RU2138567C1 - Gold recovery method

Info

Publication number: RU2138567C1
Application number: RU98109925A
Authority: RU
Inventors: С.И. Лолейт; Ю.М. Калмыков; В.Я. Давыдова; О.В. Агафонов
Original assignee: Щелковский завод вторичных драгоценных металлов
Priority date: 1998-05-25
Filing date: 1998-05-25
Publication date: 1999-09-27

Abstract

FIELD: gold recovery. SUBSTANCE: gold- containing molybdenum-based parts are treated with hydrofluoric acid and then with urea. Resulting solution is treated with copper powder to precipitate gold and form pulp, from which gold is filtered off together with other insoluble materials, mainly molybdenic acid. Precipitate is then treated with water and 10% sodium hydroxide solution to dissolve molybdenic acid, after which gold slurry on filter is washed with water, dehydrated, and melted. EFFECT: increased degree of recovery and reduced expenses.

Description

Изобретение касается излечения благородных металлов из отходов, в частности из позолоченных деталей, содержащих молибден. The invention relates to the treatment of precious metals from waste, in particular from gold-plated parts containing molybdenum.

Позолоченные детали, в основу которых входит молибден, представляют собой различные изделия-болты, проволока, стаканы, сетка и т.д. Содержание золота в них от 1,5-5,0%. Gold-plated parts, which are based on molybdenum, are various products-bolts, wire, glasses, mesh, etc. The gold content in them is from 1.5-5.0%.

Известен способ извлечения металла, включающий шихту, содержащую золото, молибден и др. металлы платиновой группы и их сочетания, которую обрабатывают смесью нитрата аммония и серной кислоты при температуре 105^oC и выше /заявка РСТ N 92/15713, кл. C 22 B 3/08, 1992 - аналог/.A known method of extracting metal, including a mixture containing gold, molybdenum and other metals of the platinum group and their combinations, which is treated with a mixture of ammonium nitrate and sulfuric acid at a temperature of 105 ^o C and above / PCT application N 92/15713, class. C 22 B 3/08, 1992 - analogue /.

Недостатком указанного способа является то, что полученный нерастворимый осадок является обогащенным продуктом по драгметаллам, содержащим труднорастворимые металлы, в том числе и молибден, отрицательное влияние которого будет сказываться при извлечении драгметаллов из нерастворимого осадка. The disadvantage of this method is that the resulting insoluble precipitate is an enriched precious metal product containing sparingly soluble metals, including molybdenum, the negative effect of which will be affected by the extraction of precious metals from insoluble precipitate.

Наиболее близким по технической сущности к изобретению является способ извлечения золота из материала, содержащего молибден, включающий обработку исходного материала раствором, содержащим иодистый водород, иод и воду, и осаждение золота /патент США N 4397690, кл. C 22 B 11/00, 1983 - прототип/. Closest to the technical nature of the invention is a method of extracting gold from a material containing molybdenum, comprising treating the starting material with a solution containing hydrogen iodide, iodine and water, and the precipitation of gold / US patent N 4397690, CL. C 22 B 11/00, 1983 - prototype.

Недостатком данного способа является дороговизна реактивов иода и иодистого калия, неполное извлечение золота в раствор, длительный процесс растворения и сложность извлечения золота из полученных растворов, с последующим аффинированием его. The disadvantage of this method is the high cost of the reagents of iodine and potassium iodide, incomplete extraction of gold into the solution, a long dissolution process and the difficulty of extracting gold from the resulting solutions, followed by refining it.

Техническим результатом изобретения является получение золота более дешевым способом и с высокой степенью извлечения. The technical result of the invention is to obtain gold in a cheaper way and with a high degree of extraction.

Технический результат достигается за счет того, что способ извлечения золота, включающий обработку исходного материала и осаждение золота, причем в качестве исходного материала используют золотосодержащее сырье на молибденовой основе, обработку которого ведут раствором царской водки, полученный золотосодержащий раствор обрабатывают карбамидом с последующим отделением осадка фильтрацией и промывкой его, затем объединяют промывные воды с золотосодержащим раствором, полученный раствор обрабатывают медным порошком с дальнейшим осаждением золота, из полученной пульпы, содержащей золото и молибденовую кислоту, отфильтровывают нерастворимый осадок, в основном золотой шлам с молибденовой кислотой, затем осадок промывают водой и 10% раствором едкого натрия, при этом молибденовая кислота растворяется и переходит в раствор в виде молибдата натрия, а золотой шлам на фильтре промывают водой, обезвоживают и плавят. The technical result is achieved due to the fact that the method of gold extraction, including processing of the starting material and the deposition of gold, moreover, as the starting material using gold-containing raw materials on a molybdenum basis, the processing of which is carried out with a solution of aqua regia, the resulting gold-containing solution is treated with carbamide, followed by separation of the precipitate by filtration and washing it, then washing water is combined with a gold-containing solution, the resulting solution is treated with copper powder with further precipitation gold, from the obtained pulp containing gold and molybdenum acid, an insoluble precipitate is filtered out, mainly the gold slurry with molybdenum acid, then the precipitate is washed with water and 10% sodium hydroxide solution, while the molybdenum acid dissolves and passes into the solution in the form of sodium molybdate, and the golden slurry on the filter is washed with water, dehydrated and melted.

