PL235244B1 - Composition of photoreactive acrylate-based varnish for wood and method of producing the acrylate-based varnish for wood - Google Patents
Composition of photoreactive acrylate-based varnish for wood and method of producing the acrylate-based varnish for wood Download PDFInfo
- Publication number
- PL235244B1 PL235244B1 PL408818A PL40881814A PL235244B1 PL 235244 B1 PL235244 B1 PL 235244B1 PL 408818 A PL408818 A PL 408818A PL 40881814 A PL40881814 A PL 40881814A PL 235244 B1 PL235244 B1 PL 235244B1
- Authority
- PL
- Poland
- Prior art keywords
- weight
- methacrylate
- acrylate
- acid
- wood
- Prior art date
Description
Opis wynalazkuDescription of the invention
Przedmiotem wynalazku jest kompozycja fotoreaktywnego lakieru na bazie akrylanów do drewna i sposób wytwarzania lakieru na bazie akrylanów do drewna.The present invention relates to a photoreactive acrylate wood lacquer composition and a method for producing an acrylate wood lacquer.
W opisie międzynarodowego zgłoszenia wynalazku WO01/51533 przedstawiono utwardzalne UV lakiery do drewna, zawierające w swoim składzie akrylowane żywice epoksydowe, akrylowane alifatyczne oligomery, akrylan izobornylu oraz metakrylan izobornylu. Z opisu międzynarodowego zgłoszenia wynalazku WO2005/111105 znany jest utwardzany lakier UV do powlekania drewna, zawierający w swoim składzie wielofunkcyjne akrylany, aminomodyfikowane akrylowane polietery, poliestroakrylany oraz aminy. W opisie międzynarodowego zgłoszenia wynalazku WO 2007/059294 ujawniono utwardzalne UV lakiery do drewna na bazie wodnych dyspersji poliuretanowych. Opis wynalazku CN101633813B dotyczy wodorozcieńczalnej utwardzalnej UV powłoki do drewna na bazie wodnej emulsji kopolimeru akrylanowego lub wodnej dyspersji poliuretanowej. Opis wynalazku CN102020913 przedstawia sposób wytwarzania utwardzalnej UV farby do drewna na bazie zmodyfikowanej nienas yconej żywicy poliestrowej oraz poliestru akrylanowego. Zgłoszenie patentowe CA2564308A1 ujawnia powłoki utwardzalne promieniowaniem ultrafioletowym na bazie wielofunkcyjnych oligomerów akrylanowych utwardzane na podłożu z drewna. Międzynarodowe zgłoszenie wynalazku WO2009077865A2 dotyczy utwardzalnej UV kompozycji powłoki na bazie izocyjanianów.The description of the international application WO01 / 51533 describes UV-curable wood varnishes containing acrylated epoxy resins, acrylated aliphatic oligomers, isobornyl acrylate and isobornyl methacrylate. The description of the international patent application WO2005 / 111105 describes a cured UV varnish for coating wood, which contains multifunctional acrylates, aminomodified acrylated polyethers, polyester acrylates and amines. WO 2007/059294 discloses UV-curable wood lacquers based on water-based polyurethane dispersions. Description of the invention CN101633813B relates to a waterborne UV curable wood coating based on an aqueous emulsion of acrylate copolymer or an aqueous polyurethane dispersion. Description of the invention CN102020913 describes a method of producing a UV curable wood paint based on a modified unsaturated polyester resin and an acrylate polyester. Patent application CA2564308A1 discloses UV curable coatings based on multifunctional acrylate oligomers cured on a wood substrate. International patent application WO2009077865A2 relates to a UV curable coating composition based on isocyanates.
Przedstawione w stanie techniki fotoreaktywne lakiery utwardzalne promieniowaniem UV, szczególnie na bazie wodnych dyspersji poliuretanowych, charakteryzują się stosunkowo długim czasem utwardzania, wynoszącym często powyżej 1 minuty.The photoreactive UV-curable varnishes presented in the prior art, especially those based on aqueous polyurethane dispersions, are characterized by a relatively long hardening time, often exceeding 1 minute.
