RU2181707C2 - Composition for manufacture of light-concrete products - Google Patents
Composition for manufacture of light-concrete products Download PDFInfo
- Publication number
- RU2181707C2 RU2181707C2 RU2000106808A RU2000106808A RU2181707C2 RU 2181707 C2 RU2181707 C2 RU 2181707C2 RU 2000106808 A RU2000106808 A RU 2000106808A RU 2000106808 A RU2000106808 A RU 2000106808A RU 2181707 C2 RU2181707 C2 RU 2181707C2
- Authority
- RU
- Russia
- Prior art keywords
- composition
- water
- manufacture
- light
- sand
- Prior art date
Abstract
Description
Предлагаемый состав относится к строительным материалам и может быть использован для производства легких бетонов. The proposed composition relates to building materials and can be used for the production of light concrete.
Известна сырьевая смесь для изготовления легкого бетона, включающая вяжущее, крупный и мелкий пористые шлаковые заполнители, порообразователь и воду, а в качестве порообразователя содержит пенополистирол фракции не более 0,4 мм, полученный обработкой сопутствующего пылевидного продукта полистирола, вспененного в кипящем 5%-ном водном растворе лигносульфоната технического при следующем соотношении компонентов, мас.%: шлакопортландцемент 11,4-12,4; крупный пористый шлаковый заполнитель - шлакопемзовый щебень фракции 5-20 мм - 51,6-51,7; мелкий пористый шлаковый заполнитель - шлакопемзовый песок фракции до 5 мм - 20,7-22,7; полистирол фракции не более 0,4 мм, полученный обработкой сопутствующего пылевидного продукта полистирола, вспененного в кипящем 5%-ном водном растворе лигносульфоната технического - 4,1-6,2; вода - остальное (авт. св. 1636386, С 04 В 28/08, 1991). A known raw material mixture for the manufacture of lightweight concrete, including binder, coarse and fine porous slag aggregates, a blowing agent and water, and as a blowing agent contains polystyrene fractions of a fraction of not more than 0.4 mm obtained by processing an accompanying dusty product polystyrene foamed in boiling 5% an aqueous solution of technical lignosulfonate in the following ratio of components, wt.%: slag Portland cement 11.4-12.4; large porous slag aggregate - slag pumice gravel fraction 5-20 mm - 51.6-51.7; fine porous slag aggregate - slag pumice sand fractions up to 5 mm - 20.7-22.7; polystyrene fractions of not more than 0.4 mm obtained by processing an accompanying dusty product of polystyrene foamed in a boiling 5% aqueous solution of technical lignosulfonate - 4.1-6.2; water - the rest (ed. St. 1636386, С 04 В 28/08, 1991).
Недостатком этой смеси является низкая прочность готовых изделий, высокая плотность бетона. The disadvantage of this mixture is the low strength of the finished product, the high density of concrete.
Известен состав для изготовления легкобетонных изделий, включающий цемент, полистирольный заполнитель ПВГ-ПП, комплексную добавку, которая содержит в том числе технические лигносульфоната и пенообразователь ПО-1 и воду при следующем содержании компонентов, мас. %: цемент 64,5-68,8; полистирольный заполнитель 1,2-1,9; комплексная добавка 0,15-0,55 (патент РФ 2143413, С 04 В 38/10, 1999). A known composition for the manufacture of lightweight concrete products, including cement, polystyrene aggregate PVG-PP, a complex additive that contains, including technical lignosulfonate and foaming agent PO-1 and water at the following content of components, wt. %: cement 64.5-68.8; polystyrene aggregate 1.2-1.9; complex additive 0.15-0.55 (RF patent 2143413, C 04 B 38/10, 1999).
Недостаток известного состава - низкая прочность готовых изделий. A disadvantage of the known composition is the low strength of the finished product.
Технический результат изобретения - повышение прочности готовых изделий. The technical result of the invention is to increase the strength of finished products.
Достигается это тем, что состав для изготовления легкобетонных изделий, включающий цемент, вспученные гранулы пенополистирола, лигносульфонат технический ЛСТ, воздухововлекающую добавку ПО-1 и воду, дополнительно содержит песок при следующем соотношении компонентов в вес. %:
Цемент - 64-66
Вспученные гранулы пенополистирола - 1,46-1,76
Лигносульфонат технический ЛСТ - 0,128-0,132
Воздухововлекающая добавка ПО-1 - 0,160-0,165
Песок - 19,2-19,9
Вода - Остальное
Воздухововлекающая добавка ПО-1 изготавливается по ГОСТ 6948-80 на основе натриевых солей алкиларилсульфокислот керосинового дистиллята.This is achieved by the fact that the composition for the manufacture of lightweight concrete products, including cement, expanded polystyrene granules, technical lignosulfonate LST, air-entraining additive PO-1 and water, additionally contains sand in the following ratio of components to weight. %:
Cement - 64-66
Expanded polystyrene beads - 1.46-1.76
Lignosulfonate technical LST - 0,128-0,132
PO-1 air entraining additive - 0.160-0.165
Sand - 19.2-19.9
Water - Else
PO-1 air-entraining additive is made in accordance with GOST 6948-80 based on sodium salts of alkylarylsulfonic acids of kerosene distillate.
Композицию готовят следующим образом. В бетоносмесителе производят предварительное сухое перемешивание цемента и песка в течение 2 мин. Затем добавляют вспученные гранулы пенополистирола, воду с ЛСТ и ПО-1. Окончательное перемешивание длится 5 мин. Добавки вводятся в смесь вместе с водой затворения. The composition is prepared as follows. In a concrete mixer, preliminary dry mixing of cement and sand is carried out for 2 minutes. Then expanded expanded polystyrene granules, water from LST and PO-1 are added. Final mixing lasts 5 minutes. Additives are introduced into the mixture along with mixing water.
Предлагаемый состав приведен в табл. 1, его свойства в табл. 2. The proposed composition is given in table. 1, its properties in table. 2.
Claims (1)
Цемент - 64 - 66
Вспученные гранулы пенополистирола - 1,46 - 1,76
Лигносульфонат технический ЛСТ - 0,128 - 0,132
Воздухововлекающая добавка ПО-1 - 0,160 - 0,165
Песок - 19,2 - 19,9
Вода - ОстальноеComposition for the manufacture of lightweight concrete products, including cement, expanded polystyrene granules, technical lignosulfonate LST, air-entraining additive PO-1 and water, characterized in that it additionally contains sand in the following ratio of components, weight. %:
Cement - 64 - 66
Expanded polystyrene beads - 1.46 - 1.76
Lignosulfonate technical LST - 0,128 - 0,132
PO-1 air entraining additive - 0.160 - 0.165
Sand - 19.2 - 19.9
Water - Else