US20060235098A1 - Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones - Google Patents
Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones Download PDFInfo
- Publication number
- US20060235098A1 US20060235098A1 US11/108,958 US10895805A US2006235098A1 US 20060235098 A1 US20060235098 A1 US 20060235098A1 US 10895805 A US10895805 A US 10895805A US 2006235098 A1 US2006235098 A1 US 2006235098A1
- Authority
- US
- United States
- Prior art keywords
- combination
- polyol
- catalyst
- hydroxyethyl
- glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 0 [1*]N([Y])CCN([2*])C Chemical compound [1*]N([Y])CCN([2*])C 0.000 description 4
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/08—Processes
- C08G18/16—Catalysts
- C08G18/18—Catalysts containing secondary or tertiary amines or salts thereof
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/08—Processes
- C08G18/16—Catalysts
- C08G18/18—Catalysts containing secondary or tertiary amines or salts thereof
- C08G18/1825—Catalysts containing secondary or tertiary amines or salts thereof having hydroxy or primary amino groups
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
- C08G18/40—High-molecular-weight compounds
- C08G18/42—Polycondensates having carboxylic or carbonic ester groups in the main chain
- C08G18/4244—Polycondensates having carboxylic or carbonic ester groups in the main chain containing oxygen in the form of ether groups
- C08G18/4247—Polycondensates having carboxylic or carbonic ester groups in the main chain containing oxygen in the form of ether groups derived from polyols containing at least one ether group and polycarboxylic acids
- C08G18/4252—Polycondensates having carboxylic or carbonic ester groups in the main chain containing oxygen in the form of ether groups derived from polyols containing at least one ether group and polycarboxylic acids derived from polyols containing polyether groups and polycarboxylic acids
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
- C08G18/40—High-molecular-weight compounds
- C08G18/42—Polycondensates having carboxylic or carbonic ester groups in the main chain
- C08G18/4244—Polycondensates having carboxylic or carbonic ester groups in the main chain containing oxygen in the form of ether groups
- C08G18/4261—Polycondensates having carboxylic or carbonic ester groups in the main chain containing oxygen in the form of ether groups prepared by oxyalkylation of polyesterpolyols
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
- C08J9/04—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent
- C08J9/06—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent by a chemical blowing agent
- C08J9/08—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent by a chemical blowing agent developing carbon dioxide
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G2110/00—Foam properties
- C08G2110/0008—Foam properties flexible
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G2110/00—Foam properties
- C08G2110/0083—Foam properties prepared using water as the sole blowing agent
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2203/00—Foams characterized by the expanding agent
- C08J2203/10—Water or water-releasing compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2205/00—Foams characterised by their properties
- C08J2205/06—Flexible foams
Definitions
- the present invention relates to the use of hydroxyl-containing tertiary amines as catalysts for producing polyurethanes.
- Polyurethane foams are widely known and used in the automotive, housing, and other industries. Such foams are produced by reaction of a polyisocyanate with a polyol in the presence of various additives.
- One such additive is a chlorofluorocarbon (CFC) blowing agent which vaporizes as a result of the reaction exotherm causing the polymerizing mass to form a foam.
- CFC chlorofluorocarbon
- the discovery that CFCs deplete ozone in the stratosphere has resulted in mandates diminishing CFC use.
- Production of water blown foams, in which blowing is performed with CO 2 generated by the reaction of water with the polyisocyanate has therefore become increasingly important.
- Tertiary amine catalysts are typically used to accelerate blowing, for example, the reaction of water with polyisocyanate to generate CO 2 , and gelling, for example, the reaction of a polyol with isocyanate.
- the ability of the tertiary amine catalyst to selectively promote either blowing or gelling is an important consideration in selecting a catalyst for the production of a particular polyurethane foam. If a catalyst promotes the blowing reaction to an excessive degree, much of the CO 2 will be evolved before sufficient reaction of isocyanate with polyol has occurred, and the CO 2 will bubble out of the formulation, resulting in a collapse of the polymerization mass and yielding foam of poor quality. In contrast, if a catalyst too strongly promotes the gelling reaction, a substantial portion of the CO 2 will be evolved after a significant degree of polymerization has occurred. Again, poor quality foams which are characterized by high density, broken or poorly defined cells, or other undesirable features will be produced.
- Tertiary amine catalysts generally are malodorous and offensive and many have high volatility due to their low molecular weight. Release of tertiary amines during foam processing may present significant safety and toxicity problems, and release of residual amines from customer products is generally undesirable. On the other hand, low vapor pressure/high molecular weight amine catalysts are expected to require very high catalyst usage due to their low nitrogen/carbon ratio, making the manufacturing cost too high.
- Tertiary amine catalysts containing hydroxyl functionality can chemically bind into the urethane matrix during the polymerization reaction, thus limiting their release from the finish product.
- amine catalysts which contain primary and/or secondary hydroxyl functionality typically have limited volatility and low odor when compared to related structures without hydroxyl functionality.
- the most effective hydroxyl-containing amine catalysts are the ones containing secondary alcohols in their structures because these catalysts exhibit a desirable balance between their promotion of the active hydrogen-isocyanate reaction (gelling and blowing) and their own reactivity with isocyanates.
- the primary alcohols described in the prior art are highly reactive with isocyanates, they tend to lose their catalytic activity too early in the polymerization process.
