Известно несколько способов повышени формировани объема дермы при дублении хромовыми сол ми: увеличение расхода солей хрома при дублении, применение комплексно-активных добавок, додубливание хромовых кож растительными и синтетическими дубител ми и друтие.There are several ways to increase the formation of the volume of the dermis during tanning with chromium salts: an increase in the consumption of chromium salts during tanning, the use of complex-active additives, the retanning of chromic leathers with vegetable and synthetic tanning agents and other substances.

Все эти (Способы св заны с применением сравнительно дорогих химикатов . Предлагаемый значительно более экономичный способ необратимого формировани хромовых кож заключаетс в обработке их после дублени ИЛИ после нейтрализации концентрированными растворами солей , например сернокислого натри или аммони . Обработанный по указанному способу полуфабрикат высушивают, после чего его можно подвергать увлажнению, т жке и раст жке на рамах. После этого кожи размачивают, тщательно промывают дл удалени солей и далее отделывают обычными способами.All of these (The methods involve the use of relatively expensive chemicals. The proposed much more economical method of irreversible formation of chrome leather is to process them after tanning OR after neutralizing with concentrated solutions of salts, such as sodium sulfate or ammonium. Processed by this method, the semi-finished product is dried, after which it it can be moistened, stretched and stretched to the frames.After this, the skin is soaked, rinsed thoroughly to remove salts and then trimmed with ordinary benefits.

При этом получающеес при первой сушке обработанного сол ми полуфабриката значительное повышение формировани объема (увеличение плош.ади и толщины) сохран етс и после удалени из полуфабриката солей (промывкой) и второй сушки, т. е. вл етс необратимым. Это объ сп етс тем, что при |Сушке полуфабриката, обработанного сол ми , усадка значительно уменьшаетс благодар увеличению жесткости стенок капилл ров и вли нию кристаллизующихс в дерме солей, а происход щее параллельно с удалением влаги дополнительное дубление полуфабриката необратимо фиксирует взаимное расположение элементов .структуры полуфабриката.At the same time, a significant increase in the formation of the volume (an increase in the flat depth and thickness) obtained during the first drying of the pre-treated semi-finished product is preserved after removal of the semi-finished product (washing) and the second drying, i.e., is irreversible. This is due to the fact that during | Drying the semi-finished product treated with salts, shrinkage is significantly reduced due to an increase in the stiffness of the walls of the capillaries and the effect of salts crystallizing in the dermis, and the additional tanning of the semi-finished product that occurs in parallel with the removal of moisture permanently fixes the mutual arrangement of the elements. semi-finished product.

Предлагаемый способ особенно рекомендуетс дл производства велюра (в частности, из свиного сырь ) и дл производства меха, предусматривающих две основных сущки.The proposed method is particularly recommended for the production of velor (in particular, from pork raw materials) and for the production of fur, which provide for two main essences.

№ 119299- 2 -No. 119299-2 -

Пример. Выработка велюра из свиного .сырь .Example. Development of velor from pork.

1)Все операции до дублени и нейтрализации кожи выполн ютс по единой методике.1) All operations before tanning and neutralization of the skin are performed by a single procedure.

2)Обработка полуфабриката ведетс в растворе, например, Na2SO4. Концентраци 140-160 г/л; Ж.К. 0,5-0,7; температура 18-20°; продолжительность 2,0-2,5 часа.2) Processing of the semi-finished product is carried out in a solution, for example, Na2SO4. Concentration of 140-160 g / l; J.K. 0.5-0.7; temperature 18-20 °; Duration 2.0-2.5 hours.

3)Пролежка не менее 12 часов.3) Laying down for at least 12 hours.

4)Сушка и все последующие операции до размачивани включительно ведутс по единой методике.4) Drying and all subsequent operations until maceration, inclusive, are carried out according to a uniform procedure.

5)Промывка. Ж-К.-Ю; температура 30-35°; продолжительность 1,0-1,5 часа; вода проточна . Вращение непрерывное.5) Flushing. J-K.-Yu; temperature 30-35 °; duration 1.0-1.5 hours; water flow. Rotation is continuous.

6)Дальнейшие операции производ тс по обычной методике выработки велюра.6) Further operations are carried out according to the usual method of making velor.

При такой обработке дО|Стигаетс м гкость и эластичность кожи по всей площади, улучшаютс услови шлифовки и качество ворса, улучшаетс маскировка отверстий от щетины, сокращаетс продолжительность золени , сокращаетс расход жира.With this treatment, the softness and elasticity of the skin over the entire area is improved, the grinding conditions and the quality of the pile are improved, the masking of the holes from the bristles is improved, the length of ash is reduced, and the consumption of fat is reduced.

Предмет изобретени Subject invention

СпО|СОб необратимого формировани хромовых кож, отличающийс тем, что кожу после дублени или после нейтрализации обрабатывают концентрированными растворами солей, например сульфатами натри или аммони .SPO | COB of irreversible formation of chrome skins, characterized in that the skin after tanning or after neutralization is treated with concentrated solutions of salts, for example sodium or ammonium sulfates.