RU2116273C1 - Guard structure of light-weight concrete and concrete mix - Google Patents

Guard structure of light-weight concrete and concrete mix Download PDF

Info

Publication number
RU2116273C1
RU2116273C1 RU94034775A RU94034775A RU2116273C1 RU 2116273 C1 RU2116273 C1 RU 2116273C1 RU 94034775 A RU94034775 A RU 94034775A RU 94034775 A RU94034775 A RU 94034775A RU 2116273 C1 RU2116273 C1 RU 2116273C1
Authority
RU
Russia
Prior art keywords
concrete
cement
fractions
mixture
water
Prior art date
Application number
RU94034775A
Other languages
Russian (ru)
Other versions
RU94034775A (en
Inventor
Вячеслав Наумович Ярмаковский
Светлана Александровна Подмазова
Александр Михайлович Тропин
Андрей Анатольевич Еремичев
Валентин Павлович Скосарь
Людмила Владимировна Дрига
Original Assignee
Вячеслав Наумович Ярмаковский
Светлана Александровна Подмазова
Александр Михайлович Тропин
Андрей Анатольевич Еремичев
Валентин Павлович Скосарь
Людмила Владимировна Дрига
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Вячеслав Наумович Ярмаковский, Светлана Александровна Подмазова, Александр Михайлович Тропин, Андрей Анатольевич Еремичев, Валентин Павлович Скосарь, Людмила Владимировна Дрига filed Critical Вячеслав Наумович Ярмаковский
Priority to RU94034775A priority Critical patent/RU2116273C1/en
Publication of RU94034775A publication Critical patent/RU94034775A/en
Application granted granted Critical
Publication of RU2116273C1 publication Critical patent/RU2116273C1/en

Abstract

FIELD: construction; concrete guard structures. SUBSTANCE: guard structure is made of concrete mix with fillers possessing absorption-desorption properties. Concrete mix contains cement, coarse filler with fractions sizing 5-10 and 10-20 mm, fine filler with fractions of 0.15-5 mm. The latter is used in the form of waste of mineral wool production or its mixture with quartz sand and active mineral additive in the form of finely ground above-mentioned waste with specific surface of 1500-2000 sq.cm/g and water. Concrete mix may additionally contain air-entraining additive to impart moderate porosity to mix and its simultaneous plasticization. Mechanical and physical characteristics of concrete: temper strength after heat treatment, 4.21-7.56 MPa; strength after heat treatment, 4.21-7.56 MPa; strength after 28 days of normal wet hardening (brand), 5.81-10.61 MPa; brand by frost resistance G 50-G, 100; heat conductivity coefficient in dry state, 0.26-0.36 W/mC. EFFECT: higher efficiency. 2 cl

Description

Изобретение относится к производству ограждающих конструкций из легкого бетона и может быть использовано для изготовления стеновых изделий и конструкций, применяемых в жилищном, гражданском, промышленном и сельскохозяйственном строительстве. The invention relates to the production of walling made of light concrete and can be used for the manufacture of wall products and structures used in housing, civil, industrial and agricultural construction.

Известна ограждающая конструкция из легкого бетона, выполненная из бетонной смеси с обжиговыми пористыми заполнителями из вспученной глины, обладающими абсорбционно-адсорбционными свойствами, включающей цемент, крупный пористый заполнитель фракций 5-10 и 10-20 мм, мелкий заполнитель фракции 0,15-5 мм и воду [1]. Known enclosing structure of lightweight concrete, made of concrete mixture with calcined porous aggregates of expanded clay, with absorption and adsorption properties, including cement, large porous aggregate fractions 5-10 and 10-20 mm, fine aggregate fractions 0.15-5 mm and water [1].

Изготовление таких конструкций требует больших затрат природных минеральных ресурсов и особенно значительных энергетических затрат. The manufacture of such structures requires large expenditures of natural mineral resources and especially significant energy costs.

