SU532650A1 - Ligature for the deoxidation of steel - Google Patents
Ligature for the deoxidation of steelInfo
- Publication number
- SU532650A1 SU532650A1 SU2151863A SU2151863A SU532650A1 SU 532650 A1 SU532650 A1 SU 532650A1 SU 2151863 A SU2151863 A SU 2151863A SU 2151863 A SU2151863 A SU 2151863A SU 532650 A1 SU532650 A1 SU 532650A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- steel
- ligature
- silicon
- deoxidation
- earth metals
- Prior art date
Description
кварцита, глинозема, железной стружки с присадкой циркони в расплав.quartzite, alumina, iron chips with zirconium additive in the melt.
Лигатуру вводили в ковш в количестве 1,5 кг на 1 т стали марки Р6М5 в процессе выпуска стали из печи.The ligature was introduced into the ladle in the amount of 1.5 kg per 1 ton of steel grade R6M5 in the process of steel production from the furnace.
Сталь разливали на слитки весом 3,5 и подвергали гор чей прокатке.The steel was cast into 3.5-inch ingots and subjected to hot rolling.
Результаты по выходу годного проката при модифицировании стали марки Р6М5 предлагаемой лигатурой приведены в таблице .The results of the yield of rolled steel when modifying the steel grade R6M5 with the proposed ligature are given in the table.
Предлагаема лигатура дл модифицировани быстрорежущих сталей повышает качество блюмов благодар уменьшению рванин и рассло в процессе гор чей прокатки .The proposed ligature for modifying high-speed steels improves the quality of blooms by reducing flaking and spillage during hot rolling.
Claims (1)