TWI577753B - 水性塗料 - Google Patents
水性塗料 Download PDFInfo
- Publication number
- TWI577753B TWI577753B TW105106759A TW105106759A TWI577753B TW I577753 B TWI577753 B TW I577753B TW 105106759 A TW105106759 A TW 105106759A TW 105106759 A TW105106759 A TW 105106759A TW I577753 B TWI577753 B TW I577753B
- Authority
- TW
- Taiwan
- Prior art keywords
- methacrylate
- acrylate
- azobis
- group
- aqueous coating
- Prior art date
Description
本發明係關於一種水性塗料,特別關於一種具有高固含量、高耐水性及低起泡性之水性塗料。
近年來,由於人們對環保的重視,世界各國對塗料中揮發性有機溶劑(VOC)的含量嚴格控制,促使塗料的研究從溶劑型塗料逐漸轉換成水性塗料。與溶劑型塗料相比,水性塗料具有不含VOC或VOC含量較低的優點,對環境的傷害較低,而且因為使用水來當溶劑,水性塗料也具有不易燃及無特別防火要求等優點。然而,水性塗料在塗膜的乾燥速率、耐水性及耐候性等方面的表現較差,此外,傳統上以一般型乳化劑所製備的水性塗料,在運送過程中,會因為搖晃而容易起泡,因此需要再多一道程序來消泡。
眾所皆知,水性塗料中顯現特性的主要物質是水性聚合物,其為影響塗料性能的首要因素。因此,為了克服上述水性塗料性質較差的問題,改善該水性聚合物的性質便成為水性塗料的研究目標。依據中國第103906768號專利案所揭露之內容,係使用反應性乳化劑,藉以在乳化聚合步驟中,由該反應性乳化劑提供乳化劑的機能,而在乳化聚合步驟之後,該反應性乳化劑則會被結合到水性聚合物的骨架中。如此便能減少乳化劑在塗膜中的遷移,降低塗膜的吸水率,而提升水性塗料的耐水性。
此外,中國第102532404號專利案,除了使用上述反應性乳化劑的技術外,更利用具有烷氧基之矽烷來進行共聚合反應,對水性塗料
的水性聚合物進行改質,使得該水性聚合物塗膜的表面形成一種疏水性結構,從而提升水性塗料的耐水性。可惜的是,該專利所使用的反應型乳化劑雖然具有聚合作用,但乳化作用很差,其聚合前的乳化作用仍然是依賴一般型乳化劑來完成,以致該專利所製成的水性塗料,仍然因該些一般型乳化劑在塗膜中遷移,導致該水性塗料,即使減少了一般乳化劑在塗膜中遷移,以及具有疏水性結構,然而其耐水性仍然無法滿足需求。此外,由秦鋼等人(環保型木器塗料用丙烯酸乳液,博士學位論文,武漢理工大學,2011年5月30日)的研究可知,該專利所使用的具有烷氧基之矽烷,若不添加水解抑制劑(二乙二醇丁醚)的話,該具有烷氧基之矽烷會在乳化聚合時,因為水解而生成許多團聚物,使所形成的水性塗料的固含量偏低。
綜上所述,習知的水性塗料具有耐水性差、固含量偏低及容易起泡的問題。
為了解決上述習知水性塗料的技術問題,本發明提供一種水性塗料,具有高固含量、高耐水性及低起泡性。
本發明提供一種水性塗料,包含0.01~5wt%之一起始劑、0.01~5wt%之一制酸劑、15~60wt%之一丙烯酸單體、0.1~10wt%之一甲基丙烯醯氧丙基聚二甲基矽氧烷、0.1~5wt%之一丙烯基苯酚乙基苯聚乙二醇硫酸銨及35~70wt%之水,經乳化聚合反應後形成。藉此,該水性塗料具有高固含量、高耐水性及低起泡性之功效。
