TW202344622A - 具有著色後處理的二氧化鈦顏料 - Google Patents
具有著色後處理的二氧化鈦顏料 Download PDFInfo
- Publication number
- TW202344622A TW202344622A TW112104449A TW112104449A TW202344622A TW 202344622 A TW202344622 A TW 202344622A TW 112104449 A TW112104449 A TW 112104449A TW 112104449 A TW112104449 A TW 112104449A TW 202344622 A TW202344622 A TW 202344622A
- Authority
- TW
- Taiwan
- Prior art keywords
- layer
- pigment particles
- colored pigment
- coloring
- colored
- Prior art date
Abstract
本發明涉及著色顏料顆粒、獲得所述著色顏料顆粒的方法以及由所述著色顏料顆粒組成的組合物。此外,本發明涉及所述著色顏料顆粒的用途。
Description
本發明涉及著色顏料顆粒、用於獲得所述著色顏料顆粒的方法以及由所述顆粒組成的組合物。最後,本發明涉及著色顏料顆粒在各種應用中的用途。
除了在高端應用中使用二氧化鈦作為白色顏料外,二氧化鈦還用於彩色應用。在後期的應用中,二氧化鈦散射可見光,從而提供著色顏料無法提供的所需遮蓋力。
根據著色二氧化鈦顏料顆粒的最終用途,其通常由以下兩種形式提供:一種形式是,施加具有二氧化鈦的底層塗料,在其上施加由著色成分組成的另一塗料。這種方法例如用於高端用途,例如汽車塗料。另一種形式是,將二氧化鈦與著色組分混合,並將獲得的混合物作為單一塗料施加。
然而,這兩種方法都有一些缺點。團聚的著色組分的衰變是強制性的,這是因為團聚物的尺寸太大。此外,對著色組分進行擠出,結果表明所述組分理想地分散在組合物中。由於絕大多數這些組分的性質,這需要施加高能量,而且耗時。
此外,當施加具有二氧化鈦和著色組分的混合物的單一塗料時,遠離塗料表面的著色組分會被二氧化鈦顆粒覆蓋,因此不提供著色效果。因此,必須加入更大量的著色顏料顆粒,以實現期望著色效果,這需要更高成本。
因此,本領域需要一種著色顏料顆粒,其易於製備和處理,有效地提供著色效果,而且具有成本效益。還希望提供一種可以採用寬範圍顏色的著色顆粒。因此,各種著色組分應該是能應用的。
有鑑於此,吾等發明人乃潛心進一步研究,並著手進行研發及改良,期以一較佳發明以解決上述問題,且在經過不斷試驗及修改後而有本發明之問世。
本發明的目的是提供一種著色顏料顆粒,其易於製備和處理,有效地提供著色效果,並且具有成本效益。此外,還希望提供一種可以採用寬範圍顏色的有色顆粒。因此,各種著色成分應該是能應用的。
該目的通過著色顏料顆粒、獲得著色顏料顆粒的方法、包含所述顆粒的組合物以及本文所述顏料顆粒的用途來實現。
