SG11201604578TA - Steel sheet hot-dip-coated with zn-al-mg-based system having excellent workability and method for manufacturing same - Google Patents

Steel sheet hot-dip-coated with zn-al-mg-based system having excellent workability and method for manufacturing same

Info

Publication number
SG11201604578TA
SG11201604578TA SG11201604578TA SG11201604578TA SG11201604578TA SG 11201604578T A SG11201604578T A SG 11201604578TA SG 11201604578T A SG11201604578T A SG 11201604578TA SG 11201604578T A SG11201604578T A SG 11201604578TA SG 11201604578T A SG11201604578T A SG 11201604578TA
Authority
SG
Singapore
Prior art keywords
dip
coated
steel sheet
based system
excellent workability
Prior art date
Application number
SG11201604578TA
Inventor
Kentarou Hirata
Shinya Uesugi
Yukio Katagiri
Masaaki Uranaka
Tomoharu Shigetomi
Original Assignee
Nisshin Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nisshin Steel Co Ltd filed Critical Nisshin Steel Co Ltd
Publication of SG11201604578TA publication Critical patent/SG11201604578TA/en

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B15/043—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/18—Layered products comprising a layer of metal comprising iron or steel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/20—Layered products comprising a layer of metal comprising aluminium or copper
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/004—Very low carbon steels, i.e. having a carbon content of less than 0,01%
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C23C30/005—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process on hard metal substrates
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/1275—Next to Group VIII or IB metal-base component
    • Y10T428/12757—Fe
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y10T428/12979—Containing more than 10% nonferrous elements [e.g., high alloy, stainless]
SG11201604578TA 2013-12-19 2014-12-19 Steel sheet hot-dip-coated with zn-al-mg-based system having excellent workability and method for manufacturing same SG11201604578TA (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013262271 2013-12-19
PCT/JP2014/083712 WO2015093596A1 (en) 2013-12-19 2014-12-19 Steel sheet hot-dip-coated with zn-al-mg-based system having excellent workability and method for manufacturing same

Publications (1)

Publication Number Publication Date
SG11201604578TA true SG11201604578TA (en) 2016-07-28

Family

ID=53402935

Family Applications (1)

Application Number Title Priority Date Filing Date
SG11201604578TA SG11201604578TA (en) 2013-12-19 2014-12-19 Steel sheet hot-dip-coated with zn-al-mg-based system having excellent workability and method for manufacturing same

Country Status (16)

