Description
Изобретение относитс к области цветной металлургии и касаетс разработки прочных и легких конструкционных материалов на основе алюмини .The invention relates to the field of non-ferrous metallurgy and concerns the development of durable and lightweight construction materials based on aluminum.
Известны литейные сплавы на основе алюмини , содержащие медь, марганец, титан, с дополнительным легированием р дом добавок , в том числе хромом и кадмием.Foundry aluminum-based alloys containing copper, manganese, and titanium are additionally doped with a number of additives, including chromium and cadmium.
Отличительной особенностью предлагаемого сплава вл етс найденное оптимальное соотношение легирующих добавок в системе А1, Си, Ми, Ti, позвол ющее создать материал , обладающий высокой размерной ста2A distinctive feature of the proposed alloy is the found optimal ratio of alloying additives in the A1, Cu, Mi, Ti system, which allows to create a material with a high dimensional grade.
бильностью, однородной структурой и высоким сопротивлением микропластической деформации во времени. Предлагаемый сплав содержит (в %): Медь5-6,5stability, uniform structure and high resistance to microplastic deformation over time. The proposed alloy contains (%): Copper 5-6,5
Марганец0,15-0,5Manganese 0.15-0.5
Титан0,05-0,3Titanium0.05-0.3
Хром0,1-0,25Chrome 0.1-0.25
Кадмий0,05-0,2Cadmium0.05-0.2
АлюминийОстальноеAluminum Else
Механические свойства Mechanical properties
предлагаемого сплава приведены в таблице Термическа обработка сплава заключаетс в нагреве под закалку в течение 2-3 час до температуры 530-540°С, выдерл ка 16- 18 час, охлаждение в воде 70-90°С. Искусственное старение 175±5° - 8 час; 190±5° - 4 час. Сплав рекомендован дл изготовлени литых деталей, к которым предъ вл ютс повышенные требовани по размерной стабильности в услови х длительного хранени и эксплуатации , а также дл высоконагруженных деталей. Предмет изобретени Литейный сплав на основе алюмини , содержащий медь, марганец, титан, хром и кадмий , отличающийс тем, что, с целью повышени физико-механических свойств, компоненты вз ты в следующем соотношении (в %): Медь5-6,5 Марганец0,15-0,5 Титан0,05-0,3 Хром0,1-0,25 Кадмий0,05-0,2 АлюминийОстальноеThe proposed alloy is given in the table. Thermal treatment of the alloy consists in heating for quenching for 2-3 hours to a temperature of 530-540 ° C, lining for 16-18 hours, cooling in water 70-90 ° C. Artificial aging 175 ± 5 ° - 8 hours; 190 ± 5 ° - 4 hours. The alloy is recommended for the manufacture of cast parts, to which increased requirements are imposed on dimensional stability under conditions of long-term storage and operation, as well as for highly loaded parts. The subject matter of the invention The aluminum-based cast alloy containing copper, manganese, titanium, chromium and cadmium, characterized in that, in order to improve the physicomechanical properties, the components are taken in the following ratio (in%): Copper 5-6,5 Manganese, 15-0.5 Titanium 0.05-0.3 Chromium 0.1-0.25 Cadmium 0.05-0.2 Aluminum Else
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU980894A SU320548A1 (en) | 1967-02-20 | 1967-02-20 |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU980894A SU320548A1 (en) | 1967-02-20 | 1967-02-20 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| SU320548A1 true SU320548A1 (en) | 1971-11-04 |
Family
ID=40010995
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| SU980894A SU320548A1 (en) | 1967-02-20 | 1967-02-20 |
Country Status (1)
| Country | Link |
|---|---|
| SU (1) | SU320548A1 (en) |
-
1967
- 1967-02-20 SU SU980894A patent/SU320548A1/ru active
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| RU96113088A (en) | LEAD-FREE ALUMINUM ALLOY 6XXX | |
| SE7904725L (en) | MAGNESIUM ALLOYS | |
| ES418116A1 (en) | Aluminium alloys | |
| DE3612675A1 (en) | COMPONENT FOR A COMBUSTION ENGINE AND METHOD FOR THE PRODUCTION THEREOF | |
| ES375477A2 (en) | Aluminum base alloy | |
| GB1234866A (en) | Thermal treatment of aluminium-magnesium alloy for improvement of stress-corrosion properties | |
| SU320548A1 (en) | ||
| ES295606A1 (en) | Improvements introduced in the manufacture of copper-based alloys (Machine-translation by Google Translate, not legally binding) | |
| KR890010256A (en) | Alloy based on copper to obtain aluminum beta-brass containing particle-size reducing additives | |
| ES439541A1 (en) | Aluminium-based alloy | |
| SU524849A1 (en) | Aluminum based alloy | |
| GB1244740A (en) | Aluminium-zinc-magnesium alloys | |
| HORI et al. | Cold workability of Mg-Li and Mg-Zr-Li alloys | |
| SU336360A1 (en) | ALLOY BASED ON ALUMINUM | |
| ES385426A1 (en) | Wrought copper-nickel alloy | |
| SU345224A1 (en) | CASTING ALLOY BASED ON ALUMINUM | |
| ES423131A1 (en) | Aluminium alloys | |
| GB159008A (en) | Improvements in or relating to aluminium alloys | |
| SU406931A1 (en) | ALLOY BASED ON ALUMINUM | |
| SU450846A1 (en) | Aluminum based alloy | |
| GB1414289A (en) | Copper material and uses thereof | |
| GB1384264A (en) | Structural parts produced from aluminium-containing alloys | |
| SU445704A1 (en) | Aluminum based foundry alloy | |
| SU212537A1 (en) | COPPER BASED ALLOY | |
| SU406936A1 (en) | Manganese based alloy |