US20020016120A1 - Non-woven fabric comprising staple fibers and an absorbent article using the same - Google Patents

Non-woven fabric comprising staple fibers and an absorbent article using the same Download PDF

Info

Publication number
US20020016120A1
US20020016120A1 US08/973,533 US97353397A US2002016120A1 US 20020016120 A1 US20020016120 A1 US 20020016120A1 US 97353397 A US97353397 A US 97353397A US 2002016120 A1 US2002016120 A1 US 2002016120A1
Authority
US
United States
Prior art keywords
woven fabric
fiber
fibers
staple
staple fibers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US08/973,533
Other languages
English (en)
Inventor
Koki Nagano
Shigeru Hirabayashi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JNC Corp
Original Assignee
Chisso Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=26499651&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20020016120(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Chisso Corp filed Critical Chisso Corp
Assigned to CHISSO CORPORATION reassignment CHISSO CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HIRABAYASHI, SHIGERU, NAGANO, KOKI
Publication of US20020016120A1 publication Critical patent/US20020016120A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/58—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives
    • D04H1/60—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives the bonding agent being applied in dry state, e.g. thermo-activatable agents in solid or molten state, and heat being applied subsequently
    • D04H1/62—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives the bonding agent being applied in dry state, e.g. thermo-activatable agents in solid or molten state, and heat being applied subsequently at spaced points or locations
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/54—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by welding together the fibres, e.g. by partially melting or dissolving
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/54—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by welding together the fibres, e.g. by partially melting or dissolving
    • D04H1/541—Composite fibres, e.g. sheath-core, sea-island or side-by-side; Mixed fibres
    • D04H1/5412—Composite fibres, e.g. sheath-core, sea-island or side-by-side; Mixed fibres sheath-core
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/54—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by welding together the fibres, e.g. by partially melting or dissolving
    • D04H1/541—Composite fibres, e.g. sheath-core, sea-island or side-by-side; Mixed fibres
    • D04H1/5414—Composite fibres, e.g. sheath-core, sea-island or side-by-side; Mixed fibres side-by-side
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/54—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by welding together the fibres, e.g. by partially melting or dissolving
    • D04H1/541—Composite fibres, e.g. sheath-core, sea-island or side-by-side; Mixed fibres
    • D04H1/5418—Mixed fibres, e.g. at least two chemically different fibres or fibre blends
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/608—Including strand or fiber material which is of specific structural definition
    • Y10T442/627—Strand or fiber material is specified as non-linear [e.g., crimped, coiled, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/608—Including strand or fiber material which is of specific structural definition
    • Y10T442/627—Strand or fiber material is specified as non-linear [e.g., crimped, coiled, etc.]
    • Y10T442/629—Composite strand or fiber material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/608—Including strand or fiber material which is of specific structural definition
    • Y10T442/627—Strand or fiber material is specified as non-linear [e.g., crimped, coiled, etc.]
    • Y10T442/632—A single nonwoven layer comprising non-linear synthetic polymeric strand or fiber material and strand or fiber material not specified as non-linear
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/608—Including strand or fiber material which is of specific structural definition
    • Y10T442/627—Strand or fiber material is specified as non-linear [e.g., crimped, coiled, etc.]
    • Y10T442/632—A single nonwoven layer comprising non-linear synthetic polymeric strand or fiber material and strand or fiber material not specified as non-linear
    • Y10T442/633—Synthetic polymeric strand or fiber material is of staple length
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/637—Including strand or fiber material which is a monofilament composed of two or more polymeric materials in physically distinct relationship [e.g., sheath-core, side-by-side, islands-in-sea, fibrils-in-matrix, etc.] or composed of physical blend of chemically different polymeric materials or a physical blend of a polymeric material and a filler material
    • Y10T442/641—Sheath-core multicomponent strand or fiber material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/69—Autogenously bonded nonwoven fabric

