US20050230072A1 - Aramid paper blend - Google Patents
Aramid paper blend Download PDFInfo
- Publication number
- US20050230072A1 US20050230072A1 US10/826,530 US82653004A US2005230072A1 US 20050230072 A1 US20050230072 A1 US 20050230072A1 US 82653004 A US82653004 A US 82653004A US 2005230072 A1 US2005230072 A1 US 2005230072A1
- Authority
- US
- United States
- Prior art keywords
- paper
- aramid
- floc
- pulp
- aramid paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H13/00—Pulp or paper, comprising synthetic cellulose or non-cellulose fibres or web-forming material
- D21H13/10—Organic non-cellulose fibres
- D21H13/20—Organic non-cellulose fibres from macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D21H13/26—Polyamides; Polyimides
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K1/00—Printed circuits
- H05K1/02—Details
- H05K1/03—Use of materials for the substrate
- H05K1/0313—Organic insulating material
- H05K1/0353—Organic insulating material consisting of two or more materials, e.g. two or more polymers, polymer + filler, + reinforcement
- H05K1/0366—Organic insulating material consisting of two or more materials, e.g. two or more polymers, polymer + filler, + reinforcement reinforced, e.g. by fibres, fabrics
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H25/00—After-treatment of paper not provided for in groups D21H17/00 - D21H23/00
- D21H25/005—Mechanical treatment
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H25/00—After-treatment of paper not provided for in groups D21H17/00 - D21H23/00
- D21H25/04—Physical treatment, e.g. heating, irradiating
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
- H05K2201/02—Fillers; Particles; Fibers; Reinforcement materials
- H05K2201/0275—Fibers and reinforcement materials
- H05K2201/0278—Polymeric fibers
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
- H05K2201/02—Fillers; Particles; Fibers; Reinforcement materials
- H05K2201/0275—Fibers and reinforcement materials
- H05K2201/0293—Non-woven fibrous reinforcement
Definitions
- This invention relates to aramid paper suitable for composite structures.
- U.S. Pat. No. 5,026,456 to Hesler et al. discloses a high porosity paper comprising 10-40% by weight of aramid fibrids, 5-30% by weight of high temperature resistant floc, and 30-85% by weight of aramid paper pulp prepared by comminuting dry aramid paper containing 50 to 60% aramid fibrids and 40 to 50% aramid floc to a particle size capable of passing through a sorting screen of 6.4-12.7 mm.
- the high porosity paper of this invention comprises previously-dried aramid fibrids and previously-dried aramid floc from aramid paper pulp and, also, fresh aramid fibrids and fresh high temperature resistant floc.
- U.S. Pat. No. 5,789,059 to Nomoto discloses a honeycomb core made from a base sheet a mixture of p-aramid fibers (floc) and m-aramid pulp wherein p-aramid fiber occupies of from not less than 20% to less than 50% by weight of the mixture.
- This invention relates to aramid paper for composite structures, which comprises 50 to 95 weight percent p-aramid pulp, 5-50 weight percent of floc with initial modulus lower than 3000 cN/tex, and, optionally, less than 20 weight percent of polymer binder material.
- the invention is also directed to a process for making the paper.
- Aramid papers find use, among others, as a basic material for honeycomb cores, a reinforcement for printed circuit boards and other laminate structures, an electrical insulation in oil or resin-filled systems, as a basic material for friction facings in automotive industry, and in other applications of high performance composite structures.
- such papers should preferably contain p-aramid fibrous components.
- papers with p-aramid floc in the composition are formed from very dilute slurries (0.01-0.05 wt. %), which require a usage of special machines for wet-laid nonwovens (inclined wire and others).
- Paper containing only p-aramid pulp as the aramid component can be formed uniformly on a regular horizontal papermaking machine, such as a Fourdrinier, from medium diluted slurries (0.2-0.6 wt. %).
- aramid paper based only on pulp does not have enough strength to be produced stably at a relatively low basis weight (e.g., below 70 g/m 2 ) and to be processed successfully into a final structure.
- a combination of 50-95% by weight of p-aramid pulp, 5-50% by weight of floc having an initial modulus lower than 3000 cN/tex and optionally, less than 20% by weight of polymer binder material provides a paper composition, which can be processed stably and uniformly on a Fourdrinier type papermaking machine into a final paper.
- Such paper with a basis weight below 70 g/m 2 , can exhibit a stiffness comparable to that of m-aramid papers.
- composite paper structure after resin impregnation to form a composite paper structure, mechanical properties (strength and stiffness) can be achieved that are much higher than those achieved with an m-aramid composition.
- Such composite paper structure can approach the properties achieved in compositions with p-aramid floc.
- the composite paper structure of this invention exhibits an increase in stiffness of 4-5 times in contrast to less than 2 times for commercial meta-aramid papers or para-aramid papers based on pra-aramid floc.
- Resins for impregnating the paper to form the composite paper structure include polyamides, polyimides, epoxies, phenolics, polyesters, polyurethanes and others equally suitable.
- the paper of this invention can exhibit lower changes in dimensions with a change in temperature (i.e., a lower coefficient of thermal expansion) in comparison with commercial papers based on para- or meta-aramid papers for honeycombs.
- floc fibers having a length of 2 to 25 millimeters, preferably 3 to 7 millimeters and a diameter of 3 to 20 micrometers, preferably 5 to 14 micrometers. If the floc length is less than 3 millimeters, its impact on the paper strength is not high enough and if it is more than 25 millimeters, it is almost impossible to form a uniform web by a wet-laid method. If the floc diameter is less than 5 micrometers, it can be difficult to produce it with enough uniformity and reproducibility and if it is more than 20 micrometers, it is virtually impossible to form uniform paper of light to medium basis weights. Floc is generally made by cutting continuous spun filaments into specific-length pieces.
- a preferred type of the floc in this invention is meta-aramid floc and, particularly, floc from poly(metaphenylene isophthalamide).
- floc from other materials with an initial modulus lower than 3000 cN/tex can be used, for example, poly(ethylene terephthalate), polyacrylonitrile, etc.
- pulp means particles of aramid material having a stalk and fibrils extending generally therefrom, wherein the stalk is generally columnar and about 10 to 50 micrometers in diameter and the fibrils are fine, hair-like members generally attached to the stalk measuring only a fraction of a micrometer or a few micrometers in diameter and about 10 to 100 micrometers long.
- Fibrids means a very finely-divided polymer product of small, filmy, essentially two-dimensional, particles known having a length and width on the order of 100 to 1000 micrometers and a thickness only on the order of 0.1 to 1 micrometer. Fibrids are made by streaming a polymer solution into a coagulating bath of liquid that is immiscible with the solvent of the solution. The stream of polymer solution is subjected to strenuous shearing forces and turbulence as the polymer is coagulated.
- “Aramid” materials are polyamides wherein at least 85% of the amide (—CO—NH—) linkages are attached directly to two aromatic rings. Additives can be used with the aramid and it has been found that up to as much as 10 percent, by weight, of other polymeric material can be blended, with the aramid. Copolymers can be used having as much as 10 percent of other diamines substituted for the diamine of the aramid or as much as 10 percent of other diacid chlorides substituted for the diacid chloride of the aramid.
- Floc, p-aramid pulp and a polymer binder material in the paper of this invention can be of natural color or colored by dyes or pigments.
- the floc and the pulp can be treated by materials which alter their surface characteristics so long as such treatment does not adversely affect the ability of binders to contact and hold to the fiber surfaces.
- Aramid fibrids are very effective types of binder.
- Other polymer binders such as floc, which can be fused during drying or calendering operations, or water-soluble resins, or combinations of different types of polymer binders can be used for this invention.
- fusible floc it performs two functions in the paper composition of this invention in that it works as floc to prevent paper breaks during paper formation and works as a binder after further processing.
- the paper of this invention can have very high permeability, with Gurley air resistance of several seconds, or have medium permeability, with Gurley air resistance up to several thousand seconds.
- the preferred material for the fibrids of this invention are generally aramids, specifically, meta-aramids, and, more specifically, poly(m-phenylene isophthalamide).
- Other suitable fibrid materials are polyacrylonitrile, polycaproamide, poly (ethylene terephthalate), and the like. Fibrids from aramid materials will provide better thermal stability of the paper in comparison with other mentioned materials.
- Resin used as a binder can be in the form of a water-soluble or dispersible polymer added directly to the paper making dispersion or in the form of thermoplastic binder fibers of the resin material intermingled with the aramid fibers to be activated as a binder by heat applied during drying or following additional compression and/or heat treatment.
- the preferred materials for the water-soluble or dispersible binder polymer are water-soluble or water-dispersible thermosetting resins such as polyamide resins, epoxy resins, phenolic resins, polyureas, polyurethanes, melamine formaldehyde resins, polyesters and alkyd resins, generally.
- water-soluble polyamide resins typical for the papermaking industry (e.g., cationic wet-strength resin KYMENE® 557LX and others).
- Water solutions and dispersion of non-cured polymers can be used as well (poly(vinyl alcohol), poly(vinyl acetate), etc.).
- Thermoplastic binder floc can be made from such polymers as poly(vinyl alcohol), polypropylene, polyester and the like and should have a length and diameter similar to those of the floc described above.
- Additional ingredients such as fillers for the adjustment of paper conductivity and other properties, pigments, antioxidants, etc in powder or fibrous form can be added to the paper composition of this invention.
- the paper of this invention can be formed on equipment of any scale from laboratory screens to commercial-sized papermaking machinery, such as a Fourdrinier or inclined wire machines.
- the general process involves making a dispersion of p-aramid pulp, floc, and a binder material (if desired) in an aqueous liquid, draining the liquid from the dispersion to yield a wet composition and drying the wet paper composition.
- the dispersion can be made either by dispersing the fibers and then adding the binder material or by dispersing the binder material and then adding the fibers;
- the dispersion can also be made by combining a dispersion of fibers with a dispersion of the binder material.
- the concentration of fibers in the dispersion can range from 0.01 to 1.0 weight percent based on the total weight of the dispersion.
- the concentration of a binder material in the dispersion can be up to 20 weight percent based on the total weight of solids.
- the aqueous liquid of the dispersion is generally water, but may include various other materials such as pH-adjusting materials, forming aids, surfactants, defoamers and the like.
- the aqueous liquid is usually drained from the dispersion by conducting the dispersion onto a screen or other perforated support, retaining the dispersed solids and then passing the liquid to yield a wet paper composition.
- the wet composition once formed on the support, is usually further dewatered by vacuum or other pressure forces and further dried by evaporating the remaining liquid.
- a next step which can be performed if higher density and strength are desired, is calendering one or more layers of the paper in the nip of metal-metal, metal-composite, or composite-composite rolls.
- one or more layers of the paper can be compressed in a platen press at a pressure, temperature and time, which are optimal for a particular composition and final application.
- heat-treatment as an independent step before, after or instead of calendering or compression can be conducted if strengthening or some other property modification is desired without or in addition to densification.
- the paper of this invention is useful as a component in structural materials such as core structures or honeycombs.
- one or more layers of the aramid paper may be used as the primarly material for forming the cells of a honeycomb structure.
- one or more layers of the aramid paper may be used in the sheets for covering or facing the honeycomb cells or other core materials.
- these laminates are impregnated with a resin such as a phenolic, epoxy, poyimide or other resin.
- the paper may be useful without any resin impregnation.
- the paper of this invention is also useful where thermal dimensional stability is desired, such as printed wiring boards; or where dielectric properties are useful, such as electrical insulating material for use in motors, transformers and other power equipment.
- the paper of this invention can, be used either with or without impregnating resins, as desired.