Country Link
US (1) US10266910B2 (en)
EP (1) EP3085805B1 (en)
JP (1) JP6238474B2 (en)
KR (1) KR102284770B1 (en)
CN (1) CN105940131A (en)
AU (1) AU2014367679B2 (en)
BR (1) BR112016013855A2 (en)
CA (1) CA2932854C (en)
ES (1) ES2791757T3 (en)
HU (1) HUE051559T2 (en)
MX (1) MX2016007942A (en)
MY (1) MY174534A (en)
PL (1) PL3085805T3 (en)
RU (1) RU2695690C1 (en)
SG (1) SG11201604578TA (en)
WO (1) WO2015093596A1 (en)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017145441A (en) * 2016-02-16 2017-08-24 日新製鋼株式会社 Black surface coated high strength steel sheet and manufacturing method therefor
CN106521385A (en) * 2016-11-22 2017-03-22 常州大学 Two-step SuperDyma alloy hot dipping technology for structural steel
JP2018119207A (en) * 2017-01-25 2018-08-02 日新製鋼株式会社 MOLTEN Zn-Al-Mg-BASED PLATED STEEL SHEET EXCELLENT IN BURRING PROPERTY AND METHOD FOR MANUFACTURING THE SAME
JP6801496B2 (en) * 2017-02-17 2020-12-16 日本製鉄株式会社 High-strength molten Zn-Al-Mg-based plated steel sheet with excellent bending workability and its manufacturing method
JP6816550B2 (en) * 2017-02-17 2021-01-20 日本製鉄株式会社 Black surface-coated high-strength molten Zn-Al-Mg-based plated steel sheet with excellent bending workability and its manufacturing method
KR102286953B1 (en) * 2017-03-10 2021-08-06 제이에프이 스틸 가부시키가이샤 High-strength hot-rolled steel sheet
CN108796363B (en) * 2017-04-27 2020-10-27 宝山钢铁股份有限公司 High-surface-quality aluminum-coated substrate steel suitable for large deformation and stamping and production method thereof
KR102031465B1 (en) 2017-12-26 2019-10-11 주식회사 포스코 Zinc alloy coated steel having excellent corrosion resistance after forming, and method for manufacturing the same
JP6958459B2 (en) * 2018-03-29 2021-11-02 日本製鉄株式会社 Fused Zn-Al-Mg alloy plated steel sheet and its manufacturing method
WO2020026594A1 (en) 2018-07-31 2020-02-06 Ｊｆｅスチール株式会社 High-strength hot-rolled plated steel sheet
CN110273121B (en) * 2019-06-12 2021-09-21 河钢股份有限公司 Zinc-aluminum-magnesium coated steel strip and preparation method thereof
JP2021042419A (en) * 2019-09-10 2021-03-18 日本電産株式会社 Zinc alloy and method for producing the same
WO2023084926A1 (en) * 2021-11-12 2023-05-19 日本製鉄株式会社 Hot-rolled steel sheet, hot-dip plated steel sheet, and method for manufacturing hot-rolled steel sheet
EP4261309A1 (en) * 2022-04-13 2023-10-18 ThyssenKrupp Steel Europe AG Cold-rolled steel sheet product and method for producing a cold-rolled steel sheet product

Family Cites Families (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3125397B2 (en) 1991-12-26 2001-01-15 日本鋼管株式会社 Manufacturing method of high tensile alloyed hot-dip galvanized steel sheet with excellent stretch flangeability
JP4445095B2 (en) 2000-04-21 2010-04-07 新日本製鐵株式会社 Composite structure steel plate excellent in burring workability and manufacturing method thereof
JP2001303187A (en) 2000-04-21 2001-10-31 Nippon Steel Corp Dual-phase steel sheet excellent in burring property, and its manufacturing method
DE60121162T2 (en) * 2000-05-26 2006-11-09 Jfe Steel Corp. COLD-ROLLED STEEL PLATE AND GALVANIZED STEEL PLATE WITH GOOD RECOILING CHARACTERISTICS AND METHOD OF MANUFACTURING THEREOF
JP3591502B2 (en) 2001-02-20 2004-11-24 Ｊｆｅスチール株式会社 High-tensile steel sheet excellent in workability, and its manufacturing method and processing method
JP3715220B2 (en) * 2001-06-22 2005-11-09 日新製鋼株式会社 Zn-Al-Mg hot-dip galvanized steel with excellent corrosion resistance
CA2571521C (en) * 2004-06-29 2010-05-04 Corus Staal B.V. Steel sheet with hot dip galvanized zinc alloy coating and process to produce it
JP4721221B2 (en) * 2004-09-01 2011-07-13 日新製鋼株式会社 Zn-Al-Mg alloy-plated steel sheet with excellent resistance to molten metal embrittlement cracking
JP5047649B2 (en) * 2006-04-11 2012-10-10 新日本製鐵株式会社 High-strength hot-rolled steel sheet and galvanized steel sheet excellent in stretch flangeability and their production method
EP2407569A4 (en) * 2009-03-10 2017-05-10 Nisshin Steel Co., Ltd. Zinc based alloy coated steel having superior resistance to liquid metal embrittlement and cracking
JP5556186B2 (en) 2010-01-15 2014-07-23 新日鐵住金株式会社 High corrosion resistance hot-dip galvanized steel sheet
JP5641741B2 (en) * 2010-01-28 2014-12-17 日新製鋼株式会社 High strength Zn-Al-Mg plated steel sheet with excellent bendability and molten metal embrittlement resistance
JP5936390B2 (en) 2011-02-28 2016-06-22 日新製鋼株式会社 Hot-dip Zn-Al-Mg-based plated steel sheet and manufacturing method
JP5541263B2 (en) * 2011-11-04 2014-07-09 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in workability and manufacturing method thereof
JP5884472B2 (en) * 2011-12-26 2016-03-15 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in stretch flangeability and manufacturing method thereof
JP5838796B2 (en) * 2011-12-27 2016-01-06 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in stretch flangeability and manufacturing method thereof
WO2013160566A1 (en) 2012-04-25 2013-10-31 Arcelormittal Investigacion Y Desarrollo, S.L. Method for producing a metal sheet having oiled zn-al-mg coatings, and corresponding metal sheet