其中,該起始劑係選自由過硫酸銨、過硫酸鉀、偶氮二咪唑啉基丙烷二鹽酸鹽、2,2’-偶氮雙[2-(2-咪唑并啉-2-基)丙烷]二硫酸二水合物、偶氮二異丁基脒鹽酸鹽、2,2’-偶氮二[N-(2-羧乙基)-2-甲基丙脒]四水合物、2,2’-偶氮雙[2-(2-咪唑并啉-2-基)丙烷]、2,2’-偶氮二[2-甲基-N-(2-羥乙基)丙醯胺及4,4’-偶氮雙(4-氰基纈草酸)所組成之群組。藉此,
引發乳化聚合反應,並且讓該乳化聚合反應能夠穩定地進行。
其中,該制酸劑可選自由碳酸氫鈉、碳酸鈉、碳酸鈣、氫氧化鋁及氫氧化鎂所組成之群組。藉此,使乳化聚合反應能夠穩定地進行,減少團聚物的產生,讓該水性塗料具有較高的固含量。
其中,該丙烯酸單體可選自由丙烯酸酯類單體、甲基丙烯酸酯類單體、丙烯腈、甲基丙烯腈、丙烯醯胺、甲基丙烯醯胺、丙烯酸、甲基丙烯酸及其組合所組成之群組,其中,該丙烯酸酯類單體包括丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、丙烯酸異丁酯、丙烯酸叔丁酯、丙烯酸戊酯、丙烯酸己酯、丙烯酸庚酯、丙烯酸辛酯、丙烯酸-2-乙基己酯、丙烯酸壬酯、丙烯酸癸酯、丙烯酸十一烷基酯、丙烯酸月桂酯、丙烯酸十三烷基酯與丙烯酸硬脂酯等;該甲基丙烯酸酯類單體,包括甲基丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸丙酯、甲基丙烯酸丁酯、甲基丙烯酸異丁酯、甲基丙烯酸叔丁酯、甲基丙烯酸戊酯、甲基丙烯酸己酯、甲基丙烯酸環己酯、甲基丙烯酸庚酯、甲基丙烯酸辛酯、甲基丙烯酸-2-乙基己酯、甲基丙烯酸壬酯、甲基丙烯酸癸酯、甲基丙烯酸十一烷基酯、甲基丙烯酸月桂酯、甲基丙烯酸十三烷基酯、甲基丙烯酸硬脂酯與甲基丙烯酸縮水甘油酯等。藉此,透過乳化聚合反應,生成水性聚合物,使該水性塗料具有高耐水性之特性。
本發明藉由適當比例的該甲基丙烯醯氧丙基聚二甲基矽氧烷與該丙烯基苯酚乙基苯聚乙二醇硫酸銨,提高該水性塗料之疏水性、耐水性,並且降低團聚物之產生,而增加該塗料之固含量與穩定性,進而增加產能、降低能耗,還不需要額外處理起泡的問題。
因此,本發明之水性塗料,具有低團聚物,高穩定性,高固含量,高疏水性,高耐水性,以及降低塗料起泡性等優點。
若將此水性塗料應用於高樓外牆,因其高疏水性,可藉由大
自然雨水的沖刷,帶走灰塵及髒汙,不需額外的清洗人力與水,而達成節能的效果。
第1圖:本發明之甲基丙烯醯氧丙基聚二甲基矽氧烷之結構式。
第2圖:市售丙烯酸乳液與本發明之水性塗料,其薄膜之水接觸角比較圖。
第3圖:不同乳化劑之耐水性測試結果。
為讓本發明之上述及其他目的、特徵及優點能更明顯易懂,下文特舉本發明之較佳實施例,並配合所附圖式,作詳細說明如下:本發明之水性塗料,包含0.01~5wt%之一起始劑、0.01~5wt%之一制酸劑、15~60wt%之一丙烯酸單體、0.1~10wt%之一甲基丙烯醯氧丙基聚二甲基矽氧烷(商品名稱為MCR-M22,由捷利斯特(Gelest)公司製造)、0.1~5wt%之一丙烯基苯酚乙基苯聚乙二醇硫酸銨(商品名稱為AR-10,由晉一化工股份有限公司提供)及35~70wt%之水,經乳化聚合反應後形成。
詳言之,本發明係將該起始劑、該制酸劑及部分去離子水混合,配製成起始劑溶液;將該丙烯酸單體、該甲基丙烯醯氧丙基聚二甲基矽氧烷、該丙烯基苯酚乙基苯聚乙二醇硫酸銨與剩餘之去離子水混合,然後進行乳化以形成一預乳液,並先將該預乳液之一部分與該起始劑溶液混合,升溫至80℃,等候反應一段時間後,再以一定速率滴加剩餘之該預乳液,在滴加完畢後,保持反應溫度在90℃,反應1小時,然後降溫、冷卻。
該起始劑為任何能引發乳化聚合反應之化合物,本發明不特
