SU435205A1 - SILICATE POLYMERBETON COMPOSITION

Info

Publication number: SU435205A1
Application number: SU1863070A
Authority: SU
Inventors: И. нюшкин Ю.
Priority date: 1972-12-26
Filing date: 1972-12-26
Publication date: 1974-07-05

Description

Изобретение относитс к силикатополимербетонным композици м в производстве кислотостойких изделий.FIELD OF THE INVENTION The invention relates to silicate polymer concrete compositions in the manufacture of acid resistant articles.

Известна силикатополимербетонна композици , включающа жидкое стекло, кремнефтористый натрий, полимерную добавку и минеральные иаполнители.The silico-polymer-concrete composition is known, including water glass, sodium silicofluoride, a polymer additive and mineral and fillers.

Известный материал имеет р д недостатков, а именно высокую усадку, малую прочность и большую диффузионную проницаемость дл растворов кислот низких концентраций.The known material has a number of disadvantages, namely high shrinkage, low strength and high diffusion permeability for solutions of acids of low concentrations.

Целью изобретени вл етс повышение прочности, снижение усадки и диффузионной проницаемости силикатополимербетонных изделий .The aim of the invention is to increase the strength, reduce shrinkage and diffusion permeability of the silicate polymer concrete products.

Достигаетс это тем, что силикатополимербетонна композици содержит в качестве полимерной добавки смесь фурилового спирта и фенолформальдегидной смолы в соотношении от 2 : 1 до 4 : 1 при следуюш,их количествах указанных компонентов (в вес. %):This is achieved by the fact that the silicopolymer concrete composition contains as a polymeric additive a mixture of furyl alcohol and phenol-formaldehyde resin in a ratio from 2: 1 to 4: 1 with the following, their amounts of the indicated components (in wt.%):

Жидкое стекло10,2-12 Кремнефтористый натрий 1,5-2,3Liquid glass 10,2-12 Silicon Fluoride Sodium 1,5-2,3

Фур иловый спирт0,18-0,43 Фенолформальдегидна Foursome alcohol 0.18-0.43 Phenol formaldehyde

смола0,12-0,3 Щебень кислотостойкий42-43resin 0.12-0.3 Crushed stone, acid-resistant42-43

Песок28-30Sand28-30

Андезитова мука15-17Andesitic flour15-17

Приготовление силикатополимербетона состоит из следующих операций: приготавливаетс полимерна добавка - в фуриловый спирт вводитс Фенолформальдегидна водорастворима смола в соотношении от 2 : 1 до 4:1; дозируютс все наполнители и кремнефтористый натрий; в жидкое стекло вводитс полимерна добавка и смесь тщательно перемешиваетс в течение 1 -1,5 мии; приготовленное св зующее вливаетс в сухую смесь наполнителей и кремнефтористого натри и вс масса перемешиваетс в течение 2- 5 мин, затем распредел етс в формы и вибрируетс 1,5-2 мин.The preparation of silica-polymer concrete consists of the following operations: a polymer additive is prepared — phenol-formaldehyde water-soluble resin is introduced into the furyl alcohol in a ratio from 2: 1 to 4: 1; all fillers and sodium silicofluoride are dosed; a polymer additive is introduced into the water glass and the mixture is thoroughly mixed for 1 -1.5 missions; The prepared binder is poured into a dry mixture of fillers and sodium silicofluoride and the whole is stirred for 2-5 minutes, then distributed into molds and vibrated for 1.5-2 minutes.

Полученные образцы имеют прочность при сжатии в 1,5 раза выше, чем образцы известного силикатополимербетона, усадка снижаетс на 40%, а диффузионна проницаемость дл слабокислых сред (концентраци от 10%The samples obtained have a compressive strength 1.5 times higher than samples of the known silicate polymer concrete, the shrinkage is reduced by 40%, and the diffusion permeability for weakly acidic media (concentration from 10%

и менее) уменьшаетс более чем в 2 раза.and less) is reduced by more than 2 times.

Силикатополимербетонные издели предложенного состава могут найти применение дл кислотостойких и кислотонепроницаемых конструкций , эксплуатирующихс в средах низких концентраций.Silicate-polymer-concrete products of the proposed composition can be used for acid-resistant and acid-proof structures, operating in environments of low concentrations.

Предмет изобретени Subject invention

Силикатополимербетонна композици ,Silica-polymeric concrete composition

включающа жидкое стекло, кремнефтористый натрий, полимерную добавку и минераль3 ные наполнители, отличающа с тем, что, с целью повышени прочности, снижени усадки и диффузионной проницаемости издеЛИЙ , она содержит в качестве полимерной добавки смесь фурилового спирта и фенолфор-5 мальдегидной смолы в соотношении от 2 : 1 до 4; 1 при следующих количествах указанных компонентов (в вес.с %): 4 Жидкое стекло10,2--12 Кремнефтористый натрий1,5-2,3 Фуриловый спирт0,18-0,43 Фенолформальдегидна смола0,12-0,3 Щебень кислотостойкий42- 43 Песок28-30 Андезитова мука15-17including liquid glass, sodium silicofluoride, polymer additives, and mineral fillers, characterized in that, in order to increase strength, reduce shrinkage and diffusion permeability of products, it contains as a polymer additive a mixture of furyl alcohol and phenol-5 maldehyde resin 2: 1 to 4; 1 with the following amounts of the indicated components (in weight%): 4 Liquid glass 10,2--12 Sodium fluorofluoride 1.5-2.3 Furyl alcohol 0.18-0.43 Phenol-formaldehyde resin 0.12-0.3 Crushed stone acid-resistant42- 43 Pesok28-30 Andesite flour15-17