RU2018127647A - Способ изготовления заготовки, заготовка и зубная реставрация - Google Patents

Способ изготовления заготовки, заготовка и зубная реставрация Download PDF

Info

Publication number
RU2018127647A
RU2018127647A RU2018127647A RU2018127647A RU2018127647A RU 2018127647 A RU2018127647 A RU 2018127647A RU 2018127647 A RU2018127647 A RU 2018127647A RU 2018127647 A RU2018127647 A RU 2018127647A RU 2018127647 A RU2018127647 A RU 2018127647A
Authority
RU
Russia
Prior art keywords
ceramic material
oxide
ceramic
procurement
paragraphs
Prior art date
Application number
RU2018127647A
Other languages
English (en)
Other versions
RU2018127647A3 (ru
RU2721074C2 (ru
Inventor
Лотар ФЕЛКЛЬ
Штефан ФЕХЕР
Мартин КУЦНЕР
Таня ЭФНЕР
Original Assignee
Дентсплай Сирона Инк.
Дегудент Гмбх
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=57737726&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=RU2018127647(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Дентсплай Сирона Инк., Дегудент Гмбх filed Critical Дентсплай Сирона Инк.
Publication of RU2018127647A3 publication Critical patent/RU2018127647A3/ru
Publication of RU2018127647A publication Critical patent/RU2018127647A/ru
Application granted granted Critical
Publication of RU2721074C2 publication Critical patent/RU2721074C2/ru

Links

Classifications

    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/0003—Making bridge-work, inlays, implants or the like
    • A61C13/0022—Blanks or green, unfinished dental restoration parts
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/08—Artificial teeth; Making same
    • A61C13/081—Making teeth by casting or moulding
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/08—Artificial teeth; Making same
    • A61C13/082—Cosmetic aspects, e.g. inlays; Determination of the colour
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/08—Artificial teeth; Making same
    • A61C13/083—Porcelain or ceramic teeth
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/08—Artificial teeth; Making same
    • A61C13/09—Composite teeth, e.g. front and back section; Multilayer teeth
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C5/00—Filling or capping teeth
    • A61C5/70—Tooth crowns; Making thereof
    • A61C5/73—Composite crowns
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C5/00—Filling or capping teeth
    • A61C5/70—Tooth crowns; Making thereof
    • A61C5/77—Methods or devices for making crowns
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C8/00—Means to be fixed to the jaw-bone for consolidating natural teeth or for fixing dental prostheses thereon; Dental implants; Implanting tools
    • A61C8/0012—Means to be fixed to the jaw-bone for consolidating natural teeth or for fixing dental prostheses thereon; Dental implants; Implanting tools characterised by the material or composition, e.g. ceramics, surface layer, metal alloy
    • A61C8/0013—Means to be fixed to the jaw-bone for consolidating natural teeth or for fixing dental prostheses thereon; Dental implants; Implanting tools characterised by the material or composition, e.g. ceramics, surface layer, metal alloy with a surface layer, coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B28—WORKING CEMENT, CLAY, OR STONE
    • B28B—SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS; SHAPING SLAG; SHAPING MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
    • B28B3/00—Producing shaped articles from the material by using presses; Presses specially adapted therefor
    • B28B3/02—Producing shaped articles from the material by using presses; Presses specially adapted therefor wherein a ram exerts pressure on the material in a moulding space; Ram heads of special form
    • B28B3/021—Ram heads of special form
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B18/00—Layered products essentially comprising ceramics, e.g. refractory products
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/48—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zirconium or hafnium oxides, zirconates, zircon or hafnates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/48—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zirconium or hafnium oxides, zirconates, zircon or hafnates
    • C04B35/486—Fine ceramics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B37/00—Joining burned ceramic articles with other burned ceramic articles or other articles by heating
    • C04B37/001—Joining burned ceramic articles with other burned ceramic articles or other articles by heating directly with other burned ceramic articles
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C04B2235/3225—Yttrium oxide or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3232—Titanium oxides or titanates, e.g. rutile or anatase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3239—Vanadium oxides, vanadates or oxide forming salts thereof, e.g. magnesium vanadate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3241—Chromium oxides, chromates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3244—Zirconium oxides, zirconates, hafnium oxides, hafnates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3262—Manganese oxides, manganates, rhenium oxides or oxide-forming salts thereof, e.g. MnO
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3272—Iron oxides or oxide forming salts thereof, e.g. hematite, magnetite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3275—Cobalt oxides, cobaltates or cobaltites or oxide forming salts thereof, e.g. bismuth cobaltate, zinc cobaltite
    • C04B2235/3277—Co3O4
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3279—Nickel oxides, nickalates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3281—Copper oxides, cuprates or oxide-forming salts thereof, e.g. CuO or Cu2O
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/60—Aspects relating to the preparation, properties or mechanical treatment of green bodies or pre-forms
    • C04B2235/604—Pressing at temperatures other than sintering temperatures
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/72—Products characterised by the absence or the low content of specific components, e.g. alkali metal free alumina ceramics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/76—Crystal structural characteristics, e.g. symmetry
    • C04B2235/765—Tetragonal symmetry
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
    • C04B2235/9607—Thermal properties, e.g. thermal expansion coefficient
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
    • C04B2235/9646—Optical properties
    • C04B2235/9653—Translucent or transparent ceramics other than alumina
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
    • C04B2235/9646—Optical properties
    • C04B2235/9661—Colour
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/345—Refractory metal oxides
    • C04B2237/348—Zirconia, hafnia, zirconates or hafnates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/58—Forming a gradient in composition or in properties across the laminate or the joined articles
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/84—Joining of a first substrate with a second substrate at least partially inside the first substrate, where the bonding area is at the inside of the first substrate, e.g. one tube inside another tube

Landscapes

  • Health & Medical Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Public Health (AREA)
  • Veterinary Medicine (AREA)
  • General Health & Medical Sciences (AREA)
  • Animal Behavior & Ethology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Epidemiology (AREA)
  • Oral & Maxillofacial Surgery (AREA)
  • Dentistry (AREA)
  • Ceramic Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Organic Chemistry (AREA)
  • Structural Engineering (AREA)
  • Materials Engineering (AREA)
  • Composite Materials (AREA)
  • Orthopedic Medicine & Surgery (AREA)
  • Mechanical Engineering (AREA)
  • Dental Preparations (AREA)
  • Dental Prosthetics (AREA)
  • Compositions Of Oxide Ceramics (AREA)

Claims (70)

1. Способ изготовления заготовки (28, 48) из керамического материала, в частности, заготовки, используемой для изготовления зубной реставрации (42), при этом первый керамический материал (14) и затем второй керамический материал (20) из различных композиций загружаются в форму (10), причем материалы спрессовываются и после прессования подвергаются спеканию,
отличающийся тем, что
слой первого керамического материала (14) загружается в сыпучем состоянии в форму (10), в слое образуется первая открытая полость (18), второй керамический материал (20) загружается в сыпучем состоянии в первую открытую полость, и материалы спрессовываются вместе и затем подвергаются термической обработке, при этом керамические материалы содержат диоксид циркония, легированный оксидом иттрия (Y2O3), оксидом кальция (CaO), оксидом магния (MgO) и/или оксидом церия (CeO2), причем первый керамический материал (14) отличается от материала второго керамического материала (20) по цвету и соотношению стабилизированных кристаллических форм, имеющихся при комнатной температуре.
2. Способ по п. 1,
отличающийся тем, что
после загрузки второго керамического материала (18) в нем создается вторая открытая полость (26, 36).
3. Способ по п. 1 или 2,
отличающийся тем, что
во вторую открытую полость (36) загружается третий керамический материал (38), имеющий композицию, отличную от композиции первого и/или второго керамического материала.
4. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
в слое первого керамического материала (14) образуется множество первых открытых полостей (18), и в эти полости загружается керамический материал (18), в частности, второй керамический материал.
5. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
по меньшей мере некоторые из множества открытых первых полостей (18) имеют различную внутреннюю геометрию.
6. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
второй керамический материал (20) представляет собой материал, который после полного спекания имеет коэффициент теплового расширения, который на 0,2-0,8 мкм/м*K больше коэффициента теплового расширения первого керамического материала (14).
7. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
внутренняя геометрия первой открытой полости (18) геометрически совмещается с порядком расположения зубного челюстного участка, например, культи зуба или абатмента, выходящего из челюстного участка, который надлежит обеспечить реставрацией.
8. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
при получении зубной реставрации из заготовки (28, 48) дентинный участок зубной реставрации по меньшей мере частично образован из второго керамического материала (20), а резцовый участок образован из первого керамического материала (14).
9. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
по меньшей мере второй керамический материал окрашен по меньшей мере одним из придающего окраску оксида элементов из группы Pr, Er, Tb, Fe, Co, Ni, Ti, V, Cr, Cu, Mn, предпочтительно Fe2O3, Er2O3 или Co3O4.
10. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
первый и/или второй керамический материал (14, 20) является/являются таким(ми) материалом(ами), что процентное содержание оксида иттрия в первом материале составляет 7,0-9,5 весовых % и/или процентное содержание во втором и/или третьем материале составляет 4,5-7,0 весовых %, при этом процентное содержание оксида иттрия в первом керамическом материале выше, чем во втором или третьем материале.
11. Способ по меньшей мере по одному из вышеуказанных пунктов,
отличающийся тем, что
используемые керамические материалы после предварительного спекания имеют отношение тетрагональной кристаллической фазы к кубической кристаллической фазе диоксида циркония в материалах (14, 20) ≥ 1.
12. Подвергнутая предварительному или полному спеканию заготовка (28, 48) для использования в изготовлении зубной реставрации (42), например, зубного каркаса, коронки, частичной коронки, мостовидного протеза, колпачка, винира, абатмента, штифтовой конструкции, в частности, коронки или частичной коронки, имеющая участки из различных композиций, при этом один первый участок (32) из первого керамического материала (14) и по меньшей мере один второй участок (34, 52, 54, 56) из второго керамического материала (20) имеют различные композиции, и указанные участки расположены рядом друг с другом, при этом керамические материалы содержат диоксид циркония, легированный оксидом иттрия (Y2O3), оксидом кальция (CaO), оксидом магния (MgO) и/или оксидом церия (CeO2), при этом первый керамический материал (14) отличается от материала второго керамического материала (20) по цвету и соотношению стабилизированных кристаллических форм, имеющихся при комнатной температуре, причем вторые участки (34, 52, 54, 56) проходят в первом участке (32) и имеют внутреннюю геометрию, сужающуюся от основного участка (35) или основной поверхности, и при этом процентное содержание оксида иттрия во втором керамическом материале (20) составляет 4,5-7,0 весовых %, а в первом керамическом материале (14) 7,0-9,5 весовых %, причем процентное содержание оксида иттрия в первом керамическом материале выше, чем во втором керамическом материале.
13. Заготовка по п. 12,
отличающаяся тем,
что основной участок (35) или основная поверхность второго участка (34) проходит в участке наружной поверхности (33) первого участка (32), и предпочтительно заподлицо с ней.
14. Заготовка по п. 12 или 13,
отличающаяся тем, что
второй участок (34) имеет полость (26), начиная от своего основного участка (35) или основной поверхности.
15. Заготовка по меньшей мере по одному из пп. 12-14,
отличающаяся тем, что
второй участок (34) имеет конусовидную форму на своей наружной стороне.
16. Заготовка по меньшей мере по одному из пп. 12-15,
отличающаяся тем, что
внутри второго участка (34) проходит третий участок (38), состоящий из третьего керамического материала, имеющего композицию, отличную от композиции первого и/или второго керамического материала (14, 20).
17. Заготовка по меньшей мере по одному из пп. 12-16,
отличающаяся тем, что
множество вторых участков (52, 54, 56) окружены первым участком (32, 50).
18. Заготовка по меньшей мере по одному из пп. 12-17,
отличающаяся тем, что
по меньшей мере некоторые из множества вторых участков (52, 54, 56) отличаются друг от друга по своей наружной геометрии.
19. Заготовка по меньшей мере по одному из пп. 12-18,
отличающаяся тем, что
заготовка (28, 48) содержит диоксид циркония с добавлением оксида иттрия.
20. Заготовка по меньшей мере по одному из пп. 12-19,
отличающаяся тем, что
второй керамический материал (20) отличается от первого керамического материала (14) по цвету.
21. Заготовка по меньшей мере по одному из пп. 12-20,
отличающаяся тем, что
после полного спекания реставрация (42), изготовленная из заготовки (28), имеет более высокую прочность на дентинной стороне, чем на резцовой стороне, и/или прозрачность на резцовой стороне выше, чем прозрачность на дентинной стороне.
22. Заготовка по меньшей мере по одному из пп. 12-21,
отличающаяся тем, что
коэффициент теплового расширения первого участка (32, 50) на 0,2-0,8 мкм/м*K ниже, чем коэффициент теплового расширения второго и/или третьего участков (34, 38).
23. Зубная реставрация (42), в частности, коронка или частичная коронка, в частности, изготовленная по меньшей мере по п. 12,
отличающаяся тем, что
реставрация (42) образуется монолитно и содержит по меньшей мере один первый слой (32), расположенный на резцовой стороне из первого керамического материала (14), и второй слой (34), расположенный на дентинной стороне из второго керамического материала (20), при этом первый слой имеет более высокую прозрачность и/или более низкую прочность, чем второй слой, при этом керамические материалы содержат диоксид циркония, легированный оксидом иттрия (Y2O3), оксидом кальция (CaO), оксидом магния (MgO) и/или оксидом церия (CeO2), причем первый керамический материал (14) отличается от материала второго керамического материала (20) по цвету и соотношению стабилизированных кристаллических форм, имеющихся при комнатной температуре, и при этом процентное содержание оксида иттрия во втором керамическом материале (20) составляет 4,5-7,0 весовых %, а в первом керамическом материале (14) 7,0-9,5 весовых %, причем процентное содержание оксида иттрия в первом керамическом материале выше, чем во втором керамическом материале.
24. Зубная реставрация по меньшей мере по п. 23,
отличающаяся тем, что
коэффициент теплового расширения первого слоя (32) на 0,2-0,8 мкм/м*K ниже, чем коэффициент теплового расширения второго слоя (34).
RU2018127647A 2015-12-28 2016-12-23 Способ изготовления заготовки для зубной реставрации, заготовка и зубная реставрация, изготовленная из заготовки RU2721074C2 (ru)