別加以限制,舉例而言,該起始劑可選自由過硫酸銨(Ammonium persulfate,APS)、過硫酸鉀(Potassium persulfate,KPS)、偶氮二咪唑啉基丙烷二鹽酸鹽(2,2’-Azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride,VA-044,由和光純藥工業株式會社製造)、2,2’-偶氮雙[2-(2-咪唑并啉-2-基)丙烷]二硫酸二水合物(2,2’-Azobis[2-(2-imidazolin-2-yl)propane]disulfate dihydrate,VA-046B,由和光純藥工業株式會社製造)、偶氮二異丁基脒鹽酸鹽(2,2’-Azobis(2-methylpropionamidine)dihydrochloride,VA-50,由和光純藥工業株式會社製造)、2,2’-偶氮二[N-(2-羧乙基)-2-甲基丙脒]四水合物(2,2’-Azobis(N-(2-carboxyethyl)2-methylpropionamidine)tetrahydrate,VA-057,由和光純藥工業株式會社製造)、2,2’-偶氮雙[2-(2-咪唑并啉-2-基)丙烷](2,2’-Azobis[2-(2-imidazolin-2-yl)propane],VA-061,由和光純藥工業株式會社製造)、2,2’-偶氮二[2-甲基-N-(2-羥乙基)丙醯胺(2,2’-Azobis[2-methyl-N-(2-hydroxyethyl)propionamide],VA-086,由和光純藥工業株式會社製造)及4,4’-偶氮雙(4-氰基纈草酸)(4,4’-Azobis(4-cyanovaleric acid),VA-501,由和光純藥工業株式會社製造)所組成之群組。而且該起始劑之添加量可為0.01~5wt%,較佳為0.48~4wt%,最佳為1~3wt%。
該制酸劑為本發明所屬技術領域中任何習用之弱鹼,不特別加以限制,舉例而言,可做為該制酸劑之弱鹼包括碳酸氫鈉、碳酸氫鉀、碳酸鈉、碳酸鈣等。該制酸劑之添加量為0.01~5wt%。藉此,維持且穩定本發明之反應混合物的酸鹼度,使乳化聚合反應能夠在該反應混合物中順利進行,減少團聚物的產生,形成高固含量之水性塗料。
該丙烯酸單體係指具有可聚合不飽和雙鍵的單體,經乳化程序後,能在起始劑的作用下,進行乳化聚合反應,形成本發明之水性塗料。舉例而言,該丙烯酸單體可選自由丙烯酸酯類單體、甲基丙烯酸酯類單體、
丙烯腈、甲基丙烯腈、丙烯醯胺、甲基丙烯醯胺、丙烯酸、甲基丙烯酸及其組合所組成之群組,其添加量為15~60wt%,較佳為20~50wt%,最佳為25~40wt%,其中,該丙烯酸酯類單體係指丙烯酸與各種醇類所形成的丙烯酸酯,只要能夠形成本發明之水性塗料中所包含之水性聚合物,該丙烯酸酯類單體沒有特別限制,舉例而言,可用來當作該丙烯酸酯類單體的實例,包括丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、丙烯酸異丁酯、丙烯酸叔丁酯、丙烯酸戊酯、丙烯酸己酯、丙烯酸庚酯、丙烯酸辛酯、丙烯酸-2-乙基己酯、丙烯酸壬酯、丙烯酸癸酯、丙烯酸十一烷基酯、丙烯酸月桂酯、丙烯酸十三烷基酯及丙烯酸硬脂酯等;該甲基丙烯酸酯類單體係指甲基丙烯酸與各種醇類所形成的甲基丙烯酸酯,只要能夠形成本發明之水性塗料中所包含之水性聚合物,該甲基丙烯酸酯類單體沒有特別限制,舉例而言,可用來當作該甲基丙烯酸酯類單體的實例,包括甲基丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸丙酯、甲基丙烯酸丁酯、甲基丙烯酸異丁酯、甲基丙烯酸叔丁酯、甲基丙烯酸戊酯、甲基丙烯酸己酯、甲基丙烯酸環己酯、甲基丙烯酸庚酯、甲基丙烯酸辛酯、甲基丙烯酸-2-乙基己酯、甲基丙烯酸壬酯、甲基丙烯酸癸酯、甲基丙烯酸十一烷基酯、甲基丙烯酸月桂酯、甲基丙烯酸十三烷基酯、甲基丙烯酸硬脂酯與甲基丙烯酸縮水甘油酯等。藉此,透過乳化聚合反應,生成水性聚合物。
