SU1502648A1 - Alloy based on magnesium for tyre treades - Google Patents

Alloy based on magnesium for tyre treades Download PDF

Info

Publication number
SU1502648A1
SU1502648A1 SU874317039A SU4317039A SU1502648A1 SU 1502648 A1 SU1502648 A1 SU 1502648A1 SU 874317039 A SU874317039 A SU 874317039A SU 4317039 A SU4317039 A SU 4317039A SU 1502648 A1 SU1502648 A1 SU 1502648A1
Authority
SU
USSR - Soviet Union
Prior art keywords
protectors
magnesium
efficiency
corrosion
zinc
Prior art date
Application number
SU874317039A
Other languages
Russian (ru)
Inventor
Усмадияр Маканович Маканов
Даляпраз Бекжановна Мамбеева
Нурайса Алимгазиновна Каражанова
Серик Бахтыбаевич Орынбеков
Тлек Айтмуханович Кетегенов
Далел Гумарович Медиханов
Original Assignee
Казахский политехнический институт им.В.И.Ленина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Казахский политехнический институт им.В.И.Ленина filed Critical Казахский политехнический институт им.В.И.Ленина
Priority to SU874317039A priority Critical patent/SU1502648A1/en
Application granted granted Critical
Publication of SU1502648A1 publication Critical patent/SU1502648A1/en

Abstract

Изобретение относитс  к защите металлов от коррозии, коррозионно-стойким материалам , в частности, к протекторам, подавл ющим коррозию металлоконструкций в жидких средах. Цель изобретени  - повышение КПД протекторов в хлорсодержащих водных средах. Сплав на основе магни  дл  протекторов содержит компоненты в следующем соотношении, мас.%: алюминий 4-5, цинк 2,5-3, железо 1,5-2, магний - остальное. КПД протекторов 72,7-80,0%. 2 табл.The invention relates to the protection of metals from corrosion, corrosion-resistant materials, in particular, to protectors that suppress corrosion of metal structures in liquid media. The purpose of the invention is to increase the efficiency of protectors in chlorine-containing aqueous media. The magnesium based alloy for protectors contains components in the following ratio, wt%: aluminum 4-5, zinc 2.5-3, iron 1.5-2, magnesium - the rest. The efficiency of protectors is 72.7-80.0%. 2 tab.

Description

1one

(21)4317039/31-02(21) 4317039 / 31-02

(22)16.10.87(22) 10/16/87

(46)23,08.89. Бюл. № 31(46) 23.08.89. Bul No. 31

(71)Казахский политехнический институт им. В.И. Ленина(71) Kazakh Polytechnic Institute. IN AND. Lenin

(72)У.М. Маканов, Д.Б. Мамбеева, Н.А.Каражанова, С.Б. Орынбеков, Т.А.Кетегенов и Д.Г. Медиханов (53)669.721(088.8)(72) U.M. Makanov, D.B. Mambeeva, N.A.Karazhanova, S.B. Orynbekov, TA Ketegenov and D.G. Medikhanov (53) 669.721 (088.8)

(56) Авторское свидетельство СССР № 36121 5,кл. С 22 С 23/00, 1972. ЦМТУ 0,5-124-69.(56) USSR Copyright Certificate No. 36121 5, cl. C 22 C 23/00, 1972. TsMTU 0.5-124-69.

(54) СПЛАВ НА ОСНОВЕ МАГНИЯ ДЛЯ ПРОТЕКТОРОВ(54) ALLOY BASED ON MAGNESIUM FOR PROTECTORS

(57) Изобретение относитс  к защите металлов от коррозии, коррозиоино- стойким материалам, в частности к протекторам, подавл ющим коррозию металлоконструкций в жидких средах. Цель изобретени  - повышение КПД протекторов в хлорсодержащих водных средах. Сплав на основе магни  дл  протекторов содержит компоненты в следующем соотношении, мас.%: алюминий 4-5, цинк 2,5-3, железо 1,5-2, магний - остальное. КПД протекторов, 72,7-80,0%. 2 табл.(57) The invention relates to the protection of metals from corrosion, corrosion-resistant materials, in particular to protectors that suppress corrosion of metal structures in liquid media. The purpose of the invention is to increase the efficiency of protectors in chlorine-containing aqueous media. The magnesium based alloy for protectors contains components in the following ratio, wt%: aluminum 4-5, zinc 2.5-3, iron 1.5-2, magnesium - the rest. Efficiency of protectors, 72.7-80.0%. 2 tab.

