RU2184098C1 - Dry building mixture - Google Patents
Dry building mixture Download PDFInfo
- Publication number
- RU2184098C1 RU2184098C1 RU2000129789A RU2000129789A RU2184098C1 RU 2184098 C1 RU2184098 C1 RU 2184098C1 RU 2000129789 A RU2000129789 A RU 2000129789A RU 2000129789 A RU2000129789 A RU 2000129789A RU 2184098 C1 RU2184098 C1 RU 2184098C1
- Authority
- RU
- Russia
- Prior art keywords
- sand
- cement
- mixture
- fraction
- dry
- Prior art date
Abstract
Description
Изобретение относится к области строительных материалов и может быть использовано для приготовления строительных растворов и мелкозернистых бетонов. The invention relates to the field of building materials and can be used for the preparation of mortars and fine concrete.
Известна сухая цементно-песчаная смесь, включающая в мас.%: портландцемент 21-42, песок 50-75, минеральную расширяющуюся добавку "ИР-1" 4-8. Добавка представляет собой смесь вулканической породы, микрокремнезема и пластификатора (см. пат. RU 2144908 С1, кл. С 04 В 28/02, опубл. 27.01.2000). Known dry cement-sand mixture, including in wt.%: Portland cement 21-42, sand 50-75, mineral expanding additive "IR-1" 4-8. The additive is a mixture of volcanic rock, silica fume and plasticizer (see US Pat. RU 2144908 C1, CL 04 04/28, publ. 01.27.2000).
Наиболее близким аналогом к предложенному изобретению является сухая строительная смесь, содержащая в мас.ч.: цемент 45-55, песок 45-55, пластификатор на основе метилцеллюлозы и метилоксипропилцеллюлозы 0,4-0,5, смесь известковая для горных буровых работ СИГБ 0,5-2,0 (см. пат. RU 2119467, МПК С 04 В 28/02, опубл. 27.09.1998). The closest analogue to the proposed invention is a dry building mixture containing, in parts by weight: cement 45-55, sand 45-55, a plasticizer based on methyl cellulose and methoxypropyl cellulose 0.4-0.5, a lime mixture for mining drilling SIGB 0 5-2.0 (see Pat. RU 2119467, IPC C 04 B 28/02, publ. 09/27/1998).
Задачей изобретения является получение строительных растворов и мелкозернистых бетонов с повышенной прочностью и водопроницаемостью. The objective of the invention is to obtain mortars and fine concrete with increased strength and water permeability.
Поставленная задача решается тем, что сухая строительная смесь, включающая цемент, песок и метилцеллюлозу, содержит песок следующего фракционного состава в мас.%: фракция 0,14-0,315 мм - 15-33, фракция 0,315-0,63 мм - 67-85, при следующем соотношении компонентов в мас.%:
Цемент - 30-40
Песок - 60-70
Метилцеллюлоза, сверх 100% от смеси цемента и песка - 0,3-0,6
Изобретение осуществляется следующим образом. Песок фракционного состава: фракции 0,14-0,315 мм - 33 мас.% и фракции 0,315-0,63 мм - 67 мас.% смешивают с цементом марки 400 или 500 и метилцеллюлозой. После перемешивания готовую смесь упаковывают в бумажные пакеты.The problem is solved in that the dry building mixture, including cement, sand and methyl cellulose, contains sand of the following fractional composition in wt.%: Fraction 0.14-0.315 mm - 15-33, fraction 0.315-0.63 mm - 67-85 , in the following ratio of components in wt.%:
Cement - 30-40
Sand - 60-70
Cellulose, in excess of 100% of the mixture of cement and sand - 0.3-0.6
The invention is as follows. Sand of fractional composition: fractions of 0.14-0.315 mm - 33 wt.% And fractions of 0.315-0.63 mm - 67 wt.% Mixed with cement grade 400 or 500 and methyl cellulose. After mixing, the finished mixture is packaged in paper bags.
В табл.1 приведены конкретные составы описываемой сухой смеси. Table 1 shows the specific compositions of the described dry mix.
Для испытания сухой смеси готовят из указанных составов (табл.1) строительные растворы, добавляя в смеси воду в количестве в/ц = 0,4. To test the dry mixture, mortars are prepared from the indicated compositions (Table 1) by adding water in the mixture in the amount of w / c = 0.4.
Испытания производят на образцах - балочках размером 4х4х16 см, твердевших в нормальных условиях в течение 28 суток. The tests are carried out on samples - beams of size 4x4x416 cm, solidified under normal conditions for 28 days.
Полученные результаты испытаний приведены в табл.2. The obtained test results are given in table.2.
Как видно из приведенных данных, описываемая сухая строительная смесь обеспечивает получение строительных растворов и бетонов повышенной прочности и водонепроницаемости. As can be seen from the above data, the described dry mortar provides obtaining mortars and concretes of increased strength and waterproofness.
Claims (1)
Цемент - 30 - 40
Песок - 60 - 70
Метилцеллюлоза, сверх 100% от смеси цемента и песка - 0,3 - 0,6Dry building mixture, including cement, sand and methyl cellulose, characterized in that it contains sand of the following fractional composition, wt. %: fraction 0.14 - 0.315 mm - 15 - 33, fraction 0.315 - 0.63 mm - 67 - 85, with the following ratio of components, wt. %:
Cement - 30 - 40
Sand - 60 - 70
Cellulose, in excess of 100% of the mixture of cement and sand - 0.3 - 0.6