該甲基丙烯醯氧丙基聚二甲基矽氧烷(Monomethacryloxypropyl Terminated Polydimethylsiloxane,MCR-M22,由捷利斯特(Gelest)公司製造)係一種無烷氧基矽烷單體,具有第1圖之結構式,其中n為125~135,其添加量為0.1~10wt%,較佳為2~8wt%,最佳為4~6wt%。由第1圖可知,該甲基丙烯醯氧丙基聚二甲基矽氧烷並無烷氧基的取代基,因此,不易在乳化聚合反應的過程中水解,而不會發生如習知技術中不需要的聚合反應,大幅降低團聚物的形成,使本發明之
水性塗料具有高固含量,提高穩定性,而且該甲基丙烯醯氧丙基聚二甲基矽氧烷與該丙烯酸單體透過乳化聚合反應,生成具有疏水性結構的水性聚合物,進一步提高本發明水性塗料之耐水性。
該丙烯基苯酚乙基苯聚乙二醇硫酸銨(商品名稱為AR-10,由晉一化工股份有限公司提供),係一種反應型乳化劑,其添加量為0.1~5wt%,較佳為1~4wt%,最佳為2~3wt%。利用該丙烯基苯酚乙基苯聚乙二醇硫酸銨的乳化作用,讓乳化程序能夠穩定地進行,而得到穩定的乳液,還能夠在乳化聚合反應之後,進入水性聚合物的結構中,成為水性聚合物結構的一部分,提升本發明水性塗料之耐水性,更能夠使本發明之水性塗料在運送過程中不易產生泡沫,也可以在泡沫產生之後,讓泡沫在較短的時間內自行消除,而具有低起泡性的特性。
為證實本發明之水性塗料確實具有適當高固含量、高耐水性及低起泡性,遂進行下述水性塗料的製備與性質量測實驗:
A.水性塗料的製備
水性塗料1~14係依下列第1表之配方,以及利用下列步驟製備:將過硫酸銨、碳酸氫鈉及去離子水A混合,配製成起始劑溶液;將乳化劑、去離子水B、甲基丙烯酸甲酯(MMA)、丙烯酸-2-乙基己酯(2-EHA)、MCR-M22,然後進行攪拌分散以形成一預乳液,並將該預乳液分為預乳液A、預乳液B兩份;將該預乳液A與該起始劑溶液混合,升溫至80℃,反應一段時間後,再以一定速率滴加該預乳液B,該預乳液B在滴加完畢後,保持反應溫度在90℃,反應1小時,然後降溫至40℃以下,以氨水調整乳液之pH值至6~7,過濾、包裝。
B.水滴角實驗
將市售丙烯酸乳液(商品名稱為WAC-1911,由安鋒實業股份有限公司製造)與水性塗料1~8以下列步驟製成薄膜:將5g該市售丙烯酸乳液或該些水性塗料1~8置於培養皿中,常溫下靜置乾燥24小時,取出薄膜。製成薄膜後以水滴角量測儀器(廠牌為GBX,型號為PX610)來測量薄膜之水接觸角,測量結果如第2圖所示。
由第2圖可知,市售丙烯酸乳液,在成膜後之水接觸角約為73.8°;水性塗料2~8,在成膜後之水接觸角,在94.2°~107.9°的範圍,
經由上述的量測結果,可以看出本發明之水性塗料(2~6)呈現出優良的疏水性。至於水性塗料7~8在成膜後之水接觸角約在107.9°附近,也具有優良的疏水性,然而水接觸角並沒有隨著MCR-M22的含量增加而增加,基於生產成本的考量,MCR-M22的含量在超過10%之後,並不適合用來製造水性塗料。
C.耐水性實驗
將市售丙烯酸乳液、使用市售乳化劑(商品名稱為SDS,由希格瑪-艾爾德利其(SIGMA-ALDRICH)公司製造)所製得之水性塗料14與使用AR-10乳化劑所製得之本發明之水性塗料11進行試驗,試驗方法如下:
1.準備一金屬試片,以50μm塗膜棒將乳液或水性塗料塗佈在該試片表面。
2.以60℃乾燥一晚,取出冷卻至室溫。
3.將含乳液或水性塗料之金屬試片浸泡於25℃純水中靜置,每12小時取出試片,以肉眼觀察表面狀態。
當金屬試片表面出現皺紋時,結束實驗。
試驗結果如第3圖所示。使用市售丙烯酸乳液所製成的試片,在第12、24小時的表面觀察結果分別如第3a、3b圖所示;使用水性塗料14所製成的試片,在第12小時的表面觀察結果如第3c圖所示;使用本發明之水性塗料11所製成的試片,在第12、24、36、48、60、120小時的表面觀察結果分別如第3d、3e、3f、3g、3h、3i圖所示。