Celem wynalazku jest między innymi opracowanie nowej receptury fotoreaktywnego utwardzalnego promieniowaniem UV lakieru do drewna, umożliwiającej jego szybkie utwardzanie pod lampą UV.The aim of the invention is, inter alia, to develop a new formulation for a photoreactive UV-curable varnish for wood, enabling its quick curing under a UV lamp.
Kompozycja fotoreaktywnego lakieru na bazie akrylanów do drewna, według wynalazku, charakteryzuje się tym, że zawiera fotoreaktywny lakier na bazie alifatycznych uretanoakrylanów, zbudowany z 40-80% wagowych alifatycznego uretanoakrylanu, 10-40% wagowych wielofunkcyjnego (met)akrylanu, 5-15% wagowych metakrylanu alkilowego, 3-15% wagowych nienasyconego kwasu karboksylowego, 1-10% wagowych fotoinicjatora rodnikowego, 1-5% wagowych N-winylokaprolaktamu oraz 1-3% wagowych wysokowrzącego rozpuszczalnika. Udział procentowy wszystkich składników wynosi 100%. Alifatyczne uretanoakrylany oraz metakrylany alkilowe odpowiedzialne są za elastyczność utwardzonej powłoki lakieru, natomiast wielofunkcyjne metakrylany oraz fotoinicjator rodnikowy są konieczne w procesie utwardzania fotoreaktywnych lakierów. Nienasycony kwas karboksylowy oraz N-winylokaprolaktam służą polepszeniu adhezji do powierzchni lakierowanego drewna. Wysokowrzący rozpuszczalnik nadaje utwardzonemu lakierowi niezbędny połysk. Korzystnie metakrylan alkilowy stanowi metakrylan 2-etyloheksylu, metakrylan butylu i/lub metakrylan heksylu.The composition of the photoreactive varnish based on acrylates for wood, according to the invention, is characterized in that it contains a photoreactive varnish based on aliphatic urethane acrylates, composed of 40-80% by weight of aliphatic urethane acrylate, 10-40% by weight of multifunctional (meth) acrylate, 5-15% by weight of alkyl methacrylate, 3-15% by weight of unsaturated carboxylic acid, 1-10% by weight of a radical photoinitiator, 1-5% by weight of N-vinyl caprolactam and 1-3% by weight of high-boiling solvent. The percentage of all ingredients is 100%. Aliphatic urethane acrylates and alkyl methacrylates are responsible for the flexibility of the hardened varnish coat, while multifunctional methacrylates and a radical photoinitiator are necessary in the process of curing photoreactive varnishes. Unsaturated carboxylic acid and N-vinyl caprolactam serve to improve adhesion to the surface of varnished wood. High-boiling solvent gives the hardened varnish the necessary shine. Preferably the alkyl methacrylate is 2-ethylhexyl methacrylate, butyl methacrylate and / or hexyl methacrylate.
Korzystnie nienasycony kwas karboksylowy stanowi kwas akrylowy, kwas metakrylowy, kwas krotonowy, kwas itakowy i/lub kwas β-akryloilooksypropionowy.Preferably the unsaturated carboxylic acid is acrylic acid, methacrylic acid, crotonic acid, itacic acid and / or β-acryloyloxypropionic acid.
Korzystnie wysokowrzący rozpuszczalnik stanowi octan 2-etyloheksylu, octan butylu, octan heptylu i/lub octan heksylu.Preferably the high boiling solvent is 2-ethylhexyl acetate, butyl acetate, heptyl acetate and / or hexyl acetate.
Kompozycja jest fotoreaktywna w promieniowaniu UV o natężeniu od 500 do 1000 mJ/cm2.The composition is photoreactive under UV radiation at an intensity of 500 to 1000 mJ / cm 2 .