Известна легкобетонная смесь для изготовления стеновых изделий и конструкций, содержащая следующие компоненты, мас.%: цемент 8,0-20,0; заполнитель крупный и мелкий (керамзит и песок) 64-85; воздухововлекающая добавка - смола древесная омыленная 0,002-0,06; вода остальное [2]. Изготовление таких изделий и конструкций так же, как в первом примере, требует значительных затрат природных минеральных ресурсов, больших материальных и энергетических затрат. Known lightweight concrete mixture for the manufacture of wall products and structures, containing the following components, wt.%: Cement 8,0-20,0; coarse and fine aggregate (expanded clay and sand) 64-85; air-entraining additive - saponified wood resin 0.002-0.06; water the rest [2]. The manufacture of such products and structures, as in the first example, requires significant costs of natural mineral resources, large material and energy costs.

Аналогом изобретения является легкобетонная смесь, включающая следующие компоненты, мас.%: цемент 22,6-22,8; крупный пористый заполнитель - керамзит 31,1-44,3; мелкий заполнитель - кварцевый песок 30,6-43,7; воздухововлекающая добавка - ЦНИПС-1 0,022-0,4; вода остальное [3]. Прочность бетона в 28 сут. нормально-влажностного твердения (НВТ) составляет 3,9-8,3 МПа, плотность бетона в сухом состоянии 1105-1150 кг/м3, коэффициент теплопроводности в сухом состоянии по СНиП П-3-75 [4] 0,37-0,39 Вт/мoC, морозостойкость F50-F75.An analogue of the invention is a lightweight concrete mixture comprising the following components, wt.%: Cement 22.6-22.8; large porous aggregate - expanded clay 31.1-44.3; fine aggregate - quartz sand 30.6-43.7; air-entraining additive - TsNIPS-1 0,022-0,4; water the rest [3]. The strength of concrete in 28 days. normal moisture curing (NVT) is 3.9-8.3 MPa, the density of concrete in the dry state is 1105-1150 kg / m 3 , the coefficient of thermal conductivity in the dry state according to SNiP P-3-75 [4] 0.37-0 , 39 W / m o C, frost resistance F50-F75.

Бетон из этой смеси характеризуется относительно высоким требуемым расходом цемента, высокими коэффициентом теплопроводности и энергоемкостью, значительной потребностью в природных сырьевых ресурсах. Concrete from this mixture is characterized by a relatively high required cement consumption, high coefficient of thermal conductivity and energy intensity, a significant demand for natural raw materials.

Известна бетонная смесь, содержащая, мас. %: портландцемент 12-22; "корольки" - отход производства шлаковой ваты из стабилизированных основных и нераспадающихся кислых доменных шлаков 48-55; золуунос 15-20; маточный щелок уксусного производства 3-5; сульфатно-дрожжевую бражку 0,035-0,445; воду остальное [5]. По показателю теплопригодности бетоны, изготовленные из такой смеси, не удовлетворяют требованиям, предъявляемым к легким бетонам для стеновых изделий и конструкций. Known concrete mixture containing, by weight. %: Portland cement 12-22; "Kings" - a waste of slag wool production from stabilized basic and non-decaying acid blast furnace slags 48-55; zoluunos 15-20; uterine liquor of vinegar production 3-5; sulphate-yeast mash 0.035-0.445; water the rest [5]. In terms of heat suitability, concrete made from such a mixture does not meet the requirements for lightweight concrete for wall products and structures.

Наиболее близким аналогом изобретению является ограждающая конструкция из легкого бетона, выполненная из бетонной смеси с заполнителями, обладающими абсорбционно-адсорбционными свойствами, включающая цемент, воду, крупный пористый заполнитель - керамзит фракции 4-25 мм и мелкий заполнитель из вспененного неорганического материала в виде частиц с гладкой поверхностью шарообразной или эллипсоидной формы фракции 0,1-4,0 мм и насыпной плотностью 0,15 ± 0,10 кг/дм3 [6]. Бетоны из этой смеси обладают достаточно высокими показателями качества, в т.ч. низкой плотностью и теплопроводностью. Однако применяемые здесь и крупный, и мелкий заполнитель требуют значительных энергозатрат на приготовление и имеют высокую себестоимость.The closest analogue of the invention is a lightweight concrete enclosure made of concrete mix with aggregates having absorption and adsorption properties, including cement, water, a large porous aggregate - expanded clay fraction 4-25 mm and a fine aggregate of foamed inorganic material in the form of particles with a smooth surface of a spherical or ellipsoidal shape of a fraction of 0.1-4.0 mm and a bulk density of 0.15 ± 0.10 kg / dm 3 [6]. Concretes from this mixture have fairly high quality indicators, including low density and thermal conductivity. However, both large and small aggregates used here require significant energy consumption for preparation and have a high cost.

Изобретение направлено на создание ограждающих конструкций с высоким термическим сопротивлением, обеспечивающим повышение уровня тепловой защиты зданий за счет использования легких бетонов, низкой теплопроводности и при этом на экономию природных сырьевых и энергетических ресурсов, на расширение сырьевой базы для изготовления бетонной смеси и снижение себестоимости ее изготовления за счет рационального использования отходов промышленности. The invention is aimed at creating enclosing structures with high thermal resistance, providing an increase in the level of thermal protection of buildings through the use of light concrete, low thermal conductivity and at the same time saving natural raw materials and energy resources, expanding the raw material base for the production of concrete mix and reducing the cost of its manufacture for account of the rational use of industrial waste.

Технический результат достигается за счет того, что ограждающие конструкции из легкого бетона выполнены из бетонной смеси с заполнителями, обладающими абсорбционно-адсорбционными свойствами, и содержащей цемент, крупный пористый заполнитель фракций 5-10 и 10-20 мм, мелкий заполнитель фракций 0,15-5 мм, в качестве которого использован отход минераловатного производства - "королек" или его смесь с кварцевым песком в соотношении соответственно от 1: 0,1 до 1:1, а также активную минеральную добавку, в качестве которой используется молотый до удельной поверхности 1500-2000 см2/г "королек" и воду. Бетонная смесь может дополнительно содержать воздухововлекающую добавку в количестве 0,02-1,0 мас.% от массы цемента. Такая бетонная смесь может содержать в объемных единицах (1 м3 на 1 м3 бетона):
Цемент - 0,125-0,168
Крупный пористый заполнитель фр. 5-10 мм - 0,38-0,43
фр. 10-20 мм - 0,58-0,62
Мелкий заполнитель фракции 0,15-5 мм в виде "королька" или его смеси с кварцевым песком - 0,2-0,28
Тонкомолотый "королек" с удельной поверхностью 1500-2000 см2/г - 0,06-0,081
Вода - 0,16-0,198
Отличается бетонная смесь от прототипа тем, что с целью использования в ней менее энергоемкого и более дешевого мелкого заполнителя и при этом с относительно низкой теплопроводностью, она содержит в качестве него "королек", имеющий специфический фазовый состав, или его смесь с кварцевым песком, а с целью снижения объемной концентрации цементного камня, а следовательно, и теплопроводности бетона - активную минеральную добавку с аморфизированной структурой, в качестве которой содержится тот же "королек", имеющий высокое содержание CaO (38-46%) и молотый до удельной поверхности 1500-2000 см2/г.The technical result is achieved due to the fact that the enclosing structures of lightweight concrete are made of concrete mix with aggregates having absorption and adsorption properties and containing cement, large porous aggregate fractions 5-10 and 10-20 mm, fine aggregate fractions 0.15- 5 mm, which is used mineral wool production waste - “Korolek” or its mixture with quartz sand in a ratio of 1: 0.1 to 1: 1, respectively, as well as an active mineral additive, which is used as a ground to specific overhnosti 1500-2000 cm 2 / g "bead" and water. The concrete mixture may additionally contain an air-entraining additive in an amount of 0.02-1.0 wt.% By weight of cement. Such a concrete mixture may contain in volume units (1 m 3 per 1 m 3 concrete):
Cement - 0.125-0.168
Large porous aggregate fr. 5-10 mm - 0.38-0.43
fr. 10-20 mm - 0.58-0.62
Fine aggregate fraction 0.15-5 mm in the form of a "king" or its mixture with quartz sand - 0.2-0.28
Fine-ground "korolek" with a specific surface of 1500-2000 cm 2 / g - 0.06-0.081
Water - 0.16-0.198
The concrete mix differs from the prototype in that, in order to use a less energy-intensive and cheaper fine aggregate in it and at the same time with relatively low thermal conductivity, it contains as it is a “bead” having a specific phase composition, or its mixture with quartz sand, and in order to reduce the volume concentration of cement stone, and therefore the thermal conductivity of concrete, an active mineral additive with an amorphized structure, the quality of which contains the same “bead” having a high CaO content (38-46%) and ground to a specific surface of 1500-2000 cm 2 / g

