Известен способ получени сульфата магни из доломита путем обработки последнего серной кислотой. Описываемый способ по сравнению с известным обеспечивает более полное прен ращепие окиси магпи доломита в сульфат магни . Это достигаетс тем, что прокаленный доломит обрабатывают раствором сульфата аммони .A method of producing magnesium sulfate from dolomite is known by treating the latter with sulfuric acid. The described method, in comparison with the known method, provides a more complete conversion of magnipolomite oxide to magnesium sulfate. This is achieved in that the calcined dolomite is treated with an ammonium sulphate solution.

При взаимодействии прокаленного при температурах пор дка 800- lOOO доломита с раствором сернокислого аммони одновременно .е образованием сульфата магни образуютс комплексные сернокислые соли аммони и магни , аммони и кальци . Дл растворени всей окиси магни доломита реакцию ведут при значительном избытке сернокислого аммони . Дл удалени аммиака из смеси и унеличепи растворимости сернокислого магни и комплексных солей процесс осуществл ют при повышенной температуре и смесь кип т т в течение 2 час. до полного удалени выдел ющегос аммиака. В осадке получают сернокислый кальций , а iB растворе-сернокислый магний в смеси с комплексными сол ми . Остающа с в растворе значительна часть сернокислого аммони в виде комплексных солей легко разрушаетс и аммиак высвобождаетс при кип чении отделенного от осадка раствора с новой порцией прокаленного доломита (при избытке окисп кальци ). После кип чени раствор содержит сернокислый магний с незначительными примес ми сернокислого .кальци , а в осадке остаюте сернокислый кальций и непрореагировавша часть окиси магни и кальци . Аммиак выдел етс полностью в .виде газа и вновь возвращаетс в производстЕО. Полученный осадок подвергаютновой обработке.раствором,, содержащим избыток сернокислого аммони дл полного растворени окиси магни и осаждени и отчасти раствбрени (в виде комплексной, соли) сернокислого., кадьци .The interaction of dolomite calcined at temperatures of the order of 800-1OOO with a solution of ammonium sulphate simultaneously. With the formation of magnesium sulphate, complex sulphate of ammonium and magnesium, ammonium and calcium form. To dissolve all the magnesium oxide dolomite, the reaction is carried out with a significant excess of ammonium sulphate. To remove ammonia from the mixture and to increase the solubility of magnesium sulphate and complex salts, the process is carried out at elevated temperature and the mixture is boiled for 2 hours. until complete liberation of ammonia occurs. Calcium sulphate is obtained in the sediment, and iB solution is magnesium sulphate mixed with complex salts. A significant portion of ammonium sulphate remaining in solution in the form of complex salts is easily destroyed and ammonia is released when the solution separated from the precipitate is boiled with a new portion of calcined dolomite (with an excess of calcium oxide). After boiling, the solution contains magnesium sulfate with insignificant impurities of calcium sulfate, and calcium sulfate and unreacted part of magnesium oxide and calcium remain in the sediment. Ammonia is released completely in the form of gas and is returned to production. The resulting precipitate is subjected to a new treatment with a solution that contains an excess of ammonium sulphate to completely dissolve the magnesium oxide and precipitate and partly dissolve (as a complex salt) sulphate.

№ .. 2 ;No. .. 2;

Чередование указанных -проце)0сов дает полное лревращение окиси магни доломита в сернокислый магний, а окиси кальци в сернокислый кальций.The alternation of the indicated samples (cpc) gives a complete reduction of magnesia dolomite to magnesium sulphate and calcium oxides to calcium sulphate.

Конечным продуктом вл етс концентрированный раствор сернокислого магни , из которого обычными приемами выкристаллизовывают соль и порошок карбоната кальци с обычными примес ми доло1мита и гипса, но почти не содержащий окиси магни . Порошок карбоната кальци может быть использован не только дл производства извести и известково-песчаных изделий, но и дл производства цемента.The final product is a concentrated solution of magnesium sulphate, from which the salt and calcium carbonate powder with the usual admixtures of dolo-mite and gypsum, but almost free of magnesia, crystallize out. Calcium carbonate powder can be used not only for the production of lime and lime-sand products, but also for the production of cement.

Выход сульфата магни - 97°/а.The yield of magnesium sulfate is 97 ° / a.

Предмет изобретени Subject invention

Способ получени сульфата магни из доломита, отличающийс тем, что, с целью более полного превращени окиси магни доломита в сульфат магни , прокаленный доломит обрабатывают ра.стваром сульфата аммони A method of producing magnesium sulphate from dolomite, characterized in that, in order to more completely convert the magnesia dolomite to magnesium sulphate, the calcined dolomite is treated with an ammonium sulfate solution.