- Tensile Strength, Modulus, Tensile Stiffness, and Tensile Index were determined for papers and composites of this invention on an Instron-type testing machine using test specimens 2.54 cm wide and a gage length of 18 cm in accordance with ASTM D 828.
- Thickness and Basis Weight (Grammage) of papers and composites was determined in accordance with ASTM D 645 and ASTM D 646 correspondingly.
- Specific Stiffness of Papers was determined as a mathematical quantity calculated by dividing tensile stiffness of a paper by basis weight of a paper.
- Specific Stiffness of Composites was determined as a mathematical quantity calculated by dividing tensile stiffness of a composite by basis weight of a raw paper.
- Specific Tensile Index for Composites was determined as a mathematical quantity calculated by dividing tensile strength of a composite by basis weight of a raw paper.
- Gurley Air Resistance for papers was determined by measuring air resistance in seconds per 100 milliliters of cylinder displacement for approximately 6.4 square centimeters circular area of a paper using a pressure differential of 1.22 kPa in accordance with TAPPI T 460.
- Coefficient of Thermal Expansion in Plane was measured on dried strips of the material with dimensions of about 8.7 mm long and 2 mm wide on a 2940 TMA Instrument at a temperature between 20° C. and 100° C. with the temperature increasing at 10° C./minute.
- the loads were 2 grams and 36 grams for the paper and resin paper, respectively. The average of the readings for the machine and cross direction of the paper web was reported as the final number.
- aqueous dispersion was made of never-dried meta-aramid fibrids at a 0.5% consistency (0.5 weight percent solid materials in water).
- Para-aramid pulp was dispersed in a pulper at 0.2% consistency for 5 minutes. After that the pulp dispersion was added into a tank with the fibrid dispersion. After ten minutes of continued agitation, meta-aramid floc was added. After five additional minutes of agitation, water was added to yield a final consistency of 0.2%.
- the solid materials were:
- the para-aramid pulp was poly(paraphenylene terephthalamide) pulp type 1 F361 (sold by E.I. du Pont de Nemours and Company (DuPont), Wilmington, Del. under the trade name KEVLAR®).
- the meta-aramid fibrids were made from poly(metaphenylene isophthalamide) as described in U.S. Pat No. 3,756,908.
- the meta-aramid floc was poly(metaphenylene isophthalamide) floc of linear density 0.22 tex (2.0 denier) and length of 0.64 cm with an initial modulus of about 800 cN/tex (sold by DuPont under the trade name NOMEX®).
- the resulting dispersion was pumped to a supply chest and fed from there to a Fourdrinier machine to make paper with a basis weight of 47.5 g/m 2 . Other properties of the paper are described in the Table 1 below.
- a slurry was prepared as in Example 1.
- a paper with a basis weight of 40.7 g/m 2 was formed on a Fourdrinier. Other properties of the paper are described in the Table 1 below.
- a slurry was prepared as in Example 1, but without addition of the floc in the composition.
- the solid materials were:
- the resulting dispersion was pumped to a supply chest and fed from there to a Fourdrinier to make paper with a basis weight of 47.5 and 60 g/m 2 .
- frequent breaks occurred and it was impossible to prepare a continuous sheet.
- Para-aramid pulp as used in Ex. 1 was dispersed in the pulper at 0.2% consistency for 5 minutes. The resulting dispersion was pumped to a supply chest and fed from there to a Fourdrinier to make paper with a basis weight of 50 and 60 g/m 2 . However, frequent breaks occurred and it was impossible to prepare a continuous sheet.
- Example 1 The paper from Example 1 was passed through the nip of a metal-metal calender with a roll diameter of about 20 cm at a temperature of about 300° C. and a linear pressure of about 1200 N/cm. Properties of the final paper are shown in Table 1.
- the paper from Example 2 was passed through the nip of a metal-metal calender with a roll diameter of about 20 cm at a temperature of about 300° C. and linear pressure of about 1200 N/cm.
- the paper from Example I was compressed for 2 minutes in a platen press at a temperature of about 304° C. and a pressure of about 3.45 MPa.
- the paper from Example 1 was compressed for 5 minutes in the platen press at a temperature of about 327° C. and a pressure of about 10.8 MPa.
- the para-aramid pulp, the meta-aramid floc and meta-aramid fibrids were the same as described in Example 1.
- the dispersion was poured, with 8 liters of water, into an approximately 21 ⁇ 21 cm handsheet mold and a wet-laid sheet was formed.
- the sheet was placed between two pieces of blotting paper, hand couched with a rolling pin and dried in a handsheet dryer at 190° C.
- the sheet was passed through the nip of a metal-metal calender with a roll diameter of about 20 cm at a temperature of about 270° C. and a linear pressure of about 3000 N/cm.
- the final paper had a basis weight of 56.6 g/m 2 .
- the papers were prepared as described in Example 9, but with varying percentages of the three components (para-aramid pulp, meta-aramid floc, and meta-aramid fibrids).
- the para-aramid pulp and the meta-aramid floc were the same as described in Example 1.
- Poly (vinyl alcohol) floc was type VPB105-1 with linear density 0.11 tex and cut length 3 mm (sold by KURARAY Co. under trade name Kuralon VP). Its initial modulus was lower than 530 cN/tex as found in R. W. Moncrieff, Man-Made Fibres, Wiley International Division, 1970, p. 488.
- the dispersion was poured, with 8 liters of water, into an approximately 21 ⁇ 21 cm handsheet mold and a wet-laid sheet was formed.
- the sheet was placed between two pieces of blotting paper, hand couched with a rolling pin and dried in a handsheet dryer at 190° C. After drying, the sheet was compressed for 5 min. in a platen press at a temperature about 304° C. and a pressure about 10.8 MPa.
- the papers were prepared as in Example 14, but with varying percentages of the three components (para-aramid pulp, meta-aramid floc and poly(vinyl alcohol) floc).