由第3a、3b圖可看出,使用市售乳液的試片在第24小時時出現皺紋;由第3c圖可看出,使用水性塗料14(使用SDS乳化劑)的試片在第12小時時出現皺紋;由第3i圖可看出,使用本發明之水性塗料11的試片在第120小時時,表面仍然沒有任何皺紋,故本發明之水性塗料具
有優良之耐水性。
D.起泡性實驗
本發明評估各種乳液與水性塗料的起泡性,係以下列測試方法進行:取一支10cm試管,加入5cm高的乳液或水性塗料,蓋住試管管口,手動翻轉10次,在室溫下靜置,以肉眼觀察泡沫完全消失時,所需要耗費的時間。
市售乳液、使用SDS乳化劑所製得之水性塗料與使用AR-10乳化劑所製得之本發明之水性塗料經過上述的測試,測試結果如第2表所示。
由本實驗結果可知,本發明含AR-10乳化劑之水性塗料9~13具有不易起泡的效果,因此當本發明之水性塗料9~13在運送過程中,不易因搖晃而產生的泡沫,即使泡沫產生之後,也能夠在短時間內,自行消除,因而不需要消泡的程序,反觀市售乳液與其他的乳化劑所製成的水性塗料14,泡沫消失的時間相當長,因此,需要額外去處理起泡的問題,而需要再多一道消泡的程序。
E.穩定性實驗
本發明評估各種水性塗料的穩定性,係以下列測試方法進行:比較反應前後,反應容器之質量差,可以得到附著於器壁之團聚物之質量;以200目篩網過濾水性塗料,可以得到存在於水性塗料中團聚物之
質量。將附著於器壁之團聚物之質量與存在於水性塗料中團聚物之質量相加,可以得到總團聚物重,再以下列算式計算,可以得到團聚物產生率(亦稱為凝膠率):團聚物產生率=總團聚物重÷投入單體總重×100%。
經過上述測試,整理各種水性塗料之穩定性,可得第3表之結果。
由第2表中本發明性塗料9~13之凝膠率與秦鋼等人(表2-11,p.24,環保型木器塗料用丙烯酸乳液,博士學位論文,武漢理工大學,2011年5月30日)之水性塗料的凝膠率(10.6%)相比,在不添加水解抑制劑(二乙二醇丁醚)的條件下,本發明水性塗料9~13,具有優良之穩定性。
F.固含量實驗
實驗方法如下:取2g乳液,滴入3滴5%對苯二酚水溶液,於60℃烘箱中靜置一夜,以除去大部分的水分;然後將其置於60℃真空乾燥箱中,直到恆重,以下列算式計算固含量:固含量=殘存樣品重÷取樣總重×100%。
本發明之水性塗料2~14,其固含量約為50%。習知的水性塗料,皆以低固含量的方式來製備,由一般文獻(Xiuxia Wang等人,Synthesis of water-soluble hyperbranched polymer and its application in acrylic latex,EUROPEAN POLYMER JOURNAL 42(2006),286-291;R.Seda T1 l1等人,Synthesis and characterization of pure poly(acrylate)latexes,
Progress in Organic Coatings 52(2005)144-150;Xuejun Cui等人,Emulsifier-free coreshell polyacrylate latex nanoparticles containing fluorine and silicon in shell,Polymer 48(2007)7241-7248)的記載可知,在該些文獻中所揭露的水性塗料,其固含量皆小於45%。
因此,本發明之水性塗料具有較高之固含量,可在運輸時,節省運送的成本。
綜上所述,本發明藉由適當比例的該甲基丙烯醯氧丙基聚二甲基矽氧烷與該丙烯基苯酚乙基苯聚乙二醇硫酸銨,提高該水性塗料之疏水性、耐水性,並且降低團聚物之產生,而增加該塗料之固含量與穩定性。
藉由生產本發明之水性塗料能進而增加產能、降低能耗,還不需要額外處理起泡的問題。
若將此塗料應用於高樓外牆,因其高疏水性,可藉由大自然雨水的沖刷,帶走灰塵及髒汙,不需額外的清洗人力與水,而達成節能的效果。
雖然本發明已利用上述較佳實施例揭示,然其並非用以限定本發明,任何熟習此技藝者在不脫離本發明之精神和範圍之內,相對上述實施例進行各種更動與修改仍屬本發明所保護之技術範疇,因此本發明之保護範圍當視後附之申請專利範圍所界定者為準。
Claims (6)
- 一種水性塗料,包含0.01~5wt%之一起始劑、0.01~5wt%之一制酸劑、15~60wt%之一丙烯酸單體、0.1~10wt%之一甲基丙烯醯氧丙基聚二甲基矽氧烷、0.1~5wt%之一丙烯基苯酚乙基苯聚乙二醇硫酸銨及35~70wt%之水,經乳化聚合反應後形成。
- 如申請專利範圍第1項所述之水性塗料,其中,該起始劑係選自由過硫酸銨(Ammonium persulfate)、過硫酸鉀(Potassium persulfate)、偶氮二咪唑啉基丙烷二鹽酸鹽(2,2’-Azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride)、2,2’-偶氮双[2-(2-咪唑并啉-2-基)丙烷]二硫酸二水合物(2,2’-Azobis[2-(2-imidazolin-2-yl)propane]disulfate dihydrate)、偶氮二異丁基脒鹽酸鹽(2,2’-Azobis(2-methylpropionamidine)dihydrochloride)、2,2’-偶氮二[N-(2-羧乙基)-2-甲基丙脒]四水合物(2,2’-Azobis(N-(2-carboxyethyl)2-methylpropionamidine)tetrahydrate)、2,2’-偶氮雙[2-(2-咪唑并啉-2-基)丙烷](2,2’-Azobis[2-(2-imidazolin-2-yl)propane])、2,2’-偶氮二[2-甲基-N-(2-羥乙基)丙醯胺(2,2’-Azobis[2-methyl-N-(2-hydroxyethyl)propionamide])及4,4’-偶氮雙(4-氰基纈草酸)(4,4’-Azobis(4-cyanovaleric acid))所組成之群組。
- 如申請專利範圍第1或2項所述之水性塗料,其中,該制酸劑係選自由碳酸氫鈉、碳酸氫鉀、碳酸鈉及碳酸鈣所組成之群組。
- 如申請專利範圍第1或2項所述之水性塗料,其中,該丙烯酸單體係選自由丙烯酸酯類單體、甲基丙烯酸酯類單體、丙烯腈、甲基丙烯腈、丙烯醯胺、甲基丙烯醯胺、丙烯酸、甲基丙烯酸及其組合所組成之群組。
- 如申請專利範圍第4項所述之水性塗料,其中,該丙烯酸酯類單體係選自由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、丙烯酸異丁酯、丙烯酸叔丁酯、丙烯酸戊酯、丙烯酸己酯、丙烯酸庚酯、丙烯酸辛酯、丙烯酸-2-乙基己酯、丙烯酸壬酯、丙烯酸癸酯、丙烯酸十一烷基酯、丙烯酸月桂酯、丙烯酸十三烷基酯及丙烯酸硬脂酯所組成之群組。
- 如申請專利範圍第4項所述之水性塗料,其中,該甲基丙烯酸酯類單體係選自由甲基丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸丙酯、甲基丙烯酸丁酯、甲基丙烯酸異丁酯、甲基丙烯酸叔丁酯、甲基丙烯酸戊酯、甲基丙烯酸己酯、甲基丙烯酸環己酯、甲基丙烯酸庚酯、甲基丙烯酸辛酯、甲基丙烯酸-2-乙基己酯、甲基丙烯酸壬酯、甲基丙烯酸癸酯、甲基丙烯酸十一烷基酯、甲基丙烯酸月桂酯、甲基丙烯酸十三烷基酯、甲基丙烯酸硬脂酯及甲基丙烯酸縮水甘油酯所組成之群組。