令人驚訝地發現,由二氧化鈦基顏料和至少一層組成的著色顏料顆粒易於製備和處理,有效地提供著色效果,並且還具有成本效益,著色顏料顆粒的特徵在於至少一層用著色組分改性。由於可以應用許多著色組分,根據本發明的著色顏料顆粒不限於特定顏色,而是可以提供許多不同的顏色。由於用著色組分對至少一層進行改性,因此不需要在額外步驟中將著色組分加入到諸如亮漆、油漆等組合物中,這是非常繁重的,因為該步驟需要大量的時間和精力。值得注意的是,加入根據本發明的顏料顆粒的負擔較小。此外,由於更有效地使用著色組分,故可以減少昂貴的著色組分的量。
因此,在第一方面,本發明涉及一種著色顏料顆粒,包括二氧化鈦基顏料和至少一層,其特徵在於,該至少一層用著色組分改性。
在第二方面,本發明涉及一種獲得著色顏料顆粒的方法,其包括以下步驟:
a) 提供二氧化鈦基顏料的水懸浮液,
b) 向所述懸浮液中添加層前體,
c) 向所述懸浮液中添加著色組分,以及
d) 從用著色組分改性的層前體在二氧化鈦基顏料上形成層,以獲得著色顏料顆粒。
在另一方面,本發明涉及包括本文所要求保護的著色顏料顆粒的組合物。
在本發明的另一方面,本發明涉及如本文所要求保護的著色顏料顆粒組成的組合物。
最後,本發明涉及如本文所要求保護的著色顏料顆粒對塗料、亮漆、油漆、塑料、紙或油墨進行著色的用途。
附屬項要求描述了本發明的另外的有利實施方式。
關於吾等發明人之技術手段,茲舉數種較佳實施例配合圖式於下文進行詳細說明,俾供 鈞上深入瞭解並認同本發明。
具體實施方式
從以下詳細描述和申請專利範圍的研究中,本發明的這些和其他方面、特徵和優點對於本發明所屬技術領域中具有通常知識者來說變得顯而易見。來自本發明一個方面的每個特徵可以用於本發明的任何其他方面。格式“從x到y”中表示的數值範圍包括上述值和本發明所屬技術領域中具有通常知識者已知的在各自測量精度範圍內的值。如果在此格式中陳述了幾個優選的數值範圍,那麼當然也包括由各種端點的組合形成的所有範圍。
根據本發明的著色顏料顆粒由二氧化鈦基顏料和至少一層組成,其特徵在於,至少一層用著色組分改性。本文所用的“二氧化鈦基顏料”是指通過硫酸鹽或氯化物工藝獲得的可任選研磨的二氧化鈦基顏料。此外,所述基顏料可存在於金紅石、銳鈦礦或板鈦礦的晶體結構中,通常存在於金紅石或銳鈦礦的晶體結構中。與銳鈦礦相比,金紅石由於其光催化活性較低而特別適合。優選地,所述二氧化鈦基顏料由至少98重量%(優選至少99重量%)的金紅石組成,其稱為所述顆粒的總重量。所述顆粒還包括至少一層。形成這種至少一層的前體和技術是本領域已知的。該至少一層用著色組分改性。可以使用本領域已知的任何賦予顏色(優選地不同於白色或黑色的顏色)的著色組分。
在本發明的範圍內,二氧化鈦基顏料具有主要尺寸,使得其散射可見光,理想地以高速率散射。粒徑是通過盤式離心機測定的200nm至400nm的質量相關中值d50(以下簡稱d50)。
在優選實施方式中,顏料顆粒包括另一層。
在又一優選實施方式中,至少一層位於二氧化鈦基顏料和另一層之間。在可選的優選實施方式中,另一層位於二氧化鈦基顏料和至少一層之間。
至少一層和另一層優選獨立地選自由二氧化矽、氧化鋁、二氧化鋯、氧化錳、氧化鈰、二氧化鈦、硫酸鹽或磷酸鹽基無機化合物或其混合物組成的組。磷酸鹽基無機化合物優選為磷酸鋁。硫酸鹽基無機化合物優選為硫酸鈰。甚至更優選地,至少一層和另一層獨立地選自由二氧化矽、氧化鋁、二氧化鋯、氧化錳、氧化鈰、二氧化鈦、硫酸鹽和磷酸鹽基無機化合物或其混合物組成的組。應注意,所述氧化物還包括相應的氫氧化物、羥基氧化物(oxyhydroxides)和相應的含水相。
