occurrence of voids. A rate of void occurrence of 30% or less was evaluated as good.
- a lead-free solder alloy according to the present invention is superior in that it has excellent impact resistance and resistance to heat cycles after exposure to thermal aging and in that it has little discoloration of solder or occurrence of voids.
- a lead-free solder alloy according to the present invention can be applied to all manner of small electronic equipment capable of being dropped, including printed circuit boards for mobile equipment such as portable phones, notebook computers, and digital cameras, as well as remote controls and hand tools.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Electric Connection Of Electric Components To Printed Circuits (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/JP2004/010803 WO2006011204A1 (ja) | 2004-07-29 | 2004-07-29 | 鉛フリーはんだ合金 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20070243098A1 true US20070243098A1 (en) | 2007-10-18 |
Family
ID=35785963
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/578,827 Abandoned US20070243098A1 (en) | 2004-07-29 | 2004-07-29 | Lead-Free Solder |
Country Status (6)
Country | Link |
---|---|
US (1) | US20070243098A1 (ja) |
EP (1) | EP1772225A4 (ja) |
JP (1) | JP3827322B2 (ja) |
CN (1) | CN1905985B (ja) |
TW (1) | TWI275648B (ja) |
WO (1) | WO2006011204A1 (ja) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070069379A1 (en) * | 2003-10-07 | 2007-03-29 | Daisuke Souma | Lead-free solder ball |
US20090289102A1 (en) * | 2005-07-19 | 2009-11-26 | Nihon Superior Sha Co., Ltd. | SOLDER FREE FROM LEAD FOR ADDITIONAL SUPPLY AND METHOD OF REGULATING Cu CONCENTRATION AND Ni CONCENTRATION IN SOLDER BATH |
CN102848100A (zh) * | 2012-10-10 | 2013-01-02 | 南京航空航天大学 | 含Nd、Ga的低银Sn-Ag-Cu无铅钎料 |
US9024442B2 (en) | 2010-08-18 | 2015-05-05 | Nippon Steel & Sumikin Materials Co., Ltd. | Solder ball for semiconductor packaging and electronic member using the same |
US9310351B2 (en) | 2010-05-17 | 2016-04-12 | The Procter & Gamble Company | Systems and methods of detecting and demonstrating hair damage via evaluation of protein fragments |
US10773345B2 (en) | 2016-03-08 | 2020-09-15 | Senju Metal Industry Co., Ltd. | Solder alloy, solder ball, chip solder, solder paste, and solder joint |
Families Citing this family (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8691143B2 (en) | 2005-06-03 | 2014-04-08 | Senju Metal Industry Co., Ltd. | Lead-free solder alloy |
JP5322469B2 (ja) * | 2007-09-07 | 2013-10-23 | トゥクサン ハイ‐メタル シーオー エルティディ | 耐落下衝撃性に優れたはんだ合金、およびそれを用いたはんだボール、ならびにはんだ接合部 |
TW200927357A (en) * | 2007-10-17 | 2009-07-01 | Ishikawa Metal Co Ltd | Lead-free solder |
TWI394846B (zh) * | 2008-09-22 | 2013-05-01 | 無鉛含銀焊錫廢渣資源再生之方法 | |
JP4554713B2 (ja) * | 2009-01-27 | 2010-09-29 | 株式会社日本フィラーメタルズ | 無鉛はんだ合金及び該はんだ合金を含む耐疲労性はんだ接合材並びに該接合材を使用した接合体 |
CN101791748A (zh) * | 2010-04-07 | 2010-08-04 | 上海交通大学 | 抑制固态界面反应的Sn-Ag-Cu-Zn-Ge无铅钎料及其制备方法 |
JP5724638B2 (ja) * | 2011-05-30 | 2015-05-27 | 日立金属株式会社 | Pbフリーはんだ及びはんだ被覆導体並びにそれを用いた電気部品 |
CN102554489A (zh) * | 2011-12-28 | 2012-07-11 | 宁波圣之岛焊锡材料有限公司 | 一种低松香无卤素无铅焊锡膏及其制备方法 |
KR20150035671A (ko) * | 2012-08-08 | 2015-04-07 | 센주긴조쿠고교 가부시키가이샤 | 고온 납프리 땜납 합금 |
US9024205B2 (en) | 2012-12-03 | 2015-05-05 | Invensas Corporation | Advanced device assembly structures and methods |
CN103243234B (zh) * | 2013-04-27 | 2015-08-26 | 深圳市同方电子新材料有限公司 | 一种电子封装软钎焊用系列低银无铅钎料及其制备方法 |
CN109014652A (zh) * | 2018-09-26 | 2018-12-18 | 深圳市安臣焊锡制品有限公司 | 一种环保型焊锡材料及其制备工艺 |
CN111673312B (zh) * | 2020-05-29 | 2022-02-22 | 西安理工大学 | 一种电子封装用Sn-Ag-Cu系无铅焊料及其制备方法 |
CN114769936B (zh) * | 2022-04-25 | 2023-09-26 | 深圳市兴鸿泰锡业有限公司 | 一种波峰焊锡条及其制作方法 |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20020051728A1 (en) * | 2000-03-14 | 2002-05-02 | Koji Sato | Solder ball and method for producing same |
US6554180B1 (en) * | 1999-08-20 | 2003-04-29 | Senju Metal Industry Co., Ltd. | Lead-free solder paste |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4152596B2 (ja) * | 2001-02-09 | 2008-09-17 | 新日鉄マテリアルズ株式会社 | ハンダ合金、ハンダボール及びハンダバンプを有する電子部材 |
