PL424691A1 - Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych - Google Patents
Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznychInfo
- Publication number
- PL424691A1 PL424691A1 PL424691A PL42469118A PL424691A1 PL 424691 A1 PL424691 A1 PL 424691A1 PL 424691 A PL424691 A PL 424691A PL 42469118 A PL42469118 A PL 42469118A PL 424691 A1 PL424691 A1 PL 424691A1
- Authority
- PL
- Poland
- Prior art keywords
- max
- group
- steel
- fasteners
- cold forging
- Prior art date
Abstract
Przedmiotem zgłoszenia jest sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych, w którym stosuje się stal o strukturze wielowazowej z efektem TRIP z fazą w postaci austenitu szczątkowego w granicach od 6 do 11% uzyskanego poprzez termomechaniczne walcowanie z kontrolowanym chłodzeniem, przy czym stosuje się stal o składzie chemicznym grupy pierwszej, dla której zawartość poszczególnych pierwiastków wynosi: C = 0,06 - 0,12%; Si = 0,2 - 0,5%; Mn = 0,0 - 1,5%; Cr = 0,0 - 0,3%; P = max 0,025%, S = max 0,025%, albo grupy drugiej, dla której zawartość poszczególnych pierwiastków wynosi: C = 0,06 - 0,14%; Si = 0,8 - 1,2%; Mn = 1,6 - 1,9%; Cr = 0,0 - 0,15%; P = max 0,025%, S = max 0,025%, natomiast średnicę materiału wsadowego oraz gniot sumaryczny podczas operacji ciągnienia jedno lub wieloetapowego dobiera się tak, aby spełniona była zależność Rm = 1142 z 0,1831 dla stali z grupy pierwszej oraz Rm = 1081 z 0,1567 dla stali z grupy drugiej, z możliwym odchyleniem ±50 MPa, gdzie Rm oznacza oczekiwaną wytrzymałość na rozciąganie drutu.
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| PL424691A PL424691A1 (pl) | 2018-02-27 | 2018-02-27 | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| PL424691A PL424691A1 (pl) | 2018-02-27 | 2018-02-27 | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| PL424691A1 true PL424691A1 (pl) | 2019-09-09 |
Family
ID=67844624
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PL424691A PL424691A1 (pl) | 2018-02-27 | 2018-02-27 | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych |
Country Status (1)
| Country | Link |
|---|---|
| PL (1) | PL424691A1 (pl) |
Citations (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3926687A (en) * | 1973-09-10 | 1975-12-16 | Nippon Steel Corp | Method for producing a killed steel wire rod |
| US4613385A (en) * | 1984-08-06 | 1986-09-23 | Regents Of The University Of California | High strength, low carbon, dual phase steel rods and wires and process for making same |
| US5338380A (en) * | 1985-08-29 | 1994-08-16 | Kabushiki Kaisha Kobe Seiko Sho | High strength low carbon steel wire rods and method of producing them |
| CN106311781A (zh) * | 2016-09-28 | 2017-01-11 | 邢台钢铁有限责任公司 | 一种超低碳钢拉拔细丝的方法 |
-
2018
- 2018-02-27 PL PL424691A patent/PL424691A1/pl unknown
Patent Citations (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3926687A (en) * | 1973-09-10 | 1975-12-16 | Nippon Steel Corp | Method for producing a killed steel wire rod |
| US4613385A (en) * | 1984-08-06 | 1986-09-23 | Regents Of The University Of California | High strength, low carbon, dual phase steel rods and wires and process for making same |
| US5338380A (en) * | 1985-08-29 | 1994-08-16 | Kabushiki Kaisha Kobe Seiko Sho | High strength low carbon steel wire rods and method of producing them |
| CN106311781A (zh) * | 2016-09-28 | 2017-01-11 | 邢台钢铁有限责任公司 | 一种超低碳钢拉拔细丝的方法 |
Non-Patent Citations (1)
| Title |
|---|
| WIEWIÓRKOWSKA S, MUSKALSKI Z, THE APPLICATION OF LOW AND MEDIUM CARBON STEEL WITH MULTIPHASE TRIP STRUCTURE IN DRAWING INDUSTRY PROCEDIA MANUFACTURING, 2015 * |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| MX2018004772A (es) | Miembro prensado en caliente y metodo de fabricacion del mismo. | |
| MX395449B (es) | Lámina de acero galvanizada de alta resistencia y método para producir la misma. | |
| MX378702B (es) | Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida. | |
| WO2015014333A3 (de) | Siliziumhaltiger, mikrolegierter hochfester mehrphasenstahl mit einer mindestzugfestigkeit von 750 mpa und verbesserten eigenschaften und verfahren zur herstellung eines bandes aus diesem stahl | |
| MX2015014437A (es) | Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma. | |
| AU2015205937B2 (en) | Pearlitic steel rail with high strength and toughness and producing method thereof | |
| UA117865C2 (uk) | Високоміцна багатофазна сталь, спосіб її одержання та застосування | |
| IN2014CN02685A (pl) | ||
| BR112017000021A2 (pt) | método para fabricar uma folha de aço e folha de aço | |
| TWI627288B (zh) | 展現良好延展性之高強度鋼及藉由熔融鋅浴槽的下游在線熱處理之製造方法 | |
| BR112017000010B1 (pt) | processo de produção de uma chapa de aço e chapa de aço | |
| MX2013005011A (es) | Hoja de acero laminado de frio de alta resistencia que tiene capacidad de embuticion profunda y capacidad de temple en horno excelentes y metodo para su fabricacion. | |
| MX356324B (es) | Método para la fabricación de acero martensítico con límite de elasticidad muy alto y placa o pieza obtenida por tal método. | |
| MX2017008296A (es) | Laminas de acero galvanizado de alta resistencia y metodos para fabricar las mismas. | |
| MX2017003732A (es) | Acero para pernos y perno. | |
| MX2018011606A (es) | Chapa de acero galvanizada de alta resistencia y metodo para producir la misma. | |
| CN104805364A (zh) | 制作1×7-15.2/1860MPa预应力钢绞线用Φ10mm高强度盘条及其生产方法 | |
| RU2011147484A (ru) | Высокопрочный, высоковязкий тонкий стальной пруток и способ его изготовления | |
| RU2017143579A (ru) | Коррозионностойкая сталь, способ изготовления указанной стали и ее применение | |
| RU2017141034A (ru) | Низколегированная особо высокопрочная сталь третьего поколения | |
| CN104233074A (zh) | 含铬的钒氮微合金化400MPa级钢筋用钢及其生产方法 | |
| MY173780A (en) | Steel sheet for can and method for manufacturing the same | |
| WO2019002041A8 (de) | Stahllegierung mit verbesserter korrosionsbeständigkeit bei hochtemperaturbeanspruchung und verfahren zur herstellung von stahlband aus dieser stahllegierung | |
| PL424691A1 (pl) | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych | |
| CN106222547A (zh) | 一种1200MPa级高强塑性钢筋及热处理方法 |