此外,著色顏料顆粒優選地包括最終層,該最終層包括矽基有機化合物。本文定義的“最終層”是著色顏料顆粒的最外層。此類化合物可選自矽氧烷、矽烷和醇,例如市售的Tegomer DA640、三羥甲基丙烷(TMP)、辛基三氯矽烷(OCTCS)、辛基三乙氧基矽烷(OCTEO)或羥乙磷酸(etidronic acid)。
著色組分優選地選自由Co
3(PO
4)
3、NH
4MnP
2O
7、Fe
4[Fe(CN)
6]
3、PbCrO
4、BaMnO
4、BaCrO
4、Fe(OH)
3、Fe(OH)
2、Cu(OH)
2、Ni(OH)
2、Co(OH)
2、Cr(OH)
3、Mn(OH)
2、V(OH)
5、Bi(OH)
3、Ce(OH)
3、FeO、Fe
2O
3、Cu
2O、CuO、CoO、CrO、Cr
2O
3、CrO
2、MnO、Mn
2O
3、Mn
3O
4、VO、V
2O
3、VO
2、V
2O
5、Bi
2O
3、Bi
2O
5、La
2O
3、La(OH)
3、CeO
2、Ce
2O
3、Ce
3O
4、Ce(OH)
3、Ce(OH)
4、Pr
6O
11、Pr(OH)
3,Ne
2O
3、Nd(OH)
3、Pm
2O
3、Pm(OH)
3、Sm
2O
3、Sm(OH)
3、Eu
2O
3、Eu(OH)
3、Gd
2O
3、Gd
2(OH)
3、Tb
4O
7、Tb(OH)
3、Dy
2O
3、Dy(OH)
3、Ho
2O
3、Ho(OH)
3、Er
2O
3、Er(OH)
3、Tm
2O
3、Tm(OH)
3、Yb
2O
3、Yb(OH)
3、Lu
2O
3和Lu(OH)
3組成的組。
更優選地,著色組分選自由Co
3(PO
4)
3、NH
4MnP
2O
7、Fe
4[Fe(CN)
6]
3、PbCrO
4、BaMnO
4和BaCrO
4組成的組。
在優選實施方式中,著色顏料顆粒的另一層也用著色組分改性。
在又一個實施方式中,用相同的著色組分改性至少一層和另一層。可選地,用不同的著色組分改性至少一層和另一層。
基於著色顏料顆粒的總重量,著色顏料顆粒優選地包含0.5重量%至6重量%,更優選0.75重量%至3重量%,甚至更優選1重量%至2重量%的著色組分。
本發明還涉及一種獲得著色顏料顆粒的方法,包括以下步驟:
a) 提供二氧化鈦基顏料的水懸浮液,
b) 向所述懸浮液中添加層前體,
c) 向所述懸浮液中添加著色組分,以及
d) 從用著色組分改性的層前體在二氧化鈦基顏料上形成層,以獲得著色顏料顆粒。
本文所述的方法步驟按以下順序進行:a)、b)、c),然後d)。然而,該方法也可以按以下順序進行:a)、c)、b),然後d)。步驟b)和c)可以同時進行。結合根據本發明的方法使用的層可以是至少一層或另一層。在一個實施方式中,步驟a)中提供的二氧化鈦基顏料包括至少一層,並且在步驟d)中形成另一層。
為了形成二氧化矽層,可以使用任何已知的二氧化矽前體,例如矽酸鈉、矽酸鉀和矽酸鋰。優選地使用矽酸鈉。通過已知的方法和技術,可以形成二氧化矽層。前體的加入優選地在攪拌下進行,並且必要時在高溫下進行。前體可以在5至60分鐘的過程中被添加到懸浮液中,優選地在30分鐘的過程中。本發明所形成的二氧化矽層不僅包括二氧化矽,還包括由該層獲得的所有化合物,例如氫氧化矽、羥基二氧化矽和含二氧化矽相的水。