с 9from 9

Изобретение откоситс  к области защиты металлов от коррозии, корро- зионностойким материалам, в частности к протекторам, подавл ющим коррозию металлоконструкций в жидких средах.The invention is committed to the field of protection of metals against corrosion, corrosion-resistant materials, in particular protectors, which suppress corrosion of metal structures in liquid media.

Цель изобретени  - повьпиение коэффициента полезного действи  протекторов , в хлорсодержащих водных средах.The purpose of the invention is to increase the efficiency of protectors in chlorine-containing aqueous media.

Пример. Смеси с различным соотношением компонентов сплавл лись в высокочастотной печи в  лундовых тигл х в атмосфере аргона при 600 С . Разливка сплава производилась в сухие формы. Химический состав известного и предложенного сплавов приведен Б табл. 1 .Example. Mixtures with different ratios of the components were fused in a high-frequency furnace in lundy crucibles in an atmosphere of argon at 600 ° C. The casting of the alloy was carried out in dry forms. The chemical composition of the known and proposed alloys is given in Table B. one .

Определение электрохимических характеристик выполн лось на потенцио- стате 11-58-48 в водных средах.Determination of electrochemical characteristics was carried out on potentiostat 11-58-48 in aqueous media.

В табл. 2 показаны значени  КПД протекторов 43 магниевых сплавов при защите стали 3 в водных средах.In tab. Figure 2 shows the efficiency values of protectors 43 of magnesium alloys when protecting steel 3 in aqueous media.

Протекторы,изготовленные из предложенного сплава, имеют КПД на 15-20% выше, чем у протектора из из- S вестного сплава.The protectors made of the proposed alloy have an efficiency of 15–20% higher than that of the known alloy.

Claims (1)

Формула изобретени Invention Formula Сплав на основе магни  дл  протекторов , содержащий алюминий и цинк, отличающийс  тем, что, с целью повышени  коэффициента полезного действи  протекторов в хлорсодержащих водных средах, спл в дополнительно содержит железо при следующем соотношении компонентов, мае. 7,1A magnesium based alloy for protectors containing aluminum and zinc, characterized in that, in order to increase the efficiency of the protectors in chlorine-containing aqueous media, Spl in additionally contains iron in the following ratio of components, May. 7.1 Алюминий Цинк Железо МагнийAluminum Zinc Iron Magnesium 4-5 2,5-3 1,5-2 Остальное4-5 2.5-3 1.5-2 Else Составитель И. Никишина Редактор В. ДанкоТехред Л.ОлийныкКорректор Л. БескидCompiled by I. Nikishin Editor V. DankoTehred L.OliynykCorrector L. Beskid Заказ 5048/36Order 5048/36 Тираж 576Circulation 576 ВНИИПИ Государственного комитета по изобретени м и открыти м при ГКНТ СССР 113035, Москва, Ж-35, Раушска  наб., д. 4/5VNIIPI State Committee for Inventions and Discoveries at the State Committee on Science and Technology of the USSR 113035, Moscow, Zh-35, Raushsk nab. 4/5 Производственно-издательский комбинат Патент, г.Ужгород, ул. Гагарина,101Production and publishing plant Patent, Uzhgorod, st. Gagarin, 101 Таблица -1Table 1 ПодписноеSubscription
SU874317039A 1987-10-16 1987-10-16 Alloy based on magnesium for tyre treades SU1502648A1 (en)