- the paper was prepared as in Example 14, except that a water-soluble resin was added to the paper composition in the quantity of 5 percent by weight based on the total weight of the composition.
- the water-soluble resin was KYMENE 557LX sold by Hercules. Paper compositions and properties are shown in Table 1.
- the paper was prepared as in Example 15, except that the water-soluble resin was added to the paper composition in the quantity of 5 percent by weight based on the total weight of the composition.
- the resin was the same as in Example 23. Paper compositions and properties are shown in Table 1.
- a composite was prepared by impregnation of the paper from Example 5 with a solvent-based phenolic resin (PLYOPHEN 23900 from the Durez Corporation) following by removing any excess resin from the surface with blotting paper and curing in an oven by ramping up the temperature as follows: heating from room temperature to 82° C. and holding at this temperature for 15 minutes, increasing the temperature to 121° C. and holding at this temperature for another 15 minutes and increasing the temperature to 182° C. and holding at this temperature for 60 minutes. Properties of the composite are shown in Table 2.
- a solvent-based phenolic resin PLYOPHEN 23900 from the Durez Corporation
- a composite was prepared as described in Example 19, except that the paper from Example 6 was used. Properties of the composite are shown in Table 2.
- a composite was prepared as described in Example 19 except that a para-aramid paper based on KEVLAR® floc and NOMEX® fibrids, sold by DuPont as KEVLAR® 1.8N636 paper, was used. Properties of the composite are shown in Table 2.
- a composite was prepared as described in Example 19 with a difference that a para-aramid paper based on KEVLAR® floc and NOMEX® fibrids, sold by DuPont as KEVLAR® 2.8N636 paper, was used. Properties of the composite are shown in Table 2.
- a composite was prepared as described in Example 19 with a difference that a meta-aramid paper based on NOMEX® floc and NOMEX® fibrids, sold DuPont as NOMEX® 2T412 paper, was used. Properties of the composite are shown in Table 2.
- a composite was prepared as described in Example 19 except that a meta-aramid paper based on NOMEX® floc and NOMEX® fibrids, sold by DuPont as NOMEX® 3T412 paper was used. Properties of the composite are shown in Table 2. TABLE 1 Properties of Papers Paper composition (wt. %) P-Aramid Gurley air Soluble M-Aramid PVA Water- Basis wt.
- the stiffness of the inventive paper is less than the stiffness of commercial paper based on p-aramid floc (i.e., comparative examples 21 and 22) and also less than even the papers based on m-aramid (i.e., comparative examples 23 and 24).
- the composites based on the inventive papers are very stiff, which is desirable for the majority of composite applications. Their stiffness is very close to that of the composites based on the p-aramid papers and much stiffer than that of the composites based on m-aramid paper. This is additionally demonstrated by the ratio between specific stiffness of the composite and the respective papers on which they were based. The ratio is much higher for the inventive paper vs. the comparative papers, demonstrating that “softer” (i.e., less stiff) paper provides for easier conversion into the final composite structure.
- the paper of the invention and corresponding composites have very good dimensional stability.
- the inventive paper by itself has dimensional stability that is better than commercial papers based on p-aramid floc and much better than commercial m-aramid papers.
- the dimensional stability of the final composite structure based on the invented paper is very close to those based on papers with p-aramid floc and much better in comparison with dimensional stability of the composites based on aramid papers.
Landscapes
- Engineering & Computer Science (AREA)
- Microelectronics & Electronic Packaging (AREA)
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Paper (AREA)
Priority Applications (8)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/826,530 US20050230072A1 (en) | 2004-04-16 | 2004-04-16 | Aramid paper blend |
CA2561329A CA2561329C (fr) | 2004-04-16 | 2005-04-15 | Melange de papier a base d'aramide |
EP05739774A EP1756360B1 (fr) | 2004-04-16 | 2005-04-15 | Melange de papier a base d'aramide |
PCT/US2005/012996 WO2005103376A1 (fr) | 2004-04-16 | 2005-04-15 | Mélange de papier à base d'aramide |
JP2007508603A JP2007532798A (ja) | 2004-04-16 | 2005-04-15 | アラミド紙ブレンド |
BRPI0509409A BRPI0509409B8 (pt) | 2004-04-16 | 2005-04-15 | Papel de aramida e processo de produção de papel de aramida |
CN2005800111380A CN1942629B (zh) | 2004-04-16 | 2005-04-15 | 芳纶纸掺合物 |