為了形成氧化鋁層,可以使用任何合適的氧化鋁前體。優選地,鋁酸鈉、硫酸鋁、硝酸鋁或氯化鋁用作前體,並且該層可以通過已知的方法和技術形成,例如添加堿,從而調節pH為4至9的範圍,優選為7。前體的加入優選地在攪拌下進行,必要時在高溫下進行。前體可以在5至60分鐘的過程中被添加到懸浮液中,優選地在30分鐘的過程中被添加到懸浮液中。本發明獲得的氧化鋁層不僅包括氧化鋁,還包括由該層獲得的所有化合物,例如氫氧化鋁、羥基氧化鋁和含氧化鋁相的水。
為了形成二氧化鋯層,可以使用任何合適的氧化鋯前體。優選地,氧氯化鋯、硫酸鋯和羧酸鋯用作前體,並且可以通過使用本領域已知的方法和技術來形成該層。前體的添加優選在攪拌下進行,必要時在高溫下進行。前體可以在5至60分鐘的過程中被添加到懸浮液中,優選地在30分鐘的過程中被添加到懸浮液中。本發明獲得的二氧化鋯層不僅包括二氧化鋯,而且包括由該層獲得的所有化合物,例如氫氧化鋯、羥基氧化鋯和含鋯相的水。
為了形成二氧化錳層,可以使用任何合適的二氧化錳前體。優選地,硫酸錳包括無水硫酸錳,以及一水合物、四水合物和七水合物,硝酸錳包括無水合物、四水合物和七水合物。用酸處理的碳酸錳也可以用作前體,並且可以通過使用本領域已知的方法和技術形成該層。前體的添加優選在攪拌下進行,必要時可以在高溫下進行。前體可以在5至60分鐘的過程中被添加到懸浮液中,優選地在30分鐘的過程中。本發明獲得的二氧化錳層不僅包括二氧化錳,還包括由該層獲得的所有化合物,例如MnOOH和Mn(II)Mn(III)
2O
4。
如果形成二氧化矽、氧化鋁和二氧化鋯層的混合物,則可以使用各自的前體。此外,二氧化矽、氧化鋁和二氧化鋯層的組合可以通過形成包含兩層材料的混合物的單層,或者均勻混合物或每層材料的梯度不同,或通過形成單獨層材料的連續層來形成。形成每種類型的層、混合層和多層層的各種方法是本領域技術人員公知的。
在根據本發明的方法的步驟c)中使用的著色組分選自由Co
3(PO
4)
3、NH
4MnP
2O
7、Fe
4[Fe(CN)
6]
3、PbCrO
4、BaMnO
4、BaCrO
4、Fe(OH)
3、Fe(OH)
2、Cu(OH)
2、Ni(OH)
2、Co(OH)
2、Cr(OH)
3、Mn(OH)
2、V(OH)
5、Bi(OH)
3、Ce(OH)
3、FeO、Fe
2O
3、Cu
2O、CuO、CoO、CrO、Cr
2O
3、CrO
2、MnO、Mn
3O
4、VO、V
2O
3、VO
2、V
2O
5、Bi
2O
3、Bi
2O
5、La
2O
3、La(OH)
3、CeO
2、Ce
2O
3、,Ce
3O
4、Ce(OH)
3、Ce(OH)
4、Pr
6O
11、Pr(OH)
3、Ne
2O
3、Nd(OH)
3、Pm
2O
3、Pm(OH)
3、Sm
2O
3、Sm(OH)
3、Eu
2O
3、Eu(OH)
3、Gd
2O
3、Gd
2(OH)
3、Tb
4O
7、Tb(OH)
3、Dy
2O
3、Dy(OH)
3、Ho
2O
3、Ho(OH)
3、Er
2O
3、Er(OH)
3、Tm
2O
3、Tm(OH)
3、Yb
2O
3、Yb(OH)
3、Lu
2O
3和Lu(OH)
3組成的組。
著色組分可以在添加到懸浮液期間或短暫地在步驟c)期間或可選地在步驟d)中被氧化。作為氧化劑,可以使用空氣、氧氣、過氧化氫或其他已知的氧化劑,其pH至少為2,優選至少為4。