Also Published As

Publication number Publication date
KR102284770B1 (en) 2021-07-30
EP3085805B1 (en) 2020-02-19
EP3085805A1 (en) 2016-10-26
MY174534A (en) 2020-04-24
US20160319386A1 (en) 2016-11-03
JPWO2015093596A1 (en) 2017-03-23
CA2932854C (en) 2017-12-12
KR20160105402A (en) 2016-09-06
ES2791757T3 (en) 2020-11-05
CN105940131A (en) 2016-09-14
AU2014367679A1 (en) 2016-06-16
EP3085805A4 (en) 2017-06-28
AU2014367679B2 (en) 2019-02-14
CA2932854A1 (en) 2015-06-25
RU2016122482A (en) 2018-01-24
WO2015093596A1 (en) 2015-06-25
MX2016007942A (en) 2016-09-19
US10266910B2 (en) 2019-04-23
HUE051559T2 (en) 2021-03-29
JP6238474B2 (en) 2017-11-29
RU2695690C1 (en) 2019-07-25
BR112016013855A2 (en) 2017-08-08
PL3085805T3 (en) 2021-07-05

Similar Documents

Publication Publication Date Title
SG11201604578TA (en) Steel sheet hot-dip-coated with zn-al-mg-based system having excellent workability and method for manufacturing same
EP3040439A4 (en) Hot-rolled steel sheet and method for manufacturing same
EP3000905A4 (en) Hot-rolled steel sheet and method for manufacturing same
EP2949772A4 (en) Hot-rolled steel sheet and method for manufacturing same
PL2998414T3 (en) Hot-rolled steel sheet and manufacturing method thereof
EP3009527A4 (en) High-strength cold-rolled steel sheet and method for manufacturing same
EP3081662A4 (en) Steel sheet and method for manufacturing same
EP2998769A4 (en) Infrared-shielding sheet, method for manufacturing same, and application for same
PL2982772T3 (en) Hot-stamp-molded article, cold-rolled steel sheet, and method for manufacturing hot-stamp-molded article
PL2987884T3 (en) Hot-rolled steel sheet
EP3034641A4 (en) Ultrahigh-strength steel sheet and manufacturing method therefor
PL3072987T3 (en) High-carbon steel sheet and method for producing the same
EP2952599A4 (en) Cold-rolled steel and manufacturing method therefor
EP2980261A4 (en) Molten-al-zn-plated steel sheet and method for manufacturing same
EP2940176A4 (en) High-strength steel sheet, method for manufacturing same, high-strength molten-zinc-plated steel sheet, and method for manufacturing same
EP2980243A4 (en) High-strength steel sheet and method for manufacturing same
PL3085801T3 (en) Hot-pressed steel sheet member and method of manufacturing the same
EP2952605A4 (en) Cold-rolled steel sheet and manufacturing method therefor
ZA201505249B (en) High strength steel sheet and manufacturing method therefor
EP3020839A4 (en) High-carbon hot-rolled steel sheet and production method for same
EP2983017A4 (en) Optical sheet and method for manufacturing same
ZA201505012B (en) Method for manufacturing galvanized steel sheet
EP3000906A4 (en) Steel sheet for can, and method for manufacturing same
PL2990500T3 (en) Steel sheet
ZA201508995B (en) Galvanized steel sheet and production method therefor