JP2011161010A JP5686688B2 (ja) | 2004-04-16 | 2011-07-22 | アラミド紙ブレンド |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/826,530 US20050230072A1 (en) | 2004-04-16 | 2004-04-16 | Aramid paper blend |
Publications (1)
Publication Number | Publication Date |
---|---|
US20050230072A1 true US20050230072A1 (en) | 2005-10-20 |
Family
ID=34967398
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/826,530 Abandoned US20050230072A1 (en) | 2004-04-16 | 2004-04-16 | Aramid paper blend |
Country Status (7)
Country | Link |
---|---|
US (1) | US20050230072A1 (fr) |
EP (1) | EP1756360B1 (fr) |
JP (2) | JP2007532798A (fr) |
CN (1) | CN1942629B (fr) |
BR (1) | BRPI0509409B8 (fr) |
CA (1) | CA2561329C (fr) |
WO (1) | WO2005103376A1 (fr) |
Cited By (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080145602A1 (en) * | 2006-12-15 | 2008-06-19 | Gary Lee Hendren | Processes for making shaped honeycomb and honeycombs made thereby |
US20080145596A1 (en) * | 2006-12-15 | 2008-06-19 | Levit Mikhail R | Honeycomb containing poly(paraphenylene terephthalamide) paper with aliphatic polyamide binder and articles made therefrom |
US20080251193A1 (en) * | 2004-10-08 | 2008-10-16 | Matsushita Electric Industrial Co., Ltd. | Method of Manufacturing Multi-Layer Circuit Board |
US20090126887A1 (en) * | 2005-12-21 | 2009-05-21 | E.I. Du Pont De Nemours And Company | Pipd Paper and Components Made Therefrom |
US20090155526A1 (en) * | 2007-11-30 | 2009-06-18 | E. I. Du Pont De Nemours And Company | Honeycomb having a high compression strength and articles made from same |
US20090159227A1 (en) * | 2007-12-21 | 2009-06-25 | Levit Mikhail R | Papers containing fibrids derived from diamino diphenyl sulfone |
US20090162605A1 (en) * | 2007-12-21 | 2009-06-25 | Levit Mikhail R | Papers containing floc derived from diamino diphenyl sulfone |
US20090236064A1 (en) * | 2005-12-21 | 2009-09-24 | Merriman Edmund A | Paper Comprising Pipd Pupl and Process for Making Same |
US20090250181A1 (en) * | 2005-12-21 | 2009-10-08 | E. I. Du Pont De Nemours And Company | Paper comprising pipd floc and process for making the same |
US8118975B2 (en) * | 2007-12-21 | 2012-02-21 | E. I. Du Pont De Nemours And Company | Papers containing fibrids derived from diamino diphenyl sulfone |
US20150050474A1 (en) * | 2012-04-18 | 2015-02-19 | E I Du Pont Nemoure and Company | Multilayered sheet |
US20150050475A1 (en) * | 2012-04-18 | 2015-02-19 | E I Du Pont De Nemours And Company | Multilayered sheet |
US20150056429A1 (en) * | 2012-04-18 | 2015-02-26 | E I Du Pont De Nemours And Company | Multilayered sheet |
KR20150114564A (ko) * | 2013-02-08 | 2015-10-12 | 듀폰 테이진 어드밴스드 페이퍼 가부시끼가이샤 | 착색 아라미드지 및 그의 제조 방법 |
US20150318078A1 (en) * | 2012-11-23 | 2015-11-05 | Teijin Aramid B.V. | Electrical insulating paper |
US10066341B2 (en) * | 2013-07-18 | 2018-09-04 | Teijin Aramid B.V. | Fire-retardant sheet material |
US10407829B2 (en) | 2015-05-28 | 2019-09-10 | Kolon Industries, Inc. | Aramid paper, manufacturing method therefor, and use thereof |
US20210140108A1 (en) * | 2018-05-28 | 2021-05-13 | Teijin Aramid B.V. | Aramid-based paper with improved properties |
Families Citing this family (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7455750B2 (en) * | 2004-06-25 | 2008-11-25 | E.I. Du Pont De Nemours And Company | Meta- and para-aramid pulp and processes of making same |
US7740741B2 (en) | 2005-12-21 | 2010-06-22 | E.I. Du Pont De Nemours And Company | Para-aramid pulp including meta-aramid fibrids and processes of making same |
US7771811B2 (en) * | 2006-12-15 | 2010-08-10 | E.I. Du Pont De Nemours And Company | Honeycomb from controlled porosity paper |
US7815993B2 (en) * | 2006-12-15 | 2010-10-19 | E.I. Du Pont De Nemours And Company | Honeycomb from paper having flame retardant thermoplastic binder |
US7771810B2 (en) * | 2006-12-15 | 2010-08-10 | E.I. Du Pont De Nemours And Company | Honeycomb from paper having a high melt point thermoplastic fiber |
US20090214818A1 (en) * | 2008-02-26 | 2009-08-27 | E. I. Du Pont De Nemours And Company | Core having a high shear strength and articles made from same |
WO2012093048A1 (fr) | 2011-01-04 | 2012-07-12 | Teijin Aramid B.V. | Papier isolant électrique |
CN102174770A (zh) * | 2011-01-27 | 2011-09-07 | 深圳昊天龙邦复合材料有限公司 | 包含芳族合成纤维纸的半固化片和由其制得的印刷电路板 |
US9666848B2 (en) | 2011-05-20 | 2017-05-30 | Dreamweaver International, Inc. | Single-layer lithium ion battery separator |
WO2013117462A1 (fr) | 2012-02-07 | 2013-08-15 | Teijin Aramid B.V. | Papier aramide présentant une résistance accrue et son procédé de fabrication |
US8936878B2 (en) | 2012-11-20 | 2015-01-20 | Dreamweaver International, Inc. | Methods of making single-layer lithium ion battery separators having nanofiber and microfiber components |
KR101515307B1 (ko) * | 2013-12-30 | 2015-04-24 | 도레이케미칼 주식회사 | 고평량 메타 아라미드 페이퍼 및 그 제조방법 |