Пример осуществления способа. An example implementation of the method.

Исходное сырье загружают в реактор, туда же подают царскую водку и ведут процесс растворения до полного прекращения реакции, при этом протекают следующие реакции:

Золото и другие металлы растворяются, в то время как серебро в форме AgCl и керамика образуют нерастворимый остаток, а молибден в виде молибденовой кислоты находится в растворе в гелеобразном состоянии.The feedstock is loaded into the reactor, aqua regia is also fed therein and the dissolution process is carried out until the reaction is completely stopped, while the following reactions proceed:

Gold and other metals dissolve, while silver in the form of AgCl and ceramics form an insoluble residue, and molybdenum in the form of molybdenum acid is in a gel state in solution.

К золотосодержащему раствору небольшими порциями при перемешивании добавляют раствор карбамида /мочевины/ для связывания азотной кислоты. A urea / urea / solution for binding nitric acid is added in small portions with stirring to the gold-containing solution.

Co(NH₂)₂ + HNO₃ ---> Co(NH₂)₂ + HNO₃.Co (NH ₂ ) ₂ + HNO ₃ ---> Co (NH ₂ ) ₂ + HNO ₃ .

Золотосодержащий раствор отделяют от нерастворимого остатка, который промывают водой, а промывные воды объединяют с золотосодержащим раствором, который сливают в емкости для осаждения золота. The gold-containing solution is separated from the insoluble residue, which is washed with water, and the wash water is combined with a gold-containing solution, which is poured into a vessel for the deposition of gold.

Золото осаждают из раствора, в котором находится молибденовая кислота H₂MoO₄, медным порошком:
2HAuCl₄ + 3Cu ---> 2CuCl₂ + 2HCl.Gold is precipitated from the solution in which the molybdenum acid H ₂ MoO _{4 is located} , with copper powder:
2HAuCl ₄ + 3Cu ---> 2CuCl ₂ + 2HCl.

Пульпу, содержащую золото и молибденовую кислоту, сливают на нутч-фильтр, отделяют фильтрат и промывают золотой шлам с молибденовой кислотой до нейтральной реакции, а затем промывают еще и 10% раствором едкого натрия, при этом молибденовая кислота растворяется и переходит в раствор в виде молибдата натрия,
H₂[MoO₄] + 2NaOH ---> Na₂MoO₄ + 2H₂O,
а золотой шлам промывают водой до нейтральной реакции, обезвоживают его, выгружают на нутч-фильтр и плавят.The pulp containing gold and molybdenum acid is poured onto a suction filter, the filtrate is separated and the gold sludge with molybdenum acid is washed until neutral, and then washed with another 10% sodium hydroxide solution, while the molybdenum acid dissolves and passes into the solution in the form of molybdate sodium
H ₂ [MoO ₄ ] + 2NaOH ---> Na ₂ MoO ₄ + 2H ₂ O,
and the gold sludge is washed with water until neutral, dehydrated, discharged to a suction filter and melted.

Claims

A method of extracting gold, including processing the initial gold-containing material on a molybdenum base with a reagent solution and precipitating gold from the solution, characterized in that the treatment is carried out with a solution of aqua regia, the obtained gold-containing solution is treated with urea, followed by separation of the precipitate by filtration and washing it, then the washing water is combined with the gold-containing solution, the resulting solution is treated with copper powder with a further deposition of gold from the resulting pulp containing gold and molybdenum hydrochloric acid, an insoluble precipitate is filtered off, mainly gold sludge with molybdenum acid, washed with water and 10% sodium hydroxide solution, while molybdenum acid dissolves and passes into the solution in the form of sodium molybdate, and the gold sludge on the filter is washed with water, dehydrated and melt.