優選地,著色組分以這樣的量添加:基於著色顏料顆粒的總重量,所獲得的著色顏料顆粒包含0.5重量%至10重量%,優選0.75重量%至6重量%,更優選1重量%至2重量%的著色組分。
本發明還涉及由本文所要求保護的著色顏料組成的組合物。在優選實施方式中,該組合物是塗料、亮漆、油漆、塑料、紙和油墨。
現有技術中已知且適用於根據本發明的目的的任何塑料都可以用作塑料。本文所用的“塑料”是指基於塑料的總重量,含有至少50重量%的聚合物的材料。所述聚合物可以是均聚物、共聚物或接枝聚合物。此外,該聚合物可以是無規立構聚合物、全同立構聚合物或間同立構聚合物。此外,塑料是熱塑性塑料、彈性體、熱固性或熱塑性彈性體,優選是熱塑性塑料。無限制地,聚合物選自由聚烯烴、聚苯乙烯、聚醯胺、聚酮、聚酯、聚氨酯、聚(甲基)丙烯酸酯及其混合物組成的組。無限制地,聚烯烴選自由聚乙烯、聚丙烯、聚丁烯及其混合物組成的組。著色顏料顆粒可以通過已知的技術和方法(例如通過擠出)併入到到塑料中。著色顏料顆粒以通常的量加工成塑料。因此,基於塑料的總重量,根據本發明獲得的塑料含有0.1重量%至30重量%,優選1重量%至25重量%的試劑。
最後,本發明涉及使用著色顏料顆粒對塗料、亮漆、油漆、塑料、紙、層壓板、建築材料或油墨進行著色。建築材料包括但不限於水泥、砂漿、石塊、砌塊、熟料(clinker)和抹灰(plastering)。
實施例
有色顏料顆粒的製備
實施例1a:製備以Fe
2O
3作為著色組分的著色顏料顆粒
通過將二氧化鈦基顏料顆粒(200g)與水(1L)混合來提供二氧化鈦基顏料懸浮液。懸浮液被加熱至60°C,並通過添加酸將pH降至2。
然後,通過將FeSO
4與水混合來提供以Fe
2O
3計算的FeSO
4水溶液(20ml,5重量%指水的重量)。在10分鐘的過程中,將該水溶液添加到二氧化鈦基顏料懸浮液中。然後,以足以將FeSO
4轉化為Fe
2O
3的量緩慢加入H
2O
2以獲得Fe
2O
3分散體。
然後,在30分鐘的過程中鋁酸鈉以一定的量被添加,以產生2.4重量%的氧化鋁層,其被稱為著色顏料顆粒的總重量。然後將pH調節至約7的值以完成層的形成。將著色顏料顆粒過濾、洗滌和乾燥。
實施例1b:製備以Fe
2O
3作為著色組分的著色顏料顆粒
按照實施例1a的方案獲得著色顏料顆粒,但使用40ml的Fe
2O
3水溶液。
實施例1c:製備以Fe
2O
3作為著色組分的著色顏料顆粒
按照實施例1a的方案獲得著色顏料顆粒,但使用80ml的Fe
2O
3水溶液。
實施例1d:製備以Fe
2O
3作為著色組分的著色顏料顆粒
按照實施例1d的方案獲得著色顏料顆粒,但使用160ml的Fe
2O
3水溶液。
CIELAB測定
實施例1a-1d的亮度(L*)和色調(a*)和(b*)的測定如下:提供具有從德國BASF商購獲得的Acronal LR 9014為粘合劑的水性漆製劑,並進行攪拌。然後,添加著色顏料顆粒並混合,直到獲得均勻的混合物。然後使用來自德國Erichsen GmbH&Co.KG的膜施加器510將所述混合物施加到可從美國Leneta公司獲得的圖表上,以獲得200µm厚的膜。將膜在無塵環境中乾燥24小時。CIELAB結果通過使用來自德國Byk Gardner的設備Colour-view,Lichtart C/2°來確定。
實施例1a-1d的CIELAB結果如圖1所示。
結果
可以看出,可以通過添加Fe
2O
3來調節色度點。每個值(a*、b*、L*)的調節與各個實驗中使用的Fe
2O
3的量有關。
試驗方法和試驗結果
粒徑測定
二氧化鈦顆粒的大小通過使用CPS盤式離心機(型號DC20000,可從位於佛羅裡達州的Florida的CPS儀器公司獲得)來測定。通過將2g幹顏料顆粒與80g六偏磷酸鈉溶液(水中0.06質量%)混合以獲得第一預混物來製備樣品。六偏磷酸鈉可從德國拉登堡的BK Giulini 有限公司商購獲得(商品名為Calgon N),直到第一預混物均質化。隨後,將2g該第一預混物添加到六偏磷酸鈉溶液(水中0.06質量%),並通過混合再次充分均勻質化以獲得第二預混物。100μL該第二預混物用作測定粒徑的樣品。離心機以3000rpm運行。校準標準參數如下:
顆粒密度:1.385g/mL
峰值直徑:1.27μL
半高峰寬:0.08μL
流體參數如下:
流體密度:1.045g/mL
流體折射率:1.344
流體粘度:1.2cps
綜上所述,本發明所揭露之技術手段確能有效解決習知等問題,並達致預期之目的與功效,且申請前未見諸於刊物、未曾公開使用且具長遠進步性,誠屬專利法所稱之發明無誤,爰依法提出申請,懇祈 鈞上惠予詳審並賜准發明專利,至感德馨。
惟以上所述者,僅為本發明之數種較佳實施例,當不能以此限定本發明實施之範圍,即大凡依本發明申請專利範圍及發明說明書內容所作之等效變化與修飾,皆應仍屬本發明專利涵蓋之範圍內。
〔本發明〕
無
[圖1]係。
Claims (15)
- 一種著色顏料顆粒,所述著色顏料顆粒包括二氧化鈦基顏料和至少一層,其特徵在於,所述至少一層用著色組分改性。
- 如請求項1所述之著色顏料顆粒,其中,所述著色顏料顆粒包括另一層。
- 如請求項1或2所述之著色顏料顆粒,其中, a)所述至少一層位於所述二氧化鈦基顏料和所述另一層之間;和/或 b)所述另一層位於所述二氧化鈦基顏料和所述至少一層之間。
- 如請求項1至3項中任一項所述之著色顏料顆粒,其中,所述另一層用著色顏料改性。
- 如請求項1至4項中任一項所述之著色顏料顆粒,其中,所述至少一層和所述另一層獨立地選自由二氧化矽、氧化鋁、氧化鋯、氧化錳、氧化鈰、二氧化鈦、硫酸鹽和磷酸鹽基無機化合物或其混合物組成的組。
- 如請求項1至5項中任一項所述之著色顏料顆粒,其中,所述著色顏料顆粒包括最終層,所述最終層包括矽基有機化合物。
- 如請求項1至6項中任一項所述之著色顏料顆粒,其中,所述著色組分選自由Co 3(PO 4) 3、NH 4MnP 2O 7、Fe 4[Fe(CN) 6] 3、PbCrO 4、BaMnO 4、BaCrO 4、Fe(OH) 3、Fe(OH) 2、Cu(OH) 2、Ni(OH) 2、Co(OH) 2、Cr(OH) 3、Mn(OH) 2、V(OH) 5、Bi(OH) 3、Ce(OH) 3、FeO、Fe 2O 3、Cu 2O、CuO、CoO、CrO、Cr 2O 3、CrO 2、MnO、Mn 2O 3、Mn 3O 4、VO、V 2O 3、VO 2、V 2O 5、Bi 2O 3、Bi 2O 5、La 2O 3、La(OH) 3、CeO 2、Ce 2O 3、Ce 3O 4、Ce(OH) 3、Ce(OH) 4、Pr 6O 11、Pr(OH) 3,Ne 2O 3、Nd(OH) 3、Pm 2O 3、Pm(OH) 3、Sm 2O 3、Sm(OH) 3、Eu 2O 3、Eu(OH) 3、Gd 2O 3、Gd 2(OH) 3、Tb 4O 7、Tb(OH) 3、Dy 2O 3、Dy(OH) 3、Ho 2O 3、Ho(OH) 3、Er 2O 3、Er(OH) 3、Tm 2O 3、Tm(OH) 3、Yb 2O 3、Yb(OH) 3、Lu 2O 3和Lu(OH) 3組成的組。
- 如請求項5所述之著色顏料顆粒,其中,所述著色組分選自由Co 3(PO 4) 3、NH 4MnP 2O 7、Fe 4[Fe(CN) 6] 3、PbCrO 4、BaMnO 4和BaCrO 4組成的組。
- 如請求項1至7項中任一項所述之著色顏料顆粒,其中,所述至少一層和所述另一層用相同的著色組分改性,或者所述至少一層和所述另一層用不同的著色組分改性。
- 如請求項1至8項中任一項所述之有色顏料顆粒,其中,基於所述著色顏料顆粒的總重量,所述顏料顆粒包括0.5重量%至10重量%,優選0.75重量%至6重量%,更優選1重量%至2重量%的所述著色組分。
- 一種獲得著色顏料顆粒的方法,所述方法包括以下步驟: a) 提供二氧化鈦基顏料的水懸浮液, b) 向所述懸浮液中添加層前體, c) 向所述懸浮液中添加著色組分,以及 d) 從用所述著色組分改性的層前體在所述二氧化鈦基顏料上形成層,以獲得所述著色顏料顆粒。
- 如請求項11所述之方法,其中,所述著色組分選自由Co 3(PO 4) 3、NH 4MnP 2O 7、Fe 4[Fe(CN) 6] 3、PbCrO 4、BaMnO 4、BaCrO 4、Fe(OH) 3、Fe(OH) 2、Cu(OH) 2、Ni(OH) 2、Co(OH) 2、Cr(OH) 3、Mn(OH) 2、V(OH) 5、Bi(OH) 3、Ce(OH) 3、FeO、Fe 2O 3、Cu 2O、CuO、CoO、CrO、Cr 2O 3、CrO 2、MnO、Mn 2O 3、Mn 3O 4、VO、V 2O 3、VO 2、V 2O 5、Bi 2O 3、Bi 2O 5、La 2O 3、La(OH) 3、CeO 2、Ce 2O 3、Ce 3O 4、Ce(OH) 3、Ce(OH) 4、Pr 6O 11、Pr(OH) 3,Ne 2O 3、Nd(OH) 3、Pm 2O 3、Pm(OH) 3、Sm 2O 3、Sm(OH) 3、Eu 2O 3、Eu(OH) 3、Gd 2O 3、Gd 2(OH) 3、Tb 4O 7、Tb(OH) 3、Dy 2O 3、Dy(OH) 3、Ho 2O 3、Ho(OH) 3、Er 2O 3、Er(OH) 3、Tm 2O 3、Tm(OH) 3、Yb 2O 3、Yb(OH) 3、Lu 2O 3和Lu(OH) 3組成的組。
- 如請求項11或12所述之方法,其中,所述著色組分以如下的量添加:基於所述著色顏料顆粒的總重量,所獲得的所述著色顏料顆粒包含0.5重量%至10重量%、優選0.75重量%至6重量%、更優選1重量%至2重量%的所述著色組分。
- 一種組合物,包括如請求項1至11項中任一項所述之著色顏料顆粒。
- 如請求項1至9項中任一項所述之著色顏料顆粒對塗料、亮漆、油漆、塑料、紙、建築材料或油墨進行著色的用途。