Sposób wytwarzania lakieru na bazie akrylanów do drewna, według wynalazku, utwardzanego promieniowaniem UV, charakteryzuje się tym, że miesza się 40-80% wagowych alifatycznego uretanoakrylanu, 10-40% wagowych wielofunkcyjnego (met)akrylanu, 5-15% wagowych metakrylanu alkilowego, 3-15% wagowych nienasyconego kwasu karboksylowego, 1-10% wagowych fotoinicjatora rodnikowego, 1-5% wagowych N-winylokaprolaktamu oraz 1-3% wagowych wysokowrzącego rozpuszczalnika. Udział procentowy wszystkich składników wynosi 100%. Następnie tak otrzymaną kompozycję lakieru nanosi się na powierzchnię drewnianą i utwardza elektromagnetycznym z zakresu UV. Alifatyczne uretanoakrylany oraz metakrylany alkilowe odpowiedzialne są za elastyczność utwardzonej powłoki lakieru, natomiast wielofunkcyjne metakrylany oraz fotoinicjator rodnikowy są konieczne w pr ocesie utwardzania fotoreaktywnych lakierów. Nienasycony kwas karboksylowy oraz N-winylokaprolaktam służą polepszeniu adhezji do powierzchni lakierowanego drewna. Wysokowrzący rozpuszczalnik nadaje utwardzonemu lakierowi niezbędny połysk.The method of producing a varnish based on acrylates for wood, according to the invention, cured with UV radiation, is characterized by mixing 40-80% by weight of aliphatic urethane acrylate, 10-40% by weight of multifunctional (meth) acrylate, 5-15% by weight of alkyl methacrylate, 3-15 wt.% Unsaturated carboxylic acid, 1-10 wt.% Radical photoinitiator, 1-5 wt.% N-vinyl caprolactam and 1-3 wt.% High-boiling solvent. The percentage of all ingredients is 100%. Then, the lacquer composition obtained in this way is applied to a wooden surface and cured with an electromagnetic UV range. Aliphatic urethane acrylates and alkyl methacrylates are responsible for the flexibility of the hardened varnish coating, while multifunctional methacrylates and a radical photoinitiator are necessary in the process of curing photoreactive varnishes. Unsaturated carboxylic acid and N-vinyl caprolactam serve to improve adhesion to the surface of varnished wood. High-boiling solvent gives the hardened varnish the necessary shine.
Korzystnie jako metakrylan alkilowy stosuje się metakrylan 2-etyloheksylu, metakrylan butylu i/lub metakrylan heksylu.Preferably, 2-ethylhexyl methacrylate, butyl methacrylate and / or hexyl methacrylate are used as the alkyl methacrylate.
Korzystnie jako nienasycony kwas karboksylowy stosuje się kwas akrylowy, kwas metakrylowy, kwas krotonowy, kwas itakowy i/lub kwas β-akryloilooksypropionowy.Preferably, acrylic acid, methacrylic acid, crotonic acid, itacic acid and / or β-acryloyloxypropionic acid are used as the unsaturated carboxylic acid.
PL 235 244 B1PL 235 244 B1
Korzystnie jako wysokowrzący rozpuszczalnik stosuje się octan 2-etyloheksylu, octan butylu, octan heptylu i/lub octan heksylu.Preferably, 2-ethylhexyl acetate, butyl acetate, heptyl acetate and / or hexyl acetate are used as high-boiling solvent.
Korzystnie do utwardzania stosuje się w promieniowaniu elektromagnetycznym z zakresu UV o natężeniu od 500 do 1000 mJ/cm2.Preferably, electromagnetic radiation in the UV range of 500 to 1000 mJ / cm 2 is used for curing.
