RU2018131618A - Огнеупорный объект из оксида хрома и способ его формования - Google Patents

Огнеупорный объект из оксида хрома и способ его формования Download PDF

Info

Publication number
RU2018131618A
RU2018131618A RU2018131618A RU2018131618A RU2018131618A RU 2018131618 A RU2018131618 A RU 2018131618A RU 2018131618 A RU2018131618 A RU 2018131618A RU 2018131618 A RU2018131618 A RU 2018131618A RU 2018131618 A RU2018131618 A RU 2018131618A
Authority
RU
Russia
Prior art keywords
refractory object
total mass
proportion
ook
refractory
Prior art date
Application number
RU2018131618A
Other languages
English (en)
Other versions
RU2716676C2 (ru
RU2018131618A3 (ru
Inventor
Кристен Е. ПАППАЦЕНА
Жульен П. ФУРКАД
Original Assignee
Сен-Гобен Серэмикс Энд Пластикс, Инк.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Сен-Гобен Серэмикс Энд Пластикс, Инк. filed Critical Сен-Гобен Серэмикс Энд Пластикс, Инк.
Publication of RU2018131618A publication Critical patent/RU2018131618A/ru
Publication of RU2018131618A3 publication Critical patent/RU2018131618A3/ru
Application granted granted Critical
Publication of RU2716676C2 publication Critical patent/RU2716676C2/ru

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/42—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on chromites
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/66—Monolithic refractories or refractory mortars, including those whether or not containing clay
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/12—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on chromium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/62204—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products using waste materials or refuse
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/76—Use at unusual temperatures, e.g. sub-zero
    • C04B2111/763—High temperatures
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3206—Magnesium oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3232—Titanium oxides or titanates, e.g. rutile or anatase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3244—Zirconium oxides, zirconates, hafnium oxides, hafnates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3244—Zirconium oxides, zirconates, hafnium oxides, hafnates, or oxide-forming salts thereof
    • C04B2235/3248—Zirconates or hafnates, e.g. zircon
    • C04B2235/3249—Zirconates or hafnates, e.g. zircon containing also titanium oxide or titanates, e.g. lead zirconate titanate (PZT)
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3418—Silicon oxide, silicic acids, or oxide forming salts thereof, e.g. silica sol, fused silica, silica fume, cristobalite, quartz or flint
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/72—Products characterised by the absence or the low content of specific components, e.g. alkali metal free alumina ceramics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/77—Density
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Compositions Of Oxide Ceramics (AREA)
  • Furnace Housings, Linings, Walls, And Ceilings (AREA)
  • Porous Artificial Stone Or Porous Ceramic Products (AREA)
  • Nanotechnology (AREA)

Claims (38)

1. Огнеупорный объект, содержащий
долю Cr2O3 по меньшей мере около 80% мас. от общей массы огнеупорного объекта;
долю Al2O3 по меньшей мере около 0,7% мас. и не более, чем около 10% мас. от общей массы огнеупорного объекта;
долю SiO2 по меньшей мере около 0,3% мас. и не более, чем около 5,0% мас. от общей массы огнеупорного объекта;
долю TiO2 по меньшей мере около 1,0% мас. и не более, чем около 5,6% мас. TiO2 от общей массы огнеупорного объекта; и
ПИ по меньшей мере около 37 МПа, измеренную при 1200°С,
при этом отношение OOКAl2O3/OOКSiO2 по меньшей мере около 1 и не более, чем около 8, причем OOКAl2O3 представлет собой долю Al2O3 в % мас. от общей массы огнеупорного объекта и OOКSiO2 представляет собой долю SiO2 в % мас. от общей массы огнеупорного объекта.
2. Огнеупорный объект, содержащий
долю Cr2O3 по меньшей мере около 80% мас. от общей массы огнеупорного объекта;
долю Al2O3 по меньшей мере около 0,7% мас. и не более, чем около 10% мас. от общей массы огнеупорного объекта;
долю SiO2 по меньшей мере около 0,3% мас. и не более, чем около 5,0% мас. от общей массы огнеупорного объекта;
долю TiO2 по меньшей мере около 1,0% мас. и не более, чем около 5,6% мас. TiO2 от общей массы огнеупорного объекта; и
отношение ООПИ/(1000*ООМУ) по меньшей мере 0,5, причем ООПИ равен ПИ огнеупорного объекта, измеренной в МПа при 1200°С, и ООМУ равен МУ огнеупорного объекта, измеренному в ГПа при 1200°С,
при этом отношение OOКAl2O3/OOКSiO2 по меньшей мере около 1 и не более, чем около 8, причем OOКAl2O3 представлет собой долю Al2O3 в % мас. от общей массы огнеупорного объекта и OOКSiO2 представляет собой долю SiO2 в % мас. от общей массы огнеупорного объекта.
3. Огнеупорный объект, содержащий
долю Cr2O3 по меньшей мере около 80% мас. от общей массы огнеупорного объекта;
долю TiO2 по меньшей мере около 1,0% мас. и не более, чем около 5,6% мас. TiO2 от общей массы огнеупорного объекта; и
отношение OOКAl2O3/OOКSiO2 по меньшей мере около 1 и не более, чем около 8, причем OOКAl2O3 представлет собой долю Al2O3 в % мас. от общей массы огнеупорного объекта и OOКSiO2 представляет собой долю SiO2 в % мас. от общей массы огнеупорного объекта.
4. Огнеупорный объект по любому одному из пп. 2 и 3, отличающийся тем, что огнеупорный объект дополнительно имеет ПИ по меньшей мере около 37 МПа, измеренную при 1200°С.
5. Огнеупорный объект по любому одному из пп. 1 и 3, отличающийся тем, что огнеупорный объект дополнительно имеет отношение ООПИ/(1000*ООМУ) не более, чем около 0,5, причем ООПИ равен ПИ огнеупорного объекта, измеренной в МПа при 1200°С, и ООМУ равен МУ огнеупорного объекта, измеренному в ГПа при 1200°С.
6. Огнеупорный объект по любому одному из пп. 1 и 2, отличающийся тем, что огнеупорный объект дополнительно имеет отношение OOКAl2O3/OOКSiO2 по меньшей мере около 0,9, причем OOКAl2O3 представлет собой долю Al2O3 в % мас. от общей массы огнеупорного объекта и OOКSiO2 представляет собой долю SiO2 в % мас. от общей массы огнеупорного объекта.
7. Огнеупорный объект по п. 3, отличающийся тем, что огнеупорный объект содержит долю Al2O3 по меньшей мере около 0,7% мас. и не более, чем около 10% мас. от общей массы огнеупорного объекта.
8. Огнеупорный объект по п. 3, отличающийся тем, что огнеупорный объект содержит долю SiO2 по меньшей мере около 0,3% мас. и не более, чем около 5,0% мас. от общей массы огнеупорного объекта.
9. Огнеупорный объект по любому одному из пп. 1, 2 и 3, отличающийся тем, что огнеупорный объект дополнительно содержит долю MgO по меньшей мере около 0,1% мас. и не более, чем около 1,0% мас. от общей массы огнеупорного объекта.
10. Огнеупорный объект по любому одному из пп. 1, 2 и 3, отличающийся тем, что огнеупорный объект дополнительно содержит долю ZrO2 по меньшей мере около 0,1% мас. и не более, чем около 10% мас. от общей массы огнеупорного объекта.
11. Огнеупорный объект по любому одному из пп.1, 2 и 3, отличающийся тем, что огнеупорный объект дополнительно имеет отношение ООКZrO2/OOКAl2O3 по меньшей мере около 0,1 и и не более, чем около 5, причем ООКZrO2 представлет собой долю ZrO2 в % мас. от общей массы огнеупорного объекта и OOКAl2O3 представляет собой долю Al2O3 в % мас. от общей массы огнеупорного объекта.
12. Огнеупорный объект по любому одному из пп. 1, 2 и 3, отличающийся тем, что огнеупорный объект имеет пористость по меньшей мере около 0,07% об. и не более, чем около 18% об. от общего объема огнеупорного объекта.
13. Огнеупорный объект по любому одному из пп. 1, 2 и 3, в котором огнеупорный объект имеет плотность по меньшей мере около 4,1 г/см3 и не более, чем около 4,8 г/см3.
14. Способ формования огнеупорного объекта, включающий:
получение формовочной композиции; и
формование формовочной композиции в огнеупорный объект,
отличающийся тем, что огнеупорный объект содержит:
долю Cr2O3 по меньшей мере около 80% мас. от общей массы огнеупорного объекта;
долю Al2O3 по меньшей мере около 0,7% мас. и не более, чем около 10% мас. от общей массы огнеупорного объекта;
долю SiO2 по меньшей мере около 0,3% мас. и не более, чем около 5,0% мас. от общей массы огнеупорного объекта;
долю TiO2 по меньшей мере около 1,0% мас. и не более, чем около 5,6% мас. TiO2 от общей массы огнеупорного объекта; и
при этом отношение OOКAl2O3/OOКSiO2 по меньшей мере около 1 и не более, чем около 8, причем OOКAl2O3 представлет собой долю Al2O3 в % мас. от общей массы огнеупорного объекта и OOКSiO2 представляет собой долю SiO2 в % мас. от общей массы огнеупорного объекта, и
ПИ по меньшей мере около 37 МПа, измеренную при 1200°С.
RU2018131618A 2016-02-05 2017-02-02 Огнеупорный объект из оксида хрома и способ его формования RU2716676C2 (ru)