- polyurethane foams produced using the primary alcohols described in the art have large voids and exhibit decreased demoldability.
- large amounts of the catalyst compositions containing primary hydroxyl functionality are required to effectively catalyze the blowing reaction. See for example, U.S. Pat. Nos.
- tertiary amine catalysts containing primary hydroxyl functionality are advantageous because they are more efficiently immobilized into the polyurethane matrix before and after polymerization.
- tertiary amines containing primary hydroxyl groups are characterized by lower odor and vapor pressure than their secondary hydroxyl counterparts. It is therefore desirable to produce a tertiary amine catalyst having primary hydroxyl functionality which more effectively promotes the blowing and gelling reactions while retaining their catalytic activity during the polymerization process.
- the present invention relates to a method for preparing polyurethane foams, which comprises contacting at least one organic isocyanate compound, at least one polyol, at least one blowing agent, and a tertiary amine catalyst composition.
- the catalyst composition has the general formula
- the present invention provides a method for making polyurethane foams using tertiary amine catalyst compositions containing primary hydroxyl functionality.
- One aspect of the present invention encompasses producing polyurethane foams by contacting at least one isocyanate compound, at least one polyol compound, at least one blowing agent, and at least one tertiary amine catalyst composition.
- Another aspect of the present invention comprises a method for catalyzing the reaction between at least one isocyanate compound and at least one active hydrogen-containing compound, such as a polyol and/or a blowing agent.
- Catalyst compositions in accordance with the present invention catalyze the reaction between an is isocyanate and an active hydrogen-containing compound.
- the active hydrogen-containing compound can be, for example, an alcohol, a polyol, an amine, or water.
- the catalyst composition can promote, among other reactions, the gelling reaction of polyols with isocyanate to produce polyurethane, the blowing reaction of water with isocyanate to release carbon dioxide, or both reactions.
- the catalyst compositions of the present invention effectively promote the blowing reaction of water with isocyanate.
- the tertiary amine catalyst composition has the general formula
- Catalyst compositions in accordance with the present invention can be prepared by methods generally known in the art, for example, by reacting ethylene oxide with an amine such as triethylenetetramine (TETA), tetraethylenepentamine (TEPA), or pentaethylenehexamine (PEHA).
- TETA triethylenetetramine
- TEPA tetraethylenepentamine
- PEHA pentaethylenehexamine
- the unreacted amine may be removed by distillation.
- the distilled product is reacted with formaldehyde and pressurized hydrogen at approximately 60-120° C. in the presence of a metal catalyst such as 5% palladium on carbon.
- tertiary amine catalyst compositions of this invention include, but are not limited to
- catalyst compositions of the present invention more effectively promote the isocyanate gelling and blowing reactions, are better immobilized in the polyurethane matrix, and have lower vapor pressures.
- the hydroxyl functionality of the catalyst composition enables the catalyst compositions to react with, and be immobilized into, the polyurethane matrix during and after polymerization.
- the prior art discusses tertiary amine catalysts containing primary hydroxyl functionality where n ⁇ 3, but discloses that such catalysts are characterized by lower catalytic activity and higher amine emissions than structurally related catalysts containing secondary hydroxyl functionality.
- the improved properties of the catalysts of the present invention may be attributable to the ability of the higher ethylenediamine backbone (n ⁇ 3) amine catalyst to form a chemical adduct with water.
- Polyurethanes are produced from the polymerization reaction of organic isocyanate compounds with polyol hydroxyl groups.
- Polyols suitable for use in the present invention include, but are not limited to, polyalkylene ether polyols and polyester polyols.
- Polyalkylene ether polyols include poly(alkylene oxide) polymers such as poly(ethylene oxide) and poly(propylene oxide) polymers and copolymers with terminal hydroxyl groups derived from polyhydric compounds, including diols and triols; for example, ethylene glycol, propylene glycol, 1,3-butane diol, 1,4-butane diol, 1,6-hexane diol, neopentyl glycol, diethylene glycol, dipropylene glycol, pentaerythritol, glycerol, diglycerol, trimethylol propane, and similar low molecular weight polyols.
- poly(alkylene oxide) polymers such as poly(ethylene oxide) and poly(propylene oxide) polymers and copolymers with terminal hydroxyl groups derived from polyhydric compounds, including diols and triols; for example, ethylene glycol, propylene glycol, 1,3-butane diol, 1,
- a single high molecular weight polyether polyol may be used.
- a mixture of high molecular weight polyether polyols for example, mixtures of di- and tri-functional materials and/or different molecular weight or different chemical composition materials may be used.
- Such di- and tri-functional materials include, but are not limited to, ethyleneglycol, polyethyleneglycol, propyleneglycol, polypropyleneglycol, glycerine, glycerine-based polyether triols, trimethylolpropane, trimethylolpropane-based polyether triols, 1,3-butane diol, 1,4-butane diol, 1,6-hexane diol, neopentyl glycol, or any combination thereof.
- Useful polyester polyols include, but are not limited to, those produced by reacting a dicarboxylic acid with an excess of a diol, for example, adipic acid with ethylene glycol or butanediol, or reaction of a lactone with an excess of a diol such as caprolactone with propylene glycol.
- polymer polyols are also suitable for use in the present invention.
