SU1381103A1 - Raw material mixture for making silicate articles - Google Patents

Raw material mixture for making silicate articles Download PDF

Info

Publication number
SU1381103A1
SU1381103A1 SU853863099A SU3863099A SU1381103A1 SU 1381103 A1 SU1381103 A1 SU 1381103A1 SU 853863099 A SU853863099 A SU 853863099A SU 3863099 A SU3863099 A SU 3863099A SU 1381103 A1 SU1381103 A1 SU 1381103A1
Authority
SU
USSR - Soviet Union
Prior art keywords
raw material
material mixture
strength
manufacture
mpa
Prior art date
Application number
SU853863099A
Other languages
Russian (ru)
Inventor
Василий Васильевич Помазков
Альбина Васильевна Уколова
Валерий Александрович Попов
Людмила Сергеевна Кульнева
Original Assignee
Воронежский инженерно-строительный институт
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Воронежский инженерно-строительный институт filed Critical Воронежский инженерно-строительный институт
Priority to SU853863099A priority Critical patent/SU1381103A1/en
Application granted granted Critical
Publication of SU1381103A1 publication Critical patent/SU1381103A1/en

Abstract

Изобретение относитс  к промышленности строительных материалов и может быть использовано при изготовлении силикатных изделий, в частности кирпича. Целью изобретени   вл етс  повьшение прочности сырца. Сырьева  смесь дл  изготовлени  силикатных изделий содержит, мас.%: известь 8,5- 10,5; отход производства конденсаторов со стадии электрохимического травлени  алюминиевой фольги 1, - 2; песок кварцевый - остальное. Сырьева  смесь обеспечивает прочность сырца 0,53 - 0,55 МПа, прочность кир- кича 11,4-11,6 МПа, морозостойкость 25 циклов. 1 табл. слThe invention relates to the building materials industry and can be used in the manufacture of silicate products, in particular bricks. The aim of the invention is to increase the strength of the raw material. The raw material mixture for the manufacture of silicate products contains, in wt.%: Lime 8.5 - 10.5; production waste of capacitors from the stage of electrochemical etching of aluminum foil 1, - 2; quartz sand - the rest. The raw mix provides raw strength of 0.53–0.55 MPa, brick strength of 11.4–11.6 MPa, frost resistance of 25 cycles. 1 tab. cl

Description

со 00from 00

Изобретение относитс  к промышленности строительных материалов и может быть использовано при изготовлении силикатных изделий, в частности кирпича.The invention relates to the building materials industry and can be used in the manufacture of silicate products, in particular bricks.

Цель изобрет ени  - повышение прочности сырца.The purpose of the invention is to increase the strength of raw material.

Пример. Дл  приготовлени  смеси используют негашеную известь активностью 70-80%, песок кварцевый и отход производства конденсаторов (завода радиодеталей), который образуетс  на стадии электрохимического травлени  алюминиевой фольги при использовании в качестве электролита раствор поваренной соли. Отход представл ет собой плотностью 1,07 г/см и содержит 70% воды и 30% сухого вещества следующего состава, мас.%: SiOj 0,2-0,22; AljO, 62,5- 62,53; ,00-1,01; CaO 0,92-0,94; MgO 0,7-0,8; NaCl 11,13-11,16; п.п.п остальное.Example. To prepare the mixture, quick lime with an activity of 70-80%, quartz sand and condenser production waste (a radio component plant), which is formed at the stage of electrochemical etching of aluminum foil using sodium chloride solution as electrolyte, are used. The waste is a density of 1.07 g / cm and contains 70% of water and 30% of dry matter of the following composition, wt.%: SiOj 0.2-0.22; AljO, 62.5- 62.53; , 00-1.01; CaO 0.92-0.94; MgO 0.7-0.8; NaCl 11.13-11.16; ppt rest.

и отход в виде пульпы перемешивают в смесителе с водой в количестве, обеспечивающем влажность формовочной сме- си 6%. Из Смеси прессуют образцы диаметром и высотой 50 мм при давлении 20 МПа. Образцы запирают по режиму 1,5-8-6 при 0,9 МПа.and the waste in the form of a slurry is mixed in a mixer with water in an amount that provides the moisture of the molding mixture of 6%. Samples are pressed from the mixture with a diameter and height of 50 mm at a pressure of 20 MPa. Samples are locked in the mode of 1.5-8-6 at 0.9 MPa.

Состав и свойства смесей приведены в таблице.The composition and properties of the mixtures are given in the table.

Claims (1)

Формула изобретени Invention Formula Сырьева  смесь дл  изготовлени  силикатных изделий, включающа  известь , песок кварцевый и добавку на основе оксида алюмини , отличающа с  тем, что, с целью повь; - шени  прочности сырца, она содержит в качестве добавки отход производства конденсаторов со стадии электрохимического травлени  алюминиевой фольги при следующем соотношении компонентов , мае.%:A raw material mixture for the manufacture of silicate products, including lime, silica sand and an additive based on alumina, characterized in that, with the aim of turning; - strength of raw material, it contains as an additive the waste from the production of capacitors from the stage of electrochemical etching of aluminum foil in the following ratio of components, wt.%: (в соотмо енми 1:1) 201 н иесок- заполмитслт, BOZ(in terms of 1: 1) 201 nesok-sub-policyst, BOZ QQ Нзвест «1 п-крсм11С1емиптпе в жущееNzvest "1 p-krsm11S1emiptpe in idle (н cooTHOmf HUM I : I) 15t и песок- аполинтсль 832(n cooTHOmf HUM I: I) 15t and sand-apolintsl 832 BiMfflH Заказ 1160/25BiMfflH Order 1160/25 Произв.-полигр. пр-тие, г. Ужгород, ул. Проектна , 4Random polygons pr-tie, Uzhgorod, st. Project, 4 10,510.5 2525 20702070 ПP Тираж 594Circulation 594 ПодписноеSubscription
SU853863099A 1985-03-11 1985-03-11 Raw material mixture for making silicate articles SU1381103A1 (en)