TWI830258B - 芯鞘纖維及其織物 - Google Patents
芯鞘纖維及其織物 Download PDFInfo
- Publication number
- TWI830258B TWI830258B TW111122756A TW111122756A TWI830258B TW I830258 B TWI830258 B TW I830258B TW 111122756 A TW111122756 A TW 111122756A TW 111122756 A TW111122756 A TW 111122756A TW I830258 B TWI830258 B TW I830258B
- Authority
- TW
- Taiwan
- Prior art keywords
- core
- sheath
- sheath fiber
- fiber
- sensitive material
- Prior art date
Abstract
一種芯鞘纖維，包含一芯部以及包覆於芯部外圍的一鞘部，該芯部以及該鞘部沿一軸方向延伸，其中，該芯部包含有一突出部，該突出部沿該軸方向的延伸並徑向的突出鞘部，該突出部裸露於該鞘部表面。
Description
關於一種纖維線，特別是一種芯鞘纖維。
市面上的人造紗、線、纖維中，依據應用所需的特性發展出具有各種功效，例如高延展性、高防水性、高熔點或是高強度不易斷裂之一纖維。然而，為使該纖維於同等外徑下同時擁有相對較輕與柔軟且能維持其一定強度，混和多種特性材料以構成該纖維成為相關產業中常見的手段。
然而，在追求該纖維產品物性品質的同時，具備有華麗外觀也極為重要的特徵。為使該纖維於市場上具備有較佳的競爭力，現行產業中多將以將該纖維於製作時添加染劑染色，然而此方法所製成的一纖維織物都僅能染出單一色系。也有先將該纖維織物製作完成後再進行染色之程序，但此方式不僅程序複雜，也容易有上色不均的問題，於長久使用下還會產生掉色或是退色的問題。有鑑於此，製作一種可以依據應用發展出具有各種功效並且同時具備美麗外觀之纖維為現行產業中急欲發展的目標。
為了製作一種可以依據應用發展出具有各種功效並且同時具備美麗外觀之纖維，本發明提供一種芯鞘纖維，包含一芯部以及包覆於芯部外圍的一鞘部，該芯部以及該鞘部沿一軸方向延伸，其中，該芯部包含有一突出部，該突出部沿該軸方向的延伸並徑向的突出鞘部，該突出部裸露於該鞘部表面。
其中，該芯部與該鞘部分別添加有不同顏色的一色料，該突出部與該鞘部表面呈現相異色彩。
進一步地，該芯部或該鞘部之成分可選擇熱塑性聚氨酯、熱塑性聚酯彈性體、聚烯系彈性體、熱塑性硫化橡膠、聚苯乙烯系彈性體、聚乙烯、聚丙烯、聚對苯二甲酸丁二酯、聚對苯二甲酸乙二酯、聚對苯二甲酸乙二醇酯、聚烯烴系、聚醯胺、聚苯乙烯、聚氯乙烯、乙烯／醋酸乙烯酯共聚物或上述成分之混合物。
進一步地，該芯部或是該鞘部可選擇的添加有一發泡劑。
進一步地，該芯部或該鞘部可選擇的添加有一溫感材料，該溫感材料可選自由玉石、礦石、氮化硼(BN)、氮化鋁(AlN)、鈦(Ti)、薄荷腦、木醣醇、奈米銀、奈米銅、奈米氧化鋅、雲母、娟雲母或是上述之混合所製成具備有涼感特性之粉體。
進一步地，該芯部或該鞘部可選擇的添加有一溫感材料，該溫感材料可選自由天然礦石、陶瓷粉末、三氧化二鋁(Al2O3)、二氧化矽(SiO2) 、遠紅外線粉體、石墨烯、椰碳、竹碳、奈米碳管或是上述之混合所製成具備有保溫及發熱特性之粉體。
本發明更提供一種芯鞘纖維織物，其由一芯鞘纖維編織而成，該芯鞘纖維包含一芯部以及包覆於芯部外圍的一鞘部，該芯部以及該鞘部沿一軸方向延伸，其中，該芯部包含有一突出部，該突出部沿該軸方向的延伸並徑向的突出鞘部，該突出部裸露於該鞘部表面。
其中，該芯部與該鞘部分別添加有不同顏色的一色料，該突出部與該鞘部表面呈現相異色彩，其中該織物依據一編織手段呈現隨機的相異顏色花紋。
本發明該芯鞘纖維可以依據所需選擇不同物理性質之材料組合，並且添加其他具備功能性之功能粉體以產生多種組合以及功效，加上製作時色料得選用，使得該芯鞘纖維不僅可以具備美麗外觀，還可以減少製程步驟，更可以避免長久使用掉色或是退色的問題產生。
如圖1a至圖1c，其為本發明芯鞘纖維較佳實施例，該芯鞘纖維由一芯部10以及一鞘部20沿一軸方向所構成，且該芯部10由該鞘部20包覆。其中，該芯部10包含有一突出部11，該突出部11徑向的突出鞘部20，且該突出部11沿該軸方向的延伸並裸露於該鞘部20表面。
該芯部10以及該鞘部20所構成之截面並不限定，只要是該芯部10所包含的該突出部11，沿該軸方向的延伸並且徑向突出及裸露於該鞘部20之樣態接可涵蓋於本發明。如圖1a本發明第一較佳實施例中，該鞘部20所構成之截面為一圓形，而該芯部10所構成之截面則為一三角形，其中，該截面中該三角形所構成的三個角皆為該突出部11，該突出部11徑向的突出鞘部20，且該突出部11沿該軸方向的延伸並裸露於該鞘部20表面。
又例如圖1b本發明第二較佳實施例中，該鞘部20所構成之截面為一圓形，而該芯部10所構成之截面同樣為該三角形，與第一較佳實施例不同之處在於，該截面中該三角形所構成的三個角中，僅有其中二個角為該突出部11。又或是如圖1c本發明第二較佳實施例中，該鞘部20所構成之截面為一圓形，而該芯部10所構成之截面則為一方形，其中截面該方形所構成的四個角皆為該突出部11突出該鞘部20。
接著請參考圖2，該芯部10與該鞘部20可以依據所需分別添加有不同顏色之色料，如此裸露於該鞘部20表面之該突出部11便可以使該芯鞘纖維織表面部分呈現相異色彩，在進一步的將該芯鞘纖維依據需求以及編織方法製作成一芯鞘纖維織物時，便可以使得該芯鞘纖維織物呈現隨機的相異顏色之花紋，達到類似段染紗於編織時所產生之紋路
該芯部10以及該鞘部20之成分可選擇熱塑性聚氨酯、熱塑性聚酯彈性體、聚烯系彈性體、熱塑性硫化橡膠、聚苯乙烯系彈性體、聚乙烯、聚丙烯、聚對苯二甲酸丁二酯、聚對苯二甲酸乙二酯、聚對苯二甲酸乙二醇酯、聚烯烴系、聚醯胺、聚苯乙烯、聚氯乙烯、乙烯／醋酸乙烯酯共聚物或上述成分之混合物，其中，該芯部10以及該鞘部20可選擇相同或不同之成分或組合成分。
舉例而言，該芯部10以及該鞘部20可為相異材質，該芯部10選用以機械強度相對較佳的材料如尼龍，而該鞘部21則選擇熱塑性聚氨酯，如此便可以賦予該芯鞘纖維具備良好的結構強度與輕量化的構造。
其中，該芯部10或是該鞘部20可選擇的添加有一功能粉體。例如，該芯部10可選用熱塑性聚氨酯，而該鞘部20則是添加有抗紫外線材料的熱塑性聚氨酯，使得該芯鞘纖維成為表面具有較佳抗老化之表皮層效果，不僅達到維持一定機械強度，更可以達到耐用的效果。
又例如，該功能粉體可為一溫感材料，使得該芯鞘纖維具有溫度調節效果。具體而言，該溫感材料可選自由玉石、礦石、氮化硼(BN)、氮化鋁(AlN)、鈦(Ti)、薄荷腦、木醣醇、奈米銀、奈米銅、奈米氧化鋅、雲母、娟雲母或是上述之混合所製成具備有涼感特性之粉體。該溫感材料也可選自天然礦石、陶瓷粉末、三氧化二鋁(Al2O3)、二氧化矽(SiO2) 、遠紅外線粉體、石墨烯、椰碳、竹碳、奈米碳管或是上述之混合所製成具備有保溫及發熱特性之粉體。
其中，該芯部10或是該鞘部20可選擇的添加有一發泡劑。具體而言，若是於該芯部10添加有該發泡劑，可以使得該芯鞘纖維具備有徑向的壓縮彈力，可以產生緩衝支撐力以及輕量化的效果，同時的該芯鞘纖維之表面因有該突出部11，使得該芯鞘纖維具有特殊的觸覺感受。若是於該鞘部20添加有該發泡劑時，可以使得該芯鞘纖維整體產生柔軟的觸感。
所述該發泡劑的種類或發泡方式並不限定，可利用化學性發泡或物理性發泡的方式使該芯部10或是該鞘部20產生發泡反應。其中，化學性發泡的該發泡劑成分可選擇偶氮類、(2，2'-偶氮二異丁腈、偶氮二甲酸二異丙酯、偶氮二甲酸鋇、偶氮二甲酸二乙酯、偶氮胺基苯)、 磺醯肼類(苯磺醯肼、對甲苯磺醯肼、4，4-氧化雙苯磺醯肼、3，3-二磺醯肼二苯碸、1，3-苯二磺醯肼 、對甲苯磺醯氨基脲、 4，4-氧代雙（苯磺醯氨基脲）)、三肼基三嗪或上述成分之混合物。物理性發泡的該發泡劑可選擇由一高分子聚合物所製成的多個中空微球，該高分子聚合物可選自於聚乙烯、聚丙烯、聚苯乙烯、聚已內酯、聚乳酸、聚甘醇酸、聚丙烯酸、聚甲基丙烯酸甲脂等或上述成分之混合物，該中空微球內含有一氣體，該氣體可選擇烴類、氫化氟烷烴(HFCs)、二氧化碳或氮氣等。
該芯鞘纖維製作方法為：（1）分別將該芯部10及該鞘部20之組成份攪拌均勻，並且依據所需添加色料及/或功能粉體及/或發泡劑；（2）將配置好的該芯部10及該鞘部20經由一模具共擠出/押出，此時該突出部11於該模具成形並於共擠出/押出後突出於該鞘部20，完成該芯鞘纖維。
本發明該芯鞘纖維可以依據所需選擇不同物理性質之材料組合，並且添加其他具備功能性之功能粉體以產生多種組合以及功效，加上製作時色料得選用，使得該芯鞘纖維不僅可以具備美麗外觀，還可以減少製程步驟，更可以避免長久使用掉色或是退色的問題產生。
10芯部
11突出部
20鞘部
圖1a為本發明第一較佳實施例徑向結構示意圖
圖1b為本發明第二較佳實施例徑向結構示意圖
圖1c為本發明第三較佳實施例徑向結構示意圖
圖2為本發明較佳實施例外觀示意圖
10芯部
11突出部
20鞘部
Claims (10)
- 一種芯鞘纖維，包含一芯部以及包覆於芯部外圍的一鞘部，該芯部以及該鞘部沿一軸方向延伸，其中，該芯部包含有一突出部，該突出部沿該軸方向的延伸並徑向的突出鞘部，該突出部裸露於該鞘部表面。
- 如請求項1所述之芯鞘纖維，該芯部與該鞘部分別添加有不同顏色的一色料，該突出部與該鞘部表面呈現相異色彩。
- 如請求項1或2所述之芯鞘纖維，該芯部或該鞘部之成分可選擇熱塑性聚氨酯、熱塑性聚酯彈性體、聚烯系彈性體、熱塑性硫化橡膠、聚苯乙烯系彈性體、聚乙烯、聚丙烯、聚對苯二甲酸丁二酯、聚對苯二甲酸乙二酯、聚對苯二甲酸乙二醇酯、聚烯烴系、聚醯胺、聚苯乙烯、聚氯乙烯、乙烯／醋酸乙烯酯共聚物或上述成分之混合物。
- 如請求項1或2所述之芯鞘纖維，該芯部或是該鞘部可選擇的添加有一發泡劑。
- 如請求項1或2所述之芯鞘纖維，該芯部或該鞘部可選擇的添加有一溫感材料，該溫感材料可選自由玉石、礦石、氮化硼(BN)、氮化鋁(AlN)、鈦(Ti)、薄荷腦、木醣醇、奈米銀、奈米銅、奈米氧化鋅、雲母、娟雲母或是上述之混合所製成具備有涼感特性之粉體。
- 如請求項1或2所述之芯鞘纖維，該芯部或該鞘部可選擇的添加有一溫感材料，該溫感材料可選自由天然礦石、陶瓷粉末、三氧化二鋁(Al2O3)、二氧化矽(SiO2) 、遠紅外線粉體、石墨烯、椰碳、竹碳、奈米碳管或是上述之混合所製成具備有保溫及發熱特性之粉體。
- 一種芯鞘纖維織物，其由一芯鞘纖維編織而成，該芯鞘纖維包含一芯部以及包覆於芯部外圍的一鞘部，該芯部以及該鞘部沿一軸方向延伸，其中，該芯部包含有一突出部，該突出部沿該軸方向的延伸並徑向的突出鞘部，該突出部裸露於該鞘部表面。
- 如請求項7所述之芯鞘纖維織物，該芯部與該鞘部分別添加有不同顏色的一色料，該突出部與該鞘部表面呈現相異色彩，其中該芯鞘纖維織物依據一編織手段呈現隨機的相異顏色花紋。
- 如請求項8所述之芯鞘纖維織物，該芯部或該鞘部之成分可選擇熱塑性聚氨酯、熱塑性聚酯彈性體、聚烯系彈性體、熱塑性硫化橡膠、聚苯乙烯系彈性體、聚乙烯、聚丙烯、聚對苯二甲酸丁二酯、聚對苯二甲酸乙二酯、聚對苯二甲酸乙二醇酯、聚烯烴系、聚醯胺、聚苯乙烯、聚氯乙烯、乙烯／醋酸乙烯酯共聚物或上述成分之混合物。
- 如請求項7所述之芯鞘纖維織物，該芯部或是該鞘部可選擇的添加有一發泡劑或是一溫感材料。