- Polymer polyols are used in polyurethane foams to increase the foam's resistance to deformation, for example, to improve the load-bearing properties of the foam.
- Examples of polymer polyols include, but are not limited to, graft polyols or polyurea modified polyols (Polyharnstoff Dispersion polyols).
- Graft polyols comprise a triol in which vinyl monomers are graft copolymerized. Suitable vinyl monomers include, for example, styrene, or acrylonitrile.
- a polyurea modified polyol is a polyol containing a polyurea dispersion formed by the reaction of a diamine and a diisocyanate in the presence of a polyol.
- a variant of polyurea modified polyols are polyisocyanate poly addition (PIPA) polyols, which are formed by the in situ reaction of an isocyanate and an alkanolamine in a polyol.
- PIPA polyisocyanate poly addition
- polymer polyols may comprise from about 20 to about 80 percent by weight of the total polyol content.
- Polyurethane foams are typically produced from the reaction of isocyanates with a polyol in the presence of a blowing agent to produce voids in the polyurethane matrix during polymerization.
- Suitable blowing agents include, for example, inert compounds with low boiling points which are vaporized during the exothermic polymerization reaction. Such blowing agents are generally inert compounds that do not decompose or react during the polymerization reaction.
- the reaction exotherm is generally sufficient to vaporize the blowing agent, which then becomes entrapped in the polyurethane matrix, resulting in the formation of voids or cells.
- additional heat can be added during the reaction to promote vaporization of the blowing agent.
- blowing agents include, but are not limited to, chlorofluorocarbons, hydrogenated fluorocarbons, hydrogenated chlorofluorocarbons, and low-boiling hydrocarbons such as cyclopentane, isopentane, or n-pentane, or any combination thereof.
- a preferred blowing agent is water.
- Catalyst compositions of the present invention are useful for catalyzing the reaction of isocyanates with water to produce carbon dioxide. As the carbon dioxide gas is produced, it becomes trapped in the polyurethane matrix, forming voids or cells.
- this invention encompasses a method for producing a polyurethane foam comprising reacting at least one isocyanate compound, at least one polyol compound, at least one blowing agent, at least one tertiary amine catalyst composition, and optionally, at least one auxiliary component.
- the present invention provides a method for catalyzing the reaction between at least one isocyanate compound, at least one active hydrogen-containing compound, and optionally, at least one auxiliary component.
- auxiliary components include, but are not limited to, cell stabilizers, crosslinking agents, chain extenders, pigments, fillers, flame retardants, auxiliary gelling catalysts, auxiliary blowing catalysts, transition metal catalysts, or any combination thereof.
- Cell stabilizers may include, for example, silicon surfactants or anionic surfactants.
- suitable silicon surfactants include, but are not limited to, polyalkylsiloxane, polyoxyalkylene polyol-modified dimethylpolysiloxane, alkylene glycol-modified dimethylpolysiloxane, or any combination thereof.
- Suitable anionic surfactants include, but are not limited to, salts of fatty acids, salts of sulfuric acid esters, salts of phosphoric acid esters, sulfonates, or any combination thereof.
- Suitable crosslinking agents include, but are not limited to, low-molecular compounds having at least two groups selected from a hydroxyl group, a primary amino group, a secondary amino group, or other active hydrogen-containing groups which are reactive with an isocyanate group.
- Crosslinking agents include, for example, polyhydric alcohols, polyamines, or any combination thereof.
- suitable polyhydric alcohols include ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, 1,4-butanediol, 1,6-hexanediol, neopentyl glycol, glycerol, trimethylolpropane, or any combination thereof.
- Non-limiting examples of polyamine crosslinking agents include diethyltoluenediamine, chlorodiaminobenzene, diethanolamine, diisopropanolamine, triethanolamine, tripropanolamine, 1,6-hexanediamine, or any combination thereof.
- chain extenders include, but are not limited to, compounds having hydroxyl or amino functional group, such as glycols, amines, diols, and water. Further non-limiting examples of chain extenders include ethylene glycol, propylene glycol, 1,4-butanediol, 1,3-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,10-decanediol, 1,12-dodecanediol, ethoxylated hydroquinone, 1,4-cyclohexanediol, N-methylethanolamine, N-methylisopropanolamine, 4-aminocyclo-hexanol, 1,2-diaminoethane, 2,4-toluenediamine, or any mixture thereof.
- Pigments may be used to color code the polyurethane foams during manufacture, to identify product grade, or to conceal yellowing.
- Pigments may include any suitable organic or inorganic pigments.
- organic pigments or colorants include, but are not limited to, azo/diazo dyes, phthalocyanines, dioxazines, or carbon black.
- inorganic pigments include, but are not limited to, titanium dioxide, iron oxides, or chromium oxide.
- Fillers may be used to increase the density and load bearing properties of polyurethane foams. Suitable fillers include, but are not limited to, barium sulfate or calcium carbonate.
- Flame retardants can be used to reduce the flammability of polyurethane foams.
- suitable flame retardants include, but are not limited to, chlorinated phosphate esters, chlorinated paraffins, or melamine powders.
- Auxiliary gelling catalysts may include, but are not limited to, diazabicyclooctane (triethylenediamine), supplied commercially as DABCO 33-LV® catalyst by Air Products and Chemicals. Inc.; quinuclidine and substituted quinuclidines; substituted pyrrolidines or pyrrolizidines; or N,N-dimethylaminoalkyl ureas and similar blends, supplied commercially, for example, as DABCO® NE1070, DABCO® NE1060, DABCO® NE200, DABCO® NE400, DABCO® NE500, and DABCO® NE600.
- diazabicyclooctane triethylenediamine
- DABCO 33-LV® catalyst supplied commercially as Air Products and Chemicals. Inc.
- quinuclidine and substituted quinuclidines substituted pyrrolidines or pyrrolizidines
- auxiliary blowing catalysts include, bis-dimethylaminoethyl ether, commercially supplied as DABCO® BL-11 catalyst by Air Products and Chemicals, Inc.; pentamethyl-diethylenetriamine and related compositions; higher permethylated polyamines; 2-[N-(dimethylaminoethoxyethyl)-N-methylamino]ethanol and related structures; alkoxylated polyamines; imidazole-boron compositions; or amino propyl-bis(amino-ethyl)ether compositions.
- Catalysts compositions in accordance with the present invention may also be used in combination with transition metal catalysts, such as organotin catalysts.
- Polyurethane foams produced in accordance with the present invention are prepared by reacting any suitable organic isocyanate compounds with any suitable polyol compounds in the presence of one or more suitable blowing agents, as described in the art.
- Organic isocyanate compounds include, but are not limited to, hexamethylene diisocyanate (HDI), phenylene diisocyanate (PDI), toluene diisocyanate (TDI), and 4,4′-diphenylmethane diisocyanate (MDI).
- HDI hexamethylene diisocyanate
- PDI phenylene diisocyanate
- TDI toluene diisocyanate
- MDI 4,4′-diphenylmethane diisocyanate
- 2,4-TDI, 2,6-TDI, or any mixture thereof is used to produce polyurethane foams.
- isocyanate compounds are mixtures of diisocyanates known commercially as “crude MDI”, marketed as PAPI by Dow Chemical Company, which contains about 60% of 4,4′-diphenylmethane diisocyanate along with other isomeric and analogous higher polyisocyanates.
- prepolymers of these isocyanate compounds, comprising a partially prereacted mixture of a polyisocyanate and a polyether or polyester polyol.
- Polyurethane foams produced using prior art tertiary amine catalysts containing primary hydroxyl functionality have poor physical properties as compared to foams produced with structurally related catalysts containing secondary hydroxyl functionality.
- polyurethane foams produced using catalyst compositions of the present invention are comparable or superior to foams produced using structurally related catalysts containing secondary hydroxyl functionality.
- polyurethane foams produced with a catalyst composition in accordance with the present invention have reduced odor and no amine emissions as compared to foams produced by structurally-related catalysts containing secondary hydroxyl functionality.
- a polyurethane foam produced in accordance with one aspect of the present invention has an isocyanate index between about 70 and about 115 and comprises the following components by weight: TABLE 1 Polyurethane Components Component Percent by Weight Polyol 20-100 Polymer polyol 0-80 Silicon surfactant 1-2.5 Blowing agent 2-4.5 Crosslinker 0.5-2 Catalyst composition 0.25-2
- isocyanate index (also commonly referred to as NCO index), is defined herein as the number of equivalents of isocyanate, divided by the total number of equivalents of active hydrogen, multiplied by 100.
- Rigid polyurethane foams can be distinguished from flexible polyurethane foams by the presence of higher isocyanurate levels in the rigid foam.
- Flexible foams typically use polymer polyol as part of the overall polyol content in the foam composition, along with conventional triols of about 4000-5000 weight average molecular weight (M w ) and hydroxyl number (OH#) of about 28-35.
- rigid polyurethane foam compositions use about 500-1000 M w polyol with about 3-8 hydroxyl functionalities and OH# of about 160-700.
- Rigid foams can also be distinguished from the flexible foams by the isocyanate (NCO) index of the foam composition.
- Rigid foam compositions typically use a 100-300 NCO index whereas flexible foam compositions typically require a 70-115 NCO index.
- the NCO index is typically from about 100 to about 300.
- the NCO index is typically from about 100 to about 120, and the foam is usually all water blown.
- Semiflexible molded foams have been utilized for many applications in the automotive area. The major applications are instrument panels and interior trims.
- the two main components are the base polyol and copolymer polyol (CPP).
- the base polyol is utilized at levels between about 70-100 pphp.
- the molecular weight of base polyols ranges from about 4500 to about 6000 for triols and from about 2000 to about 4000 for diols.
- Ethylene-oxide-capped polyether polyols have replaced most polyester polyols as the base polyol.
- the primary hydroxyl content is usually greater than about 75 wt % and the capping range is typically about 10-20 wt %.
- the other major component is CPP, which is used at levels up to about 20 wt %.
- the base polyol and CPP are blended with low molecular weight cross-linkers to build hardness and promote faster demolding.
- the level of cross-linker varies depending on the hardness requirement of the finished part. Water levels are chosen to give free rise densities from about 3 to about 6 pounds.
- Cell openers are also utilized in semiflexible foams to reduce the internal foam pressure during the cure cycle and thus reduce pressure-relief voids and “parting lines”.
- Adhesion promoters can be added, depending upon the quality of the vinyl skin, to improve the adhesion between the polyurethane foam and the vinyl skin.
- the use of the catalyst composition of the present invention can reduce the discoloration of the vinyl skin typically observed with conventional amine catalysts because the N—H group of the amide functionality can react with the isocyanate to form a covalent bond with the polyurethane polymer.
- the foams made with the reactive catalyst composition are of the same or superior quality as the foams made with the industry standard.
- catalyst composition in accordance with the present invention provide the following advantages: low amine emissions in the finished polyurethane product; low tertiary amine catalyst vapor pressure, low odor of the finished polyurethane product, effective immobilization of the tertiary amine catalyst during and after polymerization, lower amine concentration in the finished polyurethane product, and optimum physical polyurethane foam properties.
- the crude ethoxylated product was dissolved in isopropanol and placed in the reactor together with 5% palladium on a carbon catalyst.
- the reactor was pressurized with hydrogen and heated up to about 90° C.
- Formalin (37% formaldehyde in water) was slowly added while the hydrogen pressure was monitored. At the end of the addition the reaction was kept at about 90° C. for approximately one hour.
- the product was filtered and isopropanol and water were removed from the product by distillation to yield a mixture containing NN-[2-hydroxyethyl]-N,N′,N′′,N′′′,N′′′pentamethyltriethylenetetramine.
- a sample of about 500 grams of commercially available triethylenetetramine (about 67 wt %) was charged into a one-liter stainless steel reactor equipped with a cooling and heating jacket, a stirrer, a syringe pump and FTIR.
- the amine was heated to about 80° C. and propylene oxide (about 187 g) was slowly added to the mixture.
- the product was allowed to stir for approximately one hour after addition, until the reaction was completed.
- the product was collected and distilled under vacuum (20 mm Hg) to remove any unreacted amine.
- the product mixture was dissolved in methanol and placed in the reactor together with 5% palladium on carbon catalyst. The reactor was pressurize with hydrogen and heated up to about 90° C.
- Foam A was prepared using the catalyst of Example 1 (a mixture comprising, in major part, N-[2-hydroxyethyl]-N,N′,N′′,N′′′,N′′′pentamethyltriethylenetetramine) and Foam B was prepared using the catalyst of Example 2 (a mixture comprising, in major part, N-[2-hydroxypropyl]-N,N′,N′′,N′′′,N′′′pentamethyltriethylenetetramine).
- the catalyst was added to about 192 g of the premix (described in Table 2) in a 32 oz (951 mL) paper cup.
- the formulation was mixed for about 10 seconds at about 6,000 RPM using an overhead stirrer fitted with a 2 inch (5.1 cm) diameter stirring paddle.
- TABLE 2 Premix Components (Example 3) Component Percent by Weight Polyol 1 50 Polyol 2 50 Water 2.34 Silicon surfactant 0.75 DABCO 33-LV ® 0.25 DABCO ® BL-11 0.10 Crosslinker 1.76
- Toluene diisocyanate was added in an amount sufficient to produce a foam with an NCO index of approximately 100.
- the formulation was mixed well for about 6 seconds at about 6,000 RPM using the same stirrer.
- the 32 oz cup was dropped through a hole in the bottom of a 128 oz (3804 mL) paper cup on a stand. The hole was sized to catch the lip of the 32 oz cup.
- the total combined volume of the paper cups was about 160 oz (4755 ml). Foams approximated this volume at the end of the foaming process. Maximum foam height was recorded.
- a comparison of the properties of Foam A and Foam B is presented below in Tables 3 and 4.
- N-[2-hydroxyethyl]-N,N′,N′′,N′′′,N′′′pentamethyltriethylenetetramine (a tertiary amine containing primary hydroxyl functionality) and N-[2-hydroxypropyl]-N,N′,N′′,N′′′,N′′′pentamethyltriethylenetetramine (a tertiary amine containing secondary hydroxyl functionality) produce foams with comparable properties when the catalysts are used in comparable amounts.
- foam appearance and percent shrinkage were essentially identical, showing that catalyst compositions of the present invention do not exhibit either diminished reactivity as compared to a structurally-related catalyst containing secondary hydroxyl functionality or dimished foam quality as compared to a foam produced by a structurally-related catalyst containing secondary hydroxyl functionality.
- Foam A′ and Foam B′ were prepared as in Example 4, but with higher levels of catalyst composition.
- the foams produced using N-[2-hydroxyethyl]-N,N′,N′′,N′′′,N′′′pentamethyltriethylenetetramine (a tertiary amine containing primary hydroxyl functionality) and N-[2-hydroxypropyl]-N,N′,N′′,N′′′,N′′′pentamethyltriethylenetetramine (a tertiary amine containing secondary hydroxyl functionality) exhibited similar properties. See Tables 5 and 6.
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Polyurethanes Or Polyureas (AREA)
Priority Applications (9)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/108,958 US20060235098A1 (en) | 2005-04-19 | 2005-04-19 | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones |
BRPI0601355-4A BRPI0601355A (pt) | 2005-04-19 | 2006-04-12 | método para produzir poliuretana espumada, e método para catalisar uma reação emtre um composto isocianato orgánico e um composto contendo hidrogênio ativo |
KR1020060034121A KR100699299B1 (ko) | 2005-04-19 | 2006-04-14 | 1급 히드록실기 및 고분자 에틸렌디아민 백본을 함유하는발포 촉매 조성물로 제조된 폴리우레탄 발포체 |
JP2006114371A JP4291336B2 (ja) | 2005-04-19 | 2006-04-18 | 第一級ヒドロキシル基と高エチレンジアミン主鎖とを含む発泡触媒組成物から生成させたポリウレタンフォーム |
EP06008012A EP1714989B1 (de) | 2005-04-19 | 2006-04-18 | Polyurethanschäume, hergestellt mit Katalysatorzusammensetzungen, die das Aufschäumen begünstigen und die primäre Hydroxylgruppen und ein Ethylendiaminrückgrat aufweisen. |
DE602006002539T DE602006002539D1 (de) | 2005-04-19 | 2006-04-18 | Polyurethanschäume, hergestellt mit Katalysatorzusammensetzungen, die das Aufschäumen begünstigen und die primäre Hydroxylgruppen und ein Ethylendiaminrückgrat aufweisen. |
AT06008012T ATE407160T1 (de) | 2005-04-19 | 2006-04-18 | Polyurethanschäume, hergestellt mit katalysatorzusammensetzungen, die das aufschäumen begünstigen und die primäre hydroxylgruppen und ein ethylendiaminrückgrat aufweisen. |
CN2006100737920A CN1854163B (zh) | 2005-04-19 | 2006-04-19 | 使用包含伯羟基基团和高乙二胺主链的发泡催化剂组合物制备的聚氨酯泡沫 |
US12/788,667 US9309346B2 (en) | 2005-04-19 | 2010-05-27 | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/108,958 US20060235098A1 (en) | 2005-04-19 | 2005-04-19 | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/788,667 Continuation US9309346B2 (en) | 2005-04-19 | 2010-05-27 | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones |
Publications (1)
Publication Number | Publication Date |
---|---|
US20060235098A1 true US20060235098A1 (en) | 2006-10-19 |
Family
ID=36686098
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/108,958 Abandoned US20060235098A1 (en) | 2005-04-19 | 2005-04-19 | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones |
US12/788,667 Expired - Fee Related US9309346B2 (en) | 2005-04-19 | 2010-05-27 | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/788,667 Expired - Fee Related US9309346B2 (en) | 2005-04-19 | 2010-05-27 | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones |
Country Status (8)
Country | Link |
---|---|
US (2) | US20060235098A1 (de) |
EP (1) | EP1714989B1 (de) |
JP (1) | JP4291336B2 (de) |
KR (1) | KR100699299B1 (de) |
CN (1) | CN1854163B (de) |
AT (1) | ATE407160T1 (de) |
BR (1) | BRPI0601355A (de) |
DE (1) | DE602006002539D1 (de) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20130030067A1 (en) * | 2010-09-09 | 2013-01-31 | Imperial Sugar Co. | Sugar-Based Polyurethanes, Methods for Their Preparation, and Methods of Use Thereof |
US20130065978A1 (en) * | 2011-07-07 | 2013-03-14 | Air Products And Chemicals, Inc. | Additives For Improving Natural Oil Based Polyurethane Foam Peformance |
US20140031444A1 (en) * | 2012-07-27 | 2014-01-30 | Basf Se | Polyurethane foams comprising phosphorus compounds |
US20140275305A1 (en) * | 2013-03-15 | 2014-09-18 | Imperial Sugar Company | Polyurethanes, polyurethane foams and methods for their manufacture |
US9676896B2 (en) | 2010-09-09 | 2017-06-13 | Innovative Urethane, Llc | Sugar-based polyurethanes, methods for their preparation, and methods of use thereof |
US10279515B2 (en) * | 2016-02-18 | 2019-05-07 | Covestro Llc | Processes for producing flexible polyurethane foam laminates and laminates produced thereby |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102008019017B3 (de) * | 2008-04-15 | 2009-12-31 | Mankiewicz Gebr. & Co. Gmbh & Co Kg | Härtbare Massen enthaltend Farbindikatoren zur Anzeige des Aushärtungsfortschritts sowie Verfahren zur Anzeige des Aushärtungsfortschritts dieser härtbaren Massen |
JP5561951B2 (ja) * | 2009-04-16 | 2014-07-30 | アキレス株式会社 | 軟質ポリウレタンフォームからなる照明器具用パッキング材 |
JP5726318B2 (ja) * | 2010-11-29 | 2015-05-27 | ハンツマン・コーポレーション・ハンガリー・ゼーエルテー | 発泡触媒 |
CN106164117B (zh) * | 2014-06-27 | 2020-01-17 | 亨斯迈石油化学有限责任公司 | 用于聚氨酯材料的吡咯烷类催化剂 |
WO2016204981A1 (en) * | 2015-06-19 | 2016-12-22 | Dow Global Technologies Llc | Autocatalytic polyol useful for polyurethane foam manufacture |
TWI722004B (zh) | 2015-07-30 | 2021-03-21 | 大陸商正大天晴藥業集團股份有限公司 | 1,3,5-三嗪衍生物及其使用方法 |
Citations (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4026840A (en) * | 1975-06-09 | 1977-05-31 | Air Products And Chemicals, Inc. | Hydroxyalkyl tertiary amine catalysts for isocyanate reactions |
US4246360A (en) * | 1977-07-22 | 1981-01-20 | Monsanto Company | Fire retardant, non-dripping flexible polyurethane foam |
US4338408A (en) * | 1981-07-20 | 1982-07-06 | Texaco Inc. | Polyurethanes using bis(aminoethyl)ether derivatives as catalysts |
US5229430A (en) * | 1990-07-30 | 1993-07-20 | Tosoh Corporation | Amine catalyst for producing polyurethane and process for producing polyurethane |
US5508314A (en) * | 1994-02-18 | 1996-04-16 | Air Products And Chemicals, Inc. | Hydroxyl group-containing blowing catalyst compositions for the production of polyurethanes |
US5559161A (en) * | 1994-02-18 | 1996-09-24 | Air Products And Chemicals, Inc. | Hydroxy-functional triamine catalyst compositions for the production of polyurethanes |
US5633293A (en) * | 1995-11-30 | 1997-05-27 | Air Products And Chemicals, Inc. | Hydroxy-functional triamine catalyst compositions for polyurethane production |
US6187957B1 (en) * | 1998-12-23 | 2001-02-13 | Basf Aktiengesellschaft | Preparation of amines |
US20020016376A1 (en) * | 2000-06-20 | 2002-02-07 | Oliver Eyrisch | Use of reactive amines for the preparation of polyurethane foams |
US20030083393A1 (en) * | 2001-07-02 | 2003-05-01 | Hiroyuki Kiso | Method for producing a rigid polyurethane foam |
US6723819B2 (en) * | 2001-05-22 | 2004-04-20 | Tosoh Corporation | Catalyst for production of a polyurethane resin and method for producing a polyurethane resin |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0376602A3 (de) * | 1988-12-28 | 1990-08-29 | MITSUI TOATSU CHEMICALS, Inc. | Verfahren zur Herstellung von Polyurethan-Schaumstoffen |
JPH0739456B2 (ja) | 1991-07-03 | 1995-05-01 | 東ソー株式会社 | ポリウレタン製造用アミン触媒組成物及びポリウレタンの製造法 |
JPH0747619B2 (ja) | 1990-07-30 | 1995-05-24 | 東ソー株式会社 | ポリウレタン製造用アミン触媒及びポリウレタンの製造法 |
DE19962911C2 (de) * | 1999-12-23 | 2002-11-21 | Bayer Ag | Flammwidriger HR-Kaltformschaum mit reduzierter Rauchgasintensität und -toxizität |
EP1312630B1 (de) * | 2001-10-31 | 2012-12-12 | Tosoh Corporation | Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen |
US6710096B2 (en) * | 2002-07-22 | 2004-03-23 | Basf Corporation | Polyether polyol for foam applications |
-
2005
- 2005-04-19 US US11/108,958 patent/US20060235098A1/en not_active Abandoned
-
2006
- 2006-04-12 BR BRPI0601355-4A patent/BRPI0601355A/pt not_active IP Right Cessation
- 2006-04-14 KR KR1020060034121A patent/KR100699299B1/ko active IP Right Grant
- 2006-04-18 JP JP2006114371A patent/JP4291336B2/ja active Active
- 2006-04-18 DE DE602006002539T patent/DE602006002539D1/de active Active
- 2006-04-18 EP EP06008012A patent/EP1714989B1/de not_active Not-in-force
- 2006-04-18 AT AT06008012T patent/ATE407160T1/de not_active IP Right Cessation
- 2006-04-19 CN CN2006100737920A patent/CN1854163B/zh not_active Expired - Fee Related
-
2010
- 2010-05-27 US US12/788,667 patent/US9309346B2/en not_active Expired - Fee Related
Patent Citations (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4026840A (en) * | 1975-06-09 | 1977-05-31 | Air Products And Chemicals, Inc. | Hydroxyalkyl tertiary amine catalysts for isocyanate reactions |
US4246360A (en) * | 1977-07-22 | 1981-01-20 | Monsanto Company | Fire retardant, non-dripping flexible polyurethane foam |
US4338408A (en) * | 1981-07-20 | 1982-07-06 | Texaco Inc. | Polyurethanes using bis(aminoethyl)ether derivatives as catalysts |
US5229430A (en) * | 1990-07-30 | 1993-07-20 | Tosoh Corporation | Amine catalyst for producing polyurethane and process for producing polyurethane |
US5508314A (en) * | 1994-02-18 | 1996-04-16 | Air Products And Chemicals, Inc. | Hydroxyl group-containing blowing catalyst compositions for the production of polyurethanes |
US5559161A (en) * | 1994-02-18 | 1996-09-24 | Air Products And Chemicals, Inc. | Hydroxy-functional triamine catalyst compositions for the production of polyurethanes |
US5633293A (en) * | 1995-11-30 | 1997-05-27 | Air Products And Chemicals, Inc. | Hydroxy-functional triamine catalyst compositions for polyurethane production |
US6187957B1 (en) * | 1998-12-23 | 2001-02-13 | Basf Aktiengesellschaft | Preparation of amines |
US20020016376A1 (en) * | 2000-06-20 | 2002-02-07 | Oliver Eyrisch | Use of reactive amines for the preparation of polyurethane foams |
US6723819B2 (en) * | 2001-05-22 | 2004-04-20 | Tosoh Corporation | Catalyst for production of a polyurethane resin and method for producing a polyurethane resin |
US20030083393A1 (en) * | 2001-07-02 | 2003-05-01 | Hiroyuki Kiso | Method for producing a rigid polyurethane foam |
US6777456B2 (en) * | 2001-07-02 | 2004-08-17 | Tosoh Corporation | Method for producing a rigid polyurethane foam |
Cited By (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20130030067A1 (en) * | 2010-09-09 | 2013-01-31 | Imperial Sugar Co. | Sugar-Based Polyurethanes, Methods for Their Preparation, and Methods of Use Thereof |
US9676896B2 (en) | 2010-09-09 | 2017-06-13 | Innovative Urethane, Llc | Sugar-based polyurethanes, methods for their preparation, and methods of use thereof |
US9725555B2 (en) * | 2010-09-09 | 2017-08-08 | Innovative Urethane, Llc | Sugar-based polyurethanes, methods for their preparation, and methods of use thereof |
US10047187B2 (en) | 2010-09-09 | 2018-08-14 | Innovative Urethane, Llc | Sugar-based polyurethanes, methods for their preparation, and methods of use thereof |
US20130065978A1 (en) * | 2011-07-07 | 2013-03-14 | Air Products And Chemicals, Inc. | Additives For Improving Natural Oil Based Polyurethane Foam Peformance |
US9447223B2 (en) * | 2011-07-07 | 2016-09-20 | Air Products And Chemicals, Inc. | Additives for improving natural oil based polyurethane foam performance |
US20140031444A1 (en) * | 2012-07-27 | 2014-01-30 | Basf Se | Polyurethane foams comprising phosphorus compounds |
US10266635B2 (en) * | 2012-07-27 | 2019-04-23 | Basf Se | Polyurethane foams comprising phosphorus compounds |
US20140275305A1 (en) * | 2013-03-15 | 2014-09-18 | Imperial Sugar Company | Polyurethanes, polyurethane foams and methods for their manufacture |
US10323116B2 (en) * | 2013-03-15 | 2019-06-18 | Imperial Sugar Company | Polyurethanes, polyurethane foams and methods for their manufacture |
US10279515B2 (en) * | 2016-02-18 | 2019-05-07 | Covestro Llc | Processes for producing flexible polyurethane foam laminates and laminates produced thereby |
Also Published As
Publication number | Publication date |
---|---|
DE602006002539D1 (de) | 2008-10-16 |
CN1854163A (zh) | 2006-11-01 |
KR100699299B1 (ko) | 2007-03-26 |
KR20060110779A (ko) | 2006-10-25 |
BRPI0601355A (pt) | 2006-12-26 |
EP1714989A1 (de) | 2006-10-25 |
JP2006299262A (ja) | 2006-11-02 |
EP1714989B1 (de) | 2008-09-03 |
US9309346B2 (en) | 2016-04-12 |
JP4291336B2 (ja) | 2009-07-08 |
ATE407160T1 (de) | 2008-09-15 |
US20100240783A1 (en) | 2010-09-23 |
CN1854163B (zh) | 2010-06-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US9309346B2 (en) | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones | |
US6232356B1 (en) | Reactive catalyst compositions for improving water blown polyurethane foam performance | |
EP1534766B1 (de) | Verfahren zur herstellung von polyurethanschaumstoff | |
EP1702913B1 (de) | Zusammensetzungen von Treibreaktionskatalysatoren mit hydroxylhaltigen Verbindungen und Tenside für die Herstellung von Polyurethanschäumen | |
US6737446B1 (en) | Tertiary amino alkyl amide catalysts for improving the physical properties of polyurethane foams | |
US6998508B2 (en) | Tertiary alkanolamines containing surface active alkyl groups | |
EP1435364A2 (de) | Von Fettsäuren oder langen Alkylketten enthaltende Säuren abgeleitete tertiäre Aminalkylamidpolyurethankatalysatoren | |
US7169823B2 (en) | Tertiary alkanolamine polyurethane catalysts derived from long chain alkyl and fatty carboxylic acids | |
EP0877017B1 (de) | Aminomethyl-Pyrrolidin-Harnstoff-Zusammensetzungen für die Herstellung von Polyurethanen | |
US6762211B1 (en) | Tertiary amino alkyl amide polyurethane catalysts derived from long chain alkyl and fatty carboxylic acids | |
US6747069B1 (en) | Tertiary alkanolamine polyurethane catalysts derived from long chain alkyl and fatty carboxylic acids | |
US6313346B1 (en) | Catalyst compositions for the production of polyurethanes | |
EP1457480B1 (de) | Tertiäre Alkanolamine mit oberflächenaktiven Alkylgruppen | |
MXPA06004207A (en) | Polyurethane foams made with blowing catalyst compositions containing primary hydroxyl groups and high ethylenediamine backbones | |
EP1435365A2 (de) | Verwendung von tertiären Aminoalkylamidkatalysatoren zur Verbesserung der physischen Eigenschaften von Polyurethanschäumen |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: AIR PRODUCTS AND CHEMICALS, INC., PENNSYLVANIA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BURDENIUC, JUAN JESUS;FREYBERGER, DOUGLAS P.;REEL/FRAME:016275/0068 Effective date: 20050420 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |