RU2184097C1

RU2184097C1 - Decorative color stucco dry mixture

Info

Publication number: RU2184097C1
Application number: RU2001120887/03A
Authority: RU
Inventors: Е.А. Прозоров; А.А. Прозоров
Original assignee: Прозоров Евгений Анатольевич; Прозоров Алексей Анатольевич
Priority date: 2001-07-26
Filing date: 2001-07-26
Publication date: 2002-06-27

Abstract

FIELD: building materials of new generation. SUBSTANCE: decorative color stucco dry mixture has, wt.%: crushed clay and washed off sand of size 0.5 mm, not above, as a filling agent, 92; rye or wheat flour as a binding agent, 6; boric acid powder, 2. Invention provides the preparing the safety decorative stucco of the high architectural expression designated for internal works. EFFECT: design of ecologically pure stucco mixture of high strength indices of building technology. 1 tbl, 1 ex

Description

Изобретение относится к области строительных материалов нового поколения, позволяющих получать надежную с высокой архитектурной выразительностью декоративную штукатурку, предназначенную для внутренних работ. The invention relates to the field of building materials of a new generation, which allows to obtain decorative plaster, reliable with high architectural expressiveness, intended for interior work.

Широко известны сухие смеси на известковом, цементном, гипсовом и комбинированном вяжущем, используемые при штукатурных работах. В состав этих смесей входят известь, кварцевый песок, цемент, гипс и различные комплексные добавки, в том числе и синтетические. С точки зрения строительной биологии применение при строительстве жилых помещений синтетических материалов должно быть минимальным, так как может вызвать различные заболевания, в том числе и раковые. (см. Лебедева Л. М. Справочник штукатура. - М.: "Высшая школа", 2000, с. 38-49). Dry mixes based on lime, cement, gypsum and a combined binder are widely known for use in plastering. The composition of these mixtures includes lime, quartz sand, cement, gypsum and various complex additives, including synthetic ones. From the point of view of construction biology, the use of synthetic materials in the construction of residential premises should be minimal, as it can cause various diseases, including cancer. (see L. Lebedeva, Plasterer Handbook. - M.: Higher School, 2000, p. 38-49).

Ближайшим из аналогов является декоративная цветная сухая штукатурная сухая смесь, содержащая вяжущее, минеральный заполнитель-песок (см. RU 2122532, опубл. 27.12.1998)
Технической задачей изобретения является создание экологически чистой штукатурной смеси с высокими прочностными характеристиками и удовлетворяющей критериям строительной биологии.The closest of the analogues is a decorative colored dry plaster dry mix containing a binder, mineral aggregate-sand (see RU 2122532, publ. 12/27/1998)
An object of the invention is the creation of an environmentally friendly plaster mixture with high strength characteristics and satisfying the criteria of building biology.

Указанная техническая задача достигается тем, что цветная декоративная штукатурная сухая смесь, включающая вяжущее и минеральный заполнитель - песок, в качестве вяжущего содержит просеянную ржаную или пшеничную муку, а минеральный заполнитель содержит отмытый песок крупностью не более 5 мм и дополнительно глиняный порошок, причем декоративная цветная штукатурная сухая смесь дополнительно содержит порошок борной кислоты при следующем соотношении компонентов, мас.%:
Указанный заполнитель - 92
Указанное вяжущее - 6
Порошок борной кислоты - 2
Сопоставительный анализ заявленного состава с аналогами показывает, что он отличается, во-первых, применением в качестве вяжущего ржаной или пшеничной муки, а в качестве антисептика - борной кислоты, а, во-вторых, процентным соотношением компонентов, образующих декоративную цветную штукатурную сухую смесь, что позволяет сделать вывод о ее новизне.The specified technical problem is achieved by the fact that the colored decorative plaster dry mix, including binder and mineral aggregate - sand, contains as a binder sifted rye or wheat flour, and the mineral aggregate contains washed sand with a grain size of not more than 5 mm and additionally clay powder, and decorative colored the dry plaster mixture further comprises boric acid powder in the following ratio of components, wt.%:
Specified Placeholder - 92
Specified Binder - 6
Boric Acid Powder - 2
A comparative analysis of the claimed composition with analogs shows that it differs, firstly, in the use of rye or wheat flour as a binder, and as an antiseptic - boric acid, and, secondly, in the percentage of components that form a decorative colored plaster dry mix, which allows us to conclude about its novelty.

Сравнение заявленного состава с аналогичными по назначению защитными покрытиями показывает, что предложенный состав обладает высокими прочностными характеристиками. Comparison of the claimed composition with similar purpose protective coatings shows that the proposed composition has high strength characteristics.

Состав приготавливается следующим образом. В работающий бетоно- или растворосмеситель загружают отмытый песок с крупностью не более 0,5 мм, просеянную муку, глиняный порошок, порошок борной кислоты и хорошо перемешивают до получения однородной массы. Приготовленную смесь расфасовывают в бумажные пакеты или пластмассовые ведра. The composition is prepared as follows. In a working concrete or mortar mixer, washed sand with a grain size of not more than 0.5 mm, sifted flour, clay powder, boric acid powder are loaded and mixed well until a homogeneous mass is obtained. The prepared mixture is packaged in paper bags or plastic buckets.

Перед применением в декоративную цветную штукатурную сухую смесь добавляют необходимое количество воды, тщательно перемешивают, оставляют на 15 мин и после повторного перемешивания наносят на подготовленную загрунтованную поверхность. Толщина нанесенного слоя штукатурки не должная превышать 3 мм. Цвет штукатурки зависит от цвета глины. Before use, the required amount of water is added to the decorative colored stucco dry mixture, mixed thoroughly, left for 15 minutes and, after repeated mixing, applied to the prepared primed surface. The thickness of the applied layer of plaster should not exceed 3 mm. The color of the plaster depends on the color of the clay.

Пример. Готовят несколько составов декоративной цветной штукатурной смеси (см. таблицу). Example. Prepare several compositions of decorative colored stucco mixture (see table).

Оптимальным составом является состав II декоративной цветной штукатурной сухой смеси, который показал максимальную прочность. The optimal composition is composition II of decorative colored plaster dry mix, which showed maximum strength.

Claims

Decorative colored plaster dry mix, including binder and mineral aggregate - sand, characterized in that sifted rye or wheat flour is used as the binder, and the mineral aggregate contains washed sand with a grain size of not more than 0.5 mm and additionally clay powder, moreover, decorative colored plaster the dry mixture additionally contains boric acid powder in the following ratio of components, wt. %:
Specified Binder - 6
Specified Placeholder - 92
Boric Acid Powder - 2