Fotoreaktywne kompozycje polimerowe stosowane jako lakiery do drewna mogą być utwardzalne przy pomocy specjalnie do tego celu skonstruowanych lamp UV. Urządzenia te, emitują promieniowanie elektromagnetyczne, które powoduje powstanie ośrodka aktywnego w polimeryzacji rodnikowej. W pierwszym etapie fotoinicjator zastosowany w układzie polimerowym rozpada się na rodniki, które w kolejnym etapie inicjują reakcję polimeryzacji kompozycji lakieru, powodując tym samym jego utwardzanie. Aby utwardzić lakier należy dobrać lampę emitującą odpowiedni zakres długości fali promieniowania elektromagnetycznego dostosowanego do absorpcji fotoinicjatora. W tym celu stosuje się specjalne lampy emitujące promieniowanie UV.Photoreactive polymer compositions used as wood varnishes can be cured using UV lamps specially designed for this purpose. These devices emit electromagnetic radiation, which creates an active medium in free radical polymerization. In the first stage, the photoinitiator used in the polymer system breaks down into radicals, which in the next stage initiate the polymerization reaction of the varnish composition, thus causing its hardening. In order to harden the varnish, a lamp should be selected that emits the appropriate wavelength range of electromagnetic radiation adjusted to the absorption of the photoinitiator. For this purpose, special lamps that emit UV radiation are used.
Lakier wg wynalazku do drewna na bazie uretanoakrylanów utwardzalny promieniowaniem UV jest bezbarwny, posiada wysoki połysk i gładką powierzchnię oraz charakteryzuje się łatwością w rozprowadzaniu cienkiej warstwy na powierzchni drewna. Uzyskany film lakieru utwardzany jest pod lampą UV w krótkim czasie, jest stosunkowo elastyczny, co doskonale wpływa na właściwości użytkowe polakierowanych drewnianych powierzchni. Fotoreaktywny lakier ma bardzo dobrą przyczepność do powierzchni drewna i dobrze do niej przylega. UV-utwardzalne powłoki na bazie uretanoakrylanów wg wynalazku są przyjazne dla środowiska, prawie bez zapachu. Powłoka utwardzonego UV lakieru jest odporna na rozpuszczalniki organiczne, jak np. aceton, izopropanol, octan butylu, octan etylu oraz etanol.The UV-curable urethane acrylate wood varnish according to the invention is colorless, has a high gloss and smooth surface, and is easy to spread a thin layer on the wood surface. The obtained varnish film is hardened under a UV lamp in a short time, it is relatively flexible, which has a great impact on the performance of varnished wooden surfaces. The photo-reactive varnish adheres very well to the wood surface and adheres well to it. The UV-curable coatings based on urethane acrylates according to the invention are environmentally friendly, almost odorless. The coating of the UV-cured varnish is resistant to organic solvents such as acetone, isopropanol, butyl acetate, ethyl acetate and ethanol.
Wynalazek ilustrują bliżej poniższe przykłady wykonania.The invention is illustrated in more detail by the following examples.
P r z y k ł a d 1P r z k ł a d 1
Kompozycję fotoutwardzalnego UV lakieru do drewna otrzymano mieszając ze sobą 40 g (40% wag.) uretanoakrylanu Genomer 1122 (Poly-Chem), 40 g (40% wag.) wielofunkcyjnego metakrylanu EGDMA (BASF), 13 g (13% wag.) metakrylanu 2-etyloheksylu (BASF), 3 g (3% wag.) kwasu akrylowego (BASF), 2 g (2% wag.) fotoinicjatora Irgacure 184 (BASF), 1 g (1% wag.) N-winylokaprolaktamu oraz 1 g (1% wag.) octanu butylu. Tak otrzymaną kompozycję lakieru nałożono o grubości 0,06 μm na drewniane sosnowe deski, a następnie utwardzono 45 s pod lampą UV Aktiprint-mini-18-2 niemieckiej firmy Technigraf emitującej promieniowanie o dawce 850 mJ/cm2, uzyskując utwardzoną powłokę lakieru na sosnowych płytkach.The UV photo-curable wood varnish composition was obtained by mixing together 40 g (40 wt.%) Of Genomer 1122 urethane acrylate (Poly-Chem), 40 g (40 wt.%) Of the multifunctional EGDMA methacrylate (BASF), 13 g (13 wt.%). 2-ethylhexyl methacrylate (BASF), 3 g (3 wt.%) acrylic acid (BASF), 2 g (2 wt.%) Irgacure 184 photoinitiator (BASF), 1 g (1 wt.%) N-vinyl caprolactam and 1 g (1 wt.%) of butyl acetate. The thus obtained varnish composition was applied with a thickness of 0.06 μm on pine wooden boards, and then cured for 45 seconds under the Aktiprint-mini-18-2 UV lamp of the German company Technigraf emitting radiation at a dose of 850 mJ / cm 2 , obtaining a hardened varnish coating on pine boards. tiles.
P r z y k ł a d 2P r z k ł a d 2
Kompozycję fotoutwardzalnego UV lakieru do drewna otrzymano mieszając ze sobą 80 g (80% wag.) uretanoakrylanu Ebecryl 1039 (Cytec), 10 g (10% wag.) wielofunkcyjnego metakrylanu DEGDMA (BASF), 5 g (5% wag.) metakrylanu butylu (BASF), 2 g (2% wag.) kwasu metakrylowego (BASF), 1 g (1% wag.) fotoinicjatora Irgacure 127 (BASF), 1 g (1% wag.) N-winylokaprolaktamu oraz 1 g (1% wag.) octanu heptylu. Tak otrzymaną kompozycję lakieru nałożono o grubości 0,09 μm na drewniane dębowe deski, a następnie utwardzono 30 s pod lampą UV Aktiprint-mini-18-2 niemieckiej firmy Technigraf emitującej promieniowanie o dawce 900 mJ/cm2, uzyskując utwardzoną powłokę lakieru na dębowych płytkach.The composition of the UV photocurable varnish for wood was obtained by mixing together 80 g (80% by weight) of Ebecryl 1039 urethane acrylate (Cytec), 10 g (10% by weight) of DEGDMA multifunctional methacrylate (BASF), 5 g (5% by weight) of butyl methacrylate (BASF), 2 g (2 wt.%) Methacrylic acid (BASF), 1 g (1 wt.%) Irgacure 127 photoinitiator (BASF), 1 g (1 wt.%) N-vinyl caprolactam and 1 g (1% by weight) wt.) of heptyl acetate. The thus obtained varnish composition was applied with a thickness of 0.09 μm on wooden oak boards, and then cured for 30 seconds under the Aktiprint-mini-18-2 UV lamp from the German company Technigraf emitting radiation at a dose of 900 mJ / cm 2 , obtaining a hardened varnish coating on oak trees. tiles.
P r z y k ł a d 3P r z k ł a d 3
Kompozycję fotoutwardzalnego UV lakieru do drewna otrzymano mieszając ze sobą 43 g (43% wag.) uretanoakrylanu Photomer 6230 (IGM Resins), 25 g (25% wag.) wielofunkcyjnego akrylanu PEG(200)DA (IGM Resins), 15 g (15% wag.) metakrylanu heksylu (BASF), 3 g (3% wag.) kwasu krotonowego, 6 g (5% wag.) fotoinicjatora Irgacure 651 (BASF), 2 g (2% wag.) N-winylokaprolaktamu oraz 3 g (3% wag.) octanu heksylu. Tak otrzymaną kompozycję lakieru nałożono o grubości 0,10 μm na drewniane jesionowe deski, a następnie utwardzono 35 s pod lampą UV Aktiprint-mini-18-2 niemieckiej firmy Technigraf emitującej promieniowanie o dawce 650 mJ/cm2, uzyskując utwardzoną powłokę lakieru na jesionowych płytkach.The composition of the UV photo-curable wood varnish was obtained by mixing 43 g (43% by weight) of urethane acrylate Photomer 6230 (IGM Resins), 25 g (25% by weight) of the multifunctional acrylate PEG (200) DA (IGM Resins), 15 g (15 wt.% hexyl methacrylate (BASF), 3 g (3 wt.%) crotonic acid, 6 g (5 wt.%) Irgacure 651 photoinitiator (BASF), 2 g (2 wt.%) N-vinyl caprolactam and 3 g (3 wt.%) Hexyl acetate. The thus obtained varnish composition was applied with a thickness of 0.10 μm on wooden ash planks, and then hardened for 35 seconds under the Aktiprint-mini-18-2 UV lamp from the German company Technigraf emitting radiation at a dose of 650 mJ / cm 2 , obtaining a hardened varnish coating on ash planks. tiles.
P r z y k ł a d 4P r z k ł a d 4
Kompozycję fotoutwardzalnego UV lakieru do drewna otrzymano mieszając ze sobą 50 g (50% wag.) uretanoakrylanu Photomer 6010 (IGM Resins), 10 g (10% wag.) wielofunkcyjnego metakrylanu TPGDA (BASF), 9 g (9% wag.) metakrylanu butylu (BASF), 15 g (15% wag.) kwasu β-akryloilooksypropionowego (BASF), 10 g (10% wag.) fotoinicjatora Irgacure 184 (BASF), 5 g (5% wag.) N-winylokaprolaktamu oraz 1 g (1% wag.) octanu 2-etyloheksylu. Tak otrzymaną kompozycję lakieru nałożono o grubości 0,12 μm na drewniane deski grabu, a następnie utwardzono 20 s pod lampą UV Aktiprint-mini-18-2The composition of the UV photocurable varnish for wood was obtained by mixing 50 g (50% by weight) of urethane acrylate Photomer 6010 (IGM Resins), 10 g (10% by weight) of multifunctional TPGDA methacrylate (BASF), 9 g (9% by weight) of methacrylate. butyl (BASF), 15 g (15 wt.%) of β-acryloyloxypropionic acid (BASF), 10 g (10 wt.%) of Irgacure 184 photoinitiator (BASF), 5 g (5 wt.%) of N-vinyl caprolactam and 1 g (1 wt.%) 2-ethylhexyl acetate. The thus obtained varnish composition was applied with a thickness of 0.12 μm on wooden hornbeam boards, and then hardened for 20 seconds under the Aktiprint-mini-18-2 UV lamp
PL 235 244 B1 niemieckiej firmy Technigraf emitującej promieniowanie o dawce 550 mJ/cm2, uzyskując utwardzoną powłokę lakieru na płytkach z grabu.PL 235 244 B1 of the German company Technigraf emitting radiation at a dose of 550 mJ / cm 2 , obtaining a hardened coating of varnish on hornbeam tiles.
P r z y k ł a d 5P r z k ł a d 5
Kompozycję fotoutwardzalnego UV lakieru do drewna otrzymano mieszając ze sobą 50 g (50% wag.) uretanoakrylanu Genomer 1122 (Poly-Chem), 23 g (23% wag.) wielofunkcyjnego metakrylanu DPGDA (BASF), 7 g (7% wag.) metakrylanu 2-etyloheksylu (BASF), 10 g (10% wag.) kwasu itakonowego, 5 g (5% wag.) fotoinicjatora Lucirin TPO (BASF), 3 g (3% wag.) N-winylokaprolaktamu oraz 2 g (2% wag.) octanu butylu. Tak otrzymaną kompozycję lakieru nałożono o grubości 0,15 μm na drewniane deski bukowe, a następnie utwardzono 50 s pod lampą UV Aktiprint-mini-18-2 niemieckiej firmy Technigraf emitującej promieniowanie o dawce 700 mJ/cm2, uzyskując utwardzoną powłokę lakieru na płytkach z buku.The UV photo-curable wood varnish composition was obtained by mixing 50 g (50% by weight) of Genomer 1122 urethane acrylate (Poly-Chem), 23 g (23% by weight) of DPGDA multifunctional methacrylate (BASF), and 7 g (7% by weight). 2-ethylhexyl methacrylate (BASF), 10 g (10 wt.%) itaconic acid, 5 g (5 wt.%) Lucirin TPO photoinitiator (BASF), 3 g (3 wt.%) N-vinyl caprolactam and 2 g (2 wt.%) of butyl acetate. The thus obtained varnish composition was applied with a thickness of 0.15 μm on wooden beech boards, and then hardened for 50 seconds under the Aktiprint-mini-18-2 UV lamp of the German company Technigraf emitting radiation at a dose of 700 mJ / cm 2 , obtaining a hardened varnish coating on the tiles. from beech.
Claims (10)