Definitions

  • the invention relates to a non-woven fabric comprising staple fibers. More specifically, it relates to a non-woven fabric comprising staple fibers, which is suitable for sanitary materials such as disposable diapers, sanitary napkins, incontinence pads, nursing pads or the like, or wipers, and to absorbent articles using the non-woven fabric comprising staple fibers.
  • Japanese Patent Publication No. Sho 52-12830 discloses a non-woven fabric produced by a process wherein thermal adhesive conjugated fibers are aligned by the use of a carding machine and then piled up and entangled to be adjusted to the predetermined basis weight, followed by conducting a thermal adhesion between fibers by a thermal treatment.
  • the object of the present invention is to provide a bulky non-woven fabric in which the sufficient contribution to bulkiness by fibers of the non-woven fabric is exhibited.
  • the non-woven fabric comprising staple fibers of the present invention and the absorbent article using the non-woven fabric of the present invention are as follows.
  • a non-woven fabric formed of staple fibers which comprises at least one kind of staple fiber having a fiber length of 3 to 25 mm and a single fiber fineness of 1 to 100 denier, and is produced by the fibers being dropped and dispersed to be accumulated and adhered at the intersection point of each staple fiber; the non-woven fabric has a specific volume of 40 to 200 cm 3 /g, the number of fiber lumps having a volume of not less than 1 mm 3 is not more than 5 lumps per 20 g of the non-woven fabric.
  • the non-woven fabric comprising staple fibers according to the above item (1), wherein at least one kind of staple fiber is a staple fibers having 3 to 20 spiral type crimps per inch (2.54 cm).
  • the non-woven fabric comprising staple fibers according to the above item (1), wherein at least one kind of staple fiber is olefin thermoplastic fiber or polyester thermoplastic fiber.
  • the non-woven fabric comprising staple fibers according to the above item (1), wherein at least one staple fiber is a staple fiber having an eccentric core and sheath type structure comprising high crystalline polypropylene as a core component and high density polyethylene as a sheath component.
  • FIG. 1 is a side elevational view of an apparatus for producing the non-woven fabric of the present invention.
  • FIG. 2 is a partial cutaway view of an air laid apparatus 1 of the apparatus shown in FIG. 1.
  • FIG. 3 is a cross sectional view taken on line E-E′ of the apparatus according to FIG. 2.
  • the fibers used for the non-woven fabric comprising staple fibers of the present invention the following examples can be mentioned: natural fibers such as pulp, cotton and the like; regenerated fibers such as rayon; semi synthetic fibers such as acetate; and synthetic fibers such as nylon, vinylon, polyester, acrylic, polyethylene, polypropylene, polystyrene and the like.
  • the fibers used for the non-woven fabric of the present invention are not particularly limited as long as they are adhered in a case where binders are used and they do not give an adverse effect on the uniformity of the non-woven fabric.
  • thermal adhesive thermoplastic fibers being capable of thermal adhesion between fibers at the intersection points in a short time, without using powder-like binders that fall in the form of small particles or water soluble binders that need to be dried, are preferable.
  • the fiber length of the staple fiber constituting the non-woven fabric comprising staple fibers of the present invention needs to be in the range of 3 to 25 mm. Preferably, it is in the range of 3 to 15 mm, more preferably, in the range of 5 to 10 mm.
  • the number of crimps is approximately 5 crimps per inch (2.54 cm). Therefore, the appropriate fiber length is 5 mm which corresponds to the length of once winding of crimp and 10 mm which corresponds to the length of twice winding of crimps. If the fiber length is less than 3 mm, the strength of the non-woven fabric lowers.
  • the fiber length is more than 25 mm, it is difficult to produce a uniform web, because fibers are entangled with each other before passing through a sieve or a screen.
  • the fiber thickness is in the range of 1 to 100 denier, preferably in the range of 1.5 to 35 denier. More preferably, it is in the range of 1.5 to 20 denier. If the fiber thickness is less than 1 denier, the density of the fiber in the cylindrical screen increases, so that a uniform web cannot be produced. On the other hand, if the fiber thickness is more than 100 denier, the ability of fibers to entangle each other becomes strong, so that it is difficult to produce a uniform web.
  • the specific volume of the non-woven fabric comprising staple fibers of the present invention is in the range of 40 to 200 cm 3 /g. Preferably, it is in the range of 70 to 150 cm 3 /g. It is not preferable for the specific volume of the non-woven fabric to be less than 40 cm 3 /g, since the non-woven fabric becomes hard. Also, it is not preferable for the specific volume of the non-woven fabric to be more than 200 cm 3 /g, since the strength of the non-woven fabric is lowered.
  • the number of fiber lumps having a volume of not less than 1 mm 3 is not more than 5 lumps per 20 g of the non-woven fabric. It is not preferable for the fiber lumps of such size included in the non-woven fabric to be more than the above mentioned range, since there arise some disadvantages: the non-woven fabric becomes not-uniform, has a rough touch and becomes non-uniform in the coloring due to fiber lumps.
  • the fibers used for the non-woven fabric of staple fibers of the present invention are conjugated fibers comprising at least two components (hereinafter, the component (A) and the component (B) will be used for an abbreviation), the below mentioned resins etc. can be used as materials.
  • resins of the component (A) the following can be used: polyolefins such as polypropylene, high density polyethylene, medium density polyethylene, low density polyethylene, linear low density polyethylene, binary copolymer or terpolymer of propylene with other ⁇ -olefin and the like; polyamides; polyesters such as polyethylene terephthalate, polybutylene terephthalate, low melting point polyester from copolymerizing diol and terephthalic acid / isophthalic acid etc., polyester elastomer and the like; fluororesin; the mixture of the above mentioned resins; other resins that can be spun.
  • polyolefins such as polypropylene, high density polyethylene, medium density polyethylene, low density polyethylene, linear low density polyethylene, binary copolymer or terpolymer of propylene with other ⁇ -olefin and the like
  • polyamides polyesters such as polyethylene terephthalate, polybutylene terephthalate,
  • resins of the component (B) the following can be used: polyolefins such as polypropylene, high density polyethylene, medium density polyethylene, low density polyethylene, linear low density polyethylene, binary copolymer or terpolymer of propylene with other ⁇ -olefin and the like; polyamides; polyesters such as polyethylene terephthalate, polybutylene terephthalate, low melting point polyester from copolymerizing diol and terephthalic acid / isophtalic acid etc., polyester elastomer and the like; fluororesin; the mixture of the above mentioned resins; other resins that can be spun.
  • polyolefins such as polypropylene, high density polyethylene, medium density polyethylene, low density polyethylene, linear low density polyethylene, binary copolymer or terpolymer of propylene with other ⁇ -olefin and the like
  • polyamides polyesters such as polyethylene terephthalate, polybutylene terephthalate,
  • the difference in the melting point between the component (A) and the component (B) is not less than 10° C. Consequently, when the thermal treatment is conducted at the temperature not less than the melting point of the low melting point component and less than the melting point of the high melting point component, the low melting point component of the conjugated fiber melts and the high melting point component remains as it is. As a result, the thermal adhesive non-woven fabric having a three dimensional network structure can be formed. Moreover, in the above, when the melting point is not clearly determined, the melting point denotes the softening point. The measurement of the softening point is conducted under the conditions specified in JIS K 2531.
  • the following examples can be mentioned: high density polyethylene/polypropylene, low density polyethylene/propylene-ethylene-butene-1 crystalline terpolymer, high density polyethylene/polyethylene terephthalate, nylon 6/nylon 66, low melting point polyester/polyethylene terephthalate, polypropylene/polyethylene terephthalate, polyvinylidene fluoride/polyethylene terephthalate, the mixture of linear low density polyethylene and high density polyethylene/polyethylene terephthalate and the like.
  • thermoplastic conjugated fiber comprises olefin resin or polyester resin, or the combination thereof.
  • resin components (A) and (B) the following examples can be mentioned: high density polyethylene/polypropylene, low density polyethylene/propylene-ethylene-butene-1 crystalline terpolymer, high density polyethylene/polyethylene terephthalate, low melting point polyester/polyethylene terephthalate, polypropylene/polyethylene terephthalate, linear low density polyethylene/polyethylene terephthalate and the like.
  • the shapes of the conjugated fiber are not limited and can be a core and sheath type, an eccentric core and sheath type, a side-by-side type, a multi-layer type having three layers or more, a hollow multi-layer type, a modified (non-circular) multi-layer type etc. and other structures in which the low melting point resin component forms at least one part of the fiber surface.
  • thermoplastic conjugated fiber having an eccentric core and sheath type structure comprising high crystalline polypropylene as a core component and high density polyethylene as a sheath component and having spiral type crimps.
  • a fiber having spiral type crimps has much space per a single fiber, so that a web formed by piling up fibers has a very high bulkiness.
  • the bulkiness of the web depends much on the number of crimps of the thermoplastic fibers used for a non-woven fabric.
  • the thermoplastic fiber has 3 to 20 spiral type crimps per an inch (2.54 cm).
  • “3 to 20 crimps per an inch (2.54 cm)” denotes that 3 to 20 crimps are included in an inch (2.54 cm) of fiber length.
  • it is a fiber having 5 to 15 spiral type crimps per an inch (2.54 cm), more preferably it is a fiber having 5 to 10 spiral type crimps per an inch (2.54 cm).
  • the non-woven fabric using fibers having the above mentioned range of number of crimps has high bulkiness.
  • the fiber is not different from the straight type fiber and the bulkiness tends to be lowered.
  • the spiral type crimps are far more than 20 crimps per an inch (2.54 cm)
  • the space per a single fiber becomes small, and thus the bulkiness of the non-woven fabric conversely tends to be reduced.
  • the composition ratio of the low melting point component to high melting point component is: the low melting point resin component is in the range of 10 to 90 wt. % and the high melting point resin component is in the range of 90 to 10 wt. %. More preferably, the low melting point resin component is in the range of 30 to 70, wt. % and the high melting point resin component is in the range of 70 to 30 wt. %. If the low melting point component is less than 10 wt. %, the tensile strength of the thermal adhesive non-woven fabric comprising conjugated fibers tends to be reduced. On the other hand, if the low melting point component is more than 90 wt. %, too little core component remains without melting, so that the bulkiness of the thermal adhesive non-woven fabric comprising conjugated fibers tends to be reduced.
  • the non-woven fabric has a uniformity, but does not have the high bulkiness, thus making the non-woven fabric very flat. As a result, the applicability as commercial products is reduced. However, in a case where the staple fiber having actual crimps is used, the non-woven fabric having a high bulkiness can preferably be produced.
  • the shape of the crimps of staple fibers used for the non-woven fabric comprising staple fibers the following examples can be mentioned: spiral (three dimensional crimps) type crimps, zig-zag type crimps, wave type crimps or the like.
  • the staple fibers having any of the above mentioned shapes of crimps can be applied to a non-woven fabric comprising staple fibers of the present invention.
  • the most preferable crimp is a spiral type crimp.
  • staple fibers that are easily entangled and staple fibers that are less easily to be entangled there are staple fibers that are easily entangled and staple fibers that are less easily to be entangled. If classified, the staple fibers having a zig-zag type crimps and having a large number of crimps and/or having high crimp set force tend relatively to be easily entangled. Moreover, the staple fibers having the wave type crimps with fish-hook shaped ends tend to be easily entangled. The staple fibers having the spiral type crimps are particularly preferable since their ends of fibers are approximately on the same circumference and are not easily entangled.
  • a fiber lump that gives an adverse effect on the uniformity of the non-woven fabric is divided into two types: one is the entangled fibers and another is the portion where the fibers are not sufficiently opened.
  • the not-opened portions individual fibers are spaced closely after the opening step. Therefore, the effective method for preventing the generation of fiber lumps is to space each fiber less closely.
  • not-opened portions can be reduced by selecting a shape of crimps. When the shape of crimps is the wave type, fibers are easily dispersed and few not-opened portions are generated as compared with the zig-zag type crimps.
  • the shape of crimps is the spiral type, fibers are easily be dispersed and few not-opened portions are generated as compared with the wave type crimps. In other words, the entanglement of fibers and generation of the not-opening portion can be inhibited by selecting the shape of crimps.
  • the object of the present invention namely to provide the bulky non-woven fabric in which sufficient contribution to bulkiness by fibers is exhibited, can be attained by producing the non-woven fabric in the following way: a web is produced by making short fibers pass through a sieve or screen and dropped with uniform dispersion in three dimensions to be accumulated, and by thermally adhering the intersection point of each fiber by thermal treatment.
  • non-woven fabric produced by the method of making fibers pass through a sieve or screen, fibers are dropped with dispersion in three dimensions to be accumulated.
  • Such non-woven fabric has a greater specific volume as compared with the non-woven fabric in which fibers are aligned in one direction by the carding machine.
  • the non-woven fabric having a large specific volume has a soft touch and is particularly suitable for products that directly contact the users' skin, for example, absorbent articles of disposable diapers, sanitary napkins or the like.
  • such non-woven fabric is preferably used for applications that requires a cushioning property, for example, bandage or eye bandage, table linen, cooking towel, packing materials for glass or ceramics, packing materials for fresh products and flowers, packing materials for instruments and furniture and the like.
  • thermal adhesive conjugated fibers used for the non-woven fabric comprising staple fibers of the present invention can be produced by, for example, the following step.
  • Resins for a core component and a sheath component are melted and discharged from, for example, the composite spinneret having 100 to 350 holes.
  • unstretched fibers are cooled by cooling just below the spinneret.
  • Unstretched fibers of 3 to 400 denier are produced by taking up at the discharging volume of 100 to 200 g/min and at the taking up speed of 40 to 1300 m/min.
  • the unstretched fibers are stretched between the two rollers heated at temperatures of 60 to 120° C., while making the rotating speed of the second roll greater than that of the first roll.
  • Stretched fibers of 1 to 100 denier are produced by stretching with the ratio of the rotating speed of the first roll to the second roll in the range of 1:2 to 1:5. Finishing agents are applied to the stretched fibers by using a contact roller, followed by making the stretched fibers pass through a box-type crimp processor to produce a tow having crimps. It is preferable that the number of crimps is 0 to 25 crimps per an inch. Since the tow contains approximately 10 wt. % of water, it is dried by the use of a drier at 60 to 120° C. The dried tow is cut with a push-cutting type cutter into fibers having the constant length ranging from 3 to 25 mm. Such fiber length is substantially shorter than fibers used for the non-woven fabric produced by the conventional carding process.
  • the non-woven fabric having a different fineness or a different shape of staple fiber is used at each forming head. Consequently, the non-woven fabric having a density gradient in the thickness direction can be produced.
  • the non-woven fabric having a density gradient in the thickness direction produced by the above mentioned method, can be used as non-woven fabric materials for filters, such as a liquid filter, an air filter etc.
  • the non-woven fabric comprising staple fibers produced by the above mentioned method can be used for a non-woven fabric as a surface material, second sheet, or back layer material sheet.
  • the non-woven fabric comprising staple fibers has a high bulkiness, it is preferably used for the second sheet that requires the high bulkiness.
  • the non-woven fabric comprising mixture of pulp, thermal adhesive fibers and high absorptive materials is preferably used as absorbent articles which do not lose shape when absorbing urine.
  • the non-woven fabric comprising staple fibers of the present invention can be produced as follows with staple fibers having a fiber length of 3 to 25 mm and by the use of the air laid type apparatus.
  • an air laid type apparatus comprises: a casing 2 having a trapezoidal shaped cross section and having an opening portion in its bottom face only; fiber feeding openings 3 and 4 which are provided at both ends of the casing 2 ; web forming heads 5 and 6 corresponding to the feeding openings 3 and 4 , comprising cylindrical screens 5 a and 6 a which are positioned parallel to the side face of the casing 2 and are capable of rotating; needle rolls 5 b and 6 b which are provided in a way to contact each inner wall of the cylindrical screens 5 a and 6 a, and fiber circulation zones 7 and 8 which are respectively provided at the both ends of cylindrical screens 5 a and 6 a and at the both ends of the casing 2 .
  • a net conveyor 9 a is provided just below the lower face of the air laid type apparatus.
  • a pair of drive rolls 17 a and 17 b and a suction unit 10 are attached to the net conveyor 9 a.
  • an apparatus for carrying out the next step in the air laid type apparatus comprises: a suction drier 12 for thermally adhering the conjugated fibers constituting a web, a net conveyor 9 b which makes the web pass through the suction drier 12 , a pair of drive rolls 17 c and 17 d for driving the net conveyor 9 b thereunder; and a pressing roll 11 on the drive roll 17 c across the net conveyor 9 b.
  • a feed roll 18 for feeding the produced thermal adhesive non-woven fabric 14 and a pair of drive rolls 19 a and 19 b for driving a take-up roll 14 are provided.
  • the circulated fibers are discharged through the rotating cylindrical screens 5 a and 6 a by means of centrifugal force and shearing effect generated by both the rotations of the needle rolls 5 b and 6 b rotating in the direction of arrow AA′ and the cylindrical screens 5 a and 6 a rotating in the direction of arrow BB′.
  • the discharged fibers are sucked by the use of the suction unit 10 from the lower portion of the casing 2 and are collected on the net conveyor 9 a.
  • the collected web 16 is pressed between the web pressing roll 11 and the drive roll 17 c of the net conveyor 9 b. At this time, the collected fibers are oriented in random directions and form a web.
  • the web 16 is pressed by using the pressing roll 11 and provided to the suction drier 12 and then thermally treated at a temperature not less than the melting point of the low melting point component and not more than the melting point of the high melting point component, for example, in the range of 90 to 170° C., for 3 to 10 seconds.
  • the thermal adhesive non-woven fabric 13 having a three dimensional network structure is formed and taken up by the take-up roll 14 .
  • the production method of making the staple fibers pass through a sieve or net which comprises a wide variety of mesh is conducted. Specifically, it is preferable that the method of making the staple fibers pass through a screen with dispersion to be accumulated is conducted.
  • the shape of holes of the screen of the cylindrical screens 5 a and 6 a is generally a laterally longer rectangle. It is preferable that the laterally longer rectangle having the longitudinal length of which is 1 to 3 mm and the lateral length of which is 15 to 30 mm.
  • the shape of the holes is not limited to a laterally longer rectangle and may be circle, triangle, quadrangle, polygon and oval besides a laterally longer rectangle. It is preferable that the rate of the hole area of the screen is 20 to 50%.
  • the non-woven fabric comprising thermal adhesive conjugated fibers is thermally adhered in the intersection point of each fiber by thermal treatment using the suction drier 12 after the formation of web.
  • This thermal treatment may be conducted by the use of heating apparatus such as a thermal calendar roll etc. instead of the suction drier 12 .
  • the basis weight of the resultant non-woven fabric is not particularly limited. However, it is preferable that the basis weight is about 10 to 1000 g/m 2 .
  • the basis weight is about 10 to 60 g/m 2 ; in the case of wipes, about 10 to 500 g/m 2 ; in the case of filters, about 10 to 1000 g/m 2 .
  • the apparent density of the non-woven fabric is not particularly limited. However, it is preferably about 0.017 to 0.10 g/cm 3 when the hand feeling is taken into consideration.
  • the non-woven fabric having higher density can be produced by carrying out a thermal pressing process or thermal rolling process or the like as an after-processing treatment.
  • the rate of the thermo-compression area be in the range of 10 to 30%.
  • the non-woven fabrics comprising staple fibers of the present invention can be used for a wide variety of applications by themselves, or after being laminated, sewn, or thermally adhered with another material.
  • they when they are used as a member of pants type disposable diapers, they can be used for the portion where both hand feeling and strength are required, for example, as front surface materials, back sheets etc.
  • the non-woven fabric when used for the pants type disposable diapers and the like, they can be used in combination with other members or thermal adhesive non-woven fabric such as a stretchable and contractable material for closely contacting with the trunk or legs portions.
  • the thermal adhesive non-woven fabric can be used as cover materials of the above mentioned front surface materials or back surface materials or the like, by laminating other non-woven fabric or tissue papers, webs, films or the like.
  • the non-woven fabric comprising staple fibers of the present invention can be used as wipes for furniture, cars and the like by applying various kinds of lubricant.
  • the non-woven fabric comprising staple fibers can be made into filter materials by subjecting the non-woven fabrics to an after-processing treatment such as a pleat processing, forming into a cylindrical shape, winding the thermal adhesive non-woven fabric to form into a cylindrical shape, and winding while heating to form into a thermally adhered cylindrical shape.
  • an after-processing treatment such as a pleat processing
  • X denotes the basis weight of the non-woven fabric (g/m 2 ) and Y denotes the thickness of the non-woven fabric (cm).
  • the size of the non-woven fabric sample used herein was 25 cm ⁇ 25 cm.
  • the number of fiber lumps having a volume not less than 1 mm 3 existing in 20 g of the non-woven fabric was defined as the number of fiber lumps.
  • rayon fibers and thermal adhesive fibers 15 which were made to pass through the opening apparatus, were inserted into the fiber insertion openings 3 and 4 by way of the fiber feeding circulation duct and discharged from the rotating cylindrical screens 5 a and 6 a.
  • the discharged fibers were collected on the net conveyor 9 a having the suction apparatus 10 moving at the speed of 90 m/min to form the web 16 .
  • the web 16 was compressed with the web compressing roll 11 , it was thermally treated at 150° C. for three seconds by the use of the suction drier 12 , and thereby high density polyethylene of the sheath component was melted and adhered to produce the non-woven fabric 13 . Then the non-woven fabric 13 was taken up into the take-up roll 14 .
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 3.6 mm, specific volume of 143 cm 3 /g, and the number of the fiber lumps of 2.1 lumps per 20 g.
  • the results are shown in Table 1.
  • a method for producing thermal adhesive staple fibers :
  • High crystalline polypropylene having MFR (melt flow rate) of 11 g per 10 minutes (the conditions 14 specified in JIS K7210) as a core component and high density polyethylene having MI (melt index) of 16.5 g per 10 minutes (the conditions 4 specified in JIS K7210) were spun out of an eccentric core and sheath type spinneret having 621 holes at the discharging ratio of high crystalline polypropylene to high density polyethylene of 5:5 and at the discharging volume of 450 g/min, and then taken up at the speed of 592 m/min to produce 11 denier unstretched fibers.
  • fibers were cooled by air cooling just below the spinneret, and then finishing agent comprising lauryl phosphate potassium salt as a main component was applied by using a contact roll.
  • This unstretched fiber was stretched between the first roll and the second roll to produce a stretched fiber having the fineness of 3 denier and spiral type crimps.
  • the first roll was 90° C. and the second roll was 20° C., and the rotating ratio of the first roll to the second roll was set to be 1:4.5.
  • This stretched fiber having spiral type crimps was cut into fibers of 5 mm in length by using the push-cutting type cutter.
  • the conjugated fibers were fed into and made to pass through an opening apparatus and opened mechanically, and then treated by feeding the opened fibers to the air-laid type apparatus shown in FIG. 1 to FIG. 5.
  • the opened conjugated fiber 18 was fed into the fiber inserting openings 3 and 4 by way of the fiber feeding circulation duct and discharged from the rotating cylindrical screen 5 a and 6 a.
  • the discharged fibers were collected on the net conveyor 9 a having the suction apparatus 10 moving at the speed of 90 m/min to form into the web 16 . After the web was compressed with the web compressing roll 11 , it was thermally treated at 150° C.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 4.6 mm, specific volume of 185 cm 3 /g, and the number of the fiber lumps of 1.2 lumps per 20 g.
  • the results are shown in Table 1.
  • the non-woven fabric was produced under the same conditions as Example 2 except that the fiber length of the conjugated fiber was made to be 10 mm.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 4.4 mm, specific volume of 176 cm 3 /g, and the number of the fiber lumps of 1.9 lumps per 20 g.
  • the results are shown in Table 1.
  • the non-woven fabric was produced under the same conditions as Example 2 except that the fiber length of the conjugated fiber was made to be 15 mm.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 4.25 mm, specific volume of 170 cm 3 /g, and the number of the fiber lumps of 3.8 lumps per 20 g.
  • the results are shown in Table 1.
  • a method for producing the non-woven fabric using polyester staple fibers and side-by-side type conjugated fiber 30 wt. % of polyester fibers having 14 zig-zag type crimps per inch (2.54 cm), and being 2 d/f ⁇ 5 mm and 70 wt. % of side-by-side type conjugated fibers comprising a polypropylene component and a high density polyethylene component, having 6 spiral type crimps per inch (2.54 cm) and being 2 d/f ⁇ 5 mm were fed into and made to pass through an opening apparatus, thus opening the fibers mechanically. Then, the opened fibers were fed into an air laid type apparatus shown in FIG. 1 to FIG. 3 and treated therein.
  • the opened polyester fibers and side-by-side type conjugated fibers 15 were inserted into the fiber insertion openings 3 and 4 by way of the fiber feeding circulation duct and discharged from the rotating cylindrical screens 5 a and 6 a.
  • the discharged fibers were collected on the net conveyor 9 a having the suction apparatus 10 moving at the speed of 90 m/min to form into the web 16 .
  • the web was compressed with the web compressing roll 11 , it was thermally treated at 150° C. for three seconds by the use of the suction drier 12 , and thereby high density polyethylene of the sheath component was melted and adhered to produce the non-woven fabric 13 . Then the non-woven fabric 13 was taken up by the take-up roll 14 .
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 3.4 mm, specific volume of 137 cm 3 /g, and the number of the fiber lumps of 2.2 lumps per 20 g.
  • the results are shown in Table 1.
  • the non-woven fabric was produced under the same conditions as Example 2 except that high crystalline polypropylene having MFR of 11 g per 10 minutes (the conditions 14 specified in JIS K7210) and high density polyethylene having MI of 16.5 g per 10 minutes (the conditions 4 specified in JIS K7210) were spun out of a side-by-side type composite spinneret having 621 holes at the discharging ratio of high crystalline polypropylene to high density polyethylene of 5:5 and at the discharging volume of 450 g/min, and then taken up at the speed of 592 m/min to produce 8.1 denier unstretched fibers.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 4.5 mm, specific volume of 181 cm 3 /g, and the number of the fiber lumps of 1.3 lumps per 20 g.
  • the results are shown in Table 1.
  • Fibers were produced under the same conditions as Example 6 except that the number of holes of the spinneret was 60, the discharging volume was 200 g/min, the taking-up speed was 417 m/min, the unstretched fiber was 72 denier, the stretched fiber was 18 denier and the number of spiral crimps was 6 crimps per inch (2.54 cm).
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 3.9 mm, specific volume of 156 cm 3 /g, and the number of the fiber lumps of 0.5 lumps per 20 g.
  • the results are shown in Table 1.
  • a method for producing thermal adhesive staple fibers :
  • This unstretched fiber was stretched between the first roll and the second roll to form 2 denier stretched fiber.
  • the first and second rolls were heated at 90° C. respectively and the rotating ratio of the first roll to the second roll was set to be 1:4.
  • a finishing agent comprising lauryl phosphate potassium salt as a main component was applied to this stretched fiber by using a contact roll. Then, they were made to pass through a box type crimp processing apparatus to produce a tow having 14 zig-zag type crimps per inch.
  • this tow contained a water component, it was dried at the temperature of 90° C. by using a drier and then it was cut into fibers of 10 mm in length by using a push-cutting type cutter.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 2.8 mm, specific volume of 79 cm 3 /g, and the number of the fiber lumps of 4.5 lumps per 20 g.
  • the results are shown in Table 1.
  • 114 denier of unstretched fibers were produced by the use of a spinneret having 60 holes by taking up at the discharging volume of 200 g/min and at the taken-up speed of 263 m/min, then they were produced into 32 denier stretched fibers.
  • Thermally adhesive conjugated fibers were produced under the same conditions as Example 8 except that 10 crimps per inch of zig-zag type crimps were provided and the fiber length was 10 mm.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 2.6 mm, specific volume of 45 cm 3 /g, and the number of the fiber lumps of 3.6 lumps per 20 g.
  • the results are shown in Table 1.
  • Fibers were produced under the same conditions as Example 8 except that 340 denier unstretched fibers were produced by the use of a spinneret having 100 holes by taking up at the discharging volume of 200 g/min and at the taken-up speed of 53 m/min while cooling the fibers with water at the time of spinning, then they were produced into 100 denier stretched fibers, and the 10 zig-zag type crimps per inch were provided and the fiber length was 25 mm.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 2.65 mm, specific volume of 58 cm 3 /g, and the number of the fiber lumps of 2.4 lumps per 20 g.
  • the results are shown in Table 1.
  • the unstretched fibers were stretched between the first roll and the second roll. At this time, the first roll was heated at 90° C. and the second roll was heated at 20° C. and the rotating ratio of the first roll to the second roll was set to be 1:4.5. After a finishing agent comprising lauryl phosphate potassium salt as a main component was applied to this stretched fiber by using a contact roll, they were made to pass through a box-type crimps processing apparatus to produce a tow having 9 wave type crimps per inch. The stretched fibers having wave type crimps were cut into fibers of 5 mm in length by using a push-cutting type cutter.
  • the resultant non-woven fabric had a basis weight of 23 g/m 2 , a thickness of 3.75 mm, specific volume of 163 cm 3 /g, and the number of the fiber lumps of 1.8 lumps per 20 g.
  • the results are shown in Table 1.
  • Polypropylene having MFR of 10 g per 10 minutes (the conditions 14 specified in the JIS K7210) and polypropylene having MI of 23 g per 10 minutes (the conditions 14 specified in the JIS K7210) were spun out of a side-by-side type spinneret having 350 holes at the discharging ratio of each polypropylene of 5:5 and at the discharging volume of 200 g/min, and then taken up at the speed of 635 m/min to produce 8.1 denier unstretched fibers.
  • fibers were cooled by air cooling just below the spinneret.
  • a finishing agent containing lauryl phosphate potassium salt as a main component was applied by using a contact roll.
  • the unstretched fibers were stretched between the first roll and the second roll to produce 2 denier stretched fibers having spiral type crimps.
  • the first roll was heated at 90° C. and the second roll was heated at 20° C. and the rotating ratio of the first roll to the second roll was set to be 1:4.5.
  • the unstreteched fiber having spiral type crimps was cut into fibers of 10 mm in length by using a push-cutting type cutter.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 3.25 mm, specific volume of 130 cm 3 /g, and the number of the fiber lumps of 1.4 lumps per 20 g.
  • the results are shown in Table 1.
  • the unstretched fibers were stretched between the first roll and the second roll. At this time, the first and second rolls were heated at 90° C. respectively and the rotating ratio of the first roll to the second roll was set to be 1:3.3.
  • a finishing agent comprising lauryl phosphate potassium salt as a main component was applied to the stretched fibers by using a contact roll. Then, they were made to pass through a box-type crimps processing apparatus to produce a tow having 5 wave type crimps per an inch (2.54 cm).
  • the stretched fiber having wave type crimps was cut into fibers of 10 mm in length by using a push-cutting type cutter.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 3.0 mm, specific volume of 101 cm 3 /g, and the number of the fiber lumps of 2.6 lumps per 20 g.
  • the results are shown in Table 1.
  • the non-woven fabric was produced under the same conditions as Example 2 except that the fiber length was 38 mm and a carding apparatus was used at the time of production of a web.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 0.9 mm, specific volume of 36 cm 3 /g, and the number of the fiber lumps of 0.9 lumps per 20 g.
  • the resultant non-woven fabric had a smaller specific volume as compared with other Examples, because of the non-woven fabric produced by the carding process.
  • the results are shown in Table 1.
  • the non-woven fabric was produced under the same conditions as Example 2 except that the fiber length was 30 mm.
  • the resultant non-woven fabric had a basis weight of 25 g/m 2 , a thickness of 2.75 mm, specific volume of 110 cm 3 /g, and the number of the fiber lumps of 8.5 lumps per 20 g.
  • the non-woven fabric was produced by an air laid method.
  • the fiber length was longer than 25 mm, so that fibers are easily entangled and the resultant non-woven fabric had many fiber lumps. Therefore, the resultant non-woven fabric was inferior in uniformity; had a rough touch; and had not uniformed hue, namely, many white portions were found remarkably in the non-woven fabric due to fiber lumps. Therefore, this non-woven fabric was evaluated as bad in hand feeling and appearance. The results are shown in Table 1.
  • the commercially available disposable diaper comprised; a front surface material which was produced from the non-woven fabric comprising polyethylene/polypropylene thermal adhesive conjugated staple fibers and the intersection points of the fibers were thermally adhered; a water absorptive material comprising a pulp and high absorptive resin as main components; and back surface material comprising polyethylene film. Only the front surface material was cut off with a knife and removed, followed by laminating the thermal adhesive non-woven fabric obtained in the above mentioned Example 3 to the same place where the front surface material had been placed. Moreover, the thermal adhesive non-woven fabric and the remaining non-woven fabric which was located near the leg portions were thermally adhered.
  • thermal adhesive non-woven fabric was cut off with scissors and removed, to thus produce a disposable diaper in which thermal adhesive non-woven fabric was laminated as a front surface material.
  • This diaper had a great strength in the lateral direction (opposite to the longitudinal direction) of the non-woven fabric, a high bulkiness and soft hand feeling, and was usable for a preferable disposable diaper.
  • the non-woven fabric having a high bulkiness well contributed to the fibers and little generation of fiber lumps, and having good surface properties can be obtained.
  • the fiber length of the fiber used for the thermal adhesive non-woven fabric of the present invention was shorter than that of the non-woven fabrics produced by the carding method. Consequently, as the number of fibers constituting fabric increases, uneven dispersion of the fibers was prevented to thus produce a uniform non-woven fabric.
  • the non-woven fabric of the present invention since the non-woven fabric of the present invention is produced by fibers being fallen with dispersing to accumulate, the non-woven fabric of the present invention has smaller density and greater ventilation degree as compared with the non-woven fabric produced by the carding process in which fibers are combed and oriented in one direction.
  • the non-woven fabric comprising staple fibers of the present invention is produced by short fibers being dropped while being dispersed to be accumulated.
  • this non-woven fabric overcomes the defects: the non-woven fabric produced by the carding process lose the bulkiness because fibers are drawn, to thus provide the non-woven fabric having a high bulkiness and softness.
  • the non-woven fabric comprising staple fibers of the present invention has shorter fiber length than the non-woven fabric produced by the carding process, so that fibers are laminated in a random dispersion state.
  • the uniform non-woven fabric having little non-uniformity in the density can be obtained.
  • the non-woven fabrics are produced by fibers which are dropped with dispersion in the three dimensional direction to be accumulated, so that it has a smaller density, higher ventilation, more excellent soft feeling and touch as compared with the non-woven fabric produced by the carding process in which fibers are carded and oriented.
  • the non-woven fabric of the present invention has a soft feeling and is particularly suitable for such application as directly contacts with users' skin, for example, absorbent articles for disposable diapers, sanitary napkins, incontinence pads, nursing pads or the like.
  • the non-woven fabric of the present invention has a high specific volume, high bulkiness and an excellent cushioning property, it is preferably used for applications that require an excellent cushioning property, for example, bandage or eye bandage, or table linen, cooking towel, packing materials for glass ceramics, packing materials for fruits and vegetables and flowers, packing materials for instruments and furniture etc.
  • the non-woven fabric having a density inclination in the thickness direction produced by the above mentioned method can be used as non-woven fabric materials for filters, such as a liquid filter, an air filter etc.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Nonwoven Fabrics (AREA)
US08/973,533 1996-06-19 1997-06-16 Non-woven fabric comprising staple fibers and an absorbent article using the same Abandoned US20020016120A1 (en)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP8-179964 1996-06-19
JP17996496 1996-06-19
JP35186396 1996-12-11
JP8-351863 1996-12-11

Publications (1)

Publication Number Publication Date
US20020016120A1 true US20020016120A1 (en) 2002-02-07

Family

ID=26499651

Family Applications (1)

Application Number Title Priority Date Filing Date
US08/973,533 Abandoned US20020016120A1 (en) 1996-06-19 1997-06-16 Non-woven fabric comprising staple fibers and an absorbent article using the same

Country Status (6)

Country Link
US (1) US20020016120A1 (de)
EP (1) EP0906981A4 (de)
JP (1) JP3219250B2 (de)
AU (1) AU3107797A (de)
CA (1) CA2256550A1 (de)
WO (1) WO1997048846A1 (de)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020147433A1 (en) * 1998-03-12 2002-10-10 Mcosker Jocelyn Elaine Proton donating actives in absorbent articles
US20030018971A1 (en) * 2001-07-19 2003-01-23 Mckenna Thomas P. System and method for providing supplemental information related to a television program
EP1504741A1 (de) * 2003-08-07 2005-02-09 The Procter & Gamble Company Durch Latex verklebte Flüssigkeitsaufnahmeschicht mit druckunabhängigen Flüssigkeitshandhabungseigenschaften
US20060163152A1 (en) * 2005-01-21 2006-07-27 Ward Bennett C Porous composite materials comprising a plurality of bonded fiber component structures
US20080245037A1 (en) * 2005-02-04 2008-10-09 Robert Rogers Aerosol Separator; and Method
US20110154790A1 (en) * 2005-02-22 2011-06-30 Donaldson Company, Inc. Aerosol separator
US8512435B2 (en) 2004-11-05 2013-08-20 Donaldson Company, Inc. Filter medium and breather filter structure
US20140141677A1 (en) * 2012-11-21 2014-05-22 Kang Na Hsiung Enterprise Co., Ltd. Non-Woven Fabric and Method for Fabricating the Same
US20180001585A1 (en) * 2012-06-19 2018-01-04 Airbus Group Limited Filament for extrusion-based additive manufacturing system
USRE47737E1 (en) 2004-11-05 2019-11-26 Donaldson Company, Inc. Filter medium and structure
CN114867441A (zh) * 2019-12-27 2022-08-05 尤妮佳股份有限公司 无纺布和吸收性制品

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SE518130C2 (sv) * 1998-10-05 2002-08-27 Sca Hygiene Prod Ab Absorberande alster med termoplastiska fibrer i vätske överföringsskiktet
JP3404555B2 (ja) 1999-09-24 2003-05-12 チッソ株式会社 親水性繊維及び不織布、それらを用いた不織布加工品
DE60320496T2 (de) 2002-09-25 2009-05-07 Kao Corp. Verfahren zur Wiedergewinnung der Voluminosität eines Vlieses
DE10327026B4 (de) * 2003-06-16 2010-11-04 Hakle-Kimberly Deutschland Gmbh Airlaidverfahren mit verbessertem Durchsatz, Faservlies, Verwendung einer Viskosekurzfaser und Absorbierender Gegenstand
WO2005080658A1 (ja) 2004-02-23 2005-09-01 Teijin Fibers Limited エアレイド不織布用合成短繊維
WO2008053741A1 (fr) * 2006-10-30 2008-05-08 Kinsei Seishi Co., Ltd. Filtres à air à rigidité élevée
DE102014002060B4 (de) 2014-02-18 2018-01-18 Carl Freudenberg Kg Volumenvliesstoffe, Verwendungen davon und Verfahren zu ihrer Herstellung
EP3133196B1 (de) 2015-08-18 2020-10-14 Carl Freudenberg KG Volumenvliesstoff
JP7220020B2 (ja) 2017-01-06 2023-02-09 モリリン株式会社 混綿中綿

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1991019032A1 (en) * 1990-05-28 1991-12-12 Teijin Limited Novel cushioning structure and production thereof
JP3534193B2 (ja) * 1993-09-24 2004-06-07 東洋紡績株式会社 クッション構造体及びその製造法
JP3569972B2 (ja) * 1994-08-11 2004-09-29 チッソ株式会社 熱融着性複合繊維および熱融着不織布

Cited By (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020147433A1 (en) * 1998-03-12 2002-10-10 Mcosker Jocelyn Elaine Proton donating actives in absorbent articles
US20030018971A1 (en) * 2001-07-19 2003-01-23 Mckenna Thomas P. System and method for providing supplemental information related to a television program
AU2004264334B2 (en) * 2003-08-07 2009-07-16 The Procter & Gamble Company Latex bonded acquisition layer having pressure insensitive liquid handling properties
US20050043694A1 (en) * 2003-08-07 2005-02-24 The Procter & Gamble Company Diaper providing pressure insensitive liquid handling
US7767598B2 (en) * 2003-08-07 2010-08-03 The Procter & Gamble Company Diaper providing pressure insensitive liquid handling
EP1504741A1 (de) * 2003-08-07 2005-02-09 The Procter & Gamble Company Durch Latex verklebte Flüssigkeitsaufnahmeschicht mit druckunabhängigen Flüssigkeitshandhabungseigenschaften
US11504663B2 (en) 2004-11-05 2022-11-22 Donaldson Company, Inc. Filter medium and breather filter structure
US9795906B2 (en) 2004-11-05 2017-10-24 Donaldson Company, Inc. Filter medium and breather filter structure
USRE49097E1 (en) 2004-11-05 2022-06-07 Donaldson Company, Inc. Filter medium and structure
US10610813B2 (en) 2004-11-05 2020-04-07 Donaldson Company, Inc. Filter medium and breather filter structure
USRE47737E1 (en) 2004-11-05 2019-11-26 Donaldson Company, Inc. Filter medium and structure
US8512435B2 (en) 2004-11-05 2013-08-20 Donaldson Company, Inc. Filter medium and breather filter structure
US8641796B2 (en) 2004-11-05 2014-02-04 Donaldson Company, Inc. Filter medium and breather filter structure
US20060163152A1 (en) * 2005-01-21 2006-07-27 Ward Bennett C Porous composite materials comprising a plurality of bonded fiber component structures
US7888275B2 (en) 2005-01-21 2011-02-15 Filtrona Porous Technologies Corp. Porous composite materials comprising a plurality of bonded fiber component structures
US8177875B2 (en) 2005-02-04 2012-05-15 Donaldson Company, Inc. Aerosol separator; and method
US8460424B2 (en) 2005-02-04 2013-06-11 Donaldson Company, Inc. Aerosol separator; and method
US20080245037A1 (en) * 2005-02-04 2008-10-09 Robert Rogers Aerosol Separator; and Method
US8404014B2 (en) 2005-02-22 2013-03-26 Donaldson Company, Inc. Aerosol separator
US20110154790A1 (en) * 2005-02-22 2011-06-30 Donaldson Company, Inc. Aerosol separator
US20180001585A1 (en) * 2012-06-19 2018-01-04 Airbus Group Limited Filament for extrusion-based additive manufacturing system
US20140141677A1 (en) * 2012-11-21 2014-05-22 Kang Na Hsiung Enterprise Co., Ltd. Non-Woven Fabric and Method for Fabricating the Same
CN114867441A (zh) * 2019-12-27 2022-08-05 尤妮佳股份有限公司 无纺布和吸收性制品

Also Published As

Publication number Publication date
WO1997048846A1 (fr) 1997-12-24
AU3107797A (en) 1998-01-07
JP3219250B2 (ja) 2001-10-15
CA2256550A1 (en) 1997-12-24
EP0906981A1 (de) 1999-04-07
EP0906981A4 (de) 2004-11-17

Similar Documents

Publication Publication Date Title
US20020016120A1 (en) Non-woven fabric comprising staple fibers and an absorbent article using the same
CA2155315C (en) Stitchbonded articles and method of making same
EP0534562B1 (de) Biologisch abbaubarer Vliesstoff und Verfahren zu seiner Herstellung
EP1050612B1 (de) Bauschiger Vliesstoff, Herstellungsverfahren und saugfähige Artikel
US6588080B1 (en) Controlled loft and density nonwoven webs and method for producing
JP3852637B2 (ja) 短繊維不織布
US5516572A (en) Low rewet topsheet and disposable absorbent article
JP4308822B2 (ja) タフト化した繊維ウェブ
US6867156B1 (en) Materials having z-direction fibers and folds and method for producing same
US6635136B2 (en) Method for producing materials having z-direction fibers and folds
MXPA05001752A (es) Materiales no tejidos capaces de estirarse con controlada fuerza de retraccion y metodos para hacer los mismos.
JP3760599B2 (ja) 積層不織布及びそれを用いた吸収性物品
US6274237B1 (en) Potentially crimpable composite fiber and a non-woven fabric using the same
JP2002061060A (ja) 不織布及び不織布加工品
JP2800841B2 (ja) 不織布及びその製造方法並びに吸収性物品
WO2001074281A1 (en) Materials having z-direction fibers and folds and method for producing same
JPH101856A (ja) 熱接着性不織布
JPH1161614A (ja) 短繊維不織布
GB2387180A (en) A lofted non-woven material with z orientated fibres
JPH06245952A (ja) 体液吸収用物品
JPH1193054A (ja) 衛生材料
JPH07119010A (ja) 生分解性積層不織構造体
MXPA96004169A (en) Upper leaf of low rehumedment and above absorbent article
JPH0874162A (ja) 積層不織構造体

Legal Events

Date Code Title Description
AS Assignment

Owner name: CHISSO CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NAGANO, KOKI;HIRABAYASHI, SHIGERU;REEL/FRAME:009020/0386

Effective date: 19971121

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION