SU612641A3 - Электролит серебрени - Google Patents
Электролит серебрениInfo
- Publication number
- SU612641A3 SU612641A3 SU742073760A SU2073760A SU612641A3 SU 612641 A3 SU612641 A3 SU 612641A3 SU 742073760 A SU742073760 A SU 742073760A SU 2073760 A SU2073760 A SU 2073760A SU 612641 A3 SU612641 A3 SU 612641A3
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- electrolyte
- silver plating
- sodium
- plating electrolyte
- silver
- Prior art date
Description
ности тока 1 А/дм составл ет 0,6 мм/мин, что на 10% вшие скорости осаждени в известном электролите. Процесс йсаждени рекомендуют проводить при 20-3О С, рН 5-14 и пло йости тока 0,2-1,5 А/дм Предлагаемый электролит стабилен в. работе при нагрузке 400 А/j в течение двух мес цев. Серебр ные аноды раствор ютс равномерно без влений пассивировани . Анодный и катодный выходы по току составл ютV 100%. Покрыти , осаждаемые в предлагаемом электролите, имеют следующие свойства Отражательна спо90-100% собность 130-180 кгс/м Микротвердость 4-10 кгс/iv МакротвердосТь Удельное сопротив2 ,,5 мОмление Перех;одное сопротивление1 ,25 Омм Износостойкость при толщине покры1800 оборото ти 10 мкм Прочность сцепле20-30 кгс/мм ни Твердость покрыти относительно мало мен етс во времени и в зависимости от температуры. Так при темпер турах До в покрыти х не происх д т возвратные влени , а их твердос сохран етс вплоть до , а также при отжиге. При определении скорости потуск нени покрытий в 2%-ном растворе сер нистого натри получают врем , необходимое дл достижени определенной толщины сло сульфида серебра, который и вл етс мерой скорости потуск нени . Это врем составл ет 4-6 мин. Предлагаемый электролит может, содержать добавки, повышающие электр проводность, такие как сульфат аммони или соли щелочных металлов неорганических или слабых органических кислот (борной, серной, сернистой урольной, сульфаминовой, уксусной или лимонной), а также добавки, регулирующие значение рН электролита, такие как Динатрий-фосфат, карбонат, борат или ацетат натри . Полиэтиленимин, вводимый в предлагаемый электролит, имеет молекул рный вес 300-50000 Дифеиилдисульфид 2,2-дикарбоновС Й кислоты имеет следующую структурную формулу. .-s. соон ноос Б табл, 1 приведены примеры составов (г/л) -электролита, в табл. 2 - режим осаждени и экспериментальные данные. Состав 1 электролита используют преимущественно дл предварительного серебрени латунных изделий.. Дл полунени на этих издели х блест щего поккрыти твердостью 148 кг/мм и толщиной до 10 мкм провод т последующее серебрение в электролите, содержащем, г/л; Натрийсеребр на соль тиосерной кислоты Тиосульфат натри . Борна кислота Этиленгликоль Сульфат натри Поливинилпиридйний- N -сульфопропилбетаин . 0,8 при температуре , рН 5,9 плотности тока 0,6 течение 10 мин. Техническим эквивалентом соедит нени серы ( по достигаемому результату ) вл етс соединение селена. Поэтому предлагаемый электролит вместо соединени серы может содержать соединение селена, например диселенигликолевую кислоту. Т а б л и ц а-1
Натрийсеребр на соль тиосерной килоты
tNa,Ag-CS.,03-)., Тиосульфатнатри
tNOiS-jOs
Дифенилдисульфид
2,2-дикарбоновой кислоты
Тетраборат натри СМааВд04.- ОН203
Карбонат натри Сульфат натри ,1
0,5 29 60 4 235 800
0,001 2 48 20 3
60 -. 10
Полиэтиленимин мол. в. 300 длол.в. 10000 мол.в. 50000
Плотность тока. А/дм . Продолжительность, мин
Толщина покрыти , мкм
Твердость, кгс/мм Отражательна способность , %
Claims (1)
1. Патент Чехословакии № 99987, 48а, 5/26f 1961.