KR101524788B1 (ko) * | 2013-12-30 | 2015-06-01 | 도레이케미칼 주식회사 | 저평량 메타 아라미드 페이퍼 및 그 제조방법 |
US9976258B2 (en) * | 2014-10-03 | 2018-05-22 | E I Du Pont De Nemours And Company | Honeycomb core having a high compression strength |
KR101547776B1 (ko) | 2014-11-24 | 2015-09-07 | 한국섬유개발연구원 | 허니컴용 아라미드 습식부직포 및 그 제조방법 |
JP6405583B2 (ja) * | 2014-12-26 | 2018-10-17 | 特種東海製紙株式会社 | 絶縁紙 |
KR101700827B1 (ko) * | 2015-05-28 | 2017-01-31 | 코오롱인더스트리 주식회사 | 적층 아라미드 종이 및 그 제조방법 |
US10245804B2 (en) | 2015-10-16 | 2019-04-02 | Hexcel Corporation | Fire retarded aramid fiber-based honeycomb |
US10767316B2 (en) * | 2017-11-01 | 2020-09-08 | Dupont Safety & Construction, Inc. | Paper comprising aramid pulp and a friction paper made therefrom |
KR102201806B1 (ko) * | 2018-02-22 | 2021-01-11 | 코오롱인더스트리 주식회사 | 전기 절연지용 전방향족 아라미드 종이 및 그의 제조방법 |
US11078627B2 (en) | 2018-08-14 | 2021-08-03 | Dupont Safety & Construction, Inc. | High tensile strength paper suitable for use in electrochemical cells |
Citations (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2999788A (en) * | 1958-12-09 | 1961-09-12 | Du Pont | Synthetic polymer fibrid paper |
US3756908A (en) * | 1971-02-26 | 1973-09-04 | Du Pont | Synthetic paper structures of aromatic polyamides |
US4698267A (en) * | 1985-09-17 | 1987-10-06 | E. I. Du Pont De Nemours And Company | High density para-aramid papers |
US4729921A (en) * | 1984-10-19 | 1988-03-08 | E. I. Du Pont De Nemours And Company | High density para-aramid papers |
US5026456A (en) * | 1990-06-14 | 1991-06-25 | E. I. Du Pont De Nemours And Company | Aramid papers containing aramid paper pulp |
US5789059A (en) * | 1995-04-28 | 1998-08-04 | Showa Aircraft Industry Co., Ltd. | Honeycomb core |
US5833807A (en) * | 1997-04-17 | 1998-11-10 | E. I. Du Pont De Nemours And Company | Aramid dispersions and aramid sheets of increased uniformity |
US5948543A (en) * | 1996-02-21 | 1999-09-07 | Shin-Kobe Electric Machinery Co., Ltd. | Laminate base material, a method of producing the same, a prepreg and a laminate |
US6120643A (en) * | 1999-10-27 | 2000-09-19 | E. I. Du Pont De Nemours And Company | Aramid and glass fiber absorbent papers |
US6303221B1 (en) * | 2000-12-07 | 2001-10-16 | E. I. Du Pont De Nemours And Company | Two-component pulp reinforcement |
US6426310B1 (en) * | 1998-09-28 | 2002-07-30 | Shin-Kobe Electric Machinery Co., Ltd. | Electrically insulating non-woven fabric, a prepreg and a laminate |
US6436236B1 (en) * | 2001-03-05 | 2002-08-20 | E. I. Du Pont De Nemours & Company | Electrically-conductive para-aramid pulp |
US20020142689A1 (en) * | 2001-01-23 | 2002-10-03 | Levit Mikhail R. | Non-woven sheet of aramid floc |
US6544622B1 (en) * | 2000-04-03 | 2003-04-08 | Showa Aircraft Industry Co., Ltd. | Aramid honeycombs and a method for producing the same |
US6558512B2 (en) * | 1998-11-18 | 2003-05-06 | Oji Paper Co., Ltd. | Base material for laminate and process for producing the same |
US6592963B1 (en) * | 2000-06-16 | 2003-07-15 | E. I. Du Pont De Nemours And Company | Honeycomb structure |
US20040072000A1 (en) * | 2002-10-01 | 2004-04-15 | Kawka Dariusz Wlodzimierz | Aramid paper laminate |
US20050136233A1 (en) * | 2002-08-26 | 2005-06-23 | Samuels Michael R. | Sheet material especially useful for circuit boards |
US6942757B1 (en) * | 1993-11-29 | 2005-09-13 | Teijin Twaron B.V. | Process for preparing para-aromatic polyamide paper |
US20050284595A1 (en) * | 2004-06-25 | 2005-12-29 | Conley Jill A | Cellulosic and para-aramid pulp and processes of making same |
US20060266486A1 (en) * | 2005-05-26 | 2006-11-30 | Levit Mikhail R | Electroconductive aramid paper |
Family Cites Families (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0736120B1 (fr) * | 1993-12-21 | 1998-01-21 | E.I. Du Pont De Nemours And Company | Papiers aramides a surface lisse multicouche tres resistants, se caracterisant par une aptitude elevee a l'impression |
JP3340549B2 (ja) * | 1994-03-01 | 2002-11-05 | 帝人株式会社 | 多孔性アラミド成形物の製造方法 |
JPH1072752A (ja) * | 1996-05-15 | 1998-03-17 | Matsushita Electric Ind Co Ltd | プリント配線板用不織布基材とこれを用いたプリプレグ |
JPH10212688A (ja) * | 1997-01-20 | 1998-08-11 | Shin Kobe Electric Mach Co Ltd | 積層板用基材の製造法及びその製造に用いる混抄不織布 |
JP3206500B2 (ja) * | 1997-07-02 | 2001-09-10 | 王子製紙株式会社 | 積層板基材用原料の処理方法 |
JP2000273788A (ja) * | 1999-01-21 | 2000-10-03 | Toray Ind Inc | パラ系芳香族ポリアミド繊維紙およびその製造方法 |
CN1078645C (zh) * | 1999-01-22 | 2002-01-30 | 四川省对外经济贸易总公司 | 特种合成纤维纸及其生产方法 |
JP3556114B2 (ja) * | 1999-02-08 | 2004-08-18 | 帝人テクノプロダクツ株式会社 | 芳香族ポリアミド繊維紙 |
JP4287622B2 (ja) * | 2002-06-28 | 2009-07-01 | デュポン帝人アドバンスドペーパー株式会社 | コーティングセパレータ、その製造方法およびそれを用いた電気電子部品 |
JP2005200545A (ja) * | 2004-01-15 | 2005-07-28 | Yokohama Rubber Co Ltd:The | ホース補強層間ゴム組成物およびこれを用いたホース |
-
2004
- 2004-04-16 US US10/826,530 patent/US20050230072A1/en not_active Abandoned
-
