RU2487092C1 - Glazing - Google Patents

Glazing Download PDF

Info

Publication number
RU2487092C1
RU2487092C1 RU2012106563/03A RU2012106563A RU2487092C1 RU 2487092 C1 RU2487092 C1 RU 2487092C1 RU 2012106563/03 A RU2012106563/03 A RU 2012106563/03A RU 2012106563 A RU2012106563 A RU 2012106563A RU 2487092 C1 RU2487092 C1 RU 2487092C1
Authority
RU
Russia
Prior art keywords
glazing
kaolin
window
borax
prepared
Prior art date
Application number
RU2012106563/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2012106563/03A priority Critical patent/RU2487092C1/en
Application granted granted Critical
Publication of RU2487092C1 publication Critical patent/RU2487092C1/en

Abstract

FIELD: construction.
SUBSTANCE: glazing contains the following components, wt %: scraps of window and/or container glass 49-50; kaolin 1-3; calcinated soda 12-15; phosphogypsum 13-15; borax 20-22. The prepared glazing charge is melted at 1000°C. The produced frit is ground, mixed, and a suspension is prepared, which is applied onto the surface of ceramic products. Baking is done at 850°C.
EFFECT: decreased temperature of glazing baking.
1 tbl

Description

Изобретение относится к технологии силикатов и касается составов глазурей для нанесения на керамические изделия, преимущественно облицовочную плитку.The invention relates to the technology of silicates and relates to compositions of glazes for application to ceramic products, mainly facing tiles.

Известна глазурь, включающая, мас.%: бой оконного и/или тарного стекла 60-90, каолин 5-20, по крайней мере, один компонент из группы: силикат натрия, метасиликат натрия, сода кальцинированная, гидроокись кадия, плав щелочей NaOH и KOH 5-20 [1].Known glaze, including, wt.%: Window and / or container glass break 60-90, kaolin 5-20, at least one component from the group: sodium silicate, sodium metasilicate, soda ash, cadmium hydroxide, alkali melt NaOH and KOH 5-20 [1].

Задача изобретения состоит в снижении температуры обжига глазури.The objective of the invention is to reduce the firing temperature of the glaze.

Технический результат достигается тем, что глазурь, включающая бой оконного и/или тарного стекла, каолин и соду кальцинированную, дополнительно содержит фосфогипс и буру при следующем соотношении компонентов, мас.%: бой оконного и/или тарного стекла 49-50; каолин 1-3; сода кальцинированная 12-15; фосфогипс 13-15; бура 20-22.The technical result is achieved in that the glaze, including the battle of window and / or container glass, kaolin and soda ash, additionally contains phosphogypsum and borax in the following ratio of components, wt.%: Battle window and / or container glass 49-50; kaolin 1-3; soda ash 12-15; phosphogypsum 13-15; borax 20-22.

В таблице приведены составы глазури.The table shows the glaze compositions.

ТаблицаTable КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 33 Бой стекла Glass break       - оконного- window 4949 2525 -- - тарного- container -- 2525 50fifty КаолинKaolin 1one 22 33 Сода кальцинированнаяSoda ash 15fifteen 1313 1212 ФосфогипсPhosphogypsum 15fifteen 1313 1313 БураBorax 20twenty 2222 2222

Глазурь получают следующим образом. Подготавливают и дозируют компоненты. Буру, фосфогипс и соду кальцинированную сплавляют при температуре 1000°С, расплав гранулируют в воду. Полученную фритту, бой оконного и/или тарного стекла и каолин по отдельности размалывают до полного прохождения через сетку №0056, смешивают и готовят суспензию с влажностью 45-50%. Готовую глазурную суспензию наносят (напылением, поливом) на поверхность керамических изделий, сушат и обжигают при температуре 850°С.Glaze is prepared as follows. The components are prepared and dosed. Borax, phosphogypsum and soda ash are fused at a temperature of 1000 ° C, the melt is granulated into water. The resulting frit, the battle of window and / or container glass and kaolin separately are ground until they pass through the mesh No. 0056, mixed and a suspension is prepared with a moisture content of 45-50%. The finished glaze suspension is applied (by spraying, watering) on the surface of ceramic products, dried and fired at a temperature of 850 ° C.

Источники информацииInformation sources

1. А.с. СССР №773031, С04В 41/00, 1980.1. A.S. USSR No. 773031, C04B 41/00, 1980.

Claims (1)

Глазурь, включающая бой оконного и/или тарного стекла, каолин и соду кальцинированную, отличающаяся тем, что дополнительно содержит фосфогипс и буру при следующем соотношении компонентов, мас.%:
бой оконного и/или тарного стекла 49-50 каолин 1-3 сода кальцинированная 12-15 фосфогипс 13-15 бура 20-22
Glaze, including the battle of window and / or container glass, kaolin and soda ash, characterized in that it additionally contains phosphogypsum and borax in the following ratio of components, wt.%:
window and / or container glass battle 49-50 kaolin 1-3 soda ash 12-15 phosphogypsum 13-15 borax 20-22
RU2012106563/03A 2012-02-22 2012-02-22 Glazing RU2487092C1 (en)