TW592872B (en) * | 2001-06-28 | 2004-06-21 | Senju Metal Industry Co | Lead-free solder alloy |
JP2003326386A (ja) * | 2002-05-13 | 2003-11-18 | Matsushita Electric Ind Co Ltd | 無鉛はんだ合金 |
JP4023725B2 (ja) * | 2002-05-20 | 2007-12-19 | 日立金属株式会社 | はんだ合金およびはんだボール |
JP2004141910A (ja) * | 2002-10-23 | 2004-05-20 | Senju Metal Ind Co Ltd | 鉛フリーはんだ合金 |
JP2004214468A (ja) * | 2003-01-07 | 2004-07-29 | Senju Metal Ind Co Ltd | リードレス部品および鉛フリーはんだ |
CN1230567C (zh) * | 2003-07-02 | 2005-12-07 | 中国科学院金属研究所 | 一种抗液态表面氧化的工业纯锡及其应用 |
-
2004
- 2004-07-29 CN CN2004800409997A patent/CN1905985B/zh not_active Expired - Lifetime
- 2004-07-29 US US11/578,827 patent/US20070243098A1/en not_active Abandoned
- 2004-07-29 WO PCT/JP2004/010803 patent/WO2006011204A1/ja active Application Filing
- 2004-07-29 EP EP04771016A patent/EP1772225A4/en not_active Withdrawn
- 2004-07-29 JP JP2005518101A patent/JP3827322B2/ja not_active Expired - Lifetime
- 2004-12-07 TW TW093137797A patent/TWI275648B/zh active
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6554180B1 (en) * | 1999-08-20 | 2003-04-29 | Senju Metal Industry Co., Ltd. | Lead-free solder paste |
US20020051728A1 (en) * | 2000-03-14 | 2002-05-02 | Koji Sato | Solder ball and method for producing same |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070069379A1 (en) * | 2003-10-07 | 2007-03-29 | Daisuke Souma | Lead-free solder ball |
US7750475B2 (en) * | 2003-10-07 | 2010-07-06 | Senju Metal Industry Co., Ltd. | Lead-free solder ball |
US20090289102A1 (en) * | 2005-07-19 | 2009-11-26 | Nihon Superior Sha Co., Ltd. | SOLDER FREE FROM LEAD FOR ADDITIONAL SUPPLY AND METHOD OF REGULATING Cu CONCENTRATION AND Ni CONCENTRATION IN SOLDER BATH |
US7861909B2 (en) * | 2005-07-19 | 2011-01-04 | Nihon Superior Sha Co., Ltd. | Replenished lead-free solder and a control method for copper density and nickel density in a solder dipping bath |
US9310351B2 (en) | 2010-05-17 | 2016-04-12 | The Procter & Gamble Company | Systems and methods of detecting and demonstrating hair damage via evaluation of protein fragments |
US9024442B2 (en) | 2010-08-18 | 2015-05-05 | Nippon Steel & Sumikin Materials Co., Ltd. | Solder ball for semiconductor packaging and electronic member using the same |
CN102848100A (zh) * | 2012-10-10 | 2013-01-02 | 南京航空航天大学 | 含Nd、Ga的低银Sn-Ag-Cu无铅钎料 |
US10773345B2 (en) | 2016-03-08 | 2020-09-15 | Senju Metal Industry Co., Ltd. | Solder alloy, solder ball, chip solder, solder paste, and solder joint |
Also Published As
Publication number | Publication date |
---|---|
TW200604349A (en) | 2006-02-01 |
EP1772225A4 (en) | 2009-07-29 |
CN1905985A (zh) | 2007-01-31 |
JPWO2006011204A1 (ja) | 2010-01-21 |
TWI275648B (en) | 2007-03-11 |
JP3827322B2 (ja) | 2006-09-27 |
WO2006011204A1 (ja) | 2006-02-02 |
CN1905985B (zh) | 2010-12-08 |
EP1772225A1 (en) | 2007-04-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8691143B2 (en) | Lead-free solder alloy | |
EP1468777B1 (en) | Lead free solder | |
US20070243098A1 (en) | Lead-Free Solder | |
JP4144415B2 (ja) | 鉛フリーはんだ | |
KR101455966B1 (ko) | 납프리 땜납 볼 | |
JP2004141910A (ja) | 鉛フリーはんだ合金 | |
JP5724411B2 (ja) | はんだ、はんだ付け方法及び半導体装置 | |
US7029542B2 (en) | Lead-free solder alloy | |
JP2003290974A (ja) | 電子回路装置の接合構造及びそれに用いる電子部品 | |
JP2019126827A (ja) | 鉛フリーはんだ合金 | |
JP3852377B2 (ja) | 鉛フリーはんだ合金 | |
US20230129147A1 (en) | Solder Alloy, Solder Ball, and Solder Joint | |
JP2004058085A (ja) | 鉛フリーはんだ合金 | |
KR20070039477A (ko) | 무연 땜납 합금 | |
JP2004214468A (ja) | リードレス部品および鉛フリーはんだ |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: SENJU METAL INDUSTRY CO., LTD., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:OHNISHI, TSUKASA;YAMAKI, TOKURO;AMAGAI, MASAZUMI;AND OTHERS;REEL/FRAME:018448/0254;SIGNING DATES FROM 20060711 TO 20060714 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |
|
AS | Assignment |
Owner name: JPMORGAN CHASE BANK, N.A., ILLINOIS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:THE RELIABLE AUTOMATIC SPRINKLER CO. INC.;REEL/FRAME:067487/0665 Effective date: 20240515 |