2005
- 2005-04-15 BR BRPI0509409A patent/BRPI0509409B8/pt active IP Right Grant
- 2005-04-15 WO PCT/US2005/012996 patent/WO2005103376A1/fr not_active Application Discontinuation
- 2005-04-15 JP JP2007508603A patent/JP2007532798A/ja active Pending
- 2005-04-15 EP EP05739774A patent/EP1756360B1/fr active Active
- 2005-04-15 CN CN2005800111380A patent/CN1942629B/zh active Active
- 2005-04-15 CA CA2561329A patent/CA2561329C/fr active Active
-
2011
- 2011-07-22 JP JP2011161010A patent/JP5686688B2/ja active Active
Patent Citations (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2999788A (en) * | 1958-12-09 | 1961-09-12 | Du Pont | Synthetic polymer fibrid paper |
US3756908A (en) * | 1971-02-26 | 1973-09-04 | Du Pont | Synthetic paper structures of aromatic polyamides |
US4729921A (en) * | 1984-10-19 | 1988-03-08 | E. I. Du Pont De Nemours And Company | High density para-aramid papers |
US4698267A (en) * | 1985-09-17 | 1987-10-06 | E. I. Du Pont De Nemours And Company | High density para-aramid papers |
US5026456A (en) * | 1990-06-14 | 1991-06-25 | E. I. Du Pont De Nemours And Company | Aramid papers containing aramid paper pulp |
US6942757B1 (en) * | 1993-11-29 | 2005-09-13 | Teijin Twaron B.V. | Process for preparing para-aromatic polyamide paper |
US5789059A (en) * | 1995-04-28 | 1998-08-04 | Showa Aircraft Industry Co., Ltd. | Honeycomb core |
US5948543A (en) * | 1996-02-21 | 1999-09-07 | Shin-Kobe Electric Machinery Co., Ltd. | Laminate base material, a method of producing the same, a prepreg and a laminate |
US5833807A (en) * | 1997-04-17 | 1998-11-10 | E. I. Du Pont De Nemours And Company | Aramid dispersions and aramid sheets of increased uniformity |
US6566288B2 (en) * | 1998-09-24 | 2003-05-20 | Shin-Kobe Electric Machinery Co., Ltd. | Electrically insulating non-woven fabric, a prepreg and a laminate |
US6426310B1 (en) * | 1998-09-28 | 2002-07-30 | Shin-Kobe Electric Machinery Co., Ltd. | Electrically insulating non-woven fabric, a prepreg and a laminate |
US6558512B2 (en) * | 1998-11-18 | 2003-05-06 | Oji Paper Co., Ltd. | Base material for laminate and process for producing the same |
US6120643A (en) * | 1999-10-27 | 2000-09-19 | E. I. Du Pont De Nemours And Company | Aramid and glass fiber absorbent papers |
US6544622B1 (en) * | 2000-04-03 | 2003-04-08 | Showa Aircraft Industry Co., Ltd. | Aramid honeycombs and a method for producing the same |
US6592963B1 (en) * | 2000-06-16 | 2003-07-15 | E. I. Du Pont De Nemours And Company | Honeycomb structure |
US6303221B1 (en) * | 2000-12-07 | 2001-10-16 | E. I. Du Pont De Nemours And Company | Two-component pulp reinforcement |
US20020142689A1 (en) * | 2001-01-23 | 2002-10-03 | Levit Mikhail R. | Non-woven sheet of aramid floc |
US6436236B1 (en) * | 2001-03-05 | 2002-08-20 | E. I. Du Pont De Nemours & Company | Electrically-conductive para-aramid pulp |
US20050136233A1 (en) * | 2002-08-26 | 2005-06-23 | Samuels Michael R. | Sheet material especially useful for circuit boards |
US20040072000A1 (en) * | 2002-10-01 | 2004-04-15 | Kawka Dariusz Wlodzimierz | Aramid paper laminate |
US20050284595A1 (en) * | 2004-06-25 | 2005-12-29 | Conley Jill A | Cellulosic and para-aramid pulp and processes of making same |
US20060266486A1 (en) * | 2005-05-26 | 2006-11-30 | Levit Mikhail R | Electroconductive aramid paper |
Cited By (33)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080251193A1 (en) * | 2004-10-08 | 2008-10-16 | Matsushita Electric Industrial Co., Ltd. | Method of Manufacturing Multi-Layer Circuit Board |
US8007629B2 (en) * | 2004-10-08 | 2011-08-30 | Panasonic Corporation | Method of manufacturing multi-layer circuit board |
US8444814B2 (en) * | 2005-12-21 | 2013-05-21 | Mikhail R. Levit | Paper comprising PIPD floc and process for making the same |
US8137506B2 (en) * | 2005-12-21 | 2012-03-20 | E. I. Du Pont De Nemours And Company | Paper comprising PIPD pulp and process for making same |
US20090236064A1 (en) * | 2005-12-21 | 2009-09-24 | Merriman Edmund A | Paper Comprising Pipd Pupl and Process for Making Same |
US20090250181A1 (en) * | 2005-12-21 | 2009-10-08 | E. I. Du Pont De Nemours And Company | Paper comprising pipd floc and process for making the same |
US20090126887A1 (en) * | 2005-12-21 | 2009-05-21 | E.I. Du Pont De Nemours And Company | Pipd Paper and Components Made Therefrom |
US20080145602A1 (en) * | 2006-12-15 | 2008-06-19 | Gary Lee Hendren | Processes for making shaped honeycomb and honeycombs made thereby |
US20080145596A1 (en) * | 2006-12-15 | 2008-06-19 | Levit Mikhail R | Honeycomb containing poly(paraphenylene terephthalamide) paper with aliphatic polyamide binder and articles made therefrom |
US8025949B2 (en) * | 2006-12-15 | 2011-09-27 | E.I. Du Pont De Nemours And Company | Honeycomb containing poly(paraphenylene terephthalamide) paper with aliphatic polyamide binder and articles made therefrom |
US20090155526A1 (en) * | 2007-11-30 | 2009-06-18 | E. I. Du Pont De Nemours And Company | Honeycomb having a high compression strength and articles made from same |
US8268434B2 (en) * | 2007-11-30 | 2012-09-18 | E I Du Pont De Nemours And Company | Honeycomb having a high compression strength and articles made from same |
US7803247B2 (en) * | 2007-12-21 | 2010-09-28 | E.I. Du Pont De Nemours And Company | Papers containing floc derived from diamino diphenyl sulfone |
US8118975B2 (en) * | 2007-12-21 | 2012-02-21 | E. I. Du Pont De Nemours And Company | Papers containing fibrids derived from diamino diphenyl sulfone |
US8114251B2 (en) * | 2007-12-21 | 2012-02-14 | E.I. Du Pont De Nemours And Company | Papers containing fibrids derived from diamino diphenyl sulfone |
US20090162605A1 (en) * | 2007-12-21 | 2009-06-25 | Levit Mikhail R | Papers containing floc derived from diamino diphenyl sulfone |
US20090159227A1 (en) * | 2007-12-21 | 2009-06-25 | Levit Mikhail R | Papers containing fibrids derived from diamino diphenyl sulfone |
US9428864B2 (en) * | 2012-04-18 | 2016-08-30 | E I Du Pont De Nemours And Company | Multilayered sheet |
US9316342B2 (en) * | 2012-04-18 | 2016-04-19 | E I Du Pont De Nemours And Company | Multilayered sheet |
US20150056429A1 (en) * | 2012-04-18 | 2015-02-26 | E I Du Pont De Nemours And Company | Multilayered sheet |
US20150050474A1 (en) * | 2012-04-18 | 2015-02-19 | E I Du Pont Nemoure and Company | Multilayered sheet |
US9441326B2 (en) * | 2012-04-18 | 2016-09-13 | E I Du Pont De Nemours And Company | Multilayered sheet |
US20150050475A1 (en) * | 2012-04-18 | 2015-02-19 | E I Du Pont De Nemours And Company | Multilayered sheet |
US20150318078A1 (en) * | 2012-11-23 | 2015-11-05 | Teijin Aramid B.V. | Electrical insulating paper |
US9922750B2 (en) * | 2012-11-23 | 2018-03-20 | Teijin Aramid B.V. | Electrical insulating paper |
US20150376837A1 (en) * | 2013-02-08 | 2015-12-31 | Dupont Teijin Advanced Papers (Japan), Ltd. | Colored aramid paper and process for producing same |
US9903073B2 (en) * | 2013-02-08 | 2018-02-27 | Dupont Teijin Advanced Papers (Japan), Ltd. | Colored aramid paper and process for producing same |
KR102195050B1 (ko) | 2013-02-08 | 2020-12-28 | 듀폰 테이진 어드밴스드 페이퍼 가부시끼가이샤 | 착색 아라미드지 및 그의 제조 방법 |
KR20150114564A (ko) * | 2013-02-08 | 2015-10-12 | 듀폰 테이진 어드밴스드 페이퍼 가부시끼가이샤 | 착색 아라미드지 및 그의 제조 방법 |
US10066341B2 (en) * | 2013-07-18 | 2018-09-04 | Teijin Aramid B.V. | Fire-retardant sheet material |
US10407829B2 (en) | 2015-05-28 | 2019-09-10 | Kolon Industries, Inc. | Aramid paper, manufacturing method therefor, and use thereof |
US11686048B2 (en) * | 2018-05-28 | 2023-06-27 | Teijin Aramid B.V. | Aramid-based paper with improved properties |
US20210140108A1 (en) * | 2018-05-28 | 2021-05-13 | Teijin Aramid B.V. | Aramid-based paper with improved properties |
Also Published As
Publication number | Publication date |
---|---|
BRPI0509409B1 (pt) | 2015-12-22 |
JP5686688B2 (ja) | 2015-03-18 |
JP2007532798A (ja) | 2007-11-15 |
WO2005103376A1 (fr) | 2005-11-03 |
BRPI0509409B8 (pt) | 2023-01-31 |
EP1756360B1 (fr) | 2012-08-15 |
CA2561329C (fr) | 2014-07-15 |
EP1756360A1 (fr) | 2007-02-28 |
CN1942629A (zh) | 2007-04-04 |
CN1942629B (zh) | 2010-04-07 |
BRPI0509409A (pt) | 2007-09-04 |
JP2011219913A (ja) | 2011-11-04 |
CA2561329A1 (fr) | 2005-11-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1756360B1 (fr) | Melange de papier a base d'aramide | |
KR930003396B1 (ko) | 고밀도 파라-아라미드 종이 및 이의 제조방법 | |
KR20080024144A (ko) | 전기전도성 아라미드지 | |
US11686048B2 (en) | Aramid-based paper with improved properties | |
US8118975B2 (en) | Papers containing fibrids derived from diamino diphenyl sulfone | |
CA2730906C (fr) | Noyau plie ayant un module de compression eleve et articles fabriques a partir de celui-ci | |
US20040089432A1 (en) | Non-woven sheet of aramid floc | |
EP2222918B1 (fr) | Papiers contenant des floculats dérivés de diaminodiphénylsulfone | |
WO2010056659A1 (fr) | Procédé pour fabriquer des structures de feuille à performance de compression améliorée | |
JP2012500735A (ja) | 高圧縮強度を有するハニカムコアおよびそれから製造される物品 | |
US8168039B2 (en) | Electroconductive aramid paper and tape made therefrom | |
EP1963567B1 (fr) | Papier pipd et composants obtenus à partir de celui-ci | |
US20110244193A1 (en) | Folded Core Having a High Compression Modulus and Articles Made from the Same | |
WO2010056665A1 (fr) | Structures de feuilles à performance de compression améliorée |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: E. I. DU PONT DE NEMOURS AND COMPANY, DELAWARE Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:LEVIT, MIKHAIL R.;REEL/FRAME:014894/0751 Effective date: 20040520 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |