RU2015152137A - Композиционный пенопласт - Google Patents

Композиционный пенопласт Download PDF

Info

Publication number
RU2015152137A
RU2015152137A RU2015152137A RU2015152137A RU2015152137A RU 2015152137 A RU2015152137 A RU 2015152137A RU 2015152137 A RU2015152137 A RU 2015152137A RU 2015152137 A RU2015152137 A RU 2015152137A RU 2015152137 A RU2015152137 A RU 2015152137A
Authority
RU
Russia
Prior art keywords
composite material
paragraphs
composition
accordance
expandable
Prior art date
Application number
RU2015152137A
Other languages
English (en)
Other versions
RU2015152137A3 (ru
Inventor
Рен БРЕЙСГЕРДЛ
Майкл МОНТИ
Гордон СМИТ
Стефен КЛАРК
Стефен МАКМИЛЛАН
Джулиан ГЛИНН
Мюррей Орпин
Original Assignee
ЭксФЛЭМ ПТИ ЛТД
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from AU2013901615A external-priority patent/AU2013901615A0/en
Application filed by ЭксФЛЭМ ПТИ ЛТД filed Critical ЭксФЛЭМ ПТИ ЛТД
Publication of RU2015152137A publication Critical patent/RU2015152137A/ru
Publication of RU2015152137A3 publication Critical patent/RU2015152137A3/ru

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/0061—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof characterized by the use of several polymeric components
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G8/00—Condensation polymers of aldehydes or ketones with phenols only
    • C08G8/04—Condensation polymers of aldehydes or ketones with phenols only of aldehydes
    • C08G8/08—Condensation polymers of aldehydes or ketones with phenols only of aldehydes of formaldehyde, e.g. of formaldehyde formed in situ
    • C08G8/10—Condensation polymers of aldehydes or ketones with phenols only of aldehydes of formaldehyde, e.g. of formaldehyde formed in situ with phenol
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/0066—Use of inorganic compounding ingredients
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/009—Use of pretreated compounding ingredients
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/22—After-treatment of expandable particles; Forming foamed products
    • C08J9/228—Forming foamed products
    • C08J9/232—Forming foamed products by sintering expandable particles
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/22—After-treatment of expandable particles; Forming foamed products
    • C08J9/228—Forming foamed products
    • C08J9/236—Forming foamed products using binding agents
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/32—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof from compositions containing microballoons, e.g. syntactic foams
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/35—Composite foams, i.e. continuous macromolecular foams containing discontinuous cellular particles or fragments
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L25/00—Compositions of, homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Compositions of derivatives of such polymers
    • C08L25/02—Homopolymers or copolymers of hydrocarbons
    • C08L25/04—Homopolymers or copolymers of styrene
    • C08L25/06—Polystyrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L61/00—Compositions of condensation polymers of aldehydes or ketones; Compositions of derivatives of such polymers
    • C08L61/04—Condensation polymers of aldehydes or ketones with phenols only
    • C08L61/06—Condensation polymers of aldehydes or ketones with phenols only of aldehydes with phenols
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
    • C09K21/00—Fireproofing materials
    • C09K21/14—Macromolecular materials
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2203/00—Foams characterized by the expanding agent
    • C08J2203/22—Expandable microspheres, e.g. Expancel®
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2300/00—Characterised by the use of unspecified polymers
    • C08J2300/22—Thermoplastic resins
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2325/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
    • C08J2325/02—Homopolymers or copolymers of hydrocarbons
    • C08J2325/04—Homopolymers or copolymers of styrene
    • C08J2325/06—Polystyrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2327/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers
    • C08J2327/02—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment
    • C08J2327/04—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment containing chlorine atoms
    • C08J2327/06—Homopolymers or copolymers of vinyl chloride
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2327/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers
    • C08J2327/02—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment
    • C08J2327/04—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment containing chlorine atoms
    • C08J2327/08—Homopolymers or copolymers of vinylidene chloride
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2333/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Derivatives of such polymers
    • C08J2333/04—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Derivatives of such polymers esters
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2333/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Derivatives of such polymers
    • C08J2333/18—Homopolymers or copolymers of nitriles
    • C08J2333/20—Homopolymers or copolymers of acrylonitrile
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2339/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a single or double bond to nitrogen or by a heterocyclic ring containing nitrogen; Derivatives of such polymers
    • C08J2339/04—Homopolymers or copolymers of monomers containing heterocyclic rings having nitrogen as ring member
    • C08J2339/08—Homopolymers or copolymers of vinyl-pyridine
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2361/00—Characterised by the use of condensation polymers of aldehydes or ketones; Derivatives of such polymers
    • C08J2361/04—Condensation polymers of aldehydes or ketones with phenols only
    • C08J2361/06—Condensation polymers of aldehydes or ketones with phenols only of aldehydes with phenols
    • C08J2361/08—Condensation polymers of aldehydes or ketones with phenols only of aldehydes with phenols with monohydric phenols
    • C08J2361/10—Phenol-formaldehyde condensates
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2371/00—Characterised by the use of polyethers obtained by reactions forming an ether link in the main chain; Derivatives of such polymers
    • C08J2371/08—Polyethers derived from hydroxy compounds or from their metallic derivatives
    • C08J2371/10—Polyethers derived from hydroxy compounds or from their metallic derivatives from phenols
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2425/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
    • C08J2425/02—Homopolymers or copolymers of hydrocarbons
    • C08J2425/04—Homopolymers or copolymers of styrene
    • C08J2425/06—Polystyrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2461/00—Characterised by the use of condensation polymers of aldehydes or ketones; Derivatives of such polymers
    • C08J2461/04—Condensation polymers of aldehydes or ketones with phenols only
    • C08J2461/06—Condensation polymers of aldehydes or ketones with phenols only of aldehydes with phenols
    • C08J2461/08—Condensation polymers of aldehydes or ketones with phenols only of aldehydes with phenols with monohydric phenols
    • C08J2461/10—Phenol-formaldehyde condensates

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Composite Materials (AREA)
  • Inorganic Chemistry (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Compositions Of Macromolecular Compounds (AREA)

Claims (36)

1. Дисперсный состав, включающий в себя:
(a) вспенивающиеся частицы полистирола;
(b) резольную фенолоальдегидную смолу;
(c) вспенивающиеся термопластичные микросферы; и
(d) кислотный катализатор.
2. Состав в соответствии с п. 1, отличающийся тем, что вспенивающиеся частицы полистирола вспениваются частично.
3. Состав в соответствии с п. 1 или 2, отличающийся тем, что плотность вспенивающихся частиц полистирола находится в диапазоне от 5 до 20 кг/м3.
4. Состав по любому из пп. 1 и 2, содержащий один или несколько наполнителей.
5. Состав в соответствии с п. 4, отличающийся тем, что наполнитель присутствует в количестве 0,5-60 вес.% от общей массы состава.
6. Состав в соответствии с п. 5, отличающийся тем, что наполнитель представляет собой наполнитель с модифицированной поверхностью частиц.
7. Состав по любому из пп. 1 и 2, отличающийся тем, что резольная фенолоальдегидная смола является производной реакционноспособной резольной смолы с одним или несколькими следующими свойствами:
(a) вязкость от 500 до 4000 сП (сантипауз);
(b) содержание воды от 2 до 7 вес.%;
(c) содержание свободного фенола менее 25%; или
(d) содержание свободного формальдегида менее 3%.
8. Состав по любому из пп. 1 и 2, отличающийся тем, что средний размер частиц вспенивающихся термопластичных микросфер находится в пределах 1-50 мкм, и отличающийся тем, что вспенивающиеся микросферы содержат пропеллент, заключенный в оболочку из термопластичного полимера.
9. Состав в соответствии с п. 8, отличающийся тем, что оболочка из термопластичного полимера является производной из мономеров, выбранных из группы, состоящей из акрилонитрила, метакрилонитрила, α-хлоракрилонитрила, α-этоксиакрилонитоила, фумароакрилонитрила, кротоакрилонитрила, эфира акриловой кислоты, эфира метакриловой кислоты, хлористого винила, хлористого винилидена, дихлорида винилидена, винилпиридина, виниловых эфиров и их производных или смесей.
10. Состав по любому из пп. 1 и 2, отличающийся тем, что кислотный катализатор выбирается из сильной органической кислоты, эфира сильной органической кислоты, слабой неорганической кислоты, эфира слабой неорганической кислоты или их смесей.
11. Композиционный полистирол-фенольный пенопласт включает в себя:
(a) вспененный полистирол;
(b) отвержденную резольную фенолоальдегидную смолу; и
(c) вспененные термопластичные микросферы,
причем плотность композиционного материала находится в пределах 10-40 кг/м3 и композиционный материал обнаруживает время повреждения изоляции более чем 10 минут, согласно стандарту AS1530.4, для панели толщиной 100 мм.
12. Композиционный материал в соответствии с п. 12, отличающийся тем, что вспененный полистирол и/или вспененные термопластичные микросферы, по меньшей мере, частично растворены в фенолоальдегидной смоле.
13. Композиционный материал в соответствии с п. 11 или 12, отличающийся тем, что композиционный материал включает в себя от 30 до 70 вес.% (a), от 20 до 60 вес.% (b) и от 0,5 до 5 вес.% (c) от общей массы состава.
14. Композиционный материал по любому из пп. 11 и 12, отличающийся тем, что композиционный материал имеет свободный объем менее 5%, предпочтительно менее 1%, более предпочтительно менее 0,5%.
15. Композиционный материал по любому из пп. 11 и 12, отличающийся тем, что композиционный материал поглощает воду в соответствии со стандартом ASTM С272 в количестве менее 8% от объема.
16. Композиционный материал по любому из пп. 11 и 12, отличающийся тем, что скорость уноса массы при 50 кВт, измеренная согласно стандарта ISO 17554, составляет менее 8 г/м2⋅сек.
17. Композиционный материал по любому из пп. 11 и 12, отличающийся тем, что композиционный материал обнаруживает время повреждения изоляции более чем 20 мин, согласно стандарту AS 1530.4, для панели толщиной 100 мм.
18. Композиционный материал по любому из пп. 11 и 12, отличающийся тем, что композиционный материал обнаруживает время повреждения изоляции более чем 30 мин, согласно стандарту AS 1530.4, для панели толщиной 100 мм.
19. Композиционный материал по любому из пп. 11 и 12, отличающийся тем, что вспененные частицы полистирола являются производными вспениваемых частиц полистирола со средним размером от 0,1 до 5 мм, причем вспениваемые частицы полистирола содержат порообразующее вещество.
20. Композиционный материал по любому из пп. 11 и 12, отличающийся тем, что вспененные термопластичные микросферы являются производными от вспенивающихся термопластичных микросфер со средним размером частиц в пределах от 1 до 50 мкм, и отличающийся тем, что вспенивающиеся микросферы содержат пропеллент, заключенный в оболочку из термопластичного полимера.
21. Композиционный материал в соответствии с п. 20, отличающийся тем, что оболочка из термопластичного полимера является производной из мономеров, выбранных из группы, состоящей из акрилонитрила, метакрилонитрила, α-хлоракрилонитрила, α-этоксиакрилонитоила, фумароакрилонитрила, кротоакрилонитрила, эфира акриловой кислоты, эфира метакриловой кислоты, хлористого винила, хлористого винилидена, дихлорида винилидена, винилпиридина, виниловых эфиров и их производных или смесей.
22. Композиционный материал по любому из пп. 11 и 12, содержащий далее один или несколько наполнителей.
23. Композиционный материал в соответствии с п. 22, отличающийся тем, что наполнитель представляет собой наполнитель с модифицированной поверхностью частиц.
24. Композиционный блок, панель или лист, используемые в строительстве, содержащие композиционный пенопласт согласно любому из пп. 11-21.
RU2015152137A 2013-05-07 2014-05-07 Композиционный пенопласт RU2015152137A (ru)