Осуществление изобретения. The implementation of the invention.

Для приготовления бетонной смеси используют: портландцемент (ПЦ 400 Д20) или шлакопортландцемент (ШПЦ 400), крупный пористый заполнитель (ГОСТ 9757), мелкий заполнитель - отход минераловатного производства - "королек", кварцевый песок (ГОСТ 8735); активную минеральную добавку в виде тонкомолотого "королька" с удельной поверхностью 1500-2000 см2/г. Содержание основных окислов в "корольке", мас. %: SiO2 37-44; FeO 0,19-1,32; Al2O3 6,5-10,4; CaO 38-46; MgO 5,2-10,4.To prepare the concrete mixture use: Portland cement (ПЦ 400 Д20) or slag Portland cement (ШПЦ 400), coarse porous aggregate (GOST 9757), fine aggregate - waste from mineral wool production - “korolek”, quartz sand (GOST 8735); active mineral additive in the form of a finely ground "king" with a specific surface of 1500-2000 cm 2 / g The content of basic oxides in the "king", wt. %: SiO 2 37-44; FeO 0.19-1.32; Al 2 O 3 6.5-10.4; CaO 38-46; MgO 5.2-10.4.

Бетонную смесь готовят обычным способом на стандартном оборудовании. В воду затворения могут быть введены любые воздухововлекающие добавки, например смола древесная омыленная по ТУ 13-05-02-83 в количестве 0,24-0,3 мас.% от массы цемента. The concrete mixture is prepared in the usual way on standard equipment. Any air-entraining additives can be introduced into the mixing water, for example, wood saponified resin according to TU 13-05-02-83 in the amount of 0.24-0.3 wt.% By weight of cement.

Конкретные примеры приведены в табл. 1 и 2. В табл. 1 приведены составы бетонной смеси, а в табл. 2 - свойства полученного бетона. Испытания образцов на прочность проводились по ГОСТ 10180, на морозостойкость по ГОСТ 10060, на теплопроводность по ГОСТ 7076. Specific examples are given in table. 1 and 2. In the table. 1 shows the composition of the concrete mixture, and in table. 2 - properties of the resulting concrete. Strength tests of the samples were carried out according to GOST 10180, frost resistance according to GOST 10060, thermal conductivity according to GOST 7076.

Представленные примеры составной бетонной смеси проверены на практике. Presented examples of composite concrete are tested in practice.

Claims (2)

1. Ограждающая конструкция из легкого бетона, выполненная из бетонной смеси с заполнителями, обладающими абсорбционно-адсорбционными свойствами, включающей цемент, крупный пористый заполнитель фракции 5 - 10 и 10 - 20 мм, мелкий заполнитель фракции 0,15 - 5,0 мм и воду, отличающаяся тем, что бетонная смесь дополнительно содержит тонкомолотый отход минераловатного производства - "королек" с удельной поверхностью 1500 - 2000 см2/г, в качестве мелкого заполнителя - "королек" или смесь кварцевого песка и "королька" в соотношении соответственно от 1 : 0,1 до 1 : 1 при следующем соотношении компонентов бетонной смеси в объемных единицах, м3 на 1 м3 бетона:
Цемент - 0,125 - 0,168
Крупный пористый заполнитель фракции 5 - 10 мм - 0,38 - 0,43
фракции 10 - 20 мм - 0,58 - 0,62
Мелкий заполнитель - 0,2 - 0,28
Тонкомолотый "королек" с удельной поверхностью 1500 - 2000 см2/г - 0,06 - 0,081
Вода - 0,16 - 0,198
при этом бетонная смесь дополнительно содержит воздухововлекающую добавку в количестве 0,02 - 1,0 мас.% от массы цемента.1. The enclosing structure of lightweight concrete, made of concrete mixture with aggregates with absorption and adsorption properties, including cement, large porous aggregate fractions of 5 - 10 and 10 - 20 mm, fine aggregate fractions of 0.15 - 5.0 mm and water , characterized in that the concrete mixture additionally contains a finely ground waste of mineral wool production - “korolek” with a specific surface of 1500 - 2000 cm 2 / g, as a fine aggregate - “korolek” or a mixture of quartz sand and “korolka” in a ratio of 1, respectively: 0.1 to 1: 1 p In the following ratio of the components of the concrete mixture in volume units, m 3 per 1 m 3 of concrete:
Cement - 0.125 - 0.168
Coarse porous aggregate fraction 5 - 10 mm - 0.38 - 0.43
fractions 10 - 20 mm - 0.58 - 0.62
Fine aggregate - 0.2 - 0.28
Fine-ground "kinglet" with a specific surface of 1500 - 2000 cm 2 / g - 0.06 - 0.081
Water - 0.16 - 0.198
while the concrete mixture additionally contains an air-entraining additive in an amount of 0.02 - 1.0 wt.% by weight of cement. 2. Бетонная смесь с заполнителями, обладающими абсорбционно-адсорбционными свойствами, включающая цемент, крупный пористый заполнитель фракции 5 - 10 мм и 10 - 20 мм, мелкий заполнитель фракции 0,15 - 5,0 мм и воду, отличающаяся тем, что она дополнительно содержит тонкомолотый отход минераловатного производства - "королек" с удельной поверхностью 1500 - 2000 см2/г в качестве мелкого заполнителя - "королек" или смесь кварцевого песка и "королька" в соотношении соответственно от 1 : 0,1 до 1 : 1 при следующем соотношении компонентов бетонной смеси в объемных единицах, м3 на 1 м3 бетона:
Цемент - 0,125 - 0,168
Крупный пористый заполнитель фракции 5 - 10 мм - 0,38 - 0,43
фракции 10 - 20 мм - 0,58 - 0,60
Мелкий заполнитель - 0,2 - 0,28
Тонкомолотый "королек" с удельной поверхностью 1500 - 2000 см2/г - 0,06 - 0,081
Вода - 0,16 - 0,198
при этом бетонная смесь дополнительно содержит воздухововлекающую добавку в количестве 0,02 - 1,0 мас.% от массы цемента.2. Concrete mixture with aggregates having absorption and adsorption properties, including cement, coarse porous aggregate fraction 5 - 10 mm and 10 - 20 mm, fine aggregate fraction 0.15 - 5.0 mm and water, characterized in that it additionally contains finely ground waste of mineral wool production - “korolek” with a specific surface of 1500 - 2000 cm 2 / g as a fine aggregate - “korolek” or a mixture of quartz sand and “korolka” in a ratio of 1: 0.1 to 1: 1, respectively, in the following the ratio of the components of the concrete mixture in volume units itsah m 3 to 1 m 3 concrete:
Cement - 0.125 - 0.168
Coarse porous aggregate fraction 5 - 10 mm - 0.38 - 0.43
fractions 10 - 20 mm - 0.58 - 0.60
Fine aggregate - 0.2 - 0.28
Fine-ground "kinglet" with a specific surface of 1500 - 2000 cm 2 / g - 0.06 - 0.081
Water - 0.16 - 0.198
while the concrete mixture additionally contains an air-entraining additive in an amount of 0.02 - 1.0 wt.% by weight of cement.
RU94034775A 1994-09-20 1994-09-20 Guard structure of light-weight concrete